MULTILAYER PLATE

Abstract

A multilayer plate is disclosed which includes three layers. A carbon layer is covered by a metallic layer, and a substrate layer is covered at least partially by the carbon layer and the metallic layer. The metallic layer includes a first zone and a second zone. The first zone is a zone defined by the carbon layer and the second zone is a zone defined by carbon layer-free zone. The first zone has a higher thermal conductivity as the second zone. The multilayer plate can be used as a demonstration display for demonstrating the different thermal conductivity in the first zone compared to the second zone to a consumer.

Claims

1. A multilayer plate, comprising: a carbon layer, covered by a metallic layer, a substrate layer, covered at least partially by the carbon layer and the metallic layer, wherein the metallic layer comprises a first zone and a second zone and wherein the first zone is a zone defined by the carbon layer and the second zone is a zone defined by carbon layer-free zone.

2. The multilayer plate according to claim 1, wherein the carbon layer is a graphite plate with a thickness in a range of 2 millimetres and 4 millimetres.

3. The multilayer plate according to claim 2, wherein the graphite plate comprises one of a highly oriented pyrolytic graphite or a super-oriented graphite.

4. The multilayer plate according claim 1, wherein the metallic layer has a thickness in a range of 0.05 millimetres to 0.1 millimetres.

5. The multilayer plate according to claim 1, wherein the metallic layer is one of an aluminium foil, a copper foil or a steel foil.

6. The multilayer plate according to claim 1, wherein the substrate layer is made of a polyurethane flexible foam with one of a density in a range of 40 kilograms/square-meter to 50 kilograms/square-meter or a firmness in a range of 5.0 kilopascals to 9.0 kilopascals.

7. The multilayer plate according to claim 1, further comprising a frame surrounding the substrate layer and at least partially the carbon layer for holding the substrate layer and the carbon layer in place.

8. The multilayer plate according to claim 1, wherein the metallic layer is affixed on a circumferential surface of the frame.

9. The multilayer plate according to claim 1, wherein a first space between the carbon layer and the metallic layer in the first zone is a void.

10. The multilayer plate according to claim 1, wherein a second space between the substrate layer and the metallic layer in the second zone is a void.

11. The multilayer plate according to claim 1, wherein the first zone has a higher thermal conductivity as the second zone.

12. A demonstration display for demonstrating a differential thermal conductivity in a first zone or a second zone, comprising: a multilayer plate, wherein the multilayer plate comprises: a carbon layer, covered by a metallic layer, a substrate layer, covered at least partially by the carbon layer and the metallic layer, and wherein the metallic layer comprises the first zone and the second zone and wherein the first zone is a zone defined by the carbon layer and the second zone is a zone defined by carbon layer-free zone.

13. A method for demonstrating a differential thermal conductivity in a first zone or a second zone of a multilayer plate comprising the steps of: placing one or more body parts on one of the first zone or the second zone; placing a same one or a different one of the one or more body parts on a different one of the first zone or the second zone; and comparing the effect of the placing of the one or more body parts on the first zone and the second zone, wherein the multilayer plate comprises a carbon layer, covered by a metallic layer, a substrate layer, covered at least partially by the carbon layer and the metallic layer, and wherein the metallic layer comprises the first zone and the second zone and wherein the first zone is a zone defined by the carbon layer and the second zone is a zone defined by carbon layer-free zone.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0019] A more complete appreciation of the invention and many of the attendant advantages thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying figures.

[0020] FIG. 1 illustrates a schematic cross-sectional view of a multilayer plate.

[0021] FIG. 2 illustrates an exploded cross-sectional view of the multilayer plate of FIG. 1.

[0022] FIG. 3 illustrates a schematic view of a substrate layer.

[0023] FIG. 4 illustrates a flow-chart of a method for demonstrating a differential thermal conductivity in a first zone or a second zone of the multilayer plate.

DETAILED DESCRIPTION OF THE INVENTION

[0024] The invention will now be described based on the figures. It will be understood that the embodiments and aspects of the invention described herein are only examples and do not limit the protective scope of the claims in any way. The invention is defined by the claims and their equivalents. It will be understood that features of one aspect or embodiment of the invention can be combined with a feature of a different aspect or aspects and/or embodiments of the invention.

[0025] FIG. 1 is a schematic cross-sectional view of a multilayer plate 100. The multilayer plate 100 comprises a carbon layer 10, a metallic layer 20 and a substrate layer 30. The substrate layer 30 is partially covered by the carbon layer 10. The substrate layer 30 and the carbon layer 10 are surrounded by a frame 40. The frame 40 is affixed to the substrate layer 30 by one of an adhesive or a fastener. The frame 40 holds the substrate layer 30 and the carbon layer 10 in place and ensures that the carbon layer 10 stays in position relative to the substrate layer 30.

[0026] The substrate layer 30 and the carbon layer 10 are covered by the metallic layer 20. The metallic layer 20 comprises a first zone I and a second zone 11. The first zone I is a zone defined by the carbon layer 20. The second zone 11 is a zone defined by a carbon layer-free zone. The first zone I defines a first space 12 between the carbon layer 10 and the metallic layer 20. The second zone II defines a second space 32 between the substrate layer 30 and the metallic layer 20. Both of the first space 12 and the second space 32 do not comprise any solid material or liquid material.

[0027] FIG. 2 is an exploded cross-sectional view of a part of the multilayer plate 100. The substrate layer has a recess 31 to accommodate the carbon layer 10. The recess 31 has the same thickness as the carbon layer 10. The metallic layer 20 covers the carbon layer 10, the substrate layer 30 and the frame 40. The metallic layer 20 is affixed on a circumferential surface 41 of the frame 40. The metallic layer 20 can be affixed to the circumferential surface 41 by one of an adhesive or a fastener.

[0028] The substrate layer 30 is made of a foam. In an aspect the substrate layer 30 is a polyurethane flexible foam. A property of the polyurethane flexible foam is its excellent thermal insulation. The polyurethane flexible foam may comprise different densities and firmnesses. In an aspect the substrate layer 30 comprises a density in a range of 20 kilograms/square-meter to 80 kilograms/square-meter. In another aspect the substrate layer 30 comprise a density in a range of 40 kilograms/square-meter to 50 kilograms/square-meter. In an aspect the substrate layer 30 comprises a firmness in a range of 2.0 kilopascals to 14.0 kilopascals. In another aspect the substrate layer 30 comprises a firmness in a range of 5.0 kilopascals to 9.0 kilopascals.

[0029] The carbon layer 10 comprises one of a graphite plate or a steel plate. If the carbon layer 10 is a graphite plate, the graphite plate comprises one of a highly oriented pyrolytic graphite or a super-oriented graphite. Highly oriented pyrolytic graphite is a highly pure and ordered form of synthetic graphite, which is characterised by a low mosaic spread angle, meaning that the individual graphite crystallites are well aligned with each other. The super-oriented graphite is similar to the highly oriented pyrolytic graphite with a more in-plane orientation of the graphite.

[0030] One property of graphite is its high thermal conductivity. The high thermal conductivity of the carbon layer 10 generates a cooling effect in the first zone I compared to the substrate layer 30 in the second zone II. Consequently, the first zone I has a higher thermal conductivity as the second zone II. When a user touches the first zone I of the metallic layer 20 with the palm of a hand, the heat of the hand is conducted away from the carbon layer 10 (thermal conductivity) which the user feels as a cooling effect. If, on the other hand, the user touches the second zone II of the metallic layer 20, the heat from the palm of the hand is only very slowly conducted away from the substrate layer 30 (thermal insulation) and a warming effect because of the body heat connecting with the metallic layer is noticeable.

[0031] The carbon layer 10 has a thickness of at least 1.5 millimetres. In an aspect the thickness of the carbon layer 10 is in a range of 2 millimetres and 4 millimetres. If the carbon layer 10 has a thickness of 4 millimetres, the cooling effect lasts longer than if the carbon layer 10 would have a thickness of 2 millimetres. The cooling effect will last longer if the thickness of the carbon layer 10 is larger because a thicker carbon layer 10 has more capacity to absorb thermal energy than a thinner carbon layer 10.

[0032] The metallic layer 20 is one of an aluminium foil, a copper foil or a steel foil. To cover and protect the carbon layer 10, the substrate layer 30 and the frame 40, the metallic layer 20 has characteristics such as good formability, low chemical sensitivity, low air and moisture permeability, a good thermal conductivity and a good cleanability. In an aspect the metallic layer 20 comprises a thickness in a range of 0.03 millimetres to 0.15 millimetres. In another aspect the metallic layer 20 has a thickness in a range of 0.05 millimetres to 0.1 millimetres.

[0033] In an aspect the metallic layer 20 comprises an imprint such as for example a sign or a message, indicative of where to place the palm of the hand(s) on the metallic layer 20 for noticing a maximum cooling effect.

[0034] The multilayer plate 100 can be used for various purposes. In an aspect the multilayer plate 100 is used as a demonstration display for demonstrating the different thermal conductivity in the first zone I compared to the second zone II to the consumer. In this respect, the multilayer panel 100 must have certain dimensions to accommodate the palms of the consumers.

[0035] FIG. 3 illustrates a schematic view of an example of the substrate layer 30 of the demonstration display. The substrate layer 30 comprises different dimensions 301, 302, 303, 304, 305, 306 and 307. For example, the recess 31 for the carbon layer 10 has a surface defined by the dimensions 302 and 306, and a height defined by 307. In one example, the substrate layer 30 has the following values for the dimensions 301, 302, 303, 304, 305, 306 and 307, but these values are not limiting of the invention:

TABLE-US-00001 dimension value 301 288 mm 302 212 mm 303  37 mm 304  33 mm 305 138 mm 306 150 mm 307  4 mm

[0036] In an aspect the multilayer plate 100 is used as component of an assembly wherein different thermal properties of the first zone I and the second zone II are desired.

[0037] A further example of the use of the assembly with the multilayer plate 10 is in a temperature regulating device which is used to regulate the temperature of a container for serving a food dish. The food dishes are not just hot or cold but may need a precise temperature before, during or after serving of food from the food dish. The temperature of the serving dish is a factor when serving, for example, tea based on Japanese customs. The temperature chosen is often a medium setting between hot and cold and is commonly reached by heating up the container or food dish and letting the container or food dish cool down again over a (long-lasting) period of time.

[0038] The multilayer plate 100 of the assembly provides the first zone I and the second zone II, which comprise two different zones with differing cooling strengths. The cooling strength of the first zone I is higher than the cooling strength of the second zone II. If a hot food dish or a container with a hot dish is placed on the first zone I, the hot food dish or container will cool down faster. On the other hand, the hot food dish or the container with the hot food dish placed on the second zone II, will cool down slower. Shifting the container or the food dish from the first zone I to the second zone II, or vice versa, will influence the cooling-down process of the container or the food dish. For example, after the food dish is cooked and has a high temperature, the food dish could be placed directly on or in the container on the first zone I of the assembly to reach a first desired temperature. When the first desired temperature is reached, the food dish or the container with the food dish could be shifted to the second zone II until a second desired temperature is reached. The first desired temperature could be, for example, a temperature which stops the cooking process, and the second desired temperature could be, for example, a serving temperature.

[0039] In an aspect the metallic layer 20 of the assembly comprises an imprint such as a sign or a message, indicative of where to place the dish or container with the food dish on the metallic layer 20 for the higher or lower cooling-down strength.

In an aspect, the metallic layer 20 comprises a thermochromic imprint to indicate a specific temperature.

[0040] FIG. 4 illustrates a flow-chart of a method for demonstrating a differential thermal conductivity in the first zone I or the second zone II of the multilayer plate 100. In a first step S1 one or more body parts of the user is/are placed on one of the first zone I or the second zone II of the multilayer plate 100. In a second step S2 the same one or a different one of the one or more body parts is/are placed on a different one of the first zone I or the second zone II of the multilayer plate 100. In a third step S3 an effect of the placing of the one or more body parts on the first zone I and the second zone II is compared. The effect of the placing is, for example, the cooling effect of the first zone I compared to the second zone II, but this is not limiting of the invention.

REFERENCE NUMBERS

[0041] 100 multilayer plate [0042] 10 carbon layer [0043] 12 first space [0044] 20 metallic layer [0045] 32 second space [0046] 30 substrate layer [0047] 31 recess [0048] 40 frame [0049] 41 circumferential surface [0050] I first zone [0051] II second zone [0052] 301, 302, 303, 304, 305, 306, 307 dimensions [0053] S1, S2, S3 steps