INTEGRATED CASTING CORE-SHELL STRUCTURE FOR MAKING CAST COMPONENT WITH NON-LINEAR HOLES

Abstract

The present disclosure generally relates to integrated core-shell investment casting molds that provide filament structures corresponding to cooling hole patterns in the surface of the turbine blade or stator vane, which provide a leaching pathway for the core portion after metal casting. These filament structures may be linear or non-linear. The invention also relates to core filaments that can be used to supplement the leaching pathway, for example in a core tip portion of the mold.

Claims

1. A method for fabricating a ceramic mold, comprising: (a) contacting a cured portion of a workpiece with a liquid ceramic photopolymer; (b) irradiating a portion of the liquid ceramic photopolymer adjacent to the cured portion through a window contacting the liquid ceramic photopolymer; (c) removing the workpiece from the uncured liquid ceramic photopolymer; and (d) repeating steps (a)-(c) until a ceramic mold is formed, the ceramic mold comprising: (1) a core portion and a shell portion with at least one cavity between the core portion and the shell portion, the cavity adapted to define the shape of a cast component upon casting and removal of the ceramic mold, and (2) a plurality of filaments joining the core portion and the shell portion where each filament spans between the core and shell and defines a hole in the cast component upon removal of the mold, wherein at least one filament includes at least a portion having a non-linear geometry and a cross sectional area ranging from 0.01 to 2 mm.sup.2.

2. The method of claim 1, wherein the process comprises, after step (d), a step (e) comprising pouring a liquid metal into a casting mold and solidifying the liquid metal to form the cast component.

3. The method of claim 2, wherein the process comprises, after step (e), a step (f) comprising removing the mold from the cast component.

4. The method of claim 3, wherein removing the mold from the cast component comprises a combination of mechanical force and chemical leaching.

5. The method of claim 1, wherein the non-linear geometry forms an S shaped hole upon removal of the mold.

6. The method of claim 1, wherein the hole exits the surface at an angle of less than 20?.

7. The method of claim 1, wherein the hole exits the surface at an angle in the range of 5? to 15?.

8. A method of preparing a cast component comprising: (a) pouring a liquid metal into a ceramic casting mold and solidifying the liquid metal to form the cast component, the ceramic casting mold comprising: (1) a core portion and a shell portion with at least one cavity between the core portion and the shell portion, the cavity adapted to define the shape of a cast component upon casting and removal of the ceramic mold, and (2) a plurality of filaments joining the core portion and the shell portion where each filament spans between the core and shell and defines a hole in the cast component, wherein at least one filament includes at least a portion having a non-linear geometry and a cross sectional area ranging from 0.01 to 2 mm.sup.2; (b) removing the ceramic casting mold from the cast component by leaching at least a portion of the ceramic core through the holes in the cast component.

9. The method of claim 8, wherein removing the ceramic casting mold from the cast component comprises a combination of mechanical force and chemical leaching.

10. The method of claim 8, wherein the non-linear geometry forms an S shaped hole upon removal of the mold.

11. The method of claim 8, wherein the hole exits the surface at an angle in the range of less than 20?.

12. A ceramic casting mold comprising: a core portion and a shell portion with at least one cavity between the core portion and the shell portion, the cavity adapted to define the shape of a cast component upon casting and removal of the ceramic mold, and a plurality of filaments joining the core portion and the shell portion where each filament spans between the core and shell and defines a hole in the cast component, wherein at least one filament includes at least a portion having a non-linear geometry and a cross sectional area ranging from 0.01 to 2 mm.sup.2.

13. The method of claim 12, wherein the non-linear geometry forms an S shaped hole upon removal of the mold.

14. The method of claim 12, wherein the hole exits the surface at an angle of less than 20?.

15. The method of claim 12, wherein the hole exits the surface at an angle in the range of 5? to 15?.

16. A single crystal metal turbine blade or stator having an inner cavity and an outer surface, a plurality of cooling holes providing fluid communication between the inner cavity and outer surface, the plurality of cooling holes having at least a portion having a non-linear geometry and a cross sectional area ranging from 0.01 to 2 mm.sup.2.

17. The single crystal metal turbine blade or stator of claim 16, wherein the non-linear geometry forms an S shaped hole upon removal of the mold.

18. The single crystal metal turbine blade or stator of claim 16, wherein the hole exits the surface at an angle of less than 20?.

19. The single crystal metal turbine blade or stator of claim 16, wherein the hole exits the surface at an angle in the range of 5? to 15?.

20. The single crystal metal turbine blade or stator of claim 16, where the single crystal metal is a superalloy.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0015] FIG. 1 is a flow diagram showing the steps for conventional investment casting.

[0016] FIG. 2 is a schematic diagram showing an example of a conventional scheme for a core-shell mold with ball chute prepared by a conventional process.

[0017] FIG. 3 shows a perspective view of a prior art integrated core-shell mold with ties connecting the core and shell portions.

[0018] FIGS. 4, 5, 6 and 7 show schematic lateral sectional views of a device for carrying out successive phases of the method for direct light processing (DLP).

[0019] FIG. 8 shows a schematic sectional view along the line A-A of FIG. 7.

[0020] FIG. 9 shows a side view of an integrated core-shell mold with filaments connecting the core and shell portions.

[0021] FIG. 10 shows a side view of an integrated core-shell mold with non-linear filaments connecting the core and shell portions.

[0022] FIG. 11 shows a side view of a non-linear cooling hole in accordance with one aspect of the invention.

[0023] FIG. 12 shows a side view of a non-linear cooling hole in accordance with one aspect of the invention.

DETAILED DESCRIPTION

[0024] The detailed description set forth below in connection with the appended drawings is intended as a description of various configurations and is not intended to represent the only configurations in which the concepts described herein may be practiced. The detailed description includes specific details for the purpose of providing a thorough understanding of various concepts. However, it will be apparent to those skilled in the art that these concepts may be practiced without these specific details. For example, the present invention provides a preferred method for making cast metal parts, and preferably those cast metal parts used in the manufacture of jet aircraft engines. Specifically, the production of single crystal, nickel-based superalloy cast parts such as turbine blades, vanes, and shroud components can be advantageously produced in accordance with this invention. However, other cast metal components may be prepared using the techniques and integrated ceramic molds of the present invention.

[0025] The present inventors recognized that prior processes known for making integrated core-shell molds lacked the fine resolution capability necessary to print filaments extending between the core and shell portion of the mold of sufficiently small size and quantity to result in effusion cooling holes in the finished turbine blade. In the case of earlier powder bed processes, such as disclosed in U.S. Pat. No. 5,387,380 assigned to Massachusetts Institute of Technology, the action of the powder bed recoater arm precludes formation of sufficiently fine filaments extending between the core and shell to provide an effusion cooling hole pattern in the cast part. Other known techniques such as selective laser activation (SLA) such as disclosed in U.S. Pat. No. 5,256,340 assigned to 3D Systems, Inc. that employ a top-down irradiation technique may be utilized in producing an integrated core-shell mold in accordance with the present invention. However, the available printing resolution of these systems significantly limit the ability to make filaments of sufficiently small size to serve as effective cooling holes in the cast final product.

[0026] The present inventors have found that the integrated core-shell mold of the present invention can be manufactured using direct light processing (DLP). DLP differs from the above discussed powder bed and SLA processes in that the light curing of the polymer occurs through a window at the bottom of a resin tank that projects light upon a build platform that is raised as the process is conducted. With DLP an entire layer of cured polymer is produced simultaneously, and the need to scan a pattern using a laser is eliminated. Further, the polymerization occurs between the underlying window and the last cured layer of the object being built. The underlying window provides support allowing thin filaments of material to be produced without the need for a separate support structure. In other words, producing a thin filament of material bridging two portions of the build object is difficult and was typically avoided in the prior art. For example, the '151 patent discussed above in the background section of this application used vertical plate structures connected with short cylinders, the length of which was on the order of their diameter. Staggered vertical cavities are necessitated by the fact that the powder bed and SLA techniques disclosed in the '151 patent require vertically supported ceramic structures and the techniques are incapable of reliably producing filaments. In addition, the available resolution within a powder bed is on the order of ? resulting in a minimum feature cross sectional dimension on the order of 8 mm.sup.2, making the production of traditional cooling holes impracticable. For example, round cooling holes generally have a diameter of less than 2 mm corresponding to a cooling hole area below 3.2 mm2. Production of a hole of such dimensions requires a resolution far below the size of the actual hole given the need to produce the hole from several voxels. This resolution is simply not available in a powder bed process. Similarly, stereolithography is limited in its ability to produce such filaments due to lack of support and resolution problems associated laser scattering. But the fact that DLP exposes the entire length of the filament and supports it between the window and the build plate enables producing sufficiently thin filaments spanning the entire length between the core and shell to form a ceramic object having the desired cooling hole pattern. Although powder bed and SLA may be used to produce filaments, their ability to produce sufficiently fine filaments as discussed above is limited.

[0027] One suitable DLP process is disclosed in U.S. Pat. No. 9,079,357 assigned to Ivoclar Vivadent AG and Technische Universitat Wien, as well as WO 2010/045950 A1 and US 2011310370, each of which are hereby incorporated by reference and discussed below with reference to FIGS. 4-8. The apparatus includes a tank 404 having at least one translucent bottom portion 406 covering at least a portion of the exposure unit 410. The exposure unit 410 comprises a light source and modulator with which the intensity can be adjusted position-selectively under the control of a control unit, in order to produce an exposure field on the tank bottom 406 with the geometry desired for the layer currently to be formed. As an alternative, a laser may be used in the exposure unit, the light beam of which successively scans the exposure field with the desired intensity pattern by means of a mobile mirror, which is controlled by a control unit.

[0028] Opposite the exposure unit 410, a production platform 412 is provided above the tank 404; it is supported by a lifting mechanism (not shown) so that it is held in a height-adjustable way over the tank bottom 406 in the region above the exposure unit 410. The production platform 412 may likewise be transparent or translucent in order that light can be shone in by a further exposure unit above the production platform in such a way that, at least when forming the first layer on the lower side of the production platform 412, it can also be exposed from above so that the layer cured first on the production platform adheres thereto with even greater reliability.

[0029] The tank 404 contains a filling of highly viscous photopolymerizable material 420. The material level of the filling is much higher than the thickness of the layers which are intended to be defined for position-selective exposure. In order to define a layer of photopolymerizable material, the following procedure is adopted. The production platform 412 is lowered by the lifting mechanism in a controlled way so that (before the first exposure step) its lower side is immersed in the filling of photopolymerizable material 420 and approaches the tank bottom 406 to such an extent that precisely the desired layer thickness A (see FIG. 5) remains between the lower side of the production platform 412 and the tank bottom 406. During this immersion process, photopolymerizable material is displaced from the gap between the lower side of the production platform 412 and the tank bottom 406. After the layer thickness A has been set, the desired position-selective layer exposure is carried out for this layer, in order to cure it in the desired shape. Particularly when forming the first layer, exposure from above may also take place through the transparent or translucent production platform 412, so that reliable and complete curing takes place particularly in the contact region between the lower side of the production platform 412 and the photopolymerizable material, and therefore good adhesion of the first layer to the production platform 412 is ensured. After the layer has been formed, the production platform is raised again by means of the lifting mechanism.

[0030] These steps are subsequently repeated several times, the distance from the lower side of the layer 422 formed last to the tank bottom 406 respectively being set to the desired layer thickness A and the next layer thereupon being cured position-selectively in the desired way.

[0031] After the production platform 412 has been raised following an exposure step, there is a material deficit in the exposed region as indicated in FIG. 6. This is because after curing the layer set with the thickness A, the material of this layer is cured and raised with the production platform and the part of the shaped body already formed thereon. The photopolymerizable material therefore missing between the lower side of the already formed shaped body part and the tank bottom 406 must be filled from the filling of photopolymerizable material 420 from the region surrounding the exposed region. Owing to the high viscosity of the material, however, it does not flow by itself back into the exposed region between the lower side of the shaped body part and the tank bottom, so that material depressions or holes can remain here.

[0032] In order to replenish the exposure region with photopolymerizable material, an elongate mixing element 432 is moved through the filling of photopolymerizable material 420 in the tank. In the exemplary embodiment represented in FIGS. 4 to 8, the mixing element 432 comprises an elongate wire which is tensioned between two support arms 430 mounted movably on the side walls of the tank 404. The support arms 430 may be mounted movably in guide slots 434 in the side walls of the tank 404, so that the wire 432 tensioned between the support arms 430 can be moved relative to the tank 404, parallel to the tank bottom 406, by moving the support arms 430 in the guide slots 434. The elongate mixing element 432 has dimensions, and its movement is guided relative to the tank bottom, such that the upper edge of the elongate mixing element 432 remains below the material level of the filling of photopolymerizable material 420 in the tank outside the exposed region. As can be seen in the sectional view of FIG. 8, the mixing element 432 is below the material level in the tank over the entire length of the wire, and only the support arms 430 protrude beyond the material level in the tank. The effect of arranging the elongate mixing element below the material level in the tank 404 is not that the elongate mixing element 432 substantially moves material in front of it during its movement relative to the tank through the exposed region, but rather this material flows over the mixing element 432 while executing a slight upward movement. The movement of the mixing element 432 from the position shown in FIG. 6, to, for example, a new position in the direction indicated by the arrow A, is shown in FIG. 7. It has been found that by this type of action on the photopolymerizable material in the tank, the material is effectively stimulated to flow back into the material-depleted exposed region between the production platform 412 and the exposure unit 410.

[0033] The movement of the elongate mixing element 432 relative to the tank may firstly, with a stationary tank 404, be carried out by a linear drive which moves the support arms 430 along the guide slots 434 in order to achieve the desired movement of the elongate mixing element 432 through the exposed region between the production platform 412 and the exposure unit 410. As shown in FIG. 8, the tank bottom 406 has recesses 406 on both sides. The support arms 430 project with their lower ends into these recesses 406. This makes it possible for the elongate mixing element 432 to be held at the height of the tank bottom 406, without interfering with the movement of the lower ends of the support arms 430 through the tank bottom 406.

[0034] Other alternative methods of DLP may be used to prepare the integrated core-shell molds of the present invention. For example, the tank may be positioned on a rotatable platform. When the workpiece is withdrawn from the viscous polymer between successive build steps, the tank may be rotated relative to the platform and light source to provide a fresh layer of viscous polymer in which to dip the build platform for building the successive layers.

[0035] FIG. 9 shows a schematic side view of an integrated core-shell mold with filaments 902 connecting the core 900 and shell portions 901. By printing the ceramic mold using the above DLP printing process, the mold can be made in a way that allows the point of connections between the core and shell to be provided through filaments 902. Once the core-shell mold is printed, it may be subject to a post-heat treatment step to cure the printed ceramic polymer material. The cured ceramic mold may then be used similar to the traditional casting process used in the production of superalloy turbine blades. Notably because the filaments 902 are provided in a large quantity consistent with formation of a pattern of effusion cooling holes in the surface of a turbine blade, the need for a ball chute structure as shown in FIG. 2 may be eliminated. In this embodiment, the tip pins 905 connecting the tip plenum core 904 to the core 900 are retained. After removal of the ceramic mold, tip holes exist between the core 900 and tip plenum core 904 that may be subsequently brazed shut. However, the tip pins 905 may be eliminated, avoiding the need to braze shut tip holes connecting the core cavity with the tip plenum.

[0036] The filaments 902 are preferably cylindrical or oval shape but may be curved or non-linear. Their exact dimensions may be varied according to a desired film cooling scheme for a particular cast metal part. For example cooling holes may have a cross sectional area ranging from 0.01 to 2 mm.sup.2. In a turbine blade, the cross sectional area may range from 0.01 to 0.15 mm.sup.2, more preferably from 0.05 to 0.1 mm.sup.2, and most preferably about 0.07 mm.sup.2. In the case of a vane, the cooling holes may have a cross sectional area ranging from 0.05 to 0.2 mm.sup.2, more preferably 0.1 to 0.18 mm.sup.2, and most preferably about 0.16 mm.sup.2. The spacing of the cooling holes is typically a multiple of the diameter of the cooling holes ranging from 2? to 10? the diameter of the cooling holes, most preferably about 4-7? the diameter of the holes.

[0037] The length of the filament 902 is dictated by the thickness of the cast component, e.g., turbine blade or stator vane wall thickness, and the angle at which the cooling hole is disposed relative to the surface of the cast component. The typical lengths range from 0.5 to 5 mm, more preferably between 0.7 to 1 mm, and most preferably about 0.9 mm. The angle at which a cooling hole is disposed is approximately 5 to 35? relative to the surface, more preferably between 10 to 20?, and most preferably approximately 12?. It should be appreciated that the methods of casting according to the present invention allow for formation of cooling holes having a lower angle relative to the surface of the cast component than currently available using conventional machining techniques.

[0038] The specific shape of a cooling hole made in accordance with the present invention is determined by the shape of the filament connecting the core to the shell portion of the mold. Because the process for making filaments allows complete control over the dimensions of the filament, the present invention can be used to make any shape cooling hole. Moreover, a single cast object may be provided with several kinds of cooling hole designs. The following describes several non-limiting examples for cooling hole designs that may be used in accordance with the present invention. One key characteristic of the cooling holes of the present invention is that they may be provided with a non-line-of-sight shape. In practice, cooling holes drilled through a completed turbine blade using electro discharge machining (EDM) were limited to cooling holes that were generally shaped to have a line of sight through the cast metal object. This is because the EDM apparatus has a generally linear shape and operates by drilling through outer surface of the cast object to reach the core cavity. It is generally not possible to drill from the core cavity side of the cast object because the core cavity is inaccessible.

[0039] FIG. 10 shows a schematic side view of an integrated core-shell mold with non-linear filaments 1002 in accordance with the present invention connecting the core 1000 and shell portions 1001. By printing the ceramic mold using the above DLP printing process, the mold can be made in a way that allows the point of connections between the core and shell to be provided through non-linear filaments 1002. Once the core-shell mold is printed, it may be subject to a post-heat treatment step to cure the printed ceramic polymer material. The cured ceramic mold may then be used similar to the traditional casting process used in the production of superalloy turbine blades. Notably because the non-linear filaments 1002 are provided in a large quantity consistent with formation of a pattern of effusion cooling holes in the surface of a turbine blade, the need for a ball chute structure as shown in FIG. 2 may be eliminated. In this embodiment, the tip pins 1005 connecting the tip plenum core 1004 to the core 1000 are retained. After removal of the ceramic mold, tip holes exist between the core 1000 and tip plenum core 1004 that may be subsequently brazed shut. However, the tip pins 1005 may be eliminated, avoiding the need to braze shut tip holes connecting the core cavity with the tip plenum.

[0040] The non-linear filaments 1002 are preferably cylindrical or oval shape. Their exact dimensions may be varied according to a desired film cooling scheme for a particular cast metal part. For example cooling holes may have a cross sectional area ranging from 0.01 to 2 mm.sup.2. In a turbine blade, the cross sectional area may range from 0.01 to 0.15 mm.sup.2, more preferably from 0.05 to 0.1 mm.sup.2, and most preferably about 0.07 mm.sup.2. In the case of a vane, the cooling holes may have a cross sectional area ranging from 0.05 to 0.2 mm.sup.2, more preferably 0.1 to 0.18 mm.sup.2, and most preferably about 0.16 mm.sup.2. The spacing of the cooling holes is typically a multiple of the diameter of the cooling holes ranging from 2? to 10? the diameter of the cooling holes, most preferably about 4-7? the diameter of the holes.

[0041] The length of the filament 1002 is dictated by the thickness of the cast component, e.g., turbine blade wall thickness, and the angle at which the cooling hole is disposed relative to the surface of the cast component. The typical lengths range from 0.5 to 5 mm, more preferably between 0.7 to 1 mm, and most preferably about 0.9 mm. The angle at which a cooling hole is disposed is approximately 5 to 35? relative to the surface, more preferably between 10 to 20?, and most preferably approximately 12?. It should be appreciated that the methods of casting according to the present invention allow for formation of cooling holes having a lower angle relative to the surface of the cast component that currently available using conventional machining techniques.

[0042] The present invention relates also to methods of making cast metal objects, in particular single crystal turbine blades and stators used in jet aircraft engines that have non-linear cooling holes such as the exemplary design shown in FIG. 10. The method begins with the production of the ceramic mold using DLP. The DLP process involves a repetition of steps of (a) contacting a cured portion of a workpiece with a liquid ceramic photopolymer; (b) irradiating a portion of the liquid ceramic photopolymer adjacent to the cured portion through a window contacting the liquid ceramic photopolymer; and (c) removing the workpiece from the uncured liquid ceramic photopolymer. The steps (a)-(c) are repeated until the ceramic mold shown in FIG. 10 is formed. After the mold is formed, liquid metal may then be poured into the casting mold and solidified to form the cast component. The ceramic mold is then removed from the cast component using, for example, combination of mechanical removal of the outer shell and leaching of the inner ceramic core.

[0043] The specific geometry of the non-linear cooling hole filaments shown in FIG. 10 may be varied based on the needs for specific effusion cooling hole pattern to be placed in the turbine blade or stator. For example, the direction of the hole may be opposite that shown in FIG. 10 with holes aligned toward the top of the turbine blade. The filament may have a curvature that forms an S shaped hold upon removal of the mold. Alternatively, the holes may be aligned horizontally along the turbine blade such that they project inward or alternatively outward of the page. Given the flexibility possible for DLP processing, there are no limitations on the shape of the cooling hole. A few alternative exemplary cooling hole geometries are shown in FIGS. 11 and 12.

[0044] FIG. 11 shows a side view of a non-linear cooling hole that can be made in a cast object in accordance with one aspect of the invention. In this example, the effusion cooling hole 1110 extends from the inner surface 1102 of the cast component 1100 to the outer surface 1104 of the cast component 1100. The cooling hole 1110 has an upstream portion 1120 with an inlet 1122, an intermediate portion 1140, and a downstream portion 1130 with an outlet 1132. The cooling hole 1110 has a non-linear line of sight, meaning that no virtual, single straight line segment may be extended between the inlet 1122 and outlet 1132, given the areas of the inlet 1122 and outlet 1132, and the diameters, shapes, and angles of the respective portions 1120, 1130. The exemplary cooling hole geometry may be implemented by printing a filament in the reverse pattern of the cooling hole within a core-shell assembly such as shown in FIG. 10.

[0045] FIG. 12 shows an effusion cooling hole 1210 in accordance with an embodiment of the invention. The cooling hole 1210 extends from the inner surface 1202 of the cast component 1200, through the cast component 1200, to an outer surface 1204 of the cast component 1200. The cooling hole 1210 extends from an upstream portion 1220 with an inlet 1222, through a chamber 1240, to a downstream portion 1230 with an outlet 1232 to the outer surface of the cast object. The cooling hole 1210 of the present invention may have a chamber 1240 that is defined by having at least one height or width dimension that is greater than the minimum diameter of the inlet 1220. The cooling hole may have a ramp structure 1224 adjacent to the inlet 1220.

[0046] The chamber 1240 is designed to provide additional heat transfer capability to the cooling holes while serving as a trap for dust and particulate matter that makes its way into the supply of cooling air. This can be particularly advantageous when operating a jet aircraft in dusty or sandy environments. Preventing dust or sand from entering the flowpath can add useful life to downstream engine parts that may be damaged over time by dust or sand contamination. For example, turbine blades and stators in the low pressure turbine region of the jet aircraft engine may benefit from reduced contamination. In addition the ramp structure 1224 can optionally be included in the design to further reduce contamination by sand or dust.

[0047] After leaching, the resulting holes in the turbine blade from the core print filaments may be brazed shut if desired. Otherwise the holes left by the core print filaments may be incorporated into the design of the internal cooling passages. Alternatively, cooling hole filaments may be provided to connect the tip plenum core to the shell in a sufficient quantity to hold the tip plenum core in place during the metal casting step

[0048] After printing the core-shell mold structures in accordance with the invention, the core-shell mold may be cured and/or fired depending upon the requirements of the ceramic core photopolymer material. Molten metal may be poured into the mold to form a cast object in the shape and having the features provided by the integrated core-shell mold. In the case of a turbine blade, the molten metal is preferably a superalloy metal that formed into a single crystal superalloy turbine blade using techniques known to be used with conventional investment casting molds.

[0049] In an aspect, the present invention relates to the core-shell mold structures of the present invention incorporated or combined with features of other core-shell molds produced in a similar manner. The following patent applications include disclosure of these various aspects and their use:

[0050] U.S. patent application Ser. No. [ ], titled INTEGRATED CASTING CORE-SHELL STRUCTURE with attorney docket number 037216.00036/284976, and filed Dec. 13, 2016;

[0051] U.S. patent application Ser. No. [ ], titled INTEGRATED CASTING CORE-SHELL STRUCTURE WITH FLOATING TIP PLENUM with attorney docket number 037216.00037/284997, and filed Dec. 13, 2016;

[0052] U.S. patent application Ser. No. [ ], titled MULTI-PIECE INTEGRATED CORE-SHELL STRUCTURE FOR MAKING CAST COMPONENT with attorney docket number 037216.00033/284909, and filed Dec. 13, 2016;

[0053] U.S. patent application Ser. No. [ ], titled MULTI-PIECE INTEGRATED CORE-SHELL STRUCTURE WITH STANDOFF AND/OR BUMPER FOR MAKING CAST COMPONENT with attorney docket number 037216.00042/284909A, and filed Dec. 13, 2016;

[0054] U.S. patent application Ser. No. [ ], titled INTEGRATED CASTING CORE SHELL STRUCTURE WITH PRINTED TUBES FOR MAKING CAST COMPONENT with attorney docket number 037216.00032/284917, and filed Dec. 13, 2016;

[0055] U.S. patent application Ser. No. [ ], titled INTEGRATED CASTING CORE-SHELL STRUCTURE AND FILTER FOR MAKING CAST COMPONENT with attorney docket number 037216.00039/285021, and filed Dec. 13, 2016;

[0056] U.S. patent application Ser. No. [ ], titled INTEGRATED CASTING CORE SHELL STRUCTURE FOR MAKING CAST COMPONENT WITH COOLING HOLES IN INACCESSIBLE LOCATIONS with attorney docket number 037216.00055/285064A, and filed Dec. 13, 2016;

[0057] U.S. patent application Ser. No. [ ], titled INTEGRATED CASTING CORE SHELL STRUCTURE FOR MAKING CAST COMPONENT HAVING THIN ROOT COMPONENTS with attorney docket number 037216.00053/285064B, and filed Dec. 13, 2016.

[0058] The disclosures of each of these applications are incorporated herein in their entirety to the extent they disclose additional aspects of core-shell molds and methods of making that can be used in conjunction with the core-shell molds disclosed herein.

[0059] This written description uses examples to disclose the invention, including the preferred embodiments, and also to enable any person skilled in the art to practice the invention, including making and using any devices or systems and performing any incorporated methods. The patentable scope of the invention is defined by the claims, and may include other examples that occur to those skilled in the art. Such other examples are intended to be within the scope of the claims if they have structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal language of the claims. Aspects from the various embodiments described, as well as other known equivalents for each such aspect, can be mixed and matched by one of ordinary skill in the art to construct additional embodiments and techniques in accordance with principles of this application.