ZONED AMMONIA SLIP CATALYST FOR IMPROVED SELECTIVITY, ACTIVITY AND POISON TOLERANCE
20230035318 · 2023-02-02
Inventors
Cpc classification
B01J37/0246
PERFORMING OPERATIONS; TRANSPORTING
F01N13/0093
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
F01N2510/0682
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
B01J37/0248
PERFORMING OPERATIONS; TRANSPORTING
B01D2258/012
PERFORMING OPERATIONS; TRANSPORTING
F01N2370/04
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
F01N3/2803
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
B01D53/9477
PERFORMING OPERATIONS; TRANSPORTING
F01N2370/02
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
F01N3/106
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
F01N2510/0684
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
Y02T10/12
GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
F01N3/103
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
F01N3/0828
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
F01N3/2066
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
F01N3/021
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
B01J37/0244
PERFORMING OPERATIONS; TRANSPORTING
F01N13/009
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
International classification
Abstract
A catalytic article for treating exhaust gas comprising: a substrate comprising an inlet end and an outlet end with an axial length L; a first catalytic region comprising a first platinum group metal (PGM) component and a support; a second catalytic region comprising a second PGM component on a support with low ammonia storage and a first SCR catalyst; and wherein the first catalytic region is covered by at least another catalytic region.
Claims
1. A catalytic article for treating exhaust gas comprising: a substrate comprising an inlet end and an outlet end with an axial length L; a first catalytic region comprising a first platinum group metal (PGM) component and a support; a second catalytic region comprising a second PGM component on a support with low ammonia storage and a first SCR catalyst; and wherein the first catalytic region is covered by at least another catalytic region.
2. The catalytic article of claim 1, wherein the first PGM component is Pt.
3. The catalytic article of claim 1, wherein the second PGM component is Pt.
4. The catalytic article of claim 1, wherein the ratio of the first PGM component to the second PGM component is from 5:1 to 1:5.
5. The catalytic article claim 1, wherein the support is alumina, silica, zirconia, titania, ceria, and physical mixtures or composites thereof.
6. The catalytic article claim 1, wherein the first catalytic region extends for 30 to 99 percent of the axial length L.
7. The catalytic article claim 1, wherein the second catalytic region comprises a blend of the second PGM component on the support with low ammonia storage with a first SCR catalyst.
8. The catalytic article claim 1, wherein the support with low ammonia storage is a siliceous support comprising a silica or a zeolite.
9. The catalytic article of claim 8, wherein the zeolite has a silica-to-alumina ratio of ≥100.
10. The catalytic article claim 1, wherein the second catalytic region extends for 30 to 99 percent of the axial length L.
11. The catalytic article claim 1, wherein the second catalytic region covers at least 10% of the first catalytic region.
12. The catalytic article claim 1, wherein the second catalytic region covers 100% of the first catalytic region.
13. The catalytic article claim 1, wherein the first SCR catalyst comprises a first transitional metal and a first molecular sieve.
14. (canceled)
15. (canceled)
16. The catalytic article claim 1, wherein the ratio of the amount of the first SCR catalyst to the amount of the second PGM component on the support with low ammonia storage is in the range of 0:1 to 300:1.
17. The catalytic article claim 1, further comprising a third catalytic region.
18. The catalytic article of claim 17, wherein the third catalytic region comprises a second SCR catalyst, wherein the second SCR catalyst comprises a base metal, an oxide of a base metal, a noble metal, a molecular sieve, a second transitional metal exchanged molecular sieve or a mixture thereof.
19. (canceled)
20. (canceled)
21. (canceled)
22. (canceled)
23. The catalytic article of claim 17, wherein the third catalytic region covers 100% of the first catalytic region.
24. The catalytic article of claim 17, further comprising a fourth catalytic region.
25. The catalytic article of claim 24, wherein the fourth catalytic region comprises a third SCR catalyst, wherein the third SCR catalyst comprises a base metal, an oxide of a base metal, a noble metal, a molecular sieve, a third transitional metal exchanged molecular sieve or a mixture thereof.
26. (canceled)
27. The catalytic article of claim 24, wherein the fourth catalytic region begins at the inlet end and extends for less than the axial length L.
28. The catalytic article of claim 27, wherein the first catalytic region begins at the outlet end and extends for less than the axial length L.
29. The catalytic article of claim 27, wherein the second catalytic region begins at the outlet end and extends for less than the axial length L.
30. The catalytic article of claim 27, wherein the second catalytic region begins at the inlet end and extends for less than the axial length L
31. The catalytic article of claim 27, wherein the third catalytic region begins at the outlet end and extends for less than the axial length L.
32. The catalytic article of claim 27, wherein the third catalytic region begins at the inlet end and extends for less than the axial length L.
33. (canceled)
34. (canceled)
35. (canceled)
36. (canceled)
37. (canceled)
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0009]
[0010]
[0011]
[0012]
[0013]
[0014]
[0015]
[0016]
[0017]
[0018]
[0019]
[0020]
[0021]
[0022]
[0023]
[0024]
[0025]
DETAILED DESCRIPTION OF THE INVENTION
[0026] As used in this specification and the appended claims, the singular forms “a”, “an” and “the” include plural referents unless the context clearly indicates otherwise. Thus, for example, reference to “a catalyst” includes a mixture of two or more catalysts, and the like.
[0027] As used herein, the term “ammonia slip”, means the amount of unreacted ammonia that passes through the SCR catalyst.
[0028] The term “support” means the material to which a catalyst is fixed.
[0029] The term “a support with low ammonia storage” means a support that stores less than 0.001 mmol NH.sub.3 per m.sup.3 of support. The support with low ammonia storage is preferably a molecular sieve or zeolite having a framework type selected from the group consisting of AEI, ANA, ATS, BEA, CDO, CFI, CHA, CON, DDR, ERI, FAU, FER, GON, IFR, IFW, IFY, IHW, IMF, IRN, IRY, ISV, ITE, ITG, ITN, ITR, ITW, IWR, IWS, IWV, IWW, JOZ, LTA, LTF, MEL, MEP, MFI, MRE, MSE, MTF, MTN, MTT, MTW, MVY, MWW, NON, NSI, RRO, RSN, RTE, RTH, RUT, RWR, SEW, SFE, SFF, SFG, SFH, SFN, SFS, SFV, SGT, SOD, SSF, SSO, SSY, STF, STO, STT, SVR, SVV, TON, TUN, UOS, UOV, UTL, UWY, VET, VNI. More preferably, the support with low ammonia storage is a molecular sieve or zeolite having a framework type selected from the group consisting of BEA, CDO, CON, FAU, MEL, MFI and MWW, even more preferably the framework type is selected from the group consisting of BEA and MFI.
[0030] The term “calcine”, or “calcination”, means heating the material in air or oxygen. This definition is consistent with the IUPAC definition of calcination. (IUPAC. Compendium of Chemical Terminology, 2nd ed. (the “Gold Book”). Compiled by A. D. McNaught and A. Wilkinson. Blackwell Scientific Publications, Oxford (1997). XML on-line corrected version: http://goldbook.iupac.org (2006-) created by M. Nic, J. Jirat, B. Kosata; updates compiled by A. Jenkins. ISBN 0-9678550-9-8. doi:10.1351/goldbook.) Calcination is performed to decompose a metal salt and promote the exchange of metal ions within the catalyst and also to adhere the catalyst to a substrate. The temperatures used in calcination depend upon the components in the material to be calcined and generally are between about 400° C. to about 900° C. for approximately 1 to 8 hours. In some cases, calcination can be performed up to a temperature of about 1200° C. In applications involving the processes described herein, calcinations are generally performed at temperatures from about 400° C. to about 700° C. for approximately 1 to 8 hours, preferably at temperatures from about 400° C. to about 650° C. for approximately 1 to 4 hours.
[0031] The term “about” means approximately and refers to a range that is optionally ±25%, preferably ±10%, more preferably, ±5%, or most preferably ±1% of the value with which the term is associated.
[0032] When a range, or ranges, for various numerical elements are provided, the range, or ranges, can include the values, unless otherwise specified.
[0033] The term “N.sub.2 selectivity” means the percent conversion of ammonia into nitrogen.
[0034] The term “platinum group metal” or “PGM” refers to platinum, palladium, ruthenium, rhodium, osmium and iridium. The platinum group metals are preferably platinum, palladium, ruthenium or rhodium.
[0035] In the first aspect of the invention, a catalytic article for treating exhaust gas comprising: a substrate comprising an inlet end and an outlet end with an axial length L; a first catalytic region comprising a first platinum group metal (PGM) component and a support; a second catalytic region comprising a second PGM component on a support with low ammonia storage and a first SCR catalyst; and wherein the first catalytic region is covered by at least another catalytic region.
First Catalytic Region
[0036] The first catalytic region can fully oxidize NH.sub.3 into NO.sub.x and H.sub.2O, including at low temperatures such as below about 250° C., below about 200° C., or below about 150° C. The first PGM can be Pt or combinations of Pt and Pd. Preferably, the first PGM is Pt. In certain embodiments, the first catalytic region can contain at least about 30 weigh percent, at least about 50 weight percent, at least about 60 weight percent, at least about 75 weight percent, or at least about 90 weight percent Pt, based on the total weight of the noble metal present in the first catalytic region.
[0037] The support is preferably a high surface area support. The type of support is not particularly limited provided that it is a particle having a large surface area, is inert, and is suitable for use in an after-treatment system. Examples of support materials include refractory metal oxides such as alumina, silica, zirconia, titania, ceria, and physical mixtures or composites thereof, with alumina being particularly preferred. In certain embodiments, the supports have wide pores (e.g., 100-350 Å) or both wide and narrow pores. In certain embodiments, the support has a BET surface area of at least 50 m.sup.2/g, preferably about 50-500 m.sup.2/g, more preferably about 50-300 m.sup.2/g, or about 150-250 m.sup.2/g. Refractory metal oxide support preferably have a pore volume of about 0.1-0.5 g/cc, for example about 0.2-0.4 g/cc, preferably measured by mercury intrusion porosimetry. The mean particle size, based on the particle count, of the support material is preferably about 0.01-10 μm, for example about 0.5-5 μm, about 0.1-1 μm, or about 5-10 μm, and preferably has a majority of the particle count within one of these ranges. In certain embodiments, the D90 particle size of the support is within one of these ranges.
[0038] The first catalytic region can extend for 30 to 99 percent of the axial length L; preferably, 40 to 95 percent or 45 to 90 percent of the axial length L; more preferably, 50 to 85 percent of the axial length L; and even more preferably, 65 to 80 percent of the axial length L.
Second Catalytic Region
[0039] The combination of the second PGM on a support with low ammonia storage and a first SCR catalyst is either (a) a blend of the second PGM on a support with low ammonia storage with a first SCR catalyst, or (b) a bi-layer having a top layer comprising a first SCR catalyst and a bottom layer comprising the second PGM on a support with low ammonia storage, where the bottom layer can be positioned on a substrate. Preferably, the second catalytic region is a blend of the second PGM on a support with low ammonia storage with a first SCR catalyst.
[0040] The support with low ammonia storage can be a siliceous support. The siliceous support can comprise a silica or a zeolite with silica-to-alumina ratio of ≥100, preferably ≥200, more preferably ≥250, even more preferably ≥300, especially ≥400, more especially ≥500, and even more especially ≥750. In each aspect of the invention, the first SCR catalyst is preferably a Cu-SCR catalyst or a Fe-SCR catalyst, more a Cu-SCR catalyst. The second PGM is preferably Pt.
[0041] The ratio of the amount of first SCR catalyst to the amount of the second PGM (e.g., Pt) on a support with low ammonia storage in the blend can be in the range of 0.1 to 300:1, inclusive, preferably from 3:1 to 300:1, inclusive, more preferably 7:1 to 100:1, inclusive, even more preferably in the range of 10:1 to 50:1, inclusive, based on the weight of these components.
[0042] The term “active component loading” refers to the weight of the support of platinum+the weight of platinum+the weight of the first SCR catalyst in the blend. Platinum can be present in the catalyst in an active component loading from about 0.01 to about 0.3 wt. %, inclusive, preferably, from about 0.03-0.2 wt. %, inclusive, more preferably from about 0.04-0.17 wt. %, inclusive, most preferably, from about 0.05-0.15 wt. %, inclusive.
[0043] When platinum is present in the bottom layer of a bi-layer, platinum can be present at from about 0.1 wt. % to 2 wt. %, inclusive, preferably from 0.1 to 1 wt. %, inclusive, more preferably from 0.1 wt. % to 0.5 wt. %, inclusive, relative to the weight of the layer. Additional catalysts such as palladium (Pd), gold (Au) silver (Ag), ruthenium (Ru) or rhodium (Rh) can be present with Pt, preferably in the blend with Pt.
[0044] SCR Catalysts
[0045] In various embodiments, the compositions can comprise one, two or three SCR catalysts. The first SCR catalyst, which is always present in the compositions, can be present either (1) in a blend with Pt on a support with low ammonia storage or (2) in a top layer when the catalysts are present in a bilayer and Pt is present in a bottom layer. The first SCR catalyst can comprise a first transitional metal and a first molecular sieve. The first transitional metal can be Cu, Fe, Mn, or a combination thereof. The first SCR catalyst preferably a Cu-SCR catalyst or a Fe-SCR catalyst, more preferably a Cu-SCR catalyst. The Cu-SCR catalyst comprises copper and a molecular sieve. The Fe-SCR catalyst comprises iron and a molecular sieve. Molecular sieves are further described below. The molecular sieve can be an aluminosilicate, an aluminophosphate (AlPO), a silico-aluminophosphate (SAPO), or mixtures thereof. The copper or iron can be located within the framework of the molecular sieve and/or in extra-framework (exchangeable) sites within the molecular sieve.
[0046] The second and third SCR catalysts can be the same or different. The second and third SCR catalyst can be a base metal, an oxide of a base metal, a noble metal, a molecular sieve, a metal exchanged molecular sieve or a mixture thereof. The base metal can be selected from the group consisting of vanadium (V), molybdenum (Mo), tungsten (W), chromium (Cr), cerium (Ce), manganese (Mn), iron (Fe), cobalt (Co), nickel (Ni), and copper (Cu), and mixtures thereof. SCR compositions consisting of vanadium supported on a refractory metal oxide such as alumina, silica, zirconia, titania, ceria and combinations thereof are well known and widely used commercially in mobile applications. Typical compositions are described in U.S. Pat. Nos. 4,010,238 and 4,085,193, the entire contents of which are incorporated herein by reference. Compositions used commercially, especially in mobile applications, comprise TiO.sub.2 on to which WO3 and V.sub.2O.sub.5 have been dispersed at concentrations ranging from 5 to 20 wt. % and 0.5 to 6 wt. %, respectively. The noble metal can be platinum (Pt), palladium (Pd), gold (Au) silver (Ag), ruthenium (Ru) or rhodium (Rh), or a mixture thereof. The second SCR catalyst can comprise promoted Ce—Zr or MnO.sub.2. These catalysts may contain other inorganic materials such as SiO.sub.2 and ZrO.sub.2 acting as binders and promoters.
[0047] When the SCR catalyst is a base metal, the catalyst article can further comprise at least one base metal promoter. As used herein, a “promoter” is understood to mean a substance that when added into a catalyst, increases the activity of the catalyst. The base metal promoter can be in the form of a metal, an oxide of the metal, or a mixture thereof. The at least one base metal catalyst promoter may be selected from neodymium (Nd), barium (Ba), cerium (Ce), lanthanum (La), praseodymium (Pr), magnesium (Mg), calcium (Ca), manganese (Mn), zinc (Zn), niobium (Nb), zirconium (Zr), molybdenum (Mo), tin (Sn), tantalum (Ta), strontium (Sr) and oxides thereof. The at least one base metal catalyst promoter can preferably be MnO.sub.2, Mn.sub.2O.sub.3, Fe.sub.2O.sub.3, SnO.sub.2, CuO, CoO, CeO.sub.2 and mixtures thereof. The at least one base metal catalyst promoter may be added to the catalyst in the form of a salt in an aqueous solution, such as a nitrate or an acetate. The at least one base metal catalyst promoter and at least one base metal catalyst, e.g., copper, may be impregnated from an aqueous solution onto the oxide support material(s), may be added into a washcoat comprising the oxide support material(s), or may be impregnated into a support previously coated with the washcoat.
[0048] The SCR catalyst can comprise a molecular sieve or a metal exchanged molecular sieve. As is used herein “molecular sieve” is understood to mean a metastable material containing tiny pores of a precise and uniform size that may be used as an adsorbent for gases or liquids. The molecules which are small enough to pass through the pores are adsorbed while the larger molecules are not. The molecular sieve can be a zeolitic molecular sieve, a non-zeolitic molecular sieve, or a mixture thereof.
[0049] A zeolitic molecular sieve is a microporous aluminosilicate having any one of the framework structures listed in the Database of Zeolite Structures published by the International Zeolite Association (IZA). The framework structures include, but are not limited to those of the CHA, FAU, BEA, MFI, MOR types. Non-limiting examples of zeolites having these structures include chabazite, faujasite, zeolite Y, ultrastable zeolite Y, beta zeolite, mordenite, silicalite, zeolite X, and ZSM-5. Aluminosilicate zeolites can have a silica/alumina molar ratio (SAR) defined as SiO.sub.2/Al.sub.2O.sub.3) from at least about 5, preferably at least about 20, with useful ranges of from about 10 to 200.
[0050] Any of the SCR catalysts can comprise a small pore, a medium pore or a large pore molecular sieve, or a mixture thereof. A “small pore molecular sieve” is a molecular sieve containing a maximum ring size of 8 tetrahedral atoms. A “medium pore molecular sieve” is a molecular sieve containing a maximum ring size of 10 tetrahedral atoms. A “large pore molecular sieve” is a molecular sieve having a maximum ring size of 12 tetrahedral atoms. The second and/or third SCR catalysts can comprise a small pore molecular sieve selected from the group consisting of aluminosilicate molecular sieves, metal-substituted aluminosilicate molecular sieves, aluminophosphate (AlPO) molecular sieves, metal-substituted aluminophosphate (MeAlPO) molecular sieves, silico-aluminophosphate (SAPO) molecular sieves, and metal substituted silico-aluminophosphate (MeAPSO) molecular sieves, and mixtures thereof.
[0051] Any of the SCR catalysts can comprise a small pore molecular sieve selected from the group of Framework Types consisting of ACO, AEI, AEN, AFN, AFT, AFX, ANA, APC, APD, ATT, CDO, CHA, DDR, DFT, EAB, EDI, EPI, ERI, GIS, GOO, IHW, ITE, ITW, LEV, KFI, MER, MON, NSI, OWE, PAU, PHI, RHO, RTH, SAT, SAV, SFW, SIV, THO, TSC, UEI, UFI, VNI, YUG, and ZON, and mixtures and/or intergrowths thereof. Preferably the small pore molecular sieve is selected from the group of Framework Types consisting of CHA, LEV, AEI, AFX, ERI, SFW, KFI, DDR and ITE.
[0052] Any of the SCR catalysts can comprise a medium pore molecular sieve selected from the group of Framework Types consisting of AEL, AFO, AHT, BOF, BOZ, CGF, CGS, CHI, DAC, EUO, FER, HEU, IMF, ITH, ITR, JRY, JSR, JST, LAU, LOV, MEL, MFI, MFS, MRE, MTT, MVY, MWW, NAB, NAT, NES, OBW, PAR, PCR, PON, PUN, RRO, RSN, SFF, SFG, STF, STI, STT, STW, -SVR, SZR, TER, TON, TUN, UOS, VSV, WEI, and WEN, and mixtures and/or intergrowths thereof. Preferably, the medium pore molecular sieve selected from the group of Framework Types consisting of MFI, FER and STT.
[0053] Any of the SCR catalysts can comprise a large pore molecular sieve selected from the group of Framework Types consisting of AFI, AFR, AFS, AFY, ASV, ATO, ATS, BEA, BEC, BOG, BPH, BSV, CAN, CON, CZP, DFO, EMT, EON, EZT, FAU, GME, GON, IFR, ISV, ITG, IWR, IWS, IWV, IWW, JSR, LTF, LTL, MAZ, MEI, MOR, MOZ, MSE, MTW, NPO, OFF, OKO, OSI, RON, RWY, SAF, SAO, SBE, SBS, SBT, SEW, SFE, SFO, SFS, SFV, SOF, SOS, STO, SSF, SSY, USI, UWY, and VET, and mixtures and/or intergrowths thereof. Preferably, the large pore molecular sieve is selected from the group of Framework Types consisting of MOR, OFF and BEA.
[0054] The molecular sieves in the Cu-SCR and Fe-SCR catalysts are preferably selected from the group consisting of ACO, AEI, AEN, AFN, AFT, AFX, ANA, APC, APD, ATT, CDO, CHA, DDR, DFT, EAB, EDI, EPI, ERI, GIS, GOO, IHW, ITE, ITW, LEV, KFI, MER, MON, NSI, OWE, PAU, PHI, RHO, RTH, SAT, SAV, SIV, THO, TSC, UEI, UFI, VNI, YUG, ZON, BEA, MFI and FER and mixtures and/or intergrowths thereof. More preferably, the molecular sieves in the Cu-SCR and Fe-SCR are selected from the group consisting of AEI, AFX, CHA, DDR, ERI, ITE, KFI, LEV, SFW, BEA, MFI and FER, and mixtures and/or intergrowths thereof.
[0055] A metal exchanged molecular sieve can have at least one metal from one of the groups VB, VIB, VIIB, VIIIB, IB, or IIB of the periodic table deposited onto extra-framework sites on the external surface or within the channels, cavities, or cages of the molecular sieves. Metals may be in one of several forms, including, but not limited to, zero valent metal atoms or clusters, isolated cations, mononuclear or polynuclear oxycations, or as extended metal oxides. Preferably, the metals can be iron, copper, and mixtures or combinations thereof.
[0056] The metal can be combined with the zeolite using a mixture or a solution of the metal precursor in a suitable solvent. The term “metal precursor” means any compound or complex that can be dispersed on the zeolite to give a catalytically-active metal component. Preferably the solvent is water due to both economics and environmental aspects of using other solvents. When copper, a preferred metal is used, suitable complexes or compounds include, but are not limited to, anhydrous and hydrated copper sulfate, copper nitrate, copper acetate, copper acetylacetonate, copper oxide, copper hydroxide, and salts of copper ammines (e.g. [Cu(NH.sub.3).sub.4].sup.2+). This invention is not restricted to metal precursors of a particular type, composition, or purity. The molecular sieve can be added to the solution of the metal component to form a suspension, which is then allowed to react so that the metal component is distributed on the zeolite. The metal can be distributed in the pore channels as well as on the outer surface of the molecular sieve. The metal can be distributed in ionic form or as a metal oxide. For example, copper may be distributed as copper (II) ions, copper (I) ions, or as copper oxide. The molecular sieve containing the metal can be separated from the liquid phase of the suspension, washed, and dried. The resulting metal-containing molecular sieve can then be calcined to fix the metal in the molecular sieve. Preferably, the second and third catalysts comprise a Cu-SCR catalyst comprising copper and a molecular sieve, an Fe-SCR catalyst comprising iron and a molecular sieve, a vanadium based catalyst, a promoted Ce—Zr or a promoted MnO.sub.2.
[0057] A metal exchanged molecular sieve can contain in the range of about 0.10% and about 10% by weight of a group VB, VIB, VIIB, VIIIB, IB, or JIB metal located on extra framework sites on the external surface or within the channels, cavities, or cages of the molecular sieve. Preferably, the extra framework metal can be present in an amount of in the range of about 0.2% and about 5% by weight.
[0058] The metal exchanged molecular sieve can be a copper (Cu) or iron (Fe) supported molecular sieve having from about 0.1 to about 20.0 wt. % copper or iron of the total weight of the catalyst. More preferably copper or iron is present from about 0.5 wt. % to about 15 wt. % of the total weight of the catalyst. Most preferably copper or iron is present from about 1 wt. % to about 9 wt. % of the total weight of the catalyst.
[0059] The compositions can comprise one or more additional metals combined with the second PGM. These one or more additional metals can be gold (Au), iridium (Jr), palladium (Pd), rhodium (Rh), ruthenium (Ru) or silver (Ag). These metals can be present at from about 0.1 wt. % to about 20 wt. %, inclusive, preferably from about 0.3 wt. % to about 10 wt. %, inclusive.
[0060] The second catalytic region can extend for 30 to 99 percent of the axial length L; preferably, 40 to 95 percent or 45 to 90 percent of the axial length L; more preferably, 50 to 85 percent of the axial length L; and even more preferably, 65 to 80 percent of the axial length L.
[0061] The second catalytic region can cover at least 10%, 20%, 30%, 40%, or 50% of the first catalytic region. In other embodiments, the second catalytic region can cover at least 60%, 70%, 80%, 90%, or 100% of the first catalytic region.
[0062] The first catalytic region can begin at the inlet end or at the outlet end. And the second catalytic region can begin at the inlet end or at the outlet end. In some embodiments, the first and the second catalytic regions begin at the different ends. In other embodiments, the first and the second catalytic regions can begin at the same end (i.e., at the inlet end or at the outlet end).
[0063] The ratio of the first PGM component to the second PGM component can be from 5:1 to 1:5; preferably, 4:1 to 1:4; more preferably, 3:1 to 1:3; most preferably, 3:2 to 2:3.
Third Catalytic Region
[0064] In some embodiments, the catalytic article of the present invention can further comprise a third catalytic region. The third catalytic region can be a second SCR catalyst. The second SCR catalyst can be the same as the first SCR catalyst as described above. Alternatively, the second SCR catalyst can be different from the first SCR catalyst.
[0065] The third catalytic region may further comprise another support. Examples of the another support materials include refractory metal oxides such as alumina, silica, zirconia, titania, ceria, and physical mixtures or composites thereof, with alumina being particularly preferred.
[0066] The third catalytic region can extend for 20 to 100 percent or 30 to 95 percent of the axial length L; preferably, 40 to 90 percent of the axial length L; more preferably, 50 to 80 percent of the axial length L.
[0067] In certain embodiments, the third catalytic region does not cover any of the first catalytic region. In other embodiments, the third catalytic region can cover at least 10%, 20%, 30%, 40%, or 50%, 60%, 70%, 80%, 90%, or 100% of the first catalytic region.
[0068] The first, second, third catalytic regions can begin at the inlet end or at the outlet end. In some embodiments, the first, the second, and/or the third catalytic regions can begin at the different ends. In other embodiments, the first, the second, and/or the third catalytic regions can begin at the same end (i.e., at the inlet end or at the outlet end).
Fourth Catalytic Region
[0069] In some embodiments, the catalytic article of the present invention can further comprise a fourth catalytic region. The fourth catalytic region can be a third SCR catalyst. The third SCR catalyst can be the same as or different from the first and/or the second SCR catalyst as described above.
[0070] The fourth catalytic region can extend for 20 to 100 percent or 30 to 99 percent of the axial length L; preferably, 40 to 95 percent of the axial length L; more preferably, 45 to 85 percent of the axial length L; and even more preferably, 50 to 80 percent of the axial length L.
[0071] In certain embodiments, the fourth catalytic region does not cover any of the first catalytic region. In other embodiments, the fourth catalytic region can cover at least 10%, 20%, 30%, 40%, or 50%, 60%, 70%, 80%, 90%, or 100% of the first catalytic region.
[0072] The first, second, third, or fourth catalytic regions can begin at the inlet end or at the outlet end. In some embodiments, the first, the second, the third and/or the fourth catalytic regions can begin at the different ends. In other embodiments, the first, the second, the third and/or the fourth catalytic regions can begin at the same end (i.e., at the inlet end or at the outlet end).
[0073] In one aspect of the invention, various configurations of catalytic articles comprising the first, second, third, and/or fourth catalytic regions can be prepared as below.
[0074]
[0075] In the first configuration, preferably, the first, second, and third catalytic region, each independently can extend for 40 to 95 percent or 45 to 90 percent of the axial length L; more preferably, 50 to 85 percent of the axial length L; and even more preferably, 65 to 80 percent of the axial length L. In some embodiments, the overlap between the first and second catalytic regions can be at least 5%, 10%, or 15% of the axial length L. In certain embodiments, the overlap between the second and third catalytic regions can be at least 5%, 10%, or 15% of the axial length L.
[0076]
[0077]
[0078]
[0079]
[0080]
[0081]
[0082]
[0083]
[0084]
[0085] The substrate for the catalytic article of the present invention may be any material typically used for preparing automotive catalysts that comprises a flow-through or filter structure, such as a honeycomb structure, an extruded support, a metallic substrate, or a SCRF. Preferably the substrate has a plurality of fine, parallel gas flow passages extending from an inlet to an outlet face of the substrate, such that passages are open to fluid flow. Such monolithic carriers may contain up to about 700 or more flow passages (or “cells”) per square inch of cross section, although far fewer may be used. For example, the carrier may have from about 7 to 600, more usually from about 100 to 400, cells per square inch (“cpsi”). The passages, which are essentially straight paths from their fluid inlet to their fluid outlet, are defined by walls onto which the catalyst (e.g., ASC or SCR) is coated as a “washcoat” so that the gases flowing through the passages contact the catalytic material. The flow passages of the monolithic substrate are thin-walled channels which can be of any suitable cross-sectional shape such as trapezoidal, rectangular, square, triangular, sinusoidal, hexagonal, oval, circular, etc. The invention is not limited to a particular substrate type, material, or geometry.
[0086] Ceramic substrates may be made of any suitable refractory material, such as cordierite, cordierite-α alumina, α-alumina, silicon carbide, silicon nitride, zirconia, mullite, spodumene, alumina-silica magnesia, zirconium silicate, sillimanite, magnesium silicates, zircon, petalite, aluminosilicates and mixtures thereof.
[0087] Wall flow substrates may also be formed of ceramic fiber composite materials, such as those formed from cordierite and silicon carbide. Such materials are able to withstand the environment, particularly high temperatures, encountered in treating the exhaust streams.
[0088] The substrates can be a high porosity substrate. The term “high porosity substrate” refers to a substrate having a porosity of between about 40% and about 80%. The high porosity substrate can have a porosity preferably of at least about 45%, more preferably of at least about 50%. The high porosity substrate can have a porosity preferably of less than about 75%, more preferably of less than about 70%. The term porosity, as used herein, refers to the total porosity, preferably as measured with mercury porosimetry.
[0089] Preferably, the substrate can be cordierite, a high porosity cordierite, a metallic substrate, an extruded SCR, a wall flow filter, a filter or an SCRF.
[0090] In another aspect, the invention relates to exhaust systems can comprise a catalytic article have one of the ten configurations described above and a means for forming NH.sub.3 in the exhaust gas, where NH.sub.3 is formed the exhaust gas before the exhaust gas comes in contact with the catalyst.
[0091] An exhaust system can comprise (1) a catalytic article described above and (2) a means for forming NH.sub.3 in the exhaust gas. where NH.sub.3 is formed the exhaust gas before the exhaust gas comes in contact with the catalytic article. An exhaust system can further comprise a DOC, a DPF, at least one additional SCR, at least one additional ASC, or a combination thereof.
[0092] In some embodiments, the systems can have arrangements shown as below:
[0093] (1) SCR+ASC+DPF+catalytic article of the present invention
[0094] (2) SCR+catalytic article of the present invention+DPF+SCR ASC
[0095] (3) DOC/PNA or LNT>DPF>SCR>catalytic article of the present invention
[0096] In yet another aspect, the invention relates to methods of treating exhaust gas from an internal combustion engine by contacting the exhaust gas with he catalytic articles as described in the first aspect.
[0097] In still another aspect, the invention relates to methods of reducing N.sub.2O formation from NH.sub.3 in an exhaust gas, the method comprising contacting an exhaust gas comprising ammonia with he catalytic articles as described in the first aspect.
[0098] The following examples merely illustrate the invention; the skilled person will recognize many variations that are within the spirit of the invention and scope of the claims.
EXAMPLES
Comparative Catalyst 1
[0099] A bottom layer comprising a washcoat of Pt on alumina was applied to the front of a ceramic substrate. The washcoat was pulled down the substrate using a vacuum to a distance of about 50% of the length of the substrate using a vacuum. The article was dried and process repeated on rear of brick in order that entire brick was coated with bottom layer with small region of overlap. The brick was calcined at about 500° C. for about 1 hour. The loading of Pt, and alumina on the article was 2 g/ft.sup.3 and 0.35 g/in.sup.3 respectively.
[0100] A top layer comprising a second washcoat comprising a Cu-AEI was applied to the substrate coated with the bottom layer, and then the washcoat was pulled down the substrate to a distance of about 50% of the length of the substrate using a vacuum. The article was dried and process repeated on rear of brick in order that entire brick was coated with top layer with small region of overlap of top layer. The article was dried and calcined at about 500° C. for about 1 hour. The loading of Cu-AEI in the top layer was 1.8 g/in.sup.3. The final article is Comparative Catalyst 1.
Catalyst 2
[0101] A layer comprising a washcoat of Pt on alumina was applied to the rear of a ceramic substrate. The washcoat was pulled down the substrate using a vacuum to a distance of about 70% of the length of the substrate using a vacuum. The article was dried and calcined at about 500° C. for about 1 hour. The loading of Pt, and alumina on the article was 1 g/ft.sup.3 and 0.35 g/in.sup.3 respectively.
[0102] A second layer comprising a washcoat comprising a blend of 3 wt. % Pt on a ZSM-5 (MFI framework with SAR=2100) and a Cu-AEI was applied to the front of a ceramic substrate, then the washcoat was pulled down the substrate to a distance of about 70% of the length of the substrate using a vacuum. The article was dried. The loading of Pt, the high SAR zeolite and the Cu-AEI on the article was 1 g/ft.sup.3, 0.02 g/in.sup.3, and 1.05 g/in.sup.3, respectively.
[0103] A top layer comprising a second washcoat comprising a Cu-AEI was applied to the substrate coated with the two layers described, and then the washcoat was pulled down the substrate to a distance of about 70% of the length of the substrate using a vacuum. The article was dried and calcined at about 500° C. for about 1 hour. The loading of Cu-AEI in the top layer was 1.05 g/in.sup.3. The final article is Catalyst 2.
[0104] The configuration of Catalyst 2 is shown in
Comparative Catalyst 3
[0105] Comparative Catalyst 3 was made in the same manner as Comparative Catalyst 1, except for Pt loading. The Pt loading for Comparative Catalyst 3 in bottom layer was 3 g/ft.sup.3.
Catalyst 4
[0106] Catalyst 4 was made in the same manner as Catalyst 2, except for Pt loading. The Pt loading for the bottom layer (Pt on alumina) was 1.5 g/ft.sup.3 and the Pt loading for the second layer was 1.5 g/ft.sup.3.
Example 1
[0107] Table 1 compares the coldflow backpressure of Comparative Catalyst 1 and Catalyst 2, measured at 1400 m.sup.3/hr when prepared on a 10.5×3″ 400/4 ceramic brick. As shown in Table 1, Catalyst 2 of showed a ˜16% reduction in backpressure over Comparative Catalyst 1.
TABLE-US-00001 TABLE 1 Coldflow Backpressure Comparison Backpressure Percentage (mbar) Increase (%) Bare substrate 2.8 — Comparative 6.4 129% Catalyst 1 Catalyst 2 5.8 108%
Reference System
[0108] DOC-CSF-SCR only
Comparative System 1
[0109] DOC-CSF-SCR followed by Comparative Catalyst 1
System 2
[0110] DOC-CSF-SCR followed by Catalyst 2
Example 2
[0111] Example 2 compares the tailpipe emissions measured for Reference System, Comparative System 1, and System 2 on an engine test bed during a World Harmonised Transient Cycle (WHTC) when the system was dosed at an Ammonia to NO.sub.x ratio of 1.2.
[0112] SCR and ASC catalysis were tested fresh and after simulated lifetime ageing of 580° C./100 hrs/10% water. The same DOC and CSF were used in both Fresh and Aged testing.
[0113] As shown in Table 2, System 2 containing Catalyst 2 gave lower N.sub.2O (˜60% reduction) and lower NO.sub.x slip (˜5% reduction), when compared with Comparative System 1.
TABLE-US-00002 TABLE 2 WHTC cycle tailpipe NO.sub.x and N.sub.2O slip and average tailpipe NH.sub.3 slip Summary Reference Comparative Reference Comparative System System 1 System 2 System System 1 System 2 (Fresh) (Fresh) (Fresh) (Aged) (Aged) (Aged) Tailpipe NO.sub.x 1.14 0.64 0.61 1.15 0.62 0.59 (g/kWh) Tailpipe N2O slip — 0.20 0.08 — 0.20 0.09 (g/kWh) Tailpipe NH.sub.3 98.0 2.1 2.9 124.6 2.5 5.9 slip (ppm)
Example 3
[0114] Example 3 compares the N.sub.2O tailpipe emissions measured for Comparative System 1 and System 2 on an engine test bed during a WHTC cycle when the system was dosed at an Ammonia to NO.sub.x ratio of 1.2. Catalysis were tested after hydrothermal ageing at 580° C./100 hrs/10% water to simulate lifetime ageing.
[0115] As shown in
Example 4
[0116] Example 4 compares the NH.sub.3 oxidation and selective catalytic reduction (“SCR”) with associated N.sub.2O make of Comparative Catalyst 1, Catalyst 2, Comparative Catalyst 3, and Catalyst 4 when tested in SCAT under gas conditions of either 500 ppm NH.sub.3 or 500 ppm NH.sub.3/500 ppm NO (ANR=1.0) at space velocity of 180 k. Catalysts were tested both fresh and after hydrothermal ageing at 550° C./100 hrs/10% Water.
[0117]
[0118]
[0119]
[0120]
[0121] As shown in
Example 5
[0122] Comparative Catalyst 1 and Catalyst 2 were subjected to extended low temperature engine ageing in sulfur doped fuel to simulate in-field sulfation. Following this, Comparative Catalyst 1 and Catalyst 2 were tested in Comparative System 1 and System 2 respectively. Each system was subjected to 4 WHTCs, 30 minutes at increasing temperatures 350° C.-500° C. and then repeated 4×WHTCs. Each set of 4 WHTCs also included a steady state test point at 250° C./ANR=1.2. The WHTC cycle act as a performance check, whilst running engine at increasing temperature simulates engine management controls to disulfate the catalyst. Clean hydrothermally oven aged samples were also tested. To understand pollutants entering Comparative Catalyst 1 and Catalyst 2, Reference system (DOC-CSF and V-SCR) was tested over the same 4 WHTC regime and same components used in all cases.
[0123] As shown in
TABLE-US-00003 TABLE 3 Post Sulphation NO.sub.x Conversion (%) Summary* Post Post Post Post Oven Post Sulphur + Sulphur + Sulphur + Sulphur + Aged Sulphur 350° C. 400° C. 450° C. 500° C. Comparative 96.5 83.9 87.7 91.3 93.5 Error System 1 System 2 95.6 81.6 89.7 95.6 95.9 96.5 *during steady state at 250° C./Ammonia to NO.sub.x Ratio (ANR) = 1.2
TABLE-US-00004 TABLE 4 Post Sulphation Average NH.sub.3 Slip (ppm) Summary* Post Post Post Post Oven Post Sulphur + Sulphur + Sulphur + Sulphur + Aged Sulphur 350° C. 400° C. 450° C. 500° C. Comparative 50.4 62.9 57.3 57.9 52.4 46.6 System 1 System 2 58.5 64.3 64.6 62.3 57.2 55.0 *during steady state at 250° C./Ammonia to NO.sub.x Ratio (ANR) = 1.2
Example 6
[0124] Example 6 compares the NH.sub.3 oxidation with associated N.sub.2O make of Comparative Catalyst 3 and Catalyst 4 when tested in SCAT under gas conditions of 500 ppm NH.sub.3 at space velocity of 180 k. Catalysts were tested both fresh and after engine ageing. The Catalysts were aged in a SCR/passive diesel particulate filter/V-SCR/ASC configuration downstream of a V-SCR. 1×3″ cores of Comparative Catalyst 3 and Catalyst 4 were set inside a large test brick. Real driving conditions were represented by transient cycling on a test bench, also considering adjusted load points to mimic accelerated thermal and chemical ageing (i.e. steady state conditions added to the transient cycling). The ageing conditions included transient cycling within a temperature range of from 150° C. to 470° C., wherein the length of each complete cycle, run consecutively, was approximately 45 minutes. The total length of the engine ageing was 1000 hours.
[0125]
[0126] As shown in
[0127] The preceding examples are intended only as illustrations; the following claims define the scope of the invention.