Antifouling system comprising silicone hydrogel

Abstract

A multi-layer or single layer antifouling coating system. A multi-layer coating system comprises (a) a base coating for coating a substrate, and (b) an antifouling coating composition adapted to be disposed over the base coating, the antifouling coating composition comprising a hydroxyl terminated polydimethylsiloxane, a curable polyether-containing silane of the Formula (1):
(R.sup.1O).sub.a(R.sup.1).sub.(3-a)SiR.sup.2(Si(R.sup.1).sub.2O).sub.pSi(R.sup.1).sub.2R.sup.2O(CH.sub.2CHR.sup.1O).sub.qR.sup.1(1)
where a is 1-3; R.sup.1 is H or alkyl radical from C.sub.1-C.sub.10; R2 is alkylene from C.sub.2-C.sub.10; p is 1-100; and q is 1-50. The base coating composition can comprise an epoxy modified adhesion promoter. A single layer coating composition comprises a compound of Formula (4):
(R.sup.1O).sub.a(R.sup.1).sub.3-aSi-M-(Si(R.sup.1).sub.2O).sub.r(Si(R.sup.1)(O.sub.1/2)(O)).sub.t(Si(X)(O.sub.1/2)(O)).sub.vSi(R.sup.1).sub.2-M-Si(OR.sup.1).sub.a(R.sup.1).sub.3-a(4)
where R.sup.1 is H or an alkyl radical M is R.sup.2 or oxygen; r is 0-1000; t is 1 to 20; v is 0 to 20; X is R.sup.2(N(R.sup.1).sub.1-b(Y).sub.bR.sup.2).sub.cN(R.sup.1).sub.2-b(Y).sub.b; b is 0-2; c is 0-5; Y is R.sup.1 or an organic radical with an epoxide at one terminal; and R.sup.2 is an alkylene from C.sub.2-C.sub.10, with the proviso that at least one Y is an organic radical with an epoxide at one terminal. The respective compositions are such that the antifouling coating composition sufficiently adheres to the base coating composition without the need for a tie coat layer.

Claims

1. An antifouling coating system comprising: a base coating composition comprising a base coating material and a first adhesion promoter comprising an epoxy modified adhesion promoter; and an antifouling coating composition comprising a silane of the formula:
(R.sup.1O).sub.a(R.sup.1).sub.(3-a)SiR.sup.2(Si(R.sup.1).sub.2O).sub.pSi(R.sup.1).sub.2R.sup.2O(CH.sub.2CHR.sup.1O).sub.qR.sup.1 where a is 1-3; R.sup.1 is H or alkyl radical from C.sub.1-C.sub.10; R.sup.2 is alkylene from C.sub.2-C.sub.10; p is 1-100; q is 1-50, a second adhesion promoter, optionally an inorganic filler, optionally a silane cross linker, and optionally a condensation catalyst.

2. The antifouling coating system of claim 1, wherein R.sup.1 is a C.sub.1-C.sub.10 alkyl.

3. The antifouling system of claim 1, wherein R.sup.1 is methyl.

4. The antifouling system of claim 1, wherein the silane is: ##STR00007##

5. The antifouling system of claim 1, wherein the antifouling composition comprises a hydroxyl terminated polymer that is capable of reacting with the silane.

6. The antifouling system of claim 5, wherein the hydroxyl terminated polymer is a silanol terminated polymer.

7. The antifouling system of claim 5, wherein the hydroxyl terminated polymer is of the formula: ##STR00008## where R.sup.3 is individually chosen from OH, OR.sup.1, alkyl, and combinations of two or more thereof; R.sup.1 is H or an alkyl radical; R.sup.4 is individually chosen from an alkyl, an aryl fluoro alkyl, a fluoro aryl, an alkyl aryl or R.sup.5; and R.sup.5 and R.sup.6 are individually OH or OR.sup.1, with at least one of R.sup.3, R.sup.4, R.sup.5, R.sup.6, or a combination thereof being OH.

8. The antifouling system of claim 1, wherein the epoxy modified adhesion promoter comprises at least one molecule having the chemical formula:
(R.sup.1O).sub.a(R.sup.1).sub.3-aSi-M-(Si(R.sup.1).sub.2O).sub.r(Si(R.sup.1)(O.sub.1/2R.sup.1)(O)).sub.t(Si(X)(O.sub.1/2R.sup.1(O)).sub.vSi(R.sup.1).sub.2-M-Si(OR.sup.1).sub.a(R.sup.1).sub.3-a where R.sup.1 is H or an alkyl radical, M is R.sup.2 or oxygen; r is 0-1000; t is 1 to 20; v is 1 to 20; X is R.sup.2(N(R.sup.1).sub.1-b(Y).sub.bR.sup.2).sub.c-MR.sup.1).sub.2-b(Y).sub.b; b is 0-2; c is 0-5; Y is R.sup.1 or an organic radical with an epoxide at one terminal; and R.sup.2 is an alkylene from C.sub.2-C.sub.10, with the proviso that at least one Y is an organic radical with an epoxide at one terminal.

9. The antifouling system of claim 8, wherein the epoxy modified adhesion promoter is made in situ by addition to a base coating composition comprising an epoxy resin at least one molecule having the chemical formula:
(R.sub.1O).sub.a(R.sup.1).sub.3-aSi-M-(Si(R.sup.1).sub.2O.sub.r(Si(R.sup.1)(O.sub.1/2R.sup.1)(O)).sub.t(Si(Z)(O.sub.1/2R.sup.1)(O)).sub.vSi(R.sup.1).sub.2-M-Si(OR.sup.1).sub.a(R.sup.1).sub.3-a where R.sup.1 is H or an alkyl radical; M is R.sup.2 or oxygen; r is 0-1000; t is 1 to 20; v is 0 to 20; Z is R.sup.2(NR.sup.1R.sub.2).sub.cNR.sup.1.sub.2; and c is 0-5.

10. The antifouling system of claim 8, wherein Y comprises a radical of partially ring opened bisphenol A diglycidoxy ether, bisphenol F diglycidoxy ether, epoxy cresol novolac, bis-(3,4-epoxycyclohexyl)adipate, 3,4-poxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate, or a combination of two or more therof.

11. The antifouling system of claim 8, wherein the epoxy modified adhesion promoter is of the formula: ##STR00009##

12. The antifouling system of claim 1, comprising a second adhesion promoter chosen from gamma-aminpropyltriethoxysilane, N-beta-(aminoethyl)-gamma-aminopropyltrimethoxysilane, gamma-glycidoxypropyltrimethoxysilane, beta-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, and bis-(gamma-trimethoxysilylpropyl)amine.

13. The antifouling system of claim 1, wherein the second adhesion promoter comprises a combination of an aminosilane and an epoxy compound.

14. The antifouling system of claim 1, wherein the antifouling coating composition comprises a filler, a crosslinker, and/or a condensation catalyst.

15. The antifouling system of claim 1, wherein the system is substantially free of a tie coat material.

16. The antifouling system of claim 1, wherein the system comprises a tie coat layer disposed between the base coating and the antifouling coating.

17. An article comprising the coating system of claim 1, the article comprising a base coat layer formed from the base coating composition disposed on a surface of the article, and an antifouling coating layer disposed on the base coat layer.

18. The article of claim 17, wherein the coating system is substantially free of a tie coat layer disposed between the base coat layer and the antifouling coating layer.

19. An antifouling coating system comprising: a base coating composition comprising a base coating material and an epoxy modified adhesion promoter wherein the epoxy modified adhesion promoter comprises at least one molecule having the chemical formula:
(R.sup.1O).sub.a(R.sup.1).sub.3-aSi-M-(Si(R.sup.1).sub.2O).sub.t(Si(R.sup.1)(O.sub.1/2R.sup.1)(O)).sub.t(Si(X)(O.sub.1/2R.sup.1)(O)).sub.vSi(R.sup.1).sub.2-M-Si(OR.sup.1).sub.a(R.sup.1).sub.3-a where R.sup.1 is H or an alkyl radical M is R.sup.2 or oxygen; r is 0-1000; t is 1 to 20; v is 1 to 20; X is R.sub.2(N(R.sup.1).sub.1-b(Y).sub.bR.sub.2).sub.cN(R.sup.1).sub.2-b(Y).sub.b; b is 0-2; c is 0-5; Y is R.sup.1 or an organic radical with an epoxide at one terminal; and R.sup.2 is an alkylene from C.sub.2-C.sub.10, with the proviso that at least one Y is an organic radical with an epoxide at one terminal; and an antifouling coating composition comprising a silicone elastomer and optionally an inorganic filler, optionally a silane cross linker, and optionally a condensation catalyst.

20. The antifouling system of claim 19, wherein Y comprises a radical of partially ring opened bisphenol A diglycidoxy ether, bisphenol F diglycidoxy ether, epoxy cresol novolac, bis-(3,4-epoxycyclohexyl)adipate, 3,4-poxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate, or a combination of two or more thereof.

21. The antifouling system of claim 19, wherein the epoxy modified adhesion promoter having the formula: ##STR00010##

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a photograph showing panels coated with antifouling compositions in accordance with embodiments of the invention compared to a panel coated with a conventional silicone compound after exposure to oceanic conditions.

DETAILED DESCRIPTION

(2) The present invention provides an antifouling coating composition and a coating system comprising such antifouling coating composition. In embodiments, the system is such that a tie-coat layer is not required. In one aspect, the antifouling coating system comprises (a) a base coating composition for coating a target substrate, and (b) an antifouling coating composition. The system is substantially free of a tie-coat layer between the base coating composition (a) and the antifouling coating composition (b). In another aspect, the present invention the antifouling coating composition comprises a single layer coating composition. The present invention also provides a novel compound that can be used as an adhesion promoter and optimally as a material to provide a composition with antifouling characteristics.

(3) The singular forms a, an and the include plural referents unless the context clearly dictates otherwise.

(4) As used herein, the term antifouling coating composition refers to a coating composition that is applicable to a surface and capable of preventing aquatic organisms from depositing (or fouling) and growing on the surface.

(5) Multi-Layer Antifouling Coating System

(6) In one aspect, the present technology provides a multi-layer antifouling coating system comprising (a) a base coating composition for coating a target substrate, and (b) an antifouling coating composition. The system, while comprising multiple layers, is such that it is substantially free of a tie-coat layer between base coating and the antifouling coating.

(7) The antifouling coating comprises (a) a curable polyether-containing silane, and (b) a hydroxyl terminated polymer. In one embodiment, the antifouling coating further comprises (c) an adhesion promoter. The antifouling coating composition can also comprise other optional components including, but not limited to an inorganic filler, a crosslinker, a condensation catalyst, etc., or combinations of two or more thereof.

(8) The curable polyether-containing silane comprises a polymer of the Formula (1):
(R.sup.1O).sub.a(R.sup.1).sub.(3-a)SiR.sup.2(Si(R.sup.1).sub.2O).sub.pSi(R.sup.1).sub.2R.sup.2O(CH.sub.2CHR.sup.1O).sub.qR.sup.1(1)
where a is 1-3; R.sup.1 is H or alkyl radical from C.sub.1-C.sub.10; R.sup.2 is alkylene from C.sub.2-C.sub.10; p is 1-100; q is 1-50, optionally an inorganic filler, optionally a silane cross linker, and optionally a condensation catalyst. In one embodiment, p is from 1-20; from 3-15; even from 5-12. In one embodiment, q is from 1 to 20; 3 to 15; even 5 to 10. In one embodiment, q is 8. Here as elsewhere in the specification and claims, numerical values can be combined to form new and non-disclosed ranges.

(9) Non-limiting examples of suitable polyether-containing silanes are the silanes of Formula (2a) and (2b):

(10) ##STR00003##

(11) The hydroxyl terminated polymer comprises a material capable of reacting with the polyether-containing silane. In one embodiment, the hydroxyl terminated polymer comprises a silanol terminate polymer. An example of a suitable silanol terminated polymer is a hydroxyl terminated polydimethyl siloxane. In one embodiment, the silanol terminated polymer comprises an alpha,omega-bis(SiOH) terminated polymer. In one embodiment, the silanol terminated polymer comprises an alpha,omega-bis(SiOH)polydimethylsiloxane.

(12) In one embodiment, the hydroxyl terminated polymer comprises a polymer of the Formula (3):

(13) ##STR00004##
where R.sup.3 is individually chosen from OH, OR.sup.1, alkyl, and combinations of two or more thereof; R.sup.1 is H or an alkyl radical (e.g., a C.sub.1-C.sub.10 alkyl radical); R.sup.4 is individually chosen from alkyl, fluoro alkyl, alkyl aryl or R.sup.5; R.sup.5 is OH or OR.sup.1; and R.sup.6 is OH or OR.sup.1, where at least one of R.sup.3, R.sup.4, R.sup.5, or R.sup.6 is OH. In one embodiment, R.sup.5 and R.sup.6 are OH.

(14) The curable polyether-containing silane component can be present in the antifouling coating composition based on cured coating in an amount of from about 0.1 weight percent to about 40 weight percent; from about 1 weight percent to about 30 weight percent; even from about 5 weight percent to about 20 weight percent. The hydroxyl terminated polymer can be present in an amount of from about 10 weight percent to about 99 weight percent; from about 20 weight percent to about 80 weight percent; even from about 40 weight percent to about 70 weight percent. Here as elsewhere in the specification and claims, numerical values can be combined to form new and non-disclosed ranges.

(15) The antifouling coating composition can also comprise an adhesion promoter. The adhesion promoter can be chosen from adhesion-promoting silanes including, but not limited to, gamma-glycidoxypropyltrimethoxysilane, gamma-aminopropyltrimethoxysilane, N-beta-(aminoethyl)-gamma-aminopropyltrimethoxysilane, bis-(gamma-trimethoxysilylpropyl)amine, N-beta-(aminoethyl)-gamma-aminopropylmethyldimethoxysilane, tris-(gamma-trimethoxylsilyl)isocyanurate, etc. and combinations of two or more thereof. The adhesion promoter can also be selected from organic epoxy compounds and a combination of an epoxy compound and an adhesion promoting silane. In one embodiments in which the antifouling coating composition comprised an aminosilane and an epoxy compound.

(16) In embodiments in which the antifouling coating composition comprises an adhesion promoter, the adhesion promoter can be present in an amount of from about 0.1 weight percent to about 10 weight percent; from about 1 weight percent to about 7 weight percent; even from about 2 weight percent to about 5 weight percent based on cured coating.

(17) The antifouling coating composition can optionally comprise a filler material. In one embodiment, the filler is an inorganic filler. Fillers can be particulates, fibers, pellets, aggregates, agglomerates and granulates. Examples of suitable fillers include, but are not limited to, clays, alumina-silicates, talc, wollastonite, mica, fumed silica, precipitated silica, calcium carbonates, etc. and combinations of two or more thereof. Treated calcium carbonates are available under several trade names Ultra Pflex, Super Pflex, Hi Pflex from Specialty Minerals; Winnofil SPM, SPT from Solvay; Hubercarb lat, Hubercarb 3Qt and Hubercarb W from Huber; Kotomite from ECC; and Omyacarb FT and BLP-3 from Omya. Particulate materials such as any of the foregoing can be present in the antifouling coating composition comprising in an amount of from 0 to 70, even from 35 to 60, weight parts per 100 weight parts of the total composition based on cured coating.

(18) The antifouling coating composition can optionally comprise a crosslinker. In one embodiment, the crosslinker comprises a silane crosslinker. Examples of suitable crosslinkers include, but are not limited to, an alkoxysilane, an alkoxysiloxane, an oximosilane, an oximosiloxane, an enoxysilane, an enoxysiloxane, an aminosilane, a carboxysilane, a carboxysiloxane, an alkylamidosilane, an alkylamidosiloxane, an arylamidosilane, an arylamidosiloxane, an alkoxyaminosilane, an alkaryaminosiloxane, an alkoxycarbamatosilane, an alkoxycarbamatosiloxane, an imidatosilane, a ureidosilane, an isocyanatosilane, a thioisocyanatosilane, and combinations of two or more thereof. Examples of suitable cross-linkers include, but are not limited to, tetraethylorthosilicate (TEOS); methyltrimethoxysilane (MTMS); methyltriethoxysilane; vinyltrimethoxysilane; vinyltriethoxysilane; methylphenyldimethoxysilane; 3,3,3-trifluoropropyltrimethoxysilane; methyltriacetoxysilane; vinyltriacetoxysilane; ethyltriacetoxysilane; di-butoxydiacetoxysilane; phenyltripropionoxysilane; methyltris(methylethylketoxime)silane; vinyltris(methylethylketoxime)silane; 3,3,3-trifluoropropyltris(methylethylketoxime) silane; methyltris(isopropenoxy)silane; vinyltris(isopropenoxy)silane; ethylpolysilicate; dimethyltetraacetoxydisiloxane; tetra-n-propylorthosilicate; methyldimethoxy(ethylmethylketoximo) silane; methylmethoxybis-(ethylmethylketoximo)silane; methyldimethoxy(acetaldoximo)silane; methyldimethoxy(N-methylcarbamato) silane; ethyldimethoxy(N-methylcarbamato) silane; methyldimethoxyisopropenoxysilane; trimethoxyisopropenoxysilane; methyltri-iso-propenoxysilane; methyldimethoxy(but-2-ene-2-oxy)silane; methyldimethoxy(1-phenylethenoxy)silane; methyldimethoxy-2(1-carboethoxypropenoxy) silane; methylmethoxydi-N-methylaminosilane; vinyldimethoxymethylaminosilane; tetra-N,N-diethylaminosilane; methyldimethoxymethylaminosilane; methyltricyclohexylaminosilane; methyldimethoxyethylaminosilane; dimethyldi-N,N-dimethylaminosilane; methyldimethoxyisopropylaminosilane dimethyldi-N,N-diethylaminosilane. ethyldimethoxy(N-ethylpropionamido) silane; methyldimethoxy(N-methylacetamido)silane; methyltris(N-methylacetamido)silane; ethyldimethoxy(N-methylacetamido)silane; methyltris(N-methylbenzamido)silane; methylmethoxybis(N-methylacetamido)silane; methyldimethoxy(caprolactamo) silane; trimethoxy(N-methylacetamido)silane; methyldimethoxyethylacetimidatosilane; methyldimethoxypropylacetimidatosilane; methyldimethoxy(N,N,N-trimethylureido) silane; methyldimethoxy(N-allyl-N,N-dimethylureido) silane; methyldimethoxy(N-phenyl-N,N-dimethylureido)silane; methyldimethoxyisocyanatosilane; dimethoxydiisocyanatosilane; methyldimethoxythioisocyanatosilane; methylmethoxydithioisocyanatosilane, etc., and combinations of two or more thereof.

(19) The antifouling coating composition can optionally comprise a catalyst. In one embodiment, the crosslinker comprises a catalyst suitable for promoting the curing of siloxanes. Advantageously, condensation catalysts are employed since these will also catalyze the cure (hydrolysis of the alkoxysilyl groups and condensation of the resulting silanols) of the silylated polymer component of the moisture-curable compositions of the invention. Suitable condensation catalysts include, but are not limited to, dialkyltin dicarboxylates such as dibutyltin dilaurate and dioctyltin dilaurate, tertiary amines, the stannous salts of carboxylic acids, such as stannous octoate and stannous acetate, and the like. Other useful catalysts include zirconium-containing, aluminum-containing, and bismuth-containing complexes such as KAT XC6212, K-KAT 5218 and K-KAT 348, supplied by King Industries, Inc., titanium chelates such as the TYZOR. types, available from DuPont company, and the KR types, available from Kenrich Petrochemical, Inc., and other organometallic catalysts, e.g., those containing a metal such as Al, Zn, Co, Ni, Fe, etc.

(20) The base coating is not particularly limited and can be chosen as desired for a particular purpose or intended application. The base coating layer may be any material suitable for forming a coating layer in an antifouling coating. Non-limiting examples include epoxy coatings, room-temperature curable silicone coatings, epoxy-silicone coatings, etc.

(21) In one embodiment, the base coating layer is formed from an epoxy resin composition. The epoxy coating is generally formed by curing an epoxy resin composition that comprises an epoxy resin and an amine-based curing agent for curing the epoxy resin.

(22) The epoxy resin can be chosen from any suitable epoxy resin including, but not limited to, bisphenol epoxy resin, glycidylester epoxy resin, glycidylamine epoxy resin, phenol novolac epoxy resin, cresol epoxy resin, dimer acid modified epoxy resin, aliphatic epoxy resin, alicyclic epoxy resin, epoxidized oil epoxy resin, etc., and combinations of two or more thereof. Non-limiting examples of suitable bisphenol epoxy resins include bisphenol A-type and F-type resins.

(23) In one embodiment, the epoxy resin comprises from about 10 to about 60% by weight of the base coat composition; even from about 20 to about 50% by weight of the base coat composition.

(24) Examples of commercially-available products that can be used as the epoxy resin include, but are not limited to, bisphenol epoxy resins such as Epikote and Epikure resins available from Momentive Specialty Chemicals, including, for example, Epikote 828, Epikote 834, Epikote 1001, Epikote 1004, Epikote 807, Epikote 4004P, Epikote 4007P, etc.

(25) The base coat composition also generally includes an amine-based curing agent for curing the epoxy resin. Examples of suitable amine-based curing agents include, for example, modified Mannich amines formed by Mannich condensation reaction of phenols, formalin, and amine compounds, aliphatic polyamine, etc. In one embodiment, the amine-based curing agent may be present in an amount such that the number of amino groups of the amine-based curing agent is chemically equivalent to the number of epoxy groups of the epoxy resin. In another embodiment, the curing agent can be present in an amount providing an amino group to epoxy group ratio of 0.35:1 to 0.9:1; even 0.4:1 to 0.8:1. In still another embodiment, the amine-based curing agent can be present in an amount of about 10 to about 80 parts by weight with respect to 100 parts by weight of the epoxy resin. Here as elsewhere in the specification and claims, numerical values can be combined to form new and non-disclosed ranges.

(26) Non-limiting examples of commercially-available products that can be used as the amine-based curing agent for the epoxy resin include Epikure 3292-FX60 (Momentive Specialty Chemicals), Raccamide TD966 (Dainippon Ink and Chemicals, Incorporated), Sunmide 307D-60 (Sanwa Chemical Co., Ltd.), etc.

(27) Other suitable base coating materials include, but are not limited to, room-temperature curable silicone coatings, epoxy-silicone coatings, and silicone epoxy hybrid. These materials are not particularly limited and any compositions suitable for use in anti-fouling applications may be used to form the coating. Non-limiting examples of suitable room-temperature curable silicone compositions include those described in U.S. Pat. Nos. 5,449,553; 6,165,620; and 7,666,514. Non-limiting examples of suitable epoxy-siloxane copolymers for the coating include those described in U.S. Pat. No. 6,391,464.

(28) In one embodiment, the base coating comprises an epoxy modified adhesion promoter. In one embodiment, the epoxy modified adhesion promoter comprises a curable amino silicone material and an epoxy compound, where the epoxy modified adhesion promoter is not fully compatible with the base polymer of the base coating. The base coating can comprise the epoxy modified adhesion promoter in an amount of from about 0.1 weight percent to about 20 weight percent; from about 0.3 weight percent to about 5 weight percent; even from about 0.5 weight percent to about 2 weight percent. Here as elsewhere in the specification and claims, numerical values can be combined to form new and non-disclosed ranges.

(29) In one embodiment, the epoxy modified adhesion promoter is of the Formula (4):
(R.sup.1O).sub.a(R.sup.1).sub.3-aSi-M-(Si(R.sup.1).sub.2O).sub.r(Si(R.sup.1)(O.sub.1/2)(O)).sub.t(Si(X)(O.sub.1/2)(O)).sub.vSi(R.sup.1).sub.2-M-Si(OR).sub.a(R.sup.1).sub.3-a(4)
where R.sup.1 is H or an alkyl radical M is R.sup.2 or oxygen; r is 0-1000; t is 1 to 20; v is 0 to 20; X is R.sup.2(N(R.sup.1).sub.1-b(Y).sub.bR.sup.2).sub.cN(R.sup.1).sub.2-b(Y).sub.b; c is 0-5; b is 0-2; Y is R.sup.1 or an organic radical with an epoxide at one terminal; and R.sup.2 is an alkylene from C.sub.2-C.sub.10, with the proviso that at least one Y is an organic radical with an epoxide at one terminal.

(30) In one embodiment, Y comprises a radical of partially ring opened bisphenol A diglycidoxy ether, bisphenol F diglycidoxy ether, epoxy cresol novolac, bis-(3,4-epoxycyclohexyl)adipate (e.g., Cyracure UVR8128), 3,4-poxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate (e.g., Cyracure UVR6110).

(31) In one embodiment, the epoxy modified adhesion promoter is of the Formula (5):

(32) ##STR00005##

(33) The epoxy modified adhesion promoter can be prepared by the partial ring opening of the respective epoxy compound(s) with an aminosilicone. The adhesion promoter can be premade before addition to the base coat formula or it can be made in situ by adding the respective aminosilicone to the epoxy base coat formula directly. In one embodiment, the reactive aminosilicone is formulated with base coat compound prior to coating.

(34) The base coating composition can comprise other additives to the base coating with particular properties or characteristics as desired for a particular purpose or intended use. Suitable additives can include, for example, an antimicrobial agent, a pigment, an anti-sagging agent, etc.

(35) The antimicrobial agent is not particularly limited and can generally be any antimicrobial agent that is compatible with the base coating compositions or the resulting hydrogels. Suitable antimicrobial agents include, but are not limited to, chlorhexidine salts such as chlorhexidine gluconate (CHG), parachlorometaxylenol (PCMX), triclosan, hexachlorophene, fatty acid monoesters and monoethers of glycerin and propylene glycol such as glycerol monolaurate, glycerol monocaprylate, glycerol monocaprate, propylene glycol monolaurate, propylene glycol monocaprylate, propylene glycol moncaprate, phenols, surfactants and polymers that include a (C.sub.12-C.sub.22) hydrophobe and a quaternary ammonium group or a protonated tertiary amino group, quaternary amino-containing compounds such as quaternary silanes and polyquaternary amines such as polyhexamethylene biguanide, silver containing compounds such as silver metal, silver salts such as silver chloride, silver oxide and silver sulfadiazine, methyl parabens, ethyl parabens, propyl parabens, butyl parabens, octenidene, 2-bromo-2-nitropropane-1,3 diol, or mixtures of two or more thereof.

(36) Non-limiting examples of suitable quaternary ammonium compounds and phenolic antimicrobial agents include benzalkonium chlorides and/or substituted benzalkonium chlorides, di(C.sub.6-C.sub.14)alkyl di short chain (C1-4 alkyl and/or hydroxyalkyl) quaternaryammonium salts, N-(3-chloroallyl) hexaminium chlorides, benzethonium chloride, methylbenzethonium chloride, and cetylpyridinium chloride. Other suitable quaternary compounds include alkyl dimethylbenzylammonium chlorides, dialkylmethylbenzylammonium chlorides, and mixtures of two or more thereof. An example of a suitable quaternary amine containing silane is octadecyldimethyl(3-trimethoxysilyl propyl) ammonium chloride from Gelest, Inc.

(37) Examples of suitable pigments include, but are not limited to, talc, silica, mica, clay, calcium carbonate, kaolin, alumina white, white carbon, aluminum hydroxide, magnesium carbonate, barium carbonate, barium sulfate, titanium dioxide, carbon black, etc., and combinations of two or more thereof. In one embodiment, the body pigment may be present in the composition in an amount, for example, of about 5 to about 80% by weight with respect to 100% by weight of the solid content of the base coat composition.

(38) Examples of suitable anti-sagging agents include, but are not limited to, organic clay wax such as amine salt, stearate, lecithinate, alkylsulfonate of Al, Ca and Zn, polyethylene wax, amide wax, hydrogenated castor oil wax, polyamide wax, a mixture of hydrogenated castor oil wax and polyamide wax, synthetic particulate silica, polyethylene oxide wax, etc., and combinations of two or more thereof. The anti-sagging agent may be present in an amount of about 0.1 to about 5% by weight with respect to 100% by weight of the base coat composition.

(39) Each of the above components can be combined with the epoxy resin composition according to any suitable method at the desired ratios during preparation of the composition, by using, for example, commercially-available materials. Further, in addition to the above components, optional components such as a solvent, a liquid hydrocarbon resin, a surfactant, an anticorrosive pigment, and the like, that are used in an epoxy resin anticorrosive coating film may be added in appropriate quantities if necessary. In one embodiment, the epoxy resin base coat composition may be provided as a two-part composition comprising a main agent component containing the epoxy resin and a curing agent component containing the amine-based curing agent.

(40) The antifouling coating composition and the base coating composition provide an antifouling coating system. In accordance with aspects of the invention. The antifouling coating system is substantially free of a tie-coat layer disposed between the base coating and the antifouling coating composition. That is, in aspects of the invention, the antifouling coating composition is disposed immediately adjacent or adhered to the base coating composition. In embodiments, the antifouling coating composition sufficiently adheres to the base coating composition such that an adhesive or binding layer such as a tie-coat layer is not required.

(41) In one embodiment, the antifouling system comprises (a) an antifouling coating composition, and (b) a base coating composition, where the antifouling coating composition comprises a silane of the Formula (1).

(42) In one embodiment, the antifouling system comprises (a) an antifouling coating composition, and (b) a base coating composition, where the antifouling coating composition comprises a silane of the Formula (1) and an adhesion promoter.

(43) In one embodiment, the antifouling system comprises (a) an antifouling coating composition, and (b) a base coating composition, where the antifouling coating composition comprises a silane of the Formula (1), and the base coating composition comprises an epoxy modified adhesion promoter.

(44) In one embodiment, the antifouling system comprises (a) an antifouling coating composition, and (b) a base coating composition, where the antifouling coating composition comprises a silane of the Formula (1) and an adhesion promoter, and the base coating composition comprises an epoxy modified adhesion promoter.

(45) Single Layer Coating System

(46) In another aspect, the present technology provides a single layer coating system. The single layer coating system can comprise any suitable coating or film forming material and a compound of the Formula (4):
(R.sup.1O).sub.a(R.sup.1).sub.3-aSi-M-(Si(R.sup.1).sub.2O).sub.r(Si(R.sup.1)(O.sub.1/2)(O)).sub.qSi(X)(O.sub.1/2)(O)Si(R.sup.1).sub.2-M-Si(OR.sup.1).sub.a(R.sup.1).sub.3-a(4)
where R.sup.1 is H or an alkyl radical M is R.sup.2 or oxygen; r is 0-1000; t is 1 to 20; v is 0 to 20; X is R.sup.2(N(R.sup.1).sub.1-b(Y).sub.bR.sup.2).sub.cN(R.sup.1).sub.2-b(Y).sub.b; c is 0-5; b is 0-2; Y is R.sup.1 or an organic radical with an epoxide at one terminal; and R.sup.2 is an alkylene from C.sub.2-C.sub.10, with the proviso that at least one Y is an organic radical with an epoxide at one terminal. The coating or film forming material can be any material as desired for a particular purpose or intended application. In one embodiment, the coating or film forming material can be any material suitable as a base coating composition described above with respect to the multilayer coating system including, but not limited to, an epoxy, a curable silicone, an epoxy-silicone, etc.

(47) The compound of the formula can provide the film with antifouling properties and can be suitable for use in such applications. In one embodiment, the single layer antifouling coating system comprises a compound of the Formula (4) in an amount of from about 0.1 weight percent to about 20 weight percent; from about 0.25 weight percent to about 15 weight percent; from about 0.3 weight percent to about 10 weight percent; from about 0.5 weight percent to about 5 weight percent; from about 0.75 weight percent to about 2 weight percent. Here as elsewhere in the specification and claims, numerical values can be combined to form new and non-disclosed ranges.

(48) Multi-Layer Antifouling System

(49) In still another aspect, the present technology also provides a multi-layer antifouling system. The multi-layer antifouling system comprises, in one embodiment, three layers: an antifouling top coat, a tie coat, and an anticorrosion base coat. In one embodiment, the antifouling system comprises (a) an antifouling coating composition, (b) a tie coat, and (c) a base coating composition, where the antifouling coating composition comprises a silane of the Formula (1).

(50) In one embodiment, the antifouling system comprises (a) an antifouling coating composition, (b) a tie coat, and (c) a base coating composition, where the antifouling coating composition comprises a silane of the Formula (1) and an adhesion promoter.

(51) In one embodiment, the antifouling system comprises (a) an antifouling coating composition, (b) a tie coat, and (c) a base coating composition, where the antifouling coating composition comprises a silane of the Formula (1), and the base coating composition comprises an epoxy modified adhesion promoter.

(52) In one embodiment, the antifouling system comprises (a) an antifouling coating composition, (b) a tie coat, and (c) a base coating composition, where the antifouling coating composition comprises a silane of the Formula (1) and an adhesion promoter, and the base coating composition comprises an epoxy modified adhesion promoter.

(53) Applications

(54) The antifouling systems (either as a multi-layer or single layer system) can be used in a variety of applications where antifouling and/or antimicrobial properties are desired. The antifouling system comprising a silane of Formula (1) can be used to prevent the adsorption of proteins and cells on a surface.

(55) The base coat can be applied to and adhere to a variety of surfaces including, but not limited to metal (e.g., steel, iron, aluminum, etc.), fiberglass, wood, FRP, concrete etc.

(56) The coating system can be applied to a target substrate by applying the base coating layer to the target substrate, applying the antifouling composition to the base coating layer prior to the base coating being fully cured, and curing the coating compositions. The respective coating compositions can be applied by any suitable methods including, but not limited to, by brush, by roller, by spraying, by dipping, etc. Curing can be accomplished by any suitable curing mechanism including, for example, moisture condensation.

(57) The base coating and the antifouling coating can be applied to provide coating layers of a desired thickness. In one embodiment, for either the multi-layer or single coating layer systems, the base coating has a thickness of from 50 micrometers to about 500 micrometers; from about 100 micrometers to about 300 micrometers; even from about 150 micrometers to about 200 micrometers. In one embodiment, the antifouling coating (for the multi-layer system) can have a thickness of from 50 micrometers to about 400 micrometers; from about 100 micrometers to about 300 micrometers; even from about 150 micrometers to about 250 micrometers.

(58) The coating systems can be employed in a variety of applications including on the surface of vessels (including but not limited to boats, yachts, motorboats, motor launches, ocean liners, tugboats, tankers, container ships and other cargo ships, submarines, and naval vessels of all types), pipes, shore and off-shore machinery, constructions and objects of all types such as piers, pilings, bridge substructures, water-power installations and structures, underwater oil well structures, nets and other aquatic culture installations, and buoys, etc.

EXAMPLES

(59) Coated Sample Preparation

(60) A stainless steel (304-3B) coupon of 0.03716 is thoroughly cleaned by soaking in isopropanol and air drying before coating. An epoxy bottom coating is flow coated on one side of the cleaned stainless steel coupon and allowed to dry and cure at ambient conditions. After the epoxy bottom coat has cured for 24 hours, the silicone top coat is flow coated on top of the epoxy coat. The top coat is allowed to dry and cure at ambient conditions.

(61) Adhesion Test

(62) Adhesion is tested by scraping the coating with a 6 round headed wood tongue depressor. Sufficient force is applied on the tongue depressor to break or peel off the top coat from the epoxy bottom coat. Adhesion failure is assigned when the top coat is cleanly peeled off from the bottom coat. The top coat is considered to pass the adhesion test if there is only cohesion failure at the testing spot. The adhesion is ranked from 0-5 depending upon the level of cohesion failure, with 5 representing 100% cohesion failure occurred and 0 representing no cohesion failure (100% adhesion failure).

(63) Adhesion after Water Soak

(64) To estimate the long term adhesion performance of the coatings, selected coated samples are soaked in a 40 C. water bath for 1 month and adhesion is tested using the same adhesion test protocol described above.

Example 1: Synthesis of SiPEG

(65) 217 g of hydride terminated ,-(SiH)polydimethylsiloxane with a nominal structure of .sup.HMD.sub.10M.sup.H, 36.8 g of vinyltrimethoxysilane, 420 g of toluene, and 0.13 g of chlorotris(triphenylphosphine)rhodium(I) is charged to a 3-neck round bottom flask equipped with N.sub.2 inlet, condenser, and thermometer. The solution is mixed under N.sub.2 blanket for 30 minutes before heating to 80 C. for 12 hours to afford a yellowish solution.

(66) 120 g of the solution is charged to another 3-neck round bottom flask equipped with an N.sub.2 inlet, condenser, and thermometer. The reaction flask is further charged with 20.8 g polyethylene glycol monoallyl ether (eight ethylene oxide groups), 24 g toluene and 0.125 g solution of Karstedt's catalyst in isopropanol (1% Pt). The solution is mixed under N.sub.2 for 30 minutes before being heated to 100 C. for 2 hours. The resulting solution contains 40% SiPEG with a chemical structure as follows:

(67) ##STR00006##

Example 2: Synthesis of Hybrid Adhesion Promoter

(68) 10.14 grams of Epilote 828 (from Momentive Specialty Chemicals), 42 grams of toluene, and 32 grams of SF1706 (curable aminosilicone that is dimethoxysilyl terminated and amine grafted) from Momentive Performance Materials is charged to a beaker and mixed at ambient for 4 hours before use.

Example 3: Preparation of Epoxy Coatings

(69) Epoxdie-containing Epon 828 (from Momentive Specialty Chemicals) is cured with an amine (Epikure 3292-FX-60 from Momentive Specialty Chemicals) and, in some cases, the hybrid adhesion promoter of Example 2 at ambient conditions. The inputs are charged to a plastic container with formulas according to Table 1.

(70) TABLE-US-00001 TABLE 1 Example 3A Example 3B Epikure 3292-FX-60 21 12.6 Epon 828 20 12.11 Hybrid adhesion promoter 0.396 (Example 2) Xylene 4 2.4

(71) The mixing is accomplished using a Speed Mixer DAC150 from FlackTech Inc. Once the coatings are cured, water contact angle increases from 70 of standard epoxy (Example 3A) to 920 when the hybrid adhesion promoter is included in Example 3B, indicating the existing of the silicone moiety on the coating surface.

Example 4: Preparation of Silicone RTV Compound

(72) A silicone compound is mixed by co-extruding 50 parts of silicone polymer (a silanol terminated polydimethylsiloxane with a nominal viscosity of 3000 cps, CRTV 942, from Momentive Performance Materials) and 50 parts of calcium carbonate filler (Albacar 5970) at 80 C. Two RTV base compositions are then made by mixing the silicone compound with other silanol terminated polydimethylsiloxane using a Speed Mixer DAC150 from FlackTech Inc. (Table 2).

(73) TABLE-US-00002 TABLE 2 Example 4A Example 4B Silicone compound 62 62 CRTV942 27 17.35 CRTV941 17.35 88680 7.7 7.7

Example 5: Preparation of Adhesion Promoters

(74) Two adhesion promoters are made by mixing an epoxysilane (Silquest A-187 from Momentive performance Materials) and an aminosilane (Silquest A-1100 or Silquest A-1120 from Momentive Performance Materials) at ambient according to Table 3 for 24 hours before use.

(75) TABLE-US-00003 TABLE 3 Example 5A Example 5B Silquest A-1100 5.8 Silquest A-1120 4 Silquest A-187 12.4 12.4

Example 6: Preparation of Silicone Coatings

(76) Except as otherwise specified, silicone coatings are prepared using two methods. In Method A, a silicone RTV, RTV11 base (uncatalyzed) and SSG4400A from Momentive Performance Materials or the formulated compound of Example 4, is mixed with the SiPEG solution of Example 1, a commercial adhesion promoter silane, e.g., Silquest A-1100, 1200, A-1170, A-186 and A-187 (all from Momentive Performance Materials), an organic solvent, and a dibutyltin dilaurate (DBTDL) condensation catalyst. After each addition, the mixture is thoroughly mixed with a Speed Mixer. In cases when more than one adhesion promoter silane is used, the mixing is applied after each silane is added to prevent immediate reaction between the two silanes (e.g. epoxy silane and aminosilne).

(77) Method B employs a two components approach. In one component (Part A), the silicone RTV is mixed with a crosslinking silane, such as ES-40 (partially condensed tetraethoxysilane) and n-propylsilicate, and in the other component (Part B), the adhesion promoter silane, organic solvent, and DBTDL is combined into a solution.

Example 7

(78) To evaluate the impact of SiPEG to the adhesion of silicone RTV to epoxy coating, the silicone hydrogel coatings containing 0%, 5%, and 10% SiPEG with various adhesion promoter silanes are formulated according to Table 4 using Method A (Example 6). Epoxy of Example 3A is coated and dried for 1 day before the silicone hydrogel formulas are coated and cured at ambient conditions.

(79) TABLE-US-00004 TABLE 4 Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. 7-1 7-2 7-3 7-4 7-5 7-6 7-7 7-8 7-9 7-10 7-11 7-12 SSG4400A 18.0 19 20 18.0 19 20 18.0 19 20 18.0 19 20 Ex. 1 (SiPEG 5.0 2.5 5.0 2.5 5.00 2.5 5.00 2.5 solution) Siliquest A- 0.13 0.13 0.13 1100 Siliquest A- 186 Siliquest A- 0.29 0.29 0.29 0.43 0.43 0.43 187 Example 5a 0.43 0.43 0.43 Example 5b 0.43 0.43 0.43 Xylene 4.2 5.8 5.8 4.2 5.8 5.8 4.2 5.8 5.8 4.2 5.8 5.8 DBTDL 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 Total 27.67 27.77 26.27 27.68 27.78 26.28 27.68 27.78 26.28 27.68 27.28 26.28 % SiPEG in 10 5 0 10 5 0 10 5 0 10 5 0 dry film % silane in 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.1 dry film Days to N* 22 1 N* 6 1 22 1 1 N* N* 1 reach full adhesion

(80) As shown in Table 4, at a fixed amount of adhesion promoter, adhesion is delayed or never occurs in some cases with an increasing amount of SiPEG. Thus, SiPEG appears to have a profound adverse effect on adhesion of silicone RTV to epoxy coating.

Example 8

(81) A number of silanes are incorporated to the SiPEG containing silicone hydrogel coatings and the adhesion after 24 hour curing and then immersed in 40 C. water bath for 30 days. The formulations are prepared according to Tables 5 and 6 using Method A (Example 6).

(82) TABLE-US-00005 TABLE 5 Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. 8-1 8-2 8-3 8-4 8-5 8-6 8-7 8-8 8-9 SSG4400A 18.0 19 19 19 20 18.0 19 20 20 Ex. 1 (SiPEG 5 2.5 2.5 2.5 5 2.5 solution) Siliquest A-1100 0.29 0.29 0.33 0.13 0.13 Siliquest A-186 0.77 0.77 Siliquest A-187 0.73 0.29 0.29 0.43 Example 5a 1.07 Example 5b 1.07 0.43 Xylene 2 4.5 5.9 5.8 5.8 4.4 5.9 5.8 5.8 DBTDL 0.045 0.052 0.05 0.05 0.05 0.05 0.05 0.05 0.05 % SiPEG in 10 5 5 5 0 10 5 0 0 dry film % silane in dry 5.0 5.0 5.0 2.1 2.1 5.1 5.1 2.1 2.1 film Adhesion after 5 5 5 5 5 5 5 5 5 24 hr curing Adhesion after 5 5 5 5 5 5 5 5 5 40 C. water bath

(83) TABLE-US-00006 TABLE 6 Sample Sample Sample Sample Sample Sample Sample Sample Sample Sample 8-10 8-11 8-12 8-13 8-14 8-15 8-16 8-17 8-18 8-19 SSG4400A 18 18 19 19 19 18 19 18 18 19 Ex. 1 5 5 2.5 2.5 2.5 5 2.5 5 5 2.5 (SiPEG solution) Silquest 1 0.4 1 0.4 A-1170 Silquest 0.52 0.52 A-1100 Silquest 0.52 0.52 0.43 0.43 A-1120 Xylene 4 4 4 4 6.5 5 6.5 5 4.2 5.8 DBTDL 0.051 0.044 0.064 0.05 0.02 0.02 % SiPEG in 10 10 5 5 5 10 5 10 10 5 dry film % silane in 5 2 5 2 2.5 2.5 2.5 2.5 2.1 2.1 dry film Adhesion 5 5 5 5 5 5 5 5 5 5 after 24 hr curing Adhesion 5 5 5 5 5 5 5 5 5 5 after 40 C. water bath

(84) Epoxy of Example 3A is coated and dried for 1 day before the silicone hydrogel formulas are coated and cured under ambient conditions. The adhesion is measured after 24 hours curing. The cured samples are then immersed in a 40 C. water bath for 30 days and the adhesion is measured again.

Example 9: Synthesis of SiPEG-Me

(85) 217 g of hydride terminated ,-(SiH)polydimethylsiloxane with a nominal structure of .sup.HMD.sub.10M.sup.H, 36.7 g of vinyltrimethoxysilane, 420.1 g of toluene, and 0.13 g of cholorotris(triphenylphosphine)rhodium(I) is charged to a 3-neck round bottom flask equipped with N.sub.2 inlet, condenser, and thermometer. The solution is mixed under a N.sub.2 blanket for 1 hour before heating to 80 C. for 12 hours to afford a yellowish solution.

(86) 300 g of the solution is charged to another 3-neck round bottom flask equipped with N.sub.2 inlet, condenser, and thermometer. The reaction flask is further charged with 53.2 g allyloxypolyethylene glycol (7.5 EOs) methyl ether, 60 g toluene and 0.205 g solution of Karstedt's catalyst in isopropanol (1% Pt). The solution is mixed under N.sub.2 for 30 minutes before heated to 100 C. for 2 hours. The resulting solution contains 40% SiPEG-Me.

Examples 10-13

(87) In order to evaluate the adhesion improvement imparted by the hybrid adhesion promoter (Example 2), epoxy coating composition containing no hybrid adhesion promoter (Example 3A) and a composition that contains 1% hybrid adhesion promoter (Example 3B) are coated according to the coated sample preparation method. The silicone coating is prepared using Method B (Example 6). Two compositions of Part A are used (Example 4A and Example 4B). Part A is prepared by mixing ES-40 with Examples 4A and 4B, respectively. Part B is made by mixing 11.13 g SiPEG-Me (Example 9), 7.53 g xylene, 1.41 g Silquest A-1100 and 0.19 g dibutyltin dilaurate until homogeneous. The Coating compositions are shown in Table 7.

(88) TABLE-US-00007 TABLE 7 Example 10 Example 11 Example 12 Example 13 Epoxy coat Example 3A Example 3B Example 3A Example 3B Silicone top coat PART A Example 4A 20 20 Example 4B 20 20 ES-40 0.1037 0.1037 0.0798 0.0798 PART B 8.08 8.08 8.08 8.08 24 hr adhesion 0 5 0 5

(89) As shown in Table 7, incorporating 1% of a hybrid adhesion promoter in the epoxy base coat (Example 3B) greatly improved adhesion to the silicone coats.

Example 14

(90) The adhesion improvement of the hybrid adhesion promoter is further investigated by coating silicone compositions containing various adhesion promoters or no adhesion promoter on the hybrid adhesion promoter-containing epoxy (Example 3B). The silicone compositions are prepared according to Table 8 using Method A.

(91) TABLE-US-00008 TABLE 8 Example Example Example Example Example 14-1 14-2 14-3 14-4 14-5 SSG4400A 19 19 18 18 18 Example 1 0 2.5 5 5 5 (SiPEG solution) n-propyl- 0.4 0.4 silicate Silquest 0.13 0.124 A-1100 Silquest 0.105 A-1120 Silquest 0.302 A-186 Silquest 0.29 0.325 A-187 xylene 4.5 4.5 5 5 5 06082 0.1 0.1 0.02 0.02 0.05 (DBTDL) % adhesion 0 0 2.06 2.10 2.09 promoter % SiPEG 0 5 10 10 10 Adhesion 5 5 5 5 5 after 1 week curing Adhesion 5 5 5 5 5 after 40 C. bath

(92) Adhesion is measured after the silicone coatings are allowed to cure for a week and after the cured samples are soaked in a 40 C. water bath for 30 days.

Example 15

(93) The hybrid adhesion promoter does not have to be premade before addition to the epoxy base coat formula. Improvement in adhesion can also be achieved by simply mixing the aminosilicone with epoxy base coat formula before coating. In this example the amine curing agent Epikure 3292-FX-60 is predissolved in xylene and then further mixed with Epon 828, from Momentive Specialty Chemicals, (Epoxy 15-1) and SF1706 (Epoxy 15-2). The formulas are coated on aluminum panels and allowed to cure at ambient temperature (about 25 C.) for 24 hours.

(94) After the epoxy formulas are dried for a day, the top coat formulas are prepared and coated on top of the epoxy base coat. The top coat formulas comprise two components: Component A is made by mixing the silicone base of Example 4A with ES-40; and Component B is made by mixing the SiPEG-Me solution of Example 9, xylene, Silquest A-1100, and a dibutyltindilaurate (DBTDL) catalyst. Component A and Component B are mixed with a Speed Mixer and flow coated onto the epoxy coated panels. Table 9 illustrates the input charges. As illustrated in Table 9, the adhesion of the silicone top coats quickly developed on the epoxy base coat containing SF1706 (Examples 15-3 and 15-4). Examples 15-1 and 15-2, on the other hand, show without SF1706, the top coats do not develop adequate adhesion after 4 days even though these compositions employed a much higher levels of adhesion promoter (Silquest A-1100).

(95) TABLE-US-00009 TABLE 9 Example Example Example Example 15-1 15-2 15-3 15-4 Epoxy base Epoxy 15-1 Epoxy 15-1 Epoxy 15-2 Epoxy 15-2 coat Epikure 3292 12.60 12.60 12.60 12.60 solution xylene 4.20 4.20 4.20 4.20 Epon 828 12 12 12.14 12.14 SF1706 0.152 0.152 Total 28.80 28.80 29.09 29.09 Top coat Topcoat Topcoat Topcoat Topcoat 15-1 15-2 15-3 15-4 Component A Example 4A 20 20 20 20 ES-40 0.1 0.1 0.1 0.1 Component B Example 9 5.598 5.731 5.902 5.970 (SiPEG-Me solution) xylene 3.966 4.058 4.177 4.226 Silquest 0.849 0.626 0.331 0.216 A-1100 DBTDL 0.087 0.085 0.090 0.088 24 hr adhesion 0 0 5 5 4 days 0 0 5 5 adhesion

Example 16

(96) The use of a combination of aminosilane and organic epoxy in silicone top coat is also found to enhance the adhesion of water soaked coatings. In this example, a small amount of Epon 828 is incorporated into a silicone top coat formulation and adhesion is determined after the samples are immersed in a 40 C. water batch for 30 days. The epoxy base coats are prepared by mixing Epikure 3292-FX-60, Epon 828, and, optionally, SF1706 (Example 16-3). The base coat formulations are coated on aluminum panels and allowed to dry for 1 day. Table 9 shows the input charges. The top coats comprise two components: Component A comprises silicone base of Example 4A and optionally Epon 828 (Examples 16-2 and 16-3) dissolved in xylene; Component B comprises the SiPEG-Me solution of Example 9, Silquest A-1100, ES-40 and a dibutyltindilaurate catalyst mixed to homogeneous solution. Components A and B are mixed with a Speed Mixer and then coated onto the epoxy coated aluminum panels. The coatings are allowed to cure at ambient for a day, and the adhesion is tested. The samples are then immersed in a 40 C. water bath for 30 days before another adhesion test is carried out. Table 10 illustrates that the addition of SF1706 improves the initial adhesion of the top coat (Example 16-3). The addition of Epon 828 in the top coats improves the water soak adhesion (Examples 16-2 and 16-3) even if the initial adhesion did not develop in 24 hours (Example 16-2).

(97) TABLE-US-00010 TABLE 10 Example Example Example 16-1 16-2 16-3 Epoxy base coat Epoxy 16-1 Epoxy 16-1 Epoxy 16-2 Epikure 3292 -FX-60 10.5 10.5 12.6 Epon 828 10.05 10.05 12.11 xylene 4 4 4 SF1706 0.2 Top coat Topcoat Topcoat Topcoat 16-1 16-2 16-2 Component A Example 4A 20 19.08 19.08 Epon 828 0.92 0.92 xylene 3.514 4.524 4.524 Component B Example 9 5.794 5.794 5.794 (SiPEG-Me solution) Silquest A-1100 0.605 0.605 0.605 ES-40 0.119 0.119 0.119 DBTDL 0.082 0.082 0.082 24 hr adhesion 0 0 5 adhesion after 30 0 5 5 days in 40 C. water

Example 17: Ocean Test

(98) Antifouling performance testing is carried out by immersing coated samples in Indian Ocean, Tuticorin, India, conducted by Sacred Heart Marine Centre. Table 11 shows the charges for each of the top coat and base coat formulas. At ambient conditions, Epikure 3292-FX-60 is mixed in xylene until dissolved followed by further mixing with Epon 828, and if necessary SF1706 or the hybrid adhesion promoter. Steel panels 3 by 6 are coated with epoxy base coat formulas using a brush and dried at ambient conditions for a day.

(99) Silicone top coats are prepared using two components: Component A comprises (RTV 11 from Momentive Performance Materials, Inc.), or a mixture of silicone base of Example 4A and ES-40, made by mixing the two components with a Speed Mixer. Component B is made by mixing a SiPEG-Me solution of Example 9, xylene, Silquest A-1100, Silquest A-186 (in Examples 17-1 and 17-2), and a dibutyltindilaurate catalyst. After components A and B are mixed with a Speed Mixer, the respective silicone top coat formula is then coated on top of the partially cured epoxy coat according to Table 11. After curing for at least 7 days, the coated panels are immersed in the ocean and static immersion test is conducted for 2 months.

(100) TABLE-US-00011 TABLE 11 Example Example Example Example Example 17-1 17-2 17-3 17-4 17-5 Epoxy base Epoxy Epoxy Epoxy Epoxy Epoxy coat 17-1 17-2 17-3 17-4 17-5 Epikure 25.20 25.20 25.20 15.17 16.80 3292-FX-60 xylene 8.40 8.40 8.40 5.06 5.60 Example 2 0.83 SF1706 0.317 0.317 0.192 Epon 828 24.2 24.28 24.28 14.57 16 Top Coat Component A Example 4A 20 24 24 48 ES-40 0.1 0.12 0.12 0.24 RTV11 Component Topcoat Topcoat Topcoat Topcoat Topcoat B 17-1 17-2 17-3 17-4 17-5 Example 9 5.720 6.992 7.163 6.374 0.000 (SiPEG-Me solution) xylene 4.213 4.929 5.070 12.934 12.203 Silquest 0.138 0.166 0.259 0.485 0.344 A-1100 Silquest 0.340 0.419 A-186 DBTDL 0.090 0.093 0.108 0.208 0.193

(101) FIG. 1 shows pictures of the sample panels after 2 months in Indian Ocean. The panel of Example 17-5 coated with top coat of traditional silicone RTV (RTV11) exhibits fouling in the form of algae and barnacles attachment to the panel. The panels of Examples 17-1 through 17-4 coated with hydrogel top coats in accordance with aspects and embodiments of the present invention, however, remain free of fouling.

Example 18

(102) Silicone hydrogel top coats can also be used in a three-layer coating system, such as: anticorrosion epoxy coat/tie coat/top coat. This example illustrates the usefulness of the disclosed silicone hydrogel top coat in a tie coat-containing antifouling system.

(103) A substrate panel is coated with an anticorrosion epoxy primer InterProtect 2000E (from International Paint) and a then tie coat layer Intersleek731 (from International Paint) according to the manufacturer's recommended procedure of mixing 3 parts of component A and 1 part of component B of InterProtect 2000E mixed and coating with a brush. A one to one ratio of component A and component B of Intersleek731 are mixed and coated, over the anticorrosion coating layer using a brush. Each coating is allowed to dry and cure at ambient conditions for a day before another coating is applied. The silicone hydrogel top coat is applied on top of Intersleek731 and adhesion was test was conducted after the top coat is allowed to cure at ambient conditions for a day.

(104) The top coat formulation is made by preparing components A and B separately. In component A, 0.45 g Epon 828 (from Momentive Specialty Chemicals) is dissolved in 5.2 g of xylene and then mixed with 19.06 g a silicone base compound of Example 4A using a Speed Mixer. In component B, 5.474 g a SiPEG-Me solution of Example 9, 0.164 g Silquest A-1100, 0.15 g ES-40, and 0.097 g dibutyltindilaulate are mixed until homogeneous. Components A and B are mixed with Speed Mixer before applying the composition with a brush onto the partially cured tie coat layer

(105) After allowing for 24 hours curing, the adhesion is tested and found strong bonding between silicone hydrogel top coat and Intersleek 731 tie coat.

(106) While the invention has been described with reference to various exemplary embodiments, it will be appreciated that modifications may occur to those killed in the art, and the present application is intended to cover such modifications and inventions as fall within the spirit of the invention.