Acid grafted EO-PO copolymers as silica scale inhibitors

Abstract

A method for inhibiting silica scale formation which treats aqueous systems with a polymerizable-acid graft copolymer that includes an unsaturated grafting acid and having a percent acid graft of between about 3 wt. % and about 35 wt. %, as well as an alkylene oxide polymer backbone.

Claims

1. A method of inhibiting silica scale formation, said method comprising the steps of: treating an aqueous system comprising silica with an effective amount of a polymerizable-acid graft polymer consisting of an unsaturated grafting acid and an alkylene oxide polymer backbone, said alkylene oxide polymer backbone having the following formula: ##STR00004## wherein each R is independently selected from the group consisting of a hydrogen radical, and acyl radicals; wherein R is independently selected from the group consisting of a hydrogen radical, amine-containing radicals, and acyl radicals; wherein each n has, independently, a value of from 2 to 4; wherein each Z has, independently, a value of from 4 to about 1800; and wherein a has a value of from 1 to 4; wherein said grafting acid is present in an amount of 10 wt.

2. The method of claim 1 wherein the grafting acid is acrylic acid.

3. The method of claim 1 wherein said alkylene oxide polymer backbone is poly(oxyethylene-oxypropylene) having a weight ratio of oxyethylene (EO) to oxypropylene (PO) of about 50:50.

Description

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

(1) The disclosed invention covers a method of inhibiting silica scale formation via treating an aqueous system containing silica with an effective amount of a polymerizable-acid graft copolymer comprising an unsaturated grafting acid (such as an acid selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, maleic acid, 2-acrylamido-2-methylpropylsulfonic acid (AMPS), 2-methacrylamido-2-methylpropylsulfonic acid, styrene sulfonic acid, vinylsulfonic acid, ethylene glycol methacrylate phosphate, vinyl phosphonic acid), having a percent acid graft of between about 3% and about 35% weight, and an alkylene oxide polymer backbone, the alkylene oxide polymer backbone having the following formula:

(2) ##STR00002##
Wherein each R is independently selected from a hydrogen atom, hydrogen radicals, or acyl radicals; R is selected from a hydrogen atom, hydrogen radicals, amine-containing radicals, or acyl radicals; each n has, independently, a value of from 2 to 4; each Z has, independently, a value of from 4 to about 1800; and a has a value of from 1 to 4. In one embodiment, R is acyl radicals free of aliphatic unsaturation. In another embodiment, R and R are not both a hydrogen atom.

(3) All percentages stated herein are weight percentages (wt. %), unless otherwise indicated.

(4) Temperatures are in degrees Celsius ( C.), and ambient temperature means between 20 C. and 25 C., unless specified otherwise.

(5) Polymer generally refers to a polymeric compound or resin prepared by polymerizing monomers, whether of the same or different types. As used herein, the generic term polymer includes polymeric compounds made from one or more types of monomers. Copolymers as used herein are polymeric compounds prepared from two or more different types of monomers. Similarly ter-polymers are polymeric compounds prepared from three different types of monomers.

(6) Aqueous system generally refers to any system containing water including, but not limited to, cooling water, boiler water, desalination, gas scrubbers, blast furnaces, sewage sludge thermal conditioning equipment, filtration, reverse osmosis, sugar evaporators, paper processing, mining circuits, and the like.

(7) The term silica scale generally refers to solid materials containing silica that are deposited and accumulated on internal surfaces of water treatment equipment. Silica scale generally includes multiple types of silica scale such as colloidal or amorphous silica (SiO.sub.2) and silicate (such as magnesium silicate). The accumulated silica scale may be, and sometimes is, a combination of silica and silicate types of scale, often where one or the other type of scale predominates. Colloidal/amorphous silica scale is the term used hereinafter to generally refer to silica scale deposits that are predominantly of the colloidal/amorphous silicate type. Other kinds of scale besides the silica types may be present, such as calcium carbonate, calcium sulfate, calcium phosphate, calcium phosphonate, calcium oxalate, barium sulfate, silica, alluvial deposits, metal oxide, and metal hydroxide, depending upon what kinds of metals and other ions are present in the aqueous system.

(8) The chemical reaction mechanism for formation of colloidal/amorphous silica scale generally involves condensation polymerization of silicic acid to polysilicates, catalyzed by hydroxide ions. This reaction mechanism proceeds generally as follows:
Si(OH).sub.4+OH.sup..fwdarw.(OH).sub.3SiO.sup.+H2O(I)
Si(OH).sub.3.sup.+Si(OH).sub.4+OH.sup..fwdarw.(OH).sub.3SiOSi(OH).sub.3 (dimer)+OH.sup.(II)
(OH).sub.3SiOSi(OH).sub.3 (dimer).fwdarw.Cyclic.fwdarw.Colloidal.fwdarw.Amorphous Silica (scale)(III)

(9) Since the reaction mechanism is catalyzed by hydroxide ions, it proceeds slowly at low pH, but increases significantly above pH of about 7. Thus, prevention of silica scale formation in aqueous systems having neutral pH, such as, between 6.5 and 8.5, is of particular concern.

(10) The method of the present invention is suitable for controlling deposition of colloidal/amorphous silica scale in aqueous systems having a pH between 6.5 and 10.0, at temperatures ranging from 20 C. to 250 C. The method comprises adding to the aqueous system an effective amount of an acrylic acid grafted ethylene oxide-propylene oxide (EO-PO) copolymer.

(11) Graft Polymers

(12) Graft polymers are segmented copolymers comprising (1) a linear backbone polymer and (2) randomly distributed branches of another polymer.

(13) Backbone Polymer

(14) The poly(alkylene oxide) compounds used to make the graft copolymers are commonly produced by reacting an alkylene oxide or a mixture of alkylene oxides, added sequentially or in combination, with an alcohol. Such alcohols can be monohydric or polyhydric and correspond to the formula R(OH).sub.a, wherein R is selected from the group consisting of a hydrogen atom, hydrogen radicals, amine-containing radicals and acyl radicals, and a has a value of from 1 to 4. Such alcohols include methanol, ethanol, propanol, butanol, ethylene glycol, glycerol, the monoethylether of glycerol, the dimethyl ether of glycerol, sorbitol, 1,2,6-hexanetriol, trimethylolpropane, and the like.

(15) Generally, the poly(oxyalkylene) compounds used in this invention have molecular weights (number average) in the range of about 200 Daltons to about 80,000 Daltons, preferably from about 1500 Daltons to about 20,000 Daltons.

(16) The grafting of the polymerizable-acid onto the poly (oxyalkylene) compounds can be carried out by free radical polymerization, to afford a grafted acid content of between about 3 and about 35 (preferably between about 5 and about 25).

(17) Useful grafting acids include, among others, acrylic acid, methacrylic acid, itaconic acid, maleic acid, 2-acrylamido-2-methylpropylsulfonic acid (AMPS), 2-methacrylamido-2-methylpropylsulfonic acid, styrene sulfonic acid, vinylsulfonic acid, ethylene glycol methacrylate phosphate, and vinyl phosphonic acid, with acrylic acid, maleic acid and vinyl phosphonic acid being more preferable, and acrylic acid being most preferable.

(18) The poly(oxyalkylene) compounds useful in the present invention have the formula have the formula:

(19) ##STR00003##
wherein each R is independently either a hydrogen atom, hydrogen radicals, or acyl radicals; R is independently either a hydrogen atom, hydrogen radicals, amine-containing radicals, or acyl radicals; each n has, independently, a value of from 2 to 4; each Z has, independently, a value of from 4 to about 1800; and a has a value of from 1 to 4. In a preferred embodiment, the poly(oxyalkylene) compounds are poly(oxyethylene-oxypropylene) polymers such that n=2 or 3; a has a value of 1; and each R or R is independently either a hydrogen atom, hydrogen radicals, or acyl radicals, resulting respectively in either an ethylene oxide (EO) or propylene oxide (PO) polymer.

(20) The poly(oxyethylene-oxypropylene) polymers have a weight ratio of oxyethylene (EO) to oxypropylene (PO) of between 0:100 and 100:0. EO-PO copolymers are particularly suited as a backbone for the graft polymers of the present invention, as they are capable of inhibiting the formation of silica scales. EO-PO copolymers are organic compounds comprising ethoxy and propoxy groups and suitable EO-PO copolymers may comprise random copolymers of EO/PO, homo-polymers of EO, homo-polymers of PO, block copolymers of EO/PO, and reverse block copolymers of EO/PO. The weight ratio of EO:PO can be from about 100:0 to about 0:100, and is preferably from about 90:10 to about 10:90, and is more preferably from about 75:25 to about 25:75, and most preferably about 50:50. The graft polymer of the present invention preferably comprises 65 wt. % to 97 wt. % of backbone polymer.

(21) Method of Use

(22) Effective amount is that amount of the graft copolymer necessary to inhibit deposition of colloidal/amorphous silica scale in the aqueous system being treated. Inhibit means to retard the deposition of colloidal/amorphous silica scale to prolong period of maximal efficiency of equipment. The effective amount of graft copolymer added to the aqueous system may vary depending upon the temperature and pH of the aqueous system along with the concentration of silica, salts, and polyvalent metal ions present in the aqueous system. In most applications, the effective amount of graft copolymer ranges from about 0.5 ppm to about 1000 ppm, and more preferably from about 1 ppm to 100 ppm. The aqueous systems treated by the present graft copolymer typically have a silica content of more than 30 ppm, 50 ppm or even 100 ppm.

(23) The method of polymerization employed to prepare the graft polymers useful in the method of the present invention for controlling deposition is not particularly limited and may be any method known, now or in the future, to persons of ordinary skill including, but not limited to, emulsion, solution, addition and free-radical polymerization techniques, including the methods disclosed in U.S. Pat. Nos. 4,146,488, 4,392,972, 5,952,432, and 6,143,243, which are hereby incorporated by reference.

(24) The use, application and benefits of the present invention will be clarified by the following discussion and description of exemplary embodiments of the present invention.

EXAMPLES

(25) The following Examples illustrate various nonlimiting embodiments of the invention disclosed and claimed herein as well as certain attributes thereof.

(26) Grafting of Acid onto Copolymers

(27) An acid graft copolymer was prepared using acrylic acid and a base polymer consisting of butanol-initiated poly(oxyethylene-oxypropylene) copolymer having a molecular weight of 770 and a viscosity of 170 Saybolt seconds at 37.8 C. as follows:

(28) Into a 5-liter, 3-neck round bottom flask fitted with a water condenser, thermocouple, stirrer, and means of introducing acrylic acid and catalyst, was placed 2700 g of the base polymer. By means of a heating mantle, the flask was heated to a temperature of 150 C., followed by the addition of 35 g of tertiary-butyl perbenzoate and 312 g of acrylic acid. A peroxide feed was begun 10 minutes prior to starting the acid feed and both ingredients were fed over a period of 90 minutes after which the product was allowed to cool to room temperature.
Static Bottle Test

(29) Static bottle testing was used to evaluate the efficacy of various polymers to inhibit silica polymerization. Free silica remaining in solution (reactive silica) was tracked using the HACH silicomolybdate colorimetric method. Polymers with higher efficacy at inhibiting colloidal silica formation maintained higher levels of free silica in solution over time. Supersaturated silica solutions were prepared by dissolving sodium silicate salt in deionized water to yield an initial silica concentration of 400 ppm as SiO.sub.2.

(30) In the first set of static bottle tests, 5, 15 and 25 ppm (as actives) of the inhibitor of the invention were dosed into the supersaturated silica solution and the pH was adjusted to 7.5. The samples were then allowed to sit undisturbed for 24 hours at 20 C. After 24 hours, the silica solutions were mixed well and analyzed for turbidity with a turbidimeter to check for the presence of insoluble flocs. The silica samples were then filtered with 0.45 m filters and the filtrate was analyzed using the HACH colorimetric method. Sample A is the acrylic acid (AA) grafted ethylene oxide-propylene oxide copolymer. Sample B is a copolymer of ethylene oxide-propylene oxide without grafting

(31) After final soluble silica concentrations of the solutions containing the inhibitor and the solutions lacking the inhibitor were measured, the percent scale inhibition was calculated according to the following formula:

(32) $\frac{\begin{array}{c}\mathrm{Final}\mathrm{silica}\mathrm{concentration}\mathrm{with}\mathrm{inhibitor}-\\ \mathrm{Final}\mathrm{silica}\mathrm{concentration}\mathrm{without}\mathrm{inhibitor}\end{array}}{\begin{array}{c}\mathrm{Initial}\mathrm{silica}\mathrm{concentration}-\\ \mathrm{Final}\mathrm{silica}\mathrm{concentration}\mathrm{without}\mathrm{inhibitor}\end{array}}*100$
The results of the turbidity and silica inhibition tests are summarized in Table 1.

(33) TABLE-US-00001 TABLE 1 Sample A Sample B 5 15 25 5 15 25 Blank ppm ppm ppm ppm ppm ppm Soluble Silica @ t = 24 h 200 270 310 320 290 320 330 Percent inhibition 0 44 69 75 56 75 81 @ t = 24 h Turbidity @ t = 24 h 0.2 0.2 0.2 0.2 16 31 42 (NTU)

(34) It was determined that Sample A maintained a high level of reactive silica in solution without forming insoluble precipitates, or flocs. In comparison, Sample B exhibited inhibition of colloidal silica, but resulted in insoluble flocs that greatly increased the turbidity of the silica brine.

(35) In a second set of static bottle tests, 100 ppm of Ca.sup.2+, added as calcium chloride dihydrate, and 40 ppm of Mg.sup.2+, added as magnesium chloride hexahydrate, were added in addition to 400 ppm SiO.sub.2, added as sodium silicate to evaluate the effect of hardness ions. After the addition of the inhibitor at 5, 15 and 25 ppm (as actives) the brine pH was adjusted to 7.5. The samples were then allowed to sit undisturbed for 24 hours at 20 C. After 24 hours, the silica solutions were mixed well and analyzed for turbidity with a turbidimeter to check for the presence of insoluble flocs. The silica samples were then filtered with 0.45 m filters and the filtrate was analyzed using the HACH colorimetric method. Sample A is the acrylic acid (AA) grafted ethylene oxide-propylene oxide copolymer. Sample B is a copolymer of ethylene oxide-propylene oxide without grafting. The results of the turbidity and silica inhibition tests are summarized in Table 2.

(36) TABLE-US-00002 TABLE 2 Sample A Sample B 5 15 25 5 15 25 Blank ppm ppm ppm ppm ppm ppm Soluble Silica @ t = 24 h 180 250 270 280 270 290 300 Percent inhibition 0 41 53 59 52 64 70 @ t = 24 h Turbidity @ t = 24 h 0.4 1.5 5 6.5 14 29 38 (NTU)

(37) It was determined that Sample A maintained a high level of reactive silica in solution with significantly lower quantity of insoluble precipitates, or flocs, with minimum turbidity. In comparison, Sample B exhibited inhibition of colloidal silica, but resulted in greater amount of insoluble flocs that greatly increase the turbidity of the silica brine.

(38) Although the invention has been described by reference to its preferred embodiment as is disclosed in the specification and drawings above, many more embodiments of the invention are possible without departing from the invention. Thus, the scope of the invention should be limited only by the appended claims.