Gasket for pre-filled syringe

Abstract

The present invention provides a gasket for prefilled syringes having both airtightness and operability. The present invention relates to a gasket for prefilled syringes, the gasket including a plurality of circular ribs that are to be in sliding contact with the inner wall of a syringe, the gasket being laminated with an inert film, the plurality of circular ribs including a front circular rib having a front corner with a radius of curvature R1 and a rear corner with a radius of curvature R2, a ratio of the radius of curvature R2 to the radius of curvature R1 being more than 1.

Claims

1. A gasket for prefilled syringes, the gasket comprising a plurality of circular ribs that are to be in sliding contact with an inner wall of a syringe, the gasket being laminated with an inert film, the plurality of circular ribs including a front circular rib having a front corner with a radius of curvature R1 and a rear corner with a radius of curvature R2, and a ratio of the radius of curvature R2 to the radius of curvature R1 being more than 1, wherein R2 is 0.5 to 3.5 mm.

2. The gasket for prefilled syringes according to claim 1, wherein the ratio of R2 to R1 is 1.2 to 4.

3. The gasket for prefilled syringes according to claim 2, wherein R1 is 0.3 to 1.0 mm.

4. The gasket for prefilled syringes according to claim 3, wherein, provided that a sliding portion of the gasket, including the corner, has a length H2, and a linear portion of the front circular rib has a length H1, a ratio of the length H2 to the length H1 is 2 to 5.

5. The gasket for prefilled syringes according to claim 4, wherein, provided that a sliding portion of the gasket has a diameter H4, and a barrel of the syringe into which the gasket is to be inserted has an inner diameter H3, a ratio of the diameter H4 to the inner diameter H3 is 1.01 to 1.10.

6. The gasket for prefilled syringes according to claim 5, wherein the inert film is a fluororesin film, a nylon resin film, or an olefinic resin film.

7. The gasket for prefilled syringes according to claim 4, wherein the inert film is a fluororesin film, a nylon resin film, or an olefinic resin film.

8. The gasket for prefilled syringes according to claim 3, wherein, provided that a sliding portion of the gasket has a diameter H4, and a barrel of the syringe into which the gasket is to be inserted has an inner diameter H3, a ratio of the diameter H4 to the inner diameter H3 is 1.01 to 1.10.

9. The gasket for prefilled syringes according to claim 3, wherein the inert film is a fluororesin film, a nylon resin film, or an olefinic resin film.

10. The gasket for prefilled syringes according to claim 2, wherein the inert film is a fluororesin film, a nylon resin film, or an olefinic resin film.

11. The gasket for prefilled syringes according to claim 1, wherein R1 is 0.3 to 1.0 mm.

12. The gasket for prefilled syringes according to claim 1, wherein, provided that a sliding portion of the gasket, including the corner, has a length H2, and a linear portion of the front circular rib has a length H1, a ratio of the length H2 to the length H1 is 2 to 5.

13. The gasket for prefilled syringes according to claim 1, wherein, provided that a sliding portion of the gasket has a diameter H4, and a barrel of the syringe into which the gasket is to be inserted has an inner diameter H3, a ratio of the diameter H4 to the inner diameter H3 is 1.01 to 1.10.

14. The gasket for prefilled syringes according to claim 1, wherein the inert film is a fluororesin film, a nylon resin film, or an olefinic resin film.

Description

BRIEF DESCRIPTION OF DRAWINGS

(1) FIG. 1 shows a cross-sectional view of a gasket for prefilled syringes of the present invention.

(2) FIG. 2 shows a cross-sectional view of a syringe barrel portion of a prefilled syringe.

DESCRIPTION OF EMBODIMENTS

(3) The gasket for prefilled syringes of the present invention has the following features: The gasket includes a plurality of circular ribs that are to be in sliding contact with the inner wall of a syringe, and is laminated with an inert film. The plurality of circular ribs include a front circular rib having a front corner with a radius of curvature R1 and a rear corner with a radius of curvature R2, and the ratio of the radius of curvature R2 to the radius of curvature R1 is more than 1.

(4) The gasket of the present invention includes a plurality of circular ribs that are to be in sliding contact with the inner wall of a syringe (barrel), and the circular ribs form a sliding portion. The term a plurality of refers to any number of two or more. For example, the gasket for prefilled syringes shown in FIG. 1 has two circular ribs including a front circular rib 1 and a rear circular rib 2. The portion designated by 3 is a valley portion which is not to be in sliding contact with the barrel.

(5) Regarding the front circular rib among the circular ribs, the ratio of the radius of curvature R2 of the rear corner to the radius of curvature R1 of the front corner needs to be more than 1, preferably 1.2 to 4, more preferably 1.2 to 3.5. If the ratio is less than 1, sliding resistance increases. The front circular rib herein refers to a circular rib closest to the top surface of the gasket among the circular ribs.

(6) R1 is preferably 0.3 to 1.0 mm, more preferably 0.3 to 0.8 mm. If R1 is less than 0.3 mm, the gasket tends to give an unnecessarily high contact pressure to the barrel, causing an increase in sliding resistance. If R1 is more than 1.0 mm, the sealing properties of the circular rib on the front side tend to decrease, thereby causing liquid leakage. Moreover, R1 depends on the size of syringe. R1 for a 1-mL syringe is preferably 0.3 to 0.5 mm.

(7) R2 is preferably 0.5 to 3.5 mm, more preferably 0.6 to 3.0 mm. If R2 is less than 0.5 mm, the gasket tends to give an unnecessarily high contact pressure to the barrel, causing an increase in sliding resistance. If R2 is more than 3.5 mm while maintaining the contact area between the circular ribs and the barrel, the full length of the gasket tends to increase, thereby causing more molding defects. Moreover, R2 depends on the size of syringe. R2 for a 1-mL syringe is preferably 1.5 to 3.0 mm.

(8) The ratio of the length H2 of the sliding portion of the gasket, including the front corner of the front circular rib to the length H1 of the linear portion of the front circular rib is preferably 2 to 5, more preferably 2 to 4. If the ratio is less than 2, the contact area between the circular ribs and the barrel tends to increase, thereby causing an increase in sliding resistance. If the ratio is more than 5, the contact area between the circular ribs and the barrel tends to decrease, thereby causing an increase in liquid leakage. The front circular rib has a substantially constant outer diameter in the H1 region.

(9) The ratio of the diameter H4 of the sliding portion of the gasket to the inner diameter H3 of the barrel of the syringe into which the gasket is to be inserted is preferably 1.01 to 1.10, more preferably 1.01 to 1.05. If the ratio is less than 1.01, the contact pressure between the circular ribs and the barrel tends to decrease so that liquid leakage can occur easily. If the ratio is more than 1.10, the contact pressure between the circular ribs and the barrel tends to increase, resulting in increased sliding resistance.

(10) The inert film is laminated not only on the liquid-contact portion (top surface) of the gasket but also the sliding portion of the gasket. The sliding portion is preferably laminated to cover at least a rear-side circular rib.

(11) The inert resin film used for molding preferably has a thickness of 25 to 150 m, more preferably 50 to 100 m. A film having a thickness of less than 25 m tends to be frequently torn upon molding, while a film having a thickness of more than 150 m tends to result in economical disadvantages due to the dimension stability of the molded product and increased cost.

(12) The inert film is not particularly limited but is preferably a fluororesin film, a nylon resin film, or an olefinic resin film.

(13) For good chemical resistance, examples of the fluororesin of the fluororesin film include polytetrafluoroethylene (PTFE), tetrafluoroethylene-ethylene copolymer (ETFE), perfluoroalkyl vinyl ether copolymer (PFA), tetrafluoroethylene-hexafluoropropylene copolymer (FEP), polychlorotetrafluoroethylene (PCTFE), polyvinylidene fluoride (PVDF), and polyvinyl fluoride (PVF). Moreover, although containers for medical use are sterilized by steam sterilization, ethylene oxide gas sterilization, or gamma-ray sterilization, PTFE is less resistant to gamma rays. Thus, ETFE, modified ETFE, and PCTFE, which are highly resistant to gamma-ray sterilization, are particularly preferred.

(14) The ETFE refers to a copolymer of ethylene and tetrafluoroethylene at a molar ratio of 30/70 to 70/30, and it can further be copolymerized with other components for the purpose of modification to prepare modified ETFE. Examples of the other components include fluorine-containing olefins and hydrocarbon olefins. Specific examples include -olefins such as propylene and butene; fluorine-containing olefins such as hexafluoropropylene, vinylidene fluoride, perfluorobutyl ethylene, and trifluorochloroethylene; vinyl ethers such as ethylene vinyl ether, perfluoromethyl vinyl ether, and perfluoropropyl vinyl ether; and fluorine-containing acrylates. These components in an amount of about 2 to 10 mol % are copolymerized to modify ETFE.

(15) The modified ETFE may suitably be an ETFE containing an adhesion-imparting functional group. Examples of such a functional group include a carboxyl group, carboxylic anhydride group, epoxy group, hydroxy group, isocyanato group, ester group, amido group, aldehyde group, amino group, cyano group, carbon-carbon double bond, sulfonate group, and ether group. Moreover, examples of commercial products of the modified ETFE include Fluon AH-2000 (Asahi Glass Co., Ltd.).

(16) Non-limiting examples of the nylon resin of the nylon resin film include nylon 6, nylon 11, nylon 12, nylon 66, nylon 610, nylon 6T, nylon 61, nylon 9T, and nylon M5T.

(17) Examples of the olefin resin of the olefinic resin film include polyethylenic resins such as polyethylene, ethylene-propylene copolymer, ethylene-propylene-non-conjugated diene copolymer, ethylene-butene copolymer, ethylene-hexene copolymer, ethylene-octene copolymer, ethylene-vinyl acetate copolymer, ethylene-vinyl alcohol copolymer, ethylene-ethyl acrylate copolymer, and chlorinated polyethylene; polypropylenic resins such as polypropylene, propylene-ethylene random copolymer, propylene-ethylene block copolymer, and chlorinated polypropylene; and polybutene, polyisobutylene, polymethylpentene, and copolymers of cyclic olefins. Polyethylene, and especially ultra-high-molecular-weight polyethylene (UHMWPE), is preferred. These olefin resins may contain fluorine.

(18) The inert film is preferably subjected to a treatment to enhance adhesion to rubber or the like. Examples of such a treatment to enhance adhesion include chemical treatments, treatments for roughing the surface of a film, and combinations thereof. Specific examples include sodium treatment, glow discharge treatment, plasma treatment (discharge treatment) under the atmospheric pressure or in vacuum, excimer laser treatment (discharge treatment), and ion beam treatment.

(19) The base material of the gasket may be any elastic material. Examples include various rubber materials such as natural rubber, butyl rubber, polyisoprene rubber, polybutadiene rubber, styrene-butadiene rubber, silicone rubber, epichlorohydrin rubber, ethylene-propylene rubber, and nitrile rubber; and various thermoplastic elastomers such as polyurethane elastomers, polyester elastomers, polyamide elastomers, olefinic elastomers, and styrenic elastomers. These elastic materials may be used alone or as a blend of a plurality of materials. Among others, preferred are materials that acquire elasticity by vulcanization. In the case of vulcanizable materials, compounding ingredients known in the rubber industry, such as vulcanizing agents e.g. sulfur or vulcanization accelerators may be appropriately added.

(20) The gasket of the present invention can be obtained as follows. The compounding materials are kneaded at a predetermined compounding ratio using an internal mixer, an open roll mill, or the like to prepare a kneaded mixture. This kneaded mixture is formed into an unvulcanized rubber sheet using a calender or sheet forming machine. Next, the unvulcanized rubber sheet with a predetermined weight and size and an inert film are stacked and placed on a mold and then molded using a vacuum press to give a molded laminated gasket sheet.

(21) The molding conditions are not particularly limited and may be set appropriately. The molding temperature preferably ranges from 155 C. to 200 C., more preferably from 165 C. to 180 C. The molding time is preferably 1 to 20 minutes, more preferably 3 to 15 minutes, still more preferably 5 to 10 minutes.

(22) Then, unnecessary portions are cut and removed from the molded gasket, and the resulting gasket is washed, sterilized, dried, and checked for its appearance to prepare a completed gasket. The gasket laminated with the inert film is inserted into a prefilled syringe barrel to prepare a prefilled syringe.

EXAMPLES

(23) The present invention will be described in detail below with reference to, but not limited to, examples.

Examples 1-5 and Comparative Example 1

(24) A PTFE film (trade name New Valflon, Nippon Valqua Industries, Ltd., film thickness: 70 m) was stacked on an unvulcanized rubber sheet formed from a chlorinated butyl rubber (ExxonMobil Chemical), and the stack was placed on a mold and molded at 175 C. for 10 minutes using a vacuum press for vulcanization bonding. The molded sheet was punched and washed to prepare a gasket (for 1-mL COP resin syringes with a barrel inner diameter of 6.3 mm). The sliding resistance and liquid leakage of the thus prepared gaskets were evaluated for n=20 as described below.

(25) (Sliding Resistance)

(26) The gaskets were measured using a desktop autograph available from Shimadzu Corporation with a stroke of 20 mm at a speed of 100 mm/min. As well as determining the sliding resistance, the sliding properties were evaluated based on the following criteria.

(27) Good: The gasket slid without pulsations.

(28) Poor: The gasket slid with pulsations.

(29) (Liquid Leakage)

(30) The experiment was performed in conformity with the Notification Mekkin-zumi chusha-tou kijun (standards for sterile injection syringes) issued on Dec. 11, 1998, Iyakuhatsu No. 1079 by the Director of the Pharmaceutical and Medical Safety Bureau, the Ministry of Health, Labor and Welfare. A gasket sample for 1-mL syringes, a nozzle cap, a 1-mL syringe barrel, and a plunger were prepared. A jig was fit into the screw portion of the gasket. The jig was longer than the corresponding screw. The gasket in this state was placed with the liquid-contact face facing upward. Then, the gasket was inserted straight into the syringe barrel to plug the barrel. Next, water colored by methylene blue was charged into the syringe through the nozzle to a graduation line corresponding to of the nominal capacity. After the nozzle cap and the plunger were attached, the syringe barrel was placed facing down, and a pressure of 392 kPa was applied to the plunger for 10 seconds. The evaluation was performed for n=20. Then, the syringe was observed under a microscope at a magnification of 10 for the presence of leakage into the valley portion (between the front circular rib and the rear circular rib) of the gasket.

(31) Good: No leakage was observed.

(32) Fair: Slight linear leakage was observed.

(33) Poor: Leakage was clearly observed.

(34) TABLE-US-00001 TABLE 1 Example No. Comparative Example 1 Example 1 Example 2 Example 3 Example 4 Example 5 Gasket R1 (mm) 0.5 0.5 1.2 0.5 0.5 0.5 shape R2/R1 0.8 1.2 1.2 2.0 3.5 5.0 H1 (mm) 2.8 2.8 2.8 2.8 2.8 2.8 H2/H1 3.0 3.0 3.0 3.0 3.0 3.0 H3 (mm) 6.3 6.3 6.3 6.3 6.3 6.3 H4/H3 1.05 1.05 1.05 1.05 1.05 1.05 Functional Sliding resistance Poor Good Good Good Good Good test (N) 13 to 18 9 to 11 11 to 14 10 to 12 10 to 13 12 to 15 Liquid Good 20/20 20/20 13/20 20/20 20/20 15/20 leakage Fair 0/20 0/20 5/20 0/20 0/20 5/20 Poor 0/20 0/20 2/20 0/20 0/20 0/20

(35) In the gasket of Comparative Example 1 in which the radius of curvature R1 of the front corner of the front circular rib is larger than the radius of curvature R2 of the rear corner of the front circular rib, the sliding portion of the gasket makes a strong contact with the barrel and thus shows increased sliding resistance. In contrast, in the gasket of the present invention in which the radius of curvature R1 of the front corner of the front circular rib is smaller than the radius of curvature R2 of the rear corner of the front circular rib, an increase in sliding resistance is prevented while maintaining the contact between the gasket sliding portion and the barrel to an extent that prevents liquid leakage.

REFERENCE SIGNS LIST

(36) 1 front circular rib 2 rear circular rib 3 valley portion R1 radius of curvature of front corner of front circular rib R2 radius of curvature of rear corner of front circular rib H1 length of linear portion of front circular rib H2 length of sliding portion including corner H3 inner diameter of syringe barrel H4 diameter of sliding portion of gasket