METHOD FOR PRODUCING SILICA PARTICLES AND THEIR USE IN COSMETIC COMPOSITIONS

Abstract

The present disclosure relates to silica particles comprising repeating units of (SiO.sub.4/2) that are spherical in shape, which has the benefit of compatibility with personal care components and the resulting personal care applications. The present disclosure also relates to methods of preparing silica particles.

Claims

1. Silica particles comprising repeating units of (SiO.sub.4/2), wherein the silica particles have a D90/D10 particle size distribution of about 1.3 or less as measured by particle size analyzer utilizing laser diffraction particle size analysis, wherein the silica particles are spherical and have a sphericity of 0.9 or more, as defined by minor axis/major axis.

2. The silica particles of claim 1, wherein the silica particles have a D90/D10 particle size distribution of about 1.0 to about 1.2.

3. The silica particles of claim 1, wherein the silica particles have a median (D50) particle size of about 0.5 μm to about 50 μm.

4. The silica particles of claim 1, wherein the silica particles have a BET surface area of about 0.1 m.sup.2/g to about 100 m.sup.2/g.

5. The silica particles of claim 1, wherein the silica particles have sphericity of 0.95 or more as defined by minor axis/major axis.

6. The silica particles of claim 1, wherein the silica particles are non-porous.

7. The silica particles of claim 1, wherein the silica particles are surface-treated with at least one hydrophobicity-imparting agent.

8. The silica particles of claim 7, wherein the hydrophobicity-imparting agent is selected from the group consisting of an alkylsilane, a metal soap, a stearyl modified amino acid, a silicone, fluorinated silane, natural esters, and combinations thereof.

9. The silica particles of claim 7, wherein the hydrophobicity-imparting agent is hexamethyldisilazane.

10. A method of making silica particles, the method comprises heating polymethylsilsesquioxane fine particles at a temperature of 500° C. or less to form the silica particles, wherein the silica particles are spherical and have a sphericity of 0.9 or more, as defined by minor axis/major axis.

11. The method of claim 10, wherein the polymethylsilsesquioxane fine particles are heated in an atmosphere comprising about 20% oxygen or less.

12. The method of claim 10, wherein the polymethylsilsesquioxane fine particles are heated for about 10 minutes to about 6 hours.

13. The method of claim 10, further comprising reducing the temperature of the polymethylsilsesquioxane fine particles to about 400° C.

14. The method of claim 10, wherein the polymethylsilsesquioxane fine particles are heated for about 10 minutes to about 1 hour.

15. The method of claim 10, wherein the polymethylsilsesquioxane fine particles are heated in an atmosphere comprising about 20% oxygen or less.

16. The method of claim 10, wherein the polymethylsilsesquioxane fine particles are heated in an electric furnace, a gas furnace, a far infrared furnace, a medium infrared furnace, or a near infrared furnace.

17. Silica particles prepared by the method of claim 10, wherein the silica particles have a median (D50) particle size of about 0.5 μm to about 50 μm as measured by laser diffraction.

18. The silica particles of claim 17, wherein the silica particles have a mean particle size of about 0.5 μm to about 20 μm.

19. The silica particles of claim 18, wherein the silica particles have a D90/D10 particle size distribution of about 1.3 or less as measured by laser diffraction.

20. The silica particles of claim 17, wherein the silica particles are spherical in shape with sphericity higher than 0.9 as defined by minor axis/major axis.

21. The silica particles of claim 17, wherein the silica particles are non-porous.

22. A personal care formulation comprising the silica particles of claim 1.

23. The personal care formulation of claim 22 wherein the composition further comprises a preservative, an antioxidant, a binder, an anti-foam agent, an anti-static agent, a colorant, an emulsion stabilizer, an oxidation agent, a propellant, an opacity agent, a UV-filter, a UV-absorber, a denaturing agent, a viscosity regulator, a denaturing agent, a chelating agent, a gum or thickener, an oil, a wax, a fragrance, an essential oil, an emulsifier, a surfactant, and combinations thereof.

24. The personal care formulation of claim 23 wherein the personal care is a deodorant, an antiperspirant, a skin cream, a facial cream, a hair shampoo, a hair conditioner, a mousse, a hair styling gel, a hair spray, a protective cream, a lipstick, a lip color, a facial foundations, blushes, makeup, and mascara, a skin care lotion, a moisturizer, a facial treatment, a personal cleanser, a facial cleanser, a bath oil, a perfume, a shaving cream, a pre-shave lotion, an aftershave lotion, a cologne, a sachet, a toothpaste, or a sunscreen.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0021] FIG. 1 is a graph showing the powder formulation with silica with narrow particle size distribution (D90/D10=1.1) showed lower friction coefficient than the formulation with higher particle size distribution (D90/D10=1.9).

[0022] FIG. 2 is an image showing determination of sphericity of particle (minor axis/major axis).

[0023] FIG. 3A and FIG. 3B are distribution graphs showing particle size distribution of spherical particles as prepared using the method of Example 1 (FIG. 3A) and Compative Example 6 (FIG. 3B).

DETAILED DESCRIPTION

I. Definitions

[0024] Unless otherwise indicated, any atom with unsatisfied valences is assumed to have hydrogen atoms sufficient to satisfy the valences.

[0025] The singular forms “a,” “an,” and “the” include plural referents unless the context dictates otherwise.

[0026] Furthermore, “and/or”, where used herein, is to be taken as specific disclosure of each of the two specified features or components with or without the other. Thus, the term “and/or” as used in a phrase such as “A and/or B” herein is intended to include “A and B,” “A or B,” “A” (alone), and “B” (alone). Likewise, the term “and/or” as used in a phrase such as “A, B, and/or C” is intended to encompass each of the following aspects: A, B, and C; A, B, or C; A or C; A or B; B or C; A and C; A and B; B and C; A (alone); B (alone); and C (alone).

[0027] It is understood that wherever aspects are described herein with the language “comprising,” otherwise analogous aspects described in terms of “consisting of” and/or “consisting essentially of” are also provided.

[0028] The term “about” is used herein to mean approximately, roughly, around, or in the regions of. When the term “about” is used in conjunction with a numerical range, it modifies that range by extending the boundaries above and below the numerical values set forth. In general, the term “about” can modify a numerical value above and below the stated value by a variance of, e.g., 10 percent, up or down (higher or lower).

[0029] The phrase “BET surface area”, as used herein, refers to Brunauer-Emmett-Teller surface area.

[0030] The term “sphericity”, as used herein, refers to a parameter to indicate how closely the particle resembles to a perfect sphere and is defined as major axis/minor axisminor axis/major axis obtained from Scanning Microscope Images of the particles. (See FIG. 2)

[0031] As used herein, the following definitions shall apply unless otherwise indicated. For purposes of the present disclosure, the chemical elements are identified in accordance with the Periodic Table of the Elements, CAS version, and the Handbook of Chemistry and Physics, 75.sup.th Ed. 1994. Additionally, general principles of organic chemistry are described in “Organic Chemistry,” Thomas Sorrell, University Science Books, Sausalito: 1999, and “March's Advanced Organic Chemistry,” 6.sup.th Ed., Smith, M. B. and March, J., eds. John Wiley & Sons, New York: 2007, the entire contents of which are hereby incorporated by reference.

[0032] Various aspect of the disclosure are described in greater detail below.

II. Silica Particles

[0033] In one aspect, the present disclosure is directed to silica particles comprising units of (SiO.sub.4/2), wherein the silica particles have a D90/D10 particle size distribution of about 1.3 or less as measured by particle size analyzer utilizing laser diffraction particle size analysis, wherein the silica particles are spherical and have a sphericity of 0.9 or more, as defined by minor axis/major axis.

[0034] a. Particle Size

[0035] In some aspects, the silica particles have a D90/D10 particle size distribution of about 1.0 to about 1.2. In some aspects, the silica particles have a D90/D10 particle size distribution of about 1.0, about 1.1, or about 1.2.

[0036] In some aspects, the silica particles have a median (D50) particle size of about 0.5 μm to about 50 μm. In a further aspect, the the silica particles have a median (D50) particle size of about 1 μm to about 20 μm. In another aspect, the the silica particles have a median (D50) particle size of about 1 μm to about 10 μm. In yet another aspect, the the silica particles have a median (D50) particle size of about 1 μm to about 5 μm. In some aspects, the silica particles have a median (D50) particle size of about 0.5, about 0.75, about 1, about 1.25, about 1.5, about 1.75, about 2, about 2.25, about 2.5, about 2.75, about 3, about 3.25, about 3.5, about 3.75, about 4, about 4.25, about 4.5, about 4.75, about 5, about 10, about 15, about 20, about 25, about 30, about 35, about 40, about 45, or about 50 μm.

[0037] b. Surface Area

[0038] In some aspects, the silica particles have a BET surface area of about 0.1 m.sup.2/g to about 100 m.sup.2/g as measured by TriStar II Plus (Micromeritics). In a further aspect, the silica particles have a BET surface area of about 0.1 m.sup.2/g to about 90 m.sup.2/g. In some aspects, the silica particles have a BET surface area of about 0.1, about 0.25, about 0.5, about 0.75, about 1, about 1.5, about 2, about 2.5, about 3, about 3.5, about 4, about 4.5, about 5, about 10, about 15, about 20, about 25, about 30, about 35, about 40, about 45, about 50, about 55, about 60, about 65, about 70, about 75, about 80, about 85, about 90, about 95, or about 100 m.sup.2/g.

[0039] c. Particle Sphericity

[0040] In some aspects, the silica particles have sphericity of 0.95 or more. In some aspects, the silica particles have a sphericity of 0.95 to 1.

[0041] d. Particle Surface

[0042] In some aspects, the silica particles are non-porous.

[0043] In some aspects, the silica particles are surface-treated with at least one hydrophobicity-imparting agent. In some aspects, the hydrophobicity-imparting agent is an alkylsilane, (e.g., triethoxycaprylyl silane or dimethylsilyl agent), a metal soap (e.g., isopropyl titanium triisostearate), a stearyl modified amino acid (e.g., disodium stearoyl glutamate and aluminium hydroxide), a silicone (e.g., dimethicone), fluorinated (e.g., perfluorooctyl triethoxysilane), and mixtures thereof. In some aspects, the hydrophobicity-imparting agent is hexamethyldisilazane.

III. Methods

[0044] In an aspect, the present disclosure is directed to a method of making silica particles, the method comprises heating polymethylsilsesquioxane fine particles at a temperature of 600° C. or less to form the silica particles, wherein the silica particles are spherical and have a sphericity of 0.9 or more, as defined by minor axis/major axis.

[0045] i. Temperature

[0046] In some aspects, the polymethylsilsesquioxane fine particles are heated at a temperature of about 500° C. or less. In a further aspect, the polymethylsilsesquioxane fine particles are heated at a temperature or about 400° C. or less.

[0047] In some aspects, the polymethylsilsesquioxane fine particles are heated in an electric furnace, a gas furnace, a far infrared furnace, a medium infrared furnace, or a near infrared furnace.

[0048] ii. Atmosphere

[0049] In some aspects, the polymethylsilsesquioxane fine particles are heated in an atmosphere comprising about 20% oxygen or less. In a further aspect, the polymethylsilsesquioxane fine particles are heated in an atmosphere comprising about 15% oxygen or less. In still a further aspect, the polymethylsilsesquioxane fine particles are heated in an atmosphere comprising about 10% oxygen or less. In some aspects, the polymethylsilsesquioxane fine particles are heated in an atmosphere comprising about 20% or less, about 15% or less, about 10% or less, or about 5% oxygen or less. In some aspects, the polymethylsilsesquioxane fine particles are heated in an atmosphere comprising about 20%, about 15%, about 10%, about 5%, about 4%, about 3%, about 2%, or about 1% oxygen.

[0050] iii. Time

[0051] In some aspects, the polymethylsilsesquioxane fine particles are heated for about 10 minutes to about 6 hours. In a further aspect, the polymethylsilsesquioxane fine particles are heated for about 30 minutes to about 5 hours. In some aspects, the polymethylsilsesquioxane fine particles are heated for about 10 minutes, about 15 minutes, about 20 minutes, about 25 minutes, about 30 minutes, about 35 minutes, about 40 minutes, about 45 minutes, about 50 minutes, about 55 minutes, about 1 hour, about 1.25 hours, about 1.5 hours, about 1.75 hours, about 2 hours, about 2.25 hours, about 2.5 hours, about 2.75 hours, about 3 hours, about 2.25 hours, about 3.5 hours, about 3.75 hours, about 4 hours, about 4.25 hours, about 4.5 hours, about 4.75 hours, about 5 hours, about 5.25 hours, about 5.5 hours, about 5.75 hours, or about 6 hours.

[0052] b. Optional Heating Step

[0053] In some aspects, the method may further comprise reducing the temperature of the polymethylsilsesquioxane fine particles to about 400° C.

[0054] i. Atmosphere

[0055] In some aspects, the polymethylsilsesquioxane fine particles are heated in an atmosphere comprising about 20% oxygen or less. In a further aspect, the polymethylsilsesquioxane fine particles are heated in an atmosphere comprising about 15% oxygen or less. In still a further aspect, the polymethylsilsesquioxane fine particles are heated in an atmosphere comprising about 10% oxygen or less. In some aspects, the polymethylsilsesquioxane fine particles are heated in an atmosphere comprising about 20% or less, about 15% or less, about 10% or less, or about 5% oxygen or less. In some aspects, the polymethylsilsesquioxane fine particles are heated in an atmosphere comprising about 20%, about 15%, about 10%, about 5%, about 4%, about 3%, about 2%, or about 1% oxygen.

[0056] ii. Time

[0057] In some aspects, the polymethylsilsesquioxane fine particles are heated for about 10 minutes to about 1 hour. In a further aspect, the polymethylsilsesquioxane fine particles are heated for about 45 minutes. In some aspects, the polymethylsilsesquioxane fine particles are heated for about 10 minutes, about 15 minutes, about 20 minutes, about 25 minutes, about 30 minutes, about 35 minutes, about 40 minutes, about 45 minutes, about 50 minutes, about 55 minutes, or about 1 hour.

[0058] c. Properties

[0059] In an aspect, the silica particles prepared by the method, described herein, have a median (D50) particle size of about 0.5 μm to about 50 μm as measured by laser diffraction.

[0060] i. Particle Size

[0061] In some aspects, the silica particles have a median (D50) particle size of about 0.5 μm to about 50 μm. In a further aspect, the the silica particles have a median (D50) particle size of about 1 μm to about 20 μm. In another aspect, the the silica particles have a median (D50) particle size of about 1 μm to about 10 μm. In yet another aspect, the the silica particles have a median (D50) particle size of about 1 μm to about 5 μm. In some aspects, the silica particles have a median (D50) particle size of about 0.5, about 0.75, about 1, about 1.25, about 1.5, about 1.75, about 2, about 2.25, about 2.5, about 2.75, about 3, about 3.25, about 3.5, about 3.75, about 4, about 4.25, about 4.5, about 4.75, about 5, about 10, about 15, about 20, about 25, about 30, about 35, about 40, about 45, or about 50 μm.

[0062] In some aspects, the the silica particles have a D90/D10 particle size distribution of about 1.3 or less as measured by laser diffraction. In some aspects, the silica particles have a D90/D10 particle size distribution of about 1.0, about 1.1, about 1.2, or about 1.3.

[0063] ii. Particle Sphericity

[0064] In some aspects, the silica particles are spherical in shape with sphericity higher than 0.9. In some aspects, the silica particles are spherical in shape with sphericity of 0.9 to 1.

[0065] iii. Particle Surface

[0066] In some aspects, the silica particles are non-porous.

[0067] In some aspects, the silica particles are surface-treated with at least one hydrophobicity-imparting agent. In some aspects, the hydrophobicity-imparting agent is an alkylsilane, (e.g., triethoxycaprylyl silane or dimethylsilyl agent), a metal soap (e.g., isopropyl titanium triisostearate), a stearyl modified amino acid (e.g., disodium stearoyl glutamate and aluminium hydroxide), a silicone (e.g., dimethicone), fluorinated (e.g., perfluorooctyl triethoxysilane), and mixtures thereof. In some aspects, the hydrophobicity-imparting agent is hexamethyldisilazane.

IV. Personal Care

[0068] In an additional aspect of the present disclosure, the products of the present disclosure, i.e., the silica particles, may be formulated into a personal care item.

[0069] In some aspects, the personal care item may be a cosmetic or a medical product.

[0070] In an aspect, the personal care composition further comprises a preservative, an antioxidant, a binder, an anti-foam agent, an anti-static agent, a colorant, an emulsion stabilizer, an oxidation agent, a propellant, an opacity agent, a UV-filter, a UV-absorber, a denaturing agent, a viscosity regulator, a denaturing agent, a chelating agent, a gum or thickener, an oil, a wax, a fragrance, an essential oil, an emulsifier, a surfactant, and combinations thereof.

[0071] In some aspects, the personal care composition may be formulated with a preservative, an antioxidant, a chelating agent, a gum or thickener, an oil, a wax, a fragrance, an essential oil, an emulsifier, a surfactant, and combinations thereof.

[0072] In some aspects, the products of the present disclosure may be added to formulations comprising make-ups, color cosmetics, foundations, blushes, lipsticks, lip balms, eyeliners, mascaras, oil removers, color cosmetic removers, and powders.

[0073] In some aspects, the products of present disclosure are blended with a hydrophobizing powder. The hydrophobizing powder may be obtained by hydrophobizing the surface of one or more organic or inorganic powders. In some aspects, the one or more organic or inorganic powder may include, without limit, silicone resin particles, nylon-12, PMMA, cellulose, modified starch, talc, boron nitride, polyurethane, and kaolin particles.

[0074] The personal care composition can be a personal care application including deodorants, antiperspirants, antiperspirant/deodorants, shaving products, skin lotions, moisturizers, toners, bath products, cleansing products, hair care products such as shampoos, conditioners, mousses, styling gels, hair sprays, hair dyes, hair color products, hair bleaches, waving products, hair straighteners, manicure products (e.g., nail polish, nail polish remover, nail creams and lotions, cuticle softeners), protective creams (e.g., sunscreen, insect repellent and anti-aging products), color cosmetics (e.g., lipsticks, foundations, face powders, eye liners, eye shadows, blushes, makeup, and mascaras), and dental care (e.g., toothpaste). The personal care application can also be a drug delivery system for topical application of a medicinal composition that can be applied to the skin.

[0075] In one aspect, the personal care composition further comprises one or more personal care ingredients. Suitable personal care ingredients include, without limit, emollients, moisturizers, humectants, pigments (e.g., pearlescent pigments such as bismuth oxychloride and titanium dioxide coated mica), colorants, fragrances, biocides, preservatives, antioxidants, anti-fungal agents, antiperspirant agents, exfoliants, hormones, enzymes, medicinal compounds, vitamins, salts, electrolytes, alcohols, polyols, absorbing agents for ultraviolet radiation, botanical extracts, surfactants, silicone oils, organic oils, waxes, film formers, thickening agents (e.g., fumed silica or hydrated silica), particulate fillers (e.g., talc, kaolin, starch, modified starch, mica, nylon, clays, such as, for example, bentonite and organo-modified clays).

[0076] In some aspects, the one or more personal care components included in the personal care compositions are selected from the group consisting of a humectant, emollient, moisturizer, pigment, colorant, fragrance, biocide, preservative, antioxidant, anti-fungal agent, antiperspirant agent, exfoliant, hormone, enzyme, medicinal compound, vitamin, salt, electrolyte, alcohol, polyol, absorbing agent for ultraviolet radiation, botanical extract, surfactant, silicone oil, organic oil, wax, film former, and thickening agent. In some aspects, the one or more emollients is selected from the group consisting of triglyceride esters, wax esters, alkyl or alkenyl ester of fatty acids, polyhydric alcohol esters, and mixtures thereof. In some aspects, the one or more personal care components is a silicone oil, an organic oil, or mixtures thereof.

[0077] In one aspect, the personal care composition is an antiperspirant composition that comprises a polymer composition or product described herein and one or more active antiperspirant agents. Suitable antiperspirant agents include, but are not limited to, the Category I active antiperspirant ingredients listed in the U.S. Food and Drug Administration's Oct. 10, 1993 Monograph on antiperspirant drug products for over-the-counter human use including aluminum halides, aluminum hydroxyhalides, for example, aluminum chlorohydrate, and complexes or mixtures thereof with zirconyl oxyhalides and zirconyl hydroxyhalides, (e.g., aluminum-zirconium chlorohydrate, and aluminum zirconium glycine complexes, such as aluminum zirconium tetrachlorohydrex gly).

[0078] In another aspect, the personal care composition is a skin care composition comprising a polymer composition or product described herein, and a vehicle, such as a silicone oil or an organic oil. The skin care composition can also include emollients, such as triglyceride esters, wax esters, alkyl or alkenyl esters of fatty acids or polyhydric alcohol esters, pigments, vitamins (e.g., Vitamin A, Vitamin C, and Vitamin E), sunscreen or sunblock compounds (e.g., titanium dioxide, zinc oxide, oxybenzone, octylmethoxy cinnamate, butylmethoxy dibenzoylm ethane, p-aminobenzoic acid, and octyl dimethyl-p-aminobenzoic acid).

[0079] In yet another aspect, the personal care composition is a color cosmetic composition such as a lipstick, a makeup or mascara. The color cosmetic composition comprises a polymer composition or product described herein and a coloring agent (e.g., pigment, water-soluble dye, or liposoluble dye).

Examples

[0080] The following examples are included to demonstrate various aspects of the present disclosure. It should be appreciated by those of skill in the art that the techniques disclosed in the examples that follow represent techniques discovered by the inventors to function well in the practice of the disclosure, and thus can be considered to constitute preferred modes for its practice. However, those of skill in the art should, in light of the present disclosure, appreciate that many changes can be made in the specific examples which are disclosed and still obtain a like or similar result without departing from the spirit and scope of the disclosure.

Example 1: Preparation of Spherical Particles (A)

[0081] In a suitable vessel, width×depth×height of 415×415×50 mm, 500 g of polymethylsilsesquioxane fine particles (Momentive TOSPEARL 145A) with an average particle size of 4.5 m were added and heated at 500° C. for 30 minutes in an atmosphere of 10% oxygen concentration in nitrogen mixed air. The particles were then heated at 400° C. for 45 minutes in an air atmosphere. 445 g of spherical silica fine particles (A) were obtained. The median (D50) particle size of the obtained spherical silica fine particles was 3.8 μm, the particle size dispersion D90/D10 was 1.11 and the BET specific surface area was 1.32 m.sup.2/g as measured by TriStar II Plus (Micromeritics, Norcross, Ga.).

Example 2: Preparation of Spherical Particles (B)

[0082] In a suitable vessel, width×depth×height 415×415×50 mm, 500 g of polymethylsilsesquioxane fine particles (Momentive TOSPEARL 120A) with an average particle diameter of 2 m were added and heated at 450° C. in an air atmosphere for 5 hours. 448 g of spherical silica fine particles (B) were obtained. The median (D50) particle size of the obtained spherical silica fine particles was 1.7 μm, the particle size dispersion D90/D10 was 1.17, and the specific surface area was 2.7 m.sup.2/g as measured by TriStar II Plus.

Example 3: Preparation of Spherical Particles (C)

[0083] In a suitable vessel, width×depth×height of 415×415×50 mm, 300 g of polymethylsilsesquioxane fine particles (Momentive TOSPEARL 1110A) with an average particle size of 11 m were added and heated at 500° C. for 30 minutes, under 10% oxygen concentration in nitrogen mixed air atmosphere. The particles were then heated at 400° C. for 45 minutes in an air atmosphere. 267 g of spherical silica fine particles (C) was obtained. The median (D50) particle size of the obtained spherical silica fine particles was 9.4 μm, the particle size dispersion D90/D10 was 1.08, and the specific surface area was 0.6 m.sup.2/g as measured by Tri Star II Plus.

Example 4: Preparation of Surface-Treated Spherical Particles (D)

[0084] In a suitable vessel, 20 gm of spherical silica particles (A) were dispersed in 10 gms of water. The mixture was mixed with overhead stirrer (IKA Eurostar 100 digital overhead stirrer). Then, 6 gms of hexamethyldisilazane was added to the mixture and the mixture was stirred at 25° C. for 6 hrs. The slurry was then dried at 150° C. for 3 hrs. The dried powder was then sieved through 50 micron sieve. The resulted spherical powder (D) had median particle size (D50) about 3.8 micron. The particle size distribution measured as D90/D10 was 1.11.

Example 5: Powder Foundation

[0085] Powder foundations were prepared with the composition shown in Table 1 using the above silica fine particles (A) to (C) and Tospearl fine particles and Silica fine particles. In the preparation method, first, ingredients of Phase A and Phase B were mixed in Hanil Lab Mixer, then add premixed ingredients of Phase C, and again mixed uniformly using Hanil Lab Mixer, finally the mixture was compression molded into a metal plate.

TABLE-US-00001 TABLE 1 Powder Foundation Formulation Example Comparative Example Phase 1 2 3 1 2 3 4 A Spherical silica particles 10 — — — — — — (A) Spherical silica particles — 10 — — — — — (B) Spherical silica particles — — 10 — — — — (C) 4.5 μm Spherical — — — 10 — — — Methylsilsesquioxane particles, D90/D10: 1.11, specific surface area 67 m.sup.2/g 5 μm Spherical silica — — — — 10 — — particles, D90/D10: specific surface area 800 m.sup.2/g 3 μm Spherical silica — — — — — 10 — particles, D90/D10: specific surface area 40 mm.sup.2/g Polymethylhydrosiloxane 22 22 22 22 22 22 27 treated Talc Polymethylhydrosiloxane 33 33 33 33 33 33 38 treated Mica Polymethylhydrosiloxane 11.5 11.5 11.5 11.5 11.5 11.5 11.5 treated Titanium Dioxide Polymethylhydrosiloxane 3 3 3 3 3 3 3 treated Zinc Oxide Boron Nitride Powder 4 4 4 4 4 4 4 Microsphere-M-305 1 1 1 1 1 1 1 (Polymethylmethacrylate Particles) (Matsumoto Yushi-Seiyaku Co. Ltd) Magnesium Stearate 2 2 2 2 2 2 2 B Polymethylhydrosiloxane 2.2 2.2 2.2 2.2 2.2 2.2 2.2 treated Iron Oxides (CI 77492) Polymethylhydrosiloxane 0.54 0.54 0.54 0.54 0.54 0.54 0.54 treated Iron Oxides (CI 77491) Polymethylhydrosiloxane 0.36 0.36 0.36 0.36 0.36 0.36 0.36 treated Iron Oxides (CI 77499) C Polydimethylsiloxane 2 2 2 2 2 2 2 trimethylsiloxysilicate (Momentive SS4267) Pentylene Glycol 2 2 2 2 2 2 2 Silsoft B 3820 1 1 1 1 1 1 1 (Momentive) (Isododecane, Dimethicone) Caprylic/Capric 1.6 1.6 1.6 1.6 1.6 1.6 1.6 Triglyceride Sorbitan Sesquiisostearate 0.5 0.5 0.5 0.5 0.5 0.5 0.5 Diisostearyl Malate 0.5 0.5 0.5 0.5 0.5 0.5 0.5 Ethylhexyl 2 2 2 2 2 2 2 Methoxycinnamate Tocopheryl Acetate 0.5 0.5 0.5 0.5 0.5 0.5 0.5 Phenoxylethanol 0.3 0.3 0.3 0.3 0.3 0.3 0.3

[0086] The evaluation results of “Spreadability”, “Skin Smoothness”, “Skin Compatibility”, “Soft Focus effect”, and “longlasting makeup wearing after 12 hours” are also shown in Table 2 together with the composition. The evaluation was made by 10 panelists who scored each item according to the following criteria and evaluated by the average value.

[0087] “Very good”:5 points; “Good”:4 points; “Normal”:3 points; “Slightly defective”:2 points; and “Bad”:1 point.

TABLE-US-00002 TABLE 2 Evaluation Results Example Comparative Example 1 2 3 1 2 3 4 Evaluation Spreadability during 4.6 4.2 4.8 4.8 3.7 3.6 4.6 Results application Smoothness during 4.7 4.8 4.8 4.4 3.8 4.2 4.2 application Compatiblity to skin 4.7 4.7 4.5 3.9 4.2 4.1 3.9 Soft focus effect 4.5 4.8 4.1 3.8 4.2 4.6 4.3 Skin moisturized feel 4.5 4.5 4.6 3.9 2.7 4.3 3.8 Makeup lasting after 4.5 4.7 4.2 3.0 2.7 4.2 3.5 12 hours

Example 6: Powder Formulations

[0088] Powder formulations were prepared with the composition shown below in Table 3 using the above silica fine particles of Example 1 (A) and comparative spherical silica (Sunsphere NP-30, Asahi Glass SI-Tech. Co. Ltd.) with 4 micron mean particle size and with D90/D1=2.7. The ingredients were mixed in a 100 gm speedmixer container and the powders were mixed for 5 minutes to obtain a uniformly mixed loose powder formulation.

[0089] The friction coefficient of the powder formulation were measured with CSM Tribometer. The powder was rubbed on leather (2 mg/cm.sup.2) for 10 s. The friction was measured with 1 cm stainless steel diameter probe with leather (Testfabrics Inc.) attached to the flat surface. The friction was measured at 1 cm/s speed for probe reciprocating 2 cm back in forth for 10 cycles. The friction coefficient was reported as average friction coefficient for 10 cycles.

TABLE-US-00003 TABLE 3 Powder Formulations International Nomenclature Cosmetic Ingredient Example Comp. Ingredient (INCI) 5.1 Ex. 5.2 Talc U-11S2 Talc (and) Triethoxycaprylylsilane 23.4 23.4 GMS-11S2 Mica (and) Triethoxycaprylylsilane 35.1 35.1 JTTO-MS7 (Kobo) Titanium Dioxide (and) Alumina (and) Methicone 12.2 12.2 Zano Plus Zinc Oxide (and) Triethoxycaprylylsilane 3.2 3.2 Softouch Boron Nitride 4.3 4.3 CC60586058 BYO-12 CI 77492 (and) Isopropyl Titanium Triisostearate 2.3 2.3 BRO-12 CI 77491 (and) Isopropyl Titanium Triisostearate 0.6 0.6 BBO-12 CI 77499 (and) Isopropyl Titanium Triisostearate 0.4 0.4 SS4267 Dimethicone (and) Trimethylsiloxysilicate 2.1 2.1 CCTG Caprylic/Capric Triglyceride 2.8 2.8 Cosmol 182 V Sorbitan Sesquiisostearate 0.5 0.5 Cosmol 222 Diisostearyl Malate 0.5 0.5 Phenoxyethanol Phenoxyethanol 0.3 0.3 OMC Ethylhexyl Methoxy cinnamate 2.1 2.1 Example 1 (A) D50 = 3.8 micron, D50/D10 = 1.11 10.0 — Comparable silica D50 = 4 micron, D50/D10 = 2.7 — 10.0

[0090] FIG. 1 shows the powder formulation with silica with narrow particle size distribution (D90/D10=1.1) showed lower friction coefficient than the formulation with higher particle size distribution (D90/D10=2.7). FIG. 3A and FIG. 3B shows the particle size distribution of spherical particles of Example 1 (D90/D10=1.1, D50=3.9 μm) and comparative silica (D90/D10=2.70, D50=4.3 μm).

Example 7: Emulsified Foundation

[0091] Using the above silica fine particles (A), an emulsified foundation having the composition shown below was prepared. The preparation method was as follows: First, ingredients (5) to (8) were mixed with a Henschel mixer, then ingredients (1) and (3) to (4) were added thereto, and the mixture was thoroughly mixed, and then pulverized and classified. Further, ingredients (2) and (9) to (18) were added, treated with a homomixer, deaerated, and filled in a container.

TABLE-US-00004 TABLE 4 Emulsified Foundation Formulation Amount Ingredient (wt. %) 1 Silica fine particles (A) 10.0 2 Dimethyl silicone (viscosity 10 mPa .Math. s) 7.0 3 Titanium oxide 5.0 4 Anhydrous silicic acid 3.0 5 Talc 8.0 6 Bengala 1.0 7 Black iron oxide 0.5 8 Yellow iron oxide 1.0 9 Octamethylcyclotetrasiloxane 10.0 10 Rosin pentaerislit ester 2.0 11 Neopentyl glycol diisooctanoate 4.0 12 Squalene 2.5 13 Glycerin triisooctanoate 2.0 14 Purified water 35.0 15 1,3-butylene glycol 4.0 16 Ethanol 8.0 17 Preservatives 0.1 18 Fragrance Balance

Example 8: Powder Foundation

[0092] Using the above silica fine particles (A), a dual-purpose powder foundation having the composition shown below was prepared. In the preparation method, first, ingredients (1) and (3) to (10) were mixed and pulverized, transferred to a Henschel mixer, and then ingredients (2) and (11) to (16) were added and mixed uniformly. Then the mixture was compression molded into a metal plate.

TABLE-US-00005 TABLE 5 Powder Foundation Formulation Amount Ingredient (wt. %) 1 Silica fine particles (A) 15.0 2 Dimethyl silicone (viscosity 10 mPa .Math. s) 5.0 3 Mica 5.0 4 Talc 5.0 5 Titanium oxide 15.0 6 Mica Titanium 3.5 7 Iron oxide (red, yellow, black) 7.0 8 Zinc oxide 4.0 9 Aluminum oxide 10.0 10 Barium sulfate 5.0 11 Lanolin 5.0 12 Vaseline 1.5 13 Liquid paraffin 1.0 14 Isopropyl millistate 1.5 15 Preservatives Balance 16 Fragrance Balance

Example 9: Powder Eyeshadow

[0093] Using the above silicone particles (A), a powder eyeshadow with the composition shown below was prepared. The preparation method was as follows: First, ingredients (1) and (3) to (10) were mixed and crushed, transferred to a Henschel mixer, then ingredients (2) and (11) were added and mixed uniformly, then the mixture was compression molded into a metal plate.

TABLE-US-00006 TABLE 6 Powder Eyeshadow Formulation Amount Ingredient (wt. %) 1 Silica fine particles (A) 20.0 2 Dimethyl silicone (viscosity 10 mPa .Math. s) 5.0 3 Mica Balance 4 Talc 15.0 5 Mica Titanium 8.0 6 Zinc stearate 4.0 7 Zinc laurate 4.0 8 Yellow iron oxide 0.7 9 Black iron oxide 0.7 10 Red iron oxide 0.7 11 Liquid paraffin 8.0 12 Preservatives and fragrances Balance

Example 10: Two-Layer Separation Type Sunscreen

[0094] Using the above silicone particles (A), a two-layer separation type sunscreen emulsion having the composition shown below was prepared. In the preparation method, ingredients (1) to (7) were first dispersed and mixed with a disper, and then the aqueous phase ingredients (8) to (11) were added and stirred to emulsify.

TABLE-US-00007 TABLE 7 Two-Layer Sunscreen Formulation Amount Ingredient (wt. %) 1 Silica fine particles (A) 10.0 2 Dimethyl silicone (viscosity 10 mPa .Math. s) 5.0 3 Decamethylcyclopentasiloxane 20.0 4 Polyethter-modified silicone 1.0 5 Squalene 8.0 6 Hydrophobicized titanium oxide 5.0 7 Octyl methoxycinnamic acid 2.0 8 Glycerin 2.0 9 Sodium Chloride 0.4 10 Polysorbate 20 0.9 11 Ethanol 12.0 12 Fragrance Balance 13 Purified water Balance

Example 11: Sunscreen Cream

[0095] Using the above silicone particles (A), a sunscreen cream having the composition shown below was prepared. In the preparation method, ingredients (1) to (8) were first dispersed and mixed with a disper, and then the aqueous phases ingredients (8) to (10) were added and stirred to emulsify.

TABLE-US-00008 TABLE 8 Sunscreen Cream Formulation Amount Ingredient (wt. %) 1 Silica fine particles (A) 10.0 2 Dimethyl silicone (viscosity 10 mPa .Math. s) 7.0 3 Hydrophobic titanium dioxide 10.0 4 Hydrophobic zinc oxide 10.0 5 Squalene 15.0 6 Glycerin diisostearate 3.0 7 Preservatives 0.1 8 Fragrance 0.1 9 Purified water Balance 10 1,3-butylene glycol 5.0

Example 12: Solid White Powder

[0096] Using the above silicone particles (A), a solid white powder having the composition shown below was prepared. Preparation method is as below. First, the ingredients (1) and (3) to (6) were mixed and crushed, transferred to a Henschel mixer, then ingredients (2) and (7) to (10) were added, mixed uniformly, and compression-molded onto a metal plate.

TABLE-US-00009 TABLE 9 Solid White Powder Formulation Amount Ingredient (wt. %) 1 Silica fine particles (A) 20.0 2 Dimethyl silicone (viscosity 10 mPa .Math. s) 7.0 3 Mica Balance Balance 4 Talc 15.0 5 Titanium oxide 1.0 6 Yellow iron oxide 1.0 7 Liquid paraffin 10.0 8 Beeswax 3.0 9 Preservatives Balance 10 Fragrance Balance

Example 13: Blusher

[0097] Using the above silica fine particles (A), a blusher having the composition shown below was prepared. The preparation method was as follows: First, the ingredients (1) to (6) were mixed and crushed, transferred to a Henschel mixer, then the ingredients (7) to (10) were added, mixed uniformly, and compression molded into a metal plate.

TABLE-US-00010 TABLE 10 Blusher Formulation Amount Ingredient (wt. %) 1 Silica fine particles (A) 5.0 2 Mica 10.0 3 Titanium oxide 10.0 4 Red iron oxide 1.5 5 Black iron oxide 1.5 6 Yellow iron oxide 1.5 7 Squalene 7.0 8 Dimethyl silicone (viscosity 5 mPa s) 7.0 9 Preservatives 0.1 10 Fragrance Balance

Example 14: Lipstick

[0098] Using the above silica fine particles (A), a lipstick having the composition shown below was prepared. The preparation method was as follows: ingredients (1)-(11) were heated and melted, then (12) and (13) were added and mixed, the mixture was degassed and poured into a container, rapidly cooled and hardened.

TABLE-US-00011 TABLE 11 Lipstick Formulation Amount Ingredient (wt. %) 1 Silica fine particles (A) 6.0 2 Dimethyl silicone (viscosity 10 mPa .Math. s) 10.0 3 Paraffin wax 11.0 4 Lanolin wax 12.0 5 Candelilla wax 5.0 6 Beeswax 5.0 7 Castor oil Balance 8 Glycerin trioctanoate 2.0 9 Titanium oxide 1.0 10 Red No. 201 3.0 11 Blue No. 1 aluminum lake 0.5 12 Preservatives Balance 13 Fragrance Balance

Example 15: Skin Primer

[0099] Using the above silica fine particles (A), a skin primer having the composition shown below was prepared. The preparation method was as follows: Ingredients (1) to (7) were heated and mixed, ingredients (8) to (13) were separately mixed well, then added to ingredients (1) to (7) and mixed well, finally the aqueous phases ingredients (14) to (18) were added and stirred to emulsify.

TABLE-US-00012 TABLE 12 Skin Primer Formulation Amount Ingredients (wt. %) 1 Dimethicone 10.5 2 Ethylhexyl Methoxycinnamate 5 3 Silica fine particles (A) 5 4 Cylcopentasiloxane (and) Polymethylsilses- 4 quioxane 5 Dimethicone, Cetearyl Dimethicone Cross- 4 polymer 6 Sorbitan Sesquiisostearate 0.5 7 (Caprylic/Capric) Triglyceride (and) PEG/PPG- 4 20/15 Dimethicone 8 Dimethicone 3 9 Hydrogen Dimethicone (and) Zinc Oxide 1.5 10 Hydrogen Dimethicone (and) Titanium Dioxide 1.5 (and) Aluminum Hydroxide 11 Methicone (and) Iron Oxide (CI 77492) 0.05 12 Methicone (and) Iron Oxide (CI 77491) 0.05 13 Methicone (and) Iron Oxide (CI 77499) 0.015 14 water Balance 15 Glycerin 5 16 Polysorbate 20 0.5 17 Sodium Chloride 1 18 Phenoxy ethanol Balance

Example 16: BB Cream

[0100] Using the above silica fine particles (A), a BB cream having the composition shown below was prepared. The preparation method was as follows: Ingredients (1) to (9) were mixed until uniform, ingredients (10) to (15) were separately mixed well, then added to ingredients (1) to (9) and mixed well, then the aqueous phases ingredients (16) to (21) were added and mixed well, finally add (22) and homogenize to uniform.

TABLE-US-00013 TABLE 13 BB Cream Formulation Amount Ingredients (wt. %) 1 Caprylyl Methicone (and) C30-45 Alkyl Cetearyl 4 Dimethicone Crosspolymer 2 Dimethicone 15 3 Silica fine particles (A) 5 4 Trifluoropropyldimethylsiloxy/Trimethylsiloxy 2 Silsesquioxane (and) Dimethicone 5 (Caprylic/Capric) Triglyceride (and) PEG/PPG- 7 20/15 Dimethicone 6 Bisphenylpropyl Dimethicone 2 7 Boron Nitride 3 8 Phenoxyethanol (and) Ethylhexylglycerin 1 9 Fragrance Balance 10 Caprylyl Methicone 5 11 Titanium Dioxide (and) Triethoxycaprylylsilane 2 12 Iron Oxide (and) Triethoxycaprylylsilane 0.5 13 Iron Oxide (and) Triethoxycaprylylsilane 0.2 14 Iron Oxide (and) Triethoxycaprylylsilane 0.05 15 Titanium Dioxide (and) Alumina (and) Methicone 7 16 Water Balance 17 Trisodium EDTA 0.2 18 Butylene Glycol 3 19 Glycerin 5 20 Sodium Chloride 1 21 Hydroxyphenyl Propamidobenzoic Acid 1 22 Disteardimonium Hectorite 0.7

Example 17: CC Cream

[0101] Using the above silica fine particles (A), a CC cream having the composition shown below was prepared. The preparation method was as follows: Ingredients (5) to (14) were mixed until uniform, ingredients (15) to (17) were separately mixed well, then added to ingredients (5) to (14) and mixed well, then the aqueous phases ingredients (1) to (4) were added and mixed well, finally add (18) to (20) and mix to uniform.

TABLE-US-00014 TABLE 14 CC Cream Formulation Amount Ingredients (Wt. %) 1 Water Balance 2 Glycerin 5 3 Sodium Chloride 1 4 Propylene Glycol 8 5 PEG-9 Dimethicone 1 6 Caprylic/Capric Triglyceride (and) PEG/PPG-20/15 3 Dimethicone 7 Caprylyl Methicone 12 8 Diphenyl Dimethicone 5 9 Boron Nitride 1 10 Silica fine particles (A) 5 11 Polymethylsilsesquioxane 1 12 Octyl MethoxyCinnamate 4 13 Titanium Dioxide (and) Methylhydrogenpolysiloxane 5 14 Disteardimonium Hectorite 0.5 15 Yellow Iron Oxide (and) Methylhydrogenpolysiloxane 0.25 16 Red Iron Oxide (and) Methylhydrogenpolysiloxane 0.15 17 Black Iron Oxide (and) Methylhydrogenpolysiloxane 0.08 18 Dimethicone/Vinyl Dimethicone Crosspolymer (and) 5 Dimethicone (and) Isohexadecane (and) Cetearyl Methicone 19 Fragrance Balance 20 Phenoxyethanol (and) Chlorphenesin (and) Glycerin Balance

Example 18: Mascara

[0102] Using the above silica fine particles (A), a Mascara having the composition shown below was prepared. The preparation method was as follows: Ingredients (3) and (4) were mixed in water then heat to uniform, add ingredients (2) and (5) to (9) and mixed well, heat ingredients (10) to (15) separately, then added to the mixture and mixed well, then cool to 45° C., add ingredients (16) and (17) one by one, and mix to uniform.

TABLE-US-00015 TABLE 15 Mascara Formulation Amount Ingredients (wt. %) 1 Water Balance 2 Silica fine particles (A) 5 3 Polyvinylpyrrolidone 2 4 Hydroxyethylcellulose 1 5 Triethanolamine 1 6 Methylparaben 0.3 7 Disodium EDTA 0.1 8 Black Iron Oxide 10 9 Dimethicone PEG-8 Polyacrylate 7.2 10 Stearic Acid 4.5 11 Glyceryl Monostearate 2 12 White Bleached Beeswax 7 13 Carnauba Wax 4.5 14 Hydroxylated Lanolin 1 15 Propylparaben Balance 16 Acrylates Copolymer 20 17 DMDM Hydantoin Balance

Example 19: Concealer

[0103] Using the above silica fine particles (A), a Concealer having the composition shown below was prepared. The preparation method was as follows: Ingredients (1) and (7) were mixed until uniform and heat to 90° C., add ingredients (8) to (10) and mixed until uniform, pour the mixture into suitable container.

TABLE-US-00016 TABLE 16 Concealer Formulation Ingredients Amount (Wt. %) 1 Boron Nitride 10 2 Silica fine particles (A) 5 3 Dimethicone Balance 4 Titanium Dioxide (and) 4 Triethoxycaprylylsilane 5 Iron Oxide (and) 0.9 Triethoxycaprylylsilane 6 Iron Oxide (and) 0.3 Triethoxycaprylylsilane 7 Iron Oxide (and) 0.1 Triethoxycaprylylsilane 8 Ozokerite Wax 5 9 Polyethylene 5 10 Synthetic Wax (and) 2 Microcrystalline Wax

Example 20: O/W Cream

[0104] Using the above silica fine particles (A), an O/W Cream having the composition shown below was prepared. The preparation method was as follows: Ingredients (1) to (3) were mixed and heated to 80° C., ingredients (4) to (6) were mixed separately and added to ingredients (1) to (3), mixed until uniform, cool to room temperature, and add ingredients (7) and (8) and mix until uniform.

TABLE-US-00017 TABLE 17 O/W Cream Formulation Amount Ingredients (Wt. %) 1 Water Balance 2 Silica fine particles (A) 9.5 3 Titanium Dioxide, Silica, Aluminum Hydroxide 0.5 4 Polysilicone-34 (and) Isononyl Isononanoate (and) 3 Water 5 Dimethicone 8 6 Butyrospermum Parkii (Shea) Butter 2 7 Phenoxyethanol Balance 8 Sodium Hyaluronate 0.1

Example 21: W/O Cream

[0105] Using the above silica fine particles (A), a WIG Cream having the composition shown below was prepared. The preparation method was as follows: Ingredients (1) to (6) were mixed and heated to 70° C., ingredients (7) to (9) were mixed separately and added to ingredients (1) to (6), mixed to emulsify, and cool to room temperature.

TABLE-US-00018 TABLE 18 W/O Cream Formulation Amount Ingredients (Wt. %) 1 Dimethicone 1 2 Capylyl Methicone 10 3 Silica fine particles (A) 9 4 Hydrogen Dimethicone (and) Titanium Dioxide 1 (and) Aluminum Hydroxide 5 (Caprylyl/Capryl) Triglyceride 3 (and) PEG/PPG-20/15 Dimethicone 6 Phenoxy ethanol Balance 7 water Balance 8 Glycerin 8 9 Sodium Chloride 1

Example 22: Eye Cream

[0106] Using the above silica fine particles (A), an Eye Cream having the composition shown below was prepared. The preparation method was as follows: Ingredients (1) to (4) were mixed and heated to 70° C., ingredients (5) to (12) were mixed separately and heated to 70° C., then added to ingredients (1) to (4), mixed to emulsify, then cool to 50° C., add ingredient (13) and mix until uniform.

TABLE-US-00019 TABLE 19 Eye Cream Formulation Amount Ingredients (Wt. %) 1 Water Balance 2 Silica fine particles (A) 5 3 Glycerin 3 4 Di sodium EDTA 0.05 5 Glyceryl stearate citrate (and) Polyglyceryl-3 stearate 4 (and) Hydrogenated lecithin 6 Sodium acrylates copolymer (and) Lecithin 1 7 Cetyl Alcohol 1.5 8 Butyrospermum Parkii (Shea Butter) 4 9 Decyl Isostearate (and) Isostearyl Isostearate 3 10 Argania Spinosa Kernel Oil 2 11 Dimethicone 3 12 Caprylyl Methicone 3 13 Dimethicone/Vinyl Dimethicone Crosspolymer 3 (and) Dimethicone(and) Isohexadecane (and) Cetearyl Methicone

Example 23: Skin Serum

[0107] Using the above surface treated silica fine particles (D), an Skin Serum having the composition shown below was prepared. The preparation method was as follows: Ingredients (1) to (4) were mixed until uniform, ingredients (5) to (7) were mixed separately and added to ingredients (1) to (4), mixed until uniform, then add ingredients from (8) to (11) one by one, and mix until uniform.

TABLE-US-00020 TABLE 20 Skin Serum Formulation Amount Ingredients (Wt. %) 1 Water Balance 2 Silica fine particles (D) 1 3 Alpha-Glucan Oligosaccharide 0.5 4 Hydrolyzed Sodium Hyaluronate 0.01 5 BG 1 6 Pentylene Glycol 3 7 Dipropylene Glycol (and)Polysilicone-29 1 8 Malus Domestica Fruit Cell Culture Extract 0.1 9 Ascorbyl Tetraisopalmitate 0.1 10 Phenoxyethanol Balance 11 Fragrance Balance

Example 24: Shampoo

[0108] Using the above silica fine particles (A), a shampoo having the composition shown below was prepared. The preparation method was as follows: Add ingredients (3) to water, mix uniform and heat to 80° C., after the mixture is clear, add ingredients (2) and (5) to (10) to the mixture one by one and confirm the mixture is clear, cool to the room temperature, and add ingredients (11) to (15) one by one and mixed until uniform.

TABLE-US-00021 TABLE 21 Shampoo Formulation Amount Ingredients (Wt. %) 1 Water Balance 2 Dipropylene Glycol 3 3 Polyquaternium 10 0.4 5 Silica fine particles (A) 5 6 Disodium EDTA 0.05 7 Sodium Benzoate 0.5 8 Sodium Laureth Sulfate 17 9 Cocamidopropyl Betaine 10 10 Cocamide MEA 2 11 Phenoxyethanol Balance 12 Water, Glycol Distearate, Glycerin, 5 Laureth-4, Cocamidopropyl Betain 13 Citric acid 0.1 14 Dimethiconol, Water, Sodium Lauryl 2 Sulfate, Sodium Laureth Sulfate 15 Fragrance Balance

[0109] It is to be appreciated that the Detailed Description section, and not the Summary and Abstract sections, is intended to be used to interpret the claims. The Summary and Abstract sections can set forth one or more but not all exemplary embodiments of the present disclosure as contemplated by the inventor(s), and thus, are not intended to limit the present disclosure and the appended claims in any way.

[0110] The present disclosure has been described above with the aid of functional building blocks illustrating the implementation of specified functions and relationships thereof. The boundaries of these functional building blocks have been arbitrarily defined herein for the convenience of the description. Alternate boundaries can be defined so long as the specified functions and relationships thereof are appropriately performed.

[0111] The foregoing description of the specific embodiments will so fully reveal the general nature of the disclosure that others can, by applying knowledge within the skill of the art, readily modify and/or adapt for various applications such specific embodiments, without undue experimentation, without departing from the general concept of the present disclosure. Therefore, such adaptations and modifications are intended to be within the meaning and range of equivalents of the disclosed embodiments, based on the teaching and guidance presented herein. It is to be understood that the phraseology or terminology herein is for the purpose of description and not of limitation, such that the terminology or phraseology of the present specification is to be interpreted by the skilled artisan in light of the teachings and guidance.

[0112] The breadth and scope of the present disclosure should not be limited by any of the above-described exemplary embodiments, but should be defined only in accordance with the following claims and their equivalents.

Other Aspects

[0113] All publications, patents, and patent applications mentioned in this specification are incorporated herein by reference in their entirety to the same extent as if each individual publication, patent, or patent application was specifically and individually indicated to be incorporated by reference in its entirety. Where a term in the present application is found to be defined differently in a document incorporated herein by reference, the definition provided herein is to serve as the definition for the term.

[0114] While the present disclosure has been described in connection with specific aspects thereof, it will be understood that present disclosure is capable of further modifications and this application is intended to cover any variations, uses, or adaptations of the invention following, in general, the principles of the invention and including such departures from the present disclosure that come within known or customary practice within the art to which the invention pertains and can be applied to the essential features hereinbefore set forth, and follows in the scope of the claimed.