Process for obtaining a catalyst composite

Abstract

A process for obtaining a catalyst composite comprising the following steps: a). selecting a molecular sieve having pores of 10- or more-membered rings b). contacting the molecular sieve with a metal silicate different from said molecular sieve comprising at least one alkaline earth metal and one or more of the following metals: Ga, Al, Ce, In, Cs, Sc, Sn, Li, Zn, Co, Mo, Mn, Ni, Fe, Cu, Cr, Ti and V, such that the composite comprises at least 0.1 wt % of silicate.

Claims

1. A process for the catalytic cracking of an olefin-rich feedstock which is selective towards light olefins in the effluent, the process comprising: contacting a hydrocarbon feedstock containing one or more olefins with a catalyst composite comprising: at least 10 wt % of a molecular sieve having pores of 10- or more-membered rings; at least one metal silicate different from said molecular sieve comprising at least one alkaline earth metal, such that the catalyst composite comprises at least 0.1 wt % of silicate, wherein the molecular sieve is a zeolite, wherein the metal silicate is xonotlite (Ca.sub.6Si.sub.6Oi.sub.7(OH).sub.2) to produce an effluent with an olefin content of lower molecular weight than that of the hydrocarbon feedstock.

2. The process according to claim 1, wherein the catalyst composite comprises metal phosphate.

3. The process according to claim 1, wherein the catalyst composite comprises matrix material.

4. The process according to claim 1, wherein the catalyst composite comprises binder.

5. The process of claim 1 comprising: contacting an oxygen-containing, halogenide-containing or sulphur-containing organic feedstock in an XTO reactor with an XTO catalyst composite under conditions effective to convert the oxygen-containing, halogenide-containing or sulphur-containing organic feedstock to an XTO reactor effluent comprising olefin products, wherein the XTO catalyst composite comprises: at least 10 wt % of a molecular sieve having pores of 10- or more-membered rings; at least one metal silicate, different from said molecular sieve, comprising at least one alkaline earth metal, such that the XTO catalyst composite comprises at least 0.1 wt % of silicate, wherein the XTO reactor effluent comprises light olefins and a heavy hydrocarbon fraction and is sent to a fractionation section to separate the light olefins from the heavy hydrocarbon fraction; wherein the hydrocarbon fraction is the hydrocarbon feedstock containing the one or more olefins to be contacted with the catalyst composite.

6. The process according to claim 5, wherein the olefin products are fractionated to form a stream comprising essentially ethylene and at least a part of said stream is recycled in the XTO reactor to increase-propylene production.

7. The process according to claim 5, wherein the contacting a hydrocarbon feedstock containing one or more olefins with a catalyst composite is performed in an OCP reactor; and an OCP reactor effluent from the OCP reactor is sent to a fractionator and the light olefins are recovered; wherein hydrocarbons having 4 carbon atoms or more are recycled at an inlet of the OCP reactor, optionally mixed with heavy hydrocarbon recovered from the XTO reactor effluent.

8. The process according to claim 7, wherein the OCP reactor comprises a fixed bed reactor, a moving bed reactor, or a fluidized bed reactor.

9. The process according to claim 7, wherein, before recycling the hydrocarbons having 4 carbon atoms or more at the inlet of the OCP reactor, said hydrocarbons having 4 carbon atoms or more are sent to a second fractionator to purge the heavies.

10. The process according to claim 7, wherein, in order to adjust a propylene to ethylene ratio of the process, ethylene in whole or in part is recycled over the OCP reactor; wherein said ethylene is from a fractionation section of the XTO reactor, from a fractionation section of the OCP reactor, from both the fractionation section of the XTO reactor and the fractionation section of the OCP reactor, or from an optional common recovery section.

11. The process according to claim 7, wherein, in order to adjust propylene to ethylene ratio of the process, ethylene in whole or in part is recycled over the XTO reactor; wherein said ethylene is from a fractionation section of the XTO reactor, from a fractionation section of the OCP reactor, from both the fractionation section of the XTO reactor and the fractionation section of the OCP reactor, orfrom an optional common recovery section.

12. The process according to claim 5, wherein the XTO reactor effluent comprise ethylene, and wherein the ethylene is polymerized optionally with one or more comonomers.

13. The process according to claim 5, wherein the XTO reactor effluent comprise propylene, and wherein the propylene is polymerized optionally with one or more comonomers.

14. The process according to claim 5, wherein more than 50% by weight of olefins having 4 or more carbon atoms within the XTO reactor effluent are butenes.

15. The process according to claim 5, wherein more than 80% by weight of hydrocarbons having 4 or more carbon atoms within the XTO reactor effluent are C.sub.4 to C.sub.8 olefins.

16. The process according to claim 1, wherein the zeolite is selected from the group consisting of MFI, MOR, MEL, clinoptilolite, FER, FAU, MWW, BETA, ZSM-21, ZSM-22, ZSM-23, ZSM-42, ZSM-57, LTL, and combinations thereof.

17. The process according to claim 1, wherein the molecular sieve is a ZSM-5 zeolite.

Description

DETAILED DESCRIPTION OF THE INVENTION

(1) The molecular sieves that can be used in the invention are preferably zeolites, for example crystalline silicates, more precisely aluminosilicates. Crystalline silicates are microporous crystalline inorganic polymers based on a framework of XO.sub.4 tetrahydra linked to each other by sharing oxygen ions, where X may be trivalent (e.g. Al, B, . . . ) or tetravalent (e.g. Ge, Si, . . . ). The crystal structure of a crystalline silicate is defined by the specific order in which a network of tetrahedral units are linked together. The size of the crystalline silicate pore openings is determined by the number of tetrahedral units, or, alternatively, oxygen atoms, required to form the pores and the nature of the cations that are present in the pores. They possess a unique combination of the following properties: high surface area; uniform pores with one or more discrete sizes; ion exchangeability; good thermal stability; and ability to adsorb organic compounds. Since the pores of these crystalline aluminosilicates are similar in size to many organic molecules of practical interest, they control the ingress and egress of reactants and products, resulting in particular selectivity in catalytic reactions.

(2) The selected molecular sieve can be made with the help of the seeding technique, but advantageously they are made without template. However, the seeds themselves may have been made with a template, which means in this case that the molecular sieve is made without direct addition of a template. It is preferred that the molecular sieve used in the invention is made without direct addition of template.

(3) The molecular sieves selected for the purposes of this invention have pores the size of 10 or more-membered rings. It can be envisaged to use molecular sieves, which have ring pores consisting of 10, 12 or more members.

(4) The selected molecular sieve according to the present invention has an average pore size of at least 0.5, preferably from 0.5 to 10, more preferably from 0.5 to 5 and most preferably at least from 0.5 to 0.9 nm. The average pore size is determined according to the procedure of the International Zeolite Association.

(5) The selected molecular sieve has an initial atomic ratio Si/Al of at least 4 and not greater than 500. The Si/Al atomic ratio is measured by chemical analysis, for example using XRF and/or NMR. It includes only those Al that are part of the framework structure of the molecular sieve.

(6) As regards to the selected molecular sieve, advantageously it is selected from the group of MFI, MOR, MEL, clinoptilolite, FER, FAU, MWW, BETA, ZSM-21, ZSM-22, ZSM-23, ZSM-42, ZSM-57, LTL, or mixtures thereof, according to the International Zeolite Association (Atlas of Zeolite Structure Types, 1987, Butterworths). Preferably it is selected from group of the MFI, MOR, MEL, clinoptilolite, FER or a mixture of thereof. More preferably, the MFI is a ZSM-5 zeolite.

(7) In another embodiment, the molecular sieve selected from the group of MFI, MOR, MEL, clinoptilolite, FER or a mixture of, is preferably obtained without direct addition of template.

(8) The molecular sieve may be used as synthesised to form the catalyst composite. Prior to formulation of the catalyst composite the molecular sieve may undergo further treatments including steaming, leaching (e.g. acid leaching), washing, drying, calcination, impregnation and ion exchanging steps. In addition or alternatively, these steps can also be carried out after formulation of the catalyst composite.

(9) In a particular embodiment of the invention, the molecular sieve can be modified either prior to or after introduction of the metal silicate. Preferably, the molecular sieve has undergone some form of modification prior to the metal silicate introduction. By modification, it is meant herein that the molecular sieve may have undergone steaming, leaching (e.g. acid leaching), washing, drying, calcination, impregnation or some form of ion-exchange. This means that at least a portion of the cations originally comprised in the crystal structure can be replaced with a wide variety of other cations according to techniques well known in the art. The replacing cations can be hydrogen, ammonium or other metal cations, including mixtures of such cations.

(10) The selected molecular sieve is then formulated into a catalyst composite to comprise at least 10% by weight of a molecular sieve as described herein and at least one metal silicate comprising at least one alkaline earth metal, such that the composite comprises at least 0.1% by weight of silicate.

(11) At least one of the metal silicates comprised in the catalyst composite includes at least one alkaline earth metal, preferably Ca. Metal silicates are insoluble in water and alkaline earth metal ions, particularly calcium, are polyvalent and possess a large radius in the hydrated state. Thus, without wishing to be bound by theory, it is thought that the ion exchange reaction with the molecular sieve occurs very slowly, as the alkaline earth metal ion must lose many of its strongly coordinated water molecules in order to penetrate into the micropores of the molecular sieve structure. As a result, the alkaline earth metal ions expose only the acid sites located on the external surface of the molecular sieve, and thus increasing the selectivity of the catalyst.

(12) Furthermore, without wishing to be bound by theory, it is thought that the presence of silicate anions further improve the catalytic properties of the catalyst composite. The silicate anions, for example, can supply silicon atoms to heal defects in the molecular sieve. This can thus lead to additional stabilisation of the catalyst under severe hydrothermal conditions. As a result the metal silicate acts as a catalyst promoter.

(13) The metal silicate can comprise more than one alkaline earth metal selected from Ca, Mg, Sr and Ba.

(14) The metal silicates may also comprise other metals selected from one or more of the following: Ga, Al, Ce, In, Cs, Sc, Sn, Li, Zn, Co, Mo, Mn, Ni, Fe, Cu, Cr, Ti and V. Preferably, the other metal is selected from one or more of Al, Mg, Ce, Co and Zn or mixtures thereof. These bi-, tri- or polymetal silicates can be synthesised according to any method known in the art. This can be for example by ion exchange in the solution or solid state (Labhsetwar et al., Reactivity of Solids, Vol. 7, Issue 3, 1989, 225-233).

(15) The silicate anion can be present in any form in the solid metal silicate. Examples include SiO.sub.3.sup.2, SiO.sub.4.sup.4, Si.sub.2O.sub.7.sup.6, Si.sub.3O.sub.10.sup.8 and the like.

(16) The preferred catalyst promoter is a calcium silicate with a very open and accessible pore structure. An even more preferred catalyst promoter comprises a synthetic crystalline hydrated calcium silicate having a chemical composition of Ca.sub.6Si.sub.6O.sub.17(OH).sub.2 which corresponds to the known mineral xonotlite (having a molecular formula 6CaO.6SiO.sub.2.H.sub.2O).

(17) Generally, a synthetic hydrated calcium silicate is synthesised hydrothermally under autogeneous pressure. A particularly preferred synthetic hydrated calcium silicate is available in commerce from the company Promat of Ratingen in Germany under the trade name Promaxon.

(18) In order to demonstrate the thermal stability of xonotlite, and therefore the applicability of xonotlite as a catalyst promoter in MTO and OCP, commercial xonotlite sold under the trade name Promaxon D was calcined in ambient air at a relative humidity of about 50% at 650 C. for a period of 24 hours. The initial xonotlite had a crystalline phase Ca.sub.6Si.sub.6O.sub.17(OH).sub.2 with a BET surface area of 51 m.sup.2/gram and a pore volume (of less than 100 nanometers) of 0.35 ml/gram. After calcination at 650 C., the carrier retained its crystallinity, which corresponds to that of xonotlite. Thus after a 24 hour calcination at 650 C., the crystalline phase still comprised xonotlite (Ca.sub.6Si.sub.6O.sub.17(OH).sub.2) with a BET surface area of 47.4 m.sup.2/gram and a pore volume (less than 100 nanometers) of 0.30 ml/gram.

(19) Other examples of metal silicates comprising alkaline earth metals include CaAl.sub.2Si.sub.2O.sub.8, Ca.sub.2Al.sub.2SiO.sub.7, CaMg(Si.sub.2O.sub.6).sub.x, as well as mixtures thereof.

(20) Before mixing with the molecular sieve said metal silicate compounds may be modified by calcination, steaming, ion-exchange, impregnation, or phosphatation. Said metal silicates may be an individual compound or may be a part of mixed compounds.

(21) The metal silicate can be brought into contact with the molecular sieve by a simultaneous formulation step of a blend of the metal silicate with the molecular sieve or in situ blending of separately formulated materials in the reaction medium prior to the XTO or OCP process. Said contact can be realised by mechanically blending of the molecular sieve with the alkaline earth metal-comprising metal silicate. This can be carried out via any known blending method. Blending can last for a period of time starting from 1 minute up to 24 hours, preferably from 1 min to 10 hours. If not carried out in the XTO or OCP reactor in situ, it can be carried out in a batchwise Mixer or in a continuous process, such as in an extruder e.g. a single or twin screw extruder at a temperature of from 20 to 300 C. under vacuum or elevated pressure. Said contact may be performed in an aqueous or non-aqueous medium. Prior to the formulation step, other compounds that aid the formulation may be added, like thickening agents or polyelectrolytes that improve the cohesion, dispersion and flow properties of the precursor. In case of extrusion, rotating granulation or pelletising a paste-like precursor with low water content is prepared. In case of oil-drop or spray-drying a rather liquid (high water content) is prepared. In another embodiment, the contact is carried out in the presence of phosphorus containing compounds. In a particular embodiment, the contact is carried out in the aqueous medium at pH lower than 5, more preferably lower than 3.

(22) Either prior to, after or simultaneously with the formulation step to form the composite, other components may be optionally blended with the molecular sieve. In a particular embodiment, the molecular sieve can be combined with other materials that provide additional hardness or catalytic activity to the finished catalyst product. Materials, which can be blended with the molecular sieve, can be various inert or catalytically active matrix materials and/or various binder materials. Such materials include clays, silica and/or metal oxides such as alumina. The latter is either naturally occurring or in the form of gelatinous precipitates or gels including mixtures of silica and metal oxides. In an embodiment, some binder materials can also serve as diluents in order to control the rate of conversion from feed to products and consequently improve selectivity. The occurrence of hot spots in the catalyst composites can also be reduced when binder is included. According to one embodiment, the binders also improve the crush strength of the catalyst under industrial operating conditions.

(23) Naturally occurring clays, which can be used as binder, are for example clays from the kaolin family or montmorillonite family. Such clays can be used in the raw state as mined or they can be subjected to various treatments before use, such as calcination, acid treatment or chemical modification.

(24) In addition to the foregoing, other materials which can be included in the catalyst composite of the invention include various forms of metals, phosphates (for instance metal phosphates, wherein the metal is chosen from one or more of Ca, Ga, Al, Ca, Ce, In, Cs, Sr, Mg, Ba, Sc, Sn, Li, Zn, Co, Mo, Mn, Ni, Fe, Cu, Cr, Ti and V), alumina or alumina sol, titania, zirconia, quartz, silica or silica sol, and mixtures thereof. Examples of possible phospates include amorphous calcium phosphate monocalcium phosphate, dicalcium phosphate, dicalcium phosphate dehydrate, - or -tricalcium phosphate, octacalcium phosphate, hydroxyapatite etc.

(25) Examples of possibly binary oxide binder compositions include, silica-alumina, silica magnesia, silica-zirconia, silica-thoria, silica-beryllia, silica-titania, calcium-alumina. Examples of ternary binder compositions include for instance calcium-silica-alumina or silica-alumina-zirconia.

(26) These components are effective in increasing the density of the catalyst and increasing the strength of the formulated catalyst. The catalyst may be formulated into pellets, spheres, extruded into other shapes, or formed into spray-dried particles. Generally, the size of the catalyst particles can vary from about 20 to 50,000 m. In general pellets, spheres and extrudates are employed in fixed bed reactors and exhibit a particle size of from about 0.5 mm to 5 mm. In general spray-dried particles are used in fluidised bed reactors and exhibit a particle size of from about 20 to 200 m. In particular spheres are employed in moving bed reactors and exhibit a size from about 0.5 to 5 mm. Spheres can be made in rotating granulator or by oil-drop methods. The crystal size of the molecular sieve contained in the catalyst composite, is preferably less than about 10 m, more preferably less than about 5 m and most preferably less than about 2 m. The amount of molecular sieve, which is contained in the final catalyst composite ranges from 10 to 90% by weight of the total catalyst composite, preferably 20 to 70% by weight.

(27) According to another embodiment, non-modified molecular sieves were first formulated with a binder and matrix materials and then modified with phosphorous and alkaline earth metal silicates.

(28) According to a further particular embodiment, molecular sieves were optionally dealuminated and then modified with phosphorous during the formulation step. Introduction of the alkaline earth metal silicate can be performed during the formulation step or on the formulated solid. According to a preferred embodiment, molecular sieves were first optionally dealuminated and modified with phosphorous and then formulated. Introduction of the metal is performed simultaneously with the phosphorous modification step and/or on the already formulated catalyst.

(29) After formulation, the catalyst composite may undergo further treatments including further steaming, leaching, washing, drying, calcination, impregnations and ion exchanging steps. If the molecular sieve was not modified with phosphorus prior to the formulation step of the blend i.e. the step introducing the metal silicate to the molecular sieve, it may be carried out after such a step.

(30) According to another embodiment of the invention, the molecular sieve is a phosphorus-modified (P-modified) zeolite. The zeolite can be dealuminated and/or modified with phosphorus. Phosphorus can be introduced before, simultaneously or after contact of the zeolite with the metal silicate, preferably before or simultaneously, most preferably before. Preferably, the P-modification is carried out with a steaming step followed by leaching using any acid solution containing a source of P, preferably a solution of phosphoric acid.

(31) According to one embodiment of the invention, the zeolite can be modified with phosphorus according to the process comprising the following steps, in the order given: steaming of the zeolite at a temperature ranging from 400 to 870 C. for 0.01-200 h; leaching with an aqueous acid solution containing the source of P at conditions effective to remove a substantial part of Al from the zeolite and to introduce at least 0.3% of phosphorus by weight of the zeolite; separation of the solid from the liquid; an optional washing step or an optional drying step or an optional drying step followed by a washing step; a calcination step.

(32) In the steam treatment step, the temperature is preferably from 420 to 870 C., more preferably from 480 to 760 C. The pressure is preferably atmospheric pressure and the water partial pressure may range from 13 to 100 kPa. The steam atmosphere preferably contains from 5 to 100 vol % steam with from 0 to 95 vol % of an inert gas, preferably nitrogen. The steam treatment is preferably carried out for a period of from 0.05 to 200 hours, more preferably from 0.05 to 50 hours. It is generally known by the persons in the art that steam treatment of zeolites results in aluminium that leaves the zeolite framework and resides as aluminiumoxides in and outside the pores of the zeolite. This transformation is known as dealumination of zeolites and this term will be used throughout the text.

(33) The treatment of the steamed zeolite with an acid solution results in dissolution of the extra-framework aluminiumoxides. This transformation is known as leaching and this term will be used throughout the text. The leaching with an aqueous acid solution containing the source of phosphorus is advantageously made under reflux conditions, meaning boiling temperature of the solution.

(34) Amount of said acid solution is advantageously between 2 and 10 liters per kg of zeolite. A typical leaching period is around 0.5 to 24 hours. Advantageously the aqueous acid solution containing the source of P in the leaching step has a pH of 3, advantageously 2, or lower. Advantageously said aqueous acid solution is phosphorus acids, a mixture of phosphorus acids and organic or inorganic acid or mixtures of salts of phosphorus acids and organic or inorganic acids. The phosphorus acids or the corresponding salts can be of the phosphate ([PO.sub.4].sup.3, being tribasic), phosphite ([HPO.sub.3].sup.2, being dibasic), or hypophosphite ([H.sub.2PO.sub.2].sup.1, being monobasic), type. Of the phosphate type also di- or polyphosphates ([P.sub.nO.sub.3n+1].sup.(n+2)) can be used. The other organic acids may comprise an organic acid such as citric acid, formic acid, oxalic acid, tartaric acid, malonic acid, succinic acid, glutaric acid, adipic acid, maleic acid, phthalic acid, isophthalic acid, fumaric acid, nitrilotriacetic acid, hydroxyethylenediaminetriacetic acid, ethylenediaminetetracetic acid, trichloroacetic acid trifluoroacetic acid or a salt of such an acid (e.g. the sodium salt) or a mixture of two or more of such acids or salts. The other inorganic acids may comprise an inorganic acid such as nitric acid, hydrochloric acid, methansulfuric acid, sulfuric acid or a salt of such an acid (e.g. the sodium or ammonium salts) or a mixture of two or more of such acids or salts.

(35) It has been found that phosphorus acid is very efficient in complexing the extra-framework aluminiumoxides and hence removing them from the zeolite solid material. Unexpectedly, a larger quantity of phosphorus than what could be expected from the typical pore volume of the zeolite and assuming that the pores of the zeolites are filled with the used phosphorus acid solution, stays in the solid zeolite material. Both factors dealumination and the retention of P stabilize the lattice aluminium in the zeolitic lattice, thus avoiding further dealumination. This leads to higher hydrothermal stability, tuning of molecular sieves properties and adjustment of acid properties and thus increasing the zeolite's selectivity. The degree of dealumination can be adjusted by the steaming and leaching conditions.

(36) Advantageously, the final P-content of the zeolite is at least 0.3 wt % and preferably between 0.3 and 7 w %. Advantageously at least 10% of Al have been extracted and removed from the zeolite by the leaching. The residual P-content is adjusted by P-concentration in the leaching solution, drying conditions and a washing procedure if any. A drying step can be envisaged between filtering and washing steps.

(37) Then the zeolite either is separated from the washing solution or is dried without separation from the washing solution. Said separation is advantageously made by filtration. Then the zeolite is calcined, by way of example, at 400 C. for 2-10 hours.

(38) With regards to the XTO process, the catalyst composite of the invention is particularly suited for the catalytic conversion of oxygen-containing, halogenide-containing or sulphur-containing organic compounds to hydrocarbons. Accordingly, the present invention also relates to a method for making an olefin product from an oxygen-containing, halogenide-containing or sulphur-containing organic feedstock wherein said oxygen-containing, halogenide-containing or sulphur-containing organic feedstock is contacted with the above catalyst under conditions effective to convert the oxygen-containing, halogenide-containing or sulphur-containing organic feedstock to olefin products (the effluent of the XTO). Said effluent comprises light olefins and a heavy hydrocarbon fraction.

(39) In this process a feedstock containing an oxygen-containing, halogenide-containing or sulphur-containing organic compound contacts the above described catalyst composite in a reaction zone of a reactor at conditions effective to produce light olefins, particularly ethylene and propylene. Typically, the oxygen-containing, halogenide-containing or sulphur-containing organic feedstock is contacted with the catalyst composite when the oxygen-containing, halogenide-containing or sulphur-containing organic compounds are in the vapour phase. Alternately, the process may be carried out in a liquid or a mixed vapour/liquid phase. In this process, converting oxygen-containing, halogenide-containing or sulphur-containing organic compounds, olefins can generally be produced at a wide range of temperatures. An effective operating temperature range can be from about 200 C. to 700 C. At the lower end of the temperature range, the formation of the desired olefin products may become markedly slow. At the upper end of the temperature range, the process may not form an optimum amount of product. An operating temperature of at least 300 C., and up to 600 C. is preferred.

(40) The pressure also may vary over a wide range. Preferred pressures are in the range of about 0.005 bars to about 50 bars, with the most preferred range being of from about 0.05 bars to about 5 bars. The foregoing pressures refer to the partial pressure of the oxygen-containing, halogenide-containing, sulphur-containing organic compounds and/or mixtures thereof.

(41) The process can be carried out in any system using a variety of transport beds, particularly a fixed bed or moving bed system could be used. Advantageously a fluidized bed is used. It is particularly desirable to operate the reaction process at high space velocities. The process can be conducted in a single reaction zone or a number of reaction zones arranged in series or in parallel. Any standard commercial scale reactor system can be used, for example fixed bed, fluidised or moving bed systems. After a certain time on-stream the catalyst needs to be regenerated. This regeneration can be carried out in a separate reactor or in the same reactor. In case of a moving bed or fluidised bed reactor, a part of the catalyst is continuously or intermittently withdrawn from the conversion reactor and sent to a second reactor for regeneration. After the regeneration, the regenerated catalyst is continuously or intermittently sent back to the conversion reactor. In case of fixed bed reactor the reactor is taken off-line for regeneration. Generally this requires a second spare reactor that can take over the conversion into light olefins. After regeneration the fixed bed reactor is in stand-by until the spare reactor needs regeneration and the regenerated reactor takes over the conversion. Regeneration is carried out by injecting an oxygen-containing stream over the catalyst composite at a sufficiently high temperature to burn the deposited coke on the catalyst composite. The commercial scale reactor systems can be operated at a weight hourly space velocity (WHSV) of from 0.1 hr.sup.1 to 1000 hr.sup.1.

(42) One or more inert diluents may be present in the feedstock, for example, in an amount of from 1 to 95 molar percent, based on the total number of moles of all feed and diluent components fed to the reaction zone. Typical diluents include, but are not necessarily limited to helium, argon, nitrogen, carbon monoxide, carbon dioxide, hydrogen, water, paraffins, alkanes (especially methane, ethane, and propane), aromatic compounds, and mixtures thereof. The preferred diluents are water and nitrogen. Water can be injected in either liquid or vapour form.

(43) According to a specific embodiment essentially no water (or steam) is injected as a diluent of the feedstock sent to the XTO reactor. However it means that the feedstock can contain the water already contained in the fresh oxygen-containing, halogenide-containing or sulphur-containing organic feedstock or the steam used to engage proper flowing of catalyst in fluidised bed or moving bed reactors of the XTO reactor.

(44) The oxygenate feedstock is any feedstock containing a molecule or any chemical having at least an oxygen atom and capable, in the presence of the above catalyst composite, to be converted to olefin products. The oxygenate feedstock comprises at least one organic compound which contains at least one oxygen atom, such as aliphatic alcohols, ethers, carbonyl compounds (aldehydes, ketones, carboxylic acids, carbonates, esters and the like). Representative oxygenates include but are not necessarily limited to lower straight and branched chain aliphatic alcohols and their unsaturated counterparts. Examples of suitable oxygenate compounds include, but are not limited to: methanol; ethanol; n-propanol; isopropanol; C.sub.4-C.sub.20 alcohols; methyl ethyl ether; dimethyl ether; diethyl ether; di-isopropyl ether; formaldehyde; dimethyl carbonate; dimethyl ketone; acetic acid; and mixtures thereof. Representative oxygenates include lower straight chain or branched aliphatic alcohols, their unsaturated counterparts. Analogously to these oxygenates, compounds containing sulphur or halides may be used. Examples of suitable compounds include methyl mercaptan; dimethyl sulfide; ethyl mercaptan; diethyl sulfide; ethyl monochloride; methyl monochloride, methyl dichloride, n-alkyl halides, n-alkyl sulfides having n-alkyl groups of comprising the range of from about 1 to about 10 carbon atoms; and mixtures thereof. Preferred oxygenate compounds are methanol, dimethyl ether, or a mixture thereof.

(45) In the XTO effluent among the olefins having 4 or more carbon atoms, more than 50% by weight are butenes. More than 80% by weight and advantageously more than 85% of the hydrocarbons having 4 carbon atoms or more are C4 to C8 olefins.

(46) According to a specific embodiment the XTO reactor effluent comprising light olefins and a heavy hydrocarbon fraction is sent to a fractionation section to separate said light olefins from said heavy hydrocarbon fraction; said heavy hydrocarbon fraction is recycled in the XTO reactor at conditions effective to convert at least a portion of said heavy hydrocarbon fraction to olefin products.

(47) With regards to said effluent of the XTO process, light olefins means ethylene and propylene and the heavy hydrocarbon fraction is defined herein as the fraction containing hydrocarbons having a molecular weight greater than propane, which means hydrocarbons having 4 carbon atoms or more and written as C.sub.4.sup.+.

(48) According to another embodiment of the invention said olefin products (the effluent of the XTO) are fractionated to form a stream comprising essentially ethylene and at least a part of said stream is recycled in the XTO reactor to increase the propylene production and hence the flexibility of ethylene vs propylene production. Advantageously the ratio of ethylene to the oxygen-containing, halogenide-containing or sulphur-containing organic feedstock is 1.8 or less.

(49) According to another embodiment of the invention both ethylene and the C.sub.4.sup.+ can be recycled in the XTO reactor.

(50) The present invention also relates to a process (hereunder referred to as a combined XTO and OCP process) to make light olefins from an oxygen-containing, halogenide-containing or sulphur-containing organic feedstock comprising: contacting said oxygen-containing, halogenide-containing or sulphur-containing organic feedstock in the XTO reactor with the above catalyst at conditions effective to convert at least a portion of the feedstock to form an XTO reactor effluent comprising light olefins and a heavy hydrocarbon fraction; separating said light olefins from said heavy hydrocarbon fraction; contacting said heavy hydrocarbon fraction in the OCP reactor at conditions effective to convert at least a portion of said heavy hydrocarbon fraction to light olefins.

(51) The effluent of the XTO reactor comprising light olefins and a heavy hydrocarbon fraction is sent to a fractionation section to separate said light olefins from said heavy hydrocarbon fraction. With regards to said effluent of the XTO process, light olefins means ethylene and propylene and the heavy hydrocarbon fraction is defined herein as the fraction containing hydrocarbons having a molecular weight greater than propane, which means hydrocarbons having 4 carbon atoms or more and written as C.sub.4.sup.+. It is desirable to have a substantially 100% conversion of the organic compound in the primary reactor. This conversion rate is adjusted by optimisation of the contact time and the frequency of the regeneration of the catalyst.

(52) With regards to the OCP process, said process is known per se. It has been described in EP 1036133, EP 1035915, EP 1036134, EP 1036135, EP 1036136, EP 1036138, EP 1036137, EP 1036139, EP 1194502, EP 1190015, EP 1194500 and EP 1363983 the content of which are incorporated in the present invention. The heavy hydrocarbon fraction produced in the XTO reactor is converted in the OCP reactor, also called an olefin cracking reactor herein, to produce additional amounts of ethylene and propylene.

(53) According to a specific embodiment the catalysts found to produce this conversion comprise a crystalline aluminosilicate of the MFI family or the MEL family. These aluminosilicates have been described above in the description of the molecular sieve.

(54) The MFI or MEL catalyst having a high Si/Al atomic ratio for use in the OCP reactor of the present invention may be manufactured by removing aluminum from a commercially available crystalline silicate. A typical commercially available silicalite has a silicon/aluminum atomic ratio of around 120. The commercially available MFI crystalline silicate may be modified by a steaming process, which reduces the tetrahedral aluminum in the crystalline silicate framework and converts the aluminum atoms into octahedral aluminum in the form of amorphous alumina. Although in the steaming step aluminum atoms are chemically removed from the crystalline silicate framework structure to form alumina particles, those particles cause partial obstruction of the pores or channels in the framework. This inhibits the olefinic cracking processes of the present invention. Accordingly, following the steaming step, the crystalline silicate is subjected to an extraction step wherein amorphous alumina is removed from the pores and the micropore volume is, at least partially, recovered. The physical removal, by a leaching step, of the amorphous alumina from the pores by the formation of a water-soluble aluminum complex yields the overall effect of de-alumination of the MFI crystalline silicate. In this way by removing aluminum from the MFI crystalline silicate framework and then removing alumina formed there from the pores, the process aims at achieving a substantially homogeneous dealumination throughout the whole pore surface of the catalyst. This reduces the acidity of the catalyst and thereby reduces the occurrence of hydrogen transfer reactions in the cracking process. The reduction of acidity ideally occurs substantially homogeneously throughout the pores defined in the crystalline silicate framework. This is because in the olefin-cracking process hydrocarbon species can enter deeply into the pores. Accordingly, the reduction of acidity and thus the reduction in hydrogen transfer reactions, which would reduce the stability of the MFI catalyst are pursued throughout the whole pore structure in the framework. The framework silicon/aluminum ratio may be increased by this process to a value of at least about 180, preferably from about 180 to 500, more preferably at least 200, yet more preferably at least 300 and most preferably around 480.

(55) The MEL or MFI crystalline silicate catalyst may be mixed with a binder, preferably an inorganic binder. The binder is selected so as to be resistant to the temperature and other conditions employed in the catalyst manufacturing process and in the subsequent catalytic cracking process for the olefins. The binder is an inorganic material selected from clays, silica, metal oxides such as ZrO.sub.2 and/or metals, or gels including mixtures of silica and metal oxides. The binder is preferably alumina-free, although aluminum in certain chemical compounds as in aluminium phosphate's may be used as the latter are quite inert and not acidic in nature. If the binder, which is used in conjunction with the crystalline silicate, is itself catalytically active, this may alter the conversion and/or the selectivity of the catalyst. Inactive materials for the binder may suitably serve as diluents to control the amount of conversion so that products can be obtained economically and orderly without employing other means for controlling the reaction rate. It is desirable to provide a catalyst having a good crush strength. This is because in commercial use, it is desirable to prevent the catalyst from breaking down into powder-like materials. Such clay or oxide binders have been employed normally only for the purpose of improving the crush strength of the catalyst. A particularly preferred binder for the catalyst composite for use in an OCP reactor are silica or aluminium phosphates.

(56) The relative proportions of the finely divided crystalline silicate material and the inorganic oxide matrix of the binder can vary widely. Typically, the binder content ranges from 5 to 95% by weight, more typically from 20 to 50% by weight, based on the weight of the composite catalyst. Such a mixture of crystalline silicate and an inorganic oxide binder is referred to as a formulated crystalline silicate. In mixing the catalyst with a binder, the catalyst may be formulated into extended pellets, spheres, extruded into other shapes, or formed into a spray-dried powder.

(57) According to another specific embodiment the catalyst composite for the OCP process comprises a P-modified zeolite selected from a group of zeolites with a low Si/Al ratio (advantageously lower than 30) being in the H.sup.+ or NH.sub.4.sup.+-form of MFI, MEL, FER, MOR, clinoptilolite, which have been made preferably without direct addition of organic template.

(58) According to another specific embodiment of the invention, the P-zeolite can be modified with phosphorus according to the same process as described above.

(59) The catalyst composites of the invention can thus be used both in the XTO and in the OCP processes. The catalyst composite in the OCP reactor can be the same as the catalysts of the XTO reactor or they can be different, due to differences in the starting zeolite, the P content and so on. The catalyst composite of the invention can also be used only in the OCP process i.e. the process for the catalytic cracking of an olefin-rich feedstock which is selective towards light olefins in the effluent, the process comprising contacting a hydrocarbon feedstock containing one or more olefins, with a catalyst composite according to the invention, to produce an effluent with an olefin content of lower molecular weight than that of the feedstock.

(60) The crystalline aluminosilicate catalyst has structural and chemical properties and is employed under particular reaction conditions during the OCP process whereby the catalytic cracking of the C.sub.4.sup.+ olefins readily proceeds. Different reaction pathways can occur on the catalyst. The cracking of the olefins is preferably performed at an inlet temperature of the feedstock of from 400 to 650 C., more preferably from 450 to 600 C., yet more preferably from 540 C. to 590 C., typically around 560 to 585 C. and under an olefin partial pressure of from 0.1 to 2 bars, most preferably around atmospheric pressure. Olefin catalytic cracking may be understood to comprise a process yielding shorter molecules via bond breakage. In the catalytic cracking process of the OCP reactor, the process conditions are selected in order to provide high selectivity towards propylene or ethylene, as desired, a stable olefin conversion over time, and a stable olefinic product distribution in the effluent. Such objectives are favoured by the use of a low acid density in the catalyst (i.e. a high Si/Al framework atomic ratio) in conjunction with a low pressure, a high inlet temperature and a short contact time, all of which process parameters are interrelated and provide an overall cumulative effect.

(61) The process conditions are selected to disfavour hydrogen transfer reactions leading to the formation of paraffins, aromatics and coke precursors. The process operating conditions thus employ a high space velocity, a low pressure and a high reaction temperature. The LHSV ranges from 0.5 to 30 hr.sup.1, preferably from 1 to 30 hr.sup.1. The olefin partial pressure ranges from 0.1 to 2 bars, preferably from 0.5 to 1.5 bars (absolute pressures referred to herein). A particularly preferred olefin partial pressure is atmospheric pressure (i.e. 1 bar). The heavy hydrocarbon fraction feedstock is preferably fed at a total inlet pressure sufficient to convey the feedstocks through the reactor. Said feedstock may be fed undiluted or diluted in an inert gas, e.g. nitrogen or steam. Preferably, the total absolute pressure in the second reactor ranges from 0.5 to 10 bars. The use of a low olefin partial pressure, for example atmospheric pressure, tends to lower the incidence of hydrogen transfer reactions in the cracking process, which in turn reduces the potential for coke formation, which tends to reduce catalyst stability. The cracking of the olefins is preferably performed at an inlet temperature of the feedstock of from 400 to 650 C., more preferably from 450 to 600 C., yet more preferably from 540 C. to 590 C., typically around 560 to 585 C.

(62) In order to maximize the amount of ethylene and propylene and to minimize the production of methane, aromatics and coke, it is desired to minimize the presence of diolefins in the feed. Diolefin conversion to monoolefin hydrocarbons may be accomplished with a conventional selective hydrogenation process such as disclosed in U.S. Pat. No. 4,695,560 hereby incorporated by reference.

(63) The OCP reactor can be a fixed bed reactor, a moving bed reactor or a fluidized bed reactor. A typical fluid bed reactor is one of the fluid catalytic cracking (FCC) type used for fluidized-bed catalytic cracking in the oil refinery. A typical moving bed reactor is of the continuous catalytic reforming type. As described above, the process may be performed continuously using a pair of parallel swing reactors. The heavy hydrocarbon fraction cracking process is endothermic; therefore, the reactor should be adapted to supply heat as necessary to maintain a suitable reaction temperature. Online or periodic regeneration of the catalyst may be provided by any suitable means known in the art.

(64) The various preferred catalysts of the OCP reactor have been found to exhibit high stability, in particular being capable of giving a stable propylene yield over several days, e.g. up to ten days. This enables the olefin cracking process to be performed continuously in two parallel swing reactors wherein when one reactor is operating, the other reactor is undergoing catalyst regeneration. The catalyst can be regenerated several times.

(65) The OCP reactor effluent comprises methane, light olefins and hydrocarbons having 4 carbon atoms or more. Advantageously said OCP reactor effluent is sent to a fractionator and the light olefins are recovered. Advantageously the hydrocarbons having 4 carbon atoms or more are recycled at the inlet of the OCP reactor, optionally mixed with the heavy hydrocarbon recovered from the effluent of the XTO reactor. Advantageously, before recycling said hydrocarbons having 4 carbon atoms or more at the inlet of the OCP reactor, said hydrocarbons having 4 carbon atoms or more are sent to a second fractionator to purge the heavies. In a preferred embodiment the light olefins recovered from the effluent of the XTO reactor and the light olefins recovered from the fractionator following the OCP reactor are treated in a common recovery section.

(66) Optionally, in order to adjust the propylene to ethylene ratio of the whole process (XTO+OCP), ethylene in whole or in part can be recycled over the OCP reactor and advantageously converted into more propylene. This ethylene can either come from the fractionation section of the XTO reactor or from the fractionation section of the OCP reactor or from both the fractionation section of the XTO reactor and the fractionation section of the OCP reactor or even from the optional common recovery section.

(67) Optionally, in order to adjust the propylene to ethylene ratio of the whole process (XTO+OCP), ethylene in whole or in part can be recycled over the XTO reactor where it combines with the oxygen-containing, halogenide-containing or sulphur-containing organic feedstock to form more propylene. This ethylene can either come from the fractionation section of the XTO reactor or from the fractionation section of the OCP reactor or from both the fractionation section of the XTO reactor and the fractionation section of the OCP reactor or even from the optional common recovery section.

(68) These ways of operation allow to respond with the same equipment and catalyst to market propylene to ethylene demand.

(69) The method of making the olefin products from an oxygenate feedstock can include the additional step of making the oxygenate feedstock from hydrocarbons such as oil, coal, tar sand, shale, biomass and natural gas. Methods for making oxygenate feedstocks are known in the art. These methods include fermentation to alcohol or ether, making synthesis gas, then converting the synthesis gas to alcohol or ether. Synthesis gas can be produced by known processes such as steam reforming, autothermal reforming and partial oxidization in case of gas feedstocks or by reforming or gasification using oxygen and steam in case of solid (coal, organic waste) or liquid feedstocks. Methanol, methylsulfide and methylhalides can be produced by oxidation of methane with the help of dioxygen, sulphur or halides in the corresponding oxygen-containing, halogenide-containing or sulphur-containing organic compound.

(70) One skilled in the art will also appreciate that the olefin products made by the oxygenate-to-olefin conversion reaction using the molecular sieve of the present invention can be polymerized optionally with one or more comonomers to form polyolefins, particularly polyethylenes and polypropylenes. The present invention relates also to said polyethylenes and polypropylenes.

(71) The following non-limiting examples are provided to illustrate the invention.

EXAMPLES

Example 1

(72) A sample of zeolite ZSM-5 with Si/Al=12 (CBV2314) from Zeolyst International was first calcined for 6 hours at 550 C. (60/min heating rate). It was then was steamed at 680 C. for 2 hours in 100% steam. The steamed solid was treated with a 3.14-M solution of H.sub.3PO.sub.4 for 18 h under reflux conditions (4.2 liter/1 kg of zeolite). The solid was then separated by filtration from the solution. The obtained solid was dried first at 110 C. for 16 h and then at 400 C. for 3 h.

Example 2

(73) The sample obtained from example 1 was blended with 10 wt % of xonotlite (Ca.sub.6Si.sub.6O.sub.17(OH).sub.2) and subjected under reflux conditions in contact with hot water for 2 hours. Then the solid was separated by filtering from the solution, dried immediately at 110 C. for 16 hours and steamed at 600 C. for 2 hours in 100% steam (Atomic ratio Si/Al 15, P-content 2.5 wt %). The sample is hereinafter identified as SAMPLE A.

Example 3

(74) The sample described in example 1 was subjected to reflux conditions for 2 hours in contact with hot water under. Then the solid was separated by filtering from the solution and dried immediately at 110 C. for 16 hours and steamed at 600 C. for 2 hours in 100% steam. (Atomic ratio Si/Al 15, P-content 2.0 wt %). Contrary to example 2, no calcium compound is added.

(75) The sample is hereinafter identified as Comparative I.

Example 4

(76) The sample obtained in example 1 was impregnated with an aqueous solution of calcium acetate (0.5-M solution) (1 ml/1 g of zeolite) with a target of 2 wt % Ca. Then the sample was dried at 110 C. and subjected in a contact with hot water under reflux condition for 2 hours. Then the solid was separated by filtering from the solution and dried right away at 110 C. for 16 h and steamed at 600 C. for 2 hours in 100% steam. (Atomic ratio Si/Al 15, P-content 2.1 wt %). Contrary to example 2, the calcium is added in the form of calcium acetate.

(77) The sample is hereinafter identified as Comparative II.

Example 5

(78) Contrary to example 2, in this example SiO.sub.2 and calcium compound were added separately. Calcium compound was introduced as calcium acetate and SiO.sub.2 was added as in the form of Ludox LS-40.

(79) A sample of zeolite ZSM-5 with Si/Al=12 (CBV2314) from Zeolyst International was first calcined for 6 hours at 550 C. (60/min heating rate) and then was steamed at 680 C. for 2 h in 100% steam. The steamed solid was blended with 10 wt % of SiO.sub.2 in the form of Ludox LS40 treated with a 3.14-M solution of H.sub.3PO.sub.4 for 18 hours under reflux conditions (4.2 liter/1 kg of zeolite). Then the solid was separated by filtering from the solution. The obtained solid was dried first at 110 C. for 16 hours and then at 400 C. for 3 hours. The dried solid was subjected to reflux conditions for 2 h in contact with a hot 0.1-M calcium acetate aqueous solution. Then the solid was separated by filtering from the solution and dried immediately at 110 C. for 16 hours and steamed at 600 C. for 2 hours in 100%. (Atomic ratio Si/Al 15, P-content 2.0 wt %).

(80) The sample is hereinafter identified as Comparative III.

Example 6

(81) A sample of zeolite ZSM-5 with Si/Al=13 synthesized without template has been obtained from TRICAT (TZP-302). This sample was steamed at 550 C. for 48 h in 100% steam. Then the steamed solid was treated with 3.14M solution of H.sub.3PO4 for 18 h under reflux condition (4.2 liter/1 kg of zeolite). Then the solid was separated by filtering from the solution, dried at 110 C. for 16 h and calcined at 400 C. for 10 h.

(82) The sample is hereinafter identified as Comparative IV.

Example 7

(83) A sample identified hereinafter as SAMPLE B was prepared by mechanically blending 90 wt % of the solid described in example 6 and 10 wt % of xonotlite (Ca.sub.6Si.sub.6O.sub.17(OH).sub.2).

Example 8

(84) XTO Process

(85) Catalyst tests were performed on 2 g catalyst samples with a pure methanol feed in a fixed-bed, down flow stainless-steel reactor. Catalyst powders was pressed into wafers and crushed to 35-45 mesh particles. Prior to the catalytic runs all catalysts were heated in flowing N.sub.2 (5 NI/h) up to the reaction temperature. Analysis of the products was performed on-line by a gas chromatograph equipped with a capillary column. The table below presents the average catalytic performance during the cycle (from 2 to 6 h on TOS) at substantially full methanol conversion. The results are displayed on a carbon, water-free basis. The values in Table I are the weight percent on a carbon basis. Conditions: WHSV=1.6 h.sup.1, P=1.5 bara, T=550 C.

(86) TABLE-US-00001 TABLE I Comparative I Comparative II Comparative III Sample A Methane 2.0 1.3 1.8 1.3 Paraffins 5.1 5.2 6.9 3.9 (non cyclic) Olefins 86.9 86.2 81.6 89.8 Aromatics 5.4 6.2 9.2 3.9 Ethylene 8.6 12.2 14.6 7.6 Propylene 42.5 42.2 39.4 44.3

Example 9

(87) Catalyst tests were performed under the same conditions as described in example 8 for catalyst composites Comparative IV and SAMPLE B. The results are shown in table II on a carbon, water-free basis.

(88) TABLE-US-00002 TABLE II Comparative IV SAMPLE B Methane 2.0 2.0 Paraffins 6.0 5.0 (non cyclic) Olefins 86.0 87.0 Ethylene 6.8 9.4 Propylene 37.8 42.2