Selective Aerobic Oxidation of Methane

Abstract

A continuous process for aerobic oxidation of methane. The process includes a reactor (10) comprising a bed of a metal-based catalyst (16), a methane feed stream (30) into the reactor (10), an oxygen feed stream (30) into the reactor (10), and a water feed stream (12) into the reactor (10). The methane is oxidised in a single step in the reactor (10) over the metal-based catalyst (16) in the presence of liquid water to produce a reaction product including compounds selected from formaldehyde, oligomers of formaldehyde, methanediol, and products of addition reactions between methanol and formaldehyde, and mixtures thereof.

Claims

1. A continuous process for aerobic oxidation of methane, the process including: a) providing a reactor comprising a bed of a metal-based catalyst; b) providing a methane feed stream into the reactor; c) providing an oxygen feed stream into the reactor; and d) providing a water feed stream into the reactor; wherein the methane is oxidised in a single step in the reactor over the metal-based catalyst in the presence of liquid water to produce a reaction product including compounds selected from formaldehyde, oligomers of formaldehyde, methanediol, and products of addition reactions between methanol and formaldehyde, and mixtures thereof.

2. The process according to claim 1, wherein the metal of the metal-based catalyst is selected from the group consisting of Pt, Pd, Ni, Ag and Au, and alloys thereof, wherein the alloyed metal is selected from the group consisting of Pt, Pd, Ni, Cu, Ag and Au.

3. The process according to claim 1, wherein the metal of the metal-based catalyst is selected from the group consisting of Pt and Ag, and alloys thereof, wherein the alloyed metal is selected from the group consisting of Pt, Pd, Ni, Cu, Ag and Au.

4. The process according to claim 1, wherein the metal-based catalyst is a platinum-based or platinum-alloy-based catalyst.

5. The process according to claim 1, wherein the metal-based catalyst includes a support which is selected from the group consisting of titania, alumina, silica and other refractory oxides, and carbon.

6. The process according to claim 1, wherein the catalyst is selected from the group consisting of Pt/TiO.sub.2(P25), Pt/TiO.sub.2(rutile), Pt(Mo)/TiO.sub.2(rutile), Pt/Al.sub.2O.sub.3 and Pt/C.

7. The process according to claim 1, wherein the catalyst is selected from the group consisting of Pt/Au, Pt/Ag and Pt/Cu alloys, supported on alumina or titania.

8. The process according to claim 7, wherein the support is titania.

9. The process according to claim 1, wherein the reactor is a trickle-bed reactor.

10. The process according to claim 1, wherein the reactor operating temperature is between about 150 C. and about 250 C., and the reactor total operating pressure is between about 20 bar and about 100 bar.

11. The process according to claim 1, wherein heat is recovered from the reactor.

12. A continuous process for aerobic oxidation of methane, the process including: a) providing a reactor comprising a bed of a metal-based catalyst; b) providing a methane feed stream into the reactor; c) providing an oxygen feed stream into the reactor; and d) providing a water feed stream into the reactor; wherein the methane is oxidised in a single step in the reactor over the metal-based catalyst in the presence of liquid water to produce a reaction product including compounds selected from formaldehyde, oligomers of formaldehyde, methanediol, and products of addition reactions between methanol and formaldehyde, and mixtures thereof, with a selectivity of the compounds or mixtures thereof of over 70%.

Description

BRIEF DESCRIPTION OF THE FIGURES

[0037] Non-limiting embodiments of the invention will now be described by way of example only and with reference to the following figures:

[0038] FIG. 1: TEM images of platinum-based catalysts for methane oxidation comprising: [0039] Left: Incipient wetness impregnated 10 wt.-% Pt/TiO.sub.2(P25) reduced at 400 C., [0040] Middle: Incipient wetness impregnated 10 wt.-% Pt/TiO.sub.2(rutile) reduced at 400 C., and [0041] Right: Colloid impregnated 10 wt.-% Pt(Mo)/TiO.sub.2(rutile);

[0042] FIG. 2: Platinum-based nanoparticles (NPs) used as precursors for metal-based catalysts for methane oxidation;

[0043] FIG. 3: A schematic drawing of a trickle-bed reactor for methane oxidation in accordance with this invention;

[0044] FIG. 4: Methane oxidation as a function of temperature over Pt/TiO.sub.2-WI-R (inlet partial pressuressee Table 2): [0045] Top: Methane conversion as a function of temperature, [0046] Middle: Selectivity for selective oxidation products (non-CO and non-CO.sub.2), and [0047] Bottom: 1,3,5-Trioxane content in the fraction of selective oxidation;

[0048] FIG. 5: Methane oxidation as a function of temperature over Pt/TiO.sub.2-NP (inlet partial pressures CH.sub.4: 1.2-1.6 bar; O.sub.2: 1.3-1.8 bar; m.sub.catalyst=0.15 g): [0049] Top: Methane conversion as a function of temperature, and [0050] Bottom: Selectivity for selective oxidation products (non-CO and non-CO.sub.2);

[0051] FIG. 6: Methane oxidation as a function of temperature over Pt/TiO.sub.2-NP (inlet partial pressuressee Table 3; m.sub.catalyst=0.5 g): [0052] Top: Methane conversion as a function of temperature, and [0053] Bottom: Selectivity for selective oxidation products (non-CO and non-CO.sub.2);

[0054] FIG. 7: Methane oxidation as a function of temperature over Ag/TiO.sub.2-NP (inlet partial pressuressee Table 4; m.sub.catalyst=0.39 g, Ag loading=9.4 wt. %): [0055] Top: Methane conversion as a function of temperature, and [0056] Bottom: Selectivity for selective oxidation products (non-CO and non-CO.sub.2);

[0057] FIG. 8: Methane oxidation as a function of temperature over Pt.sub.3Ag/TiO.sub.2-NP (inlet partial pressuressee Table 5; m.sub.catalyst=0.152 g, 10 wt % metal loading);

[0058] FIG. 9: Methane conversion over colloid impregnated 10 wt.-% Pt_NPs/TiO.sub.2 in a gas-phase methane oxidation reactor (W/F.sub.CH4,0=4.1 g.sub.cat.Math.min/mmol);

[0059] FIG. 10: Methane conversion and product selectivity over 10 wt. % (a) Pt/rutile and (b) Pt/P-25 catalysts in presence of liquid water at 220 C. and 30 bar (PCH.sub.4=0.5 bar, PO.sub.2=1.5 bar, Psat,H.sub.2O=23.1 bar);

[0060] FIG. 11: Catalyst activity of various impregnated platinum catalysts on different supports in the selective oxidation of methane;

[0061] FIG. 12: Selectivity for the formation of formaldehyde (or methanol in the case of Pt/TiO.sub.2 (P25)) over various impregnated platinum catalysts on different supports in the selective oxidation of methane

[0062] FIG. 13: Performance of Pt.sub.3Ni/TiO.sub.2 (rutile) in a trickle bed reactor.

DETAILED DESCRIPTION OF THE INVENTION

[0063] The present invention will now be described more fully hereinafter with reference to the accompanying figures, in which some, but not all embodiments of the invention are shown.

[0064] Before any embodiments of the invention are explained in detail, it is to be understood that the invention is not limited in its application to the details of construction and the arrangement of components set forth in the following description or illustrated in the following drawings. The invention is capable of other embodiments and of being practiced or of being carried out in various ways. Also, it is to be understood that the phraseology and terminology used herein is for the purpose of description and should not be regarded as limiting. The use of including, comprising, or having and variations thereof herein is meant to encompass the items listed thereafter and equivalents thereof as well as additional items. The terminology includes the words specifically mentioned above, derivatives thereof, and words of similar import. It is noted that, as used in this specification and the appended claims, the singular forms a, an, and the, and any singular use of any word, include plural referents unless expressly and unequivocally limited to one referent. As used herein, the term include and its grammatical variants are intended to be non-limiting, such that recitation of items in a list is not to the exclusion of other like items that can be substituted or added to the listed items.

[0065] As used herein, the term selective oxidation products means products obtained from oxidation of methane, different from CO or CO.sub.2, and the term oxygenates has the same meaning.

[0066] The following examples are offered by way of illustration and not by way of limitation.

Catalyst Synthesis

[0067] The metal-based catalysts illustrated herein may be synthesised either by incipient wetness or by colloidal impregnation of Pt-nanoparticles on a titania support (either rutile or P25). It will be appreciated that Pd, Ni, Cu, Ag and Au, or alloys thereof, may similarly be used, as alternatives for Pt, and that Pt or platinum alloys are illustrated here as non-limiting examples of a metal base for the catalyst. The person of ordinary skill in the art would have a reasonable expectation that the invention could be carried out using other metals or alloys thereof, such that, but not limited to, catalytically active materials will remain in the metallic (zero-valent) state during the reaction, or that metals may be selected from group 9 to 11 metals, or alloys thereof. Without thereby wishing to be bound by any particular theory, it is believed that the catalytic activity can be tuned by manipulating the d-band centre of the surface metal atoms by an appropriate selection of alloying elements. It will also be appreciated that carbon or other refractory oxides may be used as suitable alternatives for titania, including, but not limited to, alumina and silica, and that titania is illustrated here as one non-limiting example of a support for the catalyst. Without thereby wishing to be bound by any particular theory, a refractory oxide may be selected on the basis of the surface acidity or basicity of the support, and it is believed that less basic and acidic sites will lead to improved catalytic performance.

Example 1

[0068] Incipient wetness impregnation involved contacting a support of TiO.sub.2 (either rutile or P25) with a solution of platinic acid (H.sub.2PtCl.sub.6) to obtain 10 wt.-% platinum on the support. The solid was dried, calcined at 400 C. (air flow rate: 48 ml.sub.n/min/g) and subsequently reduced at either 400 C. (H.sub.2 flow rate: 48 ml.sub.n/min/g) for 5 hrs or 600 C. in flowing hydrogen. Platinum is then in the metallic state as confirmed using XRD. The resulting average particle size for Pt/TiO.sub.2(P25) was 4.5 nm contacted and ca. 9 nm for Pt/TiO.sub.2(rutile). The active metal dispersion was measured using static H.sub.2-chemisorption performed at 80 C. in the pressure range 0.1-600 mm Hg and determined to be 8.9% for Pt/TiO.sub.2(P25) and 9.1% for Pt/TiO.sub.2(rutile).

Example 2

[0069] Monometallic platinum nanoparticles (NPs) were synthesized in a one-neck round-bottom flask: platinum acetylacetonate (0.12 g, 0.31 mmol) was dissolved via vigorous stirring at 150 C. in a ternary mixture of surfactants oleylamine (20 ml), trioctylamine (20 ml) and hexadecylamine (5 g), in the presence of high boiling point solvent benzyl ether (25 ml). The resultant pale-yellow homogeneous solution was heated up to 200 C. with a heating rate of 10 C./min. The solution rapidly turned dark brown and was maintained at this temperature for 5 min, removed from the heat source and cooled down to room temperature. The black product was finally re-dispersed in chloroform, yielding a dark brown colloidal suspension. The separation-purification-resuspension processes of the as-prepared colloidal solution were repeated several times to remove all the unwanted solvents and surface-unbound surfactants. TEM images (shown in FIG. 2) show monodisperse nanoparticles with a narrow particle size distribution and mean particle diameter of less than 5 nm. The Pt nanoparticles display a near-spherical shape.

Example 3

[0070] A second batch of monometallic platinum nanoparticles was synthesised using Mo(CO).sub.6 as the reduction agent. The precursor salt Pt(acac).sub.2 (0.16 g, 0.41 mmol) was dissolved in oleyl amine (20 ml), oleic acid (20 ml) and benzyl ether (25 ml). The resulting metal salt-surfactant-solvent reaction mixture was heated at 150 C. for 5 to 10 minutes under vigorous magnetic stirring in a round bottom flask. Upon addition of Mo(CO).sub.6 (0.1 g, 0.38 mmol), the resultant pale-yellow homogeneous solution turned dark purple with evolving cloudy smoke. The bulk organic synthesis mixture then turned dark brown during the heat-up process to 200 C., with a heating rate of 10 C./min. The resultant colloidal mixture was held at this temperature for 10 to 15 min. Thereafter, the colloidal medium was removed from the heat source and quenched using cold water to ensure no structural transformations during the cooling process. Subsequently, the as-synthesized nanoparticles were extracted from the synthesis media through flocculation by adding excess absolute ethanol. After settling (typically 1 to 2 days), the excess organic solvents were decanted and the particles were further cleaned by re-suspending in absolute ethanol. This colloidal refining process was performed 3 times. The black product was finally re-suspended in chloroform, yielding a dark brown colloidal suspension for Pt NPs. TEM images show monodisperse nanoparticles with a narrow particle size distribution and mean particle diameter of less than 5 nm. The Pt nanoparticles display a near-spherical shape. Elemental analysis showed no molybdenum in the catalyst.

Example 4

[0071] A binary platinum-silver nano-alloy with a nominal composition of Pt.sub.3Ag was synthesized by dissolving Pt(acac).sub.2 (0.16 g, 0.41 mmol) and AgNO.sub.3 (0.023 g, 0.14 mmol) in a mixture of oleyl amine (20 ml), oleic acid (20 ml) and benzyl ether (25 ml). The resulting metal salt-surfactant-solvent reaction mixture was heated at 150 C. for 5 to 10 minutes under vigorous magnetic stirring in a round bottom flask. Upon addition of Mo(CO).sub.6 (0.1 g, 0.38 mmol), the resultant pale-yellow homogeneous solution turned dark purple with evolving cloudy smoke. The bulk organic synthesis mixture then turned dark brown during the heat-up process to 200 C., with a heating rate of 10 C./min. The resultant colloidal mixture was held at this temperature for 10 to 15 min. Thereafter, the colloidal medium was removed from the heat source and quenched using cold water to ensure no structural transformations during the cooling process. Subsequently, the as-synthesized NPs were extracted from the synthesis media through flocculation by adding excess absolute ethanol. After settling (typically 1 to 2 days), the excess organic solvents were decanted and the particles were further cleaned by re-suspending in absolute ethanol. This colloidal refining process was performed 3 times. The resulting nano-alloy has a worm-like structure (see FIG. 2). The XRD-pattern of the PtAg alloy is dominated by the (111) reflection of the FCC-structure showing facile growth along the dense (111) plane. The composition according to Vegard's law is Pt:Ag=0.95:0.05. The nanoparticles were supported on TiO.sub.2(rutile) by colloidal impregnation.

Example 5

[0072] For comparison, silver nanoparticles were synthesized by dissolving AgNO.sub.3 (0.13 g, 0.77 mmol) in oleyl amine (20 ml), oleic acids (20 ml) and benzyl ether (25 ml). The resulting metal salt-surfactant-solvent reaction mixture was heated at 150 C. for 5 to 10 minutes under vigorous magnetic stirring in a round bottom flask. Upon addition of Mo(CO).sub.6 (0.1 g, 0.38 mmol), the resultant pale-yellow homogeneous solution turned dark purple with evolving cloudy smoke. The bulk organic synthesis mixture then turned dark brown during the heat-up process to 200 C., with a heating rate of 10 C./min. The resultant colloidal mixture was held at this temperature for 10 to 15 min. Thereafter, the colloidal medium was removed from the heat source and quenched using cold water to ensure no structural transformations during the cooling process. Subsequently, the as-synthesized NPs were extracted from the synthesis media through flocculation by adding excess absolute ethanol. After settling (typically 1 to 2 days), the excess organic solvents were decanted and the particles were further cleaned by re-suspending in absolute ethanol. This colloidal refining process was performed 3 times. The black product was finally re-suspended in chloroform, yielding a dark reddish colloidal suspension for Ag NPs.

[0073] Herein, catalysts are referred to according to the active metal, support, and method of synthesis or morphology. For instance, a platinum catalyst synthesised via the solution-phase synthetic approach is referred to as Pt/TiO.sub.2-NP (NPnanoparticles), Pt/TiO.sub.2-NW (NWnanowires) and Pt/TiO.sub.2-WI-R (WIwet impregnation, Rrutile). As used herein, the term Pt(Mo) means a platinum-based catalyst synthesised using Mo(CO).sub.6 as a reductant.

Reactor Setup and Analysis

[0074] The reactor (10) may be a fixed-bed reactor, more particularly a trickle-bed reactor, comprising a bed of metal-based catalysts (16) as described hereinbefore. Feed streams may be provided continuously into the reactor, comprising a methane feed stream, an oxygen feed stream and a water feed stream. The reactor may comprise further feed streams including Helium and Argon. Importantly, the oxidation of methane over the metal-based catalyst (16) may take place continuously in the presence of water in the liquid phase. The operation of the reactor (10) may be described by way of the following example.

[0075] By way of a non-limiting example, trickle-bed conditions in which the invention may be carried out, at 250 C., include water partial pressure of ca. 40 bar, CH.sub.4 partial pressure of ca. 30 bar, and a stoichiometric amount of O.sub.2 at a partial pressure of 15 bar, totalling a minimum of 85 bar.

Example 6

[0076] The trickle-bed reactor (10) consisted of a quartz tube (14) 38 cm long and 12 mm in inside diameter packed with ca. 1.5 g of pelletized and sieved (to 150-250 m particles) Pt/TiO.sub.2 catalyst (16) in its centre. The void space on top of the catalyst bed (16) was packed with silicon carbide particles (18) (diameter 300 m). The catalyst (16) and the silicon carbide (18) were held in place with 2 small glass (quartz) wool plugs (20) on either end. A quartz sheathed (22) thermocouple (24) was placed at the centre of the catalyst bed (16) for temperature measurement. The reactor body (11) is enclosed in an aluminium heating furnace controlled with multiple heating zones controlled by thermocouples on the outside of the reactor (10). The isothermal zone in the reactor (10) was ca. 10 cm. The quartz tube (14) was placed inside a 19.05 mm outside diameter stainless steel tube. An O-ring (26) (made from fluorocarbon for example) may be placed between the stainless-steel tube and quartz tube (14), located between an inert gas (Argon for example) inlet port (28) and a feed gas inlet port (30) comprising methane, oxygen and helium.

[0077] Liquid water was fed into the trickle bed reactor (10) via a liquid water inlet port (12) and mixed with oxygen, helium and methane at the top of the reactor (taking care to avoid the formation of water droplets at the entrance point of the water). The flow rates of methane, oxygen helium and liquid water were precisely controlled.

[0078] Argon flowed, pressure-controlled, through the annular space between the two tubes at the same pressure as inside the quartz tubing (14). The bottom of the reactor (10) rested on a bed of silicon carbide (18) (diameter 300 m; bed length 15.5 cm) to ensure evaporation of the liquid water dripping out of the catalyst bed (16) (the argon flow rate was typically set at ca. 2-3 times the total flow rate through the catalyst bed (16)). The temperature of the bottom zone was adjusted depending on the water flow rate to achieve smooth operation. The final mixture was expanded to 1 bar over a needle valve. The argon was allowed to mix with the reaction product exiting the quartz tubing (14) at the end of the reactor (10), via a reactor outlet port (32), to dilute it prior to its expansion to 1 bar. This, and due to the small size of the reactor, was done to minimize risks associated with the flammability of methane and oxygen mixtures as well as allowing the reactor (10) to be operated at elevated pressures (<100 bar).

[0079] Reaction products were measured and analysed online using a GC-Methanizer-FID system. Methane is the only carbon containing compound fed into the reactor. The conversion, yield and selectivity can be estimated directly from the GC-trace and assuming a quantitative conversion in the methanizer and that there is no loss in carbon:

[00001]$Y_i\left(c-\%\right)=\frac{\mathrm{Peak}\mathrm{area}\mathrm{of}i}{\mathrm{Total}\mathrm{peak}\mathrm{area}}100\left(C-\%\right)$

[0080] The methane conversion was calculated as the sum of the yields:

[00002]$X_{{\mathrm{CH}}_4}=.Math.Y_i\left(C-\%\right)=\left(1-\frac{\mathrm{Peak}\mathrm{area}\mathrm{of}{\mathrm{CH}}_4}{\mathrm{Total}\mathrm{peak}\mathrm{area}}\right)100\left(C-\%\right)$

[0081] The selectivity for the formation of compound i was calculated from the yield of compound i and the methane conversion:

[00003]$S_i\left(c-\%\right)=\frac{Y_i}{X_{{\mathrm{CH}}_4}}100\left(C-\%\right)$

[0082] Table 1 shows the products from the selective oxidation of methane as identified via GC-FID and their corresponding retention times.

TABLE-US-00001 TABLE 1 Retention times corresponding to the product obtained during the selective oxidation of methane. Retention time (min) Component Chemical Formula 1.6 Carbon monoxide CO 1.7 Methane CH.sub.4 2.1 Carbon dioxide CO.sub.2 3.2 Ethane C.sub.2H.sub.6 5.5 Formaldehyde CH.sub.2O 6.2 Methanediol 6.9 Methanol CH.sub.3OH 7.8 Methyl formate C.sub.2H.sub.4O.sub.2 9.2 Dimethylether C.sub.2H.sub.6O 9.5 Methoxymethanol CH.sub.3OCH.sub.2OH 10.05 Dimethoxymethane CH.sub.3OCH.sub.2OCH.sub.3 10.9 Formic acid CH.sub.2O.sub.2 11.4 Dimethylcarbonate CH.sub.3OCOCH.sub.3 13.36 Methylhydroperoxide CH.sub.3OOH 14.1 Trioxane CH.sub.2OCH.sub.2OCH.sub.2O 14.98 Paraformaldehyde HO(CH.sub.2O).sub.nH* *n = 8-100

[0083] A gas-phase reactor was set up for comparative purposes, and had a similar setup and design philosophy as the above trickle bed reactor, with the differences described as follows. Helium was fed into the reactor through an evaporator, acting as an inert diluent and carrier of water, which was continuously pumped into the evaporator at a constant flow rate using an HPLC-pump. The temperature in the evaporator was regulated to be below the boiling point of water at the pressure of the reactor at the top of the evaporator and ca. 20 C. above the boiling point of water at this pressure at the end of the evaporator to ensure smooth evaporation. Quantities of helium, methane and oxygen were mass flow-controlled. The water-helium mixture was mixed with the oxygen-methane mixture at the top of the reactor. The reactor consisted of a quartz tube 25 cm long and 2.4 mm in inside diameter packed with ca. 400 mg of the pelletized and sieved Pt/TiO.sub.2 catalyst in its centre. The void space on top of the catalyst was packed with silicon carbide particles (diameter 300 m). The catalyst and the silicon carbide were held in place with 2 small glass (quartz) wool plugs on either end. A quartz sheathed thermocouple was placed at the bottom of the catalyst bed for temperature control. The quartz tube was placed inside a 6.35 mm outside diameter stainless steel tube.

Continuous Selective Aerobic Oxidation of Methane

[0084] The continuous, selective, aerobic oxidation of methane as described herein may be exercised over a number of process parameters, using the aforementioned metal-based catalysts, as illustrated by the examples that follow.

Example 7

[0085] The invention may be exercised using platinum impregnated on the rutile form of titania (m.sub.catalyst=0.36 g; 9.2 wt.-% Pt) as catalyst over the process parameters shown in Table 2.

TABLE-US-00002 TABLE 2 Feed gas flow rates and partial pressures employed during the oxidation of methane to oxygenates over platinum impregnated on the rutile form of titania (m.sub.catalyst = 0.36 g; 9.2 wt.-% Pt) Feed Flowrate Partial component (ml(NTP) .Math. min.sup.1) Pressure.sup.a (Bar) He 77.0 9.8 O.sub.2 16.0 1.8 CH.sub.4 2.5 0.3 H.sub.2O 0.05 (fed as a liquid) 8.1 .sup.aPartial pressure at the inlet of the reaction zone (saturation pressure of water at lowest reaction temperature, 176 C., 9.15 bar)

[0086] FIG. 4 shows the performance of methane oxidation of the impregnated platinum on the rutile form of titania at a relatively low partial pressure of methane and oxygen upon co-feeding water. The initially obtained conversion at a low temperature is high but drops rapidly upon increasing the reaction temperature. This anomalous behaviour is related to the change in the composition of the coverage of the catalyst surface and a consequence of the start-up procedure. Low conversion of ca. 0.01% was obtained at a reaction temperature of 200 C., which was obtained after the methane oxidation at 250 C. (the original conversion at 200 C. was 0.57%).

[0087] The obtained conversion of ca. 0.5% corresponds to platinum-time-yield of 0.2 hr.sup.1 (mol CH.sub.4 converted per hr per mole of Pt), which would correspond to a turnover frequency of 0.8 hr.sup.1 if the catalyst has a dispersion of 25%.

[0088] The catalyst is selective for the formation of selective oxidation products, with a selectivity of more than 70 C-% at temperatures below 220 C. even when the catalyst had deactivated. The major selective oxidation product obtained with this catalyst was trioxane, although with increasing reaction temperature the fraction of the product identified as trioxane decreases (and a product appearing in the GC trace at a retention time of 9.2 minwhich has been identified as dimethyletherwas observed). Trioxane is an important chemical, serving as an intermediate in the production of acetal resins (polyoxymethylenes), which find application in the production of plastics.

Example 8

[0089] On-purpose synthesized platinum nanoparticles supported on the rutile form of titania with a defined particle size of platinum of ca. 4 nm were utilised for the methane oxidation. A partial pressure of methane of ca. 1.2-1.6 bar and a partial pressure of O.sub.2 between 1.3 and 1.8 bar was utilised at a reaction temperature between 20 and 300 C. At these conditions, the reaction was performed in the gas phase, instead of at trickle bed conditions, for comparative purposes. From FIG. 5, although still effective, the catalyst activity is somewhat lower than the activity obtained over platinum impregnated on the rutile form of titania. The selectivity towards selective oxidation products is reduced (with both trioxane and the dimethylether being formed; the selectivity towards trioxane is less than the one obtained over platinum impregnated on the rutile form of titania). This shows the importance of liquid water at trickle bed reaction conditions, in other words flooding at the catalyst.

Example 9

[0090] The invention was carried out over platinum nanoparticles supported on the rutile form of titania at low reaction temperatures, as shown in Table 3.

TABLE-US-00003 TABLE 3 Feed gas flow rates and partial pressures at the various reaction temperatures employed during the oxidation of methane to oxygenates over platinum nanoparticles supported on the rutile form of titania at low reaction temperatures. Partial Pressure (Bar) Feed Flowrate 100 125 150 175 200 components (ml .Math. min.sup.1) C. C. C. C. C. He 34 14.9 13.8 11.9 9.9 9.9 O.sub.2 5 2.2 2.0 1.7 1.5 1.5 CH.sub.4 4.5 2.0 1.8 1.6 1.3 1.3 H.sub.2O 0.02 (as a liquid) 1.0* 2.3* 4.8* 7.3 7.3 *liquid water in the reactor as well (flooding)

[0091] As can be seen from FIG. 6, although still effective, the conversion of methane is not very high. The selectivity for selective oxidation products (in this case mainly dimethylether), increases with decreasing reaction temperature, plateaus at ca. 60 C-% under conditions where flooding takes place.

Example 10

[0092] Silver nanoparticles supported on the rutile form of titania (Ag/TiO.sub.2-NP-R) were utilised in the oxidation of methane over a wide range of temperatures at the conditions given in Table 4.

TABLE-US-00004 TABLE 4 Feed gas flow rates and partial pressures employed during the oxidation of methane to oxygenates over Ag/TiO.sub.2-NP-R. Flowrate Partial Feed gas (ml(NTP) .Math. min.sup.1) pressure (bar) He 149.6 8.3 O.sub.2 16.8 0.9 CH.sub.4 2.0 0.1 H.sub.2O 0.01 (fed as liquid) 0.7

[0093] As can be seen from FIG. 7, the conversion increases with increasing temperature. The conversion-temperature behaviour shows two distinctly different regions in an Arrhenius diagram, viz. a low temperature region with an activation energy of ca. 19 kJ/mol and a high temperature region (T>240 C.) with an activation energy of ca. 46 kJ/mol. The selectivity for selective oxidation products (mainly dimethylether) decreases with increasing temperature (and increasing methane conversion), indicating that reaction temperatures should not be excessively high such that complete oxidation is dominant.

Example 11

[0094] The invention was carried out with platinum-silver alloy nanoparticles supported on the rutile form of titania (Pt.sub.3Ag/TiO.sub.2-NP-R) as catalyst for the oxidation of methane at 225 C. at the conditions given in Table 5.

TABLE-US-00005 TABLE 5 Feed gas flow rates and partial pressures employed during the oxidation of methane to oxygenates over platinum-silver alloy nanoparticles supported on the rutile form of titania (Pt.sub.3Ag /TiO.sub.2-NP-R) Flowrate Partial Feed gas (ml .Math. min.sup.1) Pressure (Bar) He 32 3.2 O.sub.2 12 1.2 CH.sub.4 2.5 0.3 H.sub.2O 0.12 15.4

[0095] As can be seen from FIG. 8, the conversion varied between 0.2 and 2.6%. Alloying platinum with silver resulted in an improvement in the selectivity towards formaldehyde, which was the only selective oxidation product obtained.

Example 12

[0096] Platinum nanoparticles supported on the rutile form of titania (Pt(Mo)/TiO.sub.2) were utilised in the oxidation of methane at the conditions indicated in Table 6, which also indicates the conversion and selectivity results.

TABLE-US-00006 TABLE 6 Effect of trickle bed conditions in the gas-phase methane oxidation reactor on the selective methane oxidation over 10%-Pt(Mo)/TiO.sub.2 (reaction performed at 20 bar with a constant flow rate of CH.sub.4 at 4.5 ml.sub.n/min, O.sub.2 at 5.0 ml.sub.n/min, He at 34.0 ml.sub.n/min, H.sub.2O(I) at 0.02 ml/min) Reaction temperature, C. 100 125 150 175* p.sub.CH4, inlet, bar 2.0 1.8 1.6 1.3 p.sub.O2, inlet, bar 2.2 2.0 1.7 1.5 p.sub.He, inlet, bar 14.9 13.8 11.9 9.9 p.sub.H2O,sat, bar 1.0 2.3 4.8 7.3 X.sub.CH4, % 0.13 0.02 0.15 0.01 0.17 0.04 0.10 0.01 -r.sub.CH4, mol/g/hr 143 22 166 11 188 44 110 11 S.sub.CO2, C-% 40.1 1.9 38.9 4.3 34.9 5.5 53.3 1.6 S.sub.dimethylether, C-% 56.5 3.9 61.1 4.3 51.0 18.7 46.7 1.6 S.sub.trioxane, C-% 3.3 5.8 14.0 24.2 *Under these conditions a single fluid phase is expected.

Example 13

[0097] The rate of reaction and conversion level of methane is independent of the O.sub.2 and CH.sub.4 partial pressure or feed rate, as can be seen from FIG. 9 in which the invention was carried out over 10 wt.-% Pt/TiO.sub.2(rutile)-NP at the reaction parameters indicated in the figure, in a gas-phase reactor. Upon flooding the reactor, at reaction temperatures below the saturation point of water, the valuable products of formaldehyde, oligomers of formaldehyde (1,3,5 trioxane for example), methanediol, methanol, and the add-products between methanol and formaldehyde were obtained.

Example 14

[0098] CH.sub.4 conversion and product selectivity over 10 wt. % (a) Pt/rutile and (b) Pt/P-25 catalysts in the presence of liquid water at 220 C. and 30 bar (PCH.sub.4=0.5 bar, PO.sub.2=1.5 bar, Psat,H.sub.2O=23.1 bar) can be seen in FIG. 10.

[0099] For the Pt/rutile catalyst, CH.sub.4 conversion decreases drastically from 3.9% without water to 0.04% at a water flowrate of 0.02 ml/min, which is attributed to the metal surface being covered by hydroxyl species impeding CH.sub.4 activation. For both catalysts, the initial increase in the water partial pressure steadily improves CH.sub.4 conversion, while strongly favouring the formation of oxygenates and thus suppressing CO/CO.sub.2 selectivity. Compared to Pt/P-25, Pt/rutile showed better catalytic activity and highest oxygenate selectivity with 90% of formaldehyde. In the flooding regime (feed water flowrate >0.08 ml/min) as shown in FIG. 10(a), the presence of liquid water does not have considerable effect on the formaldehyde selectivity as increases slowly until it reaches a plateau.

[0100] Importantly, in examples 7 to 14, the presence of liquid water at the catalytically active site (i.e. flooding) favours activity as well as selectivity towards selective oxidation products. See for example FIG. 10(a), and the conversion, reaction rate and selectivity changes in Table 6 between trickle bed conditions at 150 C. and the single, vapour phase conditions at 175 C.

[0101] Operating the reactor at higher temperatures, for example between 150 C. and 250 C., allows for the recovery of heat from the reactor. This aids in making the process more economically viable.

Example 15

[0102] The invention was carried out with platinum impregnated on TiO.sub.2 (rutile), TiO.sub.2 (P25), Al.sub.2O.sub.3 and C. The catalysts were prepared by incipient wetness impregnation of platinic acid in deionized water on titanium dioxide (Rutile: S.sub.BET=44.5 m.sup.2/g; P25: S.sub.BET=46.4 m.sup.2/g), alumina (-Al.sub.2O.sub.3; S.sub.BET=73.9 m.sup.2/g) or carbon (S.sub.BET=232 m.sup.2/g) as a support. The support was contacted with an aqueous solution of platinic acid (H.sub.2PtCl.sub.6) to obtain 10 wt.-% platinum on the support. The solid was dried, calcined at 400 C. (air flow rate: 48 ml.sub.n/min/g) and subsequently reduced for 5 hrs at 400 C. in flowing hydrogen (48 ml.sub.n/min/g). The activity over the various impregnated platinum catalysts on different supports in the selective oxidation of methane can be seen in FIG. 11, at reaction conditions of F.sub.CH4,0/W 3.2 mmol/min/hr; p.sub.CH4, inlet=0.5 bar; p.sub.O2, inlet=1.5 bar; p.sub.total=30 bar. The activity achieved with Pt/C is notably high, also achieving a conversion of ca. 4% at the high water to methane ratio.

[0103] FIG. 12 shows the selectivity for the formation of formaldehyde as a function of the inlet ratio of water to methane, in a trickle bed reactor at reaction conditions of F.sub.CH4,0/W3.2 mmol/min/hr; p.sub.CH4, inlet=0.5 bar; p.sub.O2, inlet=1.5 bar; p.sub.total=30 bar; T=220 C. High selectivity for the formation of formaldehyde (90-98%) can be obtained using supports such as TiO.sub.2 in its rutile form, or carbon. The reaction over Pt/TiO.sub.2(P25) yielded some methanol, and no formaldehyde.

Example 16

[0104] The invention was carried out using Pt.sub.3Ni on a TiO.sub.2 (rutile) support in a trickle bed reactor at reaction conditions of F.sub.CH4,0/W4.9 mmol/min/hr; p.sub.CH4, inlet=0.5 bar; p.sub.O2, inlet=1.5 bar; p.sub.total=30 bar; T=220 C. The results can be seen in FIG. 13, indicating good activity of 163 mol/g/hr and a conversion of 3.3% at the highest water feed rate. The selectivity had a maximum of ca. 73%.

[0105] It will be appreciated that the above examples are only some embodiments of the invention and that there may be many variations without departing from the spirit and/or the scope of the invention. It is easily understood from the present application that the particular features of the present invention, as generally described and illustrated in the figures, can be arranged and designed according to a wide variety of different configurations. In this way, the description of the present invention and the related figures are not provided to limit the scope of the invention but simply represent selected embodiments.

[0106] The skilled person will understand that the technical characteristics of a given embodiment can in fact be combined with characteristics of another embodiment, unless otherwise expressed or it is evident that these characteristics are incompatible. Also, the technical characteristics described in a given embodiment can be isolated from the other characteristics of this embodiment unless otherwise expressed.