METHOD FOR PRODUCING HIGH NICKEL LITHIATED METAL OXIDE FOR BATTERY

Abstract

A method for preparing high nickel lithiated metal oxides that includes selecting one or more nickel precursors; at least one non-corrosive lithium salt; and a plurality of metal oxide or hydroxide precursors. The metal precursors and lithium salts are mixed together to form a mixture comprising:

##STR00001##

wherein x = 1.0 - 1.1, 0.80 ≤ y ≤ 0.90, 0.03 < z ≤ 0.15, and 0 ≤ a ≤ 0.05; M is Co or Fe; and N is Al, Mn, Fe, Ca, Mg, Ti, Cr, Nb, Mo, W, B, or a mixture thereof provided N may be Fe when M is Co. The mixture is subjected to sintering (1.sup.st step) in air at ≥ 750° C. to form a powder. The powder is subjected to a 2.sup.nd sintering step in O.sub.2 at ≤ 750° C. to form the high nickel lithiated metal oxides.

Claims

1. A process for preparing high nickel lithiated metal oxides, the process comprising: a. Selecting one or more nickel precursors; b. Providing at least one non-corrosive lithium salt; c. Delivering a plurality of metal oxide or hydroxide precursors; d. Mixing the one or more nickel precursors, the at least one non-corrosive lithium salt, and the plurality of metal oxide/hydroxide precursors together to form a mixture comprising: ##STR00002## wherein x = 1.0 - 1.1, 0.80 ≤ y ≤ 0.90, 0.03 < z ≤ 0.15, and 0 ≤ a ≤ 0.05, M is Co or Fe; and N is Al, Mn, Fe, Ca, Mg, Ti, Cr, Nb, Mo, W, B, or a mixture thereof, provided N may be Fe when M is Co; e. Sintering in a 1.sup.st sintering step, the mixture in an air environment at a temperature ≥ 750° C. to form a powder; and f. Sintering in a 2.sup.nd sintering step, the powder in an O.sub.2 environment at a temperature ≤ 750° C. to form the high nickel lithiated metal oxides.

2. The process according to claim 1, wherein the M in formula (F-1) is cobalt.

3. The process according to claim 2, wherein the y in formula (F-1) is 0.80 ≤ y ≤ 0.87.

4. The process according to claim 3, wherein the y in formula (F-1) is 0.80 ≤ y ≤ 0.85.

5. The process according to claim 2, wherein N in formula (F-1) is Al.

6. The process according to claim 2, wherein N in formula (F-1) is Mn.

7. The process according to claim 2, wherein N in formula (F-1) is Al and Mn with a molar ratio of Al/Mn ranging from 0.99/0.01 to 0.01/0.99.

8. The process according to claim 2, wherein N in formula (F-1) is Al, Mn, and either Fe or Mo with a molar ratio of Al/Mn/(Fe-Mo) ranging from 0.99/0.05/0.05 to 0.05/0.99/0.05 to 0.05/0.05/0.99.

9. The process according to claim 1, wherein the O.sub.2 environment of the 2.sup.nd sintering step is pure oxygen.

10. The process according to claim 1, wherein the 1.sup.st sintering step has a temperature that is ≥ 750° C. and ≤ 1000° C.

11. The process according to claim 10, wherein the temperature in the 1.sup.st sintering step is ≥ 800° C. and ≤ 950° C.

12. The process according to claim 11, wherein the temperature in the 1.sup.st sintering step is ≥ 850° C. and ≤ 900° C.

13. The process according to claim 1, wherein the 1.sup.st sintering step is performed with a sintering time that is in a range of 2 hours to 24 hours.

14. The process according to claim 1, wherein the temperature in the 2.sup.nd sintering step is ≤ 750° C. and ≥ 700° C.

15. The process according to claim 14, wherein the 2.sup.nd sintering step is performed with a sintering time that is in a range of 2 hours to 24 hours.

16. The process according to claim 14, wherein the sintering time of the 2.sup.nd sintering step is longer than the sintering time of the 1.sup.st sintering step.

17. A cathode active material for use in a battery comprises a material formed according to the process of claim 1 having a formula according to (F-1): ##STR00003## wherein x = 1.0- 1.1, 0.80≤y ≤0.90, 0.03 < z ≤0.15, and 0 ≤ a ≤0.05; M is Co or Fe; and N is Al, Mn, Fe, Ca, Mg, Ti, Cr, Nb, Mo, W, B, or a mixture thereof, provided N may be Fe when M is Co.

18. The cathode active material according to claim 17, wherein the sintering temperature of the 2.sup.nd sintering step is lower than or equal to the sintering temperature of the 1.sup.st sintering step; wherein the O.sub.2 environment of the 2.sup.nd sintering step is pure oxygen.

19. A lithium ion or lithium battery comprising a cathode active material as one of its electrodes, wherein the cathode active material is a high nickel lithiated metal oxide Is formed according to the process of claim 1, the high nickel lithiated metal oxide having a formula according to (F-1): ##STR00004## wherein x = 1.0- 1.1, 0.80 ≤ y ≤ 0.90, 0.03 < z ≤ 0.15, and 0 ≤ a ≤0.05; M is Coor Fe; and N is Al, Mn, Fe, Ca, Mg, Ti, Cr, Nb, Mo, W, B, or a mixture thereof, provided N may be Fe when M is Co.

20. The lithium ion or lithium battery according to claim 19, wherein the sintering temperature of the 2.sup.nd sintering step is lower than or equal to the sintering temperature of the 1.sup.st sintering step; wherein the O.sub.2 environment of the 2.sup.nd sintering step is pure oxygen.

Description

DESCRIPTION OF THE DRAWINGS

[0020] In order that the disclosure may be well understood, there will now be described various forms thereof, given by way of example, reference being made to the accompanying drawings. The components in each of the drawings may not necessarily be drawn to scale, but rather emphasis is placed upon illustrating the principles of the invention.

[0021] FIG. 1 is a flowchart illustrating a two-step sintering process for producing high nickel or nickel-rich lithiated metal oxides according to the teachings of the present disclosure.

[0022] FIGS. 2A and 2B shows x-ray diffraction (XRD) patterns measured for NCA80 (FIG. 2A) and NCA90 (FIG. 2B) prepared according to the teachings of the present disclosure and sintered under different conditions.

[0023] FIG. 3 shows additional x-ray diffraction (XRD) patterns measured for NCA80 sintered using a 1.sup.st sintering step (800° C.) in an air environment with and without exposure to a 2.sup.nd sintering step (750° C.) in an oxygen (O.sub.2) environment.

[0024] FIG. 4 shows otherl x-ray diffraction (XRD) patterns for NCMA90 sintered using a 1.sup.st sintering step (800° C.) in an air environment with and without exposure to a 2.sup.nd sintering step (750° C.) in an oxygen (O.sub.2) environment.

[0025] The drawings described herein are for illustration purposes only and are not intended to limit the scope of the present disclosure in any way. It should be understood that throughout the description and drawings, corresponding reference numerals indicate like or corresponding parts and features.

DETAILED DESCRIPTION

[0026] The following description is merely exemplary in nature and is in no way intended to limit the present disclosure or its application or uses. For example, the high nickel or nickel-rich lithiated metal oxides prepared and used according to the teachings contained herein are described throughout the present disclosure as cathodic active materials used in conjunction with a battery in order to more fully illustrate the structural elements and the use thereof. The incorporation and use of such high nickel lithiated metal oxides in other applications, including without limitation as at least part of an electrode in other electrochemical cells is contemplated to be within the scope of the present disclosure.

[0027] For the purpose of this disclosure, the terms "about" and "substantially" are used herein with respect to measurable values and ranges due to expected variations known to those skilled in the art (e.g., limitations and variability in measurements).

[0028] For the purpose of this disclosure, the terms "at least one" and "one or more of" an element are used interchangeably and may have the same meaning. These terms, which refer to the inclusion of a single element or a plurality of the elements, may also be represented by the suffix "(s)" at the end of the element. For example, "at least one metal", "one or more metals", and "metal(s)" may be used interchangeably and are intended to have the same meaning.

[0029] The present disclosure generally provides a two-step process for producing high nickel or nickel-rich lithium metal oxides for use as cathode active materials using one or more non-corrosive lithium salts. Referring to FIG. 1, this process 1 comprises selecting 5 one or more nickel precursors, providing 10 at least one non-corrosive lithium salt, and delivering 15 a plurality of metal oxide/hydroxide precursors, such that at least one of the metal oxide/hydroxide precursors comprises cobalt (Co), iron (Fe) or a combination thereof and at least another metal precursor includes aluminum (Al), manganese (Mn), calcium (Ca), magnesium (Mg), titanium (Ti), chromium (Cr), niobium (Nb), molybdenum (Mo), tungsten (W), boron (B), or a combination thereof.

[0030] The one or more nickel precursors, the at least one non-corrosive lithium salt, and the plurality of metal oxide/hydroxide precursors are mixed 20 together to form a mixture that comprises, consists of, or consists essentially of the following formula (F-1):

[00002]${\text{Li}}_{\text{x}}{\text{Ni}}_{\text{y}}{\text{M}}_{\text{z}}{\text{N}}_{(1-\text{y}-z)}{\text{O}}_{(2-\text{a})}{\text{F}}_{\text{a,}}$

wherein x is in the range of 1.0 -1.1, 0.80 ≤ y ≤ 0.90, 0.03 < z ≤ 0.15, and 0 ≤ a ≤ 0.05; M is Co or Fe; and N is Al, Mn, Fe, Ca, Mg, Ti, Cr, Nb, Mo, W, B, or a combination thereof, provided N may be Fe when M is Co. Alternatively, in formula (F-1), 0.80 ≤ y ≤ 0.87; alternatively, 0.80 ≤ y ≤ 0.85. Fluorine (F) may be present purposely or included as an impurity. Alternatively, F may be absent, i.e., a = 0, and formula (F-1) may be written as Li.sub.xNi.sub.yM.sub.zN.sub.(1-y-z)O.sub.2. The N in formula (F-1) may alternatively be Al, Mn, Fe, Mo, or a combination thereof. When Al and Mn is present as a combination, the molar ratio of AI:Mn may range from 0.99/0.01 to 0.01/0.99;alternatively, in the range from 0.2/0.8 to 0.8/0.2; and alternatively, in the range from 0.3/0.7 to 0.7/0.3. When Al, Mn, and either Mo or Fe are present as a combination, the ratio of Al to Mn to Fe or Mo [AI:Mn:(Fe-Mo)] may range from 0.99/0.05/0.05 or 0.05/0.99/0.05 or 0.05/0.05/0.99. Alternatively, the ratio of Al:Mn:(Fe or Mo) is in the range from 0.1/0.8/0.1 or 0.8/0.1/0.1 or 0.1/0.1/0.8, and alternatively, in the range from 0.15/0.7/0.15 or 0.7/0.15/0.15 or 0.15/0.15/0.7.

[0031] The non-corrosive lithium salt may be selected to be lithium acetate, lithium nitrate, lithium oxalate, lithium carbonate, or a mixture thereof. Alternatively, the non-corrosive salt is lithium carbonate (Li.sub.2CO.sub.3).

[0032] The cobalt or iron precursors (M) may include, without restriction, Co.sub.3O.sub.4, CoO, Co(OH).sub.2, CoOOH, cobalt carbonate, cobalt acetate, cobalt oxalate, cobalt nitrate, Fe.sub.3O.sub.4, Fe.sub.2O.sub.3, FeO, FeOOH, Fe(OH).sub.3, Fe(OH).sub.2, iron carbonate, iron acetate, iron oxalate, iron nitrate, or similar materials. Alternatively, the cobalt or iron precursors may include Co.sub.3O.sub.4, CoO, Fe.sub.3O.sub.4, or Fe.sub.2O.sub.3 Alternatively, the cobalt precursor is Co.sub.3O.sub.4 The iron precursors may also be used for N when M is Co.

[0033] The other metal oxide or metal hydroxide precursors (N) that may be used include for example, without limitation, Al.sub.2O.sub.3, Al(OH).sub.3, aluminum acetate, aluminum carbonate, aluminum oxalate, aluminum ethoxide, aluminum propyl oxide, aluminum butyl oxide, B.sub.2O.sub.3, B.sub.2O.sub.5, H.sub.3BO.sub.3, boron acetate, and borates. The metal oxide or metal hydroxide precursors may be a metal oxide, a metal hydroxide, or a metallic compound that decomposes into either a metal oxide or a metal hydroxide. Alternatively, the metal oxide or metal hydroxide precursors (N) comprise, Al(OH).sub.3, and/or H.sub.3BO.sub.3

[0034] The nickel precursors may comprise, but not be limited to nickel oxide, nickel hydroxide, nickel oxyhydroxide, nickel acetate, nickel carbonate, nickel oxalate. When desirable, the nickel oxide may be formed from decomposing Ni(NO.sub.3).sub.2*6H.sub.2O at a high temperature for an amount of time that is in the range of 3-6 hours; alternatively, about 4-5 hours. Alternatively, the nickel precursor is nickel oxide.

[0035] The nickel precursors, non-corrosive lithium salts, and the metal oxide/hydroxide precursors may be mixed using a batch or continuous mixing system, including, for example, without limitation a ball mill, an attritor mill, a jet mill, a plowshare mixer, or like equipment. Alternatively, the materials are mixed using a ball mill with a liquid medium (e.g., water) at a solid/liquid ratio of about 4/6 with 1-20 mm beads (oxide/beads mass ratio ⅓) for a period of 1-24 hours; alternatively, about 5 hours. Alternatively, the materials are mixed using a ball mill without a liquid medium at an oxide/bead ratio ranged from 1/1 to ⅟20 and bead sizes ranged from 1 mm to 20 mm for a period of 1-24 hours. Alternatively, the materials are mixed by blending them together without any beads for a period of 1-24 hours.

[0036] After mixing, the mixture is collected and dried by any means known to one skilled in the art, including, but not limited to filtering and subjecting to a thermal environment, such as in an oven, to remove any liquid or moisture. Alternatively, the mixture may be spray dried by conventional methods known to one skilled in the art.

[0037] Referring once again to FIG. 1, a first (1.sup.st) sintering or pre-sintering step is performed 25 by exposing the mixture of non-corrosive lithium salts, the nickel precursors, and the metal oxide/hydroxide precursors to a high temperature in order to decompose the non-corrosive lithium salt and form a lithiated metal oxide with high degree of Li.sup.+/Ni.sup.2+ mixing content. The temperature of this 1.sup.st sintering step is generally greater than or equal to 750° C.; alternatively, ≥ 800° C.; or alternatively, ≥ 850° C.; alternatively, in the range of . is ≥ 750° C. and ≤ 1000° C.; alternatively, between is ≥ 800° C. and ≤ 950° C.; alternatively, between ≥ 850° C. and ≤ 900° C. The sintering environment for the pre-sintering step may be air, while the length of time for the 1.sup.st sintering step is in the range of 2 hours to 24 hours; alternatively, between about 5 hours and 20 hours; alternatively, in the range of 7 hours and 15; alternatively, about 10 hours.

[0038] Still referring to FIG. 1, after the pre-sintering or 1.sup.st sintering step, the lithiated metal oxide is then treated by further sintering 30 in a second (2.sup.nd) sintering or post-treatment step in an O.sub.2 environment at a relatively low temperature to oxidize any remaining Ni.sup.2+ to Ni.sup.3+ and to re-organize the distribution of Ni.sup.3+ in the nickel-rich lithium metal oxides to reduce the mixing content of Li.sup.+/Ni.sup.2+. The sintering temperature for this 2.sup.nd sintering step is generally, ≤ 750° C.; alternatively, between ≤ 750° C. and ≥ 700° C. For the purpose of this disclosure an O.sub.2 environment refers to an environment wherein the partial pressure of O.sub.2 is greater than that found in air. Alternatively, the oxygen environment may be pure O.sub.2. The length of time for the 2.sup.nd sintering step is in the range of 2 hours to 24 hours; alternatively, between about 5 hours and 20 hours; alternatively, in the range of 7 hours and 15; alternatively, about 10 hours. According to one aspect of the present disclosure, the sintering time of the 2.sup.nd sintering step is longer than the sintering time of the 1.sup.st sintering step.

[0039] The high nickel lithiated metal oxides are characterized using x-ray diffraction with measurements being conducted on a benchtop Rigaku x-ray machine equipped with Cu Kα radiation using an operating voltage of 30 kV and a current of 15 mA. The x-ray diffraction (XRD) peak ratio of (003)/(104) is used as an index for the mixing content of Li.sup.+/Ni.sup.2+. The higher the peak ratio of (003)/(104) indicates a lower content of cation mixing between Li.sup.+ and Ni.sup.2+, which infers a better electrochemical performance. The (003) peak occurs from the diffraction of a layered rock-salt structure, while the (104) peak appears due to both the diffraction of layered and cubic rock-salt structures. When Li.sup.+ and Ni.sup.2+ ions are mixed completely, the intensity of the (003) reflection should be zero.

[0040] The high nickel lithiated metal oxide may have a nickel (Ni) content that is in the range of about 80 mole% to less than 90 mole% relative to the total metal content present in the nickel-rich lithiated metal oxides. Alternatively, the nickel content is between 80 mole% and 85 mole%. The cobalt (Co) and/or iron (Fe) content is between 1 mole% and 20 mole% relative to the total metal content present in the nickel-rich lithiated metal oxides. Alternatively, the cobalt or iron content is between 5 -15 mole%.

[0041] The specific examples provided in this disclosure are given to illustrate various embodiments of the invention and should not be construed to limit the scope of the disclosure. The embodiments have been described in a way which enables a clear and concise specification to be written, but it is intended and will be appreciated that embodiments may be variously combined or separated without parting from the invention. For example, it will be appreciated that all preferred features described herein are applicable to all aspects of the invention described herein.

Example 1. Preparation and Testing of LiNi.SUB.0.8.Co.SUB.0.15.Al.SUB.0.05.O.SUB.2 (NCA80) and LiNi.SUB.0.9.Co.SUB.0.05.Al.SUB.0.05.O_{2 (NCA90)}

[0042] Over 100 grams of Nickel oxide (NiO) was produced by decomposing Ni(NO.sub.3).sub.2*6H.sub.2O at 600° C. in an air environment for 4 hours. For LiNi.sub.0.8Co.sub.0.15Al.sub.0.05O.sub.2 (NCA80), 19.40 grams of Li.sub.2CO.sub.3, 29.88 grams of NiO, 6.02 grams of Co3O4, and 1.95 grams of AI(OH)3 were ball-milled for 5 hours with a solid/water mass ratio of 4/6 and an oxide/bead mass ratio of ⅓. For making LiNi.sub.0.9Co.sub.0.05Al.sub.0.05O.sub.2 (NCA90), 33.61 grams of NiO was ball milled with 19.40 grams of Li.sub.2CO.sub.3, 2.01 grams of Co.sub.3O.sub.4, and 1.95 grams of Al(OH).sub.3 in water for 5 hours. The solid/water mass ratio was 4/6. The milled slurry was then spray-dried. The dried powder was sintered under various conditions as described in Table 1.

[0043] The x-ray diffraction (XRD) peak ratio of (003)/(104) was also measured for the resulting high nickel lithiated meal oxides as shown in Table 1. The x-ray diffraction (XRD) patterns measured for NCA80 and NCA90 are also provided in FIGS. 2A and 2B for comparison. The NCA80 sample comprised 80 mole% nickel as compared to all non-lithium metals, while the NCA90 sample contained 90 mole% nickel as compared to non-lithium metals.

TABLE-US-00001 Sintering conditions and peak ratio (003)/(104) for NCA80 and NCA90 Sintering conditions peak ratio (003)/(104) NCA80 850° C. in air (10 hrs) 0.95 750° C. in O.sub.2 (10 hrs) 1.25 850° C. in air (10 hrs) and then 750° C. in O.sub.2 (10 hrs) 1.47 850° C. in O.sub.2 (10 hrs) 0.77

TABLE-US-00002 Sintering conditions peak ratio (003)/(104) NCA90 850° C. in air (10 hrs) 0.99 750° C. in O.sub.2 (10 hrs) 0.98 850° C. in air (10 hrs) and then 750° C. in O.sub.2 (10 hrs) 0.82 850° C. in O.sub.2 (10 hrs) 0.99

[0044] As shown in Table 1, the peak ratio between (003)/(104) was the highest for the NCA80 sample (80 mole% Nickel) with a pre-sintering step performed in an air environment (850° C.) followed by a 2.sup.nd post-treatment sintering step in an O.sub.2 environment (750° C.). When the sintering step was performed only in air (850° C.), the NCA80 sample showed a lower peak ratio of (003)/(104) than the sample treated in O.sub.2 sintered at a lower temperature of 750° C. (i.e., compare 0.95 vs. 1.25). This result is expected because of the decrease of O.sub.2 partial pressure that occurs when sintered in air. When sintered only in O.sub.2, the sample treated at 850° C. showed a lower peak ratio of (003)/(104) than the sample treated at 750° C. This result is also expected due to the poor thermal stability of the high nickel lithiated metal oxides. For the sample sintered at 850° C. and then treated in O.sub.2 at 750° C., its (003)/(104) peak ratio was 1.47, which was higher than the samples sintered at 750° C. or 850° C. in O.sub.2. This result confirms that the O.sub.2 treatment at 750° C. has oxidized the Ni.sup.2+ impurity from the 850° C. air-sintered sample, and even more, the Li/Ni mixing level is lower than the samples sintered in O.sub.2. Thus, the use of a post-treatment (2.sup.nd) sintering step in O.sub.2 at a lower temperature than in the 1.sup.st pre-sintering step reduces the Li.sup.+/Ni.sup.2+ mixing and redistributes the Ni.sup.3+ ions.

[0045] Still referring to Table 1, the effect from the post-treatment in O.sub.2 was not observed to be the same when the Ni content was increased to 90 mole % (see NCA90). In this case, the use of a post-treatment in O.sub.2, actually decreased the (003)/(104) peak ratio to a value that is even lower than the value measured for the sample sintered in air (compare 0.82 vs 0.99). This result suggests that at this concentration of nickel a two-step sintering process is not effective for maintaining a low Li.sup.+/Ni.sup.2+ mixing level.

Example 2 - Further Preparation and Testing of LiNi.SUB.0.8.Co.SUB.0.15.Al.SUB.0.05.O.SUB.2 (NCA80)

[0046] NCA80 was made with the same conditions as the material discussed in Example 1 except that the 1.sup.st sintering temperature was 800° C. instead of 850° C. The dried powder was finally sintered under various conditions described in Table 2. The X-ray diffraction (XRD) peak ratio of (003)/(104) was also measured for the resulting high nickel lithiated meal oxides as shown in Table 2. The NCA80 sample comprised 80 mole% nickel.

[0047] The x-ray diffraction (003)/(104) peak ratios show in Table 2 exhibit the same trend as observed in Table 1. The sample sintered with a 1.sup.st sintering step in air (800° C.) and a 2.sup.nd step of O.sub.2 sintering (750° C.) exhibited a much higher (003)/(104) XRD peak ratio than the sample sintered with a single air (800° C.) sintering step (compare 1.31 vs 0.95). In fact, the (003)/(104) peak ratio in this Example 2 was even higher than the two NCA80 samples sintered at a higher temperature (850° C.) in pure O.sub.2 as shown in Table 1.

[0048] The x-ray diffraction (XRD) patterns for NCA80 sintered under the different conditions are also provided in FIG. 3 for comparison. This comparison demonstrates the peak intensity difference that exists between the two NCA80 samples. Both samples did not show any presence of impurity phases from Li.sub.2O/Li.sub.2CO.sub.3.

TABLE-US-00003 Sintering conditions and the peak ratio (003)/(104) for NCA80 NCA80 800° C. in air (10 hrs) 0.95 800° C. in air (10 hrs) and then 750° C. in O.sub.2 (10 hrs) 1.31

Example 3 -Preparation and Testing of Li.SUB.1.05.Ni.SUB.0.9.Co.SUB.0.05.Al.SUB.0.02.Mn.SUB.0.025.B.SUB.0.005.O.SUB.2 (NCMA90)

[0049] Nickel oxide (NiO) (~325 mesh, 99%) was purchased from Sigma Aldrich in USA. The NCMA90 sample was prepared by ball milling 38.8 grams of Li.sub.2CO.sub.3, 67.22 grams of NiO, 4.01 grams of Co.sub.3O.sub.4, 1.56 grams of Al(OH).sub.3, and 0.309 grams of H.sub.3BO.sub.3 in water. The solid/water mass ratio was 4/6. A total of 160 grams of 2 mm ceramic beads were added into the dispersion and the dispersion was milled for 5 hours. The targeted composition is Li.sub.1.05Ni.sub.0.9Co.sub.0.05Al.sub.0.02Mn.sub.0.025B.sub.0.005O.sub.2. A slight excess of lithium carbonate was added to compensate for the loss of lithium expected to occur during the sintering process.

[0050] After milling, the dispersion was spray dried with a benchtop spray drier. After drying, the powder was first sintered in air at 500° C. for 2 hours and then 850° C. for 10 hours. The air-sintered powder was then transferred into a glass tube and sintered again at 750° C. for 10 hours with flowing pure O.sub.2. X-ray diffraction (XRD) patterns were measured using a benchtop Rigaku X-ray machine.

[0051] The sintering conditions and the corresponding (003)/(104) peak ratio are shown in Table 3. The NCMA90 sample exposed to the pure O.sub.2 post-treatment sintering step exhibited an increase in the (003)/(104) peak ratio as compared to the sample sintered only in air (compare 0.91 ➔ 1.01). This example demonstrates that the use of a pure O.sub.2 post-treatment could increase the (003)/(104) peak ratio even at 90 mole% of Ni content, although the value for the (003)/(104) peak ratio is not at the same level as observed for samples having lower Ni content (see NCA80 in Tables 1 & 2).

TABLE-US-00004 Sintering conditions and the peak ratio (003)/(104) for NCMA90 NCMA90 850° C. in air (10 hrs) 0.91 850° C. in air (10 hrs) and then 750° C. in O.sub.2 (10 hrs) 1.01

[0052] According to another aspect of the present disclosure a cathode active material for use in an electrochemical cell is described. This material, which is formed according to the process described above and in FIG. 1 generally comprises the formula described by formula F-1. The electrochemical cell may be selected to be a lithium ion or lithium battery with the cathode active material or high nickel lithiated metal oxides being used for at least part of one of the electrodes.

[0053] Within this specification, embodiments have been described in a way which enables a clear and concise specification to be written, but it is intended and will be appreciated that embodiments may be variously combined or separated without parting from the invention. For example, it will be appreciated that all preferred features described herein are applicable to all aspects of the invention described herein.

[0054] Those skilled-in-the-art, in light of the present disclosure, will appreciate that many changes can be made in the specific embodiments which are disclosed herein and still obtain alike or similar result without departing from or exceeding the spirit or scope of the disclosure. One skilled in the art will further understand that any properties reported herein represent properties that are routinely measured and can be obtained by multiple different methods. The methods described herein represent one such method and other methods may be utilized without exceeding the scope of the present disclosure.

[0055] The foregoing description of various forms of the invention has been presented for purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise forms disclosed. Numerous modifications or variations are possible in light of the above teachings. The forms discussed were chosen and described to provide the best illustration of the principles of the invention and its practical application to thereby enable one of ordinary skill in the art to utilize the invention in various forms and with various modifications as are suited to the particular use contemplated. All such modifications and variations are within the scope of the invention as determined by the appended claims when interpreted in accordance with the breadth to which they are fairly, legally, and equitably entitled.