Rolling Bearing

20240352973 ยท 2024-10-24

    Inventors

    Cpc classification

    International classification

    Abstract

    There is provided a rolling bearing capable of suppressing the occurrence of white structure spalling. A rolling bearing contains a structure having a solid solution carbon amount in a martensitic structure after heat treatment of 0.35 mass % or more and 0.65 mass % or less and a volume ratio of spheroidized carbides having a diameter of 200 nm or more of 4.5% or less.

    Claims

    1. A rolling bearing comprising: a structure of a front surface including at least a rolling contact surface, the structure containing a structure having a solid solution carbon amount in a martensitic structure after heat treatment of 0.35 mass % or more and 0.65 mass % or less and a volume ratio of spheroidized carbides having a diameter of 200 nm or more of 4.5% or less.

    2. The rolling bearing according to claim 1, wherein Si, Mn, Cr, Mo, N, Ni, V, and Cu forming solid solutions in a total proportion of 1.0 mass % or more in the martensitic structure.

    3. The rolling bearing according to claim 2, wherein the solid solution carbon amount is 0.40 mass % or more and 0.60 mass % or less, and a solid solution Cr amount is 2.40 mass % or more and 2.95 mass % or less.

    4. The rolling bearing according to claim 3, wherein the front surface including at least the rolling contact surface has hardness of 640 HV or more.

    5. The rolling bearing according to claim 1, wherein the heat treatment is any of quenching treatment, carburizing treatment, carbonitriding treatment, and induction hardening treatment.

    Description

    BRIEF DESCRIPTION OF DRAWINGS

    [0019] FIG. 1 is a graph showing the relationship between the amount of C forming a solid solution in a martensitic structure and the life ratio between each sample and a G-1 product;

    [0020] FIG. 2 is a graph showing the relationship between the total amount of Si, Mn, Cr, and Mo forming solid solutions in the martensitic structure and the life ratio between each sample and the G-1 product; and

    [0021] FIG. 3 is a graph showing the relationship between the volume ratio of spheroidized carbides and the life ratio between each sample and the G-1 product.

    DESCRIPTION OF EMBODIMENTS

    [0022] A detailed description below describes an embodiment of the present invention. The embodiment described below exemplifies devices and methods for embodying the technical idea of the present invention. The technical idea of the present invention does not specify materials, structures, arrangement, and the like of constituent components to the materials, structures, arrangement, and the like described below. The technical idea of the present invention can be variously altered within the technical range defined by Claims.

    [0023] With respect to the use of a rolling bearing in which a white structure is generated during the use of the roller beading, leading to early spalling, the present inventors have focused on the state of a structure obtained after heat treatment, particularly the amounts of elements forming solid solutions in a martensitic structure and spheroidized carbides, and have found that the generation of the white structure can be suppressed by appropriately controlling the amounts of the elements forming solid solutions in the martensitic structure and spheroidized carbides.

    <Rolling Contact Fatigue Life Test>

    [0024] Herein, prior to the present invention, the present inventors have conducted a rolling contact fatigue life test with different additive elements, such as C, Cr, Mn, forming solid solutions in a base of the rolling bearing. In this test, inner rings and outer rings for deep groove ball bearing 6206 were first produced by turning steel materials having the alloy compositions shown in Table 1. In Table 1, the unit of O is mass ppm, and the unit of elements other than O is mass %. Subsequently, the produced inner rings and outer rings were subjected to quenching treatment or induction heat treatment, followed by tempering treatment. Further, the treated inner rings and outer rings were polished to have a finished shape, and then combined with a SUJ2 -inch steel ball and a resin cage to produce test bearings. Then, the test bearings were mounted in a radial type life tester to be subjected to a rolling contact fatigue life test under the following conditions. This test was performed seven times, and the mean value of the life where the cumulative probability of failure reaches 50% (L50) was determined. [0025] Test load (radial load): 910 kgf [0026] Rotation speed: 3000 min.sup.1 [0027] Lubricating oil: Special lubricating oil likely to generate hydrogen through decomposition of lubricating oil

    TABLE-US-00001 TABLE 1 Steel maternal No. C Si Mn P S Cr Mo Cu O A 0.40 0.44 0.79 0.015 0.001 2.99 0.35 0.09 4 B 0.53 0.18 0.87 0.013 0.013 0.15 0.02 0.11 8 C 0.53 0.65 1.22 0.021 0.001 2.10 0.35 0.08 10 D 0.58 0.44 0.79 0.013 0.001 2.97 0.36 0.10 4 E 0.79 0.44 0.79 0.014 0.001 2.99 0.35 0.10 4 F 1.03 0.46 0.80 0.014 0.001 3.05 0.35 0.09 4 G 1.07 0.23 0.38 0.008 0.002 1.41 0.04 0.09 5

    [0028] Table 2 shows the amounts of C, Si, Mn, Cr, and Mo forming solid solutions in the martensitic structure after the heat treatment, the volume ratio of carbides, the hardness, the residual austenite amount .sub.R, and the rolling contact fatigue life test results. In Table 2, the unit of the solid solution C, the solid solution Si, the solid solution Mn, the solid solution Cr, and the solid solution Mo, which are the amounts of C, Si, Mn, Cr, and Mo forming solid solutions, is mass % and the unit of the residual austenite is vol %. The amounts of solid solution elements in the martensitic structure were calculated by measuring the volume ratio of spheroidized carbides and the amount of each solid solution element in the spheroidized carbides by the EDS analysis, followed by subtraction from the addition amount of each element contained in the steel. The number of the generated white structures is indicated by (Number of bearings in which the white structure was observed)/(Number of bearings subjected to the rolling contact fatigue test). The volume ratio of carbides is intended for carbides having a diameter of 200 nm or more. The alphabet of each sample No. corresponds to the alphabet of each steel material No. Q in the heat treatment column indicates quenching treatment, and IH indicates induction hardening treatment. FIGS. 1 to 3 show the results of organizing the life ratio between each sample and G-1, which is a standard heat-treated product of a SUJ2 material, in terms of the amount of C forming a solid solution in the martensitic structure, the total amount of alloy elements other than C forming a solid solution, and the volume ratio of carbides, respectively. The volume ratio can be determined from the area ratio appearing in the cross section because an object to be measured is substantially spherical, and is substantially the same value (ratio) as the area ratio.

    TABLE-US-00002 TABLE 2 between Life ratio Number of between Solid Solid Solid Solid Solid Volume generated each Sample Heat solution solution solution solution solution ratio of white sample No. treatment C Si Mn Cr Mo carbides Hardness .sub.R structures L.sub.50 life and G-1 A-1 Q950 C. 0.40 0.44 0.79 2.97 0.35 0.07% 623 HV 6 0/7 726 hr 5.0 B-1 IH 0.53 0.18 0.87 0.15 0.02 0.00% 720 HV 8 0/7 237 hr 1.6 C-1 Q840 C. 0.43 0.65 1.11 1.45 0.28 1.71% 713 HV 8 0/7 701 hr 4.9 D-1 Q880 C. 0.41 0.44 0.76 2.43 0.29 2.71% 644 HV 6 0/7 1060 hr 7.4 D-2 Q950 C. 0.57 0.44 0.79 2.95 0.35 0.10% 700 HV 13 0/7 1728 hr 12.0 E-1 Q880 C. 0.46 0.44 0.75 2.15 0.26 4.65% 712 HV 12 1/7 337 hr 2.3 E-2 Q950 C. 0.74 0.44 0.66 2.86 0.34 0.50% 716 HV 27 7/7 237 hr 1.6 F-1 Q840 C. 0.40 0.43 0.66 1.22 0.21 9.97% 714 HV 11 1/7 293 hr 2.0 G-1 Q840 C. 0.59 0.22 0.33 0.84 0.01 6.68% 720 HV 11 7/7 144 hr 1.0 G-2 Q950 C. 1.06 0.23 0.38 1.41 0.04 0.05% 688 HV 25 7/7 211 hr 1.5

    [0029] The results of investigating whether the white structure was generated focusing on the elements forming solid solutions in the martensitic structure showed that the amount of C forming a solid solution in the martensitic structure and the volume ratio of spheroidized carbides affect the generation of the white structure irrespective of the amounts of Si, Mn, Cr, and Mo forming solid solutions (Table 2). For example, in the sample E-2 in which a large amount of Cr formed a solid solution (2.86 mass %) in the martensitic structure, the white structure is generated in all of the bearings, while the white structure is not observed irrespective of the amounts of Si, Mn, Cr, and Mo in the structures having the solid solution C amount of 0.65 mass % or less and the volume ratio of spheroidized carbides of 4.5% or less as in the samples A-1, B-1, C-1, D-1, and D-2. On the other hand, it is found that, in the case of the sample B-1 in which the amounts of Si, Mn, Cr, and Mo forming solid solutions are equal to or less than those of the comparative material G-1, the life is somewhat extended, but the sample B-1 does not have the life extension effect as compared with the other samples A-1, C-1, D-1, and D-2. This is considered to be because Si, Mn, Cr, and Mo forming solid solutions in the martensitic structure affects the generation or the propagation of cracks.

    [0030] The results above show that, as the measures against the white structure spalling due to the entrance of hydrogen, it is essential that the amount of carbon forming a solid solution in the martensitic structure after the heat treatment is 0.35 mass % or more and 0.65 mass % or less and that the volume ratio of spheroidized carbides having a diameter of 200 nm or more is 4.5% or less. As the lower limit of the solid solution carbon amount, the amount of C required to achieve the minimum hardness of 650 HV required for the bearing can be determined by the method described in Materials Science and Engineering: A Vol. 273-275, No. 15, P. 40-57 (1999), Title: Martensite in steel: strength and structure) . As the amounts of the solid solution elements other than C, the total solid solution amount of at least Si, Mn, Cr, and Mo is preferably 1.0 mass % or more and more preferably 2.0 mass % or more. The life extension effect can be further obtained by forming the structure in which the amounts of the solid solution elements other than C are set in such a range. The elements in which the solid solution amounts are specified as described above as the amounts of the solid solution elements other than C may include N, Ni, V, and Cu, for example, besides Si, Mn, Cr, and Mn. Further, this investigation evaluated the bearings subjected to the quenching treatment or the induction hardening treatment, and then subjected to the tempering treatment. However, heat treatment methods other than the heat treatment methods above, e.g., carburizing treatment or carbonitriding treatment, may be acceptable.

    <Rolling Bearing>

    [0031] More specifically, the rolling bearing according to one aspect of the present invention is based on the findings above. The rolling bearing according to this embodiment has a structure of a front surface including at least a rolling contact surface, the structure containing the structure having the solid solution carbon amount in the martensitic structure after heat treatment of 0.35 mass % or more and 0.65 mass % or less and the volume ratio of spheroidized carbides having a diameter of 200 nm or more of 4.5% or less. The front surface of the rolling bearing where the solid solution carbon amount and the volume ratio of spheroidized carbides are specified is the hardened region of the rolling bearing and is set as appropriate according to uses or standards, e.g., within 1 mm from the front surface. The heat treatment methods for the rolling bearing may be any of quenching treatment, carburizing treatment, carbonitriding treatment, and induction hardening treatment.

    [0032] Herein, the prior arts as described in the cited references 1 to 7 are not clear about the amount of carbon forming a solid solution in a base structure, and do not control the solid solution carbon amount. However, this embodiment can further suppress the occurrence of the white structure spalling by controlling the solid solution carbon amount and the volume ratio of the spheroidal carbides of the rolling bearing as described above, and thus can obtain an excellent rolling contact fatigue life.

    [0033] With respect to the above-described structure of the rolling bearing, Si, Mn, Cr, Mo, N, Ni, V, and Cu as elements other iron and carbon form solid solutions in the martensitic structure in a total proportion of preferably 1.0 mass % or more and more preferably 2.0 mass % or more. It is more preferable in the above-described structure of the rolling bearing that the solid solution carbon amount is 0.40 mass % or more and 0.60 mass % or less and the solid solution Cr amount is 2.40 mass % or more and 2.95 mass % or less. It is still more preferable in the structure where the solid solution carbon amount and the solid solution Cr amount are in the ranges above that the hardness of the front surface including at least the rolling contact surface is 640 HV or more. With such a configuration, further extension of the life of the rolling bearing can be realized.

    [0034] The rolling bearing according to this embodiment is applied as bearings for automobiles, agricultural machinery, construction machinery, steel machinery, direct acting devices, and the like, for example. More specifically, the bearing is suitable for automotive electrical auxiliary equipment and wind power generation equipment, e.g., bearings for alternators, bearings for wind turbines, and the like.