ORGANIC ELECTROLUMINESCENT ELEMENT

Abstract

To provide an organic electroluminescent device having high efficiency and high driving stability while having a low driving voltage. The organic electroluminescent device has one or more light-emitting layers between an anode and a cathode opposed to each other, wherein at least one of the light-emitting layers is a light-emitting layer composed of a vapor deposition layer containing a first host, a second host and a light-emitting dopant material; the first host is selected from oligopyridine compounds represented by the general formula (1); and the second host is selected from carbazole compounds having two or more carbazole rings, indolocarbazole compounds having an indolocarbazole ring or compounds having a carbazole ring and an indolocarbazole ring.

Claims

1-11. (canceled)

12. An organic electroluminescent device comprising one or more light-emitting layers between an anode and a cathode opposed to each other, wherein at least one of the light-emitting layers is a light-emitting layer comprising a vapor deposition layer containing a first host, a second host and a light-emitting dopant material, the first host is selected from a compound represented by the following general formula (1), and the second host is selected from a compound represented by the following general formula (2) or general formula (4): ##STR00121## wherein L.sup.1 to L.sup.3 each represent a single bond, a substituted or unsubstituted aromatic hydrocarbon group having 6 to 30 carbon atoms, or a linked aromatic group in which 2 to 10 thereof are linked to each other, R.sup.1 to R.sup.7 independently represent hydrogen, deuterium, an aliphatic hydrocarbon group having 1 to 10 carbon atoms, a substituted or unsubstituted aromatic hydrocarbon group having 6 to 10 carbon atoms, or a substituted or unsubstituted aromatic heterocyclic group having 3 to 12 carbon atoms; a, b and c represent the number of repetitions and each independently represent an integer of 0 to 3, wherein a+b≥1; and p, q, r, s, t, u and v represent the number of substitutions and each independently represent an integer of 1 to 3; ##STR00122## wherein R.sup.8 and R.sup.9 independently represent hydrogen, an aromatic hydrocarbon group having 6 to 14 carbon atoms, or a group in which two of the aromatic hydrocarbon groups are linked to each other; and L.sup.4 and L.sup.5 independently represent a phenylene group; ##STR00123## wherein L.sup.7 is an m-valent aromatic hydrocarbon group having 6 to 30 carbon atoms, an aromatic heterocyclic group having 3 to 16 carbon atoms, or a linked aromatic group in which 2 to 10 of the aromatic rings are linked to each other, provided that L.sup.7 is not a group containing a carbazole ring; R.sup.13 is each independently hydrogen, an alkyl group having 1 to 10 carbon atoms, or a cycloalkyl group having 3 to 11 carbon atoms; m is the number of substitutions and represents an integer of 1 to 3; and n is the number of repetitions and is each independently an integer of 1 to 4, provided that at least one n is an integer of 2 to 4.

13. The organic electroluminescent device according to claim 12, wherein the compound represented by the general formula (2) is a compound represented by the following formula (6): ##STR00124## wherein R.sup.8, R.sup.9, L.sup.4 and L.sup.5 are as defined for the general formula (2).

14. The organic electroluminescent device according to claim 12, wherein the general formula (4) has at least one binding structure represented by formula (c1) or (c2), ##STR00125## wherein R.sup.13 is as defined for the general formula (4), ##STR00126## wherein R.sup.13 is as defined for the general formula (4).

15. The organic electroluminescent device according to claim 12, wherein the compound represented by the general formula (1) is a compound represented by any one of formulas (9) to (11): ##STR00127## wherein L.sup.1 to L.sup.3, R.sup.1 to R.sup.7 and c and p to v are as defined for the general formula (1).

16. The organic electroluminescent device according to claim 12, wherein a proportion of the first host is larger than 20 wt % and less than 55 wt % based on the first host and the second host in total.

17. The organic electroluminescent device according to claim 12, wherein the light-emitting dopant material is an organic metal complex containing at least one metal selected from the group consisting of ruthenium, rhodium, palladium, silver, rhenium, osmium, iridium, platinum and gold.

18. The organic electroluminescent device according to claim 12, wherein the light-emitting dopant material is a thermally activated delayed fluorescence-emitting dopant material.

19. The organic electroluminescent device according to claim 12, wherein a hole blocking layer is provided adjacent to the light-emitting layer, and the compound represented by the general formula (1) is contained in the hole blocking layer.

20. A method for producing the organic electroluminescent device according to claim 12, comprising a step of mixing a first host and a second host to prepare a premixture, and then vapor-depositing a host material containing the premixture to form a light-emitting layer.

21. The method for producing the organic electroluminescent device according to claim 20, wherein a difference in 50% weight reduction temperatures of the first host and the second host is within 20° C.

22. The organic electroluminescent device according to claim 13, wherein the compound represented by the general formula (1) is a compound represented by any one of formulas (9) to (11): ##STR00128## wherein L.sup.1 to L.sup.3, R.sup.1 to R.sup.7 and c and p to v are as defined for the general formula (1).

23. The organic electroluminescent device according to claim 15, wherein the compound represented by the general formula (1) is a compound represented by any one of formulas (9) to (11): ##STR00129## wherein L.sup.1 to L.sup.3, R.sup.1 to R.sup.7 and c and p to v are as defined for the general formula (1).

24. The organic electroluminescent device according to claim 13, wherein a proportion of the first host is larger than 20 wt % and less than 55 wt % based on the first host and the second host in total.

25. The organic electroluminescent device according to claim 15, wherein a proportion of the first host is larger than 20 wt % and less than 55 wt % based on the first host and the second host in total.

Description

BRIEF DESCRIPTION OF DRAWING

[0044] FIG. 1 is a schematic cross-sectional view showing one example of an organic electroluminescent device.

DESCRIPTION OF EMBODIMENTS

[0045] An organic electroluminescent device of the present invention has a structure wherein an anode, an organic layer and a cathode laminated on a substrate, wherein at least one layer of the organic layer contains a material for the above organic electroluminescent device.

[0046] This organic electroluminescent device has an organic layer composed of a plurality of layers between the anode and the cathode opposed to each other; and at least one layer of the plurality of layers is a light-emitting layer, and there may be a plurality of light-emitting layers. Then, at least one of the light-emitting layers is a light-emitting layer composed of a vapor deposition layer containing a first host, a second host and a light-emitting dopant material.

[0047] An organic electroluminescent device is characterized in that the first host contained in the light-emitting layer is selected from the compounds represented by the general formula (1), and the second host is selected from the compounds represented by the general formula (2), general formula (3), general formula (4) or general formula (5).

[0048] The first host is selected from oligopyridine compounds represented by the general formula (1).

[0049] In the general formula (1), R.sup.1 to R.sup.7 independently represent hydrogen, deuterium, an aliphatic hydrocarbon group having 1 to 10 carbon atoms, an aromatic hydrocarbon group having 6 to 30 carbon atoms, or an aromatic heterocyclic group having 3 to 12 carbon atoms; preferably, an aliphatic hydrocarbon group having 1 to 8 carbon atoms, a phenyl group or an aromatic heterocyclic group having 3 to 12 carbon atoms; and more preferably an aliphatic hydrocarbon group having 1 to 6 carbon atoms, a phenyl group or a carbazole ring group.

[0050] In the present specification, it is understood that an aromatic hydrocarbon group, an aromatic heterocyclic group and a linked aromatic group generated by linking of these aromatic rings with a single bond may have a substituent unless they are not specified as being unsubstituted. The same applies to an aliphatic hydrocarbon group.

[0051] Specific examples of the aliphatic hydrocarbon group include methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, and decyl. An alkyl group having 1 to 4 carbon atoms is preferred.

[0052] Specific examples of the aromatic hydrocarbon groups and the aromatic heterocyclic groups include aromatic groups generated by removing one H from benzene, naphthalene, pyridine, pyrimidine, triazine, thiophene, isothiazole, thiazole, pyridazine, pyrrole, pyrazole, imidazole, triazole, thiadiazole, pyrazine, furan, isoxazole, oxazole, oxadiazole, quinoline, isoquinoline, quinoxaline, quinazoline, oxadiazole, thiadiazole, benzotriazine, phthalazine, tetrazole, indole, benzofuran, benzothiophene, benzoxazole, benzothiazole, indazole, benzimidazole, benzotriazole, benzisothiazole, benzothiadiazole, dibenzofuran, dibenzothiophene, dibenzoselenophene, and carbazole. Preferred are aromatic groups generated from benzene, pyridine, pyrimidine, triazine, thiophene, isothiazole, thiazole, pyridazine, pyrrole, pyrazole, imidazole, triazole, thiadiazole, pyrazine, furan, isoxazole, oxazole, oxadiazole, quinoline, isoquinoline, quinoxaline, quinazoline, oxadiazole, thiadiazole, benzotriazine, phthalazine, tetrazole, indole, benzofuran, benzothiophene, benzoxazole, benzothiazole, indazole, benzimidazole, benzotriazole, benzisothiazole, and benzothiadiazole. More preferred are aromatic groups generated from benzene, pyridine, pyrimidine, triazine, thiophene, isothiazole, thiazole, pyridazine, pyrrole, pyrazole, imidazole, triazole, thiadiazole, pyrazine, furan, isoxazole, oxazole, and oxadiazole.

[0053] L.sup.1 to L.sup.3 independently represent a single bond, a substituted or unsubstituted aromatic hydrocarbon group having 6 to 10 carbon atoms, or a linked aromatic group in which 2 to 10 thereof are linked to each other. Preferred examples of the aromatic hydrocarbon group include divalent groups generated from benzene and naphthalene. Preferred examples of the linked aromatic group include divalent groups generated from biphenyl and terphenyl.

[0054] a, b and c represent the number of repetitions, and each independently represent an integer of 0 to 3, preferably an integer of 0 or 1, provided that a+b≥1.

[0055] p to v represent the number of substitutions, and each independently represent an integer of 1 to 3, preferably an integer of 1 or 2.

[0056] Preferred aspects of the compounds represented by the general formula (1) include compounds represented by any of the general formulas (9) to (11). In the general formulas (9) to (11), the same symbols as in the general formula (1) have the same meaning.

[0057] Specific examples of the compounds represented by the general formula (1) are described below, but the compounds are not limited to these exemplified compounds.

##STR00010## ##STR00011## ##STR00012## ##STR00013## ##STR00014## ##STR00015## ##STR00016## ##STR00017## ##STR00018## ##STR00019## ##STR00020## ##STR00021## ##STR00022## ##STR00023## ##STR00024## ##STR00025## ##STR00026## ##STR00027## ##STR00028## ##STR00029## ##STR00030##

[0058] The second host is selected from compounds represented by the general formula (2), (3), (4) or (5).

[0059] The general formula (2) representing the second host and formula (6) representing preferred aspects thereof will be described. In the general formula (2) and formula (6), the same symbols have the same meaning.

[0060] R.sup.8 and R.sup.9 independently represent hydrogen, an aromatic hydrocarbon group having 6 to 14 carbon atoms, or a linked aromatic group in which two aromatic rings of the aromatic hydrocarbon group are linked; preferably, hydrogen or an aromatic hydrocarbon group having 6 to 12 carbon atoms; and more preferably an aromatic hydrocarbon group having 6 to 10 carbon atoms. It is a preferred embodiment that: R.sup.8 is hydrogen; or R.sup.8 is hydrogen and R.sup.9 is the above aromatic hydrocarbon group or linked aromatic group.

[0061] In the case of R.sup.8 and R.sup.9 being an aromatic hydrocarbon group or a linked aromatic group, specific examples thereof include aromatic hydrocarbons such as benzene, naphthalene, anthracene, phenanthrene, fluorene and biphenyl, or an aromatic group or linked aromatic group generated by removing one H from a compound in which two aromatic rings of these aromatic hydrocarbons are linked. Preferred are aromatic groups generated from benzene, naphthalene, anthracene, phenanthrene, or linked aromatic groups in which two of the aromatic groups are linked to each other. More preferred are aromatic groups generated from benzene, naphthalene, phenanthrene or biphenyl. It is further preferred that R.sup.8 and R.sup.9 are a phenyl group.

[0062] R.sup.8 and R.sup.9 may be hydrogen; but in that case, one of them is preferably the aromatic group or linked aromatic group. It is further preferred that R.sup.8 is hydrogen and R.sup.9 is a phenyl group. In addition, the aromatic group or linked aromatic group may have a substituent, and preferred substituents are an alkyl group having 1 to 12 carbon atoms or an alkoxy group having 1 to 12 carbon atoms.

[0063] L.sup.4 and L.sup.5 are a phenylene group, and the phenylene group may be any of o-phenylene group, m-phenylene group and p-phenylene group. Preferred is p-phenylene group or m-phenylene group. Then, L.sup.4 and L.sup.5 are preferably different from each other. In this case, when R.sup.8 and R.sup.9 are hydrogen, they are treated as a phenyl group, different from a phenylene group.

[0064] Specific examples of the compounds represented by the general formulas (2) and (6) are described below, but the compounds are not limited to these exemplified compounds.

##STR00031## ##STR00032## ##STR00033## ##STR00034## ##STR00035## ##STR00036## ##STR00037## ##STR00038## ##STR00039## ##STR00040## ##STR00041## ##STR00042## ##STR00043## ##STR00044## ##STR00045## ##STR00046## ##STR00047## ##STR00048## ##STR00049##

[0065] Next, the general formula (3) will be described.

[0066] In the general formula (3), the ring C is a heterocycle represented by formula (3a) and the ring C is fused to an adjacent ring at any position.

[0067] R.sup.10 to R.sup.12 are independently hydrogen, deuterium, an aliphatic hydrocarbon group having 1 to 10 carbon atoms, an aromatic hydrocarbon group having 6 to 10 carbon atoms or an aromatic heterocyclic group having 3 to 12 carbon atoms. Preferred is an aliphatic hydrocarbon group having 1 to 8 carbon atoms, a phenyl group or an aromatic heterocyclic group having 3 to 9 carbon atoms. More preferred is an aliphatic hydrocarbon group having 1 to 6 carbon atoms, a phenyl group or an aromatic heterocyclic group having 3 to 6 carbon atoms.

[0068] Specific examples of the aliphatic hydrocarbon group include methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, and decyl. Preferred is an alkyl group having 1 to 4 carbon atoms.

[0069] Specific examples of the aromatic hydrocarbon group or aromatic heterocyclic group include aromatic groups generated by removing one H from benzene, naphthalene, pyridine, pyrimidine, triazine, thiophene, isothiazole, thiazole, pyridazine, pyrrole, pyrazole, imidazole, triazole, thiadiazole, pyrazine, furan, isoxazole, oxazole, oxadiazole, quinoline, isoquinoline, quinoxaline, quinazoline, oxadiazole, thiadiazole, benzotriazine, phthalazine, tetrazole, indole, benzofuran, benzothiophene, benzoxazole, benzothiazole, indazole, benzimidazole, benzotriazole, benzisothiazole, benzothiadiazole, dibenzofuran, dibenzothiophene, dibenzoselenophene, and carbazole. Preferred are aromatic groups generated from benzene, pyridine, pyrimidine, triazine, thiophene, isothiazole, thiazole, pyridazine, pyrrole, pyrazole, imidazole, triazole, thiadiazole, pyrazine, furan, isoxazole, oxazole, oxadiazole, quinoline, isoquinoline, quinoxaline, quinazoline, oxadiazole, thiadiazole, benzotriazine, phthalazine, tetrazole, indole, benzofuran, benzothiophene, benzoxazole, benzothiazole, indazole, benzimidazole, benzotriazole, benzisothiazole, and benzothiadiazole. More preferred are aromatic groups generated from benzene, pyridine, pyrimidine, triazine, thiophene, isothiazole, thiazole, pyridazine, pyrrole, pyrazole, imidazole, triazole, thiadiazole, pyrazine, furan, isoxazole, oxazole, and oxadiazole.

[0070] L.sup.6 is independently a single bond, an aromatic hydrocarbon group having 6 to 10 carbon atoms or an aromatic heterocyclic group having 3 to 12 carbon atoms, or a linked aromatic group in which 2 to 10 thereof are linked to each other. Preferred examples of the aromatic hydrocarbon group or aromatic heterocyclic group are the same as in the case where R.sup.10 is of these groups except that these groups are a divalent group.

[0071] Ar.sup.1 is an aromatic hydrocarbon group having 6 to 10 carbon atoms or an aromatic heterocyclic group having 3 to 12 carbon atoms. Preferred examples of the aromatic hydrocarbon group or aromatic heterocyclic group are the same as in the case where R.sup.10 is of these groups except that these groups are a divalent group.

[0072] f, g and h each independently represent an integer of 0 to 3.

[0073] The compound represented by the general formula (3) is preferably the compound represented by the formula (7) or (8).

[0074] In formula (7) or (8), ring B, R.sup.10 to R.sup.13, Ar.sup.1, x and y are as defined for the general formula (3).

[0075] Specific examples of the indolocarbazole compound represented by the general formula (3) are described below, but the compound is not limited thereto.

##STR00050## ##STR00051## ##STR00052## ##STR00053## ##STR00054## ##STR00055## ##STR00056## ##STR00057## ##STR00058## ##STR00059## ##STR00060## ##STR00061## ##STR00062## ##STR00063## ##STR00064## ##STR00065## ##STR00066## ##STR00067## ##STR00068## ##STR00069## ##STR00070## ##STR00071## ##STR00072## ##STR00073## ##STR00074## ##STR00075##

[0076] Next, the general formula (4) will be described.

[0077] In the general formula (4), L.sup.7 represents an aromatic hydrocarbon group having 6 to 30 carbon atoms or an aromatic heterocyclic group having 3 to 30 carbon atoms, or a linked aromatic group in which these aromatic rings are linked. The linked aromatic group is a group having a structure wherein 2 to 10 of aromatic rings of the aromatic hydrocarbon group or aromatic heterocyclic group are linked by a single bond.

[0078] L.sup.7 is a group of m-valence, in which an aromatic hydrocarbon group, an aromatic heterocyclic group or a linked aromatic group may have a substituent.

[0079] In the above, L.sup.7 is not a group containing a carbazole ring.

[0080] Specific examples of the aromatic hydrocarbon group or the aromatic heterocyclic group include groups generated by removing m H atoms from benzene, pentalene, indene, naphthalene, azulene, heptalene, octalene, indacene, acenaphthylene, phenalene, phenanthrene, anthracene, trindene, fluoranthene, acephenanthrylene, aceanthrylene, triphenylene, pyrene, chrysene, tetraphene, tetracene, pleiadene, picene, perylene, pentaphene, pentacene, tetraphenylene, cholanthrylene, helicene, hexaphene, rubicene, coronene, trinaphthylene, heptaphene, pyranthrene, furan, benzofuran, isobenzofuran, xanthene, oxathrene, dibenzofuran, peri-xanthenoxanthene, thiophene, thioxanthene, thianthrene, phenoxathiin, thionaphthene, isothianaphthene, thiophthene, thiophanthrene, dibenzothiophene, pyrrole, pyrazole, tellurazole, selenazole, thiazole, isothiazole, oxazole, furazan, indolizine, indole, isoindole, indazole, purine, quinolizine, isoquinoline, imidazole, naphthyridine, phthalazine, benzodiazepine, quinoxaline, cinnoline, quinoline, pteridine, phenanthridine, acridine, perimidine, phenanthroline, phenazine, carboline, phenotellurazine, phenoselenazine, phenothiazine, phenoxazine, anthyridine, benzothiazole, benzimidazole, benzoxazole, benzisooxazole, benzisothiazole, and aromatic compounds in which a plurality of these aromatic rings is linked, and others.

[0081] In the case of the linked aromatic group, the number of linked rings is preferably 2 to 10, more preferably 2 to 7; and aromatic rings to be linked may be the same or different. In that case, in formula (3), the binding position which m carbazolyl groups bind to is not limited, and it may be either a ring at an end of linked aromatic rings and a ring at a center thereof. The aromatic ring herein collectively refers to an aromatic hydrocarbon ring and an aromatic heterocyclic ring.

[0082] Specific examples of the linked aromatic group include groups generated by removing hydrogen from biphenyl, terphenyl, quaterphenyl, binaphthalene, phenyltriphenylene, phenyldibenzofuran, phenyldibenzothiophene, bisdibenzofuran, bisdibenzothiophene, and others.

[0083] Specific examples of preferred L.sup.7 include groups generated from benzene, naphthalene, anthracene, biphenyl, terphenyl, dibenzofuran, dibenzothiophene, phenyldibenzofuran or phenyldibenzothiophene. More preferred examples include groups generated from benzene, biphenyl or terphenyl.

[0084] m represents an integer of 1 to 3. Preferably, m is 1 or 2, and more preferably 1.

[0085] n is the number of repetitions, and each independently represent an integer of 1 to 4. Preferably, n is 1 to 3. However, at least one n is an integer of 2 to 4.

[0086] The general formula (4) preferably has at least one binding structure represented by formula (c1) or formula (c2) therein. It is more preferred that all of the binding structures among carbazolyl groups should be a binding structure represented by formula (c1) or formula (c2).

[0087] The sum of n (total number of carbazolyl groups) is an integer of 2 to 12, preferably 2 to 9, and more preferably 2 to 6.

[0088] In the general formula (4), formula (c1) and formula (c2), R.sup.13 each independently represents hydrogen, an alkyl group having 1 to 10 carbon atoms, or a cycloalkyl group having 3 to 11 carbon atoms. Preferred is hydrogen, an alkyl group having 1 to 8 carbon atoms or a cycloalkyl group having 3 to 8 carbon atoms. More preferred is hydrogen, an alkyl group having 1 to 4 carbon atoms, or a cycloalkyl group having 5 to 7 carbon atoms.

[0089] Specific examples of the alkyl group include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, a nonyl group, and a decyl group. Preferred are a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, and an octyl group. The alkyl group may be either of a linear chain and a branched chain.

[0090] Specific examples of the cycloalkyl group include a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, and a methylcyclohexyl group; and preferred are a cyclohexyl group and a methylcyclohexyl group.

[0091] Specific examples of the carbazole compound represented by the general formula (4) are described below, but the compound is not limited thereto.

##STR00076## ##STR00077## ##STR00078## ##STR00079## ##STR00080## ##STR00081## ##STR00082## ##STR00083## ##STR00084## ##STR00085## ##STR00086## ##STR00087## ##STR00088## ##STR00089## ##STR00090## ##STR00091## ##STR00092## ##STR00093## ##STR00094## ##STR00095## ##STR00096## ##STR00097## ##STR00098## ##STR00099## ##STR00100## ##STR00101## ##STR00102## ##STR00103##

[0092] Next, the general formula (5) will be described.

[0093] In the general formula (5), a ring D is a heterocycle represented by formula (5a), and the ring D is fused to an adjacent ring at any position.

[0094] R.sup.14 to R.sup.16 are independently hydrogen, deuterium, an aliphatic hydrocarbon group having 1 to 10 carbon atoms, an aromatic hydrocarbon group having 6 to 30 carbon atoms, or an aromatic heterocyclic group having 3 to 12 carbon atoms. The aliphatic hydrocarbon group, aromatic hydrocarbon group and aromatic heterocyclic group are the same as in the case where R.sup.10 to R.sup.12 of the general formula (3) are of these groups, and preferred ranges therefor are also the same.

[0095] L.sup.8 is independently a single bond, an aromatic hydrocarbon group having 6 to 10 carbon atoms, or a linked aromatic group in which 2 to 10 thereof are linked to each other. The aromatic hydrocarbon groups are the same as in the case where L.sup.6 of the general formula (3) is of these groups, and a preferred range is also the same.

[0096] Ar.sup.2 is an aromatic hydrocarbon group having 6 to 30 carbon atoms. Examples of the aromatic hydrocarbon group are the same as in the case where L.sup.7 of the general formula (4) is of these groups, and a preferred range is also the same.

[0097] i, j and k each independently represent an integer of 0 to 3.

[0098] Specific examples of the indolocarbazole compound represented by the general formula (5) are described below, but the compound is not limited thereto.

##STR00104## ##STR00105## ##STR00106## ##STR00107## ##STR00108## ##STR00109## ##STR00110## ##STR00111##

[0099] Use of the first host selected from the compounds represented by the general formula (1); and the second host selected from the compounds represented by the general formula (2), (3), (4) or (5) as host materials for a light-emitting layer can provide an excellent organic electroluminescent device.

[0100] The first host and the second host which are vapor-deposited from different individual vapor deposition sources can be used; however, it is preferable to premix them as a premixture before vapor deposition and to vapor-deposit the premixture simultaneously from one vapor deposition source to thereby form a light-emitting layer. In this case, the premixture may be mixed with a light-emitting dopant material necessary for formation of a light-emitting layer, or another host to be used as necessary. However, when there is a large difference in temperatures to provide desired vapor pressure, vapor deposition may be performed from another vapor deposition source.

[0101] In addition, regarding the mixing ratio (weight ratio) between the first host and the second host, the proportion of the first host is 20 to 60%, preferably more than 20% and less than 55%, and more preferably 40 to 50% based on the first host and the second host in total.

[0102] Next, the structure of the organic electroluminescent device of the present invention will be described by referring to the drawing, but the structure of the organic electroluminescent device of the present invention is not limited thereto.

[0103] FIG. 1 is a cross-sectional view showing a structure example of an organic electroluminescent device generally used for the present invention, in which there are indicated a substrate 1, an anode 2, a hole injection layer 3, a hole transport layer 4, a light-emitting layer 5, an electron transport layer 6, and a cathode 7. The organic electroluminescent device of the present invention may have an exciton blocking layer adjacent to the light-emitting layer and may have an electron blocking layer between the light-emitting layer and the hole injection layer. The exciton blocking layer can be inserted into either of the anode side and the cathode side of the light-emitting layer and inserted into both sides at the same time. The organic electroluminescent device of the present invention has the anode, the light-emitting layer, and the cathode as essential layers, and preferably has a hole injection transport layer and an electron injection transport layer in addition to the essential layers, and further preferably has a hole blocking layer between the light-emitting layer and the electron injection transport layer. Note that the hole injection transport layer refers to either or both of a hole injection layer and a hole transport layer, and the electron injection transport layer refers to either or both of an electron injection layer and an electron transport layer.

[0104] A structure reverse to that of FIG. 1 is applicable, in which a cathode 7, an electron transport layer 6, a light-emitting layer 5, a hole transport layer 4, and an anode 2 are laminated on a substrate 1 in this order. In this case, layers may be added or omitted as necessary.

—Substrate—

[0105] The organic electroluminescent device of the present invention is preferably supported on a substrate. The substrate is not particularly limited, and those conventionally used in organic electroluminescent devices may be used, and substrates made of, for example, glass, a transparent plastic, or quartz may be used.

—Anode—

[0106] Regarding an anode material for an organic electroluminescent device, it is preferable to use a material having a large work function (4 eV or more), selected from a metal, an alloy, an electrically conductive compound or a mixture thereof. Specific examples of such an electrode material include a metal such as Au, and a conductive transparent material such as CuI, indium tin oxide (ITO), SnO.sub.2, and ZnO. In addition, an amorphous material such as IDIXO (In.sub.2O.sub.3—ZnO), which is capable of forming a transparent conductive film, may be used. Regarding the anode, such an electrode material is used to form a thin film by, for example, a vapor-deposition or sputtering method, and a desired shape pattern may be formed by a photolithographic method; or if the pattern accuracy is not particularly required (about 100 μm or more), a pattern may be formed via a desired shape mask when the electrode material is vapor-deposited or sputtered. Alternatively, when a coatable substance such as an organic conductive compound is used, a wet film formation method such as a printing method or a coating method may be used. For taking emitted light from the anode, it is desired to have a transmittance of more than 10%, and the sheet resistance for the anode is preferably several hundreds Ω/or less. The film thickness is selected usually within 10 to 1000 nm, preferably within 10 to 200 nm though depending on the material.

—Cathode—

[0107] Meanwhile, regarding a cathode material, preferable to a material having a small work function (4 eV or less), selected from a metal (an electron injection metal), an alloy, an electrically conductive compound, or a mixture thereof are used.

[0108] Specific examples of such an electrode material include sodium, a sodium-potassium alloy, magnesium, lithium, a magnesium/copper mixture, a magnesium/silver mixture, a magnesium/aluminum mixture, a magnesium/indium mixture, an aluminum/aluminum oxide (Al.sub.2O.sub.3) mixture, indium, a lithium/aluminum mixture, and a rare earth metal. Among these, from the viewpoint of the electron injectability and the durability against oxidation and the like, a mixture of an electron injection metal and a second metal which is a stable metal having a larger work function value is suitable, and examples thereof include a magnesium/silver mixture, a magnesium/aluminum mixture, a magnesium/indium mixture, an aluminum/aluminum oxide mixture, a lithium/aluminum mixture and aluminum. The cathode can be produced by forming a thin film by a method such as vapor-depositing or sputtering of such a cathode material. In addition, the sheet resistance of cathode is preferably several hundreds Ω/or less. The film thickness is selected usually within 10 nm to 5 μm, preferably within 50 to 200 nm. Note that for transmission of emitted light, if either one of the anode and cathode of the organic electroluminescent device is transparent or translucent, emission luminance is improved, which is convenient.

[0109] In addition, formation of a film of the above metal with a thickness of 1 to 20 nm on the cathode, followed by formation of a conductive transparent material described in the description on the anode thereon, enables production of a transparent or translucent cathode, and application of this enables production of a device wherein an anode and a cathode both have transmittance.

—Light-Emitting Layer—

[0110] The light-emitting layer is a layer that emits light after excitons are generated when holes and electrons injected from the anode and the cathode, respectively, are recombined. The light-emitting layer contains an organic light-emitting dopant material and a host.

[0111] As a host, the first host and the second host are used.

[0112] Regarding the compound represented by the general formula (1) as the first host, one kind thereof may be used, or two or more kinds thereof may be used. Likewise, regarding the carbazole compound or indolocarbazole compound represented by the general formulas (2) to (5) as the second host, one kind thereof may be used, or two or more kinds thereof may be used.

[0113] If necessary, one, or two or more known host materials may be used in combination; however, it is preferable that an amount thereof to be used be 50 wt % or less, preferably 25 wt % or less based on the host materials in total.

[0114] Other material may be used as the host.

[0115] The first host and the second host may be vapor-deposited from different vapor deposition sources, or alternatively, may be premixed before vapor deposition to prepare a premixture and thus the first host and the second host may be vapor-deposited from one vapor deposition source at the same time.

[0116] When the first host and the second host are premixed and used, it is desirable that a difference in 50% weight reduction temperature (T.sub.50) be small in order to produce an organic electroluminescent device having favorable characteristics with high reproducibility. The 50% weight reduction temperature is a temperature at which the weight is reduced by 50% when the temperature is raised to 550° C. from room temperature at a rate of 10° C./min in TG-DTA measurement under a nitrogen stream reduced pressure (50 Pa). It is considered that vaporization due to evaporation or sublimation the most vigorously occurs around this temperature.

[0117] The difference in 50% weight reduction temperatures of the first host and the second host is preferably within 20° C. and more preferably within 15° C. Regarding a premixing method, a known method such as pulverization and mixing can be used, and it is desirable to mix them as uniformly as possible.

[0118] When a phosphorescent dopant is used as a light-emitting dopant material, preferred is a phosphorescent dopant including an organic metal complex containing at least one metal selected from ruthenium, rhodium, palladium, silver, rhenium, osmium, iridium, platinum and gold. Specifically, iridium complexes described in J. Am. Chem. Soc. 2001, 123, 4304 and Japanese Translation of PCT International Application Publication No. 2013-53051 are preferably used, but the phosphorescent dopant is not limited thereto.

[0119] Regarding the phosphorescent dopant material, only one kind thereof may be contained in the light-emitting layer, or two or more kinds thereof may be contained. A content of the phosphorescent dopant material is preferably 0.1 to 30 wt % and more preferably 1 to 20 wt % with respect to the host material.

[0120] The phosphorescent dopant material is not particularly limited, and specific examples thereof include the following.

##STR00112## ##STR00113## ##STR00114## ##STR00115##

[0121] When a fluorescence-emitting dopant is used as the light-emitting dopant material, the fluorescence-emitting dopant is not particularly limited. Examples thereof include benzoxazole derivatives, benzothiazole derivatives, benzimidazole derivatives, styrylbenzene derivatives, polyphenyl derivatives, diphenylbutadiene derivatives, tetraphenyl butadiene derivatives, naphthalimido derivatives, coumarin derivatives, fused aromatic compounds, perinone derivatives, oxadiazole derivatives, oxazine derivatives, aldazine derivatives, pyrrolidine derivatives, cyclopentadiene derivatives, bisstyryl anthracene derivatives, quinacridone derivatives, pyrrolopyridine derivatives, thiadiazolopyridine derivatives, styrylamine derivatives, diketopyrrolopyrrole derivatives, aromatic dimethylidine compounds, metal complexes of 8-quinolinol derivatives or metal complexes of pyromethene derivatives, rare earth complexes, various metal complexes represented by transition metal complexes, polymer compounds such as polythiophene, polyphenylene, and polyphenylene vinylene, and organosilane derivatives. Preferred examples thereof include fused aromatic derivatives, styryl derivatives, diketopyrrolopyrrole derivatives, oxazine derivatives, pyromethene metal complexes, transition metal complexes, and lanthanoid complexes. More preferable examples thereof include naphthalene, pyrene, chrysene, triphenylene, benzo[c]phenanthrene, benzo[a]anthracene, pentacene, perylene, fluoranthene, acenaphthofluoranthene, dibenzo[a,j]anthracene, dibenzo[a,h]anthracene, benzo[a]naphthalene, hexacene, naphtho[2,1-f]isoquinoline, α-naphthaphenanthridine, phenanthrooxazole, quinolino[6,5-f]quinoline, and benzothiophanthrene. These may have an alkyl group, an aryl group, an aromatic heterocyclic group, or a diarylamino group as a substituent.

[0122] Regarding the fluorescence-emitting dopant material, only one kind thereof may be contained in the light-emitting layer, or two or more kinds thereof may be contained. A content of the fluorescence-emitting dopant material is preferably 0.1% to 20% and more preferably 1% to 10% with respect to the host material.

[0123] When a thermally activated delayed fluorescence-emitting dopant is used as the light-emitting dopant material, the thermally activated delayed fluorescence-emitting dopant is not particularly limited. Examples thereof include: metal complexes such as a tin complex and a copper complex; indolocarbazole derivatives described in WO2011/070963; cyanobenzene derivatives and carbazole derivatives described in Nature 2012, 492, 234; and phenazine derivatives, oxadiazole derivatives, triazole derivatives, sulfone derivatives, phenoxazine derivatives, and acridine derivatives described in Nature Photonics 2014, 8,326.

[0124] The thermally activated delayed fluorescence-emitting dopant material is not particularly limited, and specific examples thereof include the following.

##STR00116## ##STR00117## ##STR00118##

[0125] Regarding the thermally activated delayed fluorescence-emitting dopant material, only one kind thereof may be contained in the light-emitting layer, or two or more kinds thereof may be contained. In addition, the thermally activated delayed fluorescence-emitting dopant may be used by mixing with a phosphorescent dopant and a fluorescence-emitting dopant. A content of the thermally activated delayed fluorescence-emitting dopant material is preferably 0.1% to 50% and more preferably 1% to 30% with respect to the host material.

—Injection Layer—

[0126] The injection layer is a layer that is provided between an electrode and an organic layer in order to lower a driving voltage and improve emission luminance, and includes a hole injection layer and an electron injection layer, and may be present between the anode and the light-emitting layer or the hole transport layer, and between the cathode and the light-emitting layer or the electron transport layer. The injection layer can be provided as necessary.

—Hole Blocking Layer—

[0127] The hole blocking layer has a function of the electron transport layer in a broad sense, and is made of a hole blocking material having a function of transporting electrons and a significantly low ability to transport holes, and can block holes while transporting electrons, thereby improving a probability of recombining electrons and holes in the light-emitting layer.

[0128] For the hole blocking layer, a known hole blocking layer material can be used, but it is preferred for the layer to contain the compound represented by the general formula (1).

—Electron Blocking Layer—

[0129] The electron blocking layer has a function of a hole transport layer in a broad sense and blocks electrons while transporting holes, thereby enabling a probability of recombining electrons and holes in the light-emitting layer to be improved.

[0130] Regarding the material of the electron blocking layer, a known electron blocking layer material can be used and a material of the hole transport layer to be described below can be used as necessary. A film thickness of the electron blocking layer is preferably 3 to 100 nm, and more preferably 5 to 30 nm.

—Exciton Blocking Layer—

[0131] The exciton blocking layer is a layer for preventing excitons generated by recombination of holes and electrons in the light-emitting layer from being diffused in a charge transport layer, and insertion of this layer allows excitons to be efficiently confined in the light-emitting layer, enabling the luminous efficiency of the device to be improved. The exciton blocking layer can be inserted, in a device having two or more light-emitting layers adjacent to each other, between two adjacent light-emitting layers.

[0132] Regarding the material of the exciton blocking layer, a known exciton blocking layer material can be used. Examples thereof include 1,3-dicarbazolyl benzene (mCP) and bis(2-methyl-8-quinolinolato)-4-phenylphenolato aluminum (III) (BAlq).

—Hole Transport Layer—

[0133] The hole transport layer is made of a hole transport material having a function of transporting holes, and the hole transport layer can be provided as a single layer or a plurality of layers.

[0134] The hole transport material has either hole injection, transport properties or electron barrier properties, and may be an organic material or an inorganic material. For the hole transport layer, any one selected from conventionally known compounds can be used. Examples of such a hole transport material include porphyrin derivatives, arylamine derivatives, triazole derivatives, oxadiazole derivatives, imidazole derivatives, polyarylalkane derivatives, pyrazoline derivatives and pyrazolone derivatives, phenylenediamine derivatives, arylamine derivatives, amino-substituted chalcone derivatives, oxazole derivatives, styryl anthracene derivatives, fluorenone derivatives, hydrazone derivatives, stilbene derivatives, silazane derivatives, an aniline copolymer, and a conductive polymer oligomer, and particularly a thiophene oligomer. Use of porphyrin derivatives, arylamine derivatives, or styrylamine derivatives preferred. Use of arylamine compounds is more preferred.

—Electron Transport Layer—

[0135] The electron transport layer is made of a material having a function of transporting electrons, and the electron transport layer can be provided as a single layer or a plurality of layers.

[0136] The electron transport material (which may also serve as a hole blocking material) may have a function of transferring electrons injected from the cathode to the light-emitting layer. For the electron transport layer, any one selected from conventionally known compounds can be used, and examples thereof include polycyclic aromatic derivatives such as naphthalene, anthracene, and phenanthroline, tris(8-quinolinolato)aluminum(III) derivatives, phosphine oxide derivatives, nitro-substituted fluorene derivatives, diphenylquinone derivatives, thiopyrandioxide derivatives, carbodiimide, fluorenylidene methane derivatives, anthraquinodimethane and anthrone derivatives, bipyridine derivatives, quinoline derivatives, oxadiazole derivatives, benzimidazole derivatives, benzothiazole derivatives, and indolocarbazole derivatives. In addition, a polymer material in which the above material is introduced into a polymer chain or the above material is used for a main chain of a polymer can be used.

EXAMPLES

[0137] Hereafter, the present invention will be described in detail by referring to Examples, but the present invention is not limited these Examples and can be implemented in various forms without departing from the gist thereof.

Example 1

[0138] On a glass substrate on which an anode made of ITO with a film thickness of 110 nm was formed, respective thin films were laminated by a vacuum evaporation method at a degree of vacuum of 4.0×10.sup.−5 Pa. First, HAT-CN was formed with a thickness of 25 nm as a hole injection layer on ITO, and next, NPD was formed with a thickness of 30 nm as a hole transport layer. Next, HT-1 was formed with a thickness of 10 nm as an electron blocking layer. Then, compound 1-1 as a first host, compound 2-4 as a second host and Ir(ppy).sub.3 as a light-emitting dopant were co-vapor-deposited from different vapor deposition sources, respectively, to form a light-emitting layer with a thickness of 40 nm. In this case, co-vapor deposition was performed under vapor deposition conditions such that the concentration of Ir(ppy).sub.3 was 10 wt % and the weight ratio between the first host and the second host was 30:70. Next, ET-1 was formed with a thickness of 20 nm as an electron transport layer. Further, LiF was formed with a thickness of 1 nm as an electron injection layer on the electron transport layer. Finally, Al was formed with a thickness of 70 nm as a cathode on the electron injection layer to produce an organic electroluminescent device.

Examples 1 to 88

[0139] Organic electroluminescent devices were produced in the same manner as in Example 1 except that compounds shown in Tables 1 and 2 were used as the first host and the second host instead of those of Example 1.

Example 89 to 96

[0140] The first host and the second host were mixed in advance to prepare a premixture, and the premixture was co-vapor-deposited from one vapor deposition source.

[0141] Organic electroluminescent devices were produced in the same manner as in Example 1 except for use of a premixture obtained by weighing a first host (0.30 g) and a second host (0.70 g) and mixing them while grinding in a mortar.

[0142] Evaluation results of the produced organic electroluminescent devices are shown in Tables 1 to 4.

[0143] In the tables, the luminance, driving voltage, and luminous efficiency are values at the time when the driving current was 20 mA/cm.sup.2, and they exhibit initial characteristics. LT70 is a time period needed for the initial luminance to be reduced to 70% thereof, and it represents lifetime characteristics.

TABLE-US-00001 TABLE 1 Second Power First host host Luminance Voltage efficiency LT70 Example compound compound (cd/m2) (V) (Im/W) (h) 1 1-1 2-4 11000 4.0 43.2 1100 2 1-1 2-5 10000 3.8 41.3 1300 3 1-1 2-6 10000 3.8 41.3 1300 4 1-1 2-9 10000 3.9 40.3 1000 5 1-1 2-10 10000 3.9 40.3 1000 6 1-1 2-13 10000 3.9 40.3 1000 7 1-1 2-21 11000 4.2 41.1 1000 8 1-1 2-22 11000 3.9 44.3 1000 9 1-1 2-23 11000 3.9 44.3 1000 10 1-1 2-24 11000 4.3 40.2 1000 11 1-1 2-27 11000 4 43.2 1000 12 1-1 2-28 11000 4 43.2 1000 15 1-1 3-1 10000 4.1 38.3 1000 16 1-1 3-5 10000 4 39.3 1000 17 1-1 3-8 10000 4 39.3 1000 18 1-1 3-12 10000 3.9 40.3 1000 19 1-1 3-16 10000 3.9 40.3 1000 20 1-1 3-24 11000 3.6 48.0 1200 21 1-1 3-26 11000 3.5 49.4 1200 22 1-1 3-33 10500 3.4 48.5 1200 23 1-1 3-45 11000 3.8 45.5 1100 24 1-1 4-3 11000 4.5 38.4 1200 25 1-1 4-22 11000 4.5 38.4 1200 26 1-1 5-3 11000 4.4 39.3 1200 27 1-1 5-19 11000 4.5 38.4 1200 28 1-93 2-4 11550 4.2 43.2 1200 29 1-93 2-5 10500 4.0 41.3 1400 30 1-93 2-6 10500 4.0 41.3 1400 31 1-93 2-9 10500 4.1 40.3 1100

TABLE-US-00002 TABLE 2 Second Power First host host Luminance Voltage efficiency LT70 Example compound compound (cd/m2) (V) (Im/W) (h) 32 1-93 2-10 10500 4.1 40.3 1200 33 1-93 2-13 10500 4.1 40.3 1200 34 1-93 2-21 11550 4.4 41.1 1100 35 1-93 2-22 11550 4.1 44.3 1100 36 1-93 2-23 11550 4.1 44.3 1100 37 1-93 2-24 11550 4.5 40.2 1100 38 1-93 2-27 11550 4.2 43.2 1100 39 1-93 2-28 11550 4.2 43.2 1100 40 1-93 3-1 10500 4.3 38.3 1100 41 1-93 3-5 10500 4.2 39.3 1100 42 1-93 3-8 10500 4.2 39.3 1100 43 1-93 3-12 10500 4.1 40.3 1100 44 1-93 3-16 10500 4.1 40.3 1100 45 1-93 3-24 11500 3.8 47.8 1300 46 1-93 3-26 11500 3.7 49.2 1300 47 1-93 3-33 11000 3.6 48.4 1300 48 1-93 3-45 11500 4.0 45.3 1200 49 1-93 4-3 11500 4.7 38.2 1300 50 1-93 4-22 11500 4.7 38.2 1300 51 1-93 5-3 11500 4.6 39.1 1300 52 1-93 5-19 11500 4.7 38.2 1300 53 1-34 2-5 10000 3.8 41.3 1200 54 1-34 2-6 10000 3.8 41.3 1200 55 1-34 3-24 11000 3.4 50.8 1200 56 1-34 3-33 10500 3.4 48.5 1200 57 1-34 3-45 11000 3.6 48.0 1200 58 1-34 4-3 11000 4.3 40.2 1200 59 1-34 4-22 11000 4.3 40.2 1200 60 1-34 5-3 11000 4.2 41.1 1200 61 1-34 5-19 11000 4.3 40.2 1200

TABLE-US-00003 TABLE 3 Second Power First host host Luminance Voltage efficiency LT70 Example compound compound (cd/m2) (V) (Im/W) (h) 62 1-85 2-5 10000 4.0 39.3 1200 63 1-85 2-6 10000 4.0 39.3 1200 64 1-85 3-24 11000 3.6 48.0 1100 65 1-85 3-33 10500 3.4 48.5 1100 66 1-85 3-45 11000 3.8 45.5 1100 67 1-85 4-3 11000 4.5 38.4 1100 68 1-85 4-22 11000 4.5 38.4 1100 69 1-85 5-3 11000 4.4 39.3 1100 70 1-85 5-19 11000 4.5 38.4 1100 71 1-94 2-5 10000 4.0 39.3 1500 72 1-94 2-6 10000 4.0 39.3 1500 73 1-94 3-24 11000 3.6 48.0 1300 74 1-94 3-33 10500 3.4 48.5 1300 75 1-94 3-45 11000 3.8 45.5 1200 76 1-94 4-3 11000 4.5 38.4 1300 77 1-94 4-22 11000 4.5 38.4 1300 78 1-94 5-3 11000 4.4 39.3 1300 79 1-94 5-19 11000 4.5 38.4 1300 80 1-102 2-5 10000 4.0 39.3 1500 81 1-102 2-6 10000 4.0 39.3 1500 82 1-102 3-24 11000 3.6 48.0 1300 83 1-102 3-33 10500 3.4 48.5 1300 84 1-102 3-45 11000 3.8 45.5 1200 85 1-102 4-3 11000 4.5 38.4 1300 86 1-102 4-22 11000 4.5 38.4 1300 87 1-102 5-3 11000 4.4 39.3 1300 88 1-102 5-19 11000 4.5 38.4 1300 89 1-1 2-6 10000 3.8 41.3 1300 90 1-1 3-24 11000 3.6 48.0 1200 91 1-1 4-22 11000 4.5 38.4 1200

TABLE-US-00004 TABLE 4 Second Power First host host Luminance Voltage efficiency LT70 Example compound compound (cd/m2) (V) (Im/W) (h) 92 1-1 5-19 11000 4.5 38.4 1200 93 1-102 2-6 10000 4.0 39.3 1500 94 1-102 3-24 11000 3.6 48.0 1300 95 1-102 4-22 11000 4.5 38.4 1300 96 1-102 5-19 11000 4.5 38.4 1300

Comparative Example 1

[0144] An organic electroluminescent device was produced in the same manner as in Example 1 except that compound 1-1 was used alone as the host instead of the hosts of Example 1. The thickness of the light-emitting layer and the concentration of the light-emitting dopant were the same as those in Example 1.

Comparative Examples 2 to 15

[0145] Organic electroluminescent devices were produced in the same manner as Comparative Example 1 except that each of compounds shown in Table 5 was used alone instead of the host of Comparative Example 1.

Comparative Examples 16 to 24

[0146] Organic electroluminescent devices were produced in the same manner as Example 1 except that compound A was used as the first host and compound 2-5, 2-6, 3-24, 3-33, 3-45, 4-3, 4-22, 5-3 or 5-19 was used as the second host instead of those of Example 1.

Comparative Example 25 to 33

[0147] Organic electroluminescent devices were produced in the same manner as in Comparative Examples 16 to 24 except that compound B was used as the first host instead of those of Comparative Examples 16 to 24.

Comparative Example 34 to 42

[0148] Organic electroluminescent devices were produced in the same manner as in Comparative Examples 16 to 24 except that compound C was used as the first host instead of those of Comparative Example 16 to 24.

[0149] Evaluation results of the produced organic electroluminescent devices are shown in Tables 5 to 6.

TABLE-US-00005 TABLE 5 Com- Second Power parative First host host Luminance Voltage efficiency LT70 Example compound compound (cd/m2) (V) (Im/W) (h) 1 1-1 — 6000 3.4 27.7 500 2 1-34 — 6000 3.2 29.5 500 3 1-85 — 6500 3.5 29.2 500 4 1-93 — 6500 3.6 28.4 550 5 1-102 — 6500 3.6 28.4 550 6 — 2-4 9000 4.8 29.5 500 7 — 2-5 9000 4.8 29.5 550 8 — 2-6 8000 4.9 25.6 500 9 — 3-24 6500 4.1 24.9 500 10 — 3-33 6500 4.0 25.5 500 11 — 3-45 6500 4.2 24.3 400 12 — 4-3 8000 4.5 27.9 450 13 — 4-22 8000 4.4 28.6 450 14 — 5-3 8000 4.3 29.2 450 15 — 5-19 8000 4.2 29.9 500 16 A 2-5 10000 4.5 34.9 750 17 A 2-6 10000 4.5 34.9 750 18 A 3-24 10000 4.4 35.7 700 19 A 3-33 10000 4.4 35.7 700 20 A 3-45 10000 4.4 35.7 700 21 A 4-3 10000 4.5 34.9 650 22 A 4-22 10000 4.5 34.9 650 23 A 5-3 10000 4.5 34.9 650 24 A 5-19 10000 4.5 34.9 700 25 B 2-5 10500 4.4 37.5 700 26 B 2-6 10500 4.4 37.5 750 27 B 3-24 10000 4.3 36.5 650 28 B 3-33 10000 4.3 36.5 650 29 B 3-45 10000 4.3 36.5 650 30 B 4-3 10000 4.4 35.7 650

TABLE-US-00006 TABLE 6 Com- Second Power parative First host host Luminance Voltage efficiency LT70 Example compound compound (cd/m2) (V) (Im/W) (h) 31 B 4-22 10000 4.4 35.7 650 32 B 5-3 10000 4.4 35.7 650 33 B 5-19 10000 4.4 35.7 650 34 C 2-5 10000 4.4 35.7 750 35 C 2-6 10000 4.4 35.7 750 36 C 3-24 10000 4.4 35.7 650 37 C 3-33 10000 4.3 36.5 650 38 C 3-45 10000 4.4 35.7 650 39 C 4-3 10000 4.4 35.7 650 40 C 4-22 10000 4.5 34.9 650 41 C 5-3 10000 4.5 34.9 650 42 C 5-19 10000 4.5 34.9 700

[0150] From Tables 1 to 4, it is understood that Examples 1 to 96 improved the power efficiency and the lifetime characteristics, and exhibited good characteristics.

Example 97

[0151] On a glass substrate on which an anode made of ITO with a film thickness of 110 nm was formed, respective thin films were laminated by a vacuum evaporation method at a degree of vacuum of 4.0×10.sup.−5 Pa. First, HAT-CN was formed with a thickness of 25 nm as a hole injection layer on ITO, and next, NPD was formed with a thickness of 45 nm as a hole transport layer. Next, HT-1 was formed with a thickness of 10 nm as an electron blocking layer. Then, compound 1-1 as a first host, compound 2-4 as a second host and Ir(piq).sub.2acac as a light-emitting dopant were co-vapor-deposited from different vapor deposition sources, respectively, to form a light-emitting layer with a thickness of 40 nm. In this case, co-vapor deposition was performed under a vapor deposition condition such that the concentration of Ir(piq).sub.2acac was 6.0 wt %. Next, ET-1 was formed with a thickness of 37.5 nm as an electron transport layer. Then, LiF was formed with a thickness of 1 nm as an electron injection layer on the electron transport layer. Finally, Al was formed with a thickness of 70 nm as a cathode on the electron injection layer to produce an organic electroluminescent device.

Examples 98 to 182

[0152] Organic electroluminescent devices were produced in the same manner as in Example 97 except that compounds shown in Tables 7 to 9 were used as the first host and the second host instead of those of Example 97.

[0153] Evaluation results of the produced organic electroluminescent devices are shown in Tables 7 to 9. LT95 used therein is a time period needed for the initial luminance to be reduced to 95% thereof, and it represents lifetime characteristics.

TABLE-US-00007 TABLE 7 Second Power First host host Luminance Voltage efficiency LT95 Example compound compound (cd/m2) (V) (Im/W) (h) 97 1-1 2-4 5500 4.0 21.6 200 98 1-1 2-5 5000 3.8 20.7 250 99 1-1 2-6 5000 3.8 20.7 250 100 1-1 2-9 5000 3.9 20.1 200 101 1-1 2-10 5000 3.9 20.1 200 102 1-1 2-13 5000 3.9 20.1 200 103 1-1 2-21 5500 4.2 20.6 200 104 1-1 2-22 5500 3.9 22.2 200 105 1-1 2-23 5500 3.9 22.2 200 106 1-1 2-24 5500 4.3 20.1 200 107 1-1 2-27 5500 4 21.6 200 108 1-1 2-28 5500 4 21.6 200 109 1-1 3-1 5000 4.1 19.2 200 110 1-1 3-5 5000 4 19.6 200 111 1-1 3-8 5000 4 19.6 200 112 1-1 3-12 5000 3.9 20.1 200 113 1-1 3-16 5000 3.9 20.1 200 114 1-1 3-24 5500 3.6 24.0 250 115 1-1 3-26 5500 3.5 24.7 250 116 1-1 3-33 5000 3.4 23.1 250 117 1-1 3-45 5500 3.8 22.7 200 118 1-1 4-3 5500 4.5 19.2 250 119 1-1 4-22 5500 4.5 19.2 250 120 1-1 5-3 5500 4.4 19.6 250 121 1-1 5-19 5500 4.5 19.2 250 122 1-93 2-4 5500 4.2 20.6 250 123 1-93 2-5 5000 4.0 19.7 300 124 1-93 2-6 5000 4.0 19.7 300 125 1-93 2-9 5000 4.1 19.2 200 126 1-93 2-10 5000 4.1 19.2 250

TABLE-US-00008 TABLE 8 Second Power First host host Luminance Voltage efficiency LT95 Example compound compound (cd/m2) (V) (Im/W) (h) 127 1-93 2-13 5000 4.1 19.2 250 128 1-93 2-21 5500 4.4 19.6 200 129 1-93 2-22 5500 4.1 21.1 200 130 1-93 2-23 5500 4.1 21.1 200 131 1-93 2-24 5500 4.5 19.1 200 132 1-93 2-27 5500 4.2 20.6 200 133 1-93 2-28 5500 4.2 20.6 200 134 1-93 3-1 5000 4.3 18.2 200 135 1-93 3-5 5000 4.2 18.7 200 136 1-93 3-8 5000 4.2 18.7 200 137 1-93 3-12 5000 4.1 19.2 200 138 1-93 3-16 5000 4.1 19.2 200 139 1-93 3-24 5500 3.8 22.9 250 140 1-93 3-26 5500 3.7 23.5 250 141 1-93 3-33 5000 3.6 22.0 250 142 1-93 3-45 5500 4.0 21.7 250 143 1-93 4-3 5500 4.7 18.3 250 144 1-93 4-22 5500 4.7 18.3 250 145 1-93 5-3 5500 4.6 18.7 250 146 1-93 5-19 5500 4.7 18.3 250 147 1-34 2-5 5000 3.8 20.7 250 148 1-34 2-6 5000 3.8 20.7 250 149 1-34 3-24 5500 3.4 25.4 250 150 1-34 3-33 5000 3.4 23.1 250 151 1-34 3-45 5500 3.6 24.0 250 152 1-34 4-3 5500 4.3 20.1 250 153 1-34 4-22 5500 4.3 20.1 250 154 1-34 5-3 5500 4.2 20.6 250 155 1-34 5-19 5500 4.3 20.1 250 156 1-85 2-5 5000 4.0 19.6 250

TABLE-US-00009 TABLE 9 Second Power First host host Luminance Voltage efficiency LT95 Example compound compound (cd/m2) (V) (Im/W) (h) 157 1-85 2-6 5000 4.0 19.6 250 158 1-85 3-24 5500 3.6 24.0 200 159 1-85 3-33 5000 3.4 23.1 200 160 1-85 3-45 5500 3.8 22.7 200 161 1-85 4-3 5500 4.5 19.2 200 162 1-85 4-22 5500 4.5 19.2 200 163 1-85 5-3 5500 4.4 19.6 200 164 1-85 5-19 5500 4.5 19.2 200 165 1-94 2-5 5000 4.0 19.6 300 166 1-94 2-6 5000 4.0 19.6 300 167 1-94 3-24 5500 3.6 24.0 250 168 1-94 3-33 5000 3.4 23.1 250 169 1-94 3-45 5500 3.8 22.7 250 170 1-94 4-3 5500 4.5 19.2 250 171 1-94 4-22 5500 4.5 19.2 250 172 1-94 5-3 5500 4.4 19.6 250 173 1-94 5-19 5500 4.5 19.2 250 174 1-102 2-5 5000 4.0 19.6 300 175 1-102 2-6 5000 4.0 19.6 300 176 1-102 3-24 5500 3.6 24.0 250 177 1-102 3-33 5000 3.4 23.1 250 178 1-102 3-45 5500 3.8 22.7 250 179 1-102 4-3 5500 4.5 19.2 250 180 1-102 4-22 5500 4.5 19.2 250 181 1-102 5-3 5500 4.4 19.6 250 182 1-102 5-19 5500 4.5 19.2 250

Comparative Example 43

[0154] Organic electroluminescent devices were produced in the same manner as in Example 97 except that compound 1-1 was used alone as the host instead of the hosts of Example 97. The thickness of the light-emitting layer and the concentration of the light-emitting dopant were the same as those in Example 97.

Comparative Example 44 to 57

[0155] Organic electroluminescent devices were produced in the same manner as in Comparative Example 43 except that each of compounds shown in Table 10 was used alone instead of the host of Comparative Example 43.

Comparative Example 58 to 66

[0156] Organic electroluminescent devices were produced in the same manner as in Example 97 except that compound A was used as the first host, and compound 2-5, compound 2-6, compound 3-24, compound 3-33, compound 3-45, compound 4-3, compound 4-22, compound 5-3 or compound 5-19 was used as the second host instead of those of Example 97.

Comparative Examples 67 to 75

[0157] Organic electroluminescent devices were produced in the same manner as in Comparative Examples 58 to 66 except that compound B was used as the first host instead of that of Comparative Examples 58 to 66.

Comparative Examples 76 to 84

[0158] Organic electroluminescent devices were produced in the same manner as in Comparative Examples 58 to 66 except that compound C was used as the first host instead of that of Comparative Examples 58 to 66.

[0159] Evaluation results of the produced organic electroluminescent devices are shown in in Tables 10 to 11.

TABLE-US-00010 Table 10 Com- Second Power parative First host host Luminance Voltage efficiency LT95 Example compound compound (cd/m2) (V) (Im/W) (h) 43 1-1 — 3000 3.4 13.9 100 44 1-34 — 2500 3.2 12.3 100 45 1-85 — 3000 3.5 13.5 100 46 1-93 — 3000 3.6 13.1 100 47 1-102 — 3000 3.7 12.7 110 48 — 2-4 3500 4.8 11.5 90 49 — 2-5 3500 4.8 11.5 110 50 — 2-6 3500 4.9 11.2 110 51 — 3-24 3500 4.1 13.4 100 52 — 3-33 3500 4.0 13.7 100 53 — 3-45 3000 4.2 11.2 90 54 — 4-3 3500 4.5 12.2 100 55 — 4-22 3500 4.4 12.5 100 56 — 5-3 3500 4.3 12.8 100 57 — 5-19 3500 4.2 13.1 100 58 A 2-5 4000 4.4 14.3 150 59 A 2-6 4000 4.4 14.3 150 60 A 3-24 4000 4.4 14.3 150 61 A 3-33 4000 4.4 14.3 150 62 A 3-45 4000 4.4 14.3 120 63 A 4-3 4000 4.6 13.7 150 64 A 4-22 4000 4.6 13.7 150 65 A 5-3 4000 4.6 13.7 130 66 A 5-19 4000 4.5 14.0 130 67 B 2-5 4000 4.6 13.7 150 68 B 2-6 4000 4.6 13.7 150 69 B 3-24 4000 4.3 14.6 150 70 B 3-33 4000 4.2 15.0 150 71 B 3-45 4000 4.5 14.0 120 72 B 4-3 4000 4.6 13.7 150

TABLE-US-00011 TABLE 11 Com- Second Power parative First host host Luminance Voltage efficiency LT95 Example compound compound (cd/m2) (V) (Im/W) (h) 73 B 4-22 4000 4.5 14.0 150 74 B 5-3 4000 4.4 14.3 150 75 B 5-19 4000 4.4 14.3 150 76 C 2-5 4000 4.5 14.0 150 77 C 2-6 4000 4.6 13.7 150 78 C 3-24 4000 4.4 14.3 150 79 C 3-33 4000 4.3 14.6 150 80 C 3-45 4000 4.7 13.4 120 81 C 4-3 4000 4.6 13.7 150 82 C 4-22 4000 4.5 14.0 150 83 C 5-3 4000 4.5 14.0 130 84 C 5-19 4000 4.5 14.0 130

[0160] From Tables 7 to 9, it is understood that Examples 97 to 182 improved the power efficiency and the lifetime characteristics, and exhibited good characteristics.

[0161] Compounds used in Examples are shown below.

##STR00119## ##STR00120##

INDUSTRIAL APPLICABILITY

[0162] The organic electroluminescent device of the present invention is operable at a low voltage and is able to achieve high efficiency and extended life.