Plastic working method of metals and plastic working apparatus

Abstract

Provided is a plastic working method of steel including austenite, the method including: analyzing a strain ratio x of an estimated breaking point which is specified during plastic deformation of the steel; heating a steel such that a local temperature T.sub.local is within a temperature range indicated by the following expression 1, when T.sub.x represents a strain-induced-transformation-maximum-ductility-temperature in the unit of C. for the strain ratio x, L.sub.x represents the standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio x on a lower temperature side than T.sub.x, H.sub.x represents the standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio x on a higher temperature side than T.sub.x, and T.sub.local represents a local temperature in the unit of C. of the estimated breaking point; and plastically deforming the steel after heating:
T.sub.x2L.sub.xT.sub.localT.sub.x+1.25H.sub.x(Expression 1).

Claims

1. A plastic working method of steel including austenite, the method comprising: physical property analyzing process of measuring T.sub., L.sub., and H.sub. for each of strain ratios , when T.sub. represents a strain-induced-transformation-maximum-ductility-temperature in the unit of C. which is changed depending on the strain ratio , L.sub. represents a standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio on a lower temperature side than the T.sub., H.sub. represents a standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio on a higher temperature side than the T.sub.; deformation mode analyzing process of analyzing a strain ratio x to be selected from among the strain ratios , when the strain ratio x is a strain ratio of an estimated breaking point which is specified during plastic deformation of the steel; heating process of heating the steel such that a local temperature T.sub.local is within a first temperature range indicated by the following expression 1 after selecting T.sub.x from among the T.sub., selecting L.sub.x from among the L.sub., and selecting H.sub.x from among the H.sub., when T.sub.x represents a strain-induced-transformation-maximum-ductility-temperature in the unit of C. for the strain ratio x, L.sub.x represents a standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio x on a lower temperature side than the T.sub.x, H.sub.x represents a standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio x on a higher temperature side than the T.sub.x, and the T.sub.local represents a local temperature ( C.) of the estimated breaking point; and working process of plastically deforming the steel after the heating:
T.sub.xL.sub.xT.sub.localT.sub.x+1.25H.sub.x(Expression 1).

2. The plastic working method according to claim 1, wherein in the deformation mode analyzing process, a change in temperature T.sub.local is further analyzed, when the T.sub.local represents a change in temperature in the unit of C. of the local temperature T.sub.local which is changed during the plastic deformation of the steel in the working process, and wherein in the heating process, heating is performed such that the local temperature T.sub.local is within a second temperature range indicated by the following expression 2:
T.sub.xT.sub.local2L.sub.xT.sub.localT.sub.xT.sub.local+1.25H.sub.x(Expression 2).

3. The plastic working method according to claim 1, wherein in the heating process, at least one of the steel, a mold, and a surrounding space around the steel is heated such that the local temperature T.sub.local is within the first temperature range.

4. The plastic working method according to claim 1, wherein in the heating process, a heating medium is heated such that the local temperature T.sub.local is within the first temperature range, and wherein in the working process, the steel is plastically deformed using a pressure of the heating medium.

5. The plastic working method according to claim 2, wherein in the physical property analyzing process, the estimated breaking point, the strain ratio x, and the change in temperature T.sub.local are analyzed using a plastic working simulation.

6. A plastic working apparatus which performs the plastic working method according to claim 1, the apparatus comprising: a housing unit that accommodates the steel and a mold; heating units that heat at least two of the steel, the mold, and a surrounding space around the steel; a working unit that plastically deforms the steel using the mold; and a main body frame, wherein the heating units include two or more selected from the group consisting of: a heater attached to the main body frame of the housing, a heater attached to an inside of the mold, and a heating furnace provided outside the plastic working apparatus.

7. The plastic working apparatus according to claim 6, further comprising an insulating member that is arranged to cover the housing unit.

8. The plastic working apparatus according to claim 6, further comprising a temperature measuring unit that measures respective temperatures of the steel, the mold, and an internal space of the housing unit.

9. A plastic working apparatus which performs the plastic working method according to claim 4, the apparatus comprising: a housing unit that accommodates the steel and a mold; a heating medium introducing unit that introduces the heating medium into the mold; heating units that heat at least two of the steel, the mold, and a surrounding space around the steel and the heating medium; a working unit that plastically deforms the steel using a pressure of the heating medium; and a main body frame, wherein the heating units include two or more selected from the group consisting of: a heater attached to the main body frame of the housing, a heater attached to an inside of the mold, a heating furnace provided outside the plastic working apparatus, and a heater configured to heat the heating medium.

10. The plastic working apparatus according to claim 9, further comprising an insulating member that is arranged to cover the housing unit.

11. The plastic working apparatus according to claim 9, further comprising a temperature measuring unit that measures respective temperatures of the steel, the mold, an internal space of the housing unit, and the heating medium.

Description

BRIEF DESCRIPTION OF THE DRAWING

(1) FIG. 1 is a schematic diagram showing the transformation induced plasticity phenomenon.

(2) FIG. 2 is a schematic diagram showing uniaxial tension, plane strain tension, and equal biaxial tension.

(3) FIG. 3 is a diagram showing a temperature dependence of a critical equivalent strain of low carbon steel at each strain ratio .

(4) FIG. 4 is a diagram showing a normal distribution fitted curve of the temperature dependence of the critical equivalent strain when =0 in FIG. 3.

(5) FIG. 5 is a partially cutaway front view showing a schematic configuration of a plastic working apparatus according to an embodiment of the present invention.

(6) FIG. 6 is a partially cutaway front view showing a schematic configuration of a plastic working apparatus according to another embodiment of the present invention.

(7) FIG. 7 is a schematic diagram showing forming by square cylinder drawing.

EMBODIMENTS OF THE INVENTION

(8) A plastic working method and a plastic working apparatus according to embodiments of the present invention will be described in detail. However, the present invention is not limited to the configurations of the following embodiments, and various modifications can be made within a range not departing from the scope of the present invention.

(9) First, a plastic working method according to an embodiment of the present invention will be described. In the plastic working method according to the embodiment, steel including austenite is used as a workpiece, and the transformation induced plasticity phenomenon exhibited in this steel is utilized to the maximum.

(10) Here, the transformation induced plasticity (TRIP) phenomenon will be described. FIG. 1 is a schematic diagram showing the TRIP phenomenon. As shown in FIG. 1, for example, when steel including austenite (TRIP steel) is tensely deformed, necking occurs after the deformation progresses to some extent. When necking occurs, a stress applied to a neck increases. Due to this stress, stress induced transformation (indicated by A in FIG. 1) in which retained austenite is transformed into martensite occurs. Since martensite has a higher strength than other microstructures, the neck is reinforced by the stress induced transformation compared to other regions, and the deformation of the neck does not progress. As a result, deformation in the vicinity regions of the neck, where has a relatively low strength, progresses. A phenomenon in which necking caused by stress induced transformation and suppression of deformation are repeated is referred to as the transformation induced plasticity (TRIP) phenomenon. As a result, the inside of a material is uniformly deformed, and superior ductility is obtained.

(11) However, the above-described TRIP phenomenon depends on temperature. Improvement of ductility by this TRIP phenomenon is obtained only in a specific temperature range. In addition, a temperature (hereinafter referred to as strain-induced-transformation-maximum-ductility-temperature) at which maximum ductility is obtained by the TRIP phenomenon (stress induced transformation) depends on a chemical structure and a metallographic structure of TRIP steel. Further, as a result of a thorough study, the present inventors found that this strain-induced-transformation-maximum-ductility-temperature has a strain ratio dependency (plastic deformation mode dependency) in which a value thereof is changed by a strain ratio (plastic deformation mode) during plastic deformation.

(12) The strain ratio described herein is expressed by, when biaxial strains in a biaxial stress state are a maximum principal strain e, and a minimum principal strain .sub.2, =.sub.2.sub.1. In this expression, .sub.1.sub.2. In particularly, a state where =0.5 is referred to as a uniaxial tension state, a state where =0 is referred to as a plane strain tension state, and a state where =1.0 is referred to as an equal biaxial tension state. FIG. 2 is a schematic diagram showing uniaxial tension, plane strain tension, and equal biaxial tension. As shown in FIG. 2, uniaxial tension where =0.5 is a deformation mode where steel is stretched in a .sub.1 direction and is compressed in a .sub.2 direction in the FIG. 2, and this deformation mode corresponds to plastic working such as draw forming. Plane strain tension where =0 is a deformation mode where steel is stretched in the .sub.1 direction and is not deformed in the .sub.2 direction in the FIG. 2, and this deformation mode corresponds to plastic working such as bending. Equal biaxial tension where =1.0 is a deformation mode where steel is stretched in the .sub.1 direction and is stretched in the .sub.2 direction in the FIG. 2, and this deformation mode corresponds to plastic working such as stretch forming.

(13) In order to effectively utilize the TRIP phenomenon to improve plastic deformability, it is necessary that both factors be considered at the same time, the factors including: the strain-induced-transformation-maximum-ductility-temperature which is a value unique to each type of steel; and the strain ratio (plastic deformation mode) during plastic deformation which affects this strain-induced-transformation-maximum-ductility-temperature. However, in the above-described conventional technology of the related art, these factors are not considered. The strain-induced-transformation-maximum-ductility-temperature is a value which depends on the strain ratio and thus, hereinafter, will be represented by T.sub.. For example, when the strain ratio is 0.5, the strain-induced-transformation-maximum-ductility-temperature thereof will be represented by T.sub.0.5.

(14) FIG. 3 shows the temperature dependence of a critical equivalent strain .sub.eq-critical at each strain ratio when low carbon steel is examined. In FIG. 3, a square-dot line indicates the results of =0.5, a triangle-two dot chain line indicates the results of =0, and a circle-solid line indicates the results of =1.0. In addition, an equivalent strain c refers to a strain which is calculated from the following expression A when biaxial strains in a biaxial stress state are a maximum principal strain .sub.1 and a minimum principal strain .sub.2. This equivalent strain .sub.eq refers to an equivalent uniaxial stress-strain component which is converted from a stress-strain component in the multiaxial stress state. This equivalent strain .sub.eq is used to compare different plastic deformation modes, that is, to compare plastic deformability (ductility) at different strain ratios . The critical equivalent strain .sub.eq-critical refers to an equivalent strain .sub.eq at which breaking occurs in steel as a workpiece.
.sub.eq={4+3(.sub.1.sup.2+.sub.2.sup.2+.sub.1.sub.2)}.sup.1.2(Expression A)
As shown in FIG. 3, the values of the critical equivalent strain .sub.eq-critical (ductility) increase in a specific temperature range. As described above, this improvement of ductility is caused by the TRIP phenomenon. In this way, the improvement of ductility by the TRIP phenomenon depends on temperature. For example, when =0.5, a strain-induced-transformation-maximum-ductility-temperature T.sub.0.5 is 150 C., and the critical equivalent strain at this temperature is the highest value.

(15) In addition, FIG. 3 shows that the strain-induced-transformation-maximum-ductility-temperature T.sub. is changed depending on the strain ratio . For example, as described above, when =0.5, a strain-induced-transformation-maximum-ductility-temperature T.sub.0.5 is 150 C., but, when =0, a strain-induced-transformation-maximum-ductility-temperature T.sub.0 is 200 C.; and when =1.0, a strain-induced-transformation-maximum-ductility-temperature T.sub.1.0 is 250 C. In this way, the strain-induced-transformation-maximum-ductility-temperature T.sub. depends on the strain ratio .

(16) In FIG. 4, the temperature dependence of the critical equivalent strain .sub.eq-critical when =0 in FIG. 3 is indicated by a two-dot chain line, and a fitted curve which is plotted on the assumption that the temperature dependence follows a normal distribution curve is indicated by a dot line. As described above, when the strain ratio is 0, a temperature at which the critical equivalent strain .sub.eq-critical is improved to the highest value due to the TRIP phenomenon is 200 C. which is the strain-induced-transformation-maximum-ductility-temperature T.sub.0. However, as shown in FIG. 4, a temperature at which the critical equivalent strain .sub.eq-critical is improved has a specific range. This temperature range in which the critical equivalent strain .sub.eq-critical is improved can be obtained from the fitted curve which is plotted on the assumption that the temperature range follows the normal distribution curve indicated by the dot line in FIG. 4.

(17) A method of obtaining the temperature range, in which the critical equivalent strain .sub.eq-critical is improved by the above-described TRIP phenomenon, from the fitted curve (approximate function) will be described below. First, on the assumption that the temperature dependence of the critical equivalent strain .sub.eq-critical follows the normal distribution curve, the temperature dependence is approximated to a probability density function represented by the following expressions B and C. Here, the following expression B in which represents the strain ratio expresses an approximate function (fitted curve of critical equivalent strain which depends on the strain ratio on a lower temperature side than T.sub.) of the temperature dependence of the critical equivalent strain .sub.eq-critical on a lower temperature side than the strain-induced-transformation-maximum-ductility-temperature T.sub. at which the critical equivalent strain .sub.eq-critical is improved to the highest value. The following expression C in which represents the strain ratio expresses an approximate function (fitted curve of critical equivalent strain which depends on the strain ratio on a higher temperature side than T.sub.) of the temperature dependence of the critical equivalent strain .sub.eq-critical on a higher temperature side than the strain-induced-transformation-maximum-ductility-temperature T.sub. at which the critical equivalent strain .sub.eq-critical is improved to the highest value. In the expressions B and C, the respective symbols denote the following:

(18) .sub.eq-critical: critical equivalent strain

(19) T: temperature

(20) T.sub.: strain-induced-trans formation-maximum-ductility-temperature

(21) L.sub.: standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio on a lower temperature side than T.sub.

(22) H.sub.: standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio on a higher temperature side than T.sub.

(23) e: natural logarithm

(24) : circular constant

(25) C.sub.1 to C.sub.4: constant

(26) $\begin{array}{cc}{\mathrm{.Math.}}_{\mathrm{eq}-\mathrm{critical}}=C_1.Math.\frac{1}{\sqrt{2}.Math.L_{}}{}^{-\frac{{\left(T-T_{}\right)}^2}{2L_{}^2}}+C_2& \left(\mathrm{Expression}B\right)\\ {\mathrm{.Math.}}_{\mathrm{eq}-\mathrm{critical}}=C_3.Math.\frac{1}{\sqrt{2}.Math.H_{}}{}^{-\frac{{\left(T-T_{}\right)}^2}{2H_{}^2}}+C_4& \left(\mathrm{Expression}C\right)\end{array}$

(27) When the mathematical definition of the probability density function is taken into consideration, the temperature range in which the critical equivalent strain .sub.eq-critical is improved by the TRIP phenomenon can be expressed using L.sub. and H.sub. described above. That is, this temperature range can be expressed by, for example, (T.sub.3L.sub.) to (T.sub.+3H.sub.), (T.sub.2L.sub.) to (T.sub.+2H.sub.), or (T.sub.L.sub.) to (T.sub.+H.sub.). Here, the range of (T.sub.3L.sub.) to (T.sub.+3H.sub.) mathematically represents an integrated value of the probability density function being 0.9974, the range of (T.sub.2L.sub.) to (T.sub.+2H.sub.) mathematically represents an integrated value of the probability density function being 0.9544, and the range of (T.sub.L.sub.) to (T.sub.+H.sub.) mathematically represents an integrated value of the probability density function being 0.6826.

(28) In this way, the temperature range in which the critical equivalent strain .sub.eq-critical is improved by the TRIP phenomenon can be expressed using L.sub. and H.sub. which are the standard deviations of the fitted curve (fitted curve of critical equivalent strain) which is plotted on the assumption that the temperature range follows the normal distribution curve. The values of L.sub. and H.sub. depend on the strain ratio . Hereinafter, for example, when the strain ratio is 0. L.sub. and H.sub. will be represented by L.sub.0 and H.sub.0. When =0, as shown in FIG. 4, the strain-induced-transformation-maximum-ductility-temperature T.sub.0 is 200 C., and L.sub.0 is 55 C. and H.sub.0 is 19 C. as a result of analyzing the fitted curve. The analysis of the fitted curve for obtaining L.sub. and H.sub. can be performed using a general data analysis and graph making application or a spread sheet application having a general making function of graph.

(29) In FIG. 4, for example, the temperature range in which the critical equivalent strain .sub.eq-critical is improved by the TRIP phenomenon can be expressed as 35 C. to 257 C. in the case of (T.sub.03L.sub.0) to (T.sub.0+3H.sub.0), 90 C. to 238 C. in the case of (T.sub.02L.sub.0) to (T.sub.0+2H.sub.0), 145 C. to 219 C. in the case of (T.sub.0L.sub.0) to (T.sub.0+H.sub.0), or the like. However, as a result of a thorough study on various steels and various strain ratios, the present inventors found that, when (T.sub.2L.sub.) to (T.sub.+1.25H.sub.) is adopted as the temperature range, the temperature range in which the critical equivalent strain .sub.eq-critical is improved by the above-described TRIP phenomenon can be preferably expressed without excess and deficiency. Accordingly, in the plastic working method according to the embodiment, (T.sub.2L.sub.) to (T.sub.+1.25H.sub.) is adopted as the temperature range in which the critical equivalent strain .sub.eq-critical is improved by the above-described TRIP phenomenon. Otherwise, optionally, the lower limit of this temperature range may be set as (T.sub.1.75L.sub.), (T.sub.1.5L.sub.), or (T.sub.1.25L.sub.). Likewise, the upper limit of this temperature range may be set as (T.sub.+1.20H.sub.), (T.sub.+1.15H.sub.), or (T.sub.1010L.sub.).

(30) When the strain ratio is 0, and when the temperature range is set as (T.sub.2L.sub.0) to (T.sub.+1.25H.sub.0), the temperature range in which the critical equivalent strain .sub.eq-critical is improved by the above-described TRIP phenomenon is 90 C. to 223.75 C. That is, it can be seen that, in the case of low carbon steel, plastic working needs to be performed in a temperature range of 90 C. to 223.75 C. to improve plastic deformability in a plastic deformation mode where the strain ratio is 0.

(31) It can be seen from above that the following plastic working method needs to be adopted in order to form steel (TRIP steel) including austenite as a workpiece while suppressing necking or breaking to the maximum. This method may include: (1) previously measuring the strain-induced-transformation-maximum-ductility-temperature T.sub. ( C.) of steel, which is a workpiece, at each of strain ratios , measuring the standard deviation L.sub. of the fitted curve of critical equivalent strain which depends on the strain ratio on a lower temperature side than T.sub. as the standard of T.sub., and measuring the standard deviation H.sub. of the fitted curve of critical equivalent strain which depends on the strain ratio on a higher temperature side than T.sub. as the standard of T.sub.; (2) previously specifying a plastic deformation mode of a local region of the steel where necking or breaking is most likely to occur during forming, that is, specifying a strain ratio x of this local region; (3) controlling the temperature of the local region to be within a temperature range (T.sub.x2L.sub.x) to (T.sub.x+1.25H.sub.x) suitable for the strain ratio x; and (4) plastic working of the steel is performed under conditions where the temperature of the local region is within this temperature range. In this range, x represents the strain ratio being x (=); T.sub.x represents a strain-induced-transformation-maximum-ductility-temperature when the strain ratio is x; L.sub. represents a standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio x on a lower temperature side than T.sub.x as the standard of T.sub.x; and H.sub.x represents a standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio x on a higher temperature side than T.sub.x as the standard of T.sub.x. T.sub.x, L.sub.x, and H.sub.x are previously measured for each of the strain ratios and are included in T.sub., L.sub., and H.sub.. Accordingly, methods of measuring and analyzing T.sub.x, L.sub.x, and H.sub.x are the same as those of T.sub., L.sub., and H.sub..

(32) Specifically, in the plastic working method according to the embodiment, steel including austenite is used as a workpiece, the method including: a physical property analyzing process of measuring T.sub., L.sub., and H.sub. for each of strain ratios , when T.sub. represents a strain-induced-transformation-maximum-ductility-temperature of the steel in the unit of C. which is changed depending on the strain ratio . L.sub. represents a standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio on a lower temperature side than T.sub., and H.sub. represents a standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio on a higher temperature side than T.sub.; a deformation mode analyzing process of analyzing a strain ratio x to be selected from among the strain ratios , when the strain ratio x is a strain ratio of an estimated breaking point which is specified during plastic deformation of the steel; a heating process of heating a steel such that a local temperature T.sub.local is within a first temperature range indicated by the following expression D after selecting the T.sub.x from among the T.sub., selecting the L.sub.x from among the L.sub., and selecting the H.sub.x from among the H.sub. respectively, when T.sub.x represents a strain-induced-transformation-maximum-ductility-temperature of the steel in the unit of C. for the strain ratio x, L.sub.x represents a standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio x on a lower temperature side than T.sub.x, H.sub.x represents the standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio pix on a higher temperature side than T.sub.s, and T.sub.local represents a local temperature in the unit of C. of the estimated breaking point; and a working process of plastically deforming the steel after the heating process.
T.sub.x2L.sub.xT.sub.localT.sub.x+1.25H.sub.x(Expression D).

(33) In the physical property analyzing process, the strain-induced-transformation-maximum-ductility-temperature of the steel in the unit of C. used as the workpiece at each of the strain ratios is measured. A method of measuring the strain-induced-transformation-maximum-ductility-temperature T.sub. is not particularly limited. For example, a spherical stretch forming test in which an end of a test piece is fixed while changing the horizontal and vertical dimension of the test piece may be performed at each temperature. The temperature at which the critical equivalent strain .sub.eq-critical (ductility) is improved to the highest value is set as the strain-induced-transformation-maximum-ductility-temperature T.sub. at the strain ratio thereof. Next, for each of the steel ratios, the standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio on a lower temperature side than T.sub. and the standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio on a higher temperature side than T.sub. are obtained from the above-described fitted curve analysis.

(34) In the deformation mode analyzing process, when the steel is plastically deformed, a local region (estimated breaking point) of the steel where necking or breaking is most likely to occur is specified, and a strain ratio x is specified as a plastic deformation mode of the local region. This strain ratio x is selected from among the strain ratios measured in the physical property analyzing process. A method of measuring the estimated breaking point and the strain ratio x thereof is not particularly limited. For example, a scribed circle test may be performed. The scribed circle test is a method including: depicting a circular pattern or a lattice pattern on a surface of a workpiece before working; specifying a local region (estimated breaking point) where necking or breaking is likely to occur due to plastic deformation; and measuring the pattern shape of this local region in order to specify a plastic deformation mode (strain ratio x) of the local region. Based on the results of the scribed circle test, the plastic deformation mode of the local region can be classified as uniaxial tension (=0.5), a drawing region (0.5<<0), plane strain tension (=0), a stretch forming region (0<<1.0), equal biaxial tension (=1.0) or the like.

(35) As described above, the estimated breaking point and the strain ratio x thereof can be actually measured to be analyzed. However, as another analyzing method of the deformation mode analyzing process, a plastic deformation simulation using a finite element method may also be used. At this time, many plastic deformation simulation programs for computer which are commercially available may be used. By using the plastic deformation simulation, even if the inside of a workpiece is an estimated breaking point that actual measurement is difficult, the estimated breaking point can be specified and the strain ratio x thereof can be analyzed. Since the validity of the simulation result can be confirmed through an experiment, the estimated breaking point and the strain ratio x thereof can be analyzed with a minimal number of experiments.

(36) In the heating process, a local temperature T.sub.local of the estimated breaking point of the steel is controlled to be within a temperature range (T.sub.2L.sub.x) to (T.sub.x+1.25H.sub.x) corresponding to the strain ratio of the estimated breaking point. As described above, (T.sub.x3L.sub.x) to (T.sub.x3H.sub.x), (T.sub.x2L.sub.x) to (T.sub.x+2H.sub.x) as a temperature range, or the like may also be used. However, in the plastic working method according to the embodiment, (T.sub.x2L.sub.x) to (T.sub.x+1.25H.sub.x) can be adopted as a first temperature range where plastic deformability can be improved. In order to obtain a ductility improvement effect, it is preferable that the first temperature range be optionally set to, for example, (T.sub.xL.sub.x) to (T.sub.x+H.sub.x) or, (T.sub.x0.5L.sub.x) to (T.sub.x+0.5H.sub.x).

(37) In order to obtain a ductility improvement effect, it is more preferable that, in the deformation mode analyzing process, a change in temperature T.sub.local in the unit of C. that is the local temperature T.sub.local of the estimated breaking point which is changed by heat exchange, heating by working, or the like during plastic working is analyzed; and that, in the heating process, the local temperature T.sub.local be controlled to be in a second temperature range represented by the following expression E which is obtained in consideration of the change in temperature T.sub.local instead of the first temperature range represented by the expression D.
T.sub.xT.sub.local2L.sub.xT.sub.localT.sub.xT.sub.local+1.25H.sub.x(Expression E)

(38) In this way, by considering the change in temperature T.sub.local of the local temperature T.sub.local of the steel which is changed by heat exchange, heating by working, or the like during plastic working, the following effects can be obtained. For example, in plastic working in which a stain rate is slow, even if a change in temperature of the steel is large when compared with a temperature of the steel at the start of the plastic working and that at the end of the plastic working where necking or breaking is likely to occur in the steel, the local temperature T.sub.local of the estimated breaking point can be controlled to be within a temperature range, where the ductility improvement effect is obtained, at the end of the plastic working where plastic deformability is most needed. Alternatively, for example, in plastic working in which the stain rate is fast, even if an influence of heating by working is not negligible, the local temperature T.sub.local can be controlled to be within a temperature range where the ductility improvement effect is obtained. In order to obtain the ductility improvement effect, it is most preferable that the second temperature range be optionally set as, for example, (T.sub.xT.sub.localL.sub.x) to (T.sub.xT.sub.local+H.sub.x) or (T.sub.xT.sub.local0.5L.sub.x) to (T.sub.xT.sub.local+0.5H.sub.x).

(39) In order to analyze the change in temperature T.sub.local in the deformation mode analyzing process, a thermocouple or the like may be attached to the estimated breaking point to actually measure the local temperature T.sub.local of the estimated breaking point during plastic deformation. In addition, with the plastic deformation simulation using the finite element method, this change in temperature T.sub.local may be further analyzed in addition to the estimated breaking point and the strain ratio x thereof.

(40) It is preferable that, in the heating process, at least one of the steel, a mold, and a surrounding space around the steel is heated such that the local temperature T.sub.local of estimated breaking point is within the first temperature range or the second temperature range where the ductility improvement effect is obtained. For example, when it is determined that multiple estimated breaking points are present in the deformation mode analyzing process and that strain ratios between the multiple estimated breaking points are different, it is preferable that at least one of the steel, a mold, and a surrounding space around the steel be heated to control the respective temperatures of the multiple estimated breaking points to be within the first temperature range or the second temperature range suitable for the respective strain ratios thereof. As a result, in the respective multiple estimated breaking points, the ductility improvement effect corresponding thereto is obtained. In addition, in the heating process, at least one of the steel, a mold, and a surrounding space around the steel may be optionally cooled.

(41) In the working process, a plastic working method is not particularly limited as long as the steel in which the local temperature T.sub.local of the estimated breaking point is controlled to be within the first temperature range or the second temperature range where the ductility improvement effect is obtained can be plastically deformed into a desired shape thereby. As the plastic working method, free forging, die forging, press forming using a mold, or the like may be performed.

(42) In addition, in the heating process, a heating medium such as oil containing such as silicone oil, air, inert gas, water vapor mist, or oil mist may be heated such that the local temperature T.sub.local of the estimated breaking point is within the first temperature range or the second temperature range; and in the working process, the steel which is a workpiece may be plastically deformed using a pressure of the heating medium. As a result, a plastically deformed region of the workpiece is uniformly heated to be plastically deformed substantially uniformly. Therefore, effects of delaying a breaking and improving formability can be obtained.

(43) The above-described plastic working method according to the exemplary embodiment will be summarized below.

(44) (1) According to the embodiment, there is provided a plastic working method of steel including austenite, the method including: a physical property analyzing process of measuring T.sub., L.sub., and H.sub. for each of strain ratios , when T.sub. represents a strain-induced-transformation-maximum-ductility-temperature of the steel in the unit of C. which is changed depending on the strain ratio , L.sub. represents the standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio on a lower temperature side than T.sub., and H.sub. represents the standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio on a higher temperature side than T.sub.; a deformation mode analyzing process of analyzing a strain ratio x to be selected from among the strain ratios , when the strain ratio x is a strain ratio of an estimated breaking point which is specified during plastic deformation of the steel; a heating process of heating such that a local temperature T.sub.local is within a first temperature range indicated by the expression D after selecting T.sub.x from among the T.sub., selecting L.sub.x from among the L.sub., and selecting H.sub.x from among the H.sub. respectively, when T.sub.x represents a strain-induced-transformation-maximum-ductility-temperature of the steel in the unit of C. for the strain ratio x, L.sub.x represents the standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio x on a lower temperature side than T.sub.x, H.sub.x represents the standard deviation of a fitted curve of critical equivalent strain which depends on the strain ratio x on a higher temperature side than T.sub.s, and T.sub.local represents a local temperature in the unit of C. of the estimated breaking point; and a working process of plastically deforming the steel after the heating process.

(45) (2) In the deformation mode analyzing process, a change in temperature T.sub.local may be further analyzed when T.sub.local represents a change in temperature in the unit of C. of the local temperature T.sub.local which is changed during the plastic deformation in the working process; and in the heating process, heating may be performed such that the local temperature T.sub.local is within a second temperature range indicated by the expression E.

(46) (3) In the heating process, at least one of the steel, a mold, and a surrounding space around the steel may heated such that the local temperature T.sub.local is within the first temperature range or the second temperature range.

(47) (4) In the heating process, a heating medium may be heated such that the local temperature T.sub.local is within the first temperature range or the second temperature range; and in the working process, the steel may be plastically deformed using a pressure of the heating medium.

(48) (5) In the deformation mode analyzing process, the estimated breaking point and the strain ratio x may be analyzed using a plastic working simulation. Moreover, the change in temperature T.sub.local may be further analyzed using a plastic working simulation.

(49) Next, a plastic working apparatus according to an embodiment of the present invention will be described.

First Embodiment

(50) A plastic working apparatus according to a first embodiment of the present invention will be described. FIG. 5 is a partially cutaway front view showing a schematic configuration of the plastic working apparatus according to the first embodiment of the present invention.

(51) A configuration of a working unit of the plastic working apparatus 1 according to the embodiment will be described below. A main body frame 11 is provided to attach the respective components, such as a pair of molds 21, constituting the plastic working apparatus 1 thereto. A bolster 12 is disposed in an inner lower portion of the main body frame 11, and a slide 13 is disposed in an inner upper portion thereof. The slide 13 is configured to be vertically driven by a slide driving device 14 such as a motor or a cylinder disposed above the main body frame 11. An upper mold 21 is attached to a lower surface of the slide 13, and a lower mold 21 is attached to an upper surface of the bolster 12. As a result, the plastic working apparatus 1 is attached to the main body frame 11 in a state where the pair of molds 21 is arranged opposite each other and is configured to plastically deform a workpiece 3 between the pair of molds 21 by the slide 13 vertically moving. The configurations of the main body frame 11 and the like of the plastic working apparatus 1 are not particularly limited as long as the workpiece 3 can be plastically deformed by the pair of molds 21.

(52) The pair of molds 21 performs plastic working such as bending, drawing, flange forming, burring, or stretch forming on the workpiece 3 disposed between the pair of molds 21. The shape of the pair of molds 21 is adjusted according to the type of plastic working and the shape of a formed product, and a well-known configuration is used as a configuration of the pair of molds 21. The pair of molds 21 is configured to bend the work piece 3, for example, by the upper mold 21 being driven such that the workpiece 3 placed on the lower mold 21 is inserted into a concave portion 21a of the lower mold 21 by a convex portion 21b of the upper mold 21. The pair of molds 21 may be provided with, for example, a blank holder for drawing. The pair of molds 21 may have a configuration in which both the upper mold 21 and the lower mold 21 are provided with the concave portion 21a to die-forge the workpiece 3.

(53) The plastic working apparatus 1 according to the embodiment includes, as a heating unit, a heater 31 that heats an inside atmosphere of a space 16 including the workpiece 3 and the pair of molds 21 and a heater 32 that heats the pair of molds 21. In addition, the heating unit includes a heating furnace 33 that is provided outside the plastic working apparatus 1 and heats the workpiece 3. The plastic working apparatus 1 may be configured to include at least one of the heater 31, the heater 32, and the heating furnace 33. In a configuration including the heater 31, the heater 31 heats the inside atmosphere of the space 16 and thus can heat intentionally such that a temperature difference between the workpiece 3 and the space 16 is relatively small or large. In a configuration including the heater 32, the heater 32 heats the pair of molds 21 and thus can heat intentionally such that a temperature difference between the workpiece 3 and the molds 21 is relatively small or large. In a configuration including the heating furnace 33, a temperature of the workpiece 3 before being installed inside the space 16 of the plastic working apparatus 1 can be controlled to a desired temperature. In this way, at least one of the heater 31, the heater 32, and the heating furnace 33 is used. Therefore, even if multiple estimated breaking points are present in the workpiece 3, the respective temperatures of the multiple estimated breaking points can be controlled to temperatures corresponding to the estimated breaking points. In addition, in the heating unit, optionally, at least one of the workpiece 3, the molds 21, and the space 16 may be cooled.

(54) In addition, the plastic working apparatus 1 includes a cover 41 (heat insulating cover, insulating member) so as to cover the space 16. The space 16 covered with the cover 41 functions as a housing unit that accommodates the workpiece 3.

(55) The heater 31 only needs to heat the inside atmosphere 16 of the space 16 including the workpiece 3 and the pair of molds 21 and the heater 32 only needs to heat the molds 21 such that the estimated breaking point of the workpiece 3 is heated to the first temperature range or the second temperature range. Accordingly, the positions and the configurations of the heaters are not limited and may be configured of, for example, an induction heating coil, a burner, or the like in addition to an electric heater. For example, the heater 31 is attached to the main body frame 11, and the heater 32 is attached to the inside of the molds 21. In addition, optionally, the heater 31, the heater 32, and the heating furnace 33 may have a cooling function of cooling the workpiece 3 to room temperature or lower. In this case, even if the strain-induced-transformation-maximum-ductility-temperature T.sub. of the workpiece 3 is room temperature or lower, the temperature of the estimated breaking point of the workpiece 3 can be controlled to be within the first temperature range or the second temperature range. Therefore, the above configuration is preferable.

(56) The cover 41 is disposed to surround the space 16 including the workpiece 3 and the pair of molds 21 and to prevent heat radiation from the inside atmosphere of the space 16 to the outside or prevent infiltration of outside air to the inside of the space 16. The cover 41 is formed of an insulating member which is a material with high thermal insulation. For example, a heat resisting material such as glass wool or aluminum film laminate is attached to the inside of a metal outer frame having a water cooling function. Further, the cover 41 has an opening and a door which is not shown through which the workpiece is taken in and out. In the embodiment, the cover 41 is formed in a box shape and is attached to the main body frame 11 so as to cover sides and an upper of the main body frame 11. However, the shape, the position, and the attachment method of the cover 41 are not particularly limited as long as the cover 41 can surround the space 16 including at least the pair of molds 21. In the embodiment, an insertion hole 41a into which the slide driving device 14 protruding from the upper of the main body frame 11 is inserted, and an insertion hole 41b into which an inert gas introducing unit described below for introducing inert gas is inserted are formed in the cover 41.

(57) It is preferable that the plastic working apparatus 1 according to the embodiment further include an inert gas introducing unit 51. The inert gas introducing unit 51 includes a gas cylinder and a metal pipe, which are not shown, to substitute the inside atmosphere of the space 16 with, for example, inert gas such as Ar or N.sub.2. Using the inert gas introducing unit 51, the surface oxidation of the workpiece 3 can be minimized. The shape, the position, and the attachment method of the inert gas introducing unit 51 are not particularly limited. In the embodiment, inert gas such as Ar or N.sub.2 is blown from the metal pipe which is attached to the insertion hole 41b formed in the cover 41. In order to suppress the surface oxidation of the workpiece 3, it is more preferable that the inert gas introducing unit 51 further include a vacuum pump which is not shown.

(58) In addition, it is preferable that the plastic working apparatus 1 according to the embodiment further include a temperature measuring unit. The temperature measuring unit includes a thermometer and a display device, which are not shown, which are attached to each of the workpiece 3, the molds 21, and the space 16, so as to independently measure the respective temperatures of the workpiece 3, the molds 21, and the space 16. The shape, the position, and the attachment method of the temperature measuring unit are not particularly limited. As the thermometer, for example, a contact thermocouple thermometer or an infrared thermometer may be used. In the embodiment, a thermocouple is used as the temperature measuring unit.

(59) The above-described plastic working apparatus according to the exemplary embodiment will be summarized below.

(60) (6) The plastic working apparatus according to the first embodiment of the present invention includes: the housing unit that accommodates the workpiece 3 (steel) and the pair of molds 21; the heating unit that heats at least one of the workpiece 3 (steel), the pair of molds 21, and the space 16 (surrounding space around the steel) such that the local temperature T.sub.local of the estimated breaking point of the workpiece 3 (steel) is within the first temperature range and the second temperature range; and the working unit that plastically deforms the workpiece 3 (steel), which is heated by the heating unit, using the pair of molds 21.

(61) (7) The plastic working apparatus further includes the cover 41 (insulating member) that is arranged to cover the housing unit.

(62) (8) The plastic working apparatus further includes the temperature measuring unit that measures respective temperatures of the workpiece 3 (steel), the pair of molds 21, and the space 16 (internal space of the housing unit).

Second Embodiment

(63) Next, a plastic working apparatus according to a second embodiment of the present invention will be described. FIG. 6 is a partially cutaway front view showing a schematic configuration of the plastic working apparatus according to the second embodiment of the present invention.

(64) Since this second embodiment has a difference in a structure of the molds 21 from the first embodiment, this difference will be mainly described. The other structures are the same as those of the first embodiment, and thus the description thereof will not be repeated here.

(65) In the plastic working apparatus 1 according to the embodiment, the workpiece 3 disposed between the pair of molds 21 are plastically deformed by the pair of molds 21 and a heating medium. For example, the heating medium whose pressure and temperature are controlled by a heating medium introducing unit 71 is introduced through a pipe 71a from a heating medium introduction hole 21c provided in the lower mold 21. The workpiece 3 which is fixed between the upper mold 21 and the lower mold 21 by the slide driving device 14 is pressed into the concave portion 21 provided in the upper mold 21 by a pressure of the heating medium. As a result, the workpiece 3 is formed in a desired shape.

(66) As the heating medium, for example, oil such as silicone oil or gas such as air, inert gas, water vapor mist, or oil mist can be used. In addition, the heating medium introducing unit 71 is not particularly limited as long as it can control the pressure and the temperature of the heating medium.

(67) The plastic working apparatus 1 according to the embodiment includes, as a heating unit, the heater 31 that heats the inside atmosphere of the space 16 including the workpiece 3 and the pair of molds 21, the heater 32 that heats the pair of molds 21, and a heater 34 that heats the heating medium. In addition, the heating unit includes the heating furnace 33 that is provided outside the plastic working apparatus 1 and heats the workpiece 3. By using at least one of the heater 31, the heater 32, the heater 34, and the heating furnace 33, the temperature of the estimated breaking point of the workpiece 3 can be controlled to a temperature corresponding to the estimated breaking point. Even if multiple estimated breaking points are present in the workpiece 3, the respective temperatures of the multiple estimated breaking points can be more preferably controlled to temperatures corresponding to the estimated breaking points by controlling the above-described four heating sources. In addition, optionally, the heater 31, the heater 32, the heater 34, and the heating furnace 33 may have a cooling function of cooling the workpiece to room temperature or lower. In this case, even if the strain-induced-transformation-maximum-ductility-temperature T.sub. of the workpiece 3 is room temperature or lower, the temperature of the estimated breaking point of the workpiece 3 can be controlled to be within the first temperature range or the second temperature range. Therefore, the above configuration is preferable.

(68) In addition, the plastic working apparatus 1 according to the embodiment includes the cover 41 (heat insulating cover, insulating member) so as to cover the space 16. The space 16 covered with the cover 41 functions as the housing unit that accommodates the workpiece 3.

(69) In addition, it is preferable that the plastic working apparatus 1 according to the embodiment further include the temperature measuring unit. The temperature measuring unit includes a thermometer and a display device, which are not shown, which are attached to each of the workpiece 3, the molds 21, the space 16, and the heating medium introducing unit 71, so as to independently measure the respective temperatures of the workpiece 3, the molds 21, the space 16, and the heating medium. The shape, the position, and the attachment method of the temperature measuring unit are not particularly limited. As the thermometer, for example, a contact thermocouple thermometer or an infrared thermometer may be used.

(70) The above-described plastic working apparatus according to the exemplary embodiment will be summarized below.

(71) (9) The plastic working apparatus according to the second embodiment of the present invention includes: the housing unit that accommodates the workpiece 3 (steel) and the pair of molds 21; the heating medium introducing unit that introduces the heating medium into the molds 21; the heating unit that heats at least one of the workpiece 3 (steel), the pair of molds 21, the space 16 (surrounding space around the steel), and the heating medium such that the local temperature T.sub.local of the estimated breaking point of the workpiece 3 (steel) is within the first temperature range and the second temperature range; and the working unit that plastically deforms the workpiece 3 (steel), which is heated by the healing unit, using a pressure of the heating medium.

(72) (10) The plastic working apparatus further includes the cover 41 (insulating member) that is arranged to cover the housing unit.

(73) (11) The plastic working apparatus further includes the temperature measuring unit that measures respective temperatures of the workpiece 3 (steel), the pair of molds 21, the space 16 (internal space of the housing unit), and the heating medium.

Example 1

(74) Next, examples of the present invention will be described. However, conditions of the examples are condition examples for confirming the operability and the effects of the present invention, and the present invention is not limited to these condition examples. In the present invention, various conditions can be adopted within the scope of the present invention as long as the object of the present invention is achieved.

(75) In the physical property analyzing process, using steel including austenite (Examples) and steel not including austenite (Comparative Examples), each strain ratio and the critical equivalent strain .sub.eq-critical at each temperature were measured. As a method of measuring each strain ratio and the critical equivalent strain .sub.eq-critical at each temperature, a spherical stretch forming test in which an end of a test piece was fixed while changing the horizontal and vertical dimension of the test piece was performed at each temperature. The critical equivalent strain .sub.eq-critical was calculated from a strain when necking or breaking occurs.

(76) Table 1 shows the measurement results of each strain ratio and the critical equivalent strain .sub.eq-critical at each temperature. For example, in Example 1, when =0.5, a strain-induced-transformation-maximum-ductility-temperature T.sub.0.5 at which the critical equivalent strain .sub.eq-critical was maximum was 75 C.; and when =1.0, a strain-induced-transformation-maximum-ductility-temperature T.sub.1.0 was 150 C. In Example 3, when =0.5, a strain-induced-transformation-maximum-ductility-temperature T.sub.0.5 was 150 C.; and when =1.0, a strain-induced-transformation-maximum-ductility-temperature T.sub.1.0 was 250 C. In this way, in the steel including austenite (Examples), the critical equivalent strain .sub.eq-critical is changed depending on the type of steel, the working temperature, and the strain ratio . On the other hand, in Comparative Example 6, as shown in Table 1, a temperature at which the critical equivalent strain .sub.eq-critical was maximum does not depend on the strain ratio . That is, the strain-induced-transformation-maximum-ductility-temperature T.sub. does not depend on the strain ratio . This is because the TRIP phenomenon does not occur in the steel not including austenite (Comparative Examples).

(77) Table 2 shows a standard deviation L.sub. of a fitted curve of critical equivalent strain which depends on the strain ratio on a lower temperature side than T.sub.; a standard deviation H.sub. of a fitted curve of critical equivalent strain which depends on the strain ratio f on a higher temperature side than T.sub., in which T.sub. represents the strain-induced-transformation-maximum-ductility-temperature at each strain ratio which is obtained by analyzing the fitted curve (approximate function) using the results of Table 1. In this way, by analyzing L.sub. and H.sub. for each strain ratio, the temperature range in which plastic deformability can be improved at each strain ratio can be determined. For example, in Example 3, when =0, 2L.sub.0=110 C. and 1.25H.sub.0=24 C. Therefore, based on the strain-induced-transformation-maximum-ductility-temperature T.sub., the temperature range in which the critical equivalent strain .sub.eq-critical is improved by the TRIP phenomenon can be determined to be 90 C. to 224 C.

(78) Next, in the deformation mode analyzing process, an estimated breaking point of a workpiece and the strain ratio of this estimated breaking point were analyzed during forming by square cylinder drawing. FIG. 7 is a schematic diagram showing forming by square cylinder drawing. As shown in FIG. 7 using dies 61 having a size of 80 mm80 mm, a square cylinder-shaped punch 62 having a size of 75 mm75 mm, and a holder 63, forming by square cylinder drawing was performed on a blank 64 (workpiece). Analysis regarding this forming by square cylinder drawing was performed in a scribed circle test. It was able to be specified in the forming by square cylinder drawing from the analysis results of the scribed circle test that a B portion of the blank 64 (workpiece) shown in FIG. 7 was an estimated breaking point and that a plastic deformation mode of the B portion was a uniaxial tension state where the strain ratio was 0.5.

(79) Next, in the heating process, using the steel of Example 3 of Table 1 as a workpiece, the temperature of at least one of the steel, the mold, and the surrounding space was controlled such that the local temperature T.sub.local of the estimated breaking point was within a range of 25 C. to 250 C. Next, in the working process, the steel of Example 3 whose temperature was controlled in the heating process was formed by square cylinder drawing.

(80) Table 3 shows the results of the forming by square cylinder drawing in which the steel of Example 3 as the workpiece was heated such that the local temperature T.sub.local of the estimated breaking point was within a range of 25 C. to 250 C. The drawing height shown in Table 3 refers to the height at which the workpiece can be drawn without necking or breaking, and the higher the value, the higher the formability.

(81) As shown in Table 1, in the steel of Example 3, when the strain ratio was 0.5, the strain-induced-transformation-maximum-ductility-temperature T.sub.0.5 was 150 C. In addition, as shown in Table 2, in the case of .sub.0.5, 2L.sub.0.5=110 C. and 1.25H.sub.0.5=69 C. That is, in the forming by square cylinder drawing, it was expected that when the local temperature T.sub.local of the estimated breaking point was within a range of 40 C. to 219 C. (first temperature range), the drawing height would be high; and that when T.sub.local=150 C., the drawing height would be highest. Actually, as shown in Table 3, it was able to be confirmed that, when the local temperature T.sub.local of the estimated breaking point was within the first temperature range of 50 C. to 200 C., the drawing height was sufficiently high. In addition, when the local temperature T.sub.local of the estimated breaking point was 150 C., the drawing height was highest. The formability of a case where the forming by square cylinder drawing was performed in the above-described temperature range was improved to be about two times the formability of a case where the forming by square cylinder drawing was performed at 25 C. and 250 C. although the same workpiece was used. In this way, with the plastic working method according to the above embodiment of the present invention, necking or breaking can be suppressed, and formability can be improved.

(82) TABLE-US-00001 TABLE 1 Properties of Workpiece Strain Ratio : 2/ 1 = 0.5 = 0.25 = 0 = 0.25 = 0.5 = 1 Critical Critical Critical Critical Critical Critical Austenite Temperature/ Equivalent Equivalent Equivalent Equivalent Equivalent Equivalent Fraction/% C. Strain Strain Strain Strain Strain Strain Example 1 100 25 0.602 0.635 0.558 0.607 0.707 1.004 50 0.668 0.729 0.631 0.634 0.753 1.026 75 0.764 0.753 0.681 0.673 0.769 1.059 100 0.72 0.775 0.722 0.703 0.794 1.084 125 0.713 0.754 0.667 0.727 0.834 1.151 150 0.703 0.685 0.596 0.661 0.817 1.208 175 0.649 0.618 0.477 0.621 0.756 1.124 200 0.638 0.548 0.486 0.529 0.618 1.066 Example 2 100 25 0.682 0.702 0.681 0.665 0.827 0.911 50 0.712 0.704 0.715 0.725 0.907 0.949 75 0.698 0.683 0.722 0.764 0.921 0.983 100 0.687 0.624 0.669 0.798 0.953 1.007 125 0.597 0.598 0.631 0.767 0.961 1.069 150 0.501 0.571 0.59 0.739 0.948 1.087 175 0.475 0.567 0.538 0.882 0.847 0.971 200 0.457 0.51 0.455 0.583 0.759 0.808 Example 3 17.6 25 0.43 0.34 0.219 0.278 0.35 0.441 50 0.493 0.372 0.234 0.291 0.378 0.453 75 0.544 0.401 0.209 0.295 0.404 0.48 100 0.621 0.423 0.254 0.317 0.431 0.466 125 0.671 0.467 0.263 0.351 0.468 0.501 150 0.718 0.624 0.324 0.378 0.498 0.556 175 0.702 0.579 0.348 0.389 0.51 0.571 200 0.622 0.51 0.37 0.391 0.555 0.583 225 0.547 0.471 0.312 0.421 0.578 0.617 250 0.48 0.434 0.287 0.407 0.547 0.651 275 0.48 0.434 0.287 0.387 0.521 0.608 Example 4 12 25 0.416 0.372 0.202 0.295 0.375 0.527 50 0.412 0.392 0.217 0.304 0.412 0.585 75 0.41 0.391 0.216 0.314 0.439 0.574 100 0.403 0.368 0.216 0.317 0.458 0.566 125 0.463 0.37 0.246 0.33 0.454 0.561 150 0.492 0.4 0.263 0.332 0.424 0.53 175 0.529 0.406 0.261 0.349 0.471 0.601 200 0.51 0.416 0.258 0.355 0.491 0.65 225 0.497 0.41 0.304 0.386 0.624 0.708 250 0.481 0.389 0.271 0.366 0.551 0.764 275 0.47 0.38 0.251 0.359 0.514 0.732 Example 5 4.6 0 0.405 0.398 0.347 0.346 0.451 0.536 25 0.389 0.405 0.357 0.37 0.484 0.651 50 0.384 0.384 0.326 0.41 0.549 0.78 75 0.375 0.381 0.324 0.387 0.671 0.814 100 0.37 0.365 0.312 0.375 0.556 0.84 150 0.357 0.344 0.292 0.365 0.604 0.64 200 0.325 0.343 0.232 0.305 0.409 0.58 225 0.317 0.321 0.201 0.278 0.387 0.586 250 0.31 0.318 0.196 0.289 0.376 0.587 Comparative 0 25 0.752 0.707 0.514 0.67 0.82 1.034 Example 6 50 0.715 0.672 0.489 0.638 0.801 0.974 75 0.684 0.643 0.468 0.512 0.784 0.927 100 0.642 0.604 0.439 0.584 0.75 0.901 125 0.628 0.590 0.429 0.546 0.723 0.882 150 0.597 0.561 0.408 0.525 0.699 0.845 175 0.557 0.524 0.381 0.481 0.656 0.841 200 0.529 0.497 0.362 0.463 0.62 0.819 225 0.518 0.487 0.354 0.45 0.576 0.796 250 0.497 0.467 0.340 0.438 0.547 0.778

(83) TABLE-US-00002 TABLE 2 Properties of Workpiece Optimum Temperature T.sub. Of Stress Induced Transformation Austenite Optimum Temperature T.sub. Of Strain Ratio Fraction/% Stress Induced Transformation = 0.5 = 0.25 = 0 = 0.25 = 0.5 = 1.0 Example 1 100 Optimum Temperature T.sub. Of Stress 75 100 100 125 125 150 Induced Transformation ( C.) 2 L.sub. ( C.) 90 130 100 140 130 86 1.25 H.sub. ( C.) 75 58 44 50 64 38 Example 2 100 Optimum Temperature T.sub. Of Stress 50 50 75 100 125 150 Induced Transformation ( C.) 2 L.sub. ( C.) 90 160 140 100 150 100 1.25 H.sub. ( C.) 76 88 68 64 44 50 Example 3 17.5 Optimum Temperature T.sub. Of Stress 150 175 200 225 225 250 Induced Transformation ( C.) 2 L.sub. ( C.) 110 106 110 140 160 150 1.25 H.sub. ( C.) 69 56 24 38 38 19 Example 4 12 Optimum Temperature T.sub. Of Stress 175 200 225 225 250 250 Induced Transformation ( C.) 2 L.sub. ( C.) 62 120 160 140 180 120 1.25 H.sub. ( C.) 62 38 25 25 19 19 Example 5 4.5 Optimum Temperature T.sub. Of Stress 0 25 25 50 75 100 Induced Transformation ( C.) 2 L.sub. ( C.) 60 40 30 30 50 90 1.25 H.sub. ( C.) 150 114 114 100 75 38

(84) TABLE-US-00003 TABLE 3 Local Temperature T.sub.local of Estimated Drawing Height Breaking Point mm Example 3 25 27.7 50 37.1 100 50 125 50 150 50 175 47.5 200 43.5 250 26.4

INDUSTRIAL APPLICABILITY

(85) According to the above-described embodiments, it is possible to provide a plastic working method and a plastic working apparatus, in which necking or breaking can be suppressed and formability can be improved.

BRIEF DESCRIPTION OF THE REFERENCE SYMBOLS

(86) 1: PLASTIC WORKING APPARATUS 3: WORKPIECE (STEEL) 11: MAIN BODY FRAME 12: BOLSTER 13: SLIDE 14: SLIDE DRIVING DEVICE 16: SPACE (SURROUNDING SPACE AROUND STEEL, INTERNAL SPACE OF HOUSING UNIT) 21: MOLDS 31: HEATER FOR SPACE 16 (HEATING UNIT) 32: HEATER FOR MOLDS 21 (HEATING UNIT) 33: HEATING FURNACE FOR WORKPIECE 3 (HEATING UNIT) 41: HEAT INSULATING COVER (INSULATING MEMBER) 51: INERT GAS INTRODUCING UNIT 71: HEATING MEDIUM INTRODUCING UNIT (HEATING UNIT)