Porous polyamide hollow fiber membrane having very small pore diameter, and method for producing same

Abstract

[Problem] The purpose of the present invention is to provide a polyamide hollow fiber membrane having such properties that the transmission of fine particles through the membrane can be prevented effectively, the membrane has an excellent water transmissibility, the entire surface of the membrane has excellent hydrophilicity, and impurities such as metal elements are rarely eluted through the membrane. [Solution] A polyamide hollow fiber membrane produced by a TIPS method under specific production conditions has the following characteristic properties: (1) the contact angle of water on the surface of the membrane is 80? or less; (2) the external pressure water transmissibility of the membrane is 50 L/(m.sup.2.Math.atm.Math.h) or more; and (3) the 50 nm-particles blocking ratio of the membrane is 90% or more.

Claims

1. A polyamide hollow fiber membrane comprising the following properties (1) to (4): (1) the polyamide hollow fiber membrane comprises a polyamide resin having methylene and amide groups at a molar ratio of CH.sub.2:NHCO=4:1 to 10:1; (2) a contact angle between water and a surface of the polyamide hollow fiber membrane is not more than 80?; (3) a water permeability under external pressure is not less than 50 L/(m.sup.2.Math.atm.Math.h); and (4) a 10 nm particle blocking rate is not less than 90%.

2. The polyamide hollow fiber membrane according to claim 1, wherein the polyamide resin is at least one selected from the group consisting of polyamide 6, polyamide 66, polyamide 46, polyamide 610, polyamide 11, and polyamide MXD6.

3. The polyamide hollow fiber membrane according to claim 1, which has a 5 nm particle blocking rate of not less than 90%.

4. The polyamide hollow fiber membrane of claim 1, which has a water permeability under external pressure of not less than 150 L/(m.sup.2.Math.atm.Math.h).

5. The polyamide hollow fiber membrane of claim 1, which has a water permeability under external pressure of not less than 250 L/(m.sup.2.Math.atm.Math.h).

6. The polyamide hollow fiber membrane of claim 1, wherein a metal content for each metal element is not more than 10 ppm.

7. A hollow fiber membrane module comprising: a module case; and the polyamide hollow fiber membrane described in claim 1 stored in the module case.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 schematically illustrates an apparatus to measure the water permeability under external pressure of a polyamide hollow fiber membrane of the present invention.

(2) FIG. 2 illustrates the structure of a cross section of a double-pipe nozzle for hollow fiber production (spinneret) for production of the hollow fiber membrane of the present invention.

(3) FIG. 3 is an illustration of an apparatus which shows one embodiment of a method for producing a polyamide hollow fiber membrane of the present invention.

(4) FIG. 4 shows photographs of a polyamide hollow fiber membrane obtained in Example 1, which are taken under a scanning electron microscope. A is a photograph of a cross section, B is an enlarged photograph of the cross section, C is a photograph of the inside surface, and D is a photograph of the outside surface.

(5) FIG. 5A is a photograph of the appearance of a crossflow hollow fiber membrane module obtained in Example 15, and FIG. 5B is a photograph of the appearance of a dead-end hollow fiber membrane module obtained in Example 16.

EMBODIMENTS OF THE INVENTION

(6) 1. Polyamide Hollow Fiber Membrane

(7) A polyamide hollow fiber membrane of the present invention is characterized in that (1) the polyamide hollow fiber membrane contains a polyamide resin having methylene and amide groups at a molar ratio of CH.sub.2:NHCO=4:1 to 10:1, (2) the contact angle between water and the surface of the polyamide hollow fiber membrane is not more than 80?, (3) the water permeability under external pressure is not less than 50 L/(m.sup.2.Math.atm.Math.h), and (4) the 50 nm particle blocking rate is not less than 90%. The following description discusses the polyamide hollow fiber membrane of the present invention in detail.

(8) A polyamide hollow fiber membrane of the present invention is constituted by a polyamide resin having methylene and amide groups at a molar ratio of CH.sub.2:NHCO=4:1 to 10:1. The use of such a polyamide resin makes it possible to form a highly hydrophilic hollow fiber membrane that has a desired micropore size. The molar ratio of methylene groups to amide groups in the polyamide resin is, in view of a further increase in hydrophilicity and more effective formation of pores of small sizes, for example, preferably CH.sub.2:NHCO=4:1 to 7:1, more preferably CH.sub.2:NHCO=4:1 to 5:1. It should be noted that, in the present invention, the CH groups and C? groups of polyamides containing aromatic rings are regarded as CH.sub.2 groups when the molar ratio of methylene groups is calculated.

(9) Specific examples of the polyamide resin for use in the present invention include polyamide 6, polyamide 66, polyamide 46, polyamide 610, polyamide 11, polyamide MXD6, and the like. Among these polyamide resins, preferred are polyamide 6, polyamide 46, polyamide 610, and polyamide MXD6. In the present invention, the polyamide hollow fiber membrane may be constituted by a single polyamide resin or may be constituted by a blended polymer of two or more polyamide resins.

(10) The polyamide resin for use in the present invention may or may not be crosslinked, provided that the polyamide resin can be formed into the shape of a fiber. In view of cost reduction, a polyamide resin which is not crosslinked is preferable.

(11) The polyamide resin for use in the present invention is preferably synthesized without using a metal-containing polymerization catalyst. Furthermore, it is preferable that the polyamide resin does not contain additives such as an antioxidant, a lubricant, a hydrolysis inhibitor, a capping agent, a plasticizer, or a polymerization initiator. The use of such a polyamide resin makes it possible to dramatically reduce the elution of impurities when the polyamide hollow fiber membrane of the present invention is used as a filtration membrane. In view of this, suitable examples of the polyamide resin for use in the present invention include polyamide 6, polyamide 11, and the like which are obtained by ring-opening polymerization using water as a polymerization initiator.

(12) The relative viscosity of the polyamide resin is not particularly limited, including, for example 2.0 to 6.2, preferably 3.0 to 5.5. A polyamide resin having such a relative viscosity is readily formed into a hollow fiber membrane and its phase separation is easy to control. In this specification, the relative viscosity is a value obtained by: dissolving a polyamide resin in 96% sulfuric acid at a concentration of 1 g/dl; and measuring the relative viscosity at 25? C. with the use of an Ubbelohde viscometer.

(13) The surface of the polyamide hollow fiber membrane of the present invention is highly hydrophilic. The contact angle between water and the surface of the membrane is not more than 80?. The contact angle between water and the surface of the membrane is, for example, preferably not more than 70?, more preferably 40? to 65?. In this specification, the contact angle to water is a value obtained by: bringing a 1.8 ?l droplet of pure water into gentle contact with the surface of the membrane; and measuring the angle between the surface of the membrane and the tangent to the droplet on the surface of the membrane at an end of the droplet with the use of a contact angle meter by the ?/2 method. That is, it can be said that the smaller this value is, the higher the hydrophilicity is expected.

(14) The polyamide hollow fiber membrane of the present invention has such a property that the contact angle between the surface and water is not more than 80?, and therefore is capable of suppressing the adsorption of hydrophobic substances and preventing a reduction in its filtering performance within a short period of time. Furthermore, since the polyamide hollow fiber membrane has the above-described contact angle, even in the case where a dry polyamide hollow fiber membrane of the present invention is used for filtration of water, it is possible to suppress water from being repelled by surface tension when water is to pass through the membrane. Moreover, since the polyamide hollow fiber membrane of the present invention has a contact angle of this range, it is possible to specifically adsorb and remove hydrophilic impurities during the filtration in an organic solvent system.

(15) Furthermore, the polyamide hollow fiber membrane of the present invention has, as one permeation property, a water permeability under external pressure of not less than 50 L/(m.sup.2.Math.atm.Math.h) and not more than 2500 L/(m.sup.2.Math.atm.Math.h). The water permeability under external pressure varies also depending on pore size. However, in the case of a hollow fiber membrane capable of blocking 90% or more of 5 nm particles, the water permeability under external pressure is preferably not less than 50 L/(m.sup.2.Math.atm.Math.h), more preferably not less than 100 L/(m.sup.2.Math.atm.Math.h). In the case of a hollow fiber membrane capable of passing 10% or more of 5 nm particles but blocking 90% or more of 10 nm particles, the water permeability under external pressure is preferably not less than 150 L/(m.sup.2.Math.atm.Math.h), more preferably not less than 200 L/(m.sup.2.Math.atm.Math.h). In the case of a hollow fiber membrane capable of passing 10% or more of 10 nm particles but blocking 90% or more of 20 nm particles, the water permeability under external pressure is preferably not less than 250 L/(m.sup.2.Math.atm.Math.h), more preferably not less than 350 L/(m.sup.2.Math.atm.Math.h). In the case of a hollow fiber membrane capable of passing 10% or more of 20 nm particles but blocking 90% or more of 50 nm particles, the water permeability under external pressure is preferably not less than 500 L/(m.sup.2.Math.atm.Math.h), more preferably not less than 1000 L/(m.sup.2.Math.atm.Math.h). Since the polyamide hollow fiber membrane of the present invention is highly water permeable under external pressure like above, it is possible to increase the flow rate of a liquid to be treated and thus possible to increase filtration efficiency.

(16) In this specification, the water permeability under external pressure of the polyamide hollow fiber membrane is a value measured by external pressure filtration. Specifically, the water permeability under external pressure is a value obtained by: cutting the polyamide hollow fiber membrane into a length of 9 to 12 cm; inserting, into the hollow portion at both ends, injection needles having a diameter that fits the inside diameter; sealing one of the injection needles with a cap 20; connecting the other of the injection needles with an exit opening 21; setting this in an apparatus as illustrated in FIG. 1; and thereafter passing pure water with a liquid pump 14 for a predetermined period (time) while keeping the pressure at a constant pressure of 0.05 MPa by adjusting a valve of an outlet valve 18; measuring, as a permeate flow rate, the amount (L) of water that had passed through the membrane and puddled in a receiving tray 19; and finding the water permeability under external pressure through the following equation. It should be noted that the inlet pressure is measured with an inlet pressure meter 15 illustrated in FIG. 3, and the outlet pressure is measured with an outlet pressure meter 17 illustrated in FIG. 3.
Water permeability under external pressure=Permeate flow rate (L)/[Outside diameter (m)?3.14?Length (m)?{(Inlet pressure (atm)+Outlet pressure (atm))/2}?Time (h)].

(17) Furthermore, the polyamide hollow fiber membrane of the present invention has, as a filtration property, a 50 nm particle blocking rate of not less than 90%. The 50 nm particle blocking rate of the polyamide hollow fiber membrane of the present invention is, for example, preferably not less than 95%, more preferably not less than 99%.

(18) As a suitable example of the filtration property of the polyamide hollow fiber membrane of the present invention, the 20 nm particle blocking rate is not less than 90%, preferably not less than 95%, even more preferably not less than 99%. Furthermore, as a more suitable example of the filtration property of the polyamide hollow fiber membrane of the present invention, the 10 nm particle blocking rate is not less than 90%, preferably not less than 95%, even more preferably not less than 99%. In particular, as an even more suitable example of the filtration property of the polyamide hollow fiber membrane of the present invention, the 10 nm particle blocking rate is not less than 90%, preferably not less than 95%, even more preferably not less than 99%. As described above, the polyamide hollow fiber membrane of the present invention has a porous structure that can separate very small particles, and thus is capable of removing fine particles.

(19) In this specification, the rate of blocking particles of each size is calculated from the percentage of colloidal gold particles removed in the case where a filtration test is performed using colloidal gold particles having a certain mean particle size. Since colloidal gold particles have a very narrow distribution of particle size, the filtration test using colloidal gold accurately reflects the particle blocking rate of the hollow fiber membrane. Specifically, the filtration test using colloidal gold particles is performed by: adding 2 mmol/l tris(hydroxymethyl)aminomethane to an aqueous dispersion containing 10 ppm colloidal gold having a certain mean particle size; performing dead-end filtration at constant pressure under the conditions in which the filtration pressure is 0.3 MPa and the filtration temperature is 25? C.; taking a portion of filtrate every time the amount of filtrate increases by 0.005 (m.sup.3/m.sup.2); measuring the absorbance of the second portion at a wavelength of 524 nm; and calculating the rate of blocking particles of each size through the following equation.
Particle blocking rate (%)={(Absorbance of liquid to be filtered?Absorbance of filtrate)/Absorbance of liquid to be filtered}?100

(20) The breaking strength of the polyamide hollow fiber membrane of the present invention is not particularly limited, and is for example 5 to 30 MPa, preferably 7 to 25 MPa, more preferably 9 to 20 MPa. The elongation at break of the polyamide hollow fiber membrane of the present invention is also not particularly limited, and is for example 50 to 300%, preferably 80 to 250%, more preferably 100 to 230%. The tensile modulus of the polyamide hollow fiber membrane of the present invention is also not particularly limited, and is for example 50 to 250 MPa, preferably 50 to 200 MPa, more preferably 70 to 170 MPa. In this specification, breaking strength, elongation at break, and tensile modulus are values measured in accordance with JIS L-1013 under the conditions in which the length of a sample is 50 mm, tension speed is 50 mm/min, and the number of measured samples is n=5.

(21) The inside diameter and outside diameter of the polyamide hollow fiber membrane of the present invention are not particularly limited, and are adjusted appropriately depending on the purpose and the like. The inside diameter is, for example, 800 to 100 ?m, preferably 600 to 150 ?m, more preferably 450 to 200 ?m. The outside diameter is, for example, 1800 to 250 ?m, preferably 1500 to 300 ?m, more preferably 1000 to 400 ?m.

(22) The metal content for each metal element of the polyamide hollow fiber membrane of the present invention is, for example, not more than 10 ppm for each metal element, preferably not more than 5 ppm for each metal element, more preferably not more than 1 ppm for each metal element. Since the amount of impurities such as metal elements in the polyamide hollow fiber membrane of the present invention is small as described above, the elution of impurities is very small when the polyamide hollow fiber membrane is used as a filtration membrane. Examples of metal here include: Ag, Al, As, Au, B, Ba, Be, Bi, Ca, Cd, Ce, Co, Cr, Cu, Dy, Er, Eu, Fe, Ga, Gd, Ge, Hf, Hg, Ho, In, Ir, K, La, Li, Lu, Mg, Mn, Mo, Na, Nb, Nd, Ni, P, Pb, Pd, Pr, Pt, Re, Rh, Ru, Sb, Sc, Se, Si, Sm, Sn, Sr, Ta, Tb, Te, Ti, Tl, Tm, V, W, Y, Yb, Zn, and Zr.

(23) The metal content of the polyamide hollow fiber membrane of the present invention is a value obtained by: dissolving a dry sample of a hollow fiber membrane in a solvent that dissolves polyamide at room temperature such as nitric acid, sulfuric acid, formic acid, or trichloroacetic acid; and measuring the solution by inductively coupled plasma (ICP)-atomic emission spectroscopy.

(24) 2. Method for Producing Polyamide Hollow Fiber Membrane

(25) A polyamide hollow fiber membrane of the present invention can be produced by employing certain production conditions using TIPS. Specifically, the polyamide hollow fiber membrane of the present invention is produced through the following First to Third Steps.

(26) First Step: Prepare a liquid for membrane formation by dissolving, at a concentration of 21 to 35 mass %, a polyamide resin having methylene and amide groups at a molar ratio of CH.sub.2:NHCO=4:1 to 10:1 in an organic solvent that has a boiling point of 150? C. or higher and is not miscible with the polyamide resin at temperatures lower than 100? C.

(27) Second Step: Form a hollow fiber membrane with the use of a double-pipe nozzle for hollow fiber production having a double-pipe structure, by: discharging the liquid for membrane formation from the outer annular nozzle and discharging an inner fluid from the inner nozzle; and immersing the discharged product in a coagulation bath containing a polyhydric alcohol or a mixture of a polyhydric alcohol and water.

(28) Third Step: Remove the organic solvent from the hollow fiber membrane formed in Second Step.

(29) The following description discusses each step of the method for producing a polyamide hollow fiber membrane of the present invention in detail.

(30) First Step

(31) In the First Step, a liquid for membrane formation is prepared by dissolving, at a concentration of 21 to 35 mass %, a polyamide resin having methylene and amide groups at a molar ratio of CH.sub.2:NHCO=4:1 to 10:1 in an organic solvent that has a boiling point of 150? C. or higher and is not miscible with the polyamide resin at temperatures lower than 100? C.

(32) Examples of the organic solvent that has a boiling point of 150? C. or higher and is not miscible with the polyamide resin at temperatures lower than 100? C. include aprotic polar solvents, glycerol esters, glycols, organic acids and organic esters, higher alcohols, glycols, and the like. Specific examples of aprotic polar solvents include sulfolane, dimethylsulfone, dimethylsulfoxide, ?-butyrolactone, ?-valerolactone, ?-caprolactone, N,N-dimethylformamide, N,N-dimethylacetamide, N-methyl-2-pyrrolidone, ethylene carbonate, propylene carbonate, and the like. Specific examples of glycerol esters include diethylene glycol dimethyl ether, diethylene glycol diethyl ether, triethylene glycol dimethyl ether, diethylene glycol dibutyl ether, tetraethylene glycol dimethyl ether, and the like. Specific examples of glycols include glycerin, ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, propylene glycol, butylene glycol, hexylene glycol, polyethylene glycol (molecular weight 100 to 600), 1,3-butanediol, and the like. Specific examples of organic acids and organic esters include dimethyl phthalate, diethyl phthalate, diisopropyl phthalate, dibutyl phthalate, butyl benzyl phthalate, methyl salicylate, oleic acid, palmitic acid, stearic acid, lauric acid, and the like. In view of obtaining a high-strength, homogeneous polyamide hollow fiber membrane having a very small pore size, preferred are aprotic polar solvents, more preferred are sulfolane, dimethylsulfone, ?-butyrolactone, ?-valerolactone, ?-caprolactone, ethylene carbonate, and propylene carbonate, particularly preferred are sulfolane and dimethylsulfone. These organic solvents may be used individually or two or more of them may be used in combination.

(33) Of the organic solvents listed above, a mixture of sulfolane and dimethylsulfone is particularly useful for the formation of pores having a very small size, and is suitable for use in the present invention. In the case where a mixture of sulfolane and dimethylsulfone is used, the mixing ratio is, for example, as follows: the mass ratio of sulfolane:dimethylsulfone is 100:50 to 100:1000, preferably 100:100 to 100:500, more preferably 100:200 to 100:400.

(34) These organic solvents may contain a thickener, a surfactant, an amide additive, and/or the like depending on need, for the purpose of controlling pore size or improving the performance of the polyamide hollow fiber membrane.

(35) The concentration of a solution obtained by dissolving a polyamide resin in the above-described organic solvent may be adjusted within the range of 21 to 35 mass %. The concentration is preferably 21 to 30 mass %, more preferably 23 to 28 mass %. In the case where such a concentration range is satisfied, the earlier-described ranges of the water permeability under external pressure and particle blocking rate are satisfied.

(36) Furthermore, when the polyamide resin is dissolved in the organic solvent, the temperature of the solvent needs to be adjusted to 100? C. or higher. Specifically, the polyamide resin is preferably dissolved in the organic solvent at a temperature 10? C. to 50? C. higher than the phase separation temperature of that system, preferably at a temperature 20? C. to 40? C. higher than the phase separation temperature. The phase separation temperature of the system means a temperature at which, when a mixture obtained by mixing the resin and the solvent at very high temperature is gradually cooled, and liquid-liquid phase separation or solid-liquid phase separation due to separated crystals occurs. The phase separation temperature can be suitably measured with the use of, for example, a microscope with a hot stage.

(37) Second Step

(38) In the Second Step, a hollow fiber membrane is formed with the use of a double-pipe nozzle for hollow fiber production having a double-pipe structure, by: discharging the liquid for membrane formation from the outer annular nozzle and discharging an inner fluid from the inner nozzle; and immersing the discharged product in a coagulation bath containing a polyhydric alcohol or a mixture of a polyhydric alcohol and water.

(39) The double-pipe nozzle for hollow fiber production used here may be a spinneret having a double annular structure, such as those for use in the production of sheath-core composite fibers by melt spinning. FIG. 2 illustrates one example of the structure of a cross section of the double-pipe nozzle for hollow fiber production. The diameter of the outer annular nozzle of the double-pipe nozzle for hollow fiber production and the diameter of the inner nozzle of the double-pipe nozzle for hollow fiber production may be adjusted appropriately depending on the inside diameter and outside diameter of the polyamide hollow fiber membrane.

(40) In the Second Step, the inner fluid to be discharged from the inner nozzle of the double-pipe nozzle for hollow fiber production may be in the form of a liquid or a gas, provided that the inner fluid is inert to the polyamide resin. The fluid in the form of a liquid is suitably used, because the liquid allows for spinning even under the conditions in which the liquid for membrane formation has a low viscosity and it is difficult to form a yarn. The liquid for use as the inner fluid is not limited to a particular kind, provided that the liquid is inert to the polyamide resin. In the case where the pores in the inside surface of the polyamide hollow fiber are desired to be large, a good solvent that has a high affinity for the polyamide resin may be used. In the case where the pores in the surface inside the polyamide hollow fiber are desired to be small, a poor solvent may be used. Specific examples of the good solvent include glycerin, diethylene glycol, triethylene glycol, tetraethylene glycol, polyethylene glycol 200, ?-butyrolactone, ?-caprolactone, propylene glycol, benzyl alcohol, 1,3-butanediol, sulfolane, and the like. Specific examples of the poor solvent include polyethylene glycol (300 to 600), higher fatty acids, liquid paraffin, and the like. These solvents may be used individually, or two or more of them may be used in combination. On the other hand, in the case where the viscosity of the liquid for membrane formation is high and spinnability is good, a method by which to inject a gas such as an inert gas may be employed.

(41) Of the inner fluids listed above, glycerin, 1,3-butanediol, triethylene glycol, tetraethylene glycol, polyethylene glycol 200, and sulfolane are particularly suitable for the satisfaction of the earlier-described ranges of the water permeability under external pressure and particle blocking rate of the polyamide hollow fiber.

(42) In the case where the pore size is desired to be as small as 10 nm or less, a poor solvent or a mixture of a poor solvent and another solvent is preferably used. Specific examples of the poor solvent are preferably polyethylene glycol 300 and polyethylene glycol 400. The use of polyethylene glycol 300 or polyethylene glycol 400, or a mixture of polyethylene glycol 300 or polyethylene glycol 400 and another solvent, allows the polyamide hollow fiber membrane of the present invention to have a small pore size while keeping a high water permeability and to trap even smaller particles.

(43) In the Second Step, a coagulation bath containing a polyhydric alcohol or a mixture of a polyhydric alcohol and water is used as the coagulation bath. The use of such a coagulation bath makes it possible to form a polyamide hollow fiber having the earlier-described properties. Specific examples of a polyhydric alcohol for use in the coagulation bath include glycerin, ethylene glycol, propylene glycol, butylene glycol, diethylene glycol, dipropylene glycol, diglycerin, triethylene glycol, tetraethylene glycol, polyethylene glycol (200 to 400), 1,3-butanediol, and the like. Of these polyhydric alcohols, particularly suitable for the satisfaction of the earlier-described ranges of the water permeability under external pressure and particle blocking rate of the polyamide hollow fiber are glycerin, ethylene glycol, diethylene glycol, propylene glycol, 1,3-butanediol, and polyethylene glycol 200. These polyhydric alcohols may be used individually or two or more of them may be used in combination.

(44) In the case where the coagulation bath is a mixture of a polyhydric alcohol and water, the mixing ratio of these is not particularly limited. For example, the mass ratio of polyhydric alcohol:water is 25 to 80:75 to 20, preferably 40 to 70:60 to 30.

(45) The temperature of the coagulation bath is not particularly limited, and usually ?20 to 100? C., preferably ?10 to 80? C., more preferably 0 to 40? C., for example. A change in temperature of the coagulation bath changes the speed of crystallization, and therefore makes it possible to change pore size, water permeability, and strength. Generally, lower temperatures of the coagulation bath tend to reduce pore size, reduce water permeability, and increase strength, whereas higher temperatures of the coagulation bath tend to increase pore size, increase water permeability, and reduce strength. However, these tendencies may change also depending on the solubility of the solvent contained in the liquid for membrane formation with the inner fluid and the speed of crystallization of the resin itself. For the purpose of satisfying the earlier-described water permeability under external pressure and particle blocking rate of the polyamide hollow fiber, the coagulation bath preferably has a low temperature. However, the coagulation bath does not necessarily have to have a low temperature, under certain conditions. In the case where the temperature of the coagulation bath is within the above-described range, it is possible to satisfy the earlier-described ranges of water permeability under external pressure and particle blocking rate of the polyamide hollow fiber, increase the strength of the membrane, and also reduce energy required for temperature control.

(46) The flow rate of the liquid for membrane formation discharged from the outer annular nozzle of the double-pipe nozzle for hollow fiber production is not particularly limited, and, for example, 2 to 20 g/min., preferably 3 to 15 g/min., more preferably 4 to 10 g/min. The flow rate of the inner fluid is adjusted appropriately in consideration of the diameter of the inner nozzle of the double-pipe nozzle for hollow fiber production, type of inner fluid to be used, flow rate of the liquid for membrane formation, and the like. The flow rate of the inner fluid is, for example, 0.1 to 2 times, preferably 0.2 to 1 times, more preferably 0.4 to 0.7 times the flow rate of the liquid for membrane formation.

(47) By performing the Second Step in this way, the liquid for membrane formation discharged from the double-pipe nozzle for hollow fiber production solidifies in the coagulation bath and forms a polyamide hollow fiber membrane.

(48) Third Step

(49) In the Third Step, the organic solvent is removed from the hollow fiber membrane formed in the Second Step. The method of removing the organic solvent from the hollow fiber membrane is not particularly limited, and may be a method to vaporize the organic solvent by drying with a dryer. However, it is preferable to employ a method by which to immerse the hollow fiber membrane in an extractant thereby extracting and removing the organic solvent that is phase-separated in the hollow fiber membrane. The extractant for use in extraction and removal of the organic solvent is preferably a reasonable extractant that has a low boiling point and thus can be readily separated utilizing the difference in boiling points after the extraction. Examples of the extractant include water, methanol, ethanol, isopropanol, acetone, diethyl ether, hexane, petroleum ether, toluene, and the like. Preferred extractants include water, methanol, ethanol, isopropanol, and acetone, and a more preferred extractant is water. In the case where an organic solvent insoluble in water, such as phthalic acid ester, fatty acid, or the like, is to be extracted, a suitable extractant is isopropyl alcohol, petroleum ether, or the like. Furthermore, the time during which the hollow fiber membrane is immersed in the extractant is not particularly limited, and is, for example, 0.2 hour to 2 months, preferably 0.5 hour to 1 month, more preferably 2 hours to 10 days. The extractant may be replaced or stirred for the purpose of effective extraction and removal of the organic solvent remaining in the polyamide hollow fiber. In particular, in the case where the polyamide hollow fiber membrane of the present invention is used in semiconductor industry, food industry, or water purification, it is desirable that the Third Step be thoroughly performed over time because remaining impurities (metal), organic solvent, and the like are problematic.

(50) When the Third Step is performed in this way, a polyamide hollow fiber membrane of the present invention is produced.

(51) The apparatus used in the production of the polyamide hollow fiber membrane of the present invention is not particularly limited, provided that the polyamide hollow fiber membrane is produced through the above-described First to Third Steps. A preferable apparatus is, for example, a general apparatus for use in dry-wet spinning as illustrated in FIG. 3. The following description roughly discusses a production flow for the polyamide hollow fiber membrane of the present invention with reference to the apparatus illustrated in FIG. 3 as an example. The liquid for membrane formation prepared in the First Step is stored in a container 3. Alternatively, the First Step may be performed in the container 3 to obtain the liquid for membrane formation. The liquid for membrane formation stored in the container 3 and the inner fluid introduced through an inner fluid inlet 5 are each measured with a metering pump 4, and transferred to a double-pipe nozzle for hollow fiber production (spinneret) 6. The liquid for membrane formation discharged from the double-pipe nozzle for hollow fiber production (spinneret) 6 is introduced into a coagulation bath 7 through a small air gap, and is cooled to solidify. While the liquid for membrane formation is cooled to solidify, a heat-induced phase separation occurs and a polyamide hollow fiber membrane 8 having a sea-island structure is obtained. The polyamide hollow fiber membrane 8 thus obtained is taken up with a winder 9, while being taken up on a bobbin winder 10 provided with a bobbin. While the polyamide hollow fiber membrane 8 is wound onto the bobbin, a cleaning shower 11 removes the solvent of the coagulation bath, the organic solvent that is an island component of the sea-island structure remaining in the hollow fiber membrane, and the inner fluid in the hollow portion, whereby a polyamide hollow fiber membrane is obtained.

(52) 3. Hollow Fiber Membrane Module Including Polyamide Hollow Fiber Membrane

(53) A polyamide hollow fiber membrane of the present invention is stored in a module case having an inlet for a liquid to be treated, an outlet for a filtrate, and the like, to be suitably used as a filtration filter. This is used as a hollow fiber membrane module.

(54) Specifically, the hollow fiber membrane module is not limited, provided that it is configured such that a bundle of polyamide hollow fiber membranes of the present invention is stored in the module case and one or both ends of the bundle of polyamide hollow fiber membranes is sealed and fixed with a potting agent. The hollow fiber membrane module is not limited, provided that it has, as an inlet for a liquid to be treated and an outlet for a filtrate, (i) an opening communicated with a flow path outside the walls of the polyamide hollow fiber membranes and (ii) an opening communicated with the hollow portions of the polyamide hollow fiber membranes.

(55) The hollow fiber membrane module is not particularly limited in shape, and may be a dead-end module or a crossflow module. Specific examples of the shape of the hollow fiber membrane module include: a dead-end module configured such that a bundle of hollow fiber membranes is bent in a U-shape and filled in a module case and the ends of the bundle are sealed and cut thereafter so that the bundle has openings; a dead-end module configured such that the openings of a bundle of hollow fiber membranes at one end are closed with a heat seal or the like, this bundle is filled straight in a module case, and the open end of the bundle is sealed and cut thereafter so that the end has openings; a dead-end module configured such that a bundle of hollow fiber membranes is filled straight in a module case, the both ends of the bundle are sealed, and only one end is cut so that the openings are exposed; a crossflow module configured such that a bundle of hollow fiber membranes is filled straight in a module case, the both ends of the bundle are sealed, the sealed ends of the bundle are cut, and two flow paths are provided in the side face of the filter case; and the like.

(56) The filling rate of polyamide hollow fiber membranes in the module case is not particularly limited. For example, the volume of polyamide hollow fiber membranes, including the volume of the hollow portions, with respect to the volume of the inner space of the module case is 30 to 90 vol. %, preferably 35 to 75 vol. %, more preferably 40 to 65 vol. %. In the case where such a filling rate is satisfied, it is possible to fill the polyamide hollow fiber membranes readily in the module case and allow a fluid to flow readily between hollow fiber membranes while keeping a large-enough filtration area.

(57) The potting agent for use in the production of the hollow fiber membrane module is not limited to a particular kind. Examples of the potting agent include polyurethane resin, epoxy resin, polyamide, silicone resin, melamine resin, polyethylene, polypropylene, phenol resin, polyimide, polyurea resin, and the like. Of these potting agents, preferred are agents which shrink or swell to a small extent when cured and are not too hard. Suitable examples of the potting agent include polyurethane resin, epoxy resin, polyamide, silicone resin, and polyethylene. More preferred potting agents are polyurethane resin, epoxy resin, and polyamide. These potting agents may be used individually or two or more of them may be used in combination.

(58) The material for the module case for use in the hollow fiber membrane module is not particularly limited. Examples of the material include polyamide, polyester, polyethylene, polypropylene, polyvinylidene fluoride, polytetrafluoroethylene, polyvinyl chloride, polysulfone, polyether sulfone, polycarbonate, polyarylate, polyphenylene sulfide, and the like. Of these agents, preferred are polyamide, polyethylene, polypropylene, polytetrafluoroethylene, polycarbonate, polysulfone, and polyether sulfone. More preferred are polyamide, polyethylene, polypropylene, and polytetrafluoroethylene.

(59) The hollow fiber membrane module including the polyamide hollow fiber membrane of the present invention is for use in purification of water, removal of impurities, and the like, in the fields of semiconductor industry, food industry, pharmaceutical industry, medical industry, and the like. In particular, it is believed that, in the filtration of photoresist in semiconductor industry, an impurity equal to or larger than one-tenth the width of a trace on a microchip would cause deficiency (Non-patent Document: M. Yang, D. L. Tolliver, The Journal of Environmental sciences 32(4), 35-42 (1989)). As miniaturization of the traces has progressed in recent years, the polyamide hollow fiber membrane module of the present invention, which has a fine structure and is highly hydrophilic, is very useful. Furthermore, in the field of pharmaceutical industry, it is an important objective to remove viruses in the production of blood products and biomedicine. For example, the polyamide hollow fiber membrane module of the present invention is suitable for use in removal of viruses as small as approximately 20 to 25 nm such as parvoviruses.

EXAMPLES

(60) The following description more specifically discusses the present invention with reference to Examples. Note, however, that the present invention is not intended to be limited to these examples.

(61) It should be noted that, in Examples, the physical properties of a hollow fiber membrane were measured in the following manner.

(62) Contact Angle

(63) The contact angle to water was measured by the earlier-described method with the use of an automatic contact angle meter DM-500 available from Kyowa Interface Science Co., LTD.

(64) Water Permeability Under External Pressure

(65) Water permeability under external pressure was measured by the earlier-described method with the use of the apparatus illustrated in FIG. 1.

(66) Particle Blocking Rate

(67) Particle blocking rate was measured by the earlier-described method with the use of colloidal gold particles having the following particle sizes.

(68) 50 nm: Product name Gold colloid-50 nm (available from British BioCell International, Ltd.)

(69) 20 nm: Product name Gold colloid-20 nm (available from British BioCell International, Ltd.)

(70) 10 nm: Product name Gold colloid-10 nm (available from British BioCell International, Ltd.)

(71) 5 nm: Product name Gold colloid-5 nm (available from British BioCell International, Ltd.)

(72) Inside Diameter and Outside Diameter of Polyamide Hollow Fiber Membrane

(73) The inside diameter and outside diameter of a polyamide hollow fiber membrane were found by: measuring a cross section of the polyamide hollow fiber membrane at a magnification of ?200 with an optical microscope; and calculating the mean of n=3.

(74) Metal Element Content of Polyamide Hollow Fiber Membrane

(75) 0.5 g of a dry polyamide hollow fiber membrane was mixed with 5 ml of nitric acid, and decomposed by microwave wet digestion by heating at 150? C. for 10 minutes and 180? C. for 15 minutes to obtain a sample. The metal element content of the sample was measured with an ICP-atomic emission spectrophotometer iCAP6500Duo available from Thermo Fisher Scientific K.K.

Example 1

(76) A liquid for membrane formation was prepared by stirring 260 g of polyamide 6 chips (A1030BRT available from UNITIKA LTD., relative viscosity 3.53), 197 g of sulfolane (available from Tokyo Chemical Industry), and 543 g of dimethylsulfone (available from Tokyo Chemical Industry) at 180? C. for 1.5 hours to dissolve the chips. The liquid for membrane formation was transferred to a spinneret (a double-pipe nozzle for hollow fiber production having a double-pipe structure) through a metering pump, and extruded at 5 g/min. The spinneret had an outside diameter of 1.5 mm and an inside diameter of 0.6 mm. Glycerin was used as an inner fluid, and was passed at a rate of 2.0 g/min. The extruded liquid for spinning was introduced into a coagulation bath containing a 5? C. 50 mass % propylene glycol solution through an air gap of 10 mm, cooled to solidify, and taken up at a take-up speed of 20 m/min. The obtained hollow fiber was immersed in water for 24 hours, whereby the solvent was extracted, and thereafter the hollow fiber was dried with a hot-air dryer at 50? C. for 1 hour. In this way, a polyamide hollow fiber membrane was obtained.

(77) The obtained polyamide hollow fiber membrane had an outside diameter of 550 ?m and an inside diameter of 300 ?m. The performance was as follows, as shown in Table 1: contact angle was 52?, water permeability under external pressure was 450 L/(m.sup.2.Math.atm.Math.h), and 10 nm particle blocking rate was 93%. The obtained hollow fiber membrane had a breaking strength of 12 MPa, an elongation at break of 200%, and a tensile modulus of 80.0 MPa. Electron micrographs of the obtained hollow fiber membrane are shown in FIG. 4. Observation showed that the cross section had densely arranged pores of the same size and had no macrovoids. A lot of densely arranged pores were observed in both the inside surface and the outside surface.

(78) The results obtained by measuring the metal element content of the polyamide hollow fiber membrane by ICP-atomic emission spectroscopy are shown in Table 2. The results showed that most metal elements were not detected, and even the concentration of the metal element contained in a large amount was as low as approximately 4 ppm.

Example 2

(79) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that the coagulation bath was changed to a 5? C. 50 mass % glycerin. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of 520, water permeability of 410 L/(m.sup.2.Math.atm.Math.h), and 10 nm particle blocking rate of 98%.

Example 3

(80) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that the coagulation bath was changed to an equal-weight mixture of glycerin and ethylene glycol. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of 52?, water permeability under external pressure of 200 L/(m.sup.2.Math.atm.Math.h), and 10 nm particle blocking rate of 94%.

Example 4

(81) A polyamide hollow fiber membrane was obtained in the same manner as in Example 1, except that the liquid for membrane formation was extruded at 10 g/min., the inner fluid was transferred at 4 g/min., and the take-up speed was 40 m/min. The obtained polyamide hollow fiber membrane had an outside diameter of 540 ?m and an inside diameter of 290 ?m. As shown in Table 1, the performance was as follows: the contact angle was 52?, water permeability under external pressure was 560 L/(m.sup.2.Math.atm.Math.h), and 10 nm particle blocking rate was 90%.

Example 5

(82) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that the solvent for the liquid for membrane formation was 740 g of sulfolane. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of 53?, water permeability under external pressure of 400 L/(m.sup.2.Math.atm.Math.h), 10 nm particle blocking rate of 61%, and 20 nm particle blocking rate of 98%.

Example 6

(83) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that the solvent for the liquid for membrane formation was 740 g of ?-butyrolactone. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of 53?, water permeability under external pressure of 350 L/(m.sup.2.Math.atm.Math.h), 10 nm particle blocking rate of 85%, and 20 nm particle blocking rate of 94%.

Example 7

(84) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that, in preparation of the liquid for membrane formation, the amount of polyamide 6 chips was 230 g and the solvent was 770 g of sulfolane. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of 53?, water permeability under external pressure of 720 L/(m.sup.2.Math.atm.Math.h), 10 nm particle blocking rate of 81%, and 20 nm particle blocking rate of 97%.

Example 8

(85) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that, in preparation of the liquid for membrane formation, the amount of polyamide 6 chips was 210 g and the solvent was 211 g of sulfolane and 579 g of dimethylsulfone. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of 50?, water permeability under external pressure of 940 L/(m.sup.2.Math.atm.Math.h), 20 nm particle blocking rate of 20%, and 50 nm particle blocking rate of 99%.

Example 9

(86) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that, in preparation of the liquid for membrane formation, the amount of polyamide 6 chips was 300 g and the solvent was 187 g of sulfolane and 513 g of dimethylsulfone. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of 55?, water permeability under external pressure of 70 L/(m.sup.2.Math.atm.Math.h), 5 nm particle blocking rate of 93%, and 10 nm particle blocking rate of 99%.

Example 10

(87) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that, in preparation of the liquid for membrane formation, the amount of polyamide 6 chips was 350 g and the solvent was 173 g of sulfolane and 477 g of dimethylsulfone, and the membrane was formed by passing the liquid for membrane formation at 4 g/min. and passing the inner fluid at 2.5 g/min. The obtained polyamide hollow fiber membrane had an outside diameter of 490 ?m and an inside diameter of 320 ?m, and, as shown in Table 1, the contact angle was 55?, water permeability under external pressure was 53 L/(m.sup.2.Math.atm.Math.h), 5 nm particle blocking rate was 98%, and 10 nm particle blocking rate was 100%.

Example 11

(88) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that, in preparation of the liquid for membrane formation, the amount of polyamide 6 chips was 280 g and the solvent was 192 g of sulfolane and 528 g of dimethylsulfone, and the membrane was formed by passing the liquid for membrane formation at 4 g/min. and passing the inner fluid, which was changed to glycerin:polyethylene glycol 300=75:25, at 2.5 g/min. The obtained polyamide hollow fiber membrane had an outside diameter of 500 ?m and an inside diameter of 300 ?m, and, as shown in Table 1, the contact angle was 54?, water permeability under external pressure was 280 L/(m.sup.2.Math.atm.Math.h), 5 nm particle blocking rate was 93%, and 10 nm particle blocking rate was 100%.

Example 12

(89) A polyamide hollow fiber membrane was prepared in the same manner as in Example 11, except that the liquid for membrane formation was passed at 8 g/min. and the inner fluid was passed at 5 g/min., and the membrane was formed at a take-up speed of 40 m/min. The obtained polyamide hollow fiber membrane had an outside diameter of 500 ?m and an inside diameter of 310 ?m. As shown in Table 1, the performance was as follows: the contact angle was 52?, water permeability under external pressure was 310 L/(m.sup.2.Math.atm.Math.h), 5 nm particle blocking rate was 92%, and 10 nm particle blocking rate was 100%.

Example 13

(90) A hollow fiber membrane was prepared in the same manner as in Example 1, except that the inner fluid was changed to polyethylene glycol 200. As shown in Table 1, the obtained hollow fiber membrane had a contact angle of 510, water permeability under external pressure of 550 L/(m.sup.2.Math.atm.Math.h), and 10 ?m particle blocking rate of 91%.

Example 14

(91) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that the inner fluid was changed to sulfolane. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of 53?, water permeability under external pressure of 330 L/(m.sup.2.Math.atm.Math.h), and 10 nm particle blocking rate of 94%.

Example 15

(92) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that the coagulation bath was changed to 100 mass % propylene glycol. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of 52?, water permeability under external pressure of 550 L/(m.sup.2.Math.atm.Math.h), and 10 nm particle blocking rate of 92%.

Example 16

(93) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that, in the preparation of the liquid for membrane formation, polyamide 610 chips (CM2001 available from TORAY INDUSTRIES, INC.) were used as a polyamide resin. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of 68?, water permeability under external pressure of 200 L/(m.sup.2.Math.atm.Math.h), and 10 nm particle blocking rate of 99%.

Example 17

(94) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that, in the preparation of the liquid for membrane formation, polyamide MXD6 chips (S6121 available from MITSUBISHI GAS CHEMICAL COMPANY, INC.) were used as a polyamide resin. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of 72?, water permeability under external pressure of 320 L/(m.sup.2.Math.atm.Math.h), and 10 nm particle blocking rate of 95%.

Comparative Example 1

(95) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that, in the preparation of the liquid for membrane formation, polyamide 12 chips (Rilsan AECNOTL available from Arkema, relative viscosity 2.25) were used as a polyamide resin. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of as large as 95? and water permeability under external pressure of as low as 30 L/(m.sup.2.Math.atm.Math.h). The 10 nm particle blocking rate was 100%.

Comparative Example 2

(96) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that, in the preparation of the liquid for membrane formation, polyamide 6 was used in an amount of 190 g, sulfolane was used in an amount of 216 g, and dimethylsulfone was used in an amount of 594 g. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of 51? and water permeability under external pressure of as high as 1170 L/(m.sup.2.Math.atm.Math.h). However, the 50 nm particle blocking rate was 76%.

Comparative Example 3

(97) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that, in the preparation of the liquid for membrane formation, polyamide 6 was used in an amount of 410 g, sulfolane was used in an amount of 157 g, and dimethylsulfone was used in an amount of 433 g. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of 55?. It should be noted that, although the measurement of water permeability under external pressure was tried, water did not pass through the membrane even when a pressure of up to 0.3 MPa was applied.

Comparative Example 4

(98) A polyamide hollow fiber membrane was prepared in the same manner as in Example 1, except that the coagulation bath was changed to 5? C. water. As shown in Table 1, the obtained polyamide hollow fiber membrane had a contact angle of 55? and water permeability under external pressure of as low as 20 L/(m.sup.2.Math.atm.Math.h). The 10 nm particle blocking rate was 99%.

Comparative Examples 5 to 17

(99) The preparation of a polyamide hollow fiber membrane was tried in the same manner as in Example 1, except that the solvent for the liquid for membrane formation was changed to 1-propanol (Comparative Example 5), isopropanol (Comparative Example 6), n-butanol (Comparative Example 7), tetrahydrofuran (Comparative Example 8), chloroform (Comparative Example 9), acetone (Comparative Example 10), methyl ethyl ketone (Comparative Example 11), methyl isobutyl ketone (Comparative Example 12), hexane (Comparative Example 13), toluene (Comparative Example 14), cyclohexane (Comparative Example 15), pyridine (Comparative Example 16), or ethyl acetate (Comparative Example 17). However, all these solvents had too low a boiling point to dissolve a polyamide resin, and therefore even when each mixture was stirred at a temperature 5? C. which was lower than the boiling point, the polyamide resin did not dissolve uniformly. It was not possible to form a polyamide hollow fiber membrane.

(100) Summary of Physical Properties of Polyamide Hollow Fiber Membranes

(101) Table 1 shows both the production conditions and physical properties of the polyamide hollow fiber membranes of Examples 1 to 17 and the polyamide hollow fiber membranes of Comparative Examples 1 to 4. The results showed that, by employing particular compositions of the liquid for membrane formation, inner fluid, and coagulation bath, it is possible to obtain a high-performance polyamide hollow fiber membrane having a contact angle to water of not more than 80?, water permeability under external pressure of not less than 50 L/(m.sup.2.Math.atm.Math.h), and 50 nm particle blocking rate of not less than 90% (refer to Examples 1 to 17).

(102) TABLE-US-00001 TABLE 1 Polyamide Organic solvent Take-up Use Use speed Type amount Type amount Inner fluid (m/min.) Coagulation bath Example 1 PA6 260 g Dimethylsulfone 197 g Glycerin 20 60% propylene glycol Sulfolane 543 g Example 2 PA6 260 g Dimethylsulfone 197 g Glycerin 20 50% Glycerin Sulfolane 543 g Example 3 PA6 260 g Dimethylsulfone 197 g Glycerin 20 Glycerin:ethylene Sulfolane 543 g glycol = 1:1 Example 4 PA6 260 g Dimethylsulfone 197 g Glycerin 40 60% propylene glycol Sulfolane 543 g Example 5 PA6 260 g Sulfolane 740 g Glycerin 20 60% propylene glycol Example 6 PA6 260 g ?-butyrolactone 740 g Glycerin 20 60% propylene glycol Example 7 PA6 230 g Sulfolane 770 g Glycerin 20 60% propylene glycol Example 8 PA6 210 g Dimethylsulfone 579 g Glycerin 20 60% propylene glycol Sulfolane 211 g Example 9 PA6 300 g Dimethylsulfone 513 g Glycerin 20 60% propylene glycol Sulfolane 187 g Example 10 PA6 350 g Dimethylsulfone 477 g Glycerin 20 60% propylene glycol Sulfolane 173 g Example 11 PA6 280 g Dimethylsulfone 528 g Glycerin:PEG300 = 20 60% propylene glycol Sulfolane 192 g 75:25 Example 12 PA6 280 g Dimethylsulfone 528 g Glycerin:PEG300 = 40 60% propylene glycol Sulfolane 192 g 75:25 Example 13 PA6 260 g Dimethylsulfone 543 g PEG200 20 60% propylene glycol Sulfolane 197 g Example 14 PA6 260 g Dimethylsulfone 543 g Sulfolane 20 60% propylene glycol 197 g Example 15 PA6 260 g Sulfolane 543 g Glycerin 20 100% propylene glycol 197 g Example 16 PA610 260 g Dimethylsulfone 543 g Glycerin 20 60% propylene glycol 197 g Example 17 MXD6 260 g Sulfolane 543 g Glycerin 20 60% propylene glycol 197 g Comparative PA12 260 g Dimethylsulfone 543 g Glycerin 20 60% propylene glycol Example 1 197 g Comparative PA6 190 g Dimethylsulfone 594 g Glycerin 20 60% propylene glycol Example 2 Sulfolane 216 g Comparative PA6 410 g Dimethylsulfone 433 g Glycerin 20 60% propylene glycol Example 3 Sulfolane 157 g Comparative PA6 260 g Dimethylsulfone 197 g Glycerin 20 Water Example 4 Sulfolane 543 g Contact Water permeability angle under external pressure Blocking rate (%) (?) [L/(m.sup.2 .Math. atm .Math. h)] 5 nm 10 nm 20 nm 50 nm Example 1 52 450 62 93 100 100 Example 2 52 410 75 98 100 100 Example 3 52 200 68 94 100 100 Example 4 52 560 59 90 100 100 Example 5 53 400 25 61 98 100 Example 6 53 350 52 85 94 99 Example 7 53 720 50 81 97 100 Example 8 50 1530 5 12 20 99 Example 9 55 70 93 99 100 100 Example 10 55 53 98 100 100 100 Example 11 54 280 93 100 100 100 Example 12 52 310 92 100 100 100 Example 13 51 550 62 91 99 100 Example 14 53 330 70 94 100 100 Example 15 52 550 71 92 100 100 Example 16 68 200 85 99 100 100 Example 17 72 320 75 95 100 100 Comparative 95 30 91 100 100 100 Example 1 Comparative 51 1170 2 5 35 76 Example 2 Comparative 55 0 Example 3 Comparative 55 20 96 99 100 100 Example 4 PA6 denotes polyamide 6 (CH.sub.2:NHCO = 5:1) PA610 denotes polyamide 610 (CH.sub.2:NHCO = 7:1) MXD6 denotes polyamide MXD6 (CH.sub.2, CN, C?:NHCO = 6:1) PA12 denotes polyamide 12 (CH.sub.2:NHCO = 11:1)

(103) TABLE-US-00002 TABLE 2 Concentration Concentration Concentration Concentration Concentration Element (ppm) Element (ppm) Element (ppm) Element (ppm) Element (ppm) Ag 0.0 Al 0.0 As 0.0 Au 0.0 B 0.0 Ba 0.0 Be 0.0 Bi 0.0 Ca 2.6 Cd 0.0 Ce 0.0 Co 0.0 Cr 1.0 Cu 0.2 Dy 0.0 Er 0.0 Eu 0.0 Fe 4.4 Ga 0.0 Gd 0.0 Ge 0.0 Hf 0.0 Hg 0.0 Ho 0.0 In 0.0 Ir 0.0 K 0.2 La 0.0 Li 0.0 Lu 0.0 Mg 0.6 Mn 0.0 Mo 0.0 Na 3.6 Nb 0.0 Nd 0.0 Ni 0.0 P 0.0 Pb 0.0 Pd 0.0 Pr 0.0 Pt 0.0 Re 0.0 Rh 0.0 Ru 0.0 Sb 0.0 Sc 0.0 Se 0.0 Si 1.4 Sm 0.0 Sn 0.0 Sr 0.0 Ta 0.0 Tb 0.0 Te 0.0 Ti 0.1 Tl 0.0 Tm 0.0 V 0.0 W 0.0 Y 0.0 Yb 0.0 Zn 0.3 Zr 0.0

Example 18

Preparation of Crossflow Module

(104) The hollow fiber membrane obtained in Example 1 was cut into a length of 250 mm, and the both ends of a bundle of 50 membranes were fused and sealed with a heat sealer. A module case prepared was a circular pipe made of vinyl chloride, which has water openings in the positions 35 mm away from the respective opposite ends and has an outside diameter of 20 mm, an inside diameter of 17 mm, and a length of 140 mm. Next, a two-component polyurethane potting agent available from SANYU REC CO., LTD. was put in a polytetrafluoroethylene (PTFE) pot having the same outside and inside diameters as the module case and having a length of 25 mm and leveled off, one end of the module case was attached to the top, and the bundle of membranes was pushed into the PTFE pot from above until the bundle made contact with the bottom of the PTFE pot. The bundle in this state was allowed to stand for 10 hours, whereby the end was potted. After the curing, the bundle was pulled out by pulling the PTFE pot, the polyurethane resin projecting out of the module case was cut together with the bundle of membranes, whereby the hollow portions were exposed. The other end of the bundle was also potted and cut. In this way, the hollow portions were exposed at both ends. The both ends were covered with caps having water openings and bonded with the caps, whereby a crossflow module was prepared (refer to FIG. 5A). The effective membrane length of the crossflow module was 115 mm?50 membranes.

Example 19: Preparation of Dead-End Module

(105) The hollow fiber membrane obtained in Example 1 was cut into a length of 200 mm, and a bundle of 50 membranes was bent into a U-shape and its ends were fused and sealed with a heat sealer. A module case prepared was a circular pipe made of vinyl chloride, which has an outside diameter of 20 mm, an inside diameter of 17 mm, and a length of 60 mm. Next, a two-component polyurethane potting agent available from SANYU REC CO., LTD. was put in a PTFE pot having the same outside and inside diameters as the module case and having a length of 25 mm and levelled off, one end of the filter case was attached to the top, and the sealed portion of the U-shaped bundle was pushed into the PTFE pot from above until the bundle made contact with the bottom of the PTFE pot. The bundle in this state was allowed to stand for 10 hours, whereby the portion was potted. After the curing, the bundle was pulled out by pulling the PTFE pot, the polyurethane resin projecting out of the module case was cut together with the bundle of membranes, whereby the hollow portions were exposed. The both ends of the module case were covered with caps having water openings and bonded with the caps, whereby a dead-end module was prepared (refer to FIG. 5B). The effective membrane length of the dead-end module was 80 mm?50 membranes.

DESCRIPTION OF REFERENCE SIGNS

(106) 1: Stirring motor 2: Inlet for pressure gas 3: Container 4: Metering pump 5: Inlet for inner fluid 6: Double-pipe nozzle for hollow fiber production (spinneret) 7: Coagulation bath 8: Polyimide hollow fiber membrane 9: Winder 10: Bobbin winder 11: Cleaning shower 12: Inner nozzle (nozzle portion through which inner fluid is to be discharged) 13: Outer annular nozzle (nozzle portion through which liquid for membrane formation is to be discharged) 14: Liquid pump 15: Inlet pressure meter 16: Hollow fiber membrane 17: Outlet pressure meter 18: Outlet valve 19: Receiving tray 20: Cap 21: Exit opening