Method for Producing a Stainless Steel Sheet with Modified Visual Characteristics

Abstract

The invention relates to a method for producing a patterned stainless steel sheet with modified visual characteristics in the wavelength area of visible light the deformed stainless steel having a thickness of 0.3-3.5 mm. In the method the deformed stainless steel sheet is pretreated by at least one heat treatment step and at least one mechanical treatment step on at least one surface of the heat treated stainless steel sheet. The pretreated stainless steel sheet is further transferred for patterning process, and at least one heat treatment step is carried out for the patterned stainless steel sheet surface.

Claims

1. A method for producing a patterned stainless steel sheet with improved visual characteristics in the wavelength area of visible light from a deformed stainless steel having a thickness of 0.3-3.5 mm, comprising the steps of: preheating the deformed stainless steel sheet by at least one heat treatment step and at least one mechanical treatment step on at least one surface of the heat treated stainless steel sheet, transferring the pretreated stainless steel sheet for patterning process, where the emboss depth is up to 100 micrometre, and at least one heat treatment step is carried out for the patterned stainless steel sheet.

2. The method according to claim 1, wherein the heat treatment for the deformed stainless steel sheet is carried on at the temperature range 900-1200 C., preferably at the temperature range 1150-1200 C.

3. The method according to claim 1, wherein the heat treatment for the deformed stainless steel sheet is carried out as an annealing and pickling process.

4. The method according to claim 1, wherein the heat treatment for the deformed stainless steel sheet is carried out as a bright annealing process.

5. The method according to claim 1, wherein the mechanical treatment step before the patterning process is carried out by skin-pass rolling.

6. The method according to claim 1, wherein the mechanical treatment step before the patterning process is carried out by blasting.

7. The method according to claim 1, wherein the patterning operation is carried out at least on the surface of the stainless steel sheet mechanically treated before patterning.

8. The method according to claim 1, wherein the heat treatment for the patterned stainless steel sheet is carried on at the temperature range 900-1200 C.

9. The method according to claim 8, wherein the heat treatment for the patterned stainless steel sheet is carried out as an annealing and pickling process.

10. The method according to the claim 8, wherein the heat treatment for the patterned stainless steel sheet is carried out as a bright annealing process.

11. The method according to claim 1, wherein the heat treated patterned stainless steel sheet is tension levelled.

12. The method according to claim 1, wherein the stainless steel sheet is made of austenitic stainless steel.

13. The method according to claim 1, wherein the stainless steel sheet is made of ferritic stainless steel.

14. The method according to claim 1, wherein the stainless steel sheet is made of ferritic austenitic stainless steel.

15. The method according to claim 1, wherein the stainless steel sheet is applicable as exterior building material, interior building material, automotive steel plate, commercial kitchen equipment, outer plate for home appliances, outer plate for kitchen equipment and kitchen accessories.

16. The method according to claim 8, wherein the heat treatment for the patterned stainless steel sheet is carried on at the temperature range 1150-1200 C.

Description

[0009] The object of the present invention is to eliminate some drawbacks of the prior art and to establish a method for producing a patterned stainless steel sheet with modified visual characteristics in the wavelength area of visible light, such as low reflectance and low glare but remaining the inherent sparkle of the stainless steel and liveliness. The essential features of the invention are enlisted in the appended claims.

[0010] According to the present invention the material for the method is first cold deformed, such as cold rolled, in order to have a stainless steel sheet having a desired reduction degree and thus a desired thickness range of 0.3-3.5 mm for further process steps. The cold deformed stainless steel sheet is pretreated by at least one heat treatment step and at least one mechanical treatment step, before the stainless steel sheet is transferred into a mill for patterning. After patterning operation further at least one heat treatment step is carried out for the patterned stainless steel sheet before refining the sheet for the final product having the desired surface properties with visual characteristics in the wavelength area (380-800 nanometre) of visible light, such as low reflectance and low glare as well as the inherent sparkle of the stainless steel.

[0011] The deformed stainless steel sheet is heat treated before the patterning treatment at the temperature range of 900-1200 C., preferably at the temperature range of 1050-1200 C. The heat treatment for the deformed stainless steel sheet is carried out as an annealing and pickling step or as a bright annealing step.

[0012] The heat treated stainless steel sheet is further treated mechanically on at least one surface of the heat treated stainless steel sheet before the patterning operation. The mechanical treatment before patterning is advantageously carried out by skin-pass rolling with a dull roll or by blasting process in order to have matt blasted surface.

[0013] During the patterning operation, a pattern device, such as a roll, is advantageously used at least on the surface of the stainless steel sheet mechanically treated in order to carry out the patterning process of a desired design onto the surface of the stainless steel sheet. When the patterning operation is only focussed on one surface of the stainless steel sheet a smooth roll is utilized on the opposite side. The emboss depth on the side of the pattern device, such as a roll, is up to 100 micrometre.

[0014] The patterned stainless steel sheet is further heat treated at the temperature range of 900-1200 C., preferably at the temperature range of 1050-1200 C. by carrying out the heat treatment as an annealing and pickling operation or as a bright annealing operation. After the heat treatment the patterned stainless steel sheet can be used as a final product of the method. It is also possible that the heat treated patterned stainless steel sheet is refined, such as tension levelled, in order to have for instance a desired flatness, before the sheet in accordance with the method of the invention is ready as a final product.

[0015] The stainless steel sheet treated according to the method of the invention shows a superior surface homogeneity and has slightly matt but sparkling on each of nuggets of the surface. The surface shows a lower or equal specular reflectance than the value of less than 25% in the prior art, because due to higher sparkling together with the homogeneity of the surface this characteristic is achieved.

[0016] The stainless steel sheet treated according to the method of the invention further shows a specular reflectance of less than 10% in the visible wavelength range, but still shows a sparkling, lively appearance. These desired properties can be achieved when in connection with the heat treatment for the deformed sheet a mechanical blasting process is carried out in order to have a very matt blasted surface on which patterns are formed during the patterning process step.

[0017] The skin-pass rolling for the deformed and heat treated stainless steel sheet before the patterning operation can advantageously be carried out with a textured roll. The skin-pass rolling achieves a roughness R.sub.a of 0.5-2.5 micrometre for the surface which leads to a lower reflectance of the final product and due to the additional texture on the surface in order to increase sparkling in the final product of the method according to the invention.

[0018] The method for producing a patterned stainless steel sheet according to the invention is advantageously at least at intervals continuous, preferably essentially constantly continuous. Therefore, the deformed stainless steel sheet having the desired thickness can be transferred through all the process steps continuously that means lower manufacturing costs and uniform quality, such as homogeneity of the surface for the final product.

[0019] The stainless steel sheet to be used in the method of the invention can be austenitic stainless steel, ferritic stainless steel or ferritic austenitic stainless steel. The stainless steel sheet treated in accordance with the method of the present invention is applicable as exterior building material, interior building material, automotive steel plate, commercial kitchen equipment, outer plate for home appliances, outer plate for kitchen equipment and kitchen accessories.