Grain-oriented electrical steel sheet and manufacturing method thereof

Abstract

A grain-oriented electrical steel sheet to which electron beam irradiation is applied, has a film and a thickness of t (mm), wherein no rust is produced on a surface of the steel sheet after a humidity cabinet test lasting 48 hours at a temperature of 50 C. in an atmosphere of 98% humidity, and iron loss W.sub.17/50 after the electron beam irradiation is reduced by at least (500 t.sup.2+200 t6.5) % of the iron loss W.sub.17/50 before the electron beam irradiation and is (5 t.sup.22 t+1.065) W/kg or less.

Claims

1. A grain-oriented electrical steel sheet to which electron beam irradiation is applied, having a film and a thickness of t (mm), wherein no rust is produced on a surface of the steel sheet after a humidity cabinet test lasting 48 hours at a temperature of 50 C. in an atmosphere of 98% humidity, and an iron loss W.sub.17/50 after the electron beam irradiation is reduced by at least (500 t.sup.2+200 t6.5) % of the iron loss W.sub.17/50 before the electron beam irradiation and is (5 t.sup.22 t+1.065) W/kg or less.

2. The grain-oriented electrical steel sheet according to claim 1, wherein the film includes a film formed from colloidal silica and phosphate, and a forsterite film that is a base film of the film formed from colloidal silica and phosphate.

3. A method of manufacturing a grain-oriented electrical steel sheet having a film, comprising: irradiating the grain-oriented electrical steel sheet with an electron beam in a direction intersecting a rolling direction, setting electron beam irradiation conditions such that an irradiation energy of the electron beam per unit area of 1 cm.sup.2 is 1.0 Z J to 3.5 Z J and the irradiation energy of the electron beam per unit irradiation length of 1 m is 105 Z J or less, where an irradiation time per irradiation interval d (mm) of the electron beam is s.sub.1 (ms), and Z =s.sub.1.sup.0.35.

4. The method according to claim 3, further comprising setting the irradiation interval d (mm) to 0.01 mm to 0.5 mm and setting the irradiation time s.sub.1 (ms) to 0.003 ms to 0.1 ms.

5. The method according to claim 3, wherein the film includes a film formed from colloidal silica and phosphate, and a forsterite film that is a base film of the film formed from colloidal silica and phosphate.

6. The method according to claim 4, wherein the film includes a film formed from colloidal silica and phosphate, and a forsterite film that is a base film of the film formed from colloidal silica and phosphate.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a graph illustrating the relationship between frequency and the maximum irradiation energy at which the number of generated rust spots is zero.

(2) FIG. 2 is a graph illustrating the effect of the irradiation energy per unit length on the corrosion resistance after electron beam irradiation at a frequency of 100 kHz.

(3) FIG. 3 is a graph illustrating the relationship between the amount of change in the iron loss W.sub.17/50 due to electron beam irradiation (iron loss after irradiationiron loss before irradiation) and the irradiation energy per unit area at a frequency of 100 kHz.

DETAILED DESCRIPTION

(4) The following describes our steel sheets and methods in detail.

(5) First, the manufacturing conditions of a grain-oriented electrical steel sheet are described.

(6) Any chemical composition that allows secondary recrystallization to proceed may be used as the chemical composition of a slab for a grain-oriented electrical steel sheet. The chemical composition may contain appropriate amounts of Al and N in the case where an inhibitor, e.g., an AlN-based inhibitor, is used or appropriate amounts of Mn and Se and/or S in the case where an MnS.MnSe-based inhibitor is used. Of course, these inhibitors may also be used in combination. In this case, preferred contents of Al, N, S and Se are: Al: 0.01 mass % to 0.065 mass %; N: 0.005 mass % to 0.012 mass %; S: 0.005 mass % to 0.03 mass %; and Se: 0.005 mass % to 0.03 mass %, respectively.

(7) Furthermore, our grain-oriented electrical steel sheets may have limited contents of Al, N, S and Se without using an inhibitor.

(8) In this case, the contents of Al, N, S and Se are preferably limited to Al: 100 mass ppm or less, N: 50 mass ppm or less, S: 50 mass ppm or less, and Se: 50 mass ppm or less, respectively.

(9) Other than the aforementioned components, specific examples of basic components and optionally added components of a slab for the grain-oriented electrical steel sheet are as follows.

(10) C: 0.08 Mass % or Less

(11) Carbon (C) is added to improve the texture of a hot-rolled sheet. However, to reduce the C content to 50 mass ppm or less during the manufacturing process, at which point magnetic aging will not occur, the C content is preferably 0.08 mass % or less. It is not necessary to set a particular lower limit to the C content because secondary recrystallization is enabled by a material not containing C.

(12) Si: 2.0 Mass % to 8.0 Mass %

(13) Silicon (Si) is an element effective in enhancing electrical resistance of steel and improving iron loss properties thereof. The Si content in steel is preferably 2.0 mass % or more to achieve a sufficient iron loss reduction effect. On the other hand, Si content above 8.0 mass % significantly deteriorates formability and also decreases the flux density of the steel. Therefore, the Si content is preferably 2.0 mass % to 8.0 mass %.

(14) Mn: 0.005 Mass % to 1.0 Mass %

(15) Manganese (Mn) is a necessary element to achieve better hot workability of steel. However, this effect is inadequate when the Mn content in steel is below 0.005 mass %. On the other hand, Mn content in steel above 1.0 mass % deteriorates magnetic flux of a product steel sheet. Accordingly, the Mn content is preferably 0.005 mass % to 1.0 mass %.

(16) Furthermore, in addition to the above basic components, the slab may also contain the following as elements to improve magnetic properties as deemed appropriate: at least one element selected from Ni: 0.03 mass % to 1.50 mass %, Sn: 0.01 mass % to 1.50 mass %, Sb: 0.005 mass % to 1.50 mass %, Cu: 0.03 mass % to 3.0 mass %, P: 0.03 mass % to 0.50 mass %, Mo: 0.005 mass % to 0.10 mass %, and Cr: 0.03 mass % to 1.50 mass %.

(17) Nickel (Ni) is an element useful to improve the texture of a hot rolled steel sheet for better magnetic properties thereof. However, Ni content in steel below 0.03 mass % is less effective in improving magnetic properties, while Ni content in steel above 1.50 mass % makes secondary recrystallization of the steel unstable, thereby deteriorating the magnetic properties thereof. Thus, Ni content is preferably 0.03 mass % to 1.50 mass %.

(18) In addition, tin (Sn), antimony (Sb), copper (Cu), phosphorus (P), molybdenum (Mo) and chromium (Cr) are useful elements in terms of improving magnetic properties of steel. However, each of these elements becomes less effective in improving magnetic properties of the steel when contained in steel in an amount less than the aforementioned lower limit and inhibits the growth of secondary recrystallized grains of the steel when contained in steel in an amount exceeding the aforementioned upper limit. Thus, each of these elements is preferably contained within the respective ranges thereof specified above.

(19) The balance other than the above-described elements is Fe and incidental impurities incorporated during the manufacturing process.

(20) Next, the slab having the above-described chemical composition is subjected to heating before hot rolling in a conventional manner. However, the slab may also be subjected to hot rolling directly after casting, without being subjected to heating. In the case of a thin slab or thinner cast steel, it may be subjected to hot rolling or directly proceed to the subsequent step, omitting hot rolling.

(21) Furthermore, the hot rolled sheet is optionally subjected to hot band annealing. At this time, to obtain a highly-developed Goss texture in a product sheet, a hot band annealing temperature is preferably 800 C. to 1100 C. If a hot band annealing temperature is lower than 800 C., there remains a band texture resulting from hot rolling, which makes it difficult to obtain a primary recrystallization texture of uniformly-sized grains and impedes the growth of secondary recrystallization. On the other hand, if a hot band annealing temperature exceeds 1100 C., the grain size after the hot band annealing coarsens too much, which makes it extremely difficult to obtain a primary recrystallization texture of uniformly-sized grains.

(22) After the hot band annealing, the sheet is subjected to cold rolling once, or twice or more with intermediate annealing performed therebetween, followed by recrystallization annealing and application of an annealing separator to the sheet. After application of the annealing separator, the sheet is subjected to final annealing for purposes of secondary recrystallization and formation of a forsterite film.

(23) After final annealing, it is effective to subject the sheet to flattening annealing to correct the shape thereof. Insulation coating is applied to the surfaces of the steel sheet before or after the flattening annealing. As used herein, insulation coating refers to coating that may apply tension to the steel sheet to reduce iron loss (hereinafter, referred to as tension coating). Any known tension coating used in a grain-oriented electrical steel sheet may be used similarly as the tension coating, yet a tension coating formed from colloidal silica and phosphate is particularly preferable. Examples include inorganic coating containing silica, and ceramic coating formed by physical deposition, chemical deposition, and the like.

(24) The grain-oriented electrical steel sheet after the above-described tension coating is subjected to magnetic domain refining treatment by irradiating the surfaces of the steel sheet with an electron beam under the conditions indicated below. The iron loss reduction effect can be fully achieved with electron beam irradiation while suppressing damage to the film.

(25) Next, the method of irradiation with an electron beam is described.

(26) First, the conditions to generate the electron beam are described.

(27) Acceleration Voltage: 40 kV to 300 kV

(28) A higher acceleration voltage is better. An electron beam generated at a high acceleration voltage tends to pass through matter, in particular material formed from light elements. In general, a forsterite film and a tension coating are formed from light elements and, therefore, if the acceleration voltage is high, the electron beam passes through them easily, making the film less susceptible to damage. A higher acceleration voltage above 40 kV is preferable since the irradiation beam current necessary to obtain the same output is low, and the beam diameter can be narrowed. Upon exceeding 300 kV, however, the irradiation beam current becomes excessively low, which may make it difficult to perform minute adjustments thereof.

(29) Irradiation Diameter: 350 m or Less

(30) At a large irradiation diameter exceeding 350 m, the heat affected region expands, which may cause iron loss (hysteresis loss) properties to deteriorate. Therefore, a value of 350 m or less is preferable. Measurement was made using the half width of a current (or voltage) curve obtained by a known slit method. While no lower limit is placed on the irradiation diameter, an excessively small value leads to an excessively high beam energy density, which makes it easier for damage to the film due to irradiation to occur. Therefore, the irradiation diameter is preferably set to approximately 100 m or more.

(31) Electron Beam Irradiation Pattern

(32) The irradiation pattern of the electron beam is not limited to a straight line. The steel sheet may be irradiated from one widthwise edge to the other widthwise edge in a regular pattern such as a wave or the like. A plurality of electron guns may also be used, with an irradiation region being designated for each gun.

(33) For irradiation in the widthwise direction of the steel sheet, a deflection coil is used, and irradiation is repeated along irradiation positions at a constant interval d (mm) with an irradiation time of s.sub.1. These irradiation points are referred to as dots. At this time, the constant interval d (mm) is preferably set within a predetermined range. This interval d is referred to as dot pitch. Since the time in which the electron beam traverses the interval d is extremely short, the inverse of s.sub.1can be considered as the irradiation frequency.

(34) Furthermore, the above irradiation from one widthwise edge to the other widthwise edge is repeated in a direction intersecting the rolling direction of the irradiated material with a constant interval between repetitions. This interval is referred to below as line spacing. With respect to a direction perpendicular to the rolling direction of the steel plate, the irradiation direction preferably forms an angle of approximately 30.

(35) Irradiation Time Per Dot (Inverse of Irradiation Frequency) s.sub.1: 0.003 ms to 0.1 ms (3 s to 100 s)

(36) If the irradiation time s.sub.1 is less than 0.003 ms, a sufficient heat effect cannot be obtained for the steel substrate, and iron loss properties might not improve. On the other hand, with a time of longer than 0.1 ms, the irradiated heat becomes dispersed throughout the steel and the like during the irradiation time. Therefore, even if the irradiation energy per dot expressed as VIs.sub.1 is constant, the maximum attained temperature of the irradiated portion tends to decrease, and the iron loss properties might deteriorate. Accordingly, the irradiation time s.sub.1 is preferably 0.003 ms to 0.1 ms. V represents the acceleration voltage, and I represents the beam current.

(37) Dot Pitch (d): 0.01 mm to 0.5 mm

(38) A dot pitch wider than 0.5 mm causes portions of the steel substrate not to receive the heat effect. The magnetic domain is therefore not sufficiently refined, and the iron loss properties might not improve. On the other hand, at a dot pitch narrower than 0.01 mm, the irradiation speed reduces excessively, causing irradiation efficiency to drop. Accordingly, the dot pitch is preferably 0.01 mm to 0.5 mm.

(39) Line Spacing: 1 mm to 15 mm

(40) If the line spacing is narrower than 1 mm, the heat affected region expands, which may cause iron loss (hysteresis loss) properties to deteriorate. On the other hand, if the line spacing is wider than 15 mm, magnetic domain refining is insufficient, and the iron loss properties tend not to improve. Accordingly, the line spacing is preferably 1 mm to 15 mm.

(41) Pressure in Pressure Chamber: 3 Pa or Less

(42) If the pressure in the pressure chamber is higher than 3 Pa, electrons generated from the electron gun scatter, and the electron energy that provides the heat effect to the steel substrate reduces. As a result, magnetic domain refining is not sufficiently achieved, and iron loss properties might not improve. No particular lower limit is established, and a lower pressure in the pressure chamber is better.

(43) With respect to focusing current, it goes without saying that the focusing current is adjusted in advance so that the beam is uniform in the widthwise direction when irradiating by deflecting in the widthwise direction. For example, applying a dynamic focus function (see JP '852) presents no problem whatsoever.

(44) Irradiation Energy Per Unit Irradiation Length of 1 m of Electron Beam: 105 Z J or Less

(45) Z is a value representing s.sub.1.sup.0.35 or the irradiation frequency (kHz) raised to the 0.35 power. In general, as the irradiation energy per unit length in the widthwise direction of the steel sheet is higher, magnetic domain refining progresses, and eddy current loss decreases. When irradiating with excessive energy, however, not only does hysteresis loss increase, but also the beam irradiated portion reaches an excessively high temperature, causing damage to the film. Therefore, as explained below, a certain value (105 Z J/m) or less is an adequate condition. As long as the magnetic domain refining effect is obtained, no particular lower limit is established, yet a lower limit of approximately 60 Z J/m is preferable.

(46) Furthermore, the magnetic domain refining and damage to the film due to heat irradiation are presumably influenced by the maximum attained temperature of the irradiated portion, the resulting amount of expansion of the iron and the like. When the frequency is low, i.e., when s.sub.1 is large, and thermal diffusion throughout the steel during irradiation is pronounced so that the irradiated portion does not reach a high temperature, it should be noted that unless a larger amount of energy is irradiated, iron loss will therefore not be reduced and, moreover, damage to the film might not occur.

(47) We derived the value of Z based on experiments.

(48) Specifically, ten 0.23 mm thick sheets with a tension coating were prepared under the same conditions as the Examples described below, and electron beam irradiation was performed at the frequencies listed in Table 1. The minimum irradiation energy was also obtained when, for even one sample, the visually confirmed number of generated rust spots was zero after a humidity cabinet test to expose the samples for 48 hours at a temperature of 50 C. in a humid environment of 98% humidity. The results are listed in Table 1.

(49) The results for the maximum irradiation energy were plotted as a graph, shown in FIG. 1. As illustrated in FIG. 1, curve fitting was performed with the method of least squares to derive the above-described upper limit (105 Z J/m).

(50) TABLE-US-00001 TABLE 1 Frequency Irradiation energy per unit length at which the (kHz) number of generated rust spots is zero (J/m) 12.5 44 50 26 100 19 200 17 250 15 300 14

(51) Letting L (m) be the length of the straight line or curve exposed to electron beam irradiation from one widthwise edge of the steel sheet to the other widthwise edge, the energy per unit length is defined as all of the energy irradiated in the region, divided by L.

(52) FIG. 2 illustrates the effect of the irradiation energy per unit length on the corrosion resistance after irradiation with an electron beam at a frequency of 100 kHz. The electron beam irradiation conditions were an acceleration voltage of 60 kV, dot pitch of 0.35 mm, and line spacing of 5 mm. On samples with a shape of 5 cm10 cm and a sheet thickness of 0.23 mm, a humidity cabinet test was performed to expose the samples for 48 hours at a temperature of 50 C. in a humid environment of 98% humidity, after which the amount of rust generated on the electron beam irradiation surface was visually measured for evaluation as the number of spots generated per unit area.

(53) As a result, we confirmed that by lowering the irradiation energy per unit length, the amount of rust generated can be suppressed. Note that in FIG. 2, the data width in the vertical axis direction represents the maximum and minimum values during measurement for N equal to 10. This shows that by setting the irradiation energy per unit length to 105 Z=21 J/m or less, the generation of rust is effectively suppressed.

(54) Irradiation Energy Per Unit Area (1 cm.sup.2) of Irradiated Material: 1.0 Z J to 3.5 Z J

(55) When considering the effect that the frequency of irradiation has on iron loss, an effect on the maximum attained temperature of the irradiated portion, for example, can be presumed as described above. Therefore, Z is also useful when deriving the irradiation energy to optimize iron loss properties.

(56) Table 2 lists the minimum and maximum irradiation energy for which the iron loss reduction ratio is 13% or more (iron loss reduction amount of 0.13 W/kg or more). Considering the results, the irradiation energy of the electron beam that optimizes iron loss properties is derived as being from Z to 3.5 Z per unit area of 1 cm.sup.2.

(57) TABLE-US-00002 TABLE 2 Minimum irradiation Maximum irradiation energy for which iron loss energy for which iron Frequency reduction amount loss reduction amount (kHz) is 0.13 W/kg or more (J/cm.sup.2) is 0.13 W/kg or more (J/cm.sup.2) 12.5 0.40 1.40 50 0.25 0.90 100 0.21 0.70 200 0.15 0.54 250 0.15 0.50 300 0.14 0.49

(58) To set the iron loss reduction ratio W (%) at iron loss W.sub.17/50 to 13% (corresponding to an iron loss reduction amount of 0.13 W/kg in the steel sheet used in the present experiment) or more, which is a higher value than the 12% disclosed in JP '654, the range of the irradiation energy per unit area was set, and treating the range as proportional to Z, the proportional coefficient was calculated. For the samples used to calculate the results in Table 2, the flux density B.sub.8 before irradiation was from 1.90 T to 1.92 T.

(59) FIG. 3 illustrates the relationship between the amount of change in the iron loss W.sub.17/50 due to electron beam irradiation (iron loss after irradiationiron loss before irradiation) and the irradiation energy per unit area at a frequency of 100 kHz. FIG. 3 confirms that when the irradiation energy of the electron beam is from 1.0 Z to 3.5 Z (0.2 to 0.7) J/cm.sup.2, iron loss is reduced. We discovered for the first time during the above-described experiment that, as illustrated in FIG. 3, the amount of change in the iron loss W.sub.17/50 does not depend on the energy adjustment method such as the irradiation line spacing, the dot pitch, or the beam current, but rather can be regulated with the irradiation energy per unit area. Note that irradiation at this time was performed under the above conditions to generate the electron beam. The irradiation energy per unit area is the total amount of energy irradiated over an area of the sample used for magnetic measurement divided by the area.

(60) By satisfying each of the above conditions, a grain-oriented electrical steel sheet can be obtained for which the iron loss reduction effect due to the electron beam irradiation can be sufficiently achieved, while damage to the film is suppressed and corrosion resistance is maintained.

(61) The characteristics of the grain-oriented electrical steel sheet are described below: Iron loss reduction ratio W (%): (500 t.sup.2+200 t6.5) % or more Iron loss W.sub.17/50 after irradiation: (5 t.sup.22 t+1.065) W/kg or less.

(62) With conventional techniques as well, if irradiation with an electron beam is performed under conditions in which the iron loss reduction effect is weak, no damage to the film occurs and, therefore, cannot be discussed without reference to the iron loss reduction effect.

(63) The iron loss reduction ratio W (%) prescribed in the experiment is, for a sheet thickness of 0.23 mm, set to 13% or more, a higher value than the 12% disclosed in JP '654, as described above. In this case, the iron loss reduction ratio is affected by the sheet thickness t (mm), yet in FIG. 4 of Ichijima et al., the iron loss reduction ratio is W=500 t.sup.2+200 t (: 7.5 to 9) and, therefore, the higher iron loss reduction ratio of (500 t.sup.2+200 t6.5) % or more was set as the iron loss reduction ratio prescribed. Since the iron loss before irradiation for the material used in the experiment was 0.86 W/kg to 0.88 W/kg, a reduction of 13% corresponds to a reduction of 0.11 W/kg in terms of the absolute value of the reduction amount.

(64) The iron loss before irradiation strongly affects the iron loss reduction amount and, therefore, in the experiment, the iron loss reduction amount is confined to the above narrow range. Realistically, however, the iron loss of the grain-oriented electrical steel sheet before the electron beam irradiation is approximately 1.0 W/kg for high-quality material (for a sheet thickness of 0.23 mm). When the above (500 t.sup.2+200 t6.5) % iron loss reduction is performed on this electrical steel sheet, the iron loss is (5 t.sup.22 t+1.065) W/kg for W.sub.17/50, and, therefore, the iron loss achieved is limited to a range equal to or less than this value. For material with an iron loss before irradiation of less than 1.0 W/kg, the iron loss after electron beam irradiation may of course be less than (5 t.sup.22 t+1.065) W/kg as long as the iron loss is reduced by (500 t.sup.2+200 t6.5) %.

(65) Determination of film rupture is made by performing a humidity cabinet test, which is a type of corrosion resistance test such as the one described above and quantifying the amount of generated rust appearing along the irradiated portion. Specifically, test pieces after electron beam irradiation were exposed for 48 hours in an environment at a temperature of 50 C. and 98% humidity, and it was determined whether rust was generated on the surface of the steel sheets, in particular in the region affected by heat from the electron beam. The determination of whether rust was generated was made visually by checking for a change in color, and the amount was evaluated as the number of spots generated per unit area. When rust generation was pronounced, however, and rust in one location covered a wide region, the amount was evaluated as the rust generation area ratio.

(66) Other than the above-described steps and manufacturing conditions, a conventionally known method of manufacturing a grain-oriented electrical steel sheet subjected to magnetic domain refining treatment using an electron beam may be adopted.

EXAMPLES

(67) A steel slab containing the chemical composition shown in Table 3 was produced by continuous casting and heated to 1430 C. and subjected to hot rolling to form a hot rolled steel sheet having a sheet thickness of 1.6 mm. The hot rolled steel sheet thus obtained was then subjected to hot band annealing at 1000 C. for 10 seconds. The steel sheet was then subjected to cold rolling to have a sheet thickness of 0.55 mm. The cold rolled steel sheet thus obtained was subjected to intermediate annealing under the conditions of a degree of atmospheric oxidation PH.sub.2O/PH.sub.2 of 0.37, a temperature of 1100 C., and a duration of 100 seconds. Subsequently, each steel sheet was subjected to hydrochloric acid pickling to remove subscales from the surfaces thereof, followed by cold rolling again to be finished to a cold-rolled sheet having a sheet thickness of 0.20 mm to 0.30 mm.

(68) TABLE-US-00003 TABLE 3 Chemical composition O N Al Se S C (mass Ni (mass (mass (mass (mass (mass ppm) Si (mass %) Mn (mass %) (mass %) ppm) ppm) ppm) ppm) ppm) 500 2.95 0.1 0.01 25 65 250 105 30

(69) Then, each steel sheet was subjected to decarburization by being kept at a degree of atmospheric oxidation PH.sub.2O/PH.sub.2 of 0.45 and a soaking temperature of 850 C. for 150 seconds. An annealing separator composed mainly of MgO was then applied to each steel sheet. Thereafter, each steel sheet was subjected to final annealing for the purposes of secondary recrystallization and purification under the conditions of 1180 C. and 60 hours.

(70) In this final annealing, the average cooling rate during a cooling process at a temperature range of 700 C. or higher was varied. A tension coating composed of 50% of colloidal silica and magnesium phosphate was then applied to each steel sheet, and the iron loss was measured. The iron loss was as follows: eddy current loss (1.7 T, 50 Hz) was 0.54 W/kg to 0.55 W/kg (sheet thickness: 0.20 mm), 0.56 W/kg to 0.58 W/kg (sheet thickness: 0.23 mm), 0.62 W/kg to 0.63 W/kg (sheet thickness: 0.27 mm), and 0.72 W/kg to 0.73 W/kg (sheet thickness: 0.30 mm).

(71) Subsequently, magnetic domain refining treatment was performed by irradiating with an electron beam under the irradiation conditions listed in Table 4 (in terms of s.sub.1, in a range of 0.001 ms to 0.08 ms), iron loss was measured, and the number of generated rust spots after exposure for 48 hours at a temperature of 50 C. in a humid environment of 98% humidity was visually measured.

(72) Table 5 lists the measurement results.

(73) TABLE-US-00004 TABLE 4 Pressure in Irradiation Irradiation Sheet Acceleration Irradiation Irradiation Line pressure energy per energy per thickness voltage current diameter Dot pitch d spacing chamber Irradiation unit length unit area No. (mm) (V) (mA) (m) Frequency (kHz) (mm) (mm) (Pa) pattern (J/m) (J/cm.sup.2) 1 0.23 60 12 205 100 0.30 5.0 0.5 linear 24 0.48 2 0.23 60 8 200 100 0.30 3.0 2.4 linear 16 0.53 3 0.23 60 3.2 190 12.5 0.35 5.0 0.4 linear 44 0.88 4 0.23 60 1.2 180 12.5 0.35 3.5 0.06 linear 16 0.47 5 0.23 40 4.2 195 12.5 0.30 5.0 0.02 linear 45 0.90 6 0.23 40 1.4 180 12.5 0.30 2.8 2.0 linear 15 0.53 7 0.23 150 4.5 195 100 0.25 5.0 0.05 linear 27 0.54 8 0.23 150 2.5 195 100 0.25 2.8 0.05 linear 15 0.54 9 0.23 60 12 205 1000 0.03 5.0 0.5 linear 24 0.48 10 0.23 60 8 200 1000 0.06 3.5 2.4 linear 8 0.23 11 0.23 60 4.5 190 50 0.20 10.0 0.5 linear 27 0.27 12 0.23 60 4.5 200 100 0.20 3.5 2.4 linear 14 0.39 13 0.23 60 7 190 100 0.25 6.0 2.4 sinusoidal 17 0.53 14 0.20 60 7 190 100 0.35 3.3 1.2 linear 12 0.69 15 0.27 60 7 190 100 0.35 3.3 1.5 linear 12 0.69 16 0.27 60 11 200 100 0.30 6.0 1.0 linear 22 0.70 17 0.30 60 7 190 100 0.35 3.3 2.2 linear 12 0.69

(74) TABLE-US-00005 TABLE 5 Iron loss Number of W.sub.17/50 W.sub.17/50 reduction Iron loss generated Sheet before after amount reduction rust spots thickness irradiation irradiation W.sub.17/50 ratio per unit area No. (mm) (W/kg) (W/kg) (W/kg) W (%) (number/cm.sup.2) Notes 1 0.23 0.862 0.713 0.149 17 1.5 Comparative Example 2 0.23 0.876 0.723 0.153 17 0 Example 3 0.23 0.872 0.729 0.143 16 1.4 Comparative Example 4 0.23 0.874 0.721 0.153 18 0 Example 5 0.23 0.871 0.720 0.151 17 1.7 Comparative Example 6 0.23 0.861 0.708 0.153 18 0 Example 7 0.23 0.872 0.717 0.155 18 1.8 Comparative Example 8 0.23 0.861 0.701 0.160 19 0 Example 9 0.23 0.869 0.723 0.146 17 1.4 Comparative Example 10 0.23 0.864 0.718 0.146 17 0 Example 11 0.23 0.876 0.752 0.124 14 1.6 Comparative Example 12 0.23 0.878 0.732 0.146 17 0 Example 13 0.23 0.863 0.705 0.158 18 0 Example 14 0.20 0.852 0.678 0.174 20 0 Example 15 0.27 0.874 0.737 0.137 16 0 Example 16 0.27 0.874 0.730 0.144 16 1.5 Comparative Example 17 0.30 0.997 0.899 0.098 10 0 Example

(75) As shown in Table 5, by setting the electron beam irradiation conditions to 105 Z J/m or less per unit length and 1.0 Z to 3.5 Z J/cm.sup.2 per unit area yielded a low iron loss grain-oriented electrical steel sheet with an iron loss reduction ratio W of (500 t.sup.2+200 t6.5) % or more and an iron loss W.sub.17/50 of (5 t.sup.22 t+1.065) W/kg or less. Furthermore, the fact that no rust was generated after the humidity cabinet test indicated that corrosion resistance did not deteriorate due to electron beam irradiation.