TIRE HAVING IMPROVED RESISTANCE TO THERMAL DEGRADATION

Abstract

A paint having high thermal conductivity to be applied to the outer surface of a tire. The paint consists of a rubber compound having a thermal conductivity greater than or equal to 0.2 Wm.sup.1K.sup.1, a viscosity of between 0.5 and 10000 cP and an elasticity modulus less than or equal to 8 MPa.

Claims

1. A paint having high thermal conductivity to be applied to the outer surface of a tire, said paint being characterized in that it consists of a rubber compound having a thermal conductivity greater than or equal to 0.2 Wm.sup.1K.sup.1, a viscosity of between 0.5 and 10000 cP and an elasticity modulus less than or equal to 8 MPa.

2. The paint according to claim 1, characterized in that said rubber compound comprises a cross-linkable unsaturated chain polymer.

3. The paint according to claim 1, characterized in that said rubber compound is water-based.

4. The paint according to claim 3, characterized in that said water-based compound comprises a filler and an adhesive resin.

5. The paint according to claim 4, characterized in that said filler is carbon black.

6. The paint according to claim 5, characterized in that the carbon black is present in an amount of between 5 and 80 phr.

7. A tire comprising a layer having high thermal conductivity, said tire being characterized in that said layer having high thermal conductivity is made of a paint according to claim 1, applied to at least part of the outer surface of the tire itself.

8. The tire according to claim 7, characterized in that said paint is applied to the grooves of the tread portion and to the sidewalls of the tire.

9. The tire according to claim 7, characterized in that the layer having high thermal conductivity has a thickness of between 10 and 100 m.

Description

[0013] The present invention also relates to a tire comprising a layer having high thermal conductivity, said tire being characterized in that said layer having high thermal conductivity is made using the paint of the present invention, applied to at least part of the outer surface of the tire itself.

[0014] Preferably, said paint is applied to the grooves of the tread portion and to the sidewalls of the tire.

[0015] Preferably, the layer having high thermal conductivity has a thickness of between 10 and 100 m.

[0016] The following are examples of non-limiting embodiments given purely by way of illustration.

[0017] A water-based compound was prepared, the composition of which is recorded in phr in Table I together with its properties in terms of thermal conductivity, viscosity, and elastic modulus.

TABLE-US-00001 TABLE I Natural rubber 100 Carbon black 50 Adhesive resin 20 Sodium oleate 6.5 % of total solids 35 Viscosity (cP) 1000 Thermal conductivity (W/mK) 1.4 Elastic modulus (Mpa) 5

[0018] The carbon black is the N330 type.

[0019] The adhesive resin is a mixture of Icatack 650 and Icatack 1050 resins marketed by the company ICAP-SIRA.

[0020] The viscosity was measured according to the DIN EN ISO3219 standard.

[0021] The thermal conductivity was measured according to the ASTM C177 standard.

[0022] The elastic modulus was measured according to the ASTM D882 standard.

[0023] While the thermal conductivity values recorded as an essential feature of the present invention are necessary in order to achieve a reduction in temperature compared to the known art, the characteristics relating to the viscosity and elasticity are needed in order to ensure, respectively, the correct and effective application of the compound and its constant adhesion to the surface of the tire, which necessarily deforms during use.

[0024] The water-based compound referred to above was tested on the outer surface of a tire in order to verify its effects on the heating of a tire in use. In particular, the water-based compound was applied to some portions of the tread of a tire and, after said tire was exposed to operating conditions, the temperatures therein were measured. For comparison, the temperatures were also measured of other portions of the same tire arranged in a position symmetrical to the portions to which the water-based compound was applied.

[0025] The choice of two symmetrical portions of the same tire in use guarantees that said tire portions are exposed to the same conditions, with the result that the comparison of their temperatures is extremely significant.

[0026] Specifically, the water-based compound was applied (using a brush or by the spraying technique) to an internal groove and to an external groove of the tread in order to also verify the effectiveness of the water-based compound on different parts of the tread. Thereafter, the tire was exposed to the operating conditions specified by the ISO28580-2009 standard and the temperature was measured using an infrared camera of the cooled sensor type (FLIR; Model SC3000).

[0027] In this way, the temperatures recorded at the grooves where the water-based compound of the invention was applied and at the respective symmetrical grooves were measured and then compared. During the test the temperature measurements were recorded at time intervals of 10 minutes, 20 minutes, 40 minutes and 60 minutes.

[0028] Table II shows the values relating to the temperature differences measured respectively for the internal groove and for the external groove. The temperature differences in Table II were calculated by subtracting the temperature values measured at those portions having the paint of the present invention from the temperature values measured at the respective symmetrical portions.

TABLE-US-00002 TABLE II 10 min. 20 min. 40 min. 60 min. t ( C.) external 2.7 4.2 4.1 4.0 groove t ( C.) internal 3.5 3.6 3.2 3.5 groove

[0029] From the values of Table II it is clear that the water-based compound of the present invention, when applied to the outer surface of a tire, is capable of guaranteeing, in the area where it was applied, lower temperatures compared to the situation in which it is absent.

[0030] It should also be pointed out that the water-based compound of the present invention has the great advantage that it can be applied at any point in time during the life of the tire itself.

[0031] Furthermore, another advantage of the present invention relates to the simplicity of applying the paint (using a brush or by the spraying technique).

[0032] Lastly, it was determined that if the tire is found to be in a high humidity environment (for example, in the presence of water or snow) the effects due to the presence of the paint of the present invention are even greater.