METHOD FOR SOLIDIFYING LIQUID STEEL SLAG

Abstract

The liquid steel slag (2) is poured in at least four successive layers (6-8), comprising a lowermost layer (6), an uppermost layer (7) and at least two intermediate layers (8), in a reservoir (3) and the layers of liquid steel slag are allowed to solidify. After having applied the uppermost layer (7), the solidified steel slag is cooled down more quickly by means of water. The average temperature of each of the intermediate layers (8) is kept at least until the start of the water cooling step, and this for at least one hour, above a minimum temperature which is equal to or higher than the temperature at which -dicalcium silicate is formed. In this way, more crystalline phases different from dicalcium silicates are formed so that the formation of fines by the transition of into -dicalcium silicates can be considerably reduced. A glassy material and/or a phosphorus containing compound is preferably added to the liquid slag to further reduce the formation of fines.

Claims

1. A method for solidifying liquid steel slag to produce solid steel slag, which liquid steel slag comprises at least the elements calcium, silicon and oxygen and has a basicity, defined as the ratio between its calcium content, expressed as wt. % CaO, and its silicon content, expressed as wt. % SiO.sub.2, which is higher than 1.2 so that, when the liquid steel slag is cooled down to room temperature, -dicalcium silicate is formed therein as from a first temperature, which method comprises the steps of: pouring at least four successive layers of said liquid steel slag in a reservoir, which successive layers comprise a lowermost layer, an uppermost layer and at least two intermediate layers; allowing the liquid steel slag to solidify in the reservoir; and cooling the solidified steel slag in the reservoir by applying water onto the solidified steel slag, characterised in that said reservoir has a bottom delimited by side walls, which bottom has a surface area of S m.sup.2; said successive layers of liquid steel slag are poured on top of one another in said reservoir, with at least said intermediate layers having a volume of at least S0.03 m.sup.3 and; said water cooling step is started after having poured said uppermost layer of liquid steel slag in the reservoir; and the temperature of each of said intermediate layers, determined as a volume weighted average over the respective intermediate layer, is kept at least until the start of said water cooling step, and this for at least one hour, preferably for at least two hours, between 1300 C. and a minimum temperature which is equal to or higher than said first temperature.

2. A method according to claim 1, characterised in that said minimum temperature is equal to or higher than 700 C., preferably equal to or higher than 750 C., more preferably equal to or higher than 800 C., most preferably equal to or higher than 850 C. and even more preferably equal to or higher than 900 C.

3. A method according to claim 1, characterised in that the temperature as from which -dicalcium silicate is formed in the steel slag when cooling the liquid steel slag down to room temperature is lowered by adding a phosphorus containing compound to the liquid slag, in particular a phosphate and/or a pyrophosphate containing compound.

4. A method according to claim 1, characterised in that the basicity of the liquid steel slag is lowered by adding a glassy material thereto after the liquid steel slag has been separated off from the liquid steel, which glassy material has a further basicity, defined as the ratio between its calcium content, expressed as wt. % CaO, and its silicon content, expressed as wt. % SiO.sub.2, which is smaller than 0.20, and preferably smaller than 0.15.

5. A method according to claim 4, characterised in that said glassy material comprises at least 50 wt. %, preferably at least 60 wt. % silicon expressed as SiO.sub.2, said glassy material preferably comprising glass that has preferably been crushed, in particular soda-lime-silica glass.

6. A method according to claim 4, characterised in that both said liquid steel slag and said glassy material are applied in a same slag pot, said glassy material being preferably applied into the slag pot before applying the liquid steel slag therein.

7. A method according to claim 4, characterised in that per 100 parts by weight of the liquid steel slag, less than 10 parts by weight, preferably less than 9 parts by weight and more preferably less than 8 parts by weight of said glassy material are added to the liquid steel slag.

8. A method according to claim 1, characterised in that the volume of said intermediate layers of liquid steel slag is at least S0.04 m.sup.3 and preferably at least S0.05 m.sup.3.

9. A method according to claim 1, characterised in that the volume of said intermediate layers of liquid steel slag is at most S0.5 m.sup.3, preferably at most S0.4 m.sup.3, more preferably at most S0.3 m.sup.3 and most preferably at most S0.2 m.sup.3.

10. A method according to any one of the claim 1, characterised in that said water cooling step is started at least one hour, preferably at least two hours and more preferably at least three hours after having poured said uppermost layer of liquid steel slag in the reservoir.

11. A method according to claim 1, characterised in that said water cooling step is started less than ten hours, preferably less than seven hours and more preferably less than five hours after having poured said uppermost layer of liquid steel slag in the reservoir.

12. A method according to claim 1, characterised in that said successive layers have a total height of less than 2.0 m, preferably less than 1.8 m, more preferably less than 1.6 m and most preferably less than 1.4 m.

13. A method according to claim 1, characterised in that said predetermined time intervals are shorter than 90 minutes, preferably shorter than 75 minutes, more preferably shorter than 60 minutes and most preferably shorter than 50 minutes.

14. A method according to claim 1, characterised in that said predetermined time intervals are longer than 5 minutes, preferably longer than 10 minutes and more preferably longer than 15 minutes.

15. A method according to claim 1, characterised in that the temperatures of the liquid steel slag upon being poured in said successive layers are higher than 800 C., preferably higher than 900 C. and more preferably higher than 950 C.

16. A method according to claim 1, characterised in that the temperature of each of said intermediate layers, determined as a volume weighted average over the respective intermediate layer, drops at an average rate which is not higher than 50 C./min, preferably not higher than 40 C./min, more preferably not higher than 30 C./min and most preferably not higher than 20 C./min as from being applied until being covered by a further intermediate layer or by said uppermost layer.

17. A method according to claim 1, characterised in that the temperature of each of said intermediate layers, determined as a volume weighted average over the respective intermediate layer, is kept before the start of said water cooling step, for at least one hour, preferably for at least two hours, below 1200 C. and preferably below 1100 C.

18. A method according to claim 1, characterised in that said successive layers of liquid steel slag are poured at predetermined temperatures and at predetermined time intervals on top of one another in said reservoir and the temperature of each of said intermediate layers, determined as a volume weighted average over the respective intermediate layer, is kept above said minimum temperature by keeping said predetermined temperatures sufficiently high and said predetermined time intervals sufficiently short.

19. A method according to claim 1, characterised in that the solidified steel slag is cooled down by applying water onto the uppermost steel slag layer at least until said temperature of each of said intermediate layers is lower than 400 C., preferably lower than 300 C. and more preferably lower than 200 C.

20. A method according to claim 1, characterised in that the basicity of the liquid steel slag is higher than 1.4 and in particular higher than 1.6.

Description

[0027] Other particularities and advantages of the invention will become apparent from the following description of some particular embodiments of the method according to the present invention. The reference numerals used in this description relate to the annexed drawings wherein:

[0028] FIG. 1 illustrates schematically the reservoir filled with successive layers of liquid steel slag;

[0029] FIG. 2 shows the phase formations in an AOD slag calculated with the Slag-A model with manual addition of bredigite;

[0030] FIG. 3 is a graph showing the resulting temperature of a mixture of steel slag, at a temperature of 1600 C., and different amounts of glass at a temperature of 25 C.;

[0031] FIG. 4 shows the phases present in the steel slag upon addition of different amounts of glass, at a temperature of 25 C., to liquid steel slag at a temperature of 1600 C.

[0032] FIG. 5 shows the phase formations in the same AOD slag as in FIG. 2, calculated again with the Slag-A model with manual addition of bredigite, but with addition of 5% of glass to the liquid steel slag;

[0033] FIG. 6 is a graph showing the relationship between the amount of calcium magnesium silicates and the amount of dicalcium silicates in the different solidified steel slag layers of Experiment 3;

[0034] FIG. 7 is a graph showing the amounts of calcium magnesium silicates and the amounts of dicalcium silicates in the different solidified steel slag layers of Experiment 3 in function of the calculated average temperature of each of the steel slag layers just before a next layer is applied on top of it;

[0035] FIG. 8 is a graph showing the relationship between the amount of dicalcium silicates in the different solidified steel slag layers of Experiment 3 in function of the average temperature of each of the steel slag layers just before a next layer is applied on top of it; and

[0036] FIG. 9 shows the evolution of the temperature measured at one location in the lowermost layer and in the first intermediate layer of Experiment 3 in function of the time.

[0037] The present invention relates to a method for solidifying liquid steel slag to produce solid steel slag. The solid steel slag is a calcium silicate slag which may contain different crystalline phase such as dicalcium silicate phases, calcium magnesium silicate phases and other phases. The steel slag is in particular a stainless steel slag. It can in particular be an AOD (Argon Oxygen Decarburization), a VOD (Vacuum Oxygen Decarburization) an EAF (Electric Arc Furnace) slag or a combination thereof. When the steel slag consists of steel slag materials of different origins, they do not have to be mixed but they can be applied separately on top of one another as described further hereinafter.

[0038] In order to be able to valorise the resulting solid steel slag as much as possible, it should contain a minimum amount of fines, in particular a minimum amount of particles smaller than 0.5 mm. These fines are mainly the result of a disintegration of the slag which is driven by the irreversible to -C2S phase transformation causing a volume expansion of about 12%. During this phase transformation high internal stresses thus occur in the slag, as a result of which the slag disintegrates into fine particles. The coarser part of the solid steel slag can be used, after crushing and sieving, as fine or coarse aggregates, in particular in concrete and asphalt. Dicalcium silicate phases are formed in the steel slag when the steel slag has a basicity, defined as the ratio between its calcium content, expressed as wt. % CaO, and its silicon content, expressed as SiO.sub.2, which is higher than 1.2 so that the present invention is intended to solidify such steel slag material whilst reducing or preventing the formation of fines, having in particular a size of less than 0.5 mm.

[0039] In accordance with the present invention the amount of fines is reduced by a particular cooling method. In practice the liquid slag which is separated off from liquid steel, in particular from liquid stainless steel, is applied in a slag pot 1 and is transported in this slag pot 1 to a slag yard. When the liquid slag is applied in the slag pot, it has a temperature which is usually higher than 1500 C., for example in the range of 1550 C. to 1750 C. Before being transported to the slag yard, and during the transport itself, the liquid slag cools down in the slag pot, depending on the residence time in the slag pot.

[0040] As illustrated in FIG. 1, the liquid slag 2 is poured in different successive layers in a reservoir 3. This reservoir 3 has a bottom 4 delimited by side walls 5. The successive layers comprise at least a lowermost layer 6, an uppermost layer 7 and at least two intermediate layers 8. The lowermost layer 6 is normally the layer which is applied onto the bottom 4 of the reservoir 3 but it can also be one of the higher layers, especially when the bottom 4 of the reservoir is too cold and/or the layer applied onto this bottom 4 too thin to ensure the minimum temperature of the layer applied on top thereof. It is thus possible that two or even more lowermost layers 6 are first applied in the reservoir 3.

[0041] Each of the successive layers is usually applied by pouring one slag pot 1 in the reservoir. However, it is also possible to pour two or more slag pots 1 at the same time, or shortly after one another (so that the steel slag from the first slag pot has not solidified yet, for example with a time interval of less than 5 minutes), in the reservoir so that the liquid slag of these slag pots 1 flows together and forms one layer of liquid steel slag 2 in the reservoir 3. After having poured the uppermost layer 7 in the reservoir 3, water is applied, in particular sprayed, onto the steel slag in the reservoir 3 to cool the solidified steel slag layers 6-8. This water cooling step is preferably started at least one hour, preferably at least two hours and more preferably at least three hours after having poured the uppermost layer 7 of liquid steel slag 2 in the reservoir 3. In this way, the intermediate layers 8, which are intended to produce a solid steel slag with less fines, are kept for a longer time at a higher temperature before cooling them down with water. The water cooling step is preferably started less than ten hours, preferably less than seven hours and more preferably less than five hours after having poured the uppermost layer 7 of liquid steel slag in the reservoir 3. In this way, the intermediate layers 8 are not allowed to cool down to a too low temperature before they are cooled more quickly with water.

[0042] An important feature of the present invention is indeed that the temperature of each of the intermediate layers 8 should be kept at least until the start of the water cooling step, i.e. until the moment water is applied onto the uppermost layer, and this for at least one hour and preferably for at least two hours, between 1300 C. and a minimum temperature which is equal to or higher than the temperature as from which -dicalcium silicate is formed in the steel slag when the liquid steel slag is cooled down to room temperature, in particular at a cooling rate of about 10 C./min. This temperature can be determined by means of a DTA analysis (Differential Thermal Analysis) wherein the steel slag is cooled down for example at a rate of about 10 C./min. The temperature of each of the intermediate layers 8 is defined herein as a volume weighted average over the respective intermediate layer. If th of the layer has a temperature of 700 C., th a temperature of 720 C. and th a temperature of 750 C. then the temperature of the layer is equal to 700 C.+720 C.+750 C.=723 C.

[0043] The minimum temperature is preferably equal to or higher than 700 C., more preferably equal to or higher than 750 C., most preferably equal to or higher than 800 C., and even more preferably equal to or higher than 850 C. or even equal to or higher than 900 C. The temperature of each of said intermediate layers 8 (determined as a volume weighted average over the respective intermediate layer 8), is preferably kept before the start of said water cooling step, for at least one hour, preferably for at least two hours, below 1200 C., and preferably below 1100 C.

[0044] During this first slow cooling phase, at these relatively high temperatures, crystalline phases different from dicalcium silicates are formed. The steel slag usually comprises not only the elements calcium, silicon and oxygen but also magnesium (in an amount which is preferably higher than 4 wt. %, more preferably higher than 6 wt. % and most preferably higher than 8 wt. %). The presence of magnesium causes the formation of calcium magnesium silicates, in particular of merwinite and/or bredigite, during the first cooling phase at these relatively high temperatures rather than dicalcium silicates, more particularly rather than -dicalcium silicates. Dicalcium silicates ( or ) which were formed at higher temperatures are being transformed during this first cooling phase into other crystalline phases, in particular into calcium magnesium silicate phases. During the subsequent cooling phase with water, these crystalline phases, which are different from dicalcium silicate, transform less easily into and subsequently into -dicalcium silicate so that by increasing the amount of these crystalline phases the disintegration of the steel slag can be considerably reduced.

[0045] The successive layers 6-8 of liquid steel slag 2 are poured at predetermined temperatures and at predetermined time intervals on top of one another in said reservoir 3. The temperature of each of these intermediate layers 8 can be kept above the above described minimum temperature by keeping said predetermined temperatures sufficiently high and said predetermined time intervals sufficiently short. The predetermined time intervals are in particular shorter than 90 minutes, preferably shorter than 75 minutes, more preferably shorter than 60 minutes and most preferably shorter than 50 minutes. The predetermined temperatures of the liquid steel slag 2 upon being poured in said successive layers are in particular higher than 800 C., preferably higher than 900 C. and more preferably higher than 950 C. or even higher than 1000 C. In order to enable the different layers of liquid steel slag to solidify to some extent before the next layer is poured on top thereof, the predetermined intervals between the different pouring steps are preferably longer than 5 minutes, more preferably longer than 10 minutes and most preferably longer than 15 minutes.

[0046] The intermediate layers 8 should further have a sufficiently large average thickness to avoid a too quick cooling of the steel slag in the respective layer (before a next layer is applied on top thereof) and to enable to produce a sufficiently coarse aggregate by crushing the solidified steel slag within each intermediate layer 8. When the bottom 4 of the reservoir 3 has a surface area of S m.sup.2, the intermediate layers 8 should each have a volume of at least S0.03 m.sup.3 so that the intermediate layers 8 have an average thickness of at least 0.03 m. The volume of the intermediate layers 8 is preferably at least S0.04 m.sup.3 and more preferably at least S0.05 m.sup.3.

[0047] The intermediate layers 8 are preferably not too thick so that the steel slag is of a more uniform temperature within each layer. In this way too hot areas, wherein in particular -dicalcium silicate could be formed instead of calcium magnesium silicates during the first cooling phase, and/or too cold areas wherein in particular -dicalcium silicate could already be formed, can be prevented. The volume of the intermediate layers of liquid steel slag is therefore preferably at most S0.5 m.sup.3, more preferably at most S0.4 m.sup.3, most preferably at most S0.3 m.sup.3 and even more preferably at most S0.2 m.sup.3.

[0048] The temperature of each of the intermediate layers 8, determined as a volume weighted average over the respective intermediate layer, drops preferably at an average rate which is not higher than 50 C./min, preferably not higher than 40 C./min, more preferably not higher than 30 C./min and most preferably not higher than 20 C./min as from having applied the liquid steel slag until the layer is being covered by a further intermediate layer 8 or by said uppermost layer 7. This slow cooling rate can be achieved by allowing the intermediate layer to cool by air cooling, i.e. by being in contact with the atmosphere. Avoiding higher cooling rates is advantageous in view of the fact that by these relatively low cooling rates, the produced solid steel slag contains a smaller amount of amorphous phases (compared to the existing processes wherein the steel slag poured in the slag yard is immediately cooled down by water spraying to achieve a fast cooling limiting the transition of into -dicalcium silicates). Preferably the cooling rate is so low that the produced solid steel slag contains less than 10 wt. %, preferably less than 7 wt. %, and more preferably less than 5 wt. % of amorphous phases. An advantage of such small amounts of amorphous phases is that the aggregates produced from the steel slag have a high PSV value. Although less preferably, a small amount of water could be sprayed on top of the different successive layers 6-8 to accelerate the cooling/solidification of the steel slag before a next layer is applied on top thereof but this amount should not be too large to prevent a too fast cooling of the steel slag and to enable to maintain the temperature of the intermediate layers above the above described minimum temperature until the actual cooling step with water. In this respect, the reservoir is preferably shielded off from the rain.

[0049] During the water cooling step, water is applied onto the uppermost steel slag layer 7. This water is applied preferably at least until the temperature of each of said intermediate layers 7 (i.e. their volume weighted average temperature) is lower than 400 C., preferably lower than 300 C. and more preferably lower than 200 C. Applying water onto the uppermost steel slag layer 7 is preferably stopped when the temperature of this uppermost steel slag layer 7 is still higher than 100 C. In this way all of the applied water evaporates resulting in a dry steel slag material. The cooling water is preferably sprayed onto the uppermost steel slag layer 7 and is applied preferably at such a flow rate that no water accumulates onto the uppermost steel slag layer 7, i.e. so that the flow rate at which the water is applied is equal to or smaller than the rate at which the water evaporates. It was found that in this way the most effective cooling of the steel slag layers 6-8 could be achieved.

[0050] The successive steel slag layers 6-8 have preferably a total height of less than 2.0 m, preferably less than 1.8 m, more preferably less than 1.6 m and most preferably less than 1.4 m. In this way, a sufficiently quick cooling of all of these layers can be achieved by applying water on top of the uppermost layer 7.

[0051] The liquid steel slag 2 has a predetermined basicity, defined as the ratio between its calcium content, expressed as wt. % CaO, and its silicon content, expressed as wt. % SiO.sub.2. This basicity is in particular so high that upon a slow cooling of the steel slag, dicalcium silicates are formed leading to a (partial) disintegration of the steel slag, i.e. to a so-called dusting or falling of the steel slag. The basicity is more particularly usually higher than 1.2, in particular higher than 1.4 and often higher than 1.6. The basicity of EAF slags is usually lower than the basicity of AOD or VOD slags. EAF slags may have for example a basicity of about 1.4 whilst AOD slags have for example a basicity of 1.7 or even higher so that AOD slags are more prone to dusting than EAF slags.

[0052] In the method of the present invention, the basicity of the liquid steel slag is preferably lowered by adding a glassy material thereto after the liquid steel slag has been separated off from the liquid steel. This glassy material has a basicity, defined as the ratio between its calcium content, expressed as wt. % CaO, and its silicon content, expressed as wt. % SiO.sub.2, which is smaller than 0.20, and preferably smaller than 0.15. The glassy material preferably comprises at least 50 wt. %, more preferably at least 60 wt. % silicon expressed as SiO.sub.2 and comprising in particular glass, preferably waste glass, that has preferably been crushed. The glass may in particular be soda-lime-silica glass. Such glass is available as waste material and is known as glass cullet. The glassy material preferably comprises magnesium, in particular in an amount of at least 1.0, preferably at least 2.0 wt. %. An advantage of additional magnesium is that it can contribute in the formation of calcium magnesium silicate phases. Moreover, in case of the steel slag comprises chromium, for example stainless steel slag, a magnesiochromite spinel phase can be formed which reduces the leaching of chromium from the steel slag.

[0053] The glassy material can be admixed to the liquid slag when the liquid slag is being poured in the slag pot 1. It is however easier to apply the glassy material separately into the slag pot, in particular by applying it in the slag pot before introducing (pouring) the liquid steel slag therein. Tests have demonstrated that when introducing 3 wt. % of glass cullet in the slag pot before pouring the liquid steel slag therein (having a temperature higher than 1500 C.), more than 99% of the glass cullet dissolved in the liquid steel slag. More glass cullet could be dissolved in the liquid steel slag by injecting the glass cullet in the steel slag which is being poured in the slag pot. When injecting for example about 5 wt. % of glass cullet in the flow of liquid steel all of the glass cullet dissolved therein. Calculations have shown that when adding for example 15 wt. % of glass cullet (having a temperature of 25 C.) to the liquid steel slag, the temperature thereof only drops with somewhat more than 200 C. so that the liquid steel slag contains enough heat to dissolve quite large amounts of glass cullet.

[0054] The glassy material is however added to the liquid steel slag in an amount which is preferably less than 10 parts by weight, preferably less than 9 parts by weight and more preferably less than 8 parts by weight, per 100 parts by weight of the liquid steel slag. The smaller the amount of glassy material, the easier it can be dissolved homogeneously in the liquid steel slag.

[0055] An advantage of the addition of a glassy material to the liquid steel slag is that the basicity of the liquid steel slag is reduced. More importantly, however, in combination with the above described solidification method of the present invention, the addition of a glassy material has additional, synergetic effects. Indeed, the addition of glass reduces the formation of bredigite during the first cooling phase and increases the formation of merwinite. This effect can already be demonstrated at relatively low amounts of glassy material. The reduction of the amount of bredigite in favour of the formation of other calcium magnesium silicate phases has the important advantage that, in contrast to these other phases, bredigite is metastable and may thus lead to the formation of dicalcium silicate upon cooling of the steel slag, in particular during the water cooling phase. Due to the large volume of solidified steel slag contained in the different layers, a fast cooling thereof (as by water or air quenching) is indeed not possible.

Calculations on Slag Mineralogy and Glass Additions

[0056] The above described effects of the solidification method of the present invention and also of the special effects of the addition of glass in combination with this solidification method can be explained based on the following calculations. These calculations are made for an average AOD slag having the following composition:

TABLE-US-00001 TABLE 1 Average composition (in wt. %) of the AOD slag used in the FactSage Slag-A model calculations CaO SiO.sub.2 Al.sub.2O.sub.3 TiO.sub.2 MgO CaF.sub.2 51.9 30.6 1.7 1.1 7.8 6.9

[0057] Calculations were made on the equilibrium mineralogy to be expected at different temperatures with the FactSage Slag-A model with manual addition of bredigite (Ca.sub.7MgSi.sub.4O.sub.16 or C7MS4), with a stability range of about 900-1300 C. On the C2S behaviour, the model could only predict the transition to from directly. -C2S was not considered a stable phase as it only forms because it is easier to nucleate than -C2S. In practice, a transition from -C2S to -C2S occurs, and further a transformation from -C2S to -C2S (destructive and to be avoided) occurs if not blocked by boron (and/or quenching).

[0058] FIG. 2 shows the phase formation in the AOD slag upon slowly cooling thereof so that the different phases are in equilibrium at the different temperatures for which equilibrium calculations were made. Between these calculated data, linear lines were drawn. The equilibrium states were only calculated for a limited number of temperatures, more particularly for 2000; 1900; 1800; 1700; 1600; 1500; 1400; 1300; 1200; 1100; 500 and 400 C. These graphs therefore do not show exactly as from which temperature the different crystalline phases are formed, in particular not the temperature as from which -C2S is formed since there are no calculations in the range between 1100 and 500 C.

[0059] The following phases were indicated in FIG. 2: [0060] LIQ: liquid phase [0061] -C2S: -dicalcium silicate=-Ca.sub.2SiO.sub.4 [0062] -C2S: -dicalcium silicate=-Ca.sub.2SiO.sub.4 [0063] MeO: magnesium oxide [0064] SPINA: spinel=Me.sup.2+Me.sup.3+.sub.2O.sub.4 [0065] C7MS4: bredigite=Ca.sub.7MgSi.sub.4O.sub.16 [0066] CaF.sub.2 [0067] C5T4: Ca.sub.5Ti.sub.4O.sub.13 [0068] C3T2: Ca.sub.3Ti.sub.2O.sub.7 [0069] C3MS2: merwinite=Ca.sub.3MgSi.sub.2O.sub.8 [0070] +-C2S: beta and gamma dicalcium silicate [0071] C3MA4: Ca.sub.3MgAl.sub.4O.sub.10

[0072] In FIG. 2 it can be seen that at higher temperatures -C2S is first formed. In a next phase, the main phase that is formed is bredigite. At 1100 C., this bredigite forms about 70% of the slag. Upon further slow cooling, the bredigite mainly transforms into merwinite and dicalcium silicate (-C2S which subsequently transforms into -C2S: not indicated in FIG. 2). From FIG. 2 it thus appears that when slowly cooling the slag during the first cooling phase of the method of the present invention, the -C2S which is already present in the steel slag at high temperatures (occurring in the slag pot) is allowed to disappear and bredigite is allowed to form. If -C2S would not be allowed to disappear due to the fact that the slag would not be cooled sufficiently slowly during the first cooling phase, it would subsequently transform more easily than bredigite, and in particular than merwinite, into beta and gamma dicalcium silicate.

[0073] A further calculation was made with the same model but with the addition of glass. The glass had the following composition:

TABLE-US-00002 TABLE 2 Composition of the glass (in wt. %) added to the AOD slag used in the FactSage Slag-A model calculations CaO SiO.sub.2 Al.sub.2O.sub.3 Fe.sub.2O.sub.3 MgO Na.sub.2O K.sub.2O 7.15 70.49 2.72 0.29 3.82 12.2 2.76

[0074] As potassium is not modelled well in the FactSage databases, the K.sub.2O content was added to the Na.sub.2O content.

[0075] Upon addition of glass at 25 C. to the slag at 1600 C., the temperature of the slag dropped drastically as shown in FIG. 3. This is the result of an adiabatic calculation of slag and glass, which assumes that there are no losses to the environment or to stirring gas etc. When adding 15% of glass, the temperature drops by more than 200 C.

[0076] FIG. 4 shows the phases present in the slag upon addition of glass (% on X-axis) at the temperature resulting from the mixing of the slag with the added amount of glass. FIG. 4 shows that the liquid fraction does not decrease, because the low melting point of the glass and the disappearance of the (high melting) C2S phase. When adding 15% glass, the liquid fraction should rise from 60 to 80%. When adding more glass, the liquid fraction decreases again due to the formation of merwinite.

[0077] FIG. 5 shows the phases in the slag as a function of temperature for an addition of 5 wt. % of glass. The different equilibrium states have been calculated at temperatures of 1600; 1500; 1400; 1300; 1200; 1100; 1000; 900; 800; 700; 600; 500; 200 and 100 C.

[0078] The following phases were indicated in FIG. 5: [0079] LIQ: liquid phase [0080] -C2S: -dicalcium silicate=-Ca.sub.2SiO.sub.4 [0081] C7MS4: bredigite=Ca.sub.7MgSi.sub.4O.sub.16 [0082] CaF.sub.2 [0083] CT: CaTiO.sub.3 [0084] C2A2S: Ca.sub.2Al.sub.2SiO.sub.7 [0085] C3MS2: merwinite=Ca.sub.3MgSi.sub.2O.sub.8 [0086] N2C2S3: Na.sub.2Ca.sub.2Si.sub.3O.sub.9 [0087] C4S2F2: cuspidine=Ca.sub.4Si.sub.2F.sub.2O.sub.7 [0088] +-C2S: beta and gamma dicalcium silicate

[0089] When comparing FIG. 5 with FIG. 2 it can be seen that, at temperatures higher than 800 C., the amount of bredigite is reduced considerably (at 1100 C. from about 70% to about 24%) whilst the amount of merwinite is increased considerably (at 1100 C. from about 3% to about 47%). The slow cooling process, at high temperature, of the present invention enables thus, in combination with the addition of glass, to form more of the stable merwinite than of the metastable bredigite. After addition of 5 wt. % of glass, nucleation of merwinite starts already at a temperature between 1400 and 1500 C. whilst without the addition of glass the nucleation of merwinite starts only at a lower temperature, i.e. at a temperature between 1200 and 1300 C. As appears from FIG. 5 bredigite converts during a further slow cooling process mainly into dicalcium silicates. Additionally, the addition of glass causes a reduction of the amount of dicalcium silicate at lower temperatures, but this reduction (from about 40% to about 24%) is considerably smaller than the effect of the glass addition on the amounts of bredigite and merwinite. The method of the present invention enables thus to considerably improve the effect of the glass addition, and enables in particular to achieve a considerable effect on the formation of fines with only a limited amount of glass.

[0090] To further reduce the formation of fines, the usual borates can be added to the liquid slag. These borates reduce the transition of to -dicalcium silicate. An additional advantage of the addition of borates is that they lower the temperature of the phase transformation from to -C2S. In pure dicalcium silicate -C2S transforms to -C2S at a temperature of 675 C. A differential thermal analysis (DTA) has been carried out on dicalcium silicate doped with 0.13 wt. % of disodium tetraborate (Na.sub.2B.sub.4O.sub.7). The to phase transition occurred at an average temperature of 638 C., i.e. at a temperature which is about 37 C. lower than the temperature at which this phase transition occurs without the addition of borate.

[0091] A same effect can be achieved by the addition of a phosphorus containing compound. A DTA analysis has also been carried out on dicalcium silicate doped with 2 wt. % of a composition composed of about 50% CaF.sub.2 and about 50% of {(Ca.sub.5(PO.sub.4).sub.3OH)+(Ca.sub.5(PO.sub.4).sub.3F)}. The to phase transition occurred at an average temperature of 641 C., i.e. at a temperature which is about 34 C. lower than the temperature at which this phase transition occurs without the addition of the phosphorus containing compound. In contrast to borates, such phosphorus containing compounds, in particular phosphate and/or pyrophosphate containing compounds, have no toxic effect and can thus freely be added to the liquid steel slag. The phosphorus containing compound does not only reduces the transformation from to -C2S but also lowers the temperature as from which -C2S is formed when cooling down the liquid steel slag. In this way, it is thus easier in the method of the present invention to keep the layers of steel slag during the first cooling phase at a temperature which is higher than the temperature at which -C2S starts to be formed in the steel slag.

Experimental Test Results

Experiment 1

[0092] In this experiment slag pots wherein liquid AOD slag was allowed to cool to a temperature lower than 1000 C. were poured in layers in a reservoir without a fast cooling with water. This resulted in an amount of fines of more than 80%. When pouring the slag pots in layers in the reservoir when the steel slag still had a temperature of at least 1000 C., and when subsequently cooling the stack of layers by spraying water onto them, a solidified steel slag which contained nearly no fines was obtained.

Experiment 2

[0093] A same experiment was done, with the same AOD slag, with a combination of hot (>1000 C.) and cold (<1000 C.) slag pots. In one test the amount of hot pots was 55% and the amount of cold pots 45%. This resulted in 20% of fines. A combination of 2% of hot pots and 98% of cold pots resulted in about 80% of fines.

Experiment 3

[0094] 22 slag pots with varying amounts of liquid steel slag (AOD and EAF) were poured at different temperatures (mainly due to different residence times in the slag pots) and at different time intervals in a slag reservoir having a bottom with a surface area of 620 m.sup.2. The total height of the stack of layers was about 1.4 m. 4.5 hours after having poured the uppermost layer in the reservoir, water was sprayed on top of it. The surface temperature of each of the layers was measured just before pouring the next layer on top of it and the temperature was also measured in the lowermost layer and in the first intermediate layer, i.e. in the layer applied on top of the lowermost layer. The average temperature of each of the layers just before a next layer was applied thereon was calculated by means of a temperature model. The dicalcium silicate (C2S) contents and the calcium magnesium silicate (CMS) contents (sum of merwinite, bredigite and diopside) of the different layer was measured after the solidification and cooling of the layers. The different results are indicated in the following table.

TABLE-US-00003 TABLE 2 Average temperature and C2S and CMS content of the different layers. Average Steel Time in Time till layer slag Weight slag pot next layer CMS C2S temp. Layer type (tons)t (min) (min) (%) (%) ( C.) 1 AOD 38 49 135 / / / (bottom) 2 AOD 25 71 60 54.7 22.6 1049 3 EAF 29 110 25 52.3 20.2 1164 4 AOD 25 37 60 / / / 5 EAF 15 28 90 15.6 65.6 1175 6 EAF 29 19 55 18.9 60.4 750 7 AOD 28 40 30 24.8 61.4 1059 8 EAF 16 25 35 21.5 56.7 1126 9 AOD 25 17 25 44.1 12.3 1266 10 EAF 15 18 130 37.8 44.4 635 11 EAF 23 15 30 42.3 25.4 1111 12 AOD 20 22 75 38.5 38.3 714 13 AOD 21 13 15 28.2 29.2 842 14 EAF 22 45 90 22.7 49.4 541 15 AOD 23 10 10 34.9 34.7 1173 16 EAF 22 6 95 22.4 37.2 688 17 EAF 17 20 40 18.1 67.2 858 18 AOD 21 22 35 66.8 16.6 1097 19 EAF 16 18 40 31.0 47.5 774 20 AOD 21 23 90 56.8 11.6 ! 21 EAF 17 20 40 12.6 71.2 639 22 AOD 17 23 / 62.5 5.8 / (top)

[0095] FIG. 6 is a graph with a linear trend line illustrating the relationship between the C2S and the CMS contents of the different layers. It can be seen that there is a linear relationship between these two contents. Since in the solidification method of the present invention the formation of CMS is enhanced by keeping the steel slag for a sufficient period of time at a higher temperature before starting the water cooling process, the C2S content, and thus the formation of fines, should be reduced accordingly.

[0096] FIG. 7 is a graph illustrating the relationship between the C2S contents and the CMS contents in function of the average temperature of the different layers just before the next tipping, i.e. just before applying the next layer. It can be seen that generally the formation of C2S is suppressed when the average temperature of the layer just before the next layer is applied on top of it is higher. This effect is more pronounced for AOD slag. Due to the lower basicity, the EAF slag is less sensitive to dusting at lower temperatures.

[0097] FIG. 8 is a graph with an exponential trend line illustrating the relationship, for the different layers of AOD slag, between the average temperature of the layer just before the next tipping and the C2S content. It can be seen that the higher the temperature, the lower the C2S content.

[0098] FIG. 9 is a graph showing the temperatures measured for the first 11 hours by the temperature probes in the lowermost layer and in the layer applied just on top of it (positioned at a height of 0.07 and 0.27 m from the bottom). It can be seen that, notwithstanding the large volume of the first layer of liquid steel slag, the temperature dropped to a lower level, i.e. to a temperature of about 900 C. after 11 hours whilst, due to the insulation provided by this lowermost layer and the additional heat applied by the liquid slag layers poured on top of it, the temperature of the second layer initially dropped quite quickly with about 200 C. (to about 1000 C.), until the next layer of liquid slag was applied thereon, after which the temperature of the second layer remained almost constant at a temperature of about 1050 C. At this temperature, bredigite and merwinite are the main crystalline phases that are formed. The method of the present invention enables to maintain this temperature, without having to apply heat to the slag layers, until an equilibrium is established, i.e. until a maximum amount of bredigite and especially of merwinite is formed. During the next water cooling phase, the solidified slag layers are cooled down more quickly to avoid the formation of beta and gamma dicalcium silicates starting especially from the bredigite phases. The amount of these bredigite phases is preferably reduced by adding a glassy compound such as ground waste glass to the liquid slag.

[0099] In this experiment an amount of borates was added to the AOD steel slag to avoid the transition from to -C2S. Due to the low basicity of the EAF slag, i.e. a basicity of about 1.4, no borate was added thereto. The AOD slag had a basicity of about 1.8.