END-MILLS MADE OF HARD METAL AND CERAMIC COMBINED BY BRAZING METHOD

Abstract

The present invention is an end-mill (A) comprising a shank (B) and a cutting portion (C) along its longitudinal axis (4), and formed by combining ceramic and metal based materials via brazing method, comprising: a cutting diameter (1) varying between 2 to 20 mm, at least one web thickness (18) 0 found at a blade (26) part, at least one helix angle (10) having a cutting edge (13) thereon, a core diameter (16) that is at least 0.7 times the cutting diameter (1), at least one corner radius (5) found at the tip part of the blades (26) between the flutes (9) and axial and radial rake angles (17) at which cutting operation is made. TiAlN coating is applied over ceramic-metal based 5 end-mill (A) by PVD method in order to extend the service life of the end-mill, increase abrasion resistance, and minimize the welding (sticking) problem of chips on the cutting tools.

Claims

1. An end-mill (A) comprising a shank (B) and a cutting portion (C), characterized in that, the shank (B) is formed by combining metal and ceramic-based materials via a brazing method and said cutting portion (C) comprises: a cutting diameter (1) varying between 2 to 20 mm, at least one web thickness (18) found at a blade (26) part, at least one helix angle (10) having a cutting edge (13) thereon, a core diameter (16) that is at least 0.7 times the cutting diameter (1), at least one corner radius (5) found at the tip part of the blade (26) part between plurality of flutes (9) and an axial rake angle and radial rake angle (17) at which a cutting operation is made.

2. The end-mill (A) according to claim 1, characterized in that, a helical structure found at edges of the plurality of flutes (9) along a longitudinal axis (4) continues in a longitudinally helical structure and ends at the web thickness (18) found at the blade (26) part.

3. The end-mill (A) according to claim 1, characterized in that, a helix length (3) is about 1 to 2 times the cutting diameter (1).

4. The end-mill (A) according to claim 1, characterized in that, a number of blades (26) varies between 2 to 8, depending on the cutting diameter (1).

5. The end-mill (A) according to claim 1, characterized in that, the corner radius (5) is between 0.01 to 0.4 times the cutting diameter (1).

6. The end-mill (A) according to claim 1, characterized in that, the helix angle (10) varies from 28 to 43, depending on characteristics of a material to be machined.

7. The end-mill (A) according to claim 1, characterized in that, the radial rake angle (17) is between 6 to +6 interval.

8. The end-mill (A) according to claim 1, characterized in that, the axial rake angle is between 3 to +5 interval.

9. The end-mill (A) according to claim 1, characterized in that, a gash angle (24) is between 15 to 45 interval.

10. The end-mill (A) according to claim 1, characterized in that, an end rake (28) angle at a front part of the end mill is between 6 to +6 interval.

11. The end-mill (A) according to claim 1, characterized in that, a dish angle (23) at an opening part of the flutes (9) is between 1 to 3.

12. The end-mill (A) according to claim 1, characterized in that, the end mill comprises a TiAlN coating applied by a PVD method in order to extend a service life, increase abrasion resistance, and minimize a welding (sticking) problem of chips on the cutting portion.

13. The end-mill (A) according to claim 1, characterized in that, the end mill comprises a front joint type in joining metal and ceramic pieces by the brazing method.

14. The end-mill (A) according to claim 1, characterized in that, the end mill comprises a lap joint type in joining metal and ceramic pieces by the brazing method.

15. The end-mill (A) according to claim 1, characterized in that, the end mill comprises a front-lap joint type in joining metal and ceramic pieces by the brazing method.

16. The end-mill (A) according to claim 1, characterized in that, the end mill comprises a scarf joint type in joining metal and ceramic pieces by the brazing method.

Description

BRIEF DESCRIPTION OF THE FIGURES

[0034] For better understanding of the embodiment of the present invention and its advantages with its additional components, it should be evaluated together with below described figures.

[0035] FIG. 1; is the side profile view of the 4-flute embodiment of the end-mill according to the invention produced by combining ceramic-metal-based materials via brazing method.

[0036] FIG. 2; is the side profile view of the 6-flute embodiment of the end-mill according to the invention produced by combining ceramic-metal-based materials via brazing method.

[0037] FIG. 3; is the side profile view of the end-mill according to the invention produced by combining ceramic-metal-based materials via brazing method; showing the cutting edges, blades, primary relief angle adjacent to the helix angle and the secondary relief angle.

[0038] FIG. 4; is the side profile view of the end-mill according to the invention produced by combining ceramic-metal-based materials via brazing method; showing width of primary relief land and axial width of secondary relief land.

[0039] FIG. 5; is the side profile view of the end-mill according to the invention produced by combining ceramic-metal-based materials via brazing method; showing the axial primary relief angle, axial secondary relief angle, and the gear angle dimensioned according to the plain surface that is tangent to the cutting end.

[0040] FIG. 6; is the front part view of the end-mill according to the invention produced by combining ceramic-metal-based materials via brazing method; showing the web thickness, gash angle, pods, number of flutes, and end rake.

[0041] FIG. 7; is the front profile view of the end-mill according to the invention produced by combining ceramic-metal-based materials via brazing method; showing the radial primary relief angle and radial secondary relief angles found beside the blade helix angle, the core diameter and the radial rake angle.

[0042] FIG. 8; is a three-dimensional view of a preferred embodiment of the end-mill according to the invention produced by combining ceramic-metal based materials via brazing method.

[0043] FIG. 9; is the view showing the way of joint design used in combining of ceramic-metal-based materials via brazing method in production of the end-mill according to the invention.

REFERENCE NUMBERS

[0044] A: End-mill [0045] B: Shank [0046] C: Cutting Portion [0047] 1. Cutting diameter [0048] 2. Shank diameter [0049] 3. Helix length [0050] 4. Longitudinal axis [0051] 5. Corner radius [0052] 6. Cutting End [0053] 7. Total length [0054] 8. Shank length [0055] 9. Flute [0056] 10. Helix angle [0057] 11. Primary relief angle [0058] 12. Secondary relief angle [0059] 13. Cutting edge [0060] 14. Width of primary relief land [0061] 15. Width of secondary relief land [0062] 16. Core diameter [0063] 17. Radial rake angle [0064] 18. Web thickness [0065] 19. Axial primary relief angle [0066] 20. Axial secondary relief angle [0067] 21. Radial primary relief angle [0068] 22. Radial secondary relief angle [0069] 23. Dish angle [0070] 24. Gash angle [0071] 26. Blades [0072] 27. Cutting edge tangent [0073] 28. End rake [0074] 29. Brazing area

DETAILED DESCRIPTION OF THE INVENTION

[0075] In this detailed description, the preferred embodiments of the end-mill (A) according to the invention are only disclosed for better understanding of the subject without forming any limiting effect.

[0076] The present invention relates to end-mill (A) that can be made of ceramic or any other material having high strength and toughness. The improvement provided with the invention basically relates to production of ceramic end-mills (A) by means of combining ceramic-metal based materials via brazing method. Additionally, Titanium Aluminium Nitride (TiAlN) coating can be applied via PVD coating method in order to extend the service life of the ceramic cutting portion (C), increase abrasion resistance, and minimize the problem of the chips welding (sticking) to the cutting tools

[0077] FIG. 1 shows a preferably 4-flute (9) embodiment of the end-mill (A) according to the invention produced by combining ceramic-metal-based materials via brazing method, while FIG. 2 shows the side profile view of the preferably 6-flute (9) embodiment. The end-mill (A) basically consists of a shank (B) for attaching the tool holder and cutting portion (C) for machining the material surface via rotational motion. The end-mill (A) has a cylindrical shape and it is produced by brazing of metal and ceramic based materials. FIG. 8 shows a three-dimensional view of a preferred embodiment of the ceramic-metal-based end-mill (A) according to the invention.

[0078] As can be seen from FIGS. 1 and 2, the ceramic-metal-based end-mill (A) has a cutting diameter (1) comprising blades (26) along the longitudinal axis (4) of its cylindrical body, and a diameter of the shank (2) that is fixed to the holder. While the cutting diameter (1) varies between 2 to 20 mm, the helix length (3) defining the cutting length can be between 1 to 2 times of the cutting diameter (1).

[0079] The total length (7) of the end-mill (A) is equal to the summation of the helix length (3) and the shank length (8). At the tip of the cutting portion (C), the cutting end (6) and the corner radius (5) structures shown in FIG. 1 are found.

[0080] The shank diameter (2) and the cutting diameters (1) can be same or different from each other in the end-mill (A). The adjacent blades (26) arranged on the helix angle (10) of the end-mill (A) are separated from each other via flute (9) grooves. The blades (26) extending along the longitudinal axis (4) end at the end-mill (A) cutting end (6).

[0081] The core diameter (16) of the end-mill (A) can be about 0.70-0.75 times the cutting diameter (1). The blades (26) have a radial rake angle (17) where cutting operation is made and an axial rake angle. The radial rake angle (17) has a negative-positive angle.

[0082] In the side profile view of the monolithic end-mill (A) according to the invention given in FIG. 3; the cutting edges (13), 2 to 8 blades (26), the primary relief angle (11) adjacent to the helix angle (10) and the secondary relief angle (12) can be seen. In FIG. 4, the width of axial primary relief land (14) and the width of axial secondary relief land (15) corresponding to the primary relief angle (11) and the secondary relief angle (12), respectively, are shown.

[0083] In FIG. 5, the axial primary relief angle (19), the axial secondary relief angle (20), and dish angle (23) dimensioned according to the cutting edge tangent (27) that is tangent to the cutting end (6) in the front part of the end-mill (A) are shown.

[0084] From the front part view of the end-mill (A) according to the invention produced by combining ceramic-metal-based materials via brazing method given in FIG. 6; the web thickness (18) corresponding to the gap between the flutes (9) found at the cutting end (6), the gash angle (24) corresponding to the angle found at the sides of the blades (26) found at each helix angle (10), and the number of the flutes (9) found at the ends can be seen. FIG. 6 also shows the end rake (28) indicating the end of the radial rake angle (17).

[0085] From the front profile view of the end-mill (A) according to the invention produced by combining ceramic-metal-based materials via brazing method given in FIG. 7; the Radial primary relief angle (21) and Radial secondary relief angle (22) found beside the blade (26) helix angle (10) can be seen.

[0086] In the end-mill (A) according to the invention produced by combining ceramic-metal-based materials via brazing method: [0087] The length of the helical cutting portion (C) that is twice the cutting diameter (1) is less than the shank (B), [0088] If the core diameter (16) is 0.7 times the cutting diameter (1), then the helix angle (10) is between 28 to 43 around its axis. [0089] The number of flutes (9) is between 2 to 8. [0090] The end rake (28) angle is between 6 to +6 interval. [0091] The corner radius (5) is about 0.010-0.4 times the cutting diameter (1). [0092] Radial rake angle (17) is between 6 to +6. [0093] Axial rake angle is approximately between 3 to +5. [0094] The dish angle (23) varies between 1 to 3. [0095] The gash angle (24) is between 15 to 45 interval. [0096] Moreover, the cutting diameter (1) is preferred to remain constant along the helix length (3), but it can also be tapered along the helix length (3). [0097] The cutting diameter (1) can have diameters varying between 2 to 20 millimetres and the number of flutes (9) may increase as the cutting diameter (1) increases.

[0098] The production steps of the end-mill (A) according to the invention produced by combining ceramic-metal-based materials via brazing method are as follows:

[0099] The end-mill (A) according to the invention is formed by combining ceramic and metal-based materials via brazing method. In this regard, first of all, the operation of combining the metal and ceramic materials to be used in end-mill (A) is performed during production. Use of various techniques is possible in combining the metal and ceramic materials with each other via brazing method. In FIG. 9, the joint designs that can be used in the brazing method of metal and ceramic materials are shown. The joint designs provided in FIG. 9 are front joint, lap joint, front-lap joint, scarf joint, and T-joint, respectively, from top to down. While metal material and ceramic material are combined in the production of end-mill (A) according to the invention, the joint design given in FIG. 9 or their other combinations may be used. In FIGS. 1 and 2, the brazing area (29) between the shank (B) and the cutting portion (C) of the ceramic-metal-based end-mill (A) can be seen.

[0100] The ceramic-metal based end-mill (A) is obtained by placing brazing material to the brazing area (29) shown in FIG. 9 and then performing brazing operation between 650-730 C. During production of the ceramic-metal based end-mill (A), vacuum oven (vacuum or inert gas medium), induction (vacuum or inert gas medium) can be used as the thermal treatment source. A brazing material formed of the oxides shown in the below given table as recipe A or recipe B should be used as the brazing material. Brazing material can be in paste or thin strip metal sheet form. HSS, tungsten carbide, tool steel, densimet, or low alloy steels above 40 HRC can be used as the shank (B) material of the end-mill (A) manufactured by combining ceramic-metal-based materials via brazing method. As the cutting portion (C) material, Silicon Nitride (Si.sub.3N.sub.4) based ceramics, alumina-added silicon carbide whisker, silicon carbide, alpha/beta (20:80 to 80:20) SiAlON (Si.sub.3N.sub.4+Al.sub.2O.sub.3+AlN+Y.sub.2O.sub.3+Sm.sub.2O.sub.3+CaCO.sub.3), Al.sub.2O.sub.3 can be used.

TABLE-US-00001 Recipe A Recipe B Percent Ingredient Percent Oxides (%) Oxides Ingredient (%) Ag 50-75% Ag 80-99% Ti 0-5% Ti 0-10% Cu 20-40% In 0-10% In 0-20% Al 0-2% Sn 0-6%

[0101] During milling operation, the problem of the removed chip welding (sticking) on the ceramic cutting portion (C) surface due to formation of high temperature on the surface of the manufacturing part is encountered. In the end-mill (A) according to the invention produced by combining ceramic-metal based materials via brazing method, TiAlN coating is applied by PVD method in order to extend the service life, increase abrasion resistance, and minimize the welding (sticking) problem of chips on the cutting tool.

[0102] It is known that the AlN phase having hexagonal lattice structure provides better adhesion over the ceramic material surface than the cubical lattice TlN phase. This means that inter-atomic bonds are formed between the TiAlN coating and the ceramic material. By means of the inter-atomic bonds, the end-mill (A) can easily be polarized during coating. Following coating, the surface hardness and surface roughness of the ceramic material is increased. As a result of trials, it is found out that the chip welding (sticking) problem is reduced on the coated surface. In test studies made at dry 600 m/min cutting speed at a high speed machine, machining is performed on inconel 718 material with the end mill (A) according to the invention and 17.6 cm.sup.3/min chips are removed from the material.

Other Improvements Provided with the End-Mill (A) According to the Invention Produced by Combining Ceramic-Metal-Based Materials Via Brazing Method are as Follows: [0103] The cutting diameter (1) of the monolithic end-mill (A) having axial structure is between 2 to 20 mm, [0104] A web thickness (18) is found at the blade (26) part of the end-mill (A) and it has a helix angle (10) having a cutting edge (13) thereon, [0105] It has a core diameter (16) which is at least 0.7 times the cutting diameter (1), [0106] The helical structure found at the edges of the flute (9) along the longitudinal axis (4) continues in a longitudinally helical structure and ends at the web thickness (18) found at the blade (26) part. [0107] A corner radius (5) is found at the tip part of the blades (26) between the plurality of flutes (9) and axial and radial rake angles (17) are found where cutting operation is made, [0108] The helix length (3) indicating the cutting length is about 1 to 2 times of the cutting diameter (1), [0109] The number of flutes (9) vary between 2 to 8, depending on the end mill (A) diameter, [0110] The corner radius (5) is between 0.01 to 0.4 times of the cutting diameter (1), [0111] The helix angle (10) can be from 28 to 43 degrees, depending on the characteristics of the material to be machined. [0112] The radial rake angle (17) is between 6 to +6 interval, the axial rake angle is between 3 to +5 interval, the gash angle (24) is between 15 to 45 interval, the end rake (28) angle found at the front part of the milling cutter set is between 6 to +6 interval, the dish angle (23) at the blade part of the flutes (9), that is to say, the pit angle is between 1 to 3.

[0113] In the end-mill (A) according to the invention produced by combining ceramic-metal based material via brazing method, the excellent thermo-mechanical characteristics of ceramic materials and the vibration damping, high ductility and toughness etc. superior characteristics of metal materials are combined via brazing method. The length of the cutting tool could be extended by developing the ceramic-metal based end-mill form and the problem of breakage encountered in monolithic ceramic end-mills (A) due to the length/diameter ratio is greater than 2 is overcame. High speed machining of deep and narrow blade gaps that can only be achieved by end mills which have length/diameter ratio greater than 2 is enabled with ceramic-metal based end-mill (A) in production of aviation, aerospace, and gas turbine blades.

[0114] When the cost of monolithic ceramic end mill is compared with the cost of ceramic-metal based brazed end mills, it can be seen that the end mill costs are lower in production of brazed end mill, since less ceramic component is used in this method. With the end mill (A) embodiment according to the invention produced by joining ceramic-metal based materials via brazing method, both the processing costs of the end mill (A) and the manufacturing parts are reduced and the operational efficiency and profitability are increased.