OLED display apparatus and preparation method thereof

Abstract

This disclosure relates to an OLED display apparatus and the preparation method thereof. The OLED display apparatus comprises, from the bottom to the top, a substrate, an OLED device, a thin film inner layer, an ethylcellulose layer, and a thin film outer layer. By adding a hydrophobic ethylcellulose layer with a photosensitive material and a singlet oxygen receptor dissolved therein on the basis of current thin film packaging, this invention can have the functions of water vapor barrier and oxygen absorption so as to improve the service life of devices.

Claims

1. An OLED display apparatus, wherein the OLED display apparatus sequentially comprises a substrate, an OLED device, a thin film inner layer, an ethylcellulose layer, and a thin film outer layer, the ethylcellulose layer comprises an organic photosensitive material, a singlet oxygen acceptor material, and ethylcellulose.

2. The OLED display apparatus according to claim 1, wherein a molar ratio of the organic photosensitive material, the singlet oxygen acceptor material, and the ethylcellulose is 1-3:1-3:2-4.

3. The OLED display apparatus according to claim 1, wherein the organic photosensitive material is one or more selected from a complex composed of an organic molecule with an extended conjugated ? bond and a metal, rose bengal, lucifer yellow, acridine red, and methylene blue.

4. The OLED display apparatus according to claim 1, wherein the singlet oxygen acceptor material is one or more selected from: substances which may react with monoalkene; substances which may be subjected to a Diels-AlDer type reaction with a chain-like, cyclic, aromatic, or heterocyclic aromatic conjugated ? bond; substances which may react with an active double bond having an electron-donating heteroatom, N, O, or S; or substances which may react with carotenoids, amines, phenols, sulfides, or heterocyclic compounds.

5. The OLED display apparatus according to claim 1, wherein the thin film inner layer is prepared from a parylene thin film; and the thin film outer layer is prepared from a parylene thin film.

6. The OLED display apparatus according to claim 1, wherein the ethylcellulose layer has a thickness of 500 to 1000 ?m.

7. The OLED display apparatus according to claim 1, wherein the ethylcellulose layer further contains alkenyl succinic anhydride.

8. The OLED display apparatus according to claim 7, wherein a molar ratio of alkenyl succinic anhydride to ethylcellulose is 1:2 to 3.

9. A preparation method of an OLED display apparatus, characterized by comprising the steps of: producing an OLED device on a substrate, forming a thin film inner layer for the OLED device, and packaging; forming an ethylcellulose layer on the surface of the thin film inner layer, and packaging, wherein the ethylcellulose layer comprises an organic photosensitive material, a singlet oxygen acceptor material, and ethylcellulose; and forming a thin film outer layer on the surface of the ethylcellulose layer, and packaging.

10. The preparation method according to claim 9, wherein the ethylcellulose layer is prepared by the following method: coating and drying a solution of an organic photosensitive material, a singlet oxygen acceptor material, and ethylcellulose in a solvent on the thin film inner layer.

11. The preparation method according to claim 9, wherein the solvent is trichloromethane.

12. The preparation method according to claim 9, wherein a molar ratio of the organic photosensitive material, the singlet oxygen acceptor material, and the ethylcellulose is 1-3:1-3:2-4.

13. The preparation method according to claim 9, wherein the ethylcellulose layer has a thickness of 500 to 1000 ?m.

14. The preparation method according to claim 9, wherein the ethylcellulose layer further contains alkenyl succinic anhydride, and a molar ratio of alkenyl succinic anhydride to ethylcellulose is 1:2 to 3.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a structural schematic diagram of the OLED display apparatus of Example 1 of this invention.

(2) FIG. 2 is a structural diagram of a Ca electrical test system.

(3) FIG. 3 is a normalized plot of 1/R varying over time for Ca layers of Comparative Example 1 and Example 1 in a Ca electrical test.

(4) FIG. 4 is main views of Comparative Example 1 and Example 1 after testing in a Ca electrical test.

(5) In the figures, 1. substrate; 2. OLED device; 3. thin film inner layer; 4. ethylcellulose layer; 5. thin film outer layer.

DESCRIPTION OF EMBODIMENTS

(6) An aspect of this invention provides an OLED display apparatus sequentially comprises, from the bottom to the top, for example, a substrate, an OLED device, a thin film inner layer, an ethylcellulose layer, and a thin film outer layer. By adding a hydrophobic ethylcellulose layer containing an organic photosensitive material and a singlet oxygen receptor on a thin film inner layer, the OLED display apparatus is allowed to have effects of water vapor barrier and oxygen absorption so as to improve the service life of devices.

(7) The OLED display apparatus of this invention may be a top-emission type OLED display apparatus, or may be a bottom-emission type OLED display apparatus.

(8) The top and the bottom in the term from the bottom to the top herein are only used to represent the relative positional relationship of related devices of the OLED display apparatus, rather than the top and the bottom in the nature. For example, the thin film outer layer may be located on the upper surface, the lower surface, and the like of the OLED display apparatus. These devices may also be placed from the left to the right, so that the thin film outer layer may be located on the left surface, the right surface, and the like of the OLED display apparatus. Therefore, from the bottom to the top can be replaced by from the top to the bottom, from the left to the right, from the right to the left, from the front to the rear, or from the rear to the front.

(9) The ethylcellulose is a nonionic cellulose ether, which is insoluble in water but soluble in an organic solvent, and has the following structure:

(10) ##STR00001##

(11) wherein n represents polymerization degree.

(12) The ethylcellulose has the characteristic of good thermal stability. Upon combustion, it has extremely low ash content, and a tough thin film can be generated; and at a low temperature, it can still maintain the flexibility and is non-toxic, and has antibiotic performance and metabolic inertia. The ethylcellulose has the following specific characteristics:

(13) 1. Non-flammable.

(14) 2. Good thermal stability and good thermoplasticity.

(15) 3. Non-discoloring under sunlight.

(16) 4. Good flexibility.

(17) 5. Good dielectricity.

(18) 6. Good alkali resistance and good weak-acid resistance.

(19) 7. Good performance for preventing aging.

(20) 8. Good resistance to salt, cold, and moisture absorption.

(21) 9. Stable for chemicals and not deteriorated upon long-period storage.

(22) 10. Able to be compatible with a number of resins and good compatibility with all plasticizers.

(23) 11. Prone to be discolored in strongly alkaline environment and conditions of heating.

(24) In this disclosure, an organic photosensitive material and a singlet oxygen acceptor material are added to ethylcellulose, and the prepared ethylcellulose layer can effectively block water vapor and absorb oxygen. The ethylcellulose layer comprises at least an organic photosensitive material, a singlet oxygen acceptor material, and ethylcellulose. Preferably, the organic photosensitive material, the singlet oxygen acceptor material, and the ethylcellulose are mixed and prepared at a molar ratio of 1-3:1-3:2-4, more preferably 2:2:3.

(25) In order to further improve the strength of the ethylcellulose layer and enhance the effect of packaging, an appropriate amount of alkenyl succinic anhydride (ASA) may be further added to ethylcellulose. The molar ratio of alkenyl succinic anhydride to ethylcellulose may be 1:2 to 3.

(26) The organic photosensitive material may be one or more selected from a complex composed of an organic molecule with an extended conjugated ? bond and a metal (such as metalloporphyrin and metal phthalocyanine), rose bengal, lucifer yellow, acridine red, and methylene blue.

(27) The singlet oxygen acceptor material is one or more selected from: substances which may react with monoalkene; substances which is subjected to a Diels-AlDer type reaction with a chain-like, cyclic, aromatic, or heterocyclic aromatic conjugated ? bond; substances which may react with an active double bond having an electron-donating heteroatom such as N, O, S, etc.; or substances which may react with carotenoids, amines, phenols, sulfides, or heterocyclic compounds. Preferably, the singlet oxygen acceptor material may be selected from ?-carotenes.

(28) When the OLED apparatus in one aspect of this invention is working, when oxygen and water vapor permeated through the thin film outer layer encounter the ethylcellulose layer, water vapor is effectively blocked due to the hydrophobicity of the ethylcellulose film. Meanwhile, under the effect of light irradiation, the excited organic photosensitive material will sensitize permeated oxygen molecules into singlet oxygen. These singlet oxygen molecules may react with the singlet oxygen acceptor material and is in turn consumed. Therefore, the effects of water vapor barrier, oxygen absorption, and service life improvement of devices are achieved.

(29) Here, the photosensitization reaction is as follows:
S+hv.fwdarw..sup.1S*
.sup.1S*.fwdarw..sup.3S*
.sup.3S*+O.sub.2.fwdarw..sup.1O.sub.2(singlet oxygen);

(30) and the singlet oxygen reaction is as follows:

(31) ##STR00002##

(32) the thin film inner layer may be prepared from a parylene thin film; and the thin film outer layer may be prepared from a parylene thin film.

(33) Another aspect of this invention further provides a preparation method of an OLED display apparatus, comprising the steps of:

(34) 1) producing an OLED device on a substrate, forming a thin film inner layer for the OLED device, and packaging;

(35) 2) forming an ethylcellulose layer on the surface of the thin film inner layer, and packaging; and

(36) 3) forming a thin film outer layer on the surface of the ethylcellulose layer, and packaging.

(37) Preferably, the ethylcellulose layer may be prepared by the following method:

(38) (1) placing ethylcellulose (EC) in a solvent and stirring it to allow it to be dissolved, further adding an organic photosensitive material and a singlet oxygen acceptor material, and uniformly mixing them and keeping them standing until bubbles disappear; and

(39) (2) uniformly coating the mixed liquid obtained in the above step on a thin film inner layer, naturally drying it, and drying it with an oven to form an ethylcellulose layer.

(40) Here, in step (1), the solvent may be trichloromethane.

(41) Here, in step (1), alkenyl succinic anhydride may be further added.

(42) Here, in step (2), the mixed liquid is coated on the thin film inner layer, and is transferred to a vacuum oven for drying at 80? C. after naturally drying for 24 hours, to form an ethylcellulose layer.

(43) By adding a hydrophobic ethylcellulose layer with a photosensitive material and a singlet oxygen receptor dissolved therein on the basis of current thin film packaging, this invention can have the functions of water vapor barrier and oxygen absorption so as to improve the service life of devices.

(44) In FIG. 1, the OLED display apparatus comprises, from the bottom to the top, a substrate 1, an OLED device 2, a thin film inner layer 3, an ethylcellulose layer 4, and a thin film outer layer 5.

(45) The OLED device 2 sequentially comprises: an anode, an optional planarizing layer, a hole injection layer, a hole transport layer, an organic light-emitting layer, an electron transport layer, an electron injection layer, and a cathode, along the direction going away from the substrate 1, wherein the above-mentioned anode is usually produced using ITO. Forming the OLED device on the substrate 1 specifically comprises: producing an anode using the processes of magnetron sputtering and etching; producing a planarizing layer on the anode, wherein the above-mentioned planarizing layer may be optionally produced or not; forming a hole injection layer, a hole transport layer, an organic light-emitting layer, an electron transport layer, an electron injection layer, and a cathode layer by using a vacuum deposition process or a painting and printing process; and after the above process is finished, the display device is packaged to form a thin film inner layer, an ethylcellulose layer, and a thin film outer layer on the OLED device.

(46) The examples below are provided to illustrate this invention but are not intended to limit the scope of this invention.

(47) Substances used in Examples were as follows:

(48) Ethylcellulose (EC): analytically pure, Tianjin Kemiou Chemical Reagent Development Center

(49) Metallic iron porphyrin: analytically pure, Sinopharm Chemical Reagent Co., Ltd.

(50) ?-carotene: analytically pure, Sinopharm Chemical Reagent Co., Ltd.

(51) ASA: analytically pure, Hercules Inc., US.

Comparative Example 1

(52) The OLED display apparatus of Comparative Example 1 comprised, from the bottom to the top, a substrate, an OLED device, a thin film inner layer, and a thin film outer layer.

(53) The OLED display apparatus of Comparative Example 1 was prepared as follows.

(54) An OLED device was produced on a substrate, and packaging of a thin film inner layer was performed on the OLED device; and packaging of a thin film outer layer was performed on the surface of the thin film inner layer. The thin film inner layer was prepared from a parylene thin film; and the thin film outer layer was prepared from a parylene thin film, wherein the thicknesses of the thin film inner layer and the thin film outer layer are 750 ?m and 750 ?m respectively.

Example 1

(55) The OLED display apparatus of Example 1 was the same as the OLED display apparatus of Comparative Example 1, except that an ethylcellulose layer was added between the thin film inner layer and the thin film outer layer. The OLED display apparatus of Example 1 was prepared as follows:

(56) 1) producing an OLED device on a substrate, and performing packaging of a thin film inner layer on the OLED device;

(57) 2) producing an ethylcellulose layer on the surface of the thin film inner layer, and packaging; and

(58) 3) performing packaging of a thin film outer layer on the surface of the ethylcellulose layer.

(59) The ethylcellulose layer was prepared by the following method.

(60) Ethylcellulose (EC) was placed in trichloromethane and was stirred to allow it to be dissolved. Further, metallic iron porphyrin and ?-carotene were added, and were uniformly mixed and kept standing until bubbles disappeared, to obtain a mixed liquid. The resultant mixed liquid was uniformly coated on a thin film inner layer, was naturally dried for 24 hours, and was transferred to a vacuum oven for drying at 80? C., to form an ethylcellulose layer, wherein the thickness was 750 ?m.

(61) The molar ratio of metallic iron porphyrin, ?-carotene, and ethylcellulose was 2:2:3.

Example 2

(62) The OLED display apparatus of Example 2 was the same as the OLED display apparatus of Example 1, except that the ethylcellulose layer thereof further contained ASA. The preparation method thereof was the same as the preparation method of the OLED display apparatus of Example 1, except that ASA was added while ethylcellulose was added. The formed ethylcellulose layer had a thickness of 750 ?m.

(63) the molar ratio of metallic iron porphyrin, ?-carotene, ethylcellulose, and ASA was 2:2:3:1.2.

(64) Ca Electrical Test

(65) A comparison tests was performed with a Ca electrical test system, and the test system had a structure as shown in FIG. 2. The basic principle was that a Ca layer was produced on a substrate, packaging was performed with a thin film, and then a normalized curve of 1/R of the Ca layer varying over time was tested and the appearance of the OLED display apparatus was observed. The specific operation method was as follows.

(66) 1) The water-oxygen barrier properties of the OLED display apparatus packaged with an existing organic thin film (Comparative Example 1) and the OELD display apparatus of Example 1 were tested at a high temperature of 200? C. by a Ca electrical test method, respectively. The test was performed for 80 h, and data records were taken every 2 h, which were shown in Table 1.

(67) TABLE-US-00001 TABLE 1 Normalized Concentration/(1 R) Comparative Example t/h Example 1 1 2 1.000 1.000 4 0.999 0.999 6 0.998 0.999 8 0.990 0.998 10 0.985 0.998 12 0.982 0.997 14 0.980 0.997 16 0.976 0.996 18 0.975 0.996 20 0.973 0.995 22 0.970 0.994 24 0.965 0.994 26 0.963 0.993 28 0.960 0.989 30 0.955 0.987 32 0.951 0.985 34 0.947 0.983 36 0.941 0.980 38 0.934 0.978 40 0.928 0.974 42 0.920 0.970 44 0.910 0.964 46 0.902 0.960 48 0.890 0.954 50 0.880 0.950 52 0.870 0.944 54 0.860 0.939 56 0.840 0.936 58 0.810 0.931 60 0.790 0.927 62 0.770 0.923 64 0.752 0.919 66 0.729 0.915 68 0.700 0.910 70 0.675 0.906 72 0.655 0.900 74 0.600 0.892 76 0.540 0.886 78 0.480 0.880 80 0.400 0.873

(68) It can be known from Table 1 that the water-oxygen barrier property of Comparative Example 1 began to decrease from 10 h, and was significantly different from that of the OELD apparatus of Example 1 of this invention by about 30 h. After 60 h, the water-oxygen barrier property of Comparative Example 1 significantly decreased, while the OELD apparatus of Example 1 of this invention still maintained a good water-oxygen barrier property.

(69) 2) A normalized concentration plot of 1/R of a Ca layer varying over time was as shown in FIG. 3. According to the principle of the test, when the reaction of Ca with water and oxygen occurred, the conductivity of the portion where the reaction occurred decreased, and the resistance of the thin film increased. The curve in the figure exhibited a reduced conductivity, and thus it can be seen that the barrier effect of water and oxygen of Example 1 was superior to that of Comparative Example 1.

(70) The reaction equation of the Ca layer in the presence water and oxygen was as follows:
2Ca+O.sub.2.fwdarw.2CaO, Ca+H.sub.2O.fwdarw.CaO+H.sub.2, CaO+H.sub.2O.fwdarw.Ca(OH).sub.2

(71) 3) FIG. 4 was main views of the OLED display apparatus of Comparative Example 1 and the display apparatus of Example 1 after the test. It can be known from the figure that the apparatus packaged with an existing organic film was significantly oxidized and turned black, while the OLED apparatus obtained in Example 1 of this invention had normal display.

(72) In addition to good water-oxygen barrier property, which was the same as that of the OELD apparatus of Example 1, the OELD apparatus of Example 2 had a film layer of which the tensile strength was enhanced, because ASA had an effect of plasticization.

(73) Although this invention has been exhaustively described hereinbefore by using general descriptions and specific embodiments, some modifications and improvements may be made thereto based on this invention, which is apparent to the person skilled in the art. Therefore, these modifications or improvements made on the basis of not departing from the spirit of this invention all belong to the scope sought to be protected by this invention.