Enthalpy Exchanger Element, Enthalpy Exchanger Comprising Such Elements and Method for Their Production

Abstract

The present invention provides enthalpy exchanger elements (E, E) and enthalpy exchangers comprising such elements. Furthermore, the invention discloses a method for producing such enthalpy exchanger elements and enthalpy exchangers, comprising the steps of a) providing an air-permeable sheet element (1); b) laminating at least one side (1a, 1b) of the sheet element (1) with a thin polymer film (3, 4) with water vapor transmission characteristics; and c) forming the laminated sheet element (1) into a desired shape exhibiting a three-dimensional corrugation pattern (5, 5, . . . ).

Claims

1. A method for producing enthalpy exchanger elements (E, E) comprising the steps of: a) providing an air-permeable sheet element (1); b) laminating at least one side (1a, 1b) of the sheet element (1) with a thin polymer film (3, 4) with water vapor transmission characteristics; c) forming the laminated sheet element (1) into a desired shape exhibiting a three-dimensional corrugation pattern (5, 5, . . . ).

2. The method according to claim 1, wherein the sheet material of the sheet element (1) comprises a polymer.

3. The method according to claim 1, wherein the sheet element (1) is a fabric, preferably a nonwoven fabric.

4. The method according to claim 3, wherein a fraction, preferably at least 50% by weight, of the fibers (6) of the fabric are multi-component, preferably bi-component fibers.

5. The method according to claim 1, wherein the laminating step b) comprises at least one of bonding, preferably heat bonding, welding and gluing, of the thin polymer film (3, 4) to the sheet element (1).

6. The method according to claim 1, wherein the at least one thin polymer film (3, 4) on the at least one side (1a, 1b) of the sheet element (1) is an air-impermeable polymer film.

7. The method according to claim 1, wherein the thin polymer film (3, 4) is a multilayer film comprising a sequence of polymer layers of different polymer types.

8. The method according to claim 7, wherein the polymer type of each polymer layer is selected from the group consisting of polyether ester, polyether amide and polyether urethane.

9. The method according to claim 7, wherein the total thickness of the thin polymer multilayer film is between 5 pm and 200 pm, more preferably between 10 pm and 150 pm.

10. The method according to claim 7, wherein the thickness of each individual polymer layer within the thin polymer multilayer film is between 1 pm and 20 m, preferably between 4 pm and 20 pm, and more preferably between 4 pm and 15 pm.

11. The method according to claim 1, wherein the forming step c) is a thermoforming step, preferably a vacuum forming step or a pleating step.

12. The method according to claim 11, wherein at least a first mold part having first corrugation formations defining or co-defining the predetermined corrugation pattern of the enthalpy exchanger element (E, E) to be manufactured, is provided for and used in the thermoforming step c).

13. The method according to claim 12, wherein a second mold part having second corrugation formations complementary to the first corrugation formations co-defining the predetermined corrugation pattern of the enthalpy exchanger element (E, E) to be manufactured, is provided for and used in the thermoforming step c).

14. The method according to claim 10, wherein nozzles connected to a pressurized air source provided for and used in the thermoforming step c).

15. The method according to claim 14, wherein the nozzles are provided in the vicinity of the first mold part and/or the second mold part.

16. An enthalpy exchanger element (E; E), comprising: an air-permeable sheet element (1); and a predetermined three-dimensional corrugation pattern (5, 5, . . . ), wherein a first thin polymer film (3) is laminated to a first side (1a) of the sheet element (1) and/or a second thin polymer film (4) is laminated to a second side (1b) of the sheet element (1), both thin polymer films (3, 4) having water vapor transmission characteristics.

17. The enthalpy exchanger element (E) according to claim 16, wherein the first thin polymer film (3) and the second thin polymer film (4) are identical to each other.

18. The enthalpy exchanger element (E) according to claim 16, wherein the first thin polymer film (3) and the second thin polymer film (4) are different from each other.

19. An enthalpy exchanger having at least three sheet-like or plate-like enthalpy exchanger elements (E1, E2, E3; E1\E2, E3) as defined in claim 16, which are stacked onto and fixed to each other, preferably by means of welding such as laser welding or ultrasonic welding or by means of gluing, with their respective three-dimensional corrugation patterns (5, 5, . . . ) in parallel orientation to form parallel fluid paths allowing fluids to flow there through.

Description

[0083] A non-limiting embodiment of the invention is described in further detail below with reference to the drawings, wherein:

[0084] FIG. 1 is a schematic representation of the method for producing enthalpy exchanger elements according to the invention;

[0085] FIG. 2 is a schematic representation of an enthalpy exchanger according to the invention or a portion thereof including a plurality of enthalpy exchanger elements according to the invention;

[0086] FIG. 3 is a SEM (scanning electron microscope) micrograph of a cross-sectional view of a portion of an intermediate product produced during the method for producing an enthalpy exchanger element according to the invention;

[0087] FIG. 4 is a SEM micrograph of a cross-sectional view of a portion of an enthalpy exchanger element produced by the method according to the invention;

[0088] FIG. 5 is a SEM micrograph similar to the one of FIG. 3 showing of a larger scale cross-sectional view of a smaller portion of an intermediate product produced during the method for producing an enthalpy exchanger element according to the invention; and

[0089] FIG. 6 is a SEM micrograph similar to the one of FIG. 4 showing of a smaller scale cross-sectional view of a larger portion of an enthalpy exchanger element produced by the method according to the invention.

[0090] In FIG. 1, a schematic representation of the method for producing enthalpy exchanger elements according to the invention is shown. Cross-sections of the intermediate products, i.e. the results of each of steps S1, S2 and S3, are shown.

[0091] In a first step S1, an air-permeable sheet element 1 having voids or openings 2 is provided.

[0092] In a second step S2, both sides 1a, 1b of the sheet element 1 are laminated with a thin polymer film 3, 4 with water vapor transmission characteristics.

[0093] In a third step S3, the laminated sheet element 1 is formed into a desired shape exhibiting a three-dimensional corrugation pattern 5.

[0094] The sheet element 2 is a non-woven fabric including thermoplastic fibers only or a combination of thermoset fibers and thermoplastic fibers. The fabric may include bicomponent fibers together with standard thermoset and/or thermoplastic fibers.

[0095] The thin polymer film 3, 4 is a multilayer film which may comprise a sequence (not shown) of polymer layers of different polymer types.

[0096] The forming step S3 is a thermoforming step, preferably a vacuum forming step. At least a first mold part (e.g. lower tool, not shown) having first corrugation formations co-defining the predetermined corrugation pattern 5 of the enthalpy exchanger element E, E to be manufactured, is used in the thermoforming step S3. In addition to the at least first mold part, a second mold part (e.g. upper tool, not shown) having second corrugation formations complementary to the first corrugation formations and/or a forming vacuum co-defining the predetermined corrugation pattern of the enthalpy exchanger element E, E to be manufactured, is/are used in the thermoforming step S3.

[0097] The resulting enthalpy exchanger element E having a first thin polymer film 3 on the first side 1a of the sheet element 1 and a second thin polymer film 4 on the second side 1b of the sheet element 1 comprises a corrugated structure 5 with alternating squeezed portions 5a and squeezed/stretched portions 5b. The squeezed portion 5a extend in a first direction (horizontal direction in FIG. 1) and the squeezed/stretched portions 5b extend in a second direction different from the first direction. Preferably, the angle a between the first direction and the second direction in the corrugation pattern 5 of the enthalpy exchanger element E is between 90 and 120, preferably between 95 and 105, an example of which is shown in FIG. 1. Alternatively, unlike the example shown in FIG. 1, the angle between the first direction and the second direction in the corrugation pattern 5 of the enthalpy exchanger element E is between 80 and 90, preferably between 85 and 90.

[0098] In FIG. 2, a schematic representation of a first type enthalpy exchanger E1-E2-E3 or second type enthalpy exchanger E1-E2-E3 according to the invention is shown. The first type E1-E2-E3 includes a plurality of enthalpy exchanger elements E1, E2, E3 where the first thin polymer film 3 and the second thin polymer film 4 (FIG. 1) are films of the same type. The second type E1-E2-E3 includes a plurality of enthalpy exchanger elements E1, E2, E3 where the first thin polymer film 3 and the second thin polymer film 4 (FIG. 1) are films of different types including the case where one of the two films 3, 4 has zero thickness, i.e. the enthalpy exchanger element has only one thin polymer film 3 or 4 on one side 1a or 1b of the sheet element 1.

[0099] In FIG. 2, the outer walls of the housing/packaging of the enthalpy exchanger E1-E2-E3 or E1-E2-E3 is not shown. The air inlet/outlet portions (not shown) of the enthalpy exchanger E1-E2-E3 or E1-E2-E3 are provided with air distribution patterns such that the air flow direction in adjacent air ducts in the enthalpy exchanger E1-E2-E3 or E1-E2-E3 are in opposite directions, as shown by the O symbol indicating air flow towards the viewer and the X symbol indicating air flow away from the viewer.

[0100] FIG. 3 shows a SEM (scanning electron microscope) micrograph of a cross-sectional view of an air-permeable sheet element 1 laminated on its upper side 1a with a first thin polymer film 3 and laminated on its lower side 1b with a second thin polymer film 4 as a result of step b) of the method according to the invention.

[0101] The laminating step b) may comprise bonding, preferably heat bonding and/or gluing, of the thin polymer films 3, 4 to the sheet element 1. A thermoplastic adhesive (hot melt adhesive) may be used for the bonding between the polymer film 3 and 4 and the sheet element 1.

[0102] The sheet element 1 is a nonwoven fabric comprising a plurality of fibers 6. The fibers 6 may be thermoplastic fibers only or a combination of thermoset fibers and/or mineral fibers on the one hand and thermoplastic fibers on the other hand. Most preferably, the fabric includes multicomponent or bicomponent fibers together with standard thermoset and/or thermoplastic fibers. As can be best seen by comparing FIG. 3 with FIG. 4, the fibers 6 of the nonwoven fabric sheet element 1 shown in FIG. 3 are less densely packed than the fibers 6 of the nonwoven fabric sheet element 1 of the enthalpy exchanger element shown in FIG. 4.

[0103] FIG. 4 shows a SEM micrograph of a cross-sectional view of a portion of an enthalpy exchanger element E produced by forming the laminated sheet element 1 of FIG. 3 into a desired shape exhibiting a three-dimensional corrugation pattern as a result of step c) of the method according to the invention.

[0104] The forming step c) may be a pleating step or thermoforming step, preferably a vacuum forming step. At least a first mold part (e.g. lower tool, not shown) having first corrugation formations defining or co-defining the predetermined corrugation pattern of the enthalpy exchanger element E, E to be manufactured, is provided for and used in the thermoforming step. In addition to the at least first mold part, a second mold part (e.g. upper tool, not shown) having second corrugation formations complementary to the first corrugation formations and/or a forming vacuum co-defining the predetermined corrugation pattern of the enthalpy exchanger element E, E to be manufactured, may be provided in the thermoforming step.

[0105] The first mold part (e.g. lower tool) may comprise nozzles or through holes pneumatically connected to a vacuum source providing a vacuum for the vacuum forming step.

[0106] In addition to the first mold part and/or the second mold part used in the forming step c), preferably for supporting the vacuum action in the vacuum forming step, nozzles connected to a pressurized air source may be provided. These nozzles may be provided in the vicinity of, preferably adjacent to, the first mold part and/or the second mold part. Preferably, the pressurized air source comprises an air heating device for heating the pressurized air.

[0107] The combined use of the first tool and the vacuum source in the thermoforming step c) can be supplemented by the second tool and/or the pressurized air source, preferably with air heating device. As a result, using at least some of these supplements, a sheet element 1 laminated with a first thin polymer film 3 and an optional second thin polymer film 4 can be pressed more strongly against the first corrugation formations of the first mold part, thus producing an enthalpy exchanger element E with a better copy of the first corrugation formations of the first mold part defining or co-defining the predetermined corrugation pattern of the enthalpy exchanger element E to be manufactured.

[0108] The sheet element 1 of the enthalpy exchanger element E has its fibers 6 much more densely packed than the sheet element 1 of FIG. 3. During the pleating or thermoforming step c), the fabric sheet element 1 with its first thin polymer film 3 and its second thin polymer film 4 is compressed and heated. At least the thermoplastic fibers or the multicomponent or bicomponent fibers of the plurality of fibers 6 are softened or partly melted during the pleating or thermoforming step c). As a result, after cooling and hardening of the thermoplastic fibers or the multicomponent or bicomponent fibers of the plurality of fibers 6, the fabric sheet element 1 with its first thin polymer film 3 and its second thin polymer film 4 is transformed into an enthalpy exchanger element E according to the invention with a more compact fiber structure in the fabric sheet element 1 and with a three-dimensional corrugation pattern.

[0109] FIG. 5 shows a SEM micrograph similar to the one of FIG. 3 showing of a larger scale cross-sectional view of a smaller portion of the air-permeable fabric sheet element 1 laminated on its upper side 1a with the first thin polymer film 3 and laminated on its lower side 1b with the second thin polymer film 4 as a result of step b) of the method according to the invention.

[0110] FIG. 6 shows a SEM micrograph similar to the one of FIG. 4 showing of a smaller scale cross-sectional view of a larger portion of the enthalpy exchanger element E produced by the method according to the invention.

REFERENCE NUMERALS

[0111] 1 fabric sheet element [0112] 1a first surface [0113] 1b second surface [0114] 2 voids or openings [0115] 3 first thin polymer film [0116] 4 second thin polymer film [0117] 5 corrugation [0118] 5a squeezed portion [0119] 5b squeezed and/or stretched portion [0120] S1 providing step [0121] S2 laminating step [0122] S3 forming step (co-forming) [0123] O air flow direction towards viewer [0124] X air flow direction away from viewer [0125] 6 fiber [0126] angle (in corrugation pattern)