METHOD OF ANALYZING SINTERED DENSITY OF URANIUM OXIDE (UOX) USING SPECTROPHOTOMETER

Abstract

Disclosed is a method of predicting, calculating, or analyzing the sintered density of uranium oxide (UO.sub.x) before uranium oxide is added in the pelletizing process during a process of manufacturing nuclear fuel, the method including measuring the chromaticity of ammonium diuranate using a spectrophotometer. The present invention provides a simple and highly reliable method of predicting the sintered density of uranium oxide (UO.sub.x), which overcomes the problem with a conventional technology where the sintered density of uranium oxide (UO.sub.x) can be analyzed only in a pellet state and a subsequent treatment process needs to be performed according to the analysis result.

Claims

1. A method of calculating a sintered density of a powder for use in a uranium oxide (UO.sub.x) pellet for nuclear fuel during a manufacturing process of the powder for use in the uranium oxide (UO.sub.x) pellets for the nuclear fuel, the method comprising: (1) measuring a chromaticity of an ammonium diuranate powder, which is a measurement target, using a spectrophotometer; (2) comparing a measured chromaticity data value to a standard chromaticity graph value of the ammonium diuranate powder; and (3) calculating a predicted uranium oxide (UO.sub.x) sintered density of the ammonium diuranate powder, which is the measurement target, using the comparing.

2. The method of claim 1, wherein the chromaticity data value is obtained using a L* color coordinate system.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0013] The above and other objects, features and advantages of the present invention will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawings, in which:

[0014] FIG. 1 is a flowchart showing the procedure of calculating the sintered density of uranium oxide (UO.sub.x) powder;

[0015] FIGS. 2A and 2B are respective pictures of ammonium diuranate powder and uranium oxide (UO.sub.x) powder;

[0016] FIG. 3 is a graph showing sintered density as a function of a chromaticity value L* measured using a spectrophotometer;

[0017] FIG. 4 is a graph showing sintered density as a function of a chromaticity value measured using the spectrophotometer;

[0018] FIG. 5 is a graph showing sintered density as a function of a chromaticity value b* measured using the spectrophotometer; and

[0019] FIG. 6 is a graph showing the prediction of sintered density based on the relationship between the chromaticity value measured using the spectrophotometer and the sintered density.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0020] Hereinafter, the present invention will be described in detail.

[0021] In order to solve the problems with the conventional method, in the present invention, the chromaticity of ammonium diuranate, generated during precipitation/filtration/drying processes of a wet re-conversion process, is measured using a spectrophotometer, thereby enabling prediction, calculation, and analysis of the sintered density of uranium oxide (UO.sub.x) before the uranium oxide is added to the pelletizing process using the spectrophotometer. The method has been confirmed to have excellent predictive performance.

[0022] Spectrophotometry, as used in the present invention, is very frequently used at present in the chemical, life science, environment, and pharmaceutical fields. Such analysis is based on the measurement of an intrinsic absorption spectrum formed while various molecular motions, such as electron transition and rotation, occur by absorbing light energy depending on the type of material. Absorption spectra and energy value differences between the materials are represented using an * a* b* color coordinate system. The spectrophotometer analysis method is extensively applied to the quantitative or qualitative analysis of organic or inorganic compounds.

[0023] Specifically, the present invention provides a method of calculating the sintered density of a powder for use in a uranium oxide (UO.sub.x) pellet for nuclear fuel during a process of manufacturing the powder for use in the uranium oxide (UO.sub.x) pellets for the nuclear fuel. The method includes (1) measuring the chromaticity of an ammonium diuranate powder, which is a measurement target, using a spectrophotometer, (2) comparing the measured chromaticity data value with a standard chromaticity graph value for ammonium diuranate powder, and (3) calculating a predicted uranium oxide (UO.sub.x) sintered density of the ammonium diuranate powder, which is the measurement target, based on the comparison.

[0024] It is preferable for the chromaticity data value to be obtained using a L* b* color coordinate system.

[0025] It is preferable for the chromaticity data value to be obtained using an L* value of the L* b* color coordinate system.

[0026] A better understanding of the present invention may be obtained through the following Examples. It will be obvious to those skilled in the art that the Examples are set forth to illustrate the present invention but are not to be construed as limiting the scope of the present invention.

EXAMPLE 1

Determination of Standard Chromaticity Graph of Ammonium Diuranate Powder

[0027] First, a graph needs to be determined using standard data in order to predict, calculate, and analyze the sintered density of uranium oxide (UO.sub.x) by measuring the chromaticity value of an ammonium diuranate powder sample, which is the precursor of uranium oxide (UO.sub.x), using a spectrophotometer.

[0028] In the present experiment, during a precipitation process, which is an ammonium diuranate manufacturing step of a wet re-conversion process, a pH and a NH.sub.3/air ratio, which are operation variables, depend on the sintered density of uranium oxide (UO.sub.x). The operation variables also depended on the chromaticity of ammonium diuranate (represented using an L*a*b* color coordinate system in the present experiment).

[0029] Accordingly, ammonium diuranate powder samples are manufactured in a sufficient number while other variable factors are controlled and the predetermined operation variables are changed, and the chromaticity of each sample is measured. The samples are calcinated/reduced under the same conditions to manufacture uranium oxide (UO.sub.x) powder, and then the sintered density of each sample is measured, thereby obtaining a graph based on standard data usable when the process is operated in practice. The graph may be schematized or mathematically represented for each sample that is to be subsequently measured.

[0030] The ammonium diuranate and uranium oxide (UO.sub.x) powders shown in FIGS. 2A and 2B were manufactured while the final pH and the NH.sub.3/air ratio, as the operation variables of precipitation/filtration/drying, were changed. The numerical relationship between the measured chromaticity values L*, a*, and b* of ammonium diuranate and the sintered density was obtained using the graph.

[0031] Specifically, after the five ammonium diuranate samples were added in predetermined amounts to respective glass cells, calibration was performed using a spectrophotometer, followed by standard sample measurement. A trend line between the five standard samples (X axis: L*, a*, or b*, and Y axis: sintered density) was derived from L* (or a* or b*) color coordinate system data represented by the measured chromaticity values and from sintered density data of the actual pellet, thereby obtaining a standard sample formula of ammonium diuranate.

[0032] In greater detail, the values described in the following table were obtained.

TABLE-US-00001 Process of manufacturing ammonium diuranate (Within the range of operation variables) Operation Process of manufacturing UO.sub.x variables (Operation variables are fixed) [precipitation/ Operation Sample filtration/ variables characteristics drying] Ammonium [calcination/reduction] UO.sub.x Concentration Solution pH NH.sub.3/air diuranate Time/ N.sub.2/H.sub.2/air Sintered Classification (gU/L) (mL) (Final) ratio L* a* b* temperature flow rate density Standard S.1 30 50 Actual Actual 78.68 14.07 74.07 Actual Actual 10.35 variable variable variable variable Standard S.2 Actual Actual 80.54 14.50 81.17 Actual Actual 10.32 variable variable variable variable Standard S.3 Actual Actual 81.20 16.76 87.57 Actual Actual 10.29 variable variable variable variable Standard S.4 Actual Actual 79.11 18.28 89.63 Actual Actual 10.34 variable variable variable variable Standard S.5 Actual Actual 79.52 17.31 74.30 Actual Actual 10.35 variable variable variable variable

[0033] From FIG. 3, it was confirmed that the relationship between the L* value and the sintered density could be represented by an Equation of a predetermined curve (represented by a quadratic function). From the R2 value of 0.9618, it was confirmed that reliability was high.

[0034] On the other hand, from FIG. 4, it was confirmed that the relationship between the value and the sintered density could be represented by an Equation of a predetermined curve (represented by a quadratic function) but that the R2 value was 0.4034, thus exhibiting low reliability. From FIG. 5, it was confirmed that the relationship between the b* value and the sintered density could be represented by an equation corresponding to a predetermined curve (represented by a quadratic function), but that the R2 value was 0.6374, thus exhibiting low reliability.

[0035] Accordingly, it was confirmed that the sintered density could be calculated with high reliability on the basis of the L* value.

EXAMPLE 2

Measurement of Chromaticity of Ammonium Diuranate Powder as Measurement Target, and Calculation of Sintered Density of Ammonium Diuranate Powder

[0036] During the actual process of manufacturing powder for use in a uranium pellet, the manufactured ammonium oxide (UO.sub.x) diuranate powder is sampled and added in a predetermined amount to a glass cell, and then calibration is performed using a spectrophotometer, followed by measurement. According to the aforementioned procedure, chromaticity data values are obtained using an L* b* color coordinate system (Step S100 of FIG. 1).

[0037] Subsequently, the data values are compared with the standard chromaticity graph values obtained in Example 1 (Step S200 of FIG. 1), and the L* value is added to the Equation to perform calculation, thereby predicting, calculating, and analyzing the sintered density value of a uranium oxide (UO.sub.x) pellet that will be formed using the corresponding sample (Step S300 of FIG. 1).

[0038] The calculation of the sintered density using the L* value is shown in FIG. 6. Since the L* value is 79, the predicted value of the sintered density becomes 10.35, which was confirmed to be the same as the measured value after actual sintering.

[0039] Although the preferred embodiments of the present invention have been disclosed for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims.