INTEGRATED CASTING CORE-SHELL STRUCTURE FOR MAKING CAST COMPONENTS HAVING THIN ROOT COMPONENTS

Abstract

The present disclosure generally relates to integrated core-shell investment casting molds that provide an indentation structure corresponding to a thin root component of the turbine blade or vane (i.e. angel wing, skirt, damper lug).

Claims

1. A method for fabricating a ceramic mold for a turbine blade or vane, comprising: (a) contacting a cured portion of a workpiece with a liquid ceramic photopolymer; (b) irradiating a portion of the liquid ceramic photopolymer adjacent to the cured portion through a window contacting the liquid ceramic photopolymer; (c) removing the workpiece from the uncured liquid ceramic photopolymer; and (d) repeating steps (a)-(c) until a ceramic mold is formed, the ceramic mold comprising: (1) a core portion and a shell portion with at least one cavity between the core portion and the shell portion, the cavity adapted to define the shape of the turbine blade or vane upon casting and removal of the ceramic mold, and (2) the cavity defining a turbine blade or vane root component having a minimum dimension of less than 0.64 mm.

2. The method of claim 1, wherein the process comprises, after step (d), a step (e) comprising pouring a liquid metal into a casting mold and solidifying the liquid metal to form the cast component.

3. The method of claim 2, wherein the process comprises, after step (e), a step (f) comprising removing the mold from the cast component.

4. The method of claim 3, wherein removing the mold from the cast component comprises a combination of mechanical force and chemical leaching.

5. The method of claim 1, wherein the turbine blade or vane root component has a minimum dimension in the range of 0.1 and 0.6 mm.

6. The method of claim 1, wherein the turbine blade or vane root component has a minimum dimension in the range of 0.2 and 0.5 mm.

7. The method of claim 1, wherein the turbine blade or vane root component is an angel wing, skirt, or damper lug.

8. A method of preparing a turbine blade or vane comprising: (a) pouring a liquid metal into a ceramic casting mold and solidifying the liquid metal to form the turbine blade or vane, the ceramic casting mold comprising: (1) a core portion and a shell portion with at least one cavity between the core portion and the shell portion, the cavity adapted to define the shape of the turbine blade or vane upon casting and removal of the ceramic mold, and (2) the cavity defining a turbine blade or vane root component having a minimum dimension of less than 0.64 mm. (b) removing the ceramic casting mold from the cast component by leaching at least a portion of the ceramic core through the holes in the turbine blade or vane.

9. The method of claim 8, wherein removing the ceramic casting mold from the cast component comprises a combination of mechanical force and chemical leaching.

10. The method of claim 8, wherein the turbine blade or vane root component has a minimum dimension in the range of 0.1 and 0.6 mm.

11. The method of claim 8, wherein the turbine blade or vane root component is an angel wing, skirt, or damper lug.

12. A ceramic casting mold comprising: a core portion and a shell portion with at least one cavity between the core portion and the shell portion, the cavity adapted to define the shape of a cast component upon casting and removal of the ceramic mold, and the cavity defining a turbine blade or vane root component having a minimum dimension of less than 0.64 mm.

13. The ceramic casting mold of claim 12, wherein the turbine blade or vane root component has a minimum dimension in the range of 0.1 and 0.6 mm.

14. The ceramic casting mold of claim 12, wherein the turbine blade or vane root component has a minimum dimension in the range of 0.2 and 0.5 mm.

15. The ceramic casting mold of claim 12, wherein the turbine blade or vane root component is an angel wing, skirt, or damper lug.

16. A single crystal metal turbine blade or vane having an inner cavity and an outer surface, a plurality of cooling holes providing fluid communication between the inner cavity and outer surface, and a turbine blade root component having a minimum dimension of less than 0.64 mm.

17. The single crystal metal turbine blade or vane of claim 16, wherein the turbine blade or vane root component has a minimum dimension in the range of 0.1 and 0.6 mm.

18. The single crystal metal turbine blade or vane of claim 16, wherein the turbine blade or vane root component has a minimum dimension in the range of 0.2 and 0.5 mm.

19. The single crystal metal turbine blade or vane of claim 16, wherein the turbine blade or vane root component is an angel wing, skirt, or damper lug.

20. The single crystal metal turbine blade or vane of claim 16, where the single crystal metal is a superalloy.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0014] FIG. 1 is a flow diagram showing the steps for conventional investment casting.

[0015] FIG. 2 is a schematic diagram showing an example of a conventional scheme for a core-shell mold with ball chute prepared by a conventional process.

[0016] FIG. 3 shows a perspective view of a prior art integrated core-shell mold with ties connecting the core and shell portions.

[0017] FIGS. 4, 5, 6 and 7 show schematic lateral sectional views of a device for carrying out successive phases of the method sequence for direct light processing (DLP).

[0018] FIG. 8 shows a schematic sectional view along the line A-A of FIG. 7.

[0019] FIG. 9 shows a perspective view of a turbine blade root portion made in accordance with an embodiment of the present invention

DETAILED DESCRIPTION

[0020] The detailed description set forth below in connection with the appended drawings is intended as a description of various configurations and is not intended to represent the only configurations in which the concepts described herein may be practiced. The detailed description includes specific details for the purpose of providing a thorough understanding of various concepts. However, it will be apparent to those skilled in the art that these concepts may be practiced without these specific details. For example, the present invention provides a preferred method for making cast metal parts, and preferably those cast metal parts used in the manufacture of jet aircraft engines. Specifically, the production of single crystal, nickel-based superalloy cast parts such as turbine blades, stator vanes, and shroud components can be advantageously produced in accordance with this invention. However, other cast metal components may be prepared using the techniques and integrated ceramic molds of the present invention.

[0021] The present inventors recognized that prior processes known for making turbine blades and stator vanes i.e. investment casting, lacked the fine resolution capability necessary to produce turbine blades and vanes having thin blade root elements. In particular, the wax processing step in investment casting severely limits the ability to manufacture turbine blades where the blade or vane root elements may be made as thin or as fine as desired.

[0022] The present inventors have found that the integrated core-shell mold of the present invention can be manufactured using direct light processing (DLP). DLP differs from powder bed and SLA processes in that the light curing of the polymer occurs through a window at the bottom of a resin tank that projects light upon a build platform that is raised as the process is conducted. With DLP an entire layer of cured polymer is produced simultaneously, and the need to scan a pattern using a laser is eliminated. Further, the polymerization occurs between the underlying window and the last cured layer of the object being built. The underlying window provides support allowing thin filaments of material to be produced without the need for a separate support structure. In other words, producing a thin filament of material bridging two portions of the build object is difficult and was typically avoided in the prior art. For example, U.S. Pat. No. 8,851,151 assigned to Rolls-Royce Corporation describes a 3-D printing method of producing a ceramic core-shell mold that used vertical plate structures connected with short cylinders, the length of which was on the order of their diameter. Staggered vertical cavities are necessitated by the fact that the powder bed and SLA techniques disclosed in the '151 patent require vertically supported ceramic structures and the techniques are incapable of reliably producing thin indentations or recesses that correspond to thin turbine blade root components (i.e. angel wings, damper lugs, skirts) of the cast turbine blade. In addition, the available resolution within a powder bed is on the order of (3.2 mm) making the production of thin turbine blade root components impracticable. For example, these thin turbine blade root components generally have a minimum dimension of less 0.64 mm, preferably in the range of 0.1 to 0.6 mm, more preferably in the range of 0.2 to 0.5 mm. As used herein, the term minimum dimension means smallest possible dimension. Production of a turbine blade root component of such dimensions requires a resolution simply not available in a powder bed process. Similarly, stereolithography is limited in its ability to produce such thin indentations due lack of support and resolution problems associated with laser scattering. But the fact that DLP exposes the entire length of the indentation and supports it between the window and the build plate enables producing sufficiently thin indentations having the desired minimum dimensions . Although powder bed and SLA may be used to produce indentations, their ability to produce sufficiently fine indentations as discussed above is limited.

[0023] One suitable DLP process is disclosed in U.S. Pat. No. 9,079,357 assigned to Ivoclar Vivadent AG and Technische Universitat Wien, as well as WO 2010/045950 A1 and US 2011310370, each of which are hereby incorporated by reference and discussed below with reference to FIGS. 4-8. The apparatus includes a tank 404 having at least one translucent bottom portion 406 covering at least a portion of the exposure unit 410. The exposure unit 410 comprises a light source and modulator with which the intensity can be adjusted position-selectively under the control of a control unit, in order to produce an exposure field on the tank bottom 406 with the geometry desired for the layer currently to be formed. As an alternative, a laser may be used in the exposure unit, the light beam of which successively scans the exposure field with the desired intensity pattern by means of a mobile mirror, which is controlled by a control unit.

[0024] Opposite the exposure unit 410, a production platform 412 is provided above the tank 404; it is supported by a lifting mechanism (not shown) so that it is held in a height-adjustable way over the tank bottom 406 in the region above the exposure unit 410. The production platform 412 may likewise be transparent or translucent in order that light can be shone in by a further exposure unit above the production platform in such a way that, at least when forming the first layer on the lower side of the production platform 412, it can also be exposed from above so that the layer cured first on the production platform adheres thereto with even greater reliability.

[0025] The tank 404 contains a filling of highly viscous photopolymerizable material 420. The material level of the filling is much higher than the thickness of the layers which are intended to be defined for position-selective exposure. In order to define a layer of photopolymerizable material, the following procedure is adopted. The production platform 412 is lowered by the lifting mechanism in a controlled way so that (before the first exposure step) its lower side is immersed in the filling of photopolymerizable material 420 and approaches the tank bottom 406 to such an extent that precisely the desired layer thickness (see FIG. 5) remains between the lower side of the production platform 412 and the tank bottom 406. During this immersion process, photopolymerizable material is displaced from the gap between the lower side of the production platform 412 and the tank bottom 406. After the layer thickness has been set, the desired position-selective layer exposure is carried out for this layer, in order to cure it in the desired shape. Particularly when forming the first layer, exposure from above may also take place through the transparent or translucent production platform 412, so that reliable and complete curing takes place particularly in the contact region between the lower side of the production platform 412 and the photopolymerizable material, and therefore good adhesion of the first layer to the production platform 412 is ensured. After the layer has been formed, the production platform is raised again by means of the lifting mechanism.

[0026] These steps are subsequently repeated several times, the distance from the lower side of the layer 422 formed last to the tank bottom 406 respectively being set to the desired layer thickness and the next layer thereupon being cured position-selectively in the desired way.

[0027] After the production platform 412 has been raised following an exposure step, there is a material deficit in the exposed region as indicated in FIG. 6. This is because after curing the layer set with the thickness , the material of this layer is cured and raised with the production platform and the part of the shaped body already formed thereon. The photopolymerizable material therefore missing between the lower side of the already formed shaped body part and the tank bottom 406 must be filled from the filling of photopolymerizable material 420 from the region surrounding the exposed region. Owing to the high viscosity of the material, however, it does not flow by itself back into the exposed region between the lower side of the shaped body part and the tank bottom, so that material depressions or holes can remain here.

[0028] In order to replenish the exposure region with photopolymerizable material, an elongate mixing element 432 is moved through the filling of photopolymerizable material 420 in the tank. In the exemplary embodiment represented in FIGS. 4 to 8, the mixing element 432 comprises an elongate wire which is tensioned between two support arms 430 mounted movably on the side walls of the tank 404. The support arms 430 may be mounted movably in guide slots 434 in the side walls of the tank 404, so that the wire 432 tensioned between the support arms 430 can be moved relative to the tank 404, parallel to the tank bottom 406, by moving the support arms 430 in the guide slots 434. The elongate mixing element 432 has dimensions, and its movement is guided relative to the tank bottom, such that the upper edge of the elongate mixing element 432 remains below the material level of the filling of photopolymerizable material 420 in the tank outside the exposed region. As can be seen in the sectional view of FIG. 8, the mixing element 432 is below the material level in the tank over the entire length of the wire, and only the support arms 430 protrude beyond the material level in the tank. The effect of arranging the elongate mixing element below the material level in the tank 404 is not that the elongate mixing element 432 substantially moves material in front of it during its movement relative to the tank through the exposed region, but rather this material flows over the mixing element 432 while executing a slight upward movement. The movement of the mixing element 432 from the position shown in FIG. 6, to, for example, a new position in the direction indicated by the arrow A, is shown in FIG. 7. It has been found that by this type of action on the photopolymerizable material in the tank, the material is effectively stimulated to flow back into the material-depleted exposed region between the production platform 412 and the exposure unit 410.

[0029] The movement of the elongate mixing element 432 relative to the tank may firstly, with a stationary tank 404, be carried out by a linear drive which moves the support arms 430 along the guide slots 434 in order to achieve the desired movement of the elongate mixing element 432 through the exposed region between the production platform 412 and the exposure unit 410. As shown in FIG. 8, the tank bottom 406 has recesses 406 on both sides. The support arms 430 project with their lower ends into these recesses 406. This makes it possible for the elongate mixing element 432 to be held at the height of the tank bottom 406, without interfering with the movement of the lower ends of the support arms 430 through the tank bottom 406.

[0030] Other alternative methods of DLP may be used to prepare the integrated core-shell molds of the present invention. For example, the tank may be positioned on a rotatable platform. When the workpiece is withdrawn from the viscous polymer between successive build steps, the tank may be rotated relative to the platform and light source to provide a fresh layer of viscous polymer in which to dip the build platform for building the successive layers.

[0031] The present invention may be used to make turbine blades and stator vanes having root feature minimum dimensions of less than 0.64 mm. As shown in FIG. 9, the blade 900 includes an airfoil 902, a platform 904, a shank 906, and a multi-lobe dovetail 908 having a fir tree configuration. The angel wings 910, 912 and 914, skirt 918, and damper retention lugs 924, 926 preferably have a thickness of less than 0.64 mm. In general angel wings may range in thickness from 0.1 to 0.6 mm, more preferably in the range of 0.2 and 0.5 mm. The thinner dimensions of the turbine blade or vane root features allows for a significant reduction in weight and enables novel designs. It will be appreciated that the specific design of the blade shown in FIG. 9 is for illustrative purposes only and in no way limits the invention. It should be noted that turbine blades and vanes generally have root features and that those turbine blade or vane designs may be prepared using the present methods in order to achieve a reduction in weight.

[0032] After printing the core-shell mold structures in accordance with the invention, the core-shell mold may be cured and/or fired depending upon the requirements of the ceramic core photopolymer material. Molten metal may be poured into the mold to form a cast object in the shape and having the features provided by the integrated core-shell mold. In the case of a turbine blade or stator vane, the molten metal is preferably a superalloy metal that formed into a single crystal superalloy turbine blade or stator vane using techniques known to be used with conventional investment casting molds.

[0033] In an aspect, the present invention relates to the core-shell mold structures of the present invention incorporated or combined with features of other core-shell molds produced in a similar manner. The following patent applications include disclosure of these various aspects and their use:

[0034] U.S. patent application Ser. No. ______, titled INTEGRATED CASTING CORE-SHELL STRUCTURE with attorney docket number 037216.00036/284976, and filed Dec. 13, 2016;

[0035] U.S. patent application Ser. No. ______, titled INTEGRATED CASTING CORE-SHELL STRUCTURE WITH FLOATING TIP PLENUM with attorney docket number 037216.00037/284997, and filed Dec. 13, 2016;

[0036] U.S. patent application Ser. No. ______, titled MULTI-PIECE INTEGRATED CORE-SHELL STRUCTURE FOR MAKING CAST COMPONENT with attorney docket number 037216.00033/284909, and filed Dec. 13, 2016;

[0037] U.S. patent application Ser. No. ______, titled MULTI-PIECE INTEGRATED CORE-SHELL STRUCTURE WITH STANDOFF AND/OR BUMPER FOR MAKING CAST COMPONENT with attorney docket number 037216.00042/284909A, and filed Dec. 13, 2016;

[0038] U.S. patent application Ser. No. ______, titled INTEGRATED CASTING CORE SHELL STRUCTURE WITH PRINTED TUBES FOR MAKING CAST COMPONENT with attorney docket number 037216.00032/284917, and filed Dec. 13, 2016;

[0039] U.S. patent application Ser. No. ______, titled INTEGRATED CASTING CORE-SHELL STRUCTURE AND FILTER FOR MAKING CAST COMPONENT with attorney docket number 037216.00039/285021, and filed Dec. 13, 2016;

[0040] U.S. patent application Ser. No. ______, titled INTEGRATED CASTING CORE SHELL STRUCTURE FOR MAKING CAST COMPONENT WITH NON-LINEAR HOLES with attorney docket number 037216.00041/285064, and filed Dec. 13, 2016;

[0041] U.S. patent application Ser. No. ______, titled INTEGRATED CASTING CORE SHELL STRUCTURE FOR MAKING CAST COMPONENT WITH COOLING HOLES IN INACCESSIBLE LOCATIONS with attorney docket number 037216.00055/285064A, and filed Dec. 13, 2016.

[0042] The disclosures of each of these applications are incorporated herein in their entireties to the extent they disclose additional aspects of core-shell molds and methods of making that can be used in conjunction with the core-shell molds disclosed herein.

[0043] This written description uses examples to disclose the invention, including the preferred embodiments, and also to enable any person skilled in the art to practice the invention, including making and using any devices or systems and performing any incorporated methods. The patentable scope of the invention is defined by the claims, and may include other examples that occur to those skilled in the art. Such other examples are intended to be within the scope of the claims if they have structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal language of the claims. Aspects from the various embodiments described, as well as other known equivalents for each such aspect, can be mixed and matched by one of ordinary skill in the art to construct additional embodiments and techniques in accordance with principles of this application.