Powder coating composition and coated article

Abstract

A powder coating composition comprising a specific organosilicon compound forms a coating which exhibits satisfactory water-loading resistant performance.

Claims

1. A powder coating composition comprising (A) an organosilicon compound having the general formula (1): ##STR00008## wherein R.sup.1 is each independently a C.sub.1-C.sub.10 alkyl or C.sub.6-C.sub.10 aryl group, R.sup.2 is each independently a C.sub.1-C.sub.10 alkyl or C.sub.6-C.sub.10 aryl group, A is a C.sub.1-C.sub.20 divalent hydrocarbon group, B is a C.sub.1-C.sub.20 divalent hydrocarbon group, and m is an integer of 1 to 3, and (B) a resin selected from the group consisting of epoxy resins, polyester resins, epoxy-polyester resins, acrylic resins, fluoro-resins, and silicone resins, wherein the organosilicon compound is contained in an amount of 0.1 to 5 parts by weight, provided that the powder coating composition is 100 parts by weight.

2. The powder coating composition of claim 1 wherein the organosilicon compound has the general formula (2): ##STR00009## wherein R.sup.1, R.sup.2, and m are as defined above.

3. The powder coating composition of claim 1, wherein resin component (B) comprises a carboxyl-containing polyester resin.

4. The powder coating composition of claim 1, further comprising (C) a -hydroxyalkylamide compound.

5. A coated article obtained by coating a substrate with the powder coating composition of claim 1.

Description

DESCRIPTION OF PREFERRED EMBODIMENTS

(1) As used herein, the notation (Cn-Cm) means a group containing from n to m carbon atoms per group. The term silane coupling agent is encompassed in the term organosilicon compound. In the chemical formulae, Me stands for methyl, and Et for ethyl.

(2) The powder coating composition of the invention is defined as comprising (A) an organosilicon compound having the general formula (1).

(3) ##STR00003##
Herein R.sup.1 is each independently a C.sub.1-C.sub.10 alkyl or C.sub.6-C.sub.10 aryl group, R.sup.2 is each independently a C.sub.1-C.sub.10 alkyl or C.sub.6-C.sub.10 aryl group, A is a C.sub.1-C.sub.20 divalent hydrocarbon group, B is a C.sub.1-C.sub.20 divalent hydrocarbon group, and m is an integer of 1 to 3.

(4) Suitable alkyl and aryl groups represented by R.sup.1 include methyl, ethyl, propyl, butyl, and phenyl. Inter alia, methyl and ethyl are preferred.

(5) Suitable alkyl and aryl groups represented by R.sup.2 include methyl, ethyl, propyl, butyl, and phenyl. Inter alia, methyl and ethyl are preferred.

(6) Suitable divalent hydrocarbon groups represented by A are alkylene groups including methylene, ethylene, propylene, butylene, pentylene, hexylene, octylene, and decylene, with hexylene being preferred.

(7) Suitable divalent hydrocarbon groups represented by B are alkylene groups including methylene, ethylene, propylene, butylene, pentylene, hexylene, octylene, and decylene, with propylene being preferred.

(8) The preferred organosilicon compound has the general formula (2).

(9) ##STR00004##
Herein R.sup.1, R.sup.2, and m are as defined above.

(10) More preferred are organosilicon compounds having the formulae (3) and (4).

(11) ##STR00005##

(12) Since the organosilicon compounds mentioned above are solid at normal temperature, they may be added to powder coating compositions. Specifically, the organosilicon compound of formula (3) has a melting point of 120 C., and the organosilicon compound of formula (4) has a melting point of 115 C. By adding the organosilicon compound to a powder coating composition, the composition is improved in adhesion to substrates.

(13) An appropriate amount of the organosilicon compound (A) added is 0.01 to 20 parts, more preferably 0.1 to 5 parts by weight, provided that the powder coating composition is 100 parts by weight. With less than 0.01 pbw of the organosilicon compound, water-loading resistant performance may be no longer improved. In excess of 20 pbw, the performance improvement may be saturated.

(14) The powder coating composition is based on a resin, which may be selected from those resins commonly used in prior art powder coating compositions. Suitable resins include epoxy resins, polyester resins, epoxy-polyester resins, acrylic resins, fluoro-resins and silicone resins. Inter alia, (B) a carboxyl-containing resin is preferred. Included are carboxyl-containing polyester resins, carboxyl-containing acrylic resins, carboxyl-containing fluoro-resins, and carboxyl-containing silicone resins. Inter alia, carboxyl-containing polyester resins are especially preferred for processability and cost.

(15) Suitable carboxyl-containing polyester resins include those resins obtained from reaction of an aromatic or alicyclic dicarboxylic acid such as phthalic acid (anhydride), isophthalic acid, terephthalic acid, dimethyl isophthalate, dimethyl terephthalate, hexahydrophthalic acid (anhydride) or tetrahydrophthalic acid (anhydride) with a dihydric alcohol such as (poly)ethylene glycol, (poly)propylene glycol, butylene glycol, neopentyl glycol, 1,6-hexanediol, or dimethylolpropionic acid, and optionally, further with a monocarboxylic acid such as benzoic acid, a tri- or polyfunctional carboxylic acid such as trimellitic acid (anhydride), or a tri- or polyhydric alcohol such as trimethylol ethane, trimethylol propane, glycerol or pentaerythritol, such that the acid residue may be left behind.

(16) An appropriate amount of the resin, especially carboxyl-containing polyester resin (B) used is 7 to 99 parts, more preferably 15 to 95 parts by weight, provided that the powder coating composition is 100 parts by weight. A composition with less than 7 pbw of the resin may be poor in impact resistance and cupping resistance whereas a composition with more than 99 pbw of the resin may be less curable.

(17) In a preferred embodiment, (C) a hydroxylalkylamide compound as curing agent is added to the powder coating composition. Among others, hydroxylalkylamide compounds having at least two functional groups per molecule are especially preferred when low-temperature curing behavior and properties of a cured coating are taken into account. Exemplary compounds are N,N,N,N-tetrakis(2-hydroxyethyl)adipamide and N,N,N,N-tetrakis(2-hydroxypropyl)adipamide.

(18) An appropriate amount of the hydroxylalkylamide compound (C) used is 0.5 to 45 parts, more preferably 1 to 25 parts by weight, provided that the powder coating composition is 100 parts by weight. A composition with less than 0.5 pbw of compound (C) may be less curable whereas a composition with more than 45 pbw of compound (C) may be poor in impact resistance and cupping resistance.

(19) To the powder coating composition, any additives such as fillers, coloring pigments, glitters, flow modifiers, aesthetic microparticulate polymers, surface modifiers, cure accelerators, and lubricants may be added, if desired.

(20) On use of the powder coating composition, it may be applied to a substrate by an electrostatic powder coating technique using an electrostatic powder sprayer or triboelectric coater, typically to a thickness of 200 to 300 m, more preferably 30 to 150 m. The coating is baked typically at a (substrate) temperature of 140 to 230 C. for 2 to 60 minutes.

(21) The powder coating composition may be applied to any substrates commonly used in the art. Examples of the substrate include metal substrates of steel, zinc, aluminum, copper and tin, surface-treated metal substrates, and metal substrates having an undercoat such as primer or intermediate coat. The composition finds applications in a variety of fields including vehicles, electric appliances, building parts, road-related parts, and business machines.

EXAMPLE

(22) Examples of the invention are given below by way of illustration and not by way of limitation. All parts are by weight (pbw).

(23) Synthesis of Organosilicon Compounds

(24) Organosilicon Compound #1

(25) A 1-L separable flask equipped with a stirrer, reflux condenser, dropping funnel and thermometer was charged with 91.3 g of a nurate-modified hexamethylene diisocyanate (Duranate TPA-100 by Asahi Chemical Industry Co., Ltd.) and 200 g of toluene, to which 89.7 g (0.5 mol) of 3-aminopropyltrimethoxysilane (KBM-903 by Shin-Etsu Chemical Co., Ltd.) was added dropwise at an internal temperature of 100-110 C. over 10 minutes. Stirring was continued at 110 C. for 1 hour. Subsequent stripping yielded an organosilicon compound having a melting point of 120 C. On analysis by .sup.1H-NMR spectroscopy, the reaction product was identified to be a compound having the structure of the following formula (3). This is designated Organosilicon compound #1.

(26) ##STR00006##
Organosilicon Compound #2

(27) A 1-L separable flask equipped with a stirrer, reflux condenser, dropping funnel and thermometer was charged with 91.3 g of a nurate-modified hexamethylene diisocyanate (Duranate TPA-100 by Asahi Chemical Industry Co., Ltd.) and 200 g of toluene, to which 110.7 g (0.5 mol) of 3-aminopropyltriethoxysilane (KBE-903 by Shin-Etsu Chemical Co., Ltd.) was added dropwise at an internal temperature of 100-110 C. over 10 minutes. Stirring was continued at 110 C. for 1 hour. Subsequent stripping yielded an organosilicon compound having a melting point of 115 C. On analysis by .sup.1H-NMR spectroscopy, the reaction product was identified to be a compound having the structure of the following formula (4). This is designated Organosilicon compound #2.

(28) ##STR00007##

Examples 1 to 8 and Comparative Examples 1 to 2

(29) A powder coating composition of the formulation (pbw) shown in Table 1 was admitted into a mixer (trade name High-Speed Mixer by Fukae Industry Co., Ltd., volume 2 L), where the contents were uniformly mixed for 1 minutes by rotating the agitator at 500 rpm and the chopper at 4,000 rpm. The mixture was melt kneaded on an extruder/kneader (trade name Buss Ko-Kneader PR46 by Buss) at a temperature of 80-120 C. The mass was cooled, finely ground on a hammer mill and sieved through a 200-mesh screen, obtaining a powder (coating composition) having an average particle size of 35 m. Polyester resin 1: M-8961 (DIC Corp., carboxyl-containing polyester resin) Polyester resin 2: M-8962 (DIC Corp., carboxyl-containing polyester resin) Curing agent: PRIMID XL-552 (EMS Griltech, -hydroxyalkylamide) Titanium oxide: JA-1 (Tayca Co., Ltd.) Leveling agent: Resiflow P-67 (Estron Chemical)

(30) Using an electrostatic coating machine (trade name PG-1, Matsuo Sangyo Co., Ltd.), the powder coating composition was coated onto a substrate (SPCC steel plate of 0.8 mm thick treated with zinc phosphate Parbond #3118 by Nihon Parkerizing Co., Ltd.) in such a coating weight as to give a cured thickness of 60 m, and baked and dried under such conditions as to keep the substrate temperature at 150 C. for 20 minutes, completing a coated plate (test sample). The test sample was examined for coating properties, with the results shown in Table 1.

(31) [Gloss (60 G)]

(32) measured according to JIS K-5600 4.7 (reflection 60 deg.)

(33) [Impact Test]

(34) According to JIS K-5400 8.3.2 Dupont impact test, an impact was applied to the coated surface and back surface of the coated plate under conditions including a drop weight of 1,000 g, an impact tip diameter of inch, and a dropping height of 50 cm. Pressure-sensitive adhesive tape (cellophane tape) was attached to the impacted area and instantly pulled back. It was examined how the coating was stripped.

(35) : no stripping of coating observed

(36) : some stripping of coating observed

(37) x: noticeable stripping of coating observed

(38) [Cross-Hatch Adhesion]

(39) measured according to JIS K-5600 5.6

(40) [Boiling Water Resistance, Outer Appearance]

(41) The test sample was immersed in boiling water for 2 hours before the coating was visually inspected for outer appearance.

(42) : gloss maintained

(43) : a lowering of gloss, matting

(44) x: a substantial loss of gloss

(45) [Boiling Water Resistance, Cross-Hatch Adhesion]

(46) The test sample was immersed in boiling water for 2 hours before it was evaluated according to JIS K-5600 5.6.

(47) [Moisture Resistance, Outer Appearance]

(48) The test sample was subjected to 500-hour continuous test according to JIS K-5400 9.2.2 before it was visually inspected.

(49) : gloss maintained

(50) : a lowering of gloss, matting

(51) x: a substantial loss of gloss

(52) [Moisture Resistance, Cross-Hatch Adhesion]

(53) The test sample was subjected to 500-hour continuous test according to JIS K-5400 9.2.2 before it was evaluated according to JIS K-5600 5.6.

(54) [Salt Water Spraying, Cut Stripping]

(55) The test sample was cross-cut on its coated surface and subjected to 500-hour salt water spraying according to JIS K-5400 9.2. Adhesive tape was attached to the cut area and pulled back. Stripping distance is the maximum of width of a stripped portion of coating from the center line between cut lines.

(56) TABLE-US-00001 TABLE 1 Comparative Formulation Example Example (pbw) 1 2 3 4 5 6 7 8 1 2 Polyester resin 1 65 65 65 65 65 Polyester resin 2 65 65 65 65 65 Organosilicon 1 3 1 3 compound #1 Organosilicon 1 3 1 3 compound #2 Curing agent 5 5 5 5 5 5 5 5 5 5 Benzoin 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 Titanium oxide 30 30 30 30 30 30 30 30 30 30 Leveling agent 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 Test results Gloss (60 G) 94 95 95 95 94 95 95 94 95 94 Impact test Cross-hatch adhesion 100/100 100/100 100/100 100/100 100/100 100/100 100/100 100/100 100/100 100/100 Boiling water resistance, X X outer appearance Boiling water resistance, 100/100 100/100 100/100 100/100 100/100 100/100 100/100 100/100 50/100 50/100 cross-hatch adhesion Moisture resistance, X X outer appearance Moisture resistance, 100/100 100/100 100/100 100/100 100/100 100/100 100/100 100/100 20/100 20/100 cross-hatch adhesion Salt water spraying, 2.2 2.4 2.1 2.2 2.2 2.3 2.0 2.2 3.0 3.1 cut stripping (mm)

(57) Japanese Patent Application No. 2015-135344 is incorporated herein by reference.

(58) Although some preferred embodiments have been described, many modifications and variations may be made thereto in light of the above teachings. It is therefore to be understood that the invention may be practiced otherwise than as specifically described without departing from the scope of the appended claims.