HIGH-ENERGY-DENSITY SLURRY FUEL, PREPARATION METHOD, AND APPLICATION

Abstract

The present invention provides a high-energy-density slurry fuel, a preparation method, and an application. The high-energy-density slurry fuel comprises the following components in percentage by mass: 3%-40% of aluminum-based-metal hydride composite fuel; 53.6%-96% of high-density liquid hydrocarbon fuel; 0.2%-2% of anti-settling agent; and 0.2%-5% of other performance regulators, wherein an aluminum-based-metal hydride is a composite material that disperses and distributes a metal hydride inside aluminum powder particles. The high-energy-density slurry fuel may be used as a fuel for an engine such as a ramjet engine or a rocket engine. Compared with the existing liquid fuel, the present high-energy-density slurry fuel has the characteristics of high density (.sub.20 C.>0.9 g/cm3), high heat value (greater than 38 MJ/kg), rapid ignition, and efficient combustion; and compared with the existing slurry fuel, the present high-energy-density slurry fuel has the advantages of rapid ignition, efficient combustion, and no residue or less residue in combustion products.

Claims

1. A high-energy-density slurry fuel, comprising the following components in mass percentage: aluminum-based metal hydride composite fuel: 3%-40%; liquid hydrocarbon fuel: 53.6%-96%; anti-settling agent: 0.2%-2%; other performance modifiers: 0.2%-5%; wherein the aluminum-based metal hydride is a composite material in which a metal hydride is dispersedly distributed inside aluminum powder particles.

2. The high-energy-density slurry fuel according to claim 1, wherein the aluminum-based metal hydride composite fuel is an AlLiH composite fuel.

3. The high-energy-density slurry fuel according to claim 2, wherein a mass percentage of Al and LiH in the AlLiH composite fuel is: LiH: 2%-30%; and Al: balance.

4. The high-energy-density slurry fuel according to claim 2, wherein a median particle size D.sub.50 of the AlLiH composite fuel is in a range of 5-30 m.

5. The high-energy-density slurry fuel according to claim 2, wherein the AlLiH composite fuel is prepared by a method comprising: weighing aluminum powder and lithium hydride, mixing them uniformly and then putting them into a ball mill tank, sealing the ball mill tank and ball milling them in a ball mill to obtain the AlLiH composite fuel.

6. The high-energy-density slurry fuel according to claim 1, wherein the liquid hydrocarbon fuel is a petroleum distillation product or/and a synthetic hydrocarbon, with a calorific value of 40 MJ.Math.kg.sup.1 and a density of 0.78 g.Math.cm.sup.3.

7. The high-energy-density slurry fuel according to claim 6, wherein the petroleum distillation product is selected from one or more of No. 1 jet fuel RP-1, No. 2 jet fuel RP-2, No. 3 jet fuel RP-3, No. 4 jet fuel RP-4 or No. 5 jet fuel RP-5.

8. The high-energy-density slurry fuel according to claim 6, wherein the synthetic hydrocarbon is selected from one or both of tetrahydrodicyclopentadiene or quadricyclane.

9. The high-energy-density slurry fuel according to claim 1, wherein the anti-settling agent is white carbon black.

10. The high-energy-density slurry fuel according to claim 1, wherein the other performance modifier is one or more selected from iron oxide, octylferrocene, catocene, 3-amino-1,2,4-triazole copper perchlorate, copper chromite, ammonium oxalate, sodium oxalate, diethyl oxalate, nitromethane, isopropanol, octyl nitrate or isooctyl nitrate.

11. A method for preparing a high-energy-density slurry fuel, comprising the following steps: adding liquid hydrocarbon fuel, aluminum-based metal hydride composite fuel, anti-settling agent and other performance modifiers in a mixer according to a ratio of each component, and mixing them at room temperature to a uniform slurry to obtain the high-energy-density slurry fuel.

12. A method for preparing a fuel for an engine, comprising using the high-energy-density slurry fuel according to claim 1.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0021] FIG. 1 is a schematic diagram of a combustion mechanism of the AlLiH composite fuel.

DETAILED DESCRIPTION OF EMBODIMENTS

[0022] The present disclosure is described in detail as follows. The features and advantages of the present disclosure will become more clear and definite along with these descriptions.

[0023] The word exemplary is used exclusively herein to mean serving as an example, an embodiment, or an illustration. Any embodiment described herein as exemplary is not necessarily to be construed as superior or better than other embodiments.

[0024] According to the first aspect of the present disclosure, provided is a high-energy-density slurry fuel, comprising following components in mass percentage: [0025] aluminum-based metal hydride composite fuel: 3%-40%; [0026] liquid hydrocarbon fuel: 53.6%-96%; [0027] anti-settling agent: 0.2%-2%; [0028] other performance modifiers: 0.2%-5%; [0029] wherein the aluminum-based metal hydride is a composite material in which a metal hydride is dispersedly distributed inside aluminum powder particles, and the dispersed distribution refer to embedding the metal hydride inside the aluminum powder particles by means such as ball milling to form a structure of coating metal hydrides with aluminum powder.

[0030] In a preferred embodiment, the high-energy-density slurry fuel, based on the sum of the mass percentages of the components being 100%, comprises the following components in mass percentage: aluminum-based metal hydride composite fuel: 10%-25%; liquid hydrocarbon fuel: 74%-90%; anti-settling agent: 0.5%-2%; other performance modifiers: 0.2%-3%.

[0031] In a preferred embodiment, the aluminum-based metal hydride composite fuel is an AlLiH composite fuel. The AlLiH composite fuel is a powder composed of main phase aluminum and dispersed phase lithium hydride, wherein LiH is in a mass proportion of 2%-30%, preferably 5%-25%. The AlLiH composite fuel is micron-sized, with a median particle size D50 of 5-30 m.

[0032] The AlLiH composite fuel is prepared by a method comprising: weighing aluminum powder and lithium hydride in a glove box, mixing them uniformly, and then putting them into a ball mill tank, sealing the ball mill tank, and ball milling them in a ball mill to obtain the AlLiH composite fuel.

[0033] The aluminum powder is micron aluminum powder, and its specification is any one of FLQT1 (with a median particle size of 293 m), FLQT2 (with a median particle size of 243 m), FLQT3 (with a median particle size of 132 m), FLQT4 (with a median particle size of 61.5 m), FLQT5 (with a median particle size of 21 m), or a combination thereof.

[0034] The lithium hydride is in a micron size, with a median particle size D50 of 1 m to 15 m.

[0035] In the present disclosure, the ball mill is any one of a planetary ball mill, a horizontal ball mill and a conical ball mill.

[0036] When grinding, the ball-to-material ratio (that is, the mass ratio of the grinding balls of the ball mill to the material) is (10-50): 1.

[0037] The speed of the ball mill is 200 r/min to 400 r/min, and the duration of the ball milling is 30 min to 10 h.

[0038] Researches have found that the particle size of the aluminum powder and the lithium hydride, the rotation speed and the duration of the ball milling are closely related to the dispersion state of LiH in Al powder. The particle size of aluminum powder and lithium hydride is within the above range. By optimizing the ball milling process, the dispersed distribution of LiH in the Al powder can be realized. If the rotation speed is lower than the above range and the duration of the ball milling is shorter than the above range, the LiH is difficult to be dispersedly distributed in the Al powder: if the rotation speed is higher than the above range and the duration of the ball milling is longer than the above range, the particle size is too small, the aluminum powder has a large specific surface area, is easy to oxidize, and has low fuel energy.

[0039] The basic performance of the fuel is its ability to reliably realize the smooth conversion of chemical energy storage into gas kinetic energy to meet the application requirements of various engines. The AlLiH composite fuel is used to replace Al powder for high-energy-density slurry fuel. The AlLiH composite fuel is micron-sized on a macroscopic level, and the LiH is dispersedly distributed inside the aluminum powder on a microscopic level. During the combustion process of AlLiH composite fuel, without the participation of water, due to the property of LiH that it decomposes at a temperature (850 C.), which is slightly higher than the melting point of aluminum powder (660 C.), to generate gas (H.sub.2), a micro-explosion effect is formed inside the metal agglomeration. The large agglomerate explodes and disperses into numerous AlLi droplets. Furthermore, due to the characteristic that the boiling point of Li is significantly lower than that of Al (the boiling point of Al is 2327 C. and the boiling point of Li is 1340 C.), Li gasifies at high temperature, and AlLi continuously explodes into smaller droplets and enters the gas phase combustion, which not only makes the aluminum powder burn more fully, but also greatly can reduce the size of condensed phase combustion products and reduce the two-phase flow loss. The combustion mechanism of the AlLiH composite fuel is shown in FIG. 1.

[0040] The mass percentage content of the aluminum-based metal hydride composite fuel in the slurry fuel is in a range of 3% to 40%. If the content is lower and less than a minimum value of the above range, it will have no significant effect on the improvement of combustion performance and the increase of energy density of the fuel: if the content is higher and higher than the maximum value of the above range, there will be problems of insufficient fluidity of the slurry fuel and poor processability.

[0041] In a preferred embodiment, the liquid hydrocarbon fuel is a petroleum distillation product or/and a synthetic hydrocarbon, with a calorific value of 40 MJ.Math.kg.sup. and a density of 0.78 g.Math.cm.sup.3.

[0042] Furthermore, the petroleum distillation product is selected from one or more of No. 1 jet fuel RP-1, No. 2 jet fuel RP-2, No. 3 jet fuel RP-3, No. 4 jet fuel RP-4 or No. 5 jet fuel RP-5.

[0043] Furthermore, the synthetic hydrocarbon is selected from one or both of tetrahydrodicyclopentadiene or quadricyclane.

[0044] In a preferred embodiment, the anti-settling agent is white carbon black. The amount of white carbon black is crucial to the settling performance and energy performance of the slurry fuel. If the amount of white carbon black is too high and higher than 2%, the energy performance of the fuel will be affected. If the amount of white carbon black is too low and lower than 0.2%, the anti-settling performance of the fuel will decrease.

[0045] In a preferred embodiment, the other performance modifiers are used to adjust the combustion performance, flow performance and antioxidant performance of the high-energy-density slurry fuel, and are selected from one or more of iron oxide, octyl ferrocene, catocene, 3-amino-1,2,4-triazole copper perchlorate, copper chromite, ammonium oxalate, sodium oxalate, diethyl oxalate, nitromethane, isopropanol, octyl nitrate or isooctyl nitrate.

[0046] According to the second aspect of the present disclosure, a method for preparing the high-energy-density slurry fuel is provided, the method comprising the following steps: adding liquid hydrocarbon fuel, aluminum-based metal hydride composite fuel, anti-settling agent and other performance modifiers in a mixer according to a ratio of each component, mixing them at room temperature to a uniform slurry to obtain the high-energy-density slurry fuel.

[0047] According to the third aspect of the present disclosure, use of the high-energy-density slurry fuel according to the first aspect as a fuel for an engine such as a ramjet or a rocket engine is provided.

EXAMPLES

[0048] In order to enable those skilled in the art to better understand the present disclosure, the present disclosure can be further described in detail below in conjunction with specific examples. The calorific value is measured according to QGT219-2001, the density is measured according to GJB770B-401-2, the content of active aluminum in the residue is measured according to GJB1738A, and the combustion efficiency is calculated from the ratio of the measured calorific value to the theoretical calorific value.

Example 1

[0049]

TABLE-US-00001 (1) Composition of the fuel composition Formula composition Content/% Al2LiH (D.sub.50 30 m) 3 Tetrahydrodicyclopentadiene 96 White carbon black 0.8 Nitromethane 0.2

[0050] The method for preparing the high-energy-density slurry fuel was as follows. Tetrahydrodicyclopentadiene, AlLiH, white carbon black, and nitromethane were added in a 5 L vertical mixer according to the above ratio, and mixed at room temperature for 45 minutes to a uniform slurry to obtain a high-energy-density slurry fuel.

[0051] The method for preparing the Al-2LiH was as follows.

[0052] 9.8 g FLQT3 aluminum powder and 0.2 g LiH (D.sub.50 was 2 m) were mixed uniformly in a glove box and poured into the ball mill tank, and the ball mill tank was sealed and then the mixture was taken out and milled on a planetary ball mill at a speed of 200 r/min for 8 hours in which the ball-to-material ratio was 10:1, to obtain the Al-2LiH composite fuel.

TABLE-US-00002 (2) Performance of the fuel Measured calorific value Hu/MJ .Math. kg.sup.1 40.5 Density .sub.20 C./g .Math. cm.sup.3 0.954 Combustion efficiency/% 98 Content of active aluminum in residue/% 0.02

[0053] It can be known from Example 1 that the measured calorific value=40.5 MJ.Math.kg.sup.1 (greater than 38 MJ.Math.kg.sup.1), the density=0.954 g.Math.cm.sup.3 (.sub.20 C.>0.9 g.Math.cm.sup.3), the combustion efficiency=98%, the content of the active aluminum in the residue=0.02%. The fuel has advantages of high density, high energy, fast ignition speed and high combustion efficiency.

Example 2

[0054]

TABLE-US-00003 (1) Composition of the fuel composition Formula composition Content/% Al25LiH (D.sub.50 8 m) 18.5 Quadricyclane 80 White carbon black 0.5 Octyl ferrocene 1

[0055] The method for preparing the high-energy-density slurry fuel was the same as that in Example 1.

[0056] The method for preparing the Al-25LiH was as follows.

[0057] 7.5 g FLQT1 aluminum powder and 2.5 g LiH (D.sub.50 was 2 m) were mixed uniformly in a glove box and poured into the ball mill tank, and the ball mill tank was sealed and then the mixture was taken out and milled on a planetary ball mill at a speed of 300 r/min for 3 h in which the ball-to-material ratio was 20:1, to obtain the Al-25LiH composite fuel.

TABLE-US-00004 (2) Performance of the propellant Measured calorific value Hu/MJ .Math. kg.sup.1 40.9 Density .sub.20 C./g .Math. cm.sup.3 1.067 Combustion efficiency/% 99 Content of active aluminum in residue/% 0

[0058] It can be known from Example 2 that the measured calorific value=40.9 MJ.Math.kg.sup.1 (greater than 38 MJ.Math.kg.sup.1), the density=1.067 g.Math.cm.sup.3 (P20c>0.9 g cm.sup.3), the combustion efficiency=99%, the content of the active aluminum in the residue=0. The fuel has the advantages of high density, high energy, fast ignition speed and high combustion efficiency.

Example 3

[0059]

TABLE-US-00005 (1) Composition of the fuel composition Formula composition Content/% Al10LiH (D.sub.50 20 m) 40 RP-3 53.6 White carbon black 1.4 Isopropanol 3 Octyl ferrocene 1 Isooctyl nitrate 1

[0060] The method for preparing the high-energy-density slurry fuel was the same as that in Example 1.

[0061] The method for preparing the Al-10LiH was as follows.

[0062] 9.0 g FLQT1 aluminum powder and 1.0 g LiH (D.sub.50 was 2 m) were mixed uniformly in a glove box and poured into the ball mill tank, and the ball mill tank was sealed and then the mixture was taken out and milled on a planetary ball mill at a speed of 300 r/min for 5 hours in which the ball-to-material ratio was 25:1, to obtain the Al-10LiH composite fuel.

TABLE-US-00006 (2) Performance of the propellant Measured calorific value Hu/MJ .Math. kg.sup.1 38.9 Density .sub.20 C./g .Math. cm.sup.3 1.075 Combustion efficiency/% 98.5 Content of active aluminum in residue/% 0.05

[0063] It can be known from Example 3 that the measured calorific value=38.9 MJ.Math.kg.sup.1 (greater than 38 MJ.Math.kg.sup.1), the density=1.075 g.Math.cm.sup.3 (.sub.20 C.>0.9 g.Math.cm.sup.3), the combustion efficiency=98.5%, the content of the active aluminum in the residue=0.05%. The fuel has advantages of high density, high energy, fast ignition speed and high combustion efficiency.

Example 4

[0064]

TABLE-US-00007 (1) Composition of the fuel composition Formula composition Content/% Al20LiH (D.sub.50 10 m) 20.6 Tetrahydrodicyclopentadiene 74.8 White carbon black 2 Iron oxide 1 Isopropanol 1 Copper chromite 0.6

[0065] The method for preparing the high-energy-density slurry fuel was the same as that in Example 1.

[0066] The method for preparing the Al-20LiH was as follows.

[0067] 8.0 g FLQT5 aluminum powder and 2.0 g LiH (D.sub.50 was 2 m) were mixed uniformly in a glove box and poured into the ball mill tank, and the ball mill tank was sealed and then the mixture was taken out and milled on a planetary ball mill at a speed of 300 r/min for 8 hours in which the ball-to-material ratio was 30:1, to obtain the Al-20LiH composite fuel.

TABLE-US-00008 (2) Performance of the propellant Measured calorific value Hu/MJ .Math. kg.sup.1 38.4 Density .sub.20 C./g .Math. cm.sup.3 1.06 Combustion efficiency/% 99.5 Content of active aluminum in residue/% 0

[0068] It can be known from Example 4 that the measured calorific value=38.4 MJ.Math.kg.sup.1 (greater than 38 MJ.Math.kg.sup.1), the density=1.06 g.Math.cm.sup.3 (.sub.20 C.>0.9 g.Math.cm.sup.3), the combustion efficiency=99.5%, the content of the active aluminum in the residue=0. The fuel has advantages of high density, high energy, fast ignition speed and high combustion efficiency.

Example 5

[0069]

TABLE-US-00009 (1) Composition of the fuel composition Formula composition Content/% Al30LiH (D.sub.50 5 m) 38 Quadricyclane 60 White carbon black 0.2 Catocene 1.8

[0070] The method for preparing the high-energy-density slurry fuel was the same as that in Example 1.

[0071] The method for preparing the Al-30LiH was as follows.

[0072] 7.0 g FLQT5 aluminum powder and 3.0 g LiH (D.sub.50 was 2 m) were mixed uniformly in a glove box and poured into the ball mill tank, and the ball mill tank was sealed and then the mixture was taken out and milled on a planetary ball mill at a speed of 300 r/min for 5 hours in which the ball-to-material ratio was 40:1, to obtain the Al-30LiH composite fuel.

TABLE-US-00010 (2) Performance of the propellant Measured calorific value Hu/MJ .Math. kg.sup.1 39.1 Density .sub.20 C./g .Math. cm.sup.3 1.153 Combustion efficiency/% 98.9 Content of active aluminum in residue/% 0.02

[0073] It can be known from Example 5 that the measured calorific value=39.1 MJ.Math.kg.sup.1 (greater than 38 MJ.Math.kg.sup.1), the density=1.153 g.Math.cm.sup.3 (.sub.20 C.>0.9 g.Math.cm.sup.3), the combustion efficiency=98.9%, the content of the active aluminum in the residue=0.02%. The fuel has advantages of high density, high energy, fast ignition speed and high combustion efficiency.

Example 6

[0074]

TABLE-US-00011 (1) Composition of the fuel composition Formula composition Content/% Al15LiH (D.sub.50 15 m) 10 Quadricyclane 88 White carbon black 1.1 Iron oxide 0.9

[0075] The method for preparing the high-energy-density slurry fuel was the same as that in Example 1.

[0076] The method for preparing the Al-15LiH was as follows.

[0077] 8.5 g FLQT3 aluminum powder and 1.5 g LiH (D50 was 14 m) were mixed uniformly in a glove box and poured into the ball mill tank, and the ball mill tank was sealed and then the mixture was taken out and milled on a planetary ball mill at a speed of 250 r/min for 5 hours in which the ball-to-material ratio was 20:1, to obtain the Al-15LiH composite fuel.

TABLE-US-00012 (2) Performance of propellant Measured calorific value Hu/MJ .Math. kg.sup.1 41.3 Density .sub.20 C./g .Math. cm.sup.3 1.048 Combustion efficiency/% 99.5 Content of active aluminum in residue/% 0.01

[0078] It can be known from Example 6 that the measured calorific value=41.3 MJ.Math.kg.sup.1 (greater than 38 MJ.Math.kg-2), the density=1.048 g.Math.cm.sup.3 (.sub.20 C.>0.9 g.Math.cm.sup.3), the combustion efficiency=99.5%, the content of the active aluminum in the residue=0.01%. The fuel has advantages of high density, high energy, fast ignition speed and high combustion efficiency.

Example 7

[0079]

TABLE-US-00013 (1) Composition of the fuel composition Formula composition Content/% Al16LiH (D.sub.50 13 m) 21.5 Tetrahydrodicyclopentadiene 74 White carbon black 1.5 Octylferrocene 2 Nitromethane 1

[0080] The method for preparing the high-energy-density slurry fuel was the same as that in Example 1.

[0081] The method for preparing the Al-16LiH was as follows.

[0082] 8.4 g FLQT1 aluminum powder and 1.6 g LiH (D.sub.50 was 14 m) were mixed uniformly in a glove box and poured into the ball mill tank, and the ball mill tank was sealed and then the mixture was taken out, and milled on a planetary ball mill at a speed of 300 r/min for 3 hours in which the ball-to-material ratio was 25:1, to obtain the Al-16LiH composite fuel.

TABLE-US-00014 (2) Propellant performance Measured calorific value Hu/MJ .Math. kg.sup.1 38.6 Density .sub.20 C./g .Math. cm.sup.3 1.067 Combustion efficiency/% 99.2 Content of active aluminum in residue/% 0.02

[0083] It can be known from Example 7 that the measured calorific value=38.6 MJ.Math.kg.sup.1 (greater than 38 MJ.Math.kg.sup.1), the density=1.067 g cm.sup.3 (.sub.20 C.>0.9 g.Math.cm.sup.3), the combustion efficiency=99.2%, the content of the active aluminum in the residue=0.02%, which has the advantages of high density, high energy, fast ignition speed and high combustion efficiency.

COMPARATIVE EXAMPLES

[0084]

TABLE-US-00015 Comparative example 1 Composition of the fuel composition Formula composition Content/% Al2LiH (D.sub.50 30 m) 2 Tetrahydrodicyclopentadiene 97 White carbon black 0.8 Nitromethane 0.2

[0085] The method for preparing the slurry fuel and Al-2LiH was the same as that in Example 1.

[0086] The above-mentioned slurry fuel was subjected to a settling test. After 3 days, visual inspection showed that the fuel was stratified with metal powder at the bottom layer and liquid fuel at the upper layer. It can be seen that reducing the AlLiH content is not conducive to the stable storage performance of the fuel.

TABLE-US-00016 Comparative example 2 Composition of the fuel composition Formula composition Content/% Al10LiH (D.sub.50 20 m) 45 RP-3 48.6 White carbon black 1.4 Isopropanol 3 Octylferrocene 1 Isooctyl nitrate 1

[0087] The method for preparing the slurry fuel was as follows. RP-3, AlLiH, white carbon black, isopropanol, octylferrocene and isooctyl nitrate were added in a 5 L vertical mixer according to the above ratio, and mixed at room temperature. Since the viscosity of the fuel was high, the powder was agglomerated and difficult to disperse, and a uniform slurry fuel cannot be obtained.

[0088] The method for preparing the Al-10LiH was the same as that in Example 3.

TABLE-US-00017 Comparative example 3 Composition of the fuel composition Formula composition Content/% Al20LiH (D.sub.50 10 m) 20.6 Tetrahydrodicyclopentadiene 71.8 White carbon black 5 Iron oxide 1 Isopropanol 1 Copper chromite 0.6

[0089] The method for preparing the slurry fuel was the same as that in Example 1.

[0090] The method for preparing the Al-20LiH was the same as that in Example 4.

TABLE-US-00018 Measured calorific value Hu/MJ .Math. kg.sup.1 33.5 Density .sub.20 C./g .Math. cm.sup.3 1.084 Combustion efficiency/% 90 Content of active aluminum in residue/% 1

[0091] Compared with Example 4, the anti-settling performance of the fuel was equivalent (it could be stored stably within one month), but the calorific value of the fuel was significantly reduced, and the combustion efficiency was reduced. It can be seen that an excessive white carbon black will affect the combustion efficiency and energy performance of the fuel.

TABLE-US-00019 Comparative example 4 Composition of the fuel composition Formula composition Content/% Al30LiH (D.sub.50 5 m) 38 Quadricyclane 60 White carbon black 0.05 Catocene 1.95

[0092] The method for preparing the slurry fuel was the same as that in Example 1.

[0093] The method for preparing the Al-30LiH was the same as that in Example 5.

[0094] The above-mentioned slurry fuel was subjected to a settling test. After one week, visual inspection showed that the fuel was stratified with metal powder at the bottom layer and liquid fuel at the upper layer.

TABLE-US-00020 Comparative example 5 (1) Composition of the fuel composition Formula composition Content/% Aluminum powder (D.sub.50 28 m) 3 Tetrahydrodicyclopentadiene 96 White carbon black 0.8 Nitromethane 0.2

[0095] The method for preparing the slurry fuel was as follows. Tetrahydrodicyclopentadiene, Al powder, white carbon black, and nitromethane were added in a 5 L vertical mixer according to the above ratio, and mixed at room temperature for 45 minutes to a uniform slurry.

TABLE-US-00021 (2) Performance of the fuel Measured calorific value Hu/MJ .Math. kg.sup.1 39 Density .sub.20 C./g .Math. cm.sup.3 0.958 Combustion efficiency/% 93 Content of active aluminum in residue/% 0.2

[0096] It can be known from Comparative Example 5 that the measured calorific value=39 MJ.Math.kg.sup.1, the density=0.958 g.Math.cm.sup.3, the combustion efficiency=93%, the active aluminum content in the residue=0.2%. Compared with the fuel in the formula of Example 1, there are problems of incomplete combustion and deposition phenomena.

[0097] The present disclosure has been described in detail above in conjunction with specific implementations and exemplary embodiments, but these descriptions should not be construed as limiting the present disclosure. Those skilled in the art understand that without departing from the spirit and scope of the present disclosure, various equivalent replacements, modifications or improvements can be made to the technical solutions and implementations of the present disclosure, all of which fall within the scope of the present disclosure. The protection scope of the present disclosure shall be determined by the appended claims.

[0098] The content that is not described in detail in the description of the present disclosure belongs to the well-known technology of those skilled in the art.