CARBON FIBERS DERIVED FROM POLY-(CAFFEYL ALCOHOL) (PCFA)

Abstract

Poly-(caffeyl alcohol) (PCFA), also known as C-lignin, is a promising new source of both carbon fibers and pure carbon. PCFA can be used to produce carbon fibers by direct electrospinning, without blending with another polymer to reduce breakage. Analyses have shown that the carbon obtained from PCFA is superior to that obtained from other lignins. The fibers formed from PCFA are smoother, have a narrower diameter distribution, and show very low defects. The PCFA can be obtained by extraction from plant seed coats. Examples of these plants include the vanilla orchid, Vanilla planifolia, and Jatropha curcas. The fibers may be formed through electrospinning, although other methods for forming the fibers, such as extrusion with a carrier polymer, could be used. The fibers may then be carbonized to increase the carbon yield.

Claims

1. Carbon fibers, consisting of: 100 wt. % PCFA, wherein the carbon fibers are produced by extracting poly-(caffeyl alcohol) (PCFA) from a plant to produce extracted PCFA and electrospinning the extracted PCFA to produce the carbon fibers.

2. The carbon fibers of claim 1, wherein the carbon fibers have a narrower size distribution than carbon fibers comprised of 100 wt. % Kraft lignin.

3. The carbon fibers of claim 1, wherein the carbon fibers have diameters of about 10.5 m to about 14 m.

4. The carbon fibers of claim 1, wherein the carbon fibers are further produced by carbonizing to produce carbonized PCFA carbon fibers, and wherein the carbonized PCFA carbon fibers have higher crystallinity than carbonized carbon fibers comprised of 100 wt. % Kraft lignin.

5. The carbon fibers of claim 4, wherein the carbonized PCFA carbon fibers have higher purity than carbonized carbon fibers comprised of polyacrylonitrile (PAN).

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0015] FIG. 1 shows ESEM images of electrospun PCFA fibers (A,B) and Kraft fibers (C,D);

[0016] FIG. 2 shows histograms of the diameters of electrospun PCFA fibers (A), and Kraft lignin fibers (B);

[0017] FIG. 3 shows (A) ESEM image of electrospun PCFA fibers and (B, C and, D) surface variation analysis for the areas marked with open yellow rectangle in (A);

[0018] FIG. 4 shows (A) ESEM image of electrospun Kraft lignin fibers and (B, C and, D) surface variation analysis for the areas marked with open yellow rectangle in (A);

[0019] FIG. 5 shows Zeta potentials for carbon from (A) PCFA powder and (B) Kraft lignin; and

[0020] FIG. 6 shows Raman spectroscopy of (A) PCFA powder and derived carbon, and (B) Kraft lignin powder and derived carbon.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

[0021] Generally, the present disclosure relates to carbon fibers derived from poly-(caffeyl alcohol) or PCFA and the methods for preparing these fibers.

[0022] In preferred embodiments, the carbon fibers are made up of 100% PCFA with no carrier polymer. Alternatively, the carbon fibers may be made up of about 10% to about 90% PCFA in combination with a polymer carrier PAN, polyesters, polyolefins, polyamides and other thermoplastic and thermoset polymers can be used.

[0023] The PCFA is preferably obtained by plant extraction from any plant that has PCFA in its seed coats. Examples of these plants include the vanilla orchid, Vanilla planifolia, and Jatropha curcas. Any suitable method for extraction can be used. The fibers may be formed through electrospinning, although other methods for forming the fibers, such as extrusion with a carrier polymer, could be used. The fibers may then be carbonized to increase the carbon yield.

[0024] In the present disclosure, PCFA was extracted from the ground seed coats of Vanilla planifolia using an alkaline solvent and the lignin was precipitated from solution. In parallel, Kraft lignin was precipitated from the black liquor obtained from the paper and pulping industry. 50% solutions of each sample in dioxane were prepared and electrospun through a syringe needle to which a voltage has been applied. Neither lignin sample was blended with other polymers to facilitate electrospinning. The spun fibers were then carbonized. This process resulted in similar carbon yields for PCFA and Kraft lignin. However, the electrospinning process produced more continuous fiber with a narrower size distribution in the case of PCFA compared with Kraft lignin. Both lignins produced fibers of higher percentage crystallinity (by Raman spectroscopy) than PAN-based carbon fibers, with PCFA fiber showing the highest crystallinity, consistent with its more linear molecule. The higher purity of PCFA and Kraft fibers over PAN-based fibers is expected to translate into higher mechanical stiffness, thermal and electrical conductivity.

[0025] Generally, PCFA offers a linear molecular architecture that helps enable the formation of fibers. The fiber formed from Kraft lignin has high surface roughness compared to the smooth PCFA carbon fibers. PCFA based carbon fiber also shows very low defects compared to Kraft lignin. Carbon defects are associated with inferior mechanical and thermal properties. Finally, higher ionic conductivity of Kraft lignin points to remnant impurities and complex sources of the originating liquid compared to that of PCFA.

[0026] This disclosure pertains to the fabrication of PCFA-based carbon fiber. As shown more fully in the examples below, Kraft lignin has been used as a comparative basis for examining the carbon fiber obtained from PCFA. Notable is that the PCFA fibers were successfully electrospun directly from solutions without any chemical treatment or addition of polymers to provide fiber extensional flow strength to produce uniform fibers. As reported previously, Kraft lignin in the unmodified state produced fibers that were of high diameter (50 M) and exhibited surface roughness. In contrast, the PCFA-sourced carbon fibers were of low diameter (10 m) and smooth. Manufacture of Kraft lignin based carbon has utilized co-axial electrospinning to enable melt strength for long fiber spools to be formed, and the porosity has been used for activated carbon. However, smooth PCFA-based carbon fibers can be obtained by direct electrospinning with no fiber breakage.

[0027] Carbonization at 900 C. imparted more graphitic properties to the PCFA carbon than to the Kraft lignin, as seen in the Raman spectroscopy analysis described below, with G/D ratios of 1.92 vs 1.15 respectively. In this respect, the PCFA-derived carbon compares very well to commercial carbon from PAN and approaches that based on pitch. The carbon yield is around 86% for both sources of carbon. Zeta potential shows good dispersion stability in DI water for carbon from both fibers. On the basis of the results of the analyses described below, PCFA appears to be a promising new source of both carbon fibers and pure carbon.

Example 1. Extraction of PCFA

[0028] PCFA (C-lignin) was obtained from seed coats of Vanilla planifolia. Vanilla seeds were ground to a powder using a Freezer/Mill 6870 (SPEX Sample Prep, Metuchen, N.J.), then extracted with chlorofom and methanol three times consecutively. To isolate PCFA, the extracted seeds were mixed with 1% NaOH in a liquid to solid ratio of 10. The mixture was then heated to 120 C., and the temperature maintained at 120 C. for one hour in an autoclave. After cooling, the black liquid was separated from the residue by filtration, and PCFA was precipited from the liquid phase by adjusting the pH to 3.0 with concentrated HCl. The precipited PCFA was separated by centrifugation, washed with water and freeze dried.

Example 2. Extraction of Kraft Lignin

[0029] The kraft lignin extraction process was as follows. Black liquor with pH 11.0 and total solids 88.9%, Klasson lignin 25.1%, and ash 63.8% was received from Zellstoff Pols AG, Austria. The black liquor was produced as by-product during sulphate pulping of 70% spruce, 25% pine and 5% larch. Kraft lignin (KL) was isolated from black liquor by acid precipitation with 37% hydrochloric acid. After lowering the pH to 2, the precipitated sample was filtered on a Buchner funnel and washed with distilled water twice, to remove unreacted compounds. The filtered sample was dialyzed against fresh distilled water for 7 days, and subsequently was freeze dried.

Example 3. Comparative Chemical Analyses of Lignin Samples

[0030] The purity of Kraft lignin samples was determined from the analyses for Klason lignin, acid-soluble lignin and ash according to Tappi Standard procedures (T 13 m-54, T 222 om-02, and T15 os-58). The composition of lignin samples was determined by elemental analysis for C, H, N and S contents by a Universal-Elemental analyser Vario El III (Elementar, Germany). The results of elemental analysis and ash were used to calculate lignin C.sub.9 formulae. Average molecular weights (M.sub.n and M.sub.w), and polydispersity PDI (M.sub.w/M.sub.n) were determined by gel permeation chromatography (GPC) instrument equipped with L6000A Merck-Hitachi pump, PPS sizing column (5 m, 850 mm), three linear PPS gel columns (5 m, 8300 mm) connected in series, and a Viscotek differential refractometer/viscometer (Malvern, UK). The columns were calibrated using a series of 12 narrow molecular weight polystyrene standards with molar mass ranging from 680 to 1 600 000 g/mol (Polymer Standard Service). The samples were dissolved in tetrahydrofurane at concentration 4 mg/ml and were analysed at room temperature. THF was used as eluent at flow rate of 1.0 ml/min and the injection volume was 100 l. The results are shown below in Table 1.

TABLE-US-00001 TABLE 1 Kraft Lignin Sample Klason lignin (wt %).sup.a 89.6 Total lignin content (wt %).sup.b 92.5 Ash (wt %) 0.2 Carbon (wt %) 64.1 Hydrogen (wt %) 5.6 Nitrogen (wt %) 0.1 Sulphur (wt %) 2.4 Molecular weight 1749 Polydispersity 2.38 .sup.aEstimated by difference .sup.bKlason lignin with acid soluble lignin part

Example 4. Electrospinning and Carbonization

[0031] A 50% solution of PCFA was prepared in 1,4 dioxane (boiling point of 101 C.). The powder was mixed at 50 C. for 4 h, and then transferred to the syringe for electrospinning. The same process was repeated for Kraft lignin. A 5 ml syringe (National Scientific, Rockwood, Tenn., Model #57510-5) with an 18 gauge (1.27 mm) 1 long stainless steel blunt needle with a Luer polypropylene hub was used. The syringe with needle was placed on a Razel syringe pump (Model #R99-FM, Razel Scientific Instruments, St. Albans, Vt.). The rate of syringe pump was 0.763 with a flow rate of 2.65 ml/h, the distance between the needle and the plate was 20 cm and the voltage was 20 kV. The solution was pumped from the syringe. The needle was then charged to the prescribed voltage using a high voltage power supply (Model #ES30P-5W/DAM, Gamma High Voltage Research Inc., Ormond Beach, Fla.). The collector plate was set at the prescribed distance from the needle, covered with non-stick aluminium foil, and grounded. As the syringe pump and the high voltage power supply were switched on, the lignin solution came out of the needle forming a Taylor cone that was attracted by the electrostatic force towards the grounded collector plate.

[0032] The electrospun fibers from PCFA and Kraft lignin were subjected to carbonization in a horizontal tube furnace. The heating and cooling ramp rate was set at 5 C./min. Fibers were held at 900 C. for 45 min under a flow of nitrogen of 0.5 standard cubic feet per hour (SCFH). The carbon obtained was analyzed for carbon yield.

Example 5. Comparative Analyses

[0033] Environmental Scanning Electron Microscopy (ESEM):

[0034] A FEI Quanta Environmental Scanning Electron Microscope (ESEM; FEI Company, Oregon, USA) was used to image the cross section of the burnt PCFA and Kraft lignin fibers at an accelerating voltage of 12.5 kV at 10 mm working distance. The samples were sputter coated with gold-palladium to make them conductive and make imaging possible.

[0035] Raman Spectroscopy:

[0036] A 532 nm intensity laser was used at 25% power with aperture of 10 m slit and objective lens with 10 zoom to give a spot size of 2.1 m. The scan was done from 750 to 2000 l/cm. The exposure time was 15 sec. Background and sample exposure was performed five times. Background was collected before every sample. This background was subtracted from the Raman spectroscopy results and a baseline correction was performed.

[0037] Zeta Potential:

[0038] A Delta NanoC particle analyzer from Beckman Coulter (Pasadena, Calif.) was used to determine Zeta potential. The dispersions of the PCFA powder and Kraft lignin were made in deionized water at room temperature and dispersed using sonication for 1 h.

[0039] Results:

[0040] Solutions of both PCFA and Kraft lignin are electrospinnable. Continuous electrospun fibers were obtained under conditions of 20 kV and 2.65 cc/h solution flow rate with a distance of 20 cm to the stationary collector plate. The ESEM images of PCFA (FIG. 1A, 1B) and Kraft lignin (FIG. 1C, 1D) suggest that the fibers obtained are highly uniform with no beads. Obtaining bead-free fibers depends on the conductivity of the solution which elongates the Taylor cone formed at the tip of the needle to give electrospun fibers. During electrospinning of both PCFA and Kraft lignin a minimum voltage of 20 kV was essential to overcome the surface tension of the Taylor cone. A 50% solution in 1,4 dioxane at 50 C. gives enough entanglement of PCFA to spin it into fibers.

[0041] The ESEM images were analyzed using ImageJ software (NIH). The images were corrected for the scale from pixels of the original tiff image to the known distance on the image to calibrate for scale. A total of 58 measurements of diameters were made and the histogram was plotted for the most frequent occurrence of the diameter range, as shown in FIG. 2. PCFA produced fine uniform fibers and processed unceasingly compared to Kraft lignin which could only electrospin for a short period of time. The diameters of the electrospun fibers from PCFA and Kraft lignin were in the range of 10.5 to 14 m and 30 to 40 m, respectively.

[0042] ESEM images of PCFA and Kraft lignin were also analyzed for surface variation. As shown in FIGS. 3 and 4, the surface is significantly smoother in the PCFA lignin compared to the Kraft lignin sourced carbon fibers.

[0043] As shown in FIG. 5, the Zeta potentials for PCFA and Kraft lignin carbon powders in deionized water are similar, around 43.350.48 mV and 42.052.37 mV respectively. This suggests that the stability of the carbon particles obtained from PCFA is good enough to keep them in suspension for long durations. The Zeta value indicates repulsion between the particles, thus stopping them from attracting each other and flocculating. The low mobility and conductivity values indicate that the ionic double layer is thick due to low ionic strength. The mobility of the particles in the suspension, 3.40e-00400 cm.sup.2/Vs, indicates that the attraction of particles to the electrodes is very low. Table 2 below shows the suspension properties of carbon from PCFA and Kraft lignin.

TABLE-US-00002 TABLE 2 Zeta potential Mobility Ionic conductivity Sample (mV) (cm.sup.2/Vs) (mS/cm) PCFA powder 43.35 0.48 3.40e004 00 0.028 0.00042 Kraft lignin 42.05 2.37 3.1e04 2.0E06 0.6457 0.00051

[0044] Raman spectroscopy was performed to compare the purity of carbon obtained from PCFA and Kraft lignin powder samples (FIG. 6). The D and G bands give the defect-derived structures and graphite derived structure of the carbon, respectively. The D band is due to the breathing modes of sp.sup.2 atoms in the aromatic ring while the G band results from sp.sup.2 site stretching of CC bonds. A high G/D ratio is symptomatic of higher crystalline structure. Carbon from PAN has G/D ratios ranging from 0.57-0.67, while pitch-based carbon shows higher crystal perfection with G/D ratios ranging from 2.27 to 7.6. The G/D ratios of PCFA powder and PCFA carbon are 2.68 and 1.92, respectively (see Table 3 below). It is important to note that carbonization at 900 C. has increased the graphitic structure as seen by the intensity of the G-band (FIG. 6A). There is a 133% increase in highly ordered G-band. The G-band intensity can also be used to check the purity of the samples. This is because, unlike with the D band, there is no effect of chirality on the G-band. Thus the Raman spectra show that high purity carbon is obtained from PCFA, comparable to PAN. The highly ordered graphitic structure in PCFA-derived carbon is correlated to higher mechanical stiffness, thermal and electrical conductivity. Also, the unburnt Kraft lignin shows no presence of G and D bands, whereas the carbonized material shows a distinct presence of both bands (FIG. 6B). The G/D ratio is 1.15, indicating the presence of ordered graphitic structure. However, PCFA shows a higher carbon purity when produced with the carbonization method described in Example 4 above.

[0045] Table 3 below shows a comparison of the Raman spectral parameters of PCFA and Kraft lignin, before and after carbonization.

TABLE-US-00003 TABLE 3 PCFA PCFA Kraft Kraft lignin powder carbon lignin carbon G/D 2.68 1.92 1.15 D/G 1.96 0.92 1.84 G 2 0.57 M 7 0.3 Full Width Half Maximum (FWHM) of the related peaks G 59 122 85 D 116 112 156 G 58 30 M 31 40 FWHM(D) x 227 103 287 (D/G)