COPOLYMERS COMPRISING (PER)FLUOROPOLYETHER CHAINS

Abstract

The present patent application relates to block copolymers comprising (per)fluoropolyether chains useful as lubricants and characterized by increased viscosity.

Claims

1. A block copolymer (P) having two chain ends, wherein both said chain ends comprise a perfluorinated alkyl group, and comprising a first and a second (per)fluoropolyether chain [PFPE chain] each having two chain ends, wherein the first chain end of said first and second PFPE chain comprises a perfluorinated alkyl group and the second chain end of said first and second PFPE chain are bonded to each other via a block of formula (I): $\begin{array}{cc}\left[AB\right]& \left(I\right)\end{array}$ wherein (A) is a PFPE chain, and (B) is a moiety complying with the following formula (II): ##STR00003## wherein n is an integer from 1 to 3; R.sub.1 to R.sub.4, each independently, is selected from the group consisting of, fluorine atom, perfluorinated linear or branched alkyl group having from 1 to 6 carbon atoms, group of formula (III): $\begin{array}{cc}-{{\left(R_{10}\right)}_t\left[C\left(R_{11}\right)\left(R_{12}\right)-C\left(R_{13}\right)\left(R_{14}\right)\left(R_{15}\right)\right]}_z& \left(\mathrm{III}\right)\end{array}$ wherein R.sub.10 is an oxygen atom, or a bi-/tri-/tetravalent perfluorinated alkyl chain comprising from 1 to 24 carbon atoms, optionally interrupted by and/or comprising at least one oxygen atom, t is zero or 1, z is an integer from 1 to 3; R.sub.11 to R.sub.15, each independently, is selected from the group consisting of, fluorine atom, perfluorinated linear or branched alkyl group having from 1 to 6 carbon atoms and group of formula (IV): $\begin{array}{cc}-\left[{\left(A^{.Math.}\right)}_a-{\left(B^{.Math.}\right)}_v\right]-\left(C^{.Math.}\right)-T& \left(\mathrm{IV}\right)\end{array}$ wherein A{circumflex over ()} is a PFPE chain, a is zero or 1, v is zero or an integer from 1 to 3, B{circumflex over ()} is a group of formula [C(R.sup.1{circumflex over ()})(R.sup.2{circumflex over ()})C(R.sup.3{circumflex over ()})(R.sup.4{circumflex over ()})] wherein R.sup.1{circumflex over ()} to R.sup.4{circumflex over ()} each independently has the meaning defined above for R.sub.1 to R.sub.4, C{circumflex over ()} is a PFPE chain, and T is a perfluorinated alkyl group; wherein: said A and B in formula (I) and said A{circumflex over ()} and B{circumflex over ()} in formula (IV) are statistically distributed, at least one of R.sub.1 to R.sub.4 is a group of formula (III), one of R.sub.11 or R.sub.12 and one of R.sub.13 to R.sub.15, is a group of formula (IV) wherein a is 1, and the sum of (B+B{circumflex over ()}) is from 1 to 15.

2. The block copolymer (P) according to claim 1, wherein said first and second PFPE chain, said A, A{circumflex over ()}, C{circumflex over ()} are the same or different from each other; and/or each of said perfluorinated alkyl groups, being the same or different from each others, are a linear perfluoroalkyl group comprising from 1 to 3 carbon atoms; and/or said first PFPE chain is bonded to said at least one block of formula (I) via a sigma bond or a group selected from CF.sub.2, CF.sub.2CF.sub.2or O; and/or said second PFPE chain is bonded to said at least one block of formula (I) via a sigma bond or a group selected from CF.sub.2, CF.sub.2CF.sub.2or O; said A and B in formula (I) are linked via a sigma bond or a group selected from CF.sub.2or CF.sub.2CF.sub.2.

3. The block copolymer (P) according to claim 1, wherein each of said first and second PFPE chain, A in formula (I) and said A{circumflex over ()} and C{circumflex over ()} in formula (IV) is independently a partially or fully fluorinated chain [chain (R.sub.f)] comprising, repeating units being independently selected from the group consisting of: (Rf-i) CFXO, wherein X is F or CF.sub.3; (Rf-ii) CFXCFXO, wherein X, equal or different at each occurrence, is F or CF.sub.3, with the proviso that at least one of X is F; (Rf-iii) CF.sub.2CF.sub.2CW.sub.2O, wherein each of W, equal or different from each other, are F, Cl, H; (Rf-iv) CF.sub.2CF.sub.2CF.sub.2CF.sub.2O; (Rf-v) (CF.sub.2).sub.jCFZOwherein j is an integer from 0 to 3 and Z is a group of general formula OR.sub.(f-a)-T, wherein R.sub.(f-a) is a fluoropolyoxyalkene chain comprising a number of repeating units from 0 to 10, said recurring units being selected from the group consisting of: CFXO, CF.sub.2CFXO, CF.sub.2CF.sub.2CF.sub.2O, and CF.sub.2CF.sub.2CF.sub.2CF.sub.2O, with each of X being independently F or CF.sub.3 and T being a C.sub.1-C.sub.3 perfluoroalkyl group.

4. The block copolymer (P) according to claim 1, wherein in formula (II): n is an integer equal to 1 or 2; and/or at least one of substituents R1 to R4 is a group of formula (III) and the other substituents are each independently selected from a fluorine atom or a perfluorinated alkyl chain having from 1 to 3 carbon atoms.

5. The block copolymer (P) according to claim 1, wherein in formula (III): t is 0; or t is 1 and R.sub.10 complies with one of the following formulae: $\begin{array}{cc}{\left({\mathrm{CF}}_2\right)}_d{\left(O\right)}_e{\left(C{F}_{2}O\right)}_f{R_{CF}\left(O\right)}_{e^{*}}{\left({\mathrm{CF}}_2\right)}_{d^{*}}{\left(\mathrm{CF2O}\right)}_{f^{*}}& \left(R_{10}-i\right)\end{array}$ wherein each of d, d*, e, e*, f and f* is independently zero or 1 and R.sub.CF is a perfluoroalkyl chain comprising from 1 to 12, optionally interrupted by one or more oxygen atoms $\begin{array}{cc}O{\left(C_3{F}_{6}O\right)}_h{\left({\mathrm{CF}}_2\right)}_i{\left(C_3{F}_{6}O\right)}_{j}O& \left(R_{10}-\mathrm{ii}\right)\end{array}$ wherein h=j and h+j is from 2 to 6, and i is from 2 to 6.

6. The block copolymer (P) according to claim 1, wherein in formula (III): z is equal to 1 and R.sub.10 is an oxygen atom or a bivalent perfluorinated alkyl chain comprising from 1 to 24 carbon atoms, optionally interrupted by and/or comprising at least one oxygen atom; and/or one of substituents R.sub.11 and R.sub.12 is a group of formula (IV) and the other substituent is selected from a fluorine atom or a perfluorinated alkyl chain having from 1 to 3 carbon atoms; and/or one of substituents R.sub.13 to R.sub.15 is a group of formula (IV) and the other two substituents are independently selected from a fluorine atom or a perfluorinated alkyl chain having from 1 to 3 carbon atoms.

7. The block copolymer (P) according to claim 1, wherein in formula (IV): a is 1, v is 1 and B{circumflex over ()} is a group of formula [C(R.sup.1{circumflex over ()})(R.sup.2{circumflex over ()})C(R.sup.3{circumflex over ()})(R.sup.4{circumflex over ()})] wherein R.sup.1{circumflex over ()} to R.sup.4{circumflex over ()} each independently is selected from the group consisting of fluorine atom, perfluorinated linear or branched alkyl group having from 1 to 6 carbon atoms, or group of formula (III).

8. The block copolymer (P) according to claim 1, said copolymer (P) having a complex viscosity, measured at 0.1 rad/s and at 25 C. according to ISO 6721 part 10, from 10 Pa*s to 2000 Pa*s.

9. The block copolymer (P) according to claim 1, said copolymer (P) being free from pendant groups comprising moieties capable of undergoing a chemical reaction.

10. A mixture (P) comprising two or more block copolymers (P) as defined in claim 1.

11. A process (P) for the manufacture of block copolymer (P) as defined in claim 1, said process comprising the steps of: a) contacting at least one peroxidic (per)fluoropolyether polymer [PFPE peroxy] comprising a (per)fluoropolyether chain having two chain ends, each of said chain ends comprising a (per)fluorinated alkyl chain having from 1 to 3 carbon atoms, optionally containing one or more chlorine atoms or functional end groups selected from acyl fluoride, fluoroformate and ketones, said chain ends being bonded to opposite sides of said (per)fluoropolyether chain, said (per)fluoropolyether chain comprising repeating units being independently selected from the group consisting of formulae (Rf-i) to (Rf-v), wherein (Rf-i) to (Rf-v) are independently selected from the group consisting of: (Rf-i) CFXO, wherein X is F or CF.sub.3; (Rf-ii) CFXCFXO, wherein X, equal or different at each occurrence, is F or CF.sub.3, with the proviso that at least one of X is F; (Rf-iii) CF.sub.2CF.sub.2CW.sub.2O, wherein each of W, equal or different from each other, are F, Cl, H; (Rf-iv) CF.sub.2CF.sub.2CF.sub.2CF.sub.2O; (Rf-v) (CF.sub.2).sub.jCFZOwherein j is an integer from 0 to 3 and Z is a group of general formula OR.sub.(f-a)-T, wherein R.sub.(f-a) is a fluoropolyoxyalkene chain comprising a number of repeating units from 0 to 10, said recurring units being selected from the group consisting of: CFXO, CF.sub.2CFXO, CF.sub.2CF.sub.2CF.sub.2O, and CF.sub.2CF.sub.2CF.sub.2CF.sub.2O, with each of X being independently F or CF.sub.3 and T being a C.sub.1-C.sub.3 perfluoroalkyl group and having a peroxidic content (PO), defined as grams of active oxygen (Mw=16) in 100 g of PFPE peroxy between 0.1 and 4, with at least one perfluorinated compound of formula (III-p): ##STR00004## wherein each of R.sub.21 to R.sub.23 and R.sub.31 to R.sub.33 is independently fluorine atom, perfluorinated linear or branched alkyl group having from 1 to 6 carbon atoms, R.sub.10 is an oxygen atom, a perfluorinated linear or branched alkyl group comprising from 1 to 24 carbon atoms, optionally interrupted by and/or comprising at least one oxygen atom, t is zero or 1; each of z* and z** is independently 1 or 2; wherein the amount of the compound of formula (III-p) is less than 5 wt. % of the amount of the PFPE peroxy; b) letting the PFPE peroxy and the compound of formula (III) react in the presence of UV radiation or heating; c) fluorinating, thus obtaining said copolymer (P).

12. The process (P) according to claim 11, wherein t is 1, and the two, three or four unsaturated moieties are bonded to the same or to different carbon atoms belonging to R.sub.10.

13. The process (P) according to claim 12, wherein said at least one compound of formula (III-p) complies with the following formula: $C{F}_2=C{F\left(R_{10}\right)}_{t}CF=C{F}_2$ wherein t is zero or 1, R.sub.10 complies with one of the following formulae: (R.sub.10-i) (CF.sub.2).sub.d(O).sub.e(CF.sub.2O).sub.fR.sub.CF(O).sub.e*(CF.sub.2).sub.d*(CF.sub.2O).sub.f* wherein each of d, d*, e, e*, f and f* is independently zero or 1 and R.sub.CF is a perfluoroalkyl chain comprising from 1 to 12, optionally interrupted by one or more oxygen atoms $\begin{array}{cc}O{\left(C_3{F}_{6}O\right)}_h{\left({\mathrm{CF}}_2\right)}_i{\left(C_3{F}_{6}O\right)}_{j}O& \left(R_{10}-\mathrm{ii}\right)\end{array}$ wherein h=j and h+j is from 2 to 6, and i is from 2 to 6.

14. The process (P) according to claim 11, said process (P) comprising: before step (a), a step of partial reduction of the peroxid bonds in the PFPE peroxy, and/or after step (c), step (d) of removal of the solvent and/or step (e) of fractionation.

15. A composition (CL) comprising the block copolymer (P) as defined in claim 1, at least one base oil selected from the group consisting of partially fluorinated, fully fluorinated and hydrogenated base oils, provided that said base oil is capable of forming a solution with the block copolymer (P), and optionally at least one additive selected from thickening agents, antirust agents, antioxidants, thermal stabilizers, pour-point depressants, anti-wear agents, dispersants, tracers, dyestuffs, talc and inorganic fillers.

16. A method for lubricating at least one surface of at least one article, said method comprising contacting said block copolymer (P) as defined in claim 1, with said at least one surface.

17. The method of claim 16, wherein said article is selected from pumps for use in oil and gas applications, rotary machines; electrical connectors; bearings of fan clutches or cooling fans; and heavy duty truck automatic clutches.

18. A method for counteracting vibrations and/or shocks in a device, said method comprising providing an apparatus comprising a damper device, said damper device comprising at least one block copolymer (P) as defined in claim 1.

Description

DESCRIPTION OF EMBODIMENTS

[0060] For the purpose of the present description and of the following claims: [0061] the use of parentheses around symbols or numbers identifying the formulae, for example in expressions like polymer (P), etc., has the mere purpose of better distinguishing the symbol or number from the rest of the text and, hence, said parenthesis can also be omitted; [0062] the acronym PFPE stands for (per)fluoropolyether and, when used as substantive, is intended to mean either the singular or the plural form, depending on the context; [0063] the term (per)fluoropolyether is intended to indicate a fully or partially fluorinated polyether polymer.

[0064] Preferably, in copolymer (P), the first PFPE chain, the second PFPE chain, A, A{circumflex over ()}, C{circumflex over ()} are the same or different from each other.

[0065] Preferably, said perfluorinated alkyl groups are the same or different from each other.

[0066] Preferably, said perfluorinated alkyl group is a linear perfluoroalkyl group comprising from 1 to 3 carbon atoms.

[0067] Preferably, in copolymer (P), said at least one first PFPE chain is bonded to said at least one block of formula (I) via a sigma bond or a group selected from CF.sub.2, CF.sub.2CF.sub.2 or O.

[0068] Preferably, in copolymer (P), said second PFPE chain is bonded to said at least one block of formula (I) via a sigma bond or a group selected from CF.sub.2, CF.sub.2CF.sub.2 or O.

[0069] Preferably, in copolymer (P), (A) and (B) in formula (I) are linked via a sigma bond or a group selected from O, CF.sub.2 or CF.sub.2CF.sub.2.

[0070] Preferably, in copolymer (P), each of said first PFPE chain, second PFPE chain, A in formula (I) and said A{circumflex over ()} and C{circumflex over ()} in formula (IV) is a partially or fully fluorinated chain [chain (R.sub.f)] comprising, preferably consists of, repeating units being independently selected from the group consisting of: [0071] (Rf-i) CFXO, wherein X is F or CF.sub.3; [0072] (Rf-ii) CFXCFXO, wherein X, equal or different at each occurrence, is F or CF.sub.3, with the proviso that at least one of X is F; [0073] (Rf-iii) CF.sub.2CF.sub.2CW.sub.2O, wherein each of W, equal or different from each other, are F, Cl, H; [0074] (Rf-iv) CF.sub.2CF.sub.2CF.sub.2CF.sub.2O; [0075] (Rf-v) (CF.sub.2).sub.jCFZO wherein j is an integer from 0 to 3 and Z is a group of general formula OR.sub.(f-a)T, wherein R.sub.(f-a) is a fluoropolyoxyalkene chain comprising a number of repeating units from 0 to 10, said recurring units being chosen among the following: CFXO, CF.sub.2CFXO, CF.sub.2CF.sub.2CF.sub.2O, CF.sub.2CF.sub.2CF.sub.2CF.sub.2O, with each of X being independently F or CF.sub.3 and T being a C.sub.1-C.sub.3 perfluoroalkyl group.

[0076] Preferably, said chain (R.sub.f) complies with the following formula:

[00006]$\begin{array}{cc}-\left[{\left(CF{X}^{1}O\right)}_{g1}{\left(CF{X}^{2}CF{X}^{3}O\right)}_{g2}{\left(C{F}_{2}C{F}_{2}C{F}_{2}O\right)}_{g3}{\left(C{F}_{2}C{F}_{2}C{F}_{2}C{F}_{2}O\right)}_{g4}\right]-& \left(R_f-I\right)\end{array}$

wherein [0077] X.sup.1 is independently selected from F and CF.sub.3, [0078] X.sup.2, X.sup.3, equal or different from each other and at each occurrence, are independently F, CF.sub.3, with the proviso that at least one of X is F; [0079] g1, g2, g3, and g4, equal or different from each other, are independently integers 0, such that g1+g2+g3+g4 is in the range from 2 to 1000; should at least two of g1, g2, g3 and g4 be different from zero, the different recurring units are generally statistically distributed along the chain.

[0080] More preferably, chain (R.sub.f) is selected from chains of formula:

[00007]$\begin{array}{cc}-\left[{\left(C{F}_{2}C{F}_{2}O\right)}_{a1}{\left(C{F}_{2}O\right)}_{a2}\right]-& \left(R_f-\mathrm{IIA}\right)\end{array}$

wherein: [0081] a1 and a2 are independently integers0 such that the number average molecular weight is between 1,000 and 100,000; both a1 and a2 are preferably different from zero, with the ratio a1/a2 being preferably comprised between 0.1 and 10;

[00008]$\begin{array}{cc}\left[{\left({\mathrm{CF}}_2{\mathrm{CF}}_{2}O\right)}_{b1}{\left(C{F}_{2}O\right)}_{b2}{\left(CF\left(C{F}_3\right)O\right)}_{b3}{\left(C{F}_{2}CF\left(C{F}_3\right)O\right)}_{b4}\right]& \left(R_f-\mathrm{IIB}\right)\end{array}$

wherein: [0082] b1, b2, b3, b4, are independently integers0 such that the number average molecular weight is between 1,000 and 100,000; preferably b1 is 0, b2, b3, b4 are >0, with the ratio b4/(b2+b3) being 1;

[00009]$\begin{array}{cc}\left[{\left({\mathrm{CF}}_{2}C{F}_{2}O\right)}_{c1}{\left(C{F}_{2}O\right)}_{c2}{\left(C{F_2\left({\mathrm{CF}}_2\right)}_{\mathrm{cw}}{\mathrm{CF}}_{2}O\right)}_{c3}\right]& \left(R_f-\mathrm{IIC}\right)\end{array}$

wherein: [0083] cw=1 or 2; [0084] c1, c2, and c3 are independently integers0 chosen so that the number average molecular weight is between 1,000 and 100,000; preferably c1, c2 and c3 are all >0, with the ratio c3/(c1+c2) being generally lower than 0.2.

[0085] Still more preferably, chain (R.sub.f) complies with formula (R.sub.fIII) here below:

[00010]$\begin{array}{cc}\left[{\left(C{F}_{2}C{F}_{2}O\right)}_{a1}{\left(C{F}_{2}O\right)}_{a2}\right]& \left(R_f-\mathrm{III}\right)\end{array}$

wherein: [0086] a1, and a2 are integers >0 such that the number average molecular weight is between 1,000 and 100,000 with the ratio a1/a2 being generally between 0.1 and 10, more preferably between 0.2 and 5.

[0087] Preferably, in formula (II), n is an integer equal to 1 or 2, more preferably 1.

[0088] Preferably, in formula (II), at least one of substituents R.sub.1 to R.sub.4 is a group of formula (III) and the other substituents are each independently selected from a fluorine atom or a perfluorinated alkyl chain having from 1 to 3 carbon atoms, more preferably a fluorine atom or a perfluorinated alkyl chain having 1 carbon atoms.

[0089] According to one embodiment, in formula (III), t is 0.

[0090] According to another embodiment, in formula (III), t is 1 and [0091] R.sub.10 complies with one of the following formulae:

[00011]$\begin{array}{cc}{\left({\mathrm{CF}}_2\right)}_d{\left(O\right)}_e{\left(C{F}_{2}O\right)}_f{R_{\mathrm{CF}}\left(O\right)}_{e^{}}{\left(C{F}_2\right)}_{d^{}}{\left(C\mathrm{F2O}\right)}_{f^{}}& \left(R_{10}-i\right)\end{array}$

wherein [0092] each of d, d*, e, e*, f and f* is independently zero or 1 and [0093] R.sub.CF is a perfluoroalkyl chain comprising from 1 to 12, preferably from 1 to 8 carbon atoms, optionally interrupted by one or more oxygen atoms

[00012]$\begin{array}{cc}O{\left(C_3{F}_{6}O\right)}_h{\left({\mathrm{CF}}_2\right)}_i{\left(C_3{F}_{6}O\right)}_{j}O& \left(R_{10}-\mathrm{ii}\right)\end{array}$

wherein h=j and h+j is from 2 to 6, and i is from 2 to 6.

[0094] According to this embodiment, preferably R.sub.10 complies with formula:

[00013]$\begin{array}{cc}{\left({\mathrm{CF}}_2\right)}_d{\left(O\right)}_e{\left(C{F}_{2}O\right)}_f{R_{CF}\left(O\right)}_{e^{}}{\left(C{F}_2\right)}_{d^{}}{\left(C\mathrm{F2O}\right)}_{f^{}}& \left(R_{10}-i\right)\end{array}$

wherein [0095] d, f, d* and f* are zero, [0096] e and e* are 1, and [0097] R.sub.CF is a linear perfluoroalkyl chain comprising from 1 to 10, preferably from 1 to 8 carbon atoms

[0098] Preferably, in formula (III), z is equal to 1 and R.sub.10 is an oxygen atom or a bivalent perfluorinated alkyl chain comprising from 1 to 24 carbon atoms, optionally interrupted by and/or comprising at least one oxygen atom.

[0099] Preferably, in formula (III), one of substituents R.sub.11 and R.sub.12 is a group of formula (IV) and the other substituent is selected from a fluorine atom or a perfluorinated alkyl chain having from 1 to 3 carbon atoms, more preferably a fluorine atom or a perfluorinated alkyl chain having 1 carbon atoms.

[0100] Preferably, in formula (III), one of substituents R.sub.13 to R.sub.15 is a group of formula (IV) and the other two substituents are independently selected from a fluorine atom or a perfluorinated alkyl chain having from 1 to 3 carbon atoms, more preferably a fluorine atom or a perfluorinated alkyl chain having 1 carbon atoms. More preferably said two substituents are the same and are a fluorine atom.

[0101] Preferably, in formula (IV), a is 1, v is 1 and B{circumflex over ()} is a group of formula [C(R.sup.1{circumflex over ()})(R.sup.2{circumflex over ()})C(R.sup.3{circumflex over ()})(R.sup.4{circumflex over ()})] wherein R.sup.1{circumflex over ()} to R.sup.4{circumflex over ()} each independently are the same as each of R.sub.1 to R.sub.4, respectively.

[0102] Preferably, copolymer (P) is characterized by a complex viscosity, measured at 0.1 rad/s and at 25 C., from 10 Pa*s to 5000 Pa*s.

[0103] According to the present invention, said copolymer (P) is obtained via process (P) as described above.

[0104] Before step (a), the PFPE peroxy can be subjected to partial reduction of the peroxid bonds, for example by chemical reduction or UV treatment or thermal treatment.

[0105] Preferably, said PFPE peroxy is a peroxidic (per)fluoropolyether polymer comprising a (per)fluoropolyether chain having two chain ends, each of said chain ends comprising a (per)fluorinated alkyl chain having from 1 to 3 carbon atoms, optionally containing one or more chlorine atoms or functional end groups selected from acyl fluoride, fluoroformate and ketones, said chain ends being bonded to opposite sides of said (per)fluoropolyether chain, said (per)fluoropolyether chain comprising, preferably consisting of, repeating units being independently selected from the group consisting of formulae (Rf-i) to (Rf-v) as above defined and having a peroxidic content (PO), defined as grams of active oxygen (Mw=16) in 100 g of PFPE peroxy between 0.1 and 4, preferably between 0.1 and 3.5.

[0106] Preferably, in said compound of formula (III-p), when t is 1, the two, three or four unsaturated moieties are bonded to the same or different atoms, preferably carbon atoms, belonging to R.sub.10.

[0107] Preferably, said at least one compound of formula (III-p) complies with the following formula:

[00014]$C{F}_2=C{F\left(R_{10}\right)}_{t}CF=C{F}_2$

wherein [0108] t is zero or 1, [0109] R.sub.10 complies with one of the following formulae:

[00015]$\begin{array}{cc}{\left({\mathrm{CF}}_2\right)}_d{\left(O\right)}_e{\left(C{F}_{2}O\right)}_f{R_{CF}\left(O\right)}_{e^{}}{\left(C{F}_2\right)}_{d^{}}{\left(C\mathrm{F2O}\right)}_{f^{}}& \left(R_{10}-i\right)\end{array}$

wherein [0110] each of d, d*, e, e*, f and f* is independently zero or 1 and [0111] R.sub.CF is a perfluoroalkyl chain comprising from 1 to 12, preferably from 1 to 8 carbon atoms, optionally interrupted by one or more oxygen atoms

[00016]$\begin{array}{cc}O{\left(C_3{F}_{6}O\right)}_h{\left({\mathrm{CF}}_2\right)}_i{\left(C_3{F}_{6}O\right)}_{j}O& \left(R_{10}-\mathrm{ii}\right)\end{array}$

wherein h=j and h+j is from 2 to 6, and i is from 2 to 6.

[0112] Preferably, said compound of formula (III-p) is selected from the group comprising, more preferably consisting of:

[00017]$C{F}_2=CFOCF=C{F}_2$$C{F}_2=CFC{F}_{2}OC{F}_{2}CF=C{F}_2$$C{F}_2=CFO-{\left(C{F}_2\right)}_{3}CF=C{F}_2$$C{F}_2=CFC{F}_2{O\left(C{F}_2\right)}_{3}OC{F}_{2^{-}}CF=C{F}_2$$C{F}_2=CFC{F}_{2}CF=C{F}_2$$C{F}_2=C{F\left(C{F}_2\right)}_{2}CF=C{F}_2$$C{F}_2=C{F\left(C{F}_2\right)}_{3}CF=C{F}_2$$C{F}_2=C{F\left(C{F}_2\right)}_{4}CF=C{F}_2$$C{F}_2=CFOC{F}_{2}OCF=C{F}_2$$C{F}_2=CF{O\left(C{F}_2\right)}_{2}OCF=C{F}_2$$C{F}_2=CF{O\left(C{F}_2\right)}_{3}OCF=C{F}_2$$C{F}_2=CF{O\left(C{F}_2\right)}_{4}OCF=C{F}_2$$C{F}_2=C{F\left(C{F}_2\right)}_{2}OCF=C{F}_2$$C{F}_2=C{F\left(C{F}_2\right)}_{3}OCF=C{F}_2$$C{F}_2=C{F\left(C{F}_2\right)}_{4}OCF=C{F}_2$$C{F}_2=CFC{F}_2{O\left(C{F}_2\right)}_{2}OC{F}_{2}O-CF=C{F}_2$$C{F}_2=CFC{F}_2{O\left(C{F}_2\right)}_{3}OC{F}_{2}O-CF=C{F}_2$$C{F}_2=CFC{F}_2{O\left(C{F}_2\right)}_{4}OC{F}_{2}OCF=C{F}_2$$C{F}_2=CFC{F}_2{O\left(C{F}_2\right)}_{6}OC{F}_{2}CF=C{F}_2$$C{F}_2=CFO-C{F}_{2}O-{\left(C{F}_2\right)}_{2}O-C{F}_{2}O-CF=C{F}_2$$C{F}_2=CFO-C{F}_{2}O-{\left(C{F}_2\right)}_{3}O-C{F}_{2}O-CF=C{F}_2$$C{F}_2=CFO-C{F}_{2}O-{\left(C{F}_2\right)}_{4}O-C{F}_{2}O-CF=C{F}_2$$C{F}_2=CFO-{\left(C{F}_{2}O\right)}_{6^{-}}CF=C{F}_2$$C{F}_2=CFO-{\left(C{F}_{2}C{F}_{2}O\right)}_{2^{-}}CF=C{F}_2$$C{F}_2=CFO-{\left(C{F}_{2}C{F}_{2}O\right)}_{2^{-}}C{F}_{2}OCF=C{F}_2$$C{F}_2=CF{O\left(C_3{F}_{6}O\right)}_{h^{-}}{\left(C{F}_2\right)}_{i^{-}}{\left(C_3{F}_{6}O\right)}_{j^{-}}OCF=C{F}_2$

wherein h and j are the same and [0113] their sum is from 2 to 6 and i is from 2 to 6.

[0114] According to a particularly preferred embodiment, said at least one compound of wherein formula (III-p) complies with the following formula:

[00018]$C{F}_2=C{F\left(R_{10}\right)}_{t}CF=C{F}_2$

wherein t is 1 and [0115] R.sub.10 complies with formula:

[00019]$\begin{array}{cc}{\left({\mathrm{CF}}_2\right)}_d{\left(O\right)}_e{\left(C{F}_{2}O\right)}_f{R_{CF}\left(O\right)}_{e^{}}{\left(C{F}_2\right)}_{d^{}}{\left(C\mathrm{F2O}\right)}_{f^{}}& \left(R_{10}-i\right)\end{array}$

wherein [0116] d, f, d* and f* are zero, [0117] e and e* are 1, and [0118] R.sub.CF is a linear perfluoroalkyl chain comprising from 1 to 10, preferably from 1 to 8 carbon atoms.

[0119] Preferably, in step (a), the amount of the compound of formula (III-p) is less than 3 wt. %, even more preferably less than 1 wt. %, of the amount of the PFPE peroxy.

[0120] It will be easily understood by those skilled in the art, that as the reaction proceeds and copolymer (P) is obtained, the unsaturated moieties in compound of formula (III-p) become saturated moieties in copolymer (P), such that substituents R.sub.21 to R.sub.23 in formula (III-p) become substituents R.sub.1 to R.sub.3 in formula (III) of copolymer (P), substituent R.sub.31 become any of substituents R.sub.11 or R.sub.12 in formula (III) and substituents R.sub.32 and R.sub.33 become any of substituents R.sub.13 to R.sub.15 in formula (III) of copolymer (P).

[0121] Step (a) and step (b) can be performed in the presence of a fluorinated solvent. Preferably said fluorinated solvent is selected in the group comprising: perfluorocarbons, hydrofluorocarbons, perfluoropolyethers, hydrofluoropolyethers.

[0122] Preferably, step (b) is performed in the presence of UV radiation for a time from 2 to 60 hours.

[0123] Preferably, step (b) is performed in the presence of UV radiation at a temperature from 60 C. to +60 C., more preferably from 20 C. to +40 C. and even more preferably from 0 C. to 30 C.

[0124] As an alternative, step (b) can be performed under thermal treatment, preferably by heating at a temperature from 100 C. to 250 C.

[0125] It will be clear to those skilled in the art that the polymer obtained at the end of step (b) has a peroxide content (PO) lower than 0.05, preferably lower than 0.001.

[0126] Preferably, said step (c) is performed by treating with fluorine in the presence of anhydrous nitrogen flow.

[0127] Preferably, said process (P) comprises after step (c), step (d) of removal of the solvent and/or step (e) of fractionation.

[0128] Said step (d) of removal of the solvent can be carried out by evaporation, for example by distillation under vacuum.

[0129] Said step (e) of fractionation can be performed via solvent extraction, using supercritical CO.sub.2, hexafluoroxylene or hydrofluorocarbons as solvents, and mixtures thereof when the fractionation step is performed via precipitation fractionation. Supercritical CO.sub.2 is preferred.

[0130] As explained above, purification steps can be performed after step or step (d), it will be clear to those skilled in the art that the copolymers (P) according to the present invention are obtained at the end of step (c) or of step (d) of process (P) as mixture (P), wherein copolymers (P) characterized by different viscosities and/or molecular weight and/or substituents are present.

[0131] Copolymer (P) is advantageously used as lubricant, notably for application in harsh environments, for example subjected to a wide range of working temperatures.

[0132] Copolymer (P) or mixture (P) can be used as such, or in admixture with additive(s) known to the person skilled in the art of lubrication, so that a composition [composition (CL)] is obtained.

[0133] For example, composition (CL) can comprise other suitable lubricants as base oil, such base oil being selected in the group comprising partially fluorinated, fully fluorinated and hydrogenated base oils, provided that said base oil is capable of forming a solution with copolymer (P).

[0134] Non-limiting examples of fully fluorinated lubricant base oils are those identified as compounds (1)-(8) in EP 2100909 A (SOLVAY SOLEXIS S.p.A.).

[0135] For example, suitable additives are selected from thickening agents, antirust agents, antioxidants, thermal stabilizers, pour-point depressants, anti-wear agents, including those for high pressures, dispersants, tracers, dyestuffs, talc and inorganic fillers.

[0136] Examples of thickening agents are talc, silica, boron nitride, polyureas, alkali or alkali-earth metals terephthalates, calcium and lithium soaps and complexes thereof and PTFE (polytetrafluoroethylene); among them, PTFE is preferred.

[0137] Examples of dispersants are, for example, surfactants, preferably non-ionic surfactants, more preferably (per)fluoropolyether surfactants and (per)fluoroalkyl surfactants.

[0138] If required by the application, solvents can also be used.

[0139] Examples of solvents are fluorinated or partially fluorinated solvents, such as Galden PFPEs, Novec HFEs and other organic solvents like fluoro-alkane, fluoro-aromatic compound, fluoroalkyl ether, fluoroalkyl amine, fluoro-alcohol, ketone such as methyl-ethyl-ketone, alcohol such as isopropyl alcohol, ester such as butylacetate, hydrofluorocarbons, and the like.

[0140] The article that can benefit from the lubricant properties of copolymer (P), mixture (P) or composition (CL) according to the present invention is not particularly limited.

[0141] Said article preferably comprises at least one metal surface.

[0142] Examples of said article are pumps for use in oil and gas applications, such as electrical submersible pump and the like, rotary machines, such as steam turbines and gas turbines; electrical connectors; bearings of fan clutches or cooling fans; or heavy duty truck automatic clutches, more particularly bearings of said clutches.

[0143] Copolymer (P), mixture (P) or composition (CL) according to the present invention can be advantageously used as damper fluids in a damping device.

[0144] Thus, in a further aspect, the present invention relates to a method for counteract vibrations and/or shocks in a device, said method comprising providing an apparatus comprising a damper device, said damper device comprising at least one copolymer (P), mixture (P) or composition (CL) as defined above.

[0145] Should the disclosure of any patents, patent applications, and publications which are incorporated herein by reference conflict with the description of the present application to the extent that it may render a term unclear, the present description shall take precedence.

[0146] The invention will be now described in connection with the following examples, whose purpose is merely illustrative and not intended to limit the scope of the invention.

EXPERIMENTAL SECTION

Materials

[0147] Peroxidic perfluoropolyether oil having formula

[00020]$TO{\left({\mathrm{CF}}_{2}C{F}_{2}O\right)}_m{\left(C{F}_{2}O\right)}_n{\left(O\right)}_h{T}^{}$ [0148] number average molecular weight (Mn)=48600 g/mol, [0149] m/n=1.0 and PO=1.65%

[00021]$T,T^{}={\mathrm{CF}}_3\left(83\%\right),C\left(=O\right)F\left(6\%\right),{\mathrm{CF}}_{2}C\left(=O\right)F\left(11\%\right)$

was obtained by Solvay Specialty Polymers Italy S.p.A.

[0150] Galden HT200 were obtained by Solvay Specialty Polymers Italy S.p.A.

[0151] Perfluoro(bis vinyl ether) (PBVE) was obtained by Anles Ltd.

[0152] Hexafluorobenzene was obtained by Sigma Aldrich.

Methods

19F-NMR Spectroscopy:

[0153] Varian Mercury 200 MHz spectrometer working for the fluorine nucleus was used to obtain the structure, the number average molecular weight and the composition of the PFPE oils reported in the following examples. The .sup.19F-NMR spectrum was obtained on pure samples using CFCl.sub.3 as internal reference. Hexafluorobenzene was also used as solvent.

Determination of the Peroxidic Content (PO):

[0154] The peroxidic content (PO) is expressed as grams of peroxidic oxygen per 100 g of polymer. The analysis of the peroxide content was carried out by iodometric titration using a Mettler DL40 device equipped with platinum electrode. The sensitivity limit for the PO determination was 0.0002%.

Determination of the Complex Viscosity:

[0155] The complex viscosity was measured with frequency sweep tests using an MCR502 Anton-Paar rheometer with parallel plate geometry (25 mm diameter) according to ISO 6721 part 10.

Gel Permeation Chromatography (GPC):

[0156] The analysis was performed with Mixed CCD column with a Waters 410 refractometer detector using HFE7100 as eluent.

Example 1Synthesis of Copolymer (P-1)

[0157] The reaction was performed using a 1000 mL cylindrical photochemical glass reactor equipped with a high-pressure mercury lamp (HANAU TQ150) enclosed in a quartz cylinder, a magnetic stirrer, a thermocouple and a condenser.

[0158] 200.3 g of the starting peroxidic perfluoropolyether oil were charged in the photochemical reactor together with 1501 g of Galden HT200 and 1.30 g of PBVE and stirred thoroughly to obtain a homogenous mixture. The reaction mixture was then cooled down to about 10 C. with an ice/water bath and nitrogen was purged into the system at a rate of 1.0 NI/h. The UV lamp was switched on.

[0159] After 55 hours of irradiation, the lamp was switched off and the reaction mixture was transferred into a second glass reactor and fluorinated at 40 C. with 1.0 NI/h of fluorine gas for a total of 24 hours in the presence of UV radiation. .sup.19F-NMR analysis confirmed the complete fluorination of the product and the absence of CF.sub.2COF and COF terminals at the chain ends.

[0160] The obtained solution was distilled at 240 C. for 4 h in a round bottom flask equipped with a magnetic stirrer in order to remove the solvent.

[0161] The distillation was conducted first at atmospheric pressure, then under reduced pressure (0.1 mbar) until complete removal of the solvent.

[0162] 163.6 g of copolymer (P-1) in the form of a clear viscous oil were obtained as residue, which was analyzed by iodometric titration to confirm the complete removal of the peroxide units.

[0163] .sup.19F-NMR analysis confirmed the absence of residual peroxide. Polymer (P-1) had m/n=1.0 and T, T=CF.sub.3.

Example 2Synthesis of Comparative Polymer (C-1{circumflex over ()}) without PBVE

[0164] The same photochemical apparatus and peroxidic perfluoropolyether precursor as Example 1 were adopted for this comparative example.

[0165] 199.9 g of the starting peroxidic perfluoropolyether oil were charged in the photochemical reactor together with 1502 g of Galden HT200 and stirred thoroughly to obtain a homogenous mixture.

[0166] The synthesis then proceeded as described in Example 1. .sup.19F-NMR analysis confirmed the complete fluorination of the product and the absence of CF.sub.2COF and COF terminals at the chain ends.

[0167] Distillation was also performed as described in Example 1.

[0168] 172.4 g of comparative polymer (C-1{circumflex over ()}) were obtained in the form of a clear viscous oil were obtained as residue, which was analyzed by iodometric titration to confirm the complete removal of the peroxide units.

[0169] .sup.19F-NMR analysis confirmed the absence of residual peroxide. Comparative copolymer (C-1{circumflex over ()}) had m/n=1.0 and T, T=CF.sub.3.

TABLE-US-00001 TABLE 1 Complex Viscosity viscosity (at index Mn Mw 0.1 rad/s and (ASTM g/mol g/mol Mw/M 25 C.) D2270) Copolymer 52100 323000 6.2 57.5 Pa*s 559 mm.sup.2/s (P-1) Comparative 24000 63000 2.6 5.6 Pa*s 380 mm.sup.2/s polymer (C-1{circumflex over ()})

[0170] The increased molecular weight distribution and complex viscosity of copolymer (P-1) according to the present invention confirmed the chain extension with respect to the comparative polymer (C-1{circumflex over ()}).