Abstract
A visible light response photocatalyst structure and a process for manufacturing the same are disclosed, where the structure is manufactured by the GRR for two times, so that the structure has a large surface area, high surface activity, being apt to get integrated with a silicon substrate and endurable to the environment, and further has the rapid and simple manufacturing characteristics without any additional energy required and has a high reproductively.
Claims
1. A visible light response photocatalyst structure, comprising: a silicon substrate; a silver nano-layer, grown on a surface of the silicon substrate through a first galvanic replacement reaction (GRR) for 300-480 seconds and having a solid dendritic shape after experiencing the first GRR; a precious metal layer, grown on a surface of the silver nano-layer through a second GRR for 5 minutes: and a silver chloride layer, grown on a surface of the precious metal layer through the second GRR for 5 minutes, wherein, the silver-nano-layer has a hollow dendritic shape after experiencing the second GRR.
2. The visible light response photocatalyst structure as claimed in claim 1, wherein the first GRR is a fluorine ions assisted GRR, so that the silver nano-layer is grown on the surface of the silicon substrate.
3. The visible light response photocatalyst structure as claimed in claim 1, wherein the precious metal layer grown on the surface of the silver nano-layer through the second GRR has a precious metal material portion comprising gold (Au), palladium (Pd), and platinum (Pt).
4. The visible light response photocatalyst structure as claimed in claim 1, wherein the first GRR has a reaction equation: Si+4.sup.31 Ag.sup.++6HF.fwdarw.4Ag+H.sub.2SiF.sub.6+4H.sup.+.
5. The visible light response photocatalyst structure as claimed in claim 1, wherein the second GRR has a reaction equation: 4Ag+(PtCl.sub.6).sup.2?.fwdarw.Pt+4AgCl+2Cl.sup.?.
6. The visible light response photocatalyst structure as claimed in claim 1, wherein the second GRR has a reaction equation: 4Ag+HAuCl.sub.4.fwdarw.Au+4AgCl+?H.sub.2.
7. The visible light response photocatalyst structure as claimed in claim 1, wherein materials of the visible light response photocatalyst structure viewed from an outer contour of the visible light response photocatalyst structure to an interior of the visible light response photocatalyst structure are AgCl, Pt, and Ag.
8. The visible light response photocatalyst structure as claimed in claim 1, wherein materials of the visible light response photocatalyst structure viewed from an outer contour of the visible light response photocatalyst structure to an interior of the visible light response photocatalyst structure are AgCl, Au, and Ag.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
(1) The present invention will be better understood from the following detailed descriptions of the preferred embodiments according to the present invention, taken in conjunction with the accompanying drawings, in which:
(2) FIG. 1 is a schematic diagram of a side view of a visible light response photocatalyst structure according to the present invention;
(3) FIG. 2 is a flowchart of a method for manufacturing the visible light response photocatalyst structure according to the present invention;
(4) FIG. 3A through FIG. 3F are actual structural plan-diagrams of the visible light response photocatalyst structure only having a silver nano-layer obtained at different time points according to the present invention, respectively;
(5) FIG. 3G through FIG. 3I are actual structural plan-diagrams of the visible light response photocatalyst structure only having the silver nano-layer obtained at different time points according to the present invention, respectively;
(6) FIG. 4A through FIG. 4D are actual structural diagrams of the visible light response photocatalyst structure only having the silver nano-layer obtained by different magnifications and viewing angles according to the present invention, respectively;
(7) FIG. 5A is a visible light response diagram of the visible light response photocatalyst structure according to the present invention, respectively;
(8) FIG. 5B is an amplified visible light response diagram of the visible light response photocatalyst structure only having the silver nano-layer according to the present invention;
(9) FIG. 6A through FIG. 6C are actual structural diagrams of the visible light response photocatalyst structure obtained by different magnifications according to a first aspect of the present invention, respectively;
(10) FIG. 7A is an actual structural diagram of the visible light response photocatalyst structure according to the first aspect of the present invention, respectively;
(11) FIG. 7B is an actual amplified visible light response diagram of the visible light response photocatalyst structure according to the first aspect of the present invention, respectively;
(12) FIG. 8A through FIG. 8C are actual structural diagrams of the visible light response photocatalyst structure obtained by different magnifications according to the first aspect of the present invention, respectively;
(13) FIG. 9 is an actual structural diagram of the visible light response photocatalyst structure according to the first aspect of the present invention; and
(14) FIG. 10A through FIG. 10B are actual structural diagrams of the visible light response photocatalyst structure obtained by different magnifications according to the second aspect of the present invention, respectively.
DETAILED DESCRIPTION
(15) The present invention will be apparent from the following detailed description, which proceeds with reference to the accompanying drawings, wherein the same references relate to the same elements.
(16) In the following, the visible light response photocatalyst structure and a process for manufacturing the same according to the present invention will be described as follows, with simultaneous reference to FIG. 1 and FIG. 2, in which FIG. 1 is a schematic diagram of a side view of a visible light response photocatalyst structure according to the present invention, while FIG. 2 is a flowchart of a method for manufacturing the visible light response photocatalyst structure according to the present invention.
(17) The visible light response photocatalyst structure of the present invention comprises a silicon substrate 10, a silver nano-layer 21, a precious metal layer 22 and a silver chloride layer 23.
(18) In the present invention, the galvanic replacement reaction (GRR) is used to manufacture a visible light response photocatalyst structure. At first, a silicon substrate 10 is provided. The silicon substrate 10 may have an unlimited shape and size. Assume the silicon substrate 10 is a cubic body with each side length of 2 cm. The silicon substrate 10 is placed into a solution having HF and Ag.sup.+ therein. The silicon substrate 10, HF, and Ag.sup.+ are subject to a first GRR for 5 min, which is merely an example without limiting the present invention, and may be 8 min., 1 hr., 24 hr., etc. The first GRR is the fluoride assisted GRR, and has the reaction equation of Si+4Ag.sup.++6HF.fwdarw.4Ag+H.sub.2SiF.sub.6+4H.sup.+. In this manner, a silver nano-layer 21 could grow on the silicon substrate 10, and such grown silver nano-layer has a solid dendritic shape (S101).
(19) Thereafter, referring to FIG. 3A through FIG. 3F and FIG. 3G through FIG. 3I, in which FIG. 3A through FIG. 3F are actual structural plan-diagrams of the visible light response photocatalyst structure only having a silver nano-layer obtained at different time points according to the present invention, respectively, while FIG. 3G through FIG. 3I are actual structural plan-diagrams of the visible light response photocatalyst structure only having the silver nano-layer obtained at different time points according to the present invention, respectively.
(20) FIG. 3A involves a scale bar of 2 ?m, and shows the silver nano-layer 21 grown in the case where the silicon substrate 10, HF and Ag.sup.+ are subject to the first GRR for a reaction time of 20 seconds. It may be apparently known that a solid silver nano-layer 21 has been grown on the silicon substrate 10 within a short time.
(21) FIG. 3B involves a scale bar of 5 ?m, and shows the silver nano-layer 21 grown in the case where the silicon substrate 10, HF and Ag.sup.+ are subject to the first GRR for a reaction time of 40 seconds. It may be apparently known that a solid silver nano-layer 21 has been grown on the silicon substrate 10 within the 40-seconds time, and the silver nano-layer 21 grows gradually to have a dendritic shape.
(22) FIG. 3C involves a scale bar of 5 ?m, and shows the silver nano-layer 21 grown in the case where the silicon substrate 10, HF and Ag.sup.+ are subject to the first GRR for a reaction time of 80 seconds. It may be apparently known that a solid silver nano-layer 21 has been grown on the silicon substrate 10 within the 80-seconds time, and the silver nano-layer 21 grows gradually to have a dendritic shape.
(23) FIG. 3D involves a scale bar of 5 ?m while FIG. 3D involves a scale bar of 10 ?m, which show the silver nano-layer 21 grown in the case where the silicon substrate 10, HF and Ag.sup.+ are subject to the first GRR for a reaction time of 160 seconds, respectively. It may be apparently known that a solid silver nano-layer 21 has been grown on the silicon substrate 10 within the 160-seconds time, and the silver nano-layer 21 grows gradually to have a dendritic shape.
(24) FIG. 3E involves a scale bar of 5 ?m while FIG. 3D involves a scale bar of 10 ?m, which show the silver nano-layer 21 grown in the case where the silicon substrate 10, HF and Ag.sup.+ are subject to the first GRR for a reaction time of 300 seconds, i.e. 5 min., respectively. It may be apparently known that a solid silver nano-layer 21 has been grown on the silicon substrate 10 within the 300-seconds time, and the silver nano-layer 21 grows gradually to have a dendritic shape.
(25) FIG. 3F involves a scale bar of 5 ?m while FIG. 3D involves a scale bar of 20 ?m, which show the silver nano-layer 21 grown in the case where the silicon substrate 10, HF and Ag.sup.+ are subject to the first GRR for a reaction time of 480 seconds, i.e. 8 min., respectively. It may be apparently known that a solid silver nano-layer 21 has been grown on the silicon substrate 10 within the 480-seconds time, and the silver nano-layer 21 grows gradually to have a dendritic shape, which is simlar to that in the case of 300 seconds of growth.
(26) Thereafter, referring to FIG. 4A through FIG. 4D, actual structural plan-diagrams of the visible light response photocatalyst structure only having the silver nano-layer obtained at different magnifications and viewing angles according to the present invention are shown, respectively.
(27) FIG. 4A through FIG. 4D involve a scale bar of 500 nm, 1 ?m, 10 ?m, 10 ?m, and 20 ?m, respectively, and FIG. 4A through FIG. 4C show the silver nano-layer 21 as having the solid dendritic shape viewed from a plane viewing angle and with different magnifications, while FIG. 4D is obtained from a side view where the silicon substrate 10 may be readily known as having grown on the surface of the silicon substrate 10.
(28) Thereafter, FIG. 5A is a visible light response diagram of the visible light response photocatalyst structure according to the present invention, while FIG. 5B is an amplified visible light response diagram of the visible light response photocatalyst structure only having the silver nano-layer according to the present invention. As shown, a first data 31 indicates that the structure having only the silver nano-layer 21 and the silicon substrate 10 has already the visible light response, and FIG. 5B is an amplified diagram of FIG. 5A with respect to the first data 31.
(29) To verify the structure only having the silver nano-layer 21 and the silicon substrate 10 has already the visible light response, the first data 31 is obtained by providing a visible light source at the 40.sup.th seconds, 80.sup.th seconds, 120.sup.th seconds, etc., to the silver nano-layer structure 21 and the silicon substrate 10. The result shows instantaneous data leaps are found on the first data 31 at the 40.sup.th, 80.sup.th, 120.sup.th seconds, and thus the evidence that the structure only having the silver nano-layer 21 and the silicon substrate 10 begins to have the visible light response at these time points is readily ascertained. Further, such structure may continuously maintain such visible light response. This may be evidenced by closing the visible light at some particular time points. On the first data 31, the data has a significant change at the 80.sup.th, 120.sup.th, 160.sup.th, etc., respectively, and which corresponds to the time points when the visible light is closed. It may be thus readily known that the structure having only the silver-nano-layer 21 and the silicon substrate 10 does not show the visible light response again due to the absence of the visible light.
(30) Referring again to FIG. 1 and FIG. 2, the only silver nano-layer 21 and the silicon substrate 10 structures may be reinforced. After the silver nano-layer 21 is grown on the surface of the silicon substrate 10 through the first GGR, the structure may be further placed into a solution having PtCl.sub.6.sup.2?, so that the silicon substrate 10, the silver nano-layer 21 and PtCl.sub.6.sup.2? are jointly subject to a second GRR for 5 min. For reinforcing the structure having only the silver nano-layer 21 and the silicon substrate 10, which is merely an example without limiting the present invention, and may be 8 min., 1 hr., 24 hr., etc. The second GRR has the reaction equation: 4Ag?(PtCl.sub.6).sup.2?.fwdarw.Pt+4AgCl+2Cl.sup.?. In this manner, the precious metal layer 22 could grow on the surface of the silver nano-layer 21, and a silver chloride layer 23 could grow on a surface of the precious metal layer 22. And, grown silver nano-layer 21 has a hollow dendritic shape (S102). The visible light response catalyst structure is thus completed, and this structure is a AgClPtAg composite structure from an inward view.
(31) Referring to FIG. 6A through FIG. 6C, actual structural diagrams of the visible light response photocatalyst structure obtained by different magnifications according to a first aspect of the present invention are shown therein, respectively.
(32) FIG. 6A involves a scale bar of 500 nm, FIG. 6B involves a scale bar of 500 ?m, while FIG. 6C involves a scale bar of 500 nm. It is to be noted that the structures respectively shown in FIG. 6B and FIG. 4B may be found their difference in comparison. From FIG. 6C, the silver nano-layer 21 may be found as having changed into a hollow dendritic shape.
(33) Thereafter, referring to FIG. 7A and FIG. 7B, an actual structural diagram of the visible light response photocatalyst structure according to the first aspect of the present invention, respectively, and an actual amplified visible light response diagram of the visible light response photocatalyst structure according to the first aspect of the present invention, respectively, are shown, respectively.
(34) As shown, a second data 32 may be found with the visible light response from the visible light photocatalyst structure at a portion thereof, the amplified second data 32 is otherwise shown in FIG. 7B.
(35) To verify the visible light photocatalyust structure has already the visible light response, the second data 32 is obtained by providing a visible light source at the 40th seconds, 80th seconds, 120th seconds, etc., to the structure. The result shows that instantaneous data leaps are found on the second data 32 at the 40.sup.th, 80.sup.th, 120.sup.th seconds, and thus the evidence that the structure begins to have the visible light response at these time points is readily ascertained. Further, such structure may continuously maintain such visible light response. This may be evidenced by closing the visible light at some particular time points. On the second data 32, the data has a significant change at the 60th, 100th, 140th, etc., respectively, and which corresponds to the time points when the visible light is closed. It may be thus readily known that the structure does not show the visible light response again due to the absence of the visible light.
(36) Thereafter, referring to FIG. 8A through FIG. 8C, actual structural diagrams of the visible light response photocatalyst structure obtained by different magnifications according to the first aspect of the present invention are shown, respectively.
(37) Referring to FIG. 8A through FIG. 8C, actual structural diagrams of the visible light response photocatalyst structure obtained by different magnifications by using a microscope according to the present invention are shown therein, respectively, where the silicon substrate 10, the silver nano-layer 21 and PtCl.sub.6.sup.2? have been subject to the second GRR for 1 hr. to form the visible light photocatalyst structure. FIG. 8A. FIG. 8A involves a scale bar of 500 nm, FIG. 8B involves a scale bar of 2?m, while FIG. 8C involves a scale bar of 500 nm. It is to be noted that the structures respectively shown in FIG. 8A and FIG. 6A may be found their difference in comparison, i.e. in the two cases the silver nano-layer 21, the precious metal layer 22 and the silver chloride layer 23 each have their thickness differences. From FIG. 8C, the silver nano-layer 21 may be found as having changed into a hollow dendritic shape.
(38) Thereafter, referring to FIG. 9, an actual structural diagram of the visible light response photocatalyst structure according to the first aspect of the present invention is shown therein.
(39) As shown in FIG. 9, the actual data of the visible light photocatalyst structure having only the silver nano-layer 21 and the silicon substrate 10 is shown as the first data 31, the second data 32 is obtained from the case where the silicon substrate 10, the silver nano-layer 21 and PtCl.sub.6.sup.2? are jointly subject to the second GRR for 5 min., the third data 33 is obtained from the case where the silicon substrate 10, the silver nano-layer 21 and PtCl.sub.6.sup.2? are jointly subject to the second GRR for 1 hr., the fourth data 34 is obtained from the case where the silicon substrate 10, the silver nano-layer 21 and PtCl.sub.6.sup.2? are jointly subject to the second GRR for 3 hr., while the fifth data 35 is obtained from the case where the silicon substrate 10, the silver nano-layer 21 and PtCl.sub.6.sup.2? are jointly subject to the second GRR for 24 hr.
(40) From a comparison among the second data 32 to the fifth data 35, it may be apparently known that the shorter the second GRR time is, such as 5 min., the netter result the visible light photocatalyst of the present invention is.
(41) Referring again to FIG. 1 and FIG. 2, after the silver nano-layer 21 could grow on the surface of the silicon substrate 10 through the first GGR, the structure may be further placed into a solution having PtCl.sub.6.sup.2?, so that the silicon substrate 10, the silver nano-layer 21 and PtCl.sub.6.sup.2? are jointly subject to a second GRR for 1 hr., for reinforcing the structure having only the silver nano-layer 21 and the silicon substrate 10, which is merely an example without limiting the present invention, and may be 5 min , 8 min., 24 hr., etc. The second GRR has the reaction equation: 4Ag+(PtCl.sub.6).sup.2?.fwdarw.Pt+4AgCl+2Cl.sup.?. In this manner, the precious metal layer 22 could grow on the surface of the silver nano-layer 21, and the silver chloride layer 23 could grow on the surface of the precious metal layer 22. And, grown silver nano-layer 21 has a hollow dendritic shape (S102). The visible light response catalyst structure is thus completed, and this structure is a AgClAuAg composite structure from an inward view.
(42) Thereafter, referring to FIG. 10A through FIG. 10B, actual structural diagrams of the visible light response photocatalyst structure obtained by different magnifications according to the second aspect of the present invention are shown therein, respectively.
(43) FIG. 10A and FIG. 10B are actual structural diagrams of the visible light response photocatalyst structure obtained by different magnifications according to the second aspect of the present invention, respectively, where the silicon substrate 10, the silver nano-layer 21 and PtCl.sub.6.sup.2? are jointly subject to the second GRR for 1 hr. FIG. 10A involves a scale bar of 1 ?m, while FIG. 10B involves a scale bar of 500 nm. Regarding the precious metal layer 22, the first and second embodiments take Pt and Au as the layer 22, respectively. However, these are merely examples without limiting the present invention.
(44) In summary, the structure and process of the present invention have the difference as compared to the prior art that the visible light response photocatalyst structure is manufactured by the GRR for two times, so that the structure has a large surface area, high surface activity, being apt to get integrated with a silicon substrate and endurable to the environment, and further has the rapid and simple manufacturing characteristics without any additional energy required and has a high reproductively.
(45) By using the above technical means, the present invention may overcome the demerits of the prior art and achieve in manufacture of the visible light response photocatalyst structure by using the GRR.
(46) Although the invention has been described with reference to specific embodiments, this description is not meant to be construed in a limiting sense. Various modifications of the disclosed embodiments, as well as alternative embodiments, will be apparent to persons skilled in the art. It is, therefore, contemplated that the appended claims will cover all modifications that fall within the true scope of the invention.