Method for Treating Water to Reduce the Dissolved Silica Content Thereof

Abstract

Method for treating water to reduce the dissolved silica content thereof, the method being characterised in that it comprises at least one step of adsorbing the dissolved silica, the step consisting in passing the water through a reactor housing an adsorbent granular material consisting of grains of iron hydroxide (III) and/or iron oxyhydroxide (III) and at least one step of regenerating the adsorbing power of the granular material, the step consisting in bringing the granular material into contact with a base and at least one chloride.

Claims

1-9, (Canceled)

10. A method for treating water in order to reduce the dissolved silica content thereof, characterised in that it comprises at least one step of adsorbing said dissolved silica, the step comprising passing said water through a reactor containing an adsorbent granular material including grains of iron hydroxide (III) or iron oxyhydroxide (III) and at least one step of regenerating adsorbing power of said granular material, the step including bringing said granular material into contact with a base and at least one chloride.

11. The method according to claim 10 characterised in that at least part of said adsorbent granular material is in the form of akaganeite.

12. The method according to claim 11 characterised in that said granular material comprises at least 5% by weight of akaganeite.

13. The method according to claim 10, characterised in that said regeneration step is carried out with two regeneration solutions, one containing said base, the other containing said chloride.

14. The method according to claim 10, characterised in that said base is selected from the group consisting of NaOH, KOH, NH.sub.4OH, LiOH.

15. The method according to claim 10 characterised in that said chloride is selected from the group consisting of NaCl, KCl, LiCl, NH.sub.4Cl, MgCl.sub.2, CaCl.sub.2, BaCl.sub.2, MnCl.sub.2.

16. The method according to claim 10 characterised in that said granular material is used in the form of a fixed bed and said adsorption step is carried out with a volume load comprised between 5 and 30 cubic metres of water passing per cubic metre of granular material and per hour.

17. The method according to claim 10 characterised in that said grains of iron hydroxide (III) or iron oxyhydroxide (III) have a size comprised between 0.2 mm and 5 mm.

18. A method of treating water containing dissolved silica and removing the dissolved silica from the water, comprising: directing the water containing dissolved silica into a reactor containing an adsorbent granular material including iron hydroxide (III) or iron oxyhydroxide (III); passing the water containing the dissolved silica through the reactor and contacting the water with said adsorbent granular material; reducing the concentration of dissolved silica in the water by adsorbing the silica in the water onto the adsorbent granular material, thereby forming treated water; directing the treated water from the reactor; at selected times, regenerating the adsorbent granular material by: employing a regeneration solution containing a base and chloride ions; ceasing to flow the water through the reactor; directing the regeneration solution through the reactor and through the adsorbent granular material therein; transferring silica adsorbed onto the absorbent granular material to the regeneration solution; and directing the regeneration solution containing the silica from the reactor.

19. The method of claim 18 wherein the adsorbent granular material includes akaganeite.

20. The method of claim 19 wherein said adsorbent granular material comprises at least 5% by weight of akaganeite.

21. The method of claim 18 including forming the regeneration solution by mixing a base solution with a chloride solution.

22. The method of claim 18 including forming the regeneration solution by mixing a sodium hydroxide solution with a sodium chloride solution.

23. The method of claim 18 wherein the base solution includes NaOH, KOH, NH4OH, or LiOH.

24. The method of claim 23 wherein the chloride solution comprises NaCl, KCl, LiCl, NH4Cl, MgCl.sub.2, CaCl.sub.2, BaCl.sub.2, or MnCl.sub.2.

25. The method of claim 18 including controlling the flow of water through the reactor such that 5-30 cubic meters of water per cubic meter of granular material passes through the reactor per hour.

26. The method of claim 18 including monitoring the concentration of the dissolved silica in the treated water and when the concentration of the dissolved silica in the treated water reaches a threshold value, ceasing the flow of water through the reactor and thereafter directing the regeneration solution through the reactor so as to regenerate the granular material.

Description

BRIEF DESCRIPTION OF THE FIGURES

[0029] The invention, as well as the various advantages that it has will be better understood thanks to the following description of an embodiment thereof given with reference to the drawings wherein: [0030] FIG. 1 is a schematic view of an installation for implementing the method according to the invention; [0031] FIG. 2 is a graph indicating the evolution of the adsorbing power of the granular bed of the installation according to FIG. 1 after a regeneration step according to the invention (upper curve) and two regeneration steps outside the invention (two lower curves).

[0032] DESCRIPTION OF EMBODIMENTS

[0033] With reference to FIG. 1, a water treatment installation comprises a tank 1 of water to be treated, a reactor 2 containing the adsorbent granular material 3, a tank of treated water 4 and a tank of regeneration solution 5.

[0034] The tank of water to be treated 1 is connected by a pipe 1a equipped with a valve 1b at the upper part of the reactor 2, and the tank of treated water 4 is connected to the lower part of the reactor 2 by a pipe a equipped with a valve 4b.

[0035] The tank of regeneration solution 5 is connected to the lower part of the reactor 2 by a pipe 5a equipped with a valve 5b and a pump 5c and the upper part of the reactor 2 is connected by a recycling pipe 5e to this tank of regeneration solution 5. Finally, this tank of regeneration solution 5 comprises an evacuation pipe 5d.

[0036] It will be noted that the height of the granular adsorbent bed 3 in the reactor 2 may vary according to the embodiments and that it will generally be comprised between 0.5 m and 2 m.

[0037] The granular bed 3 is composed of grains of 0.2 mm to 5 mm of iron oxyhydroxide containing at least 5% by weight of akaganeite.

[0038] To treat the water contained in the tank 1 in order to reduce the dissolved silica content, the valves 1b and 4b are open so as to allow said water to flow through the pipe 1a into the reactor 2 in a downward flow and thus come into contact with the adsorbent granular material 3. The treated water is collected in the tank 4 through the pipe 4a. It will be noted that in other embodiments, it could just as well be considered to pass the water to be treated through the reactor in an upward flow.

[0039] This adsorption step is carried out with a volume load comprised between 5 and 30 BV/h (“bed volume per hour”), that is to say between 5 and 30 cubic metres of water passing per cubic metre of granular bed and per hour.

[0040] During the implementation of the adsorption step, the granular adsorbent bed gradually becomes loaded with silica and its adsorbing power decreases.

[0041] According to the embodiments, it may therefore be considered to monitor the concentration of dissolved silica remaining in the treated water collected in the tank 4 or to opt to limit the adsorption step to a predetermined time.

[0042] Once the adsorbent bed is considered to have an adsorption capacity below a given threshold or to have operated long enough, the valves 1b and 4b are closed so as to interrupt the passage of water to be treated into the reactor.

[0043] A step of regenerating the adsorbing power of the granular bed 3 can then be implemented.

[0044] To this end, a regeneration medium is produced. In the context of the present example, a 1 N sodium hydroxide solution NaOH was used wherein 50 g/L of 0.86 N sodium chloride NaCl were dissolved.

[0045] The valve 5b is then open and the pump 5c which is operated to inject this regeneration solution into the adsorbent granular bed 3. The regeneration solution then passes through the granular bed and is recovered in the upper part of the reactor 2 via the recycling pipe 5e which allows said regeneration solution to be redirected to the tank 5. During this regeneration step, the silica adsorbed on the iron oxyhydroxide grains containing at least 5% by weight of akaganeite, is transferred into the regeneration solution.

[0046] At the end of this step, the pump 5c is turned off and the valve 5b is closed, then the valves 1b and 4b are re-opened to start a new adsorption step.

[0047] Several cycles containing an adsorption step and a regeneration step can thus take place using the same regeneration solution. Said regeneration solution gradually becomes loaded with silica and when its silica concentration is considered too high and/or at the end of a predetermined number of such cycles, the consumed regeneration solution can be discharged through the pipe 5d and be completely or partially replaced by a new regeneration solution.

[0048] Thus, the method according to the invention is not very reagent hungry (base and chloride).

[0049] By way of comparison, a regeneration solution containing no chloride but containing only 1N NaOH was used, at 20° C. and at 50° C.

[0050] In the graph of FIG. 2 are plotted on the abscissa the volume load in BV/h and on the ordinate the adsorbing power of the adsorbent granular bed in milligrams of SiO.sub.2 per gram of adsorbent material.

[0051] On this graph, the upper curve shows the adsorbing power of the granular bed after regeneration according to the invention with the regeneration medium described above made from 1N NaOH and 50 g/L of NaCl at 20° C., while the two lower curves reflect the adsorbing power of an identical granular bed after regeneration with a regeneration medium containing 1N NaOH but not containing chloride, at 20° C. (lower curve) and at 50° C. (median curve).

[0052] According to this graph, the regeneration of the adsorbent bed is notably better when, according to the invention, chloride ions are present in the regeneration solution. Even by heating the regeneration solution containing only NaOH at 50° C., the regeneration performance of the adsorbent bed remains lower than that observed with the regeneration solution produced, according to the invention, from NaOH and NaCl.

[0053] The method according to the present embodiment was carried out with a water to be treated containing 300 mg of dissolved silica per litre. The amount of silica adsorbed on the adsorbent material was measured after the first, seventh and eighth regeneration cycle with the regeneration solution containing chloride and base. The results are given in Table 1 below. These results also show that, unexpectedly, the adsorbing power of the granular material increases with the number of regeneration cycles recommended according to the invention. These tests were repeated and the same surprising result was obtained, highlighting a probable and continual activation and/or development of new adsorption sites on the material, induced by this mode of regeneration. A method according to the invention applied to a water to be treated containing a dissolved silica concentration comprised between 70 mg(SiO.sub.2)/L and 100 mg(SiO.sub.2)/L also showed an increase in the adsorbing power of the granular material with the number of regeneration cycles according to the invention, with values close to those presented in Table 1.

TABLE-US-00001 TABLE 1 Number of milligrams of adsorbed % by weight of silica regeneration silica per gram of adsorbed on the cycles adsorbent material granular material 1 10.72 71 7 11.63 78 8 12.44 83