HIGH-PRESSURE SEAMLESS STEEL CYLINDER WITH SECOND INNER NECK AND THE METHOD OF ITS PRODUCTION

Abstract

A method of producing a high-pressure steel cylinder by forming from an individual dimension piece, consisting of an upper neck on the rounded end, which protrudes from the cylinder and it is provided by an opening the cylinder is additionally provided on its bottom with another bottom neck made in an inner material strengthening which is orientated insidewards of the high-pressure steel cylinder and the inner material strengthening is provided by a through-out opening.

Claims

1. The high-pressure steel cylinder (1) made by forming from an individual dimension piece, consisting of an upper neck (3) on the rounded end, which protrudes from the cylinder and it is provided by an opening (14), characterized in, that it is additionally provided on its bottom (12) with another bottom neck (5) made in an inner material strenghtening (11) which is orientated insidewards of the high-pressure steel cylinder (1) and the inner material strenghtening (11) is provided by a through-out opening (13).

2. Method of production of seamless high-pressure steel cylinder (1) according to the claim 1, where the cylinder is made in the first step by backwards extrusion process, when first the bottom is produced by using of a shaped punching head, wherein the head has a bigger outer diameter and the die has greater inner diameter than the final dimensions are, and afterwards the broaching with monolitic pressing mandrel provided with the shaped end is done, which has the same form of the bottom surface as the shaped punching head, characterized in, that on the outer surface (10) of the shaped punching head (8) a cavity (6) for creating of the inner material stranghtening (11) of the bottom (12) of the high-pressure steel cylinder (1) is created and the backwards extrusion using such modified shaped punching head (8) is done, afterwords in the subsequent step the backwards extrusion process with monolitic pressing mandrel (7) is done, the mandrel (7) is provided by the shaped end (18) provided with the cavity (6), wherein the rest of the high-pressure steel cylinder (1) is made by the known method and in the end the inner material strenghtening (11) on the bottom (12) of the high-pressure steel cylinder (1) is drilled through and so the through-out bottom neck (5) is created.

Description

DESCRIPTION OF THE DRAWINGS

[0014] The invention will be explained by use of drawings, where

[0015] FIG. 1 is a view on the one-side open steel cylinder with one neck made by forming according to the state of art,

[0016] FIG. 2 is a view on the flat forming punching head according to the state of art to production of the cylinders according to FIG. 1,

[0017] FIG. 3 is a view on both-side open steel cylinder made of tube using the rotation forming technology,

[0018] FIG. 4 presents the steel cylinder according to the invention,

[0019] FIG. 5 presents a shaped punching head according to the invention for production of the steel cylinder according to FIG. 4,

[0020] FIG. 6 presents the first operation of forming of the steel cylinder according to FIG. 4 with the shaped punching head according to FIG. 5,

[0021] FIG. 7 is a view on monolitic pressing mandrel with shaped end of the same shape of the bottom as by the forming punching head from FIG. 5,

[0022] FIG. 8 presents a semi-finished blank after realization of operation from FIG. 6 and

[0023] FIG. 9 presents an another step of production of the second neck by the steel cylinder from FIG. 4.

PREFERRED EMBODIMENTS OF THE INVENTION

[0024] In FIG. 4 the high-pressure steel cylinder 1 according to the invention is presented. It consists of an upper part 2 with an upper neck 3 of already known embodiment and further of inovatively made bottom part 4 with a bottom neck 5, which is completely over the level of lower surface of the bottom part 4.

[0025] In FIG. 5 a shaped punching head 8 according to the invention is presented, which is like by the method according to the state of the art an individual part and it is placed on the end of an unillustrated pressing mandrel. In the first forming operation a thick-wall semi-finished blank is producedsee FIG. 6. The shaped punching head 8 has again a little bit bigger outer diameter and the die 16 a little bit bigger inner diameter, so the bottom of the cylinder is pressed practically on final thickness, nevertheless the wall of the pressed semi-finished blank is more thick than the final thicknessthat is good to see in FIG. 6, where there is the different thickness of the bottompractically the final thicknessand of the walls. The face 9 of the shaped punching head 8 according to the invention is on its outer surface 10 provided with a cavity 6. This is advantageously made as cylindrical and it is in the axis of the shaped punching head 8. It is obvious, that into this cavity 6 the material flows and an inner material strenghtening 11 of the bottom 12 is created.

[0026] It is good to see in FIG. 6, where the shaped punching head 8 is placed on an here unillustrated punching mandrel during the process of the backward extrusion.

[0027] In FIG. 7 there is a view on a whole monolitic pressing madrel 7, which is on its face provided with shaped end 18 with the cavity 6, but they create together one piece.

[0028] In FIG. 8 the final shape of the bottom part 4 of the high-pressure steel cylinder 1 after its drawing off from last broaching set can be seen. The bottom part 4 is provided with inner material strenghtening 11.

[0029] In FIG. 9 it is seen, that through this inner material strenghtening 11 in the end a through-out opening 13 is drilled and into it a valve or a screw joint like into the opening 14 in the upper neck 3.

[0030] Such high-pressure steel cylinder 1 is made by the following way according to the invention:

[0031] It is made by backward extrusion and broaching method. The forming of the bottom neck 5 is realized already during the first stepbackwards extrusion by the shaped punching head 8 placed on the pressing mandrel. How it is mentioned above, the shaped punching head 8 has a little bit bigger outer diameter and the die 16 has a little bit bigger inner diameter, so the bottom of the cylinder is pressed practically on its final thickness, nevertheless the thickness of the semi-finished blank is more thick than the final thickness of the cylinder.

[0032] With use of the especially modified shaped punching head 8 with the cavity 6 the material is flowing during the forming process into the empty cavity 6 in the shaped punching head 8.

[0033] Next step is the backwards extrusion process on the modified pressing mandrel 7, which is provided with the shaped end 18 with the cavity 6, but it is made as only one piece. That is seen in FIG. 7 where by use of the monolitic pressing mandrel 7 with the shaped end 18, calibration of geometry of the bottom 12 is done. Afterwards the final calibration of sizes of the second neck is done, as illustrated in FIG. 1 or 3.

[0034] Subsequently, the inner material strenghtening 11 in the bottom 12 of the high-pressure steel cylinder 1 is drilled through and the through-out opening 13 is created.

[0035] Due with this way produced steel cylinder the total size of known double neck steel cylinder illustrated in FIG. 3 gets shorter, although the whole volume is kept, not regarding, that the forming technology from individual dimension pieces is substantially easier than the forming technology of steel tubes and also the needed space for transport gets shorter in size and integrity of the steel cylinder is greater, the distribution of strength within the cylinder is lowered, simultaneously there is no lowering of any use parameters or mechanical characteristics etc.

[0036] For realization of the production of the high-pressure steel cylinders according to the invention is necessary only to adjust the geometry of the face of the shaped punching head, when in the center of the face of the shaped punching head make the cavity is made, where the material during the backward extrusion process can flow. Another tool, which is necessary to adjust for production of this new type of cylinders is the monolitic pressing mandrel, on its face it is necessary to create a shaped end with the similar cavity as in case of punching head from the first operation as it is seen in FIG. 7. Other forming tools can stay without geometrical changes. The final process of forming continues in the same way as in the case of production of common high-pressure steel cylinders, as it is described above.

[0037] This type of steel cylinder is unique regarding of broadening of user's attributes because of inner necksit is possible to increase water volume by keeping the same total length of steel cylinders even with valves.