ORGANIC ELECTRONIC MATERIAL CONTAINING NITROGEN ATOM HETEROCYCLIC RING, PREPARATION METHOD THEREFOR AND APPLICATION THEREOF
20230086539 · 2023-03-23
Assignee
Inventors
Cpc classification
C07D401/10
CHEMISTRY; METALLURGY
H10K85/615
ELECTRICITY
Y02E10/549
GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
International classification
Abstract
The present disclosure provides an organic electronic material containing a nitrogen heterocycle and a preparation method and use thereof, and relates to the technical field of organic electroluminescence. Nitrogen-containing heterocycles such as pyridine, triazine or pyrimidine are introduced into a main structure of phenanthrene, such that the electronegativity of the material is enhanced, and the electron transport performance and the thermal stability of a compound are improved. The organic electron transport material provided by the present disclosure has a relatively good thermal stability, a high luminous efficiency and a high luminous purity. An organic light-emitting device prepared from the organic electronic material has effects of reducing a driving voltage, improving a luminous efficiency, enabling color purity to be excellent and prolonging a service life.
Claims
1. An organic electronic material containing a nitrogen heterocycle, wherein the organic electronic material contains a compound of the following structural formula (I) or (II): ##STR00022## and wherein Py is substituted or unsubstituted C.sub.5-C.sub.30 pyridine; R is hydrogen, C.sub.1-C.sub.4 alkyl, and substituted or unsubstituted C.sub.6-C.sub.30 aryl; Ar.sub.1 and Ar.sub.2 are independently selected from substituted or unsubstituted C.sub.6-C.sub.30 aryl; and at least one of Z.sub.1, Z.sub.2 and Z.sub.3 is N and the others are CH.
2. The organic electronic material according to claim 1, wherein R is independently selected from the group consisting of hydrogen, phenyl, tolyl, biphenyl, or naphthyl; and Ar.sub.1 and Ar.sub.2 are independently selected from the group consisting of phenyl, tolyl, biphenyl, naphthyl, phenanthryl, anthracyl, perylenyl, phenylnaphthyl, naphthylphenyl, diphenylphenyl, 9,9-dimethylfluorenyl, 9,9-diphenylfluorenyl, 9,9-spirobifluorenyl, dibenzofuranyl, dibenzothienyl, or benzophenanthryl.
3. The organic electronic material according to claim 1, wherein Py is pyridyl, R is phenyl, and Ar.sub.1 and Ar.sub.2 are independently selected from the group consisting of phenyl, biphenyl or naphthyl.
4. The organic electronic material according to claim 1, wherein the organic electronic material contains any one of the following compounds CQ1-CQ28: ##STR00023## ##STR00024## ##STR00025## ##STR00026## ##STR00027## ##STR00028## ##STR00029## ##STR00030## ##STR00031##
5. The organic electronic material according to claim 1, wherein a method for preparing the compound of structural formula (I) or (II) comprises the following steps: (A1) synthesis of compound b: preparing compound b by a Sonogashira reaction of o-bromoiodobenzene with an alkynyl compound; (A2) synthesis of compound c: preparing compound c by a Suzuki reaction of compound b with halogenated phenylboronic acid; (A3) synthesis of compound d: preparing compound d by reacting compound c with iodine chloride or bromosuccinimide, wherein a solvent is dichloromethane, chloroform, tetrahydrothran, 1,2-dichloroethane, acetonitrile, N,N-dimethylformamaide, N,N-dimethylacetamide or dioxane; (A4) synthesis of compound f: obtaining compound f by a Suzuki reaction of compound d and pyridinylboronic acid e or a pyridinylboronic ester; and (A5) synthesis of compound of structural formula (I): obtaining compound of structural formula (I) by a Suzuki reaction of compound j with boronate ester h; or (B1) synthesis of compound b: preparing compound b by a Sonogashira reaction of o-bromoiodobenzene with an alkynyl compound; (B2) synthesis of compound c: preparing compound c by a Suzuki reaction of compound b with halogenated phenylboronic acid; (B3) synthesis of compound d: in a reaction of step 3, preparing compound d by reacting compound c with iodine chloride or bromosuccinimide, wherein a solvent is dichloromethane, chloroform, tetrahydrofuran, 1,2-dichloroethane, acetonitrile, N,N-dimethylfonnamide, N,N-dimethylacetamide or dioxane; (B4) synthesis of compound j: obtaining cornpound j by a Suzuki reaction of compound d and boronate ester h; and (B5) synthesis of compound of structural formula (II): obtaining compound of structural formula (II) by a Suzuki reaction of compound j with pyridinylboronic acid e or a pyridinylboronic ester; ##STR00032## ##STR00033## ##STR00034##
6. An organic light-emitting device, wherein the organic light-emitting device comprises an, anode, a cathode and an organic layer; the organic layer comprises one or more than one of a light-emitting layer, a hole injection layer, a hole transport layer, a hole blocking layer, an electron injection layer or an electron transport layer; and at least one of the organic layer comprises the organic electronic material according to claim 1.
7. The organic light-emitting device according to claim 6, wherein the light-emitting layer in the organic layer comprises the organic electronic material according to claim 1.
8. The organic light-emitting device according to claim 6 wherein the electron transport layer or the electron injection layer in the organic layer comprises the organic electronic material according to claim 1.
9. The organic light-emitting device according to claim 6, wherein the hole blocking layer in the organic layer comprises the organic electronic material according to claim 1.
10. Use of the organic electronic material according to claim 1, wherein the organic electronic material is usable for producing an organic light-emitting device, an organic solar cell, an organic thin film transistor, an organic photodetector, an organic field effect transistor, an organic integrated circuit, and an organic photoreceptor.
Description
BRIEF DESCRIPTION OF DRAWINGS
[0040]
[0041]
[0042]
[0043] 110, glass substrate; 120, anode; 130, hole injection layer; 140, hole transport layer; 150, blocking layer; 160, light-emitting layer; 170, electron transport layer; 180, electron injection layer; and 190, cathode;
[0044]
[0045]
[0046]
DETAILED DESCRIPTION OF EMBODIMENTS
[0047] The present disclosure will be further described below with reference to the accompanying drawings and specific embodiments, but the following examples are only preferred examples of the present disclosure, not all. All other examples obtained by those skilled in the art based on the examples of the embodiments without creative efforts shall fall within the protection scope of the present disclosure.
EXAMPLE 1
[0048] An organic electronic material containing a nitrogen heterocycle was provided, the organic electronic material contained compound CQ1 and compound CQ1 had the following synthetic route:
##STR00014##
[0049] Synthesis of intermediate CQ1-1:
[0050] o-bromoiodobenzene (52.2 g, 184.5 mmol), phenylacetylene (18.85 g, 184.5 mmol) and triethylamine (260 mL) were added into a flask, cuprous iodide (0.35 g, 1.84 mmol) and triphenylphosphine palladium chloride (0.5 g, 0.7 mmol) were added under nitrogen protection, a reaction was carried out at a room temperature for 0.5 h while stirring was carried out, the reaction was stopped, an obtained product was filtered, the triethylamine was concentrated off, and 46.8 g of a yellow oily liquid with a yield of 98% was obtained.
[0051] .sup.1H NMR (400 MHz, CDCl.sub.3, δ): 7.62-7.64 (m, 2H), 7.57 (dd, J=7.2, 1.2 Hz, 1H), 7.51 (dd, J=5.2, 1.2 Hz, 1H), 7.32-7.40 (m, 5H).
[0052] Synthesis of intermediate CQ1-2:
[0053] intermediate CQ1-1 (13.4 g, 52.1 mmol), p-chlorobenzeneboronic acid (8.5 g, 54.4 mmol) and potassium carbonate (14.4 g, 104.2 mmol) were added into the flask, toluene (80 mL), tetrahydrofuran (40 mL) and deionized water (40 mL) were added, triphenylphosphine palladium chloride (0.27 g, 0.38 mmol) was added under nitrogen protection, a reaction was carried out under reflux for 3 h, the reaction was stopped, cooling and liquid separation were carried out, and an organic phase was washed with water to be neutral and concentrated to obtain 16 g of a yellow oily liquid.
[0054] .sup.1H NMR (400 MHz, CDCl.sub.3,δ): 7.60-7.66(m, 3H), 7.30-7.44(m, 10H).
[0055] Synthesis of intermediate CQ1-3:
[0056] intermediate CQ1-2 (15 g, 51.9 mmol) and dichloromethane (225 mL) were added into the flask, a temperature was reduced to 0-5° C, iodine chloride (10 g, 61.6 mmol) was dissolved in dichloromethane (75 mL) and dropwise added into the solution, after the dropwise adding, the solution was stirred for 0.5 h, 200 mL of a 5% sodium sulfite aqueous solution was dropwise added to quench a reaction until an obtained solution was neutral, liquid separation, drying, concentration and passing through a column were performed and thus 13 g of a light yellow solid with a yield of 60% was obtained.
[0057] .sup.1H NMR (400 MHz, CDCl.sub.3, δ): 8.61-8.67 (m, 2H), 8.45-8.48 (m, 1H), 7.68-7.75 (m, 2H), 7.53-7.62 (m, 4H), 7.37 (d, J=2.0 Hz, 1H), 7.26-7.29 (m, 2H).
[0058] Synthesis of intermediate CQ1-4:
[0059] intermediate CQ1-3 (13.6 g, 32.8 mmol), 3-pyridylboronic acid pinacol ester (10 g, 48.8 mmol) and potassium carbonate (13.6 g, 98.4 mmol) were added into the flask, toluene (81 mL), ethanol (27 mL) and deionized water (27 mL) were added, triphenylphosphine palladium chloride (0.68 g, 0.97 mmol) was added under nitrogen protection, a reaction was carried out under reflux for 6 h, cooling and liquid separation were performed, an organic phase was washed with water, a part of a solvent was concentrated off, a solid was precipitated, an obtained solution was filtered, a filter cake was recrystallized once with toluene, and drying was performed and 9.7 g of a product with a yield of 81% was obtained.
[0060] .sup.1NMR (400 MHz, CDCl.sub.3, δ): 8.73-8.77 (m, 2H), 8.42-8.46 (m, 2H), 7.63-7.73 (m, 2H), 7.45-7.56 (m, 4H), 7.09-7.29 (m, 6H).
[0061] Synthesis of compound CQ1:
[0062] intermediate CQ1-4 (2 g, 5.5 mmol), 2,4-diphenyl-6-(4-phenylboronic acid pinacol)pyrimidine (2.5 g, 5.7 mmol) and potassium carbonate (2.3 g, 16.6 mmol) were added into the flask, toluene (20 mL), ethanol (10 mL) and deionized water (10 mL) were added, palladium acetate (0.06 g, 0.27 mmol) and x-phos (0.12 g, 0.54 mmol) were added under nitrogen, protection, a reaction was carried out under reflux for 2 h, a large amount of, a solid was precipitated, cooling and filtration were performed, a filter cake was washed with water to be neutral and washed with ethanol, and the filter cake was dried. The filter cake was recrystallized once with toluene and dried to obtain 2.5 g of a product with a yield of 71%.
[0063] .sup.1H NMR (400 MHz, CDCl.sub.3, δ): 8.86 (d,1H), 8.64-8.73 (m, 3H), 8.34-8.36 (m, 2H), 8.05-8.15 (m, 5H), 7.95-7.98 (m, 1H), 7.89-7.92 (m,2H), 7.78-7.81 (m, 2H), 7.64-7.67 (m, 2H), 7.36-7.60(m,14H). MS (ESI, m/z): [M+H].sup.+:638.74.
EXAMPLE 2
[0064] An organic electronic material containing a nitrogen heterocycle was provided, the organic electronic material contained compound CQ2 and compound CQ2 had the following synthetic route:
##STR00015##
[0065] Synthesis of compound CQ2
[0066] intermediate CQ1-4 (2 g, 5.5 mmol), 2,4-diphenyl-6-(4-phenylboronic acid pinacol)-1,3,5-triazine (2.5 g, 5.7 mmol) and potassium carbonate (2.3 g, 16.6 mmol) were added into the flask, toluene (20 mL), ethanol (10 mL) and deionized water (10 mL) were added, palladium acetate (0.06 g, 0.27 mmol) and x-phos (0.12 g, 0.54 mmol) were added under nitrogen protection, a reaction was carried out under reflux for 2 h, a large amount of a solid was precipitated, cooling and filtration were performed, a filter cake was washed with water to be neutral and washed with ethanol, and the filter cake was dried. The filter cake was recrystallized once with toluene and dried to obtain 2.2 g of a product with a yield of 63%. The obtained product was compound CQ2 whose proton nuclear magnetic resonance spectrum was shown in
[0067] .sup.1H NMR: (400 MHz, CDCl.sub.3) δ 8.77-8.95(m, 8H), 8.47-8.48(m, 2H), 8.05-8.08(m, 1H), 7.90(d, 1H),7.72-7.77(m, 3H), 7.50-7.62(m, 9H), 7.27-7.32(m, 3H), 7.19-7.23(m, 3H). MS (ESI, m/z): [M+H].sup.+: 639.52.
EXAMPLE 3
[0068] An organic electronic material containing a nitrogen heterocycle was provided, the organic electronic material contained compound CQ5 and compound CQ5 had the following synthetic route:
##STR00016##
[0069] Synthesis of compound CQ5
[0070] intermediate CQ1-4 (8 g, 21.9 mmol), 2,4-diphenyl-6-(3-phenylboronic acid pinacol)-1,3,5-triazine (10 g, 23.0 mmol) and potassium carbonate (9.1 g, 65.8 mmol) were added into the flask, toluene (80 mL), ethanol (40 mL) and deionized water (40 mL) were added, palladium acetate (0.24 g, 1.1 mmol) and x-phos (0.48 g, 2.2 mmol) were added under nitrogen protection, a reaction was carried out under reflux for 2 h, a large amount of a solid was precipitated, cooling and filtration were performed, a filter cake was washed with water to be neutral and washed with ethanol, and the filter cake was dried. The filter cake was recrystallized once with toluene and dried to obtain 4.6 g of a product with a yield of 33%.
[0071] .sup.1H NMR (400 MHz, CDCl.sub.3, δ): 8.88-8.98 (m, 3H) , 8.74-8.78(m,5H), 8.47-8.49(m, 2H), 8.10-8.13(m, 1H), 7.94(s, 1H), 7.73-7.81(m, 2H), 7.51-7.64(m, 10H), 7.21-7.30(m, 6H). MS (ESI, m/z): [M+H]+ : 639.34.
EXAMPLE 4
[0072] An organic electronic material containing a nitrogen heterocycle was provided, the organic electronic material contained compound CQ7 and compound CQ7 had the following synthetic route:
##STR00017##
[0073] Synthesis of compound CQ7
[0074] intermediate CQ1-4 (2 g, 5.5 mmol), 2-phenyl-4-biphenyl-6-(3-phenylboronic acid pinacol)-1,3,5-triazine (2.9 g, 5.7 mmol) and potassium carbonate (2.3 g, 16.6 rnmol) were added into the flask, toluene (20 mL), ethanol (10 mL) and deionized water (10 mL) were added, palladium acetate (0.06 g, 0.27 mmol) and x-phos (0.12 g, 0.54 mmol) were added under nitrogen protection, a reaction was carried out under reflux for 3 h, a large amount of a solid was precipitated, cooling and filtration were performed, a filter cake was washed with water to be neutral and washed with ethanol, and the filter cake was dried. The filter cake was recrystallized once with toluene and dried to obtain 2.9 g of a product with a yield of 74%.
[0075] .sup.1H NMR (400 MHz, CDCl.sub.3 , δ) : 8.92 (d, J=2.0 Hz, 1H), 8.86 (d, 1H), 8.68-8.73 (m, 2H), 8.64-8.66 (m, 1H), 8.39-8.43 (m, 2H), 8.12-8.14 (m, 1H), 8.06-8.09 (m, 1H), 7.99-8.05 (m, 2H), 7.95-7.98 (m, 2H), 7.89-7.92 (m, 1H), 7.64-7.72 (m, 3H), 7.42-7.61 (m, 15H), 7.35-7.40 (m, 2H), MS (ESI, m/z): [M+H].sup.+: 715.48.
EXAMPLE 5
[0076] An organic electronic material containing a nitrogen heterocycle was provided, the organic electronic material contained compound CQ10 and compound CQ10 had the following synthetic route:
##STR00018##
[0077] Synthesis of intermediate CQ10-1:
[0078] intermediate CQ1-1 (15 g, 58.3 mmol), o-chlorophenylboronic acid (10 g. 63.9 mmol) and potassium carbonate (20 g, 144.7 mmol) were added into the flask, toluene (90 mL), tetrahydrofuran (45 mL) and deionized water (45 mL) were added, triphenylphosphine palladium chloride (0.3 g, 0.43 rnmol) was added under nitrogen protection, a reaction was carried out under reflux for 4 h, the reaction was stopped, cooling and liquid separation were carried out, and an organic phase was washed with water to be neutral and concentrated to obtain 11.5 g of a yellow oily liquid with a yield of 68%.
[0079] .sup.1H NMR (400 MHz, CDCl.sub.3, δ): 7.67-7.70 (m, 1H), 7.61-7.64 (m, 2H), 7.51-7.56 (m, 3H), 7.45-7.49 (m, 1H), 7.38-7.44 (m, 3H), 7.34-7.37 (m, 3H).
[0080] Synthesis of intermediate CQ10-2:
[0081] intermediate CQ1-1 (9.5 g, 32.9 mmol) and dichloromethane (150 mL) were added into the flask, a temperature was reduced to 0-5° C., iodine chloride (6.4 g, 39.4 mmol) was dissolved in dichloromethane (50 mL) and dropwise added into the solution, after the dropwise adding, the solution was stirred for 0.5 h, 150 mL of a 5% sodium sulfite aqueous solution was dropwise added to quench a reaction until an obtained solution was neutral, liquid separation, drying, concentration and passing through a column with petroleum ether were performed and thus 13.9 g of a light yellow oily liquid was obtained.
[0082] .sup.1 H NMR (400 MHz, CDCl.sub.3, δ): 9.77-9.80 (m, 1H), 8.52-8.54 (rn, 1H), 7.71-7.74 (m, 3H), 7.54-7.56 (m, 3H), 7.35-7.36 (m, 1H), 7.25-7.30 (m, 3H).
[0083] Synthesis of intermediate CQ10-3:
[0084] intermediate CQ10-2 (12 g, 28.9 mmol), 3-pyridylboronic acid pinacol ester (8.9 g, 43.4 mmol) and potassium carbonate (12 g, 86.8 minol) were added into the flask, toluene (120 mL), ethanol (60 mL) and deionized water (60 mL) were added, triphenylphosphine palladium chloride (0.6 g, 0.85 mmol) was added under nitrogen protection, a reaction was carried out under reflux for 6 h, cooling and liquid separation were performed, an organic phase was washed with water, a part of a solvent was concentrated off, a solid was precipitated, an obtained solution was filtered, a filter cake was recrystallized once with toluene, and drying was performed and 7.9 g of a product with a yield of 75% was obtained.
[0085] .sup.1H NMR (400 MHz, CDCl.sub.3, δ): 9.76 (d, 1H), 8.41-8.46 (m, 2H), 7.66-7.79 (m, 2H), 7.43-7.57 (m, 4H), 7.34-7.38 (m, 1H), 7.07-7.29 (m, 6H).
[0086] Synthesis of compound CQ10:
[0087] intermediate CQ 1-4 (2 g, 5.5 mmol), 2,4-diphenyl-6-(3-phenylboronic acid pinacol)-1,3,5-triazine (2.5 g, 5.7 mmol) and potassium carbonate (2.3 g, 16.6 mmol) were added into the flask, toluene (20 mL), ethanol (10 mL) and deionized water (10 mL) were added, palladium acetate (0.06 g, 0.27 mmol) and x-phos (0.12 g, 0.54 mmol) were added under nitrogen protection, a reaction was carried out under reflux for 2 h, cooling and filtration were performed, a filter cake was washed with water to be neutral and washed with ethanol, and the filter cake was dried. The filter cake was recrystallized once with toluene and dried to obtain 2.8 g of a product with a yield of 80%.
[0088] .sup.1H NMR (400 MHz, CDCl.sub.3, δ): 9.00-9.01 (d, 1H), 8.88-8.89 (m, 1H), 8.76-8.79 (m, 4H), 8.45-8.49 (m, 2H), 8.02-8.04 (m, 1H), 7.42-7.68 (m, 13H), 7.01-7.33 (m, 8H). MS (ESI, m/z): [M+H].sup.+: 639.39.
EXAMPLE 6
[0089] An organic electronic material containing a nitrogen heterocycle was provided, the organic electronic material contained compound CQ21 and compound CQ21 had the following synthetic route:
##STR00019##
[0090] Synthesis of intermediate CQ21-1:
[0091] intermediate CQ1-3 (6 g, 14.5 mmol), 2,4-diphenyl-6-(3-phenylboronic acid pinacol)-1,3,5-triazine (6.6 g, 15.2 mmol) and potassium carbonate (6 g, 43.4 mmol) were added into the flask, toluene (36 mL), ethanol (18 mL) and deionized water (18 mL) were added, triphenylphosphine palladium chloride (0.18 g, 0.28 mmol) was added under nitrogen protection, a reaction was carried out under reflux for 3 h, cooling and liquid separation were performed, an organic phase was washed with water, a part of a solvent was concentrated off, a solid was precipitated, an obtained solution was filtered, a filter cake was recrystallized once with toluene, and drying was performed and 7.6 g of a product with a yield of 88% was obtained.
[0092] .sup.1H NMR (400 MHz, CDCl.sub.3, δ): 8.60-8.81(m, 8H), 7.39-7.74(m, 13H), 7.27-7.29(m, 2H), 7.16-7.22(m, 3H).:
[0093] Synthesis of intermediate CQ21:
[0094] intermediate CQ21-1 (4.7 g, 7.9 mmol), 3-pyridylboronic acid pinacol ester (2.5 g, 5.7 mmol) and potassium carbonate (3.3 g, 23.9 mmol) were added into the flask, toluene (30 mL), dioxane (30 mL) and deionized water (15 mL) were added, palladium acetate (0.14 g. 0.63 mmol) and x-phos (0.28 g, 1.3 mmol) were added under nitrogen protection, a reaction was carried out under reflux for 5 h, cooling and filtration were peifonmed, a filter cake was washed with water to be neutral and washed with ethanol, and the filter cake was dried. The filter cake was recrystallized once with toluene and dried to obtain 4.2 g of a product with a yield of 84%. The obtained product was compound CQ21 whose proton nuclear magnetic resonance spectrum was shown in
[0095] .sup.1H NMR (400 MHz, CDCl.sub.3, δ): 8.96-8.98 (d, 1H), 8.84-8.91 (m, 2H), 8.72-8.74 (m, 4H), 8.57-8.67 (m, 3H), 7.94-7.96 (m, 1H), 7.83-7.88(m, 21-1), 7.68-7.76(m, 2H), 7.42-7.59 (m, 9H), 7.32-7.36(m, 2H), 7.15-7.22 (m, 4H). MS (ESI, m/z): [M+H].sup.+: 639.28.
[0096] Effects of the compounds of the present disclosure will be described in detail below with reference to examples.
[0097] Preparation of an organic light-emitting device whose structural diagram was shown in
EXAMPLE 7
Preparation of OLED Using Compound CQ1 of Example 1
[0098] (1) A transparent and, conductive ITO glass substrate 110 (with an anode 120 on top) (CSG Holding Co.,Ltd.) was subjected to ultrasonic treatment in a commercial detergent, rinsed in deionized water, sequentially washed with ethanol, acetone and deionized water, baked in a clean environment to completely remove water, washed with ultraviolet photosynthetic ozone, and treated with oxygen plasma for 30 s.
[0099] (2) The, glass substrate with the anode was placed in a vacuum chamber, vacuum pumping was carried out, and HIL (60 nm) was evaporated on the ITO to be used as a hole injection layer 130 at a rate of 0.1 nm/s.
[0100] (3) A compound NPB was evaporated on the hole injection layer to form a hole transport layer 140 having a thickness of 10 nm at a rate of 0.1 nm/s, TCTA was evaporated to form an electron blocking layer 150 having a thickness of 5 nm at a rate of 0.1 nm/s.
[0101] (4) A light-emitting layer 160 having a thickness of 20 nm was evaporated on the hole blocking layer at a rate of 0.1 nm/s, where CBP was a host light-emitting material, Ir(ppy)3 in an amount of 5 wt % was a phosphorescent dopant guest material.
[0102] (5) Compound CQ1 was evaporated on a light-emitting layer to a thickness of 30 nm, as an electron transport layer 170 at a rate of 0.1 nm/s, 1 nm LiF was evaporated to form an electron injection layer 180, and 80 nm Al was used as a cathode 190 of the device.
EXAMPLE 8
[0103] An only difference from example 7 was that in step (5), compound CQ2 having a thickness of 30 nm was evaporated on a light-emitting layer as an electron transport layer 170.
EXAMPLE 9
[0104] An only difference from example 7 was that in step (5), compound CQ5 having a thickness of 30 nm was evaporated on a light-emitting layer as, an electron transport layer 170.
EXAMPLE 10
[0105] An only difference from example 7 was that in step (5), compound CQ7 having a thickness of 30 nm was evaporated on a light-emitting layer as an electron transport layer 170.
EXAMPLE 11
[0106] An only difference from example 7 was that in step (5), compound CQ10 having a thickness of 30 nm was evaporated on a light-emitting layer as an electron transport layer 170.
EXAMPLE 12
[0107] An only difference from example 7 was that in step (5), compound CQ21 having a thickness of 30 nm was evaporated on a light-emitting layer as an electron transport layer 170.
COMPARATIVE EXAMPLE 1
[0108] An only difference from example 7 was that compound 8 (i.e.: ET1) described in manufacturing example 8 disclosed in Chinese Patent CN107445910A was used instead of compound CQ1 used in step (5).
COMPARATIVE EXAMPLE 2
[0109] An only difference from example 7 was that compound 37 (i.e.: ET2) described in example 5 disclosed in Chinese Patent CN108299388A was used instead of compound CQ1 used in step (5).
COMPARATIVE EXAMPLE 3
[0110] An only difference from example 7 was that compound Alq3 was used instead of compound CQ1 used in step (5).
EXPERIMENTAL EXAMPLE 1
[0111] The prepared devices were measured using a Photo Research PR650 spectrometer for operating voltage, brightness, efficiency, and CIE coordinates at a current density of 20 mA/cm.sup.2 and time (T90) for the brightness to become 90% of the initial brightness at this current density.
[0112] The results were specifically shown in Table 1.
TABLE-US-00001 TABLE 1 Power Current External Voltage Brightness efficiency efficiency quantum CIE T90 Example Compound (V) (cd/m.sup.2) (lm/W) (cd/A) efficiency (x, y) (h) 7 CQ1 6.90 10028 22.9 50 14.7% (0.2587, 146 0.6328) 8 CQ2 6.52 10804 26.2 54 16.0% (0.2584, 175 0.6395) 9 CQ5 6.76 11208 25.7 56 16.3% (0.2596, 168 0.6374) 10 CQ7 6.84 10204 23.6 52 14.9% (0.2581, 153 0.6348) 11 CQ10 6.67 10956 25.8 55 16.7% (0.2542, 165 0.6328) 12 CQ21 6.94 11649 23.4 57 16.1% (0.2553, 157 0.6318) Com- ET1 7.43 7762 17.8 43 12.5% (0.2586, 98 parative 0.6381) example 1 Com- ET2 7.28 8678 19.1 44 12.9% (0.2597, 109 parative 0.6313) example 2 Com- Alq3 7.61 6327 14.1 32 9.4% (0.2583, 76 parative 0.6327) example 3
[0113] As can be seen from experimental data of Table 1,
[0114] The organic light-emitting devices prepared from the organic electronic material containing a nitrogen heterocycle had a lower working voltage than that of comparative examples 1-3 in the prior art, a high brightness, and an improved current efficiency, power efficiency and external quantum efficiency under a same current density. Meanwhile, under the same current density, the devices prepared from the compounds of the present disclosure had a greatly prolonged service life compared with the comparative examples in the prior art. Under the same current density, the organic electronic material of the present disclosure had a better electron transport capability, thus the devices had a lower working voltage, a less power consumption and an improved service life.
[0115] The excellent performances were mainly gained by simultaneously introducing pyridine and pyrimidine or triazine into different positions of phenanthryl to obtain the organic electronic material containing a nitrogen heterocycle which can effectively reduce an HOMO energy level and an LUMO energy level, increase an electron injection and transmission capacity, reduce the working voltage of the devices and improve the efficiency. Meanwhile, asymmetric groups were introduced into different positions of phenanthrene, such that a mutual influence of different groups can be reduced, the thermal stability of the material can be improved, an amorphous film can be prepared, the efficiency of the devices was improved, and the service, life of the devices was prolonged.
[0116] The structural formulas in the device were as follows:
##STR00020## ##STR00021##
[0117] The above organic materials are all existing known materials and commercially available.
[0118] The foregoing is detailed description of the preferred specific examples of the present disclose. It should be understood that, a person of ordinary skill in the art can make various modifications and variations according to the concept of the present disclosure without creative efforts. Therefore, all technical solutions that, can be obtained by those skilled in the art based on the prior art through logical analysis, reasoning, or finite experiments according to the concept of the present disclosure shall fall within the protection scope defined by the appended claims.