A SULPHUR ADDITIVE TO SUPPRESS HYDROGEN SULPHIDE EMISSIONS FROM SULPHUR EXTENDED ASPHALT

Abstract

The present disclosure relates to a sulphur additive to suppress hydrogen sulphide emissions from Sulphur Extended Asphalt. The sulphur additive of the present disclosure comprises 5 sulphur in an amount ranging from 80 to 98 wt % and at least one aluminosilicate in an amount ranging from 2 to 20 wt %. The sulphur additive of the present disclosure suppresses the H2S emission up to acceptable safe limit during the preparation and application of the sulphur extended asphalt at elevated temperature.

Claims

1. A sulphur additive for preparing sulphur extended asphalt, said sulphur additive comprising: a) sulphur in an amount ranging from 80 to 98 wt % of the sulphur additive; and b) at least one aluminosilicate in an amount ranging from 2 to 20 wt % of the sulphur additive.

2. The sulphur additive as claimed in claim 1, wherein said at least one aluminosilicate has an ordered porous structure with pore size ranging from 4 to 8 .

3. The sulphur additive as claimed in claim 1, wherein said at least one aluminosilicate includes at least one metal ion in its framework, said at least one metal ion is selected from the group consisting of alkali metals, alkaline earth metals, rare earth metals and transition metals.

4. The sulphur additive as claimed in claim 3, wherein said metal ion is inherently present or introduced in the framework of said at least one aluminosilicate.

5. The sulphur additive as claimed in claim 1, wherein said additive is molded into at least one solid shaped article selected from the group consisting of pastilles, flakes, extrudates and granules.

6. The sulphur additive as claimed in claim 1, wherein said at least one aluminosilicate is at least one selected from the group consisting of virgin aluminosilicate and a spent aluminosilicate catalyst.

7. The sulphur additive as claimed in claim 1, wherein said at least one aluminosilicate is modified aluminosilicate, said modified aluminosilicate is prepared by one of the following processes: a) treating said aluminosilicate with at least one metal salt solution containing at least one adsorbent at ambient temperature for a time period in the range of 1 to 8 hours to obtain a mixture; filtering said mixture to obtain a residue; washing and drying said residue to obtain said modified aluminosilicate; and b) treating said aluminosilicate contained in a spent catalyst with a caustic aqueous solution to a temperature in the range of 30 to 60 C. for a time period in the range of 10 to 40 hours or sonicating for a time period in the range of 10 to 120 minutes or heating with a caustic powder to a temperature in the range of 400 to 800 C. for a time period in the range of 1 to 4 hours to obtain a mixture; hydrothermally heating said mixture at temperature in the range of 70 to 100 C. under autogenic pressure for a time period in the range of 15 to 40 hours to obtain said modified aluminosilicate.

8. The sulphur additive as claimed in claim 7, wherein said adsorbent is zeolite or mixture of zeolites with at least one zeolite having pore size ranging from 4 to 8 .

9. A process for the preparation of a sulphur additive as claimed in claim 1, said process comprising the following steps: a) introducing sulphur in the reactor and heating said sulphur to obtain a molten sulphur; b) adding at least one aluminosilicate to said molten sulphur to obtain a mixture; c) heating and stirring said mixture at temperature up to 170 C. to obtain a slurry; and d) cooling said slurry to obtain the sulphur additive.

10. The process as claimed in claim 9, wherein the ratio of the amount of said aluminosilicate and the amount of said sulphur is in the range of 1:4 to 1:15.

11. The process as claimed in claim 9, wherein said sulphur and said aluminosilicate are mixed together before introducing in the reactor.

12. A process for the preparation of sulphur extended asphalt using the sulphur additive of claim 1, said process comprising the following steps: a. introducing bitumen in a reactor; b. heating said bitumen to obtain a heated bitumen; and c. mixing said heated bitumen and said sulphur additive to obtain sulphur extended asphalt.

13. The process as claimed in claim 12, wherein the step of mixing said heated bitumen and said sulphur additive to obtain sulphur extended asphalt is carried out at a temperature in the range of 110 to 190 C., under stirring with a speed of less than 100 rpm.

Description

DETAILED DESCRIPTION

[0024] The present disclosure relates to a sulphur additive for reducing the emission of H.sub.2S during the preparation and the application of sulphur extended asphalt (SEA). The sulphur additive of the present disclosure suppresses H.sub.2S emission up to an acceptable safe limit during the preparation and the application of the SEA at elevated temperatures.

[0025] In accordance with one aspect of the present disclosure, there is provided a sulphur additive for the preparation of sulphur extended asphalt, wherein the sulphur additive comprises: [0026] sulphur in an amount ranging from 80 to 98 wt % of the sulphur additive; and [0027] at least one aluminosilicate in an amount ranging from 2 to 20 wt % of the sulphur additive.

[0028] In accordance with the present disclosure, the at least one aluminosilicate has an ordered porous structure with pore size in the range of 4 to 8 .

[0029] In accordance with one embodiment of the present disclosure, the aluminosilicate comprises at least one metal ion in its framework selected from the group consisting of alkali metals, alkaline earth metals, rare earth metals and transition metals.

[0030] The metal ion is inherently present or introduced in the framework of the aluminosilicate using known modification methods, before adding to sulphur for the preparation of the sulphur additive.

[0031] In accordance with another aspect of the present disclosure, there is provided a process for the preparation of a sulphur additive, wherein the process comprises the following steps: [0032] sulphur is introduced in the reactor and heated to obtain a molten sulphur; [0033] at least one aluminosilicate is added to the molten sulfur to obtain a mixture; [0034] the mixture is heated at the temperature up to 170 C. and stirred to obtain a slurry; and [0035] the slurry is cooled to obtain the sulphur additive;

[0036] In accordance with one embodiment of the present disclosure, sulphur, introduced into the reactor, is raw sulphur.

[0037] In accordance with one embodiment of the present disclosure, sulphur is in molten form.

[0038] In accordance with another embodiment of the present disclosure, the sulphur is melted before adding the at least one aluminosilicate to it.

[0039] The sulphur additive is molded into at least one solid shaped article selected from the group consisting of pastilles, flakes, extrudates and granules. The molding unit is selected from the group consisting of, but is not limited to, a pastillation unit, an extruder unit, a nodulizer unit, a granulator and the like to obtain at least one solid shaped article of the sulphur additive.

[0040] The step heating of sulphur to obtain the molten sulphur is carried out at a temperature in the range of 110 to 150 C. In accordance with one embodiment of the present disclosure, sulphur is heated to 150 C. to obtain molten sulphur.

[0041] The ratio of the amount of the aluminosilicate and the amount of sulphur is in the range of 1:4 to 1:15. In accordance with one embodiment of the present disclosure, the ratio of the amount of the aluminosilicate and the amount of sulphur is 1:12.

[0042] In accordance with the present disclosure, the at least one aluminosilicate is modified using at least one of the following processes: [0043] In one method aluminosilicate is treated with a metal salt solution containing a commercially available adsorbents at ambient temperature for a time period in the range of 1 to 8 hours to obtain a mixture; the mixture is filtered to obtain a first residue; the first residue is washed and dried to obtain the modified aluminosilicate; and [0044] another method of modifying at least one aluminosilicate is by treating aluminosilicate contained in a spent catalyst, wherein the process comprises the following steps: contacting aluminosilicate with a caustic aqueous solution to a temperature in the range of 30 to 60 C. for a time period in the range of 10 to 40 hours or sonication is carried out for a time period in the range of 10 to 120 minutes or heating with a caustic powder to a temperature in the range of 400 to 800 C. for a time period in the range of 1 to 4 hours to obtain a mixture; the mixture is hydrothermally heated to a temperature in the range of 70 to 100 C. under autogenic pressure for a time period in the range of 15 to 40 hours to obtain the modified aluminosilicate.

[0045] In accordance with one embodiment of the present disclosure, the aluminosilicate is at least one selected from the group consisting of virgin aluminosilicate and an aluminosilicate previously used as catalyst. The spent catalyst can be modified using one of the modification processes for aluminosilicate.

[0046] In accordance with yet another aspect of the present disclosure there is provided a process for the preparation of Sulphur Extended Asphalt, wherein bitumen is introduced in a reactor and heated to obtain a heated bitumen. Thereafter, the heated bitumen and the sulphur additive are mixed to obtain the Sulphur Extended Asphalt.

[0047] Bitumen is heated at a temperature in the range of 70 to 180 C.

[0048] In accordance with one embodiment of the present disclosure, the bitumen is heated at 165 C.

[0049] The weight ratio of the sulphur additive and the bitumen is in the range of 1:1 to 1:10.

[0050] The Sulphur Extended Asphalt prepared using the sulphur additive of the present disclosure shows the decreased H.sub.2S emission at a temperature in the range of 110 to 180 C.

[0051] The process for the preparation of Sulphur Extended Asphalt comprises mixing the sulphur additive and bitumen at a temperature in the range of 110 to 190 C., preferably between 135 to 180 C., under stirring with a speed of less than 100 rpm, preferably less than 70 rpm.

[0052] In one of the embodiment, the solid bitumen and the sulphur additive are mixed together before heating.

[0053] The present disclosure is further described in light of the following experiments which are set forth for illustration purpose only and not to be construed for limiting the scope of the disclosure. The following experiments can be scaled up to industrial/commercial scale and the results obtained can be extrapolated to industrial scale.

Experiment 1: Process for the Preparation of a Sulphur Additive

[0054] A reactor was charged with 30 g of sulphur. The sulphur was heated to 150 C. to obtain molten sulphur. 2.5 g of zeolite was added to the molten sulphur to obtain a slurry. The slurry was continuously stirred to make a homogeneous mixture. The homogeneous mixture was cooled to obtain the sulphur additive.

[0055] Experiment 2A: Preparation of Sulphur Extended Asphalt Using a Sulphur Additive (Containing Aluminosilicate with Alkali/Alkaline Earth Metal Ions)

[0056] A flask was charged with 70 g of bitumen. The bitumen in the flask was heated to 165 C. to obtain heated bitumen. 30 g of sulphur additive of experiment 1 was added to the heated bitumen to obtain a homogeneous mixture. The homogeneous mixture was stirred at a speed of 100 rpm. The emission of hydrogen sulphide (H.sub.2S) from the flask was monitored in the temperature range of 120 C. to 180 C. using a multi-gas detector.

TABLE-US-00001 TABLE 2A H.sub.2S emission at increasing temperature Sulphur H.sub.2S emission additive Bitumen Stirring rate Temperature on detector (wt %) (wt %) (rpm) ( C.) (ppm) 30 70 70 120 0 (undetectable) 30 70 70 140 0 (undetectable) 30 70 70 160 0 (undetectable) 30 70 70 170 2 30 70 70 180 4

[0057] It was observed that the emission of hydrogen sulphide (H.sub.2S) and sulphur dioxide (SO.sub.2) during the preparation of sulphur extended asphalt at 160 C. was found to be 0 ppm. As temperature of the sulphur extended asphalt was further raised to 180 C., it was observed that the emission of hydrogen sulphide (H.sub.2S) was 4 ppm, which is found to be well within the safer limit

Experiment 2B: H.SUB.2.S Emission from Sulphur Extended Asphalt (SEA) with Increasing Temperature

[0058] The sulphur extended asphalt samples prepared in Experiments 2A were cooled to room temperature. The cooled samples were further cut into pieces. The pieces were heated to 80 C. and the emission of hydrogen sulphide (H.sub.2S) was monitored at different levels using multi-gas detector. It was observed that there was no emission of hydrogen sulphide (H.sub.2S) and sulphur dioxide (SO.sub.2) upto 80 C.

TABLE-US-00002 TABLE 2B H.sub.2S emission with increasing temperature SEA (wt %) Temperature ( C.) H.sub.2S emission (ppm) 100 40 0 (undetectable) 100 60 0 (undetectable) 100 80 0 (undetectable)

Experiment 3A: Preparation of Sulphur Extended Asphalt Using a Sulphur Additive (Containing Aluminosilicate with Rare Earth/Transition Metal Ions)

[0059] The experimental procedure was followed as reacted in Experiment 2A. The results are tabulated in Table 3A.

TABLE-US-00003 TABLE 3A sulphur additive Bitumen Stirring rate Temperature H.sub.2S emission on (wt %) (wt %) (rpm) ( C.) detector (ppm) 30 70 70 120 0 (undetectable) 30 70 70 140 0 (undetectable) 30 70 70 160 0 (undetectable) 30 70 70 170 0 (undetectable) 30 70 70 180 2

[0060] No H.sub.2S emission was noted up to 170 C.

Experiment 3B: H.SUB.2.S Emission from Sulphur Extended Asphalt with Increasing Temperature

[0061] Sulphur Extended Asphalt samples prepared in Experiments 3A were cooled to room temperature. The solid mass obtained was cut into pieces and heated to 80 C. to check H.sub.2S emission. H.sub.2S emission was checked at different levels using the multi-gas detector. At 80 C., no H.sub.2S emission was observed at the zero inch level of the beaker brim.

TABLE-US-00004 TABLE 3B H.sub.2S emission from Sulphur Extended Asphalt (SEA) with increasing temperature H.sub.2S emission on detector SEA (wt %) Temperature ( C.) (ppm) 100 40 0 (undetectable) 100 60 0 (undetectable) 100 80 0 (undetectable)
(The H.sub.2S emission was monitored up to 80 C. on the basis of the fact that the maximum temperature of road surface is raised up to 60 C. in the Indian climate.)

Experiment 4A: Preparation of Sulphur Extended Asphalt Using Sulphur Additive (Containing Aluminosilicate with Caustic/Ultrasonic Treatment)

[0062] Experimental procedure was followed as given in Experiment 2A. The results are shown in Table 4A.

TABLE-US-00005 TABLE 4A H.sub.2S emission with increasing mixing temperature sulphur additive Bitumen Stirring rate Temperature H.sub.2S emission on (wt %) (wt %) (rpm) ( C.) detector (ppm) 30 70 70 120 0 (undetectable) 30 70 70 140 0 (undetectable) 30 70 70 160 0 (undetectable) 30 70 70 170 0 (undetectable) 30 70 70 180 4

[0063] No emission of hydrogen sulphide (H.sub.2S) and sulphur dioxide (SO.sub.2) was observed till 170 C. 4 ppm H.sub.2S was observed at 180 C.

Experiment 4B: H.SUB.2.S Emission from Sulphur Extended Asphalt with Increasing Temperature

[0064] The experimental procedure was followed as given in Experiment 2B using sulphur extended asphalt of Experiment 4A.

TABLE-US-00006 TABLE 4B H.sub.2S emission with increasing temperature SEA (wt %) Temperature ( C.) H.sub.2S emission on detector (ppm) 100 40 0 (non-detectable) 100 60 0 (non-detectable) 100 80 0 (non-detectable)
(The H.sub.2S detection experiments are conducted up to 80 C. on the basis of the fact that the maximum temperature of road surface raised up to 60 C. in the Indian climate.)
No emission of hydrogen sulphide (H.sub.2S) and Sulphur dioxide (SO.sub.2) was observed throughout the experiment indicating efficacy assurance during field application.

Experiment 5: Compaction Test

[0065] A flask was charged with 14 g of bitumen and heated at 165 C. to obtain a heated bitumen. 380 g of gravel (aggregates as per mix design, preheated at 170 C.) was added to the heated bitumen to obtain a slurry. The slurry was continuously stirred to get a homogeneous mixture. 6 g of sulphur additive was added to the homogeneous mixture and stirred to a speed of 100 rpm. The homogeneous mixture was aged at 135 C. for 4 hours followed by aging at 150 C. for 30 minutes. Further, the homogeneous mixture was pressed at 150 C. and 600 kPa. No emission of hydrogen sulphide (H.sub.2S) and sulphur dioxide (SO.sub.2) was observed throughout the experiment.

TECHNICAL ADVANCEMENTS

[0066] The present disclosure described herein above has several technical advantages including, but not limited to, the realization of: [0067] a sulphur additive that reduces/suppresses H.sub.2S emission during the preparation of SEA at a temperature greater than 80 C.; [0068] a sulphur additive that comprises re-used/spent aluminosilicate; and [0069] a process for the preparation of the sulphur additive that is economically viable.
Throughout this specification the word comprise, or variations such as comprises or comprising, will be understood to imply the inclusion of a stated element, integer or step, or group of elements, integers or steps, but not the exclusion of any other element, integer or step, or group of elements, integers or steps.

[0070] The use of the expression at least or at least one suggests the use of one or more elements or ingredients or quantities, as the use may be in the embodiment of the invention to achieve one or more of the desired objects or results. While certain embodiments of the inventions have been described, these embodiments have been presented by way of example only, and are not intended to limit the scope of the inventions. Variations or modifications to the formulation of this invention, within the scope of the invention, may occur to those skilled in the art upon reviewing the disclosure herein. Such variations or modifications are well within the spirit of this invention.

[0071] The numerical values given for various physical parameters, dimensions and quantities are only approximate values and it is envisaged that the values higher than the numerical value assigned to the physical parameters, dimensions and quantities fall within the scope of the invention unless there is a statement in the specification to the contrary.

[0072] While considerable emphasis has been placed herein on the specific features of the preferred embodiment, it will be appreciated that many additional features can be added and that many changes can be made in the preferred embodiment without departing from the principles of the disclosure. These and other changes in the preferred embodiment of the disclosure will be apparent to those skilled in the art from the disclosure herein, whereby it is to be distinctly understood that the foregoing descriptive matter is to be interpreted merely as illustrative of the disclosure and not as a limitation.