Microwell device and method of manufacturing the same

Abstract

A microwell device and a method of manufacturing the same are provided. The microwell device includes a substrate and a plurality of microwells formed on the substrate. In addition, each of the microwells includes a cavity being recessed on the substrate and an opening, and the diameter of the opening is smaller than the largest inner diameter of the cavity. Furthermore, the microwells are curved.

Claims

1. A microwell device, comprising: a substrate; and a plurality of microwells formed on the substrate, each of the microwells including a cavity being recessed on the substrate and an opening, and wherein a diameter of the opening is smaller than a largest inner diameter of the cavity and the largest inner diameter of the cavity ranges from 38.7 μm to 83.6 μm; wherein the plurality of microwells are curved, and the diameter of the opening ranges from 26 μm to 56.3 μm.

2. The microwell device according to claim 1, wherein the substrate is selected from the group consisting of poly(acrylamide), polydimethylsiloxane, poly(lactic-co-glycolic acid), gelatin, silicone, polydimethylsiloxane, polyethylene, polystyrene, polyolefin, polyolefin copolymers, polycarbonate, ethylene vinyl acetate, polypropylene, polysulfone, polytetrafluoroethylene (PTFE), compatible fluoropolymer, poly(styrene-butadiene-styrene), and combinations thereof.

3. The microwell device according to claim 1, wherein a length of the substrate ranges from 10 mm to 30 mm, and a width of the substrate ranges from 10 mm to 30 mm.

4. The microwell device according to claim 1, wherein a number of the microwells is greater than or equal to 100.

5. The microwell device according to claim 1, wherein a spacing between adjacent ones of the microwells is uniform or non-uniform.

6. The microwell device according to claim 1, wherein a shape of each of the microwells is spherical or ellipsoidal.

7. The microwell device according to claim 1, wherein each of the microwells has a side surface and a bottom surface, and wherein the curvatures of the side surface and the bottom surface are not 0.

8. The microwell device according to claim 7, wherein the side surface and the bottom surface have different curvatures or the same curvature.

9. The microwell device according to claim 1, wherein the microwell device further includes a functional coating layer being coated on an inner surface of at least one of the plurality of microwells.

10. The microwell device according to claim 1, wherein the microwell device further includes a functional coating layer being coated on the surfaces of both a top surface of the substrate and an inner surface of the s.

11. The microwell device according to claim 9, wherein the microwell device further includes a lid having a functional layer on a surface of the lid, and wherein the lid is detachably covered onto the microwell device.

12. The microwell device according to claim 9, wherein the functional coating layer is selected from the group consisting of extracellular matrix proteins, glycosaminoglycan, polypeptide, proteoglycan, aminoglycan, and polysaccharide protein.

13. The microwell device according to claim 10, wherein the functional coating layer is selected from the group consisting of extracellular matrix proteins, glycosaminoglycan, polypeptide, proteoglycan, aminoglycan, and polysaccharide protein.

14. The microwell device according to claim 11, wherein the functional coating layer and the functional layer are selected from the group consisting of extracellular matrix proteins, glycosaminoglycan, polypeptide, proteoglycan, aminoglycan, and polysaccharide protein.

15. The microwell device according to claim 1, wherein the plurality of microwells are in at least two different sizes.

16. A method for manufacturing a microwell device, comprising: (a) producing a microcolumn array from a first template by photolithography or soft lithography, wherein the microcolumn array includes a plurality of microcolumns; (b) coating a lift-off layer on the microcolumn array; (c) disposing a plurality of glass microspheres on each of the plurality of the microcolumns of the microcolumn array; (d) pouring silicone onto the microcolumn array disposed with the glass microspheres, then curing the silicone, and then separating the cured silicone from the microcolumn array and the glass microspheres to form a second template having a plurality of microcavities, (e) pouring an epoxy material onto the second template, then curing the epoxy material, and then separating the cured epoxy material from the second template to form a microwell device mold; and (f) pouring a mold material onto the microwell device mold, then curing the mold material, and then separating the cured mold material from the microwell device mold to obtain the microwell device.

17. The method according to claim 16, wherein the depth of each of the microcolumns is shallower than 45 μm.

18. The method according to claim 16, wherein the lift-off layer is protein.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) The present disclosure will become more fully understood from the following detailed description and accompanying drawings.

(2) FIG. 1 is a top view of a microwell device according to a first embodiment of the present disclosure.

(3) FIG. 2 is a cross-sectional view of the microwell device according to the first embodiment of the present disclosure.

(4) FIG. 3 is another cross-sectional view of the microwell device of the present disclosure.

(5) FIG. 4 is a cross-sectional view of the microwell device M1 of the present disclosure.

(6) FIG. 5 is a cross-sectional view of the microwell device M2 of the present disclosure.

(7) FIG. 6 is a cross-sectional view of the microwell device M3 of the present disclosure.

(8) FIG. 7 is a flow chart of a method for manufacturing the microwell device according to a second embodiment of the present disclosure.

(9) FIG. 8 is a schematic view of step S100 of the method for manufacturing the microwell device according to the second embodiment of the present disclosure.

(10) FIG. 9 is a schematic view of step S102 of the method for manufacturing the microwell device according to the second embodiment of the present disclosure.

(11) FIG. 10 is a schematic view of step S104 of the method for manufacturing the microwell device according to the second embodiment of the present disclosure.

(12) FIG. 11 is a schematic view of step S106 of the method for manufacturing the microwell device according to the second embodiment of the present disclosure.

(13) FIG. 12 is a schematic view of step S108 of the method for manufacturing the microwell device according to the second embodiment of the present disclosure.

(14) FIG. 13 is a schematic view of step S110 of the method for manufacturing the microwell device according to the second embodiment of the present disclosure.

(15) FIG. 14 is a schematic view from the result culturing 80 μm microwell substrates containing MDCK cells after step (1) of a third embodiment of the present disclosure.

(16) FIG. 15 is a schematic view from the result culturing 80 μm microwell substrates containing MDCK cells after step (4) of a third embodiment of the present disclosure.

(17) FIG. 16 is a schematic view of MDCK cells in a “bare substrate” 60 μm in diameter, after 4 days of culture.

(18) FIG. 17 is a schematic view of MDCK cells in an “all-conjugated substrate” 60 μm in diameter, after 6 days of culture.

(19) FIG. 18 is a schematic view of MDCK cells in an “isolated microwell” 60 μm in diameter, after 7 days of culture.

(20) FIG. 19 is a schematic view of MDCK cells in a “closed micowells” 40 μm in diameter, after 7 days of culture.

(21) FIG. 20 is a scatter plots of percentages of undivided cell-tracking data from the microwell device with different diameters (the largest inner diameters=40, 60, 80, 100, 200 μm), 2D cultures (a flat culture device), and cylindrical microwells.

DETAILED DESCRIPTION OF THE EXEMPLARY EMBODIMENTS

(22) The present disclosure is more particularly described in the following examples that are intended as illustrative only since numerous modifications and variations therein will be apparent to those skilled in the art. Like numbers in the drawings indicate like components throughout the views. As used in the description herein and throughout the claims that follow, unless the context clearly dictates otherwise, the meaning of “a”, “an”, and “the” includes plural reference, and the meaning of “in” includes “in” and “on”. Titles or subtitles can be used herein for the convenience of a reader, which shall have no influence on the scope of the present disclosure.

(23) The terms used herein generally have their ordinary meanings in the art. In the case of conflict, the present document, including any definitions given herein, will prevail. The same thing can be expressed in more than one way. Alternative language and synonyms can be used for any term(s) discussed herein, and no special significance is to be placed upon whether a term is elaborated or discussed herein. A recital of one or more synonyms does not exclude the use of other synonyms. The use of examples anywhere in this specification including examples of any terms is illustrative only, and in no way limits the scope and meaning of the present disclosure or of any exemplified term. Likewise, the present disclosure is not limited to various embodiments given herein. Numbering terms such as “first”, “second” or “third” can be used to describe various components, signals or the like, which are for distinguishing one component/signal from another one only, and are not intended to, nor should be construed to impose any substantive limitations on the components, signals or the like.

First Embodiment

(24) Referring to FIG. 1 to FIG. 2, a first embodiment of the present disclosure provides a microwell device M including a substrate 10 and a plurality of microwells 20 formed on the substrate 10. Each of the microwells 20 includes a cavity 21 being recessed on the substrate 10 and an opening 22, and wherein the diameter D1 of the opening 22 is smaller than the largest inner diameter D2 of the cavity 21. In addition, the plurality of microwells 20 are curved.

(25) Further, the material of the substrate 10 can, but not limited to being, poly(acrylamide), polydimethylsiloxane, poly(lactic-co-glycolic acid), gelatin, silicone, polydimethylsiloxane, polyethylene, polystyrene, polyolefin, polyolefin copolymers, polycarbonate, ethylene vinyl acetate, polypropylene, polysulfone, polytetrafluoroethylene (PTFE), compatible fluoropolymer, or poly(styrene-butadiene-styrene).

(26) Referring to FIG. 1, the length L of the substrate 10 of the device M of the present disclosure can be 10 mm to 30 mm, and the width W of the substrate 10 can be 10 mm to 30 mm, but is not limited thereto. Further, the spacing between adjacent ones of the microwells 20 can be uniform or non-uniform, and the number of the microwells 20 can be greater than or equal to 100. In other embodiments, the substrate of the microwell device of the present disclosure can be disc-shaped, oval-shaped, or a polygon from the top view.

(27) Referring to FIG. 2 and FIG. 3, the shape of each of the microwells 20 can be spherical 20a or ellipsoidal 20b, 20c. Preferably, the ratio of the diameter D1 of the opening 22 of the microwell 20 to the largest inner diameter D2 of the cavity 21 of the microwell 20 is from 1:0.13 to 1:0.97. More preferably, the ratio of the diameter D1 of the opening 22 of the microwell 20 to the largest inner diameter D2 of the cavity 21 of the microwell 20 is from 1:0.43 to 1:0.66. Therefore, during cell culture, a single cell can be seeded into each microwell 20 separately, and the opening 22 which is narrower than the cavity 21 can effectively prevent the cells from sliding out of the microwell 20.

(28) Specifically speaking, the diameter D1 of the opening 22 ranges from 26 μm to 155 μm, and the largest inner diameter D2 of the cavity 21 ranges from 40 μm to 215 μm, but is not limited thereto. Each of the microwells 20 includes a side surface 23 and a bottom surface 24, the curvatures of the side surface 23 and the bottom surface 24 are not 0, and the side surface 23 and the bottom surface 24 have different curvatures or the same curvature. In addition, at least two of the microwells 20 can have different sizes.

(29) Referring to FIG. 2, the microwell device M with no coating (conjugation) can be called a “bare substrate”. Referring to FIG. 4, in other embodiments, the device M1 can further include a functional coating layer 30 being coated only on the surface of at least one of the microwells 20, and the functional coating layer 30 can to selected from the group consisting of glycosaminoglycan, polypeptide, proteoglycan, aminoglycan, and polysaccharide protein, refer to as “isolated s”. Referring to FIG. 5, in other embodiments, the functional coating layer 30 of the microwell device M2 can be coated on the surfaces the top surface 11 of the substrate 10 and the inner surface 25 of each of the cavity 21 of the microwells 20, referred to as an “all-coated substrate”. Referring to FIG. 6, in other embodiments, the microwell device M3 can further include a lid 40 having a functional layer 41 on the surface of the lid 40, and the lid 40 is detachably covered onto the microwell device M3 which the microwells 20 with the functional coating layer 30, and referred to as “closed s”. In addition, the material of the lid 40 is same as the substrate 10 thereof, and the material of the functional layer 41 of the lid 40 is same as the functional coating layer 30 thereof.

Second Embodiment

(30) Referring to FIG. 7 to FIG. 13, a second embodiment of the present disclosure provides a method for manufacturing a microwell device M, which at least includes step S100 to step S110. Firstly, in step S100, a microcolumn array N having a plurality of microcolumns 70 is produced from a first template by photolithography or soft lithography. In addition, the microcolumn array N can be made of polydimethylsiloxane (PDMS). In step S102, after a lift-off layer 80 [1% bovine serum albumin (BSA) in phosphate-buffered saline (PBS)] is coated on the microcolumns array N, a plurality of glass microspheres 90 are disposed on each of the plurality of the microcolumns 70 of the microcolumn array N (step S104). Next, in step S106, silicon (fast-curing silicone) is poured onto the microcolumn array N being disposed with the glass microspheres 90, after curing, the cured silicone is separated from the microcolumn array N and the glass microspheres 90 to form a second template K having a plurality of microcavities. After that, in step S108, epoxy material (two-part 5-min epoxy resin) is poured onto the second template K, the epoxy material is cured, and then the cured epoxy material is separated from the second template K to form a microwell device mold J. Lastly, in step S110, a mold material (polyacrylamide) is poured onto the microwell device mold J, the mold material is cured, and then the cured mold material is separated from the device mold J to obtain the microwell device M. It should be noted that, the microwell device M with no conjugation can be called a “bare substrate”.

(31) Referring to FIG. 2 and FIG. 10, specifically speaking, the diameters D3 of the microcolumns 70 determine the diameters D1 of the openings 22 of the microwells 20 of the microwell device M. It is worth mentioning that, the diameters D4 of the glass microspheres 90 determine the largest inner diameter D2 of the cavities 21 of the microwells 20 of the microwell device M. In other embodiments, the depth of each of the plurality of microcolumns is 45 μm, and the glass microspheres 90 of diameters (D3)=40, 60, 80, 100, and 200 μm are placed into the diameters (D4)=26, 40, 53, 66, or 132 μm of microcolumns 70, respectively, and the final geometry is shown in Table 1. In addition, the mold material such as polyacrylamide can be slightly elongated along the Z axis.

(32) TABLE-US-00001 TABLE 1 Summary of microwell and template geometry (all units except ε are μm.) the largest glass inner microcolumns the diameters elongation microspheres diameter diameter of openings ε along (D4) (D2) (D3) (D1) the z axis 40 41.0 ± 2.3 26 33.6 ± 4.0 1.13 ± 0.05 60 59.4 ± 3.8 40 46.1 ± 6.2 1.15 ± 0.04 80 80.3 ± 3.3 53 62.9 ± 6.6 1.14 ± 0.03 100 97.7 ± 3.6 66 78.0 ± 4.7 1.15 ± 0.08 200 204.7 ± 7.7  132 145.2 ± 8.1  1.16 ± 0.03

(33) Preferably, the ratio of the diameter D3 of the microcolumns 70 to the diameter D4 of the glass microspheres 90 is from 1:0.13 to 1:0.97. More preferably, the ratio of the diameter D3 of the microcolumns 70 to the diameter D4 of the glass microspheres 90 is from 1:0.43 to 1:0.66.

(34) To culture cells with strong cell-matrix adhesions, the extracellular matrix (ECM) proteins such as collagen or fibronectin is conjugated to the substrate and/or the microwells by using the bifunctional crosslinker sulfo-SANPAH, as the functional coating layer (and the functional layer of the lid).

Third Embodiment

(35) The Madin-Darby canine kidney (MDCK) cells were cultured in the s of the microwell device (80 μm of the largest inner diameter) on an orbital shaker. The microwell device was perturbed sequentially using four 30 minutes sessions using different parameters: (1) at 100 rpm with s facing upward; (2) at 100 rpm with microwells facing downward; (3) at 200 rpm with microwells facing upward; and (4) at 200 rpm with microwells facing downward. Results from after step (1) and (4) are shown in FIG. 14 and FIG. 15, respectively. Over the 2 hours perturbation, only one microwell of MDCK cell (black border in FIG. 15) was lost out of 32 microwells (dashed box in FIGS. 14 and 15). Therefore, this embodiment shows that the microwells of the microwell device of the present disclosure can prevent cells from slipping out of the microwells.

Fourth Embodiment

(36) Epithelial cells were cultured on the microwell device conjugated with ECM proteins (the functional layer 30) under four scenarios: a bare substrate (no conjugation), an all-coated substrate (ECM proteins everywhere), isolated microwells (only walls conjugated), and closed microwells (thin conjugated lids). On bare substrate, MDCK cells did not adhere to the substrate 10 nor the microwell 20 and exhibited an inverted polarity, with tight junctions T facing outward (as shown in FIG. 16), as reported when MDCK cells were cultured in suspension. On the all-coated substrate, MDCK cells covered the microwell 20 and top surface 11 of the substrate 10 over time, with the tight junctions T facing the culture medium (as shown in FIG. 17). In isolated microwells, cells grew and divided on the microwell 20, with the population of daughter cells eventually growing out of the microwell 20 (as shown in FIG. 18). In closed microwells, MDCK cells had their tight junctions T facing the lumen (as shown in FIG. 19), which is the same polarity as cysts grown in 3D gel in the related literature. Therefore, this embodiment shows that the coating position of the functional coating layer 30 (ECM proteins) will affect organization of cell aggregates.

Fifth Embodiment

(37) In addition to epithelial cells, fibroblasts were cultured in the device of the present disclosure. When cultured on “all-coated substrates”, fibroblasts tend to migrate to the flat substrate (data not shown). When cultured in “isolated microwells”, fibroblasts exhibited cell-cycle arrest. G1-synchronized REF52 cells were seeded into microwells 40, 60, 80, 100, or 200 μm in diameter, as well as on control planar substrate and cylindrical s of 90 μm in diameter and tracked cell division every day for 3 days. Referring to FIG. 20, on day 3, it is clear to see that the greater the ratio of substrate curvatures, the less division occurs in the cells. The division rate of cells in cylindrical wells is between the division rate of cells grown on a flat culture device and that of cells grown in spherical s, but closer to the cells on the flat substrate. The bottom of the cylindrical is still flat and the adhesions of cells on attaching to the bottom part are coplanar and thus cells may still sense and respond to the partial 2D microenvironment. In other words, the flat bottom of the cylindrical well may have affected cellular behaviors more than the curved wall. Some cells start to divide one day after seeding in 80, 100, and 200 μm microwells, but most cells do not divide in the first day even on the flat control and cylindrical well. Therefore, this embodiment shows that cell proliferation can be controlled through a well-defined geometric microenvironment in 3D cell culture device, which is never shown before.

(38) One of the advantages of the present disclosure is that, the device and the method of manufacturing the same of the present disclosure can make the cell culture device closer reflect the growth environment of cells in vivo, reduce cell loss, and make it easy for the experimenters to operate through the technical solution of “each of the microwells includes a cavity being recessed on the substrate and an opening, and wherein the diameter of the opening is smaller than the largest inner diameter of the cavity” and “the plurality of microwells are curved”.

(39) In addition, having the design of 3D cell culture compatible with the high-throughput screening is important for the application in drug screening where there are large compound libraries. Therefore, arranging the microwells into arrays can increase the throughput of analysis at the single well resolution and also makes the long-term tracking more easily.

(40) The foregoing description of the exemplary embodiments of the disclosure has been presented only for the purposes of illustration and description and is not intended to be exhaustive or to limit the disclosure to the precise forms disclosed. Many modifications and variations are possible in light of the above teaching.

(41) The embodiments were chosen and described in order to explain the principles of the disclosure and their practical application so as to enable others skilled in the art to utilize the disclosure and various embodiments and with various modifications as are suited to the particular use contemplated. Alternative embodiments will become apparent to those skilled in the art to which the present disclosure pertains without departing from its spirit and scope.