METHOD FOR PRODUCING AN OXYHYDRIDE-BASED PHOTOCHROMIC DEVICE

Abstract

The present invention relates to a method for producing a photochromic oxy-hydride material as well as a photochromic component. The method comprising the steps of: —first the formation on a substrate of a layer of an essentially oxygen free rare earth metal hydride with a predetermined thickness using a physical vapor deposition process; and—second exposing the metal hydride layer to oxygen where the oxygen reacts with the metal hydride, said second step being performed in an environment having a water content defined by a water amount in air at sea level pressure with RH between >0% and 100% RH for temperatures between 0° C. and 40° C., preferably 25° Celsius.

Claims

1. A method for producing a photochromic rare-earth metal oxyhydride material, the method comprising: first, in an environment with less than 0.1 ppm O.sub.2, formation on a substrate of a layer of an essentially oxygen free rare-earth metal hydride with a predetermined thickness using a physical vapor deposition process; and second, exposing the rare-earth metal hydride layer to an oxygen containing environment where the layer oxidizes and results with rare-earth metal oxyhydride, the second step being performed in an environment having water content in any form with a range defined by a water amount in air at sea level pressure with RH between >0% and 60% RH for temperatures between 0° C. and 40° C.

2. The method according to claim 1, wherein the metal in the metal hydride is yttrium.

3. The method according to claim 1, wherein the thickness of the formed rare earth metal hydride layer is within the range of 50-1500 nm using a physical vapor deposition process

4. The method according to claim 1, followed by the step of oxidizing the material in a humidity tight container.

5. The method according to claim 1, followed by the step of containing or covering the oxyhydride material in a humidity/watertight material maintaining a humidity/water content in the container at a level less than air at sea level pressure with 10% RH at 25° C. and the oxyhydride material having a water content H.sub.2O≥0.1 ppm.

6. The method according to claim 1, wherein the metal hydride is fabricated on a transparent substrate.

7. The method according to claim 1, wherein the water content as defined in step 2 is less than 60% RH at a temperature of 25° Celsius.

8. A photochromic component comprising: a first transparent substrate and a layer constituted rare earth metal oxyhydride produced according to the method of claim 1; wherein the first transparent substrate is covered by a humidity/water tight container; and wherein an environment in the container comprises water content in any form, equal or less than the water content of air at sea level pressure with 20% RH at 25° C. and the photochromic rare-earth metal oxyhydride material has a water content of H.sub.2O≥0.1 ppm.

9. The photochromic component according to claim 8, wherein the thickness of the rare earth metal hydride layer is within the range of 50-1500 nm.

10. The photochromic component according to claim 8, wherein the rare earth metal is yttrium.

11. The photochromic component according to claim 8, wherein the container comprises water content in any form, equal or less than the water content of air at sea level pressure with 10% RH at 25° C.

12. The photochromic component according to claim 8, wherein the container comprises water content in any form, equal or less than the water content of air at sea level pressure with 5% RH at 30° C.

13. The photochromic component according to claim 8, comprising the material produced using the method according to claim 1.

14. The method according to claim 6, wherein the transparent substrate is a glass or polymer-based substrate.

Description

[0007] The invention will be described more in detail with reference to the accompanying drawings, illustrating the reason of the improvement to the device described above:

[0008] FIG. 1a-c Illustrates the production method according to the invention.

[0009] FIG. 2a-e Illustrates photochromic oxyhydride material optical kinetic degradation after stored at varying relative humidity levels.

[0010] FIG. 3 Illustrates microstructure deformation, caused by varying relative humidity levels.

[0011] FIG. 4a,b Illustrates the photochromic kinetic difference between dry air (H2O<0.1 ppm) environment and ambient air environment.

[0012] FIG. 1a-c illustrates the production method according to the invention where the process with the deposition of an essentially oxygen-free metal hydride 2, preferably less than 0.1 ppm O.sub.2, onto a substrate 1 (e.g. glass or a polymer-based substrate) as in FIG. 1a. The substrate is transparent where the aim of the photochromic layer is to provide a variable transmission rate depending on the light intensity. Transparent in this case also including a degree of attenuation, e.g. for permanent shading. The performance of the step of applying the metal hydride in the oxygen-free environment is known to the person skilled in the art, e.g. as discussed in WO2018/024394. The metal hydride may comprise a metal from the groups of rare earth elements, but according to the preferred embodiment of the invention the metal is yttrium, forming yttrium hydride.

[0013] In FIG. 1b the rare-earth metal hydride is exposed to an environment 3 that oxidizes the metal hydride, preferably in an environment where humidity present, forming rare-earth metal oxyhydride. Humidity in this case referring to any one of water vapour, liquid water in air or liquid water, as it is the chemical response with the water molecules that initiates the reaction. The oxidising environment should contain water in any form with a range of: water amount in air at sea level pressure with RH between >0% RH and 100% RH, preferably 60% RH, for temperatures between 0° C. and 40° C., preferably 25° Celsius.

[0014] In FIG. 1c the substrate 1 and the resulting oxyhydride is enclosed in a container 5 or similar keeping the relative humidity around the photochromic material at a low level which would contain less water in any form than the air at sea level pressure with 10% RH at 25° Celsius and above than 0.1 ppm H.sub.2O.

[0015] According to the present invention the exposure to humidity is therefore limited afterward production so as to maintain the photochromic characteristics of the material.

[0016] The final oxygen content of the active photochromic film can be pre-defined by controlling properties like porosity and microstructure, thickness and other features of the as-deposited metal hydride as discussed in the publications mentioned above. These properties, as described below, can be achieved by tuning the deposition parameters, such as substrate temperature, substrate type, chamber pressure, sputtering power, deposition time, deposition gas flow, etc.

[0017] As mentioned above rare-earth metal oxyhydride materials, particularly yttrium oxyhydrides, are highly susceptible to environment. After oxidation at the end of the production process environmental elements, specifically water content in the air, cause cracking of the films, delamination, reducing the contrast, and damaging the photochromic kinetics. To illustrate this, we refer to the accompanying graphs in FIG. 2a-2e, an experimental procedure was designed using yttrium oxyhydride thin film coatings which were prepared according to the T. Mongstad (2011), C.C. You (2014) articles and WO2017/125573, then immediately after oxidation on air, placed in airtight boxes filled with regular air but with varying relative humidity at 25° C. temperature. FIGS. 2a-e demonstrate photochromic kinetics of stored samples in relative humidity (RH) from <10% RH to 100% RH, respectively. Photochromic kinetic studies were performed with 30 minutes of illumination using an UV Laser and 30 minutes of storing at dark for recovery (bleaching). Kinetic studies were performed after 2, 4 and 14 days storing inside the airtight boxes with respective relative humidity.

[0018] Photochromic yttrium oxyhydride coatings, initially, showing 25% contrast however, every sample demonstrates lower contrast with increased contrast loss depending on storage time (FIG. 2(a-e)). Contrast loss is strongly dependent on storage time but also water content level in the air is a factor for the speed of contrast loss. This can be observed, from FIGS. 2a-2e where contrast loss is more notable for samples stored at 100% RH after 14 days than at <10% RH and, samples stored at 100% RH lost the same contrast under 4 days as the samples stored at <10% RH but after 14 days.

[0019] FIG. 3 Scanning electron microscopy (SEM) images of microstructure deformation, caused by varying relative humidity levels; <10% (a), 30% (b), 50% (c), 75% (d) and 100% (e) after 14 days storage at room temperature. Panel (f) showing one deformation in detail. As can be seen structural change depending on the water content level in the air after 14 days of storage. Parallel to the increasing water content in air, increasing number of cracks and deformation can be observed which is correlated with contrast loss of photochromic oxyhydride material. On the other hand, absence of moisture as how conventional insulating glass units on buildings being prepared, has negative impact on the material's photochromic kinetics. In FIG. 4(a,b), photochromic kinetics of yttrium oxyhydride in dry air environment (H.sub.2O<0.1 ppm) and ambient air environment can be observed. Bleaching speed of yttrium oxyhydride slowed considerably as a result of reduced oxidation agent presence, namely water content in air.

[0020] Due to the kinetic loss and structural deformation under air with higher water content than the water content of air with 10% RH at 25° C., storage and working environment of oxyhydride materials should therefore contain less water than the water content of air with 10% RH at 25° C. water. Additionally, due to the kinetic loss under dry air environment with water content of H.sub.2O<0.1 ppm, storage and working environment of oxyhydride materials should therefore contain water; H.sub.2O≥0.1 ppm. Therefore, the produced material is preferably enclosed in a container after production having the described humidity in the contained environment.

[0021] As will also be understood by the person skilled in the art a small change of humidity and temperature would have the same water content but technically different humidity. Thus a water content of air with same volume at sea level pressure that is 25° C. and 10% RH may correspond to 5% RH at 30° C. more or less equal as higher temperature can hold more water and this humidity is Relative Humidity to the same water content to this defined limit. Therefore, under some circumstances the water content corresponding to 20% at sea level pressure and is 25° C. depending on the intended use of the component, for example with varying temperatures.

[0022] To summarize the present invention relates to a method for producing a photochromic rare-earth metal oxyhydride material comprising the steps of formation on a substrate of a layer of an essentially oxygen free rare-earth metal hydride with a predetermined thickness preferably within the range of 50-1500 nm using a physical vapor deposition process. The substrate will preferably be a transparent substrate, e.g. a glass or polymer-based substrate. Following this the rare-earth metal hydride layer is exposed to air in a second step, where the metal hydride oxidises, by oxygen and water (humidity, vapour and/or moisture). The second step is performed in an environment which contain water in any form with a range of: water amount in air at sea level pressure with RH between >0% and 100% RH, preferably 60%, for temperatures between 0° C. and 40° C., preferably 25° Celsius

[0023] The metal hydride is chosen from the groups of rare earth metals, and according to the preferred embodiment of the invention an yttrium hydride.

[0024] In order to maintain the characteristics of the photochromic material the second step may be followed by a step of containing the material in a tight container or covering the photochromic material in a humidity/water tight material, sealing it from the environment.

[0025] The rare-earth metal hydride may have a porosity being above zero, i.e. it contains hollow pores, voids and/or cavities to improve the absorption of oxygen in the oxyhydride.

[0026] According to one preferred aspect of the invention a photochromic component is provided comprising a first, transparent substrate and a layer constituted metal oxyhydride enclosed in a humidity/water tight enclosure, where the oxyhydride is made from a rare-earth metal oxy-hydride, preferably an yttrium oxyhydride, which can be made using the method described above. The environment in the container comprise water content in any form, equal or less than the water content of air at sea level pressure with 20% RH at 25° C., preferably 10% RH and above 0.1 ppm H.sub.2O.