ELASTIC ANTI-CORROSION ADHESIVE, ELASTIC ANTI-CORROSION ADHESIVE TAPE AND PREPARATION METHOD THEREOF

Abstract

The present invention discloses an elastic anti-corrosion adhesive, an elastic anti-corrosion adhesive tape and a preparation method thereof, which belongs to the technical field of anti-corrosion adhesive tape materials, comprising: by weight, 5 to 8 parts of elastic rubber, 3 to 5 parts of high molecular weight polyisobutylene, 20 to 35 parts of medium molecular weight polyisobutylene, 5 to 10 parts of elastic fiber, 40 to 60 parts of inorganic powder and 1 to 5 parts of anti-aging agent. The elastic anti-corrosion adhesive provided by the present invention possesses excellent extensibility and resilience. The extensibility thereof allows it to be applied to irregular surfaces, forming a tight bond with the substrate surface, and reducing voids. And the resilience thereof gives the anti-corrosion adhesive self-tightening properties, promoting its penetration into the microscopic surface of the substrate, effectively isolating air and moisture, thereby enhancing its corrosion resistance.

Claims

1. An elastic anti-corrosion adhesive, characterized by comprising the following components in weight percentages: 5 to 8 parts of elastic rubber, 3 to 5 parts of high molecular weight polyisobutylene, 20 to 35 parts of medium molecular weight polyisobutylene, and 5 to 10 parts of elastic fiber, 40 to 60 parts of inorganic powder and 1 to 5 parts of anti-aging agent.

2. The elastic anti-corrosion adhesive according to claim 1, characterized in that the elastic rubber comprises EPDM rubber and/or butyl rubber.

3. The elastic anti-corrosion adhesive according to claim 1, characterized in that the molecular weight of the high molecular weight polyisobutylene is 80000 to 90000.

4. The elastic anti-corrosion adhesive according to claim 1, characterized in that the molecular weight of the medium molecular weight polyisobutylene is 30,000 to 50,000.

5. The elastic anti-corrosion adhesive according to claim 4, characterized in that the elastic fibers include polyolefin elastic fibers and/or polyester composite elastic fibers.

6. The elastic anti-corrosion adhesive according to claim 4, characterized in that the inorganic powder comprises: one or more of the following: calcium carbonate, barium sulfate, mica powder, talc powder, wollastonite powder and kaolin.

7. A method for preparing the elastic anti-corrosion adhesive according to claim 1, characterized in that it comprises the following steps: mixing elastic rubber, high molecular weight polyisobutylene, medium molecular weight polyisobutylene, elastic fiber, inorganic powder and anti-aging agent at a temperature below 130 C. for 1 to 4 hours to obtain an elastic anti-corrosion adhesive.

8. An elastic anti-corrosion adhesive tape, characterized in that it comprises: a first elastic anti-corrosion adhesive layer (1), an elastic reinforcing rib (2), a second elastic anti-corrosion adhesive layer (3) and a composite backing layer (4) arranged in sequence; wherein the first elastic anti-corrosion adhesive layer (1) and the second elastic anti-corrosion adhesive layer (3) are made of the elastic anti-corrosion adhesive according to claim 1; Wherein, the elastic reinforcement rib (2) comprises: a plurality of tows, which are laid between the first elastic anti-corrosion adhesive layer (1) and the second elastic anti-corrosion adhesive layer (3) in a parallel and spaced manner along the longitudinal direction of the elastic anti-corrosion adhesive tape; The tows comprise: polyolefin elastic fiber bundles or polyester composite elastic fiber bundles.

9. The elastic anti-corrosion adhesive tape according to claim 8, characterized in that the composite backing layer (4) comprises: a first backing layer (41) and a second backing layer (42). In addition, the first backing layer (41) and the second backing layer (42) are bonded through an adhesive layer (43), and the first backing layer (41) is provided on the side of the second elastic anti-corrosion adhesive layer (3) away from the side of the first elastic anti-corrosion adhesive layer (1).

10. The elastic anti-corrosion adhesive tape according to claim 8, characterized in that the elastic anti-corrosion adhesive tape further comprises an anti-adhesion isolation layer (5), and the anti-adhesion isolation layer (5) is provided on the first elastic anti-corrosion adhesive layer (1) on the side away from the second elastic anti-corrosion adhesive layer (3).

Description

DESCRIPTION OF THE DRAWINGS

[0024] In order to provide a clearer explanation of the technical solutions of the Embodiments of the present invention, a brief introduction to the drawings used in the Embodiments will be provided below. It should be understood that the following drawings only illustrate some Embodiments of the present invention and should not be considered as limiting the scope. Ordinary technicians in this field can also obtain other related drawings without exerting creative effort.

[0025] FIG. 1 shows a diagram of the structure of the elastic anti-corrosion adhesive tape of the present utility model. In the drawing, 1First elastic anti-corrosion adhesive layer, 2elastic reinforcement rib, 3Second elastic anti-corrosion adhesive layer, 4composite backing layer, 41First backing layer, 42Second backing layer, 43bonding layer, 5anti-adhesive isolation layer.

SPECIFIC IMPLEMENTATION METHOD

[0026] The following description of the principles and features of the present invention is combined with Embodiments and drawings. The Embodiments provided are only used to explain the present invention and are not intended to limit the scope of the present invention. For parts that specific conditions are not specified in the Embodiments, conventional conditions or conditions recommended by manufacturers are used. Reagents or instruments not specified by manufacturers are conventional products that can be obtained through commercial purchase.

Embodiment 1

[0027] The elastic anti-corrosion adhesive in this Embodiment comprises: by weight, 5 parts of elastic rubber, 3 parts of high molecular weight polyisobutylene, 25 parts of medium molecular weight polyisobutylene, 6 parts of elastic fibers, 55 parts of inorganic powder, and 2 parts of anti-aging agent, which are mixed at 110 C. for 4 hours.

[0028] Wherein, the elastic rubber is a mixture of ternary ethylene-propylene rubber and butyl rubber in equal proportions; the molecular weight of the high molecular weight polyisobutylene is 80,000; the molecular weight of the medium molecular weight polyisobutylene is 30,000; the elastic fibers are a mixture of polyolefin elastic fibers and polyester composite elastic fibers in equal proportions; the inorganic powder is a mixture of calcium carbonate, barium sulfate, mica powder, and talcum powder in equal proportions; the anti-aging agent is a hindered phenolic binary antioxidant.

Embodiment 2

[0029] The elastic anti-corrosion adhesive in this example comprises: by weight, 8 parts of elastic rubber, 5 parts of high molecular weight polyisobutylene, 20 parts of medium molecular weight polyisobutylene, 10 parts of elastic fibers, 60 parts of inorganic powder, and 2 parts of anti-aging agent, which are mixed at 120 C. for 2.5 hours.

[0030] Wherein, the elastic rubber is a mixture of ternary ethylene-propylene rubber and butyl rubber in equal proportions; the molecular weight of the high molecular weight polyisobutylene is 90,000; the molecular weight of the medium molecular weight polyisobutylene is 50,000; the elastic fibers are a mixture of polyolefin elastic fibers and polyester composite elastic fibers in equal proportions; the inorganic powder is a mixture of calcium carbonate, barium sulfate, mica powder, and talcum powder in equal proportions; the anti-aging agent is a hindered phenolic binary antioxidant.

Embodiment 3

[0031] The elastic anti-corrosion adhesive in this Embodiment comprises: by weight, 6 parts of elastic rubber, 4 parts of high molecular weight polyisobutylene, 20 parts of medium molecular weight polyisobutylene, 8 parts of elastic fibers, 58 parts of inorganic powder, and 2 parts of anti-aging agent mixed at 130 C. for 1 hour.

[0032] Wherein, the elastic rubber is a mixture of ternary ethylene-propylene rubber and butyl rubber in equal proportions; the molecular weight of the high molecular weight polyisobutylene is 85,000; the molecular weight of the medium molecular weight polyisobutylene is 45,000; the elastic fibers are a mixture of polyolefin elastic fibers and polyester composite elastic fibers in equal proportions; the inorganic powder is a mixture of calcium carbonate, barium sulfate, mica powder, and talcum powder in equal proportions; the anti-aging agent is a hindered phenolic binary antioxidant.

Embodiment 4

[0033] The elastic anti-corrosion adhesive in this example includes: by weight, 5 parts of elastic rubber, 3 parts of high molecular weight polyisobutylene, 10 parts of medium molecular weight polyisobutylene, 5 parts of elastic fibers, 40 parts of inorganic powder, and 1 part of anti-aging agent mixed at 125 C. for 1 hour.

[0034] Wherein, the elastic rubber is ternary ethylene-propylene rubber; the molecular weight of the high molecular weight polyisobutylene is 85,000; the molecular weight of the medium molecular weight polyisobutylene is 45,000; the elastic fibers are polyolefin elastic fibers; the inorganic powder is a mixture of calcium carbonate, barium sulfate, mica powder, and talcum powder in equal proportions; the anti-aging agent is a hindered phenolic binary antioxidant.

Embodiment 5

[0035] The elastic anti-corrosion adhesive in this embodiment comprises: by weight, 8 parts of elastic rubber, 5 parts of high molecular weight polyisobutylene, 25 parts of medium molecular weight polyisobutylene, 10 parts of elastic fiber, 60 parts of inorganic powder and 2 parts of anti-aging agent mixed at 115 C. for 3 hours.

[0036] Among them, the elastic rubber is butyl rubber; the molecular weight of high molecular weight polyisobutylene is 85,000; the molecular weight of medium molecular weight polyisobutylene is 45,000; the elastic fiber is polyester composite elastic fiber warp; the inorganic powder is calcium carbonate, barium sulfate, mica powder and Talcum powder is mixed in equal proportions; the anti-aging agent is a hindered phenolic binary antioxidant.

Comparative Example 1

[0037] The formula of the elastic anti-corrosion adhesive in this comparative example is the same as that of Embodiment 3, except that no elastic fibers are added.

Comparative Example 2

[0038] The formula of the elastic anti-corrosion adhesive in this comparative example is the same as that of Embodiment 3, except that no medium molecular weight polyisobutylene is added.

Comparative Example 3

[0039] The formula of the elastic anti-corrosion adhesive in this comparative example is the same as that of Embodiment 3, except that no elastic rubber is added.

Comparative Example 4

[0040] The formula of the elastic anti-corrosion adhesive in this comparative example is the same as that of Embodiment 3, except that no high molecular weight polyisobutylene is added.

Comparative Example 5

[0041] The formula of the elastic anti-corrosion adhesive in this comparative example is the same as that of Embodiment 3, except that 12 parts of low molecular weight polyisobutylene with a molecular weight of 10,000 are also added.

Comparative Example 6

[0042] The formula of the elastic anti-corrosion adhesive in this comparative example comprises: 5 parts of butyl rubber, 8 parts of high molecular weight polyisobutylene, 30 parts of medium molecular weight polyisobutylene, 15 parts of low molecular weight polyisobutylene, 40 parts of inorganic reinforcing filler calcium carbonate, 0.5 part of antioxidant 1010, 0.5 part of anti-aging agent 264, and 1.0 part of pigment phthalocyanine green. The preparation method is the same as that of Embodiment 3.

[0043] The elastic anti-corrosion adhesive made from Embodiments 1-5 was used to produce anti-corrosion adhesive tapes for wrapping and covering the surface of pipelines. Testing was conducted 24 hours later, and the specific test results are as follows:

TABLE-US-00001 Embodi- Embodi- Embodi- Embodi- Embodi- Test items ment 1 ment 2 ment 3 ment 4 ment 5 Elongation 157% 180% 201% 188% 130% at break Resilience 53% 61% 69% 58% 51% Peel 3.5 4.8 4.2 5.7 3.3 strength/N/ cm Peel 96 95 100 95% 98 coverage rate/%

[0044] Based on the experimental results, the comprehensive performance of the elastic anti-corrosion adhesive made in Embodiments 1 to 5 is optimal and meets the requirements of ISO 21809-3 standard for tape peel strength 2N/cm and coverage rate 95%. Among them, Embodiment 3 is selected as the preferred formula for the elastic anti-corrosion adhesive tape.

[0045] Anti-corrosion adhesive tapes made from the elastic anti-corrosion adhesive prepared in Comparative Examples 1-6 were wrapped and covered on the surface of irregular-shaped pipes. Testing was conducted 24 hours later, and the specific test results are as follows:

TABLE-US-00002 Comparative Comparative Comparative Comparative Comparative Comparative Test items example 1 example 2 example 3 example 4 example5 example 6 Elongation at 108% 203% 125% 162% 159% 136% break Resilience 39% 93% 40% 53% 28% 15% Peel strength/ 2.3 5.5 3.3 1.8 2.5 2.1 N/cm Peel coverage 70 50 85 95 61 33 rate/%

[0046] Based on the analysis of the experimental results above, compared to Example 3, Comparative Example 1 shows a significant decrease in resilience due to the absence of elastic fibers. Resilience corresponds to the self-tightening force of the adhesive layer, and the decrease in resilience leads to a reduction in the self-tightening force of the adhesive layer, resulting in decreased cold flow properties and poor bonding effectiveness with irregular-shaped pipeline surfaces, leading to decreased peel strength and coverage rate.

[0047] Since medium molecular weight polyisobutylene plays a primary role in initial adhesion and certain bonding and sealing effects in the entire adhesive structure, Comparative Example 2 shows a significant decrease in bonding coverage rate due to the absence of medium molecular weight polyisobutylene.

[0048] Comparing Comparative Example 3 with Embodiment 3 and Comparative Example 1, it is evident that resilience and elongation at break are the result of the combined action of elastic fibers and elastic rubber. The absence of elastic rubber also leads to a slight decrease in elongation at break and resilience of the adhesive, resulting in insufficient tightening force and inadequate coverage rate of the adhesive.

[0049] In Comparative Example 4, no high molecular weight polyisobutylene was added, and high molecular weight polyisobutylene provides resilience and significantly enhances its own cohesive strength. Therefore, compared with Example 3, the elongation at break and rebound rate are slightly reduced, and the peel strength is reduced at a certain level.

[0050] Comparing Comparative Example 5 with Embodiment 3, the difference lies in the addition of low molecular weight polyisobutylene. Low molecular weight polyisobutylene, being in liquid form, has a significant effect on reducing the elongation at break and resilience of the adhesive, leading to a substantial decrease in resilience. This prevents effective adhesion with the surface of irregular-shaped pipelines, resulting in a decrease in coverage rate.

[0051] Comparative Example 6 differs from Embodiment 3 by adding low molecular weight polyisobutylene while removing the amount of elastic rubber and elastic fibers. Compared to Comparative Example 5, the main difference lies in the removal of elastic rubber and elastic fiber. According to the experimental results, the performance of this Comparative Example is further reduced compared to Comparative Example 5. This further demonstrates the significant reduction in elasticity and resilience of the elastic adhesive due to the introduction of low molecular weight polyisobutylene. It also further proves the simultaneous enhancement of elasticity and resilience by elastic rubber and elastic fibers, which significantly benefits the use of elastic adhesives in irregular-shaped pipelines.

Embodiment 6

[0052] The elastic anti-corrosion adhesive tape of the present Embodiment, as shown in FIG. 1, comprises the following parts arranged sequentially: the first elastic anti-corrosion adhesive layer 1, the elastic reinforcement rib 2, the second elastic anti-corrosion adhesive layer 3, and the composite backing layer 4.

[0053] In the present invention, the first elastic anti-corrosion adhesive layer 1 and the second elastic anti-corrosion adhesive layer 3 are made of the elastic anti-corrosion adhesive prepared from any one of Examples 1-5. In practical use, the thickness of the first elastic anti-corrosion adhesive layer 1 is 1 to 2 mm, preferably 1.2 to 1.8 mm, and more preferably 1.4 to 1.6 mm. The thickness of the second elastic anti-corrosion adhesive layer 3 is 0.5 to 1 mm, preferably 0.6 to 0.9 mm, and more preferably 0.65 to 0.85 mm. The thickness of the first elastic anti-corrosion adhesive layer 1 is slightly greater than that of the second elastic anti-corrosion adhesive layer 3 because the first elastic anti-corrosion adhesive layer 1 contacts with the surface of the anti-corrosion workpiece, and a slightly larger thickness makes it easier to stretch and maintain integrity. In actual use, the thickness of the first elastic anti-corrosion adhesive layer 1 and the second elastic anti-corrosion adhesive layer 3 can be selected according to the specific requirements of use.

[0054] The elastic reinforcement rib 2 comprises: a plurality of tows, which are arranged between the first elastic anti-corrosion adhesive layer 1 and the second elastic anti-corrosion adhesive layer 3 in a parallel and spaced apart manner along the longitudinal direction of the elastic anti-corrosion adhesive tape. The elastic reinforcement rib 2 is positioned between the first elastic anti-corrosion adhesive layer 1 and the second elastic anti-corrosion adhesive layer 3, enhancing the overall structural strength of the elastic anti-corrosion adhesive tape. The elastic reinforcement 2 has high resilience, providing self-tightening force during use, allowing the anti-corrosion adhesive layer to penetrate more easily into the microscopic surface of the anti-corrosion workpiece, forming a solid anti-corrosion layer, filling gaps between the anti-corrosion adhesive layer and the workpiece, and improving sealing, thereby effectively isolating air and moisture from contacting the anti-corrosion workpiece, and enhancing corrosion resistance. Additionally, the excellent self-tightening force also helps to improve the bonding strength between the elastic anti-corrosion adhesive tape and the anti-corrosion workpiece, increasing the degree of integration, and thereby enhancing the peel strength of the elastic anti-corrosion adhesive tape. The tows comprises polyolefin elastic fiber bundles or polyester composite elastic fiber bundles, which are tough, have high resilience, and are easy to stretch, providing self-tightening force to the elastic anti-corrosion adhesive tape. The diameter of each fiber bundle is 0.3 to 0.8 mm, preferably 0.4 to 0.7 mm, and more preferably 0.5 to 0.6 mm. The spacing between the fiber bundles is 3 to 5 mm, preferably 3.5 to 4.5 mm, and more preferably 3.7 to 4.2 mm. The spaced arrangement of the fiber bundles provides good resilience to the elastic anti-corrosion adhesive tape without affecting its extensibility and also helps control costs. In actual use, the diameter of each fiber bundle and the spacing between the fiber bundles can be selected according to the specific requirements of use.

[0055] The composite backing layer 4 comprises a first backing layer 41 and a second backing layer 42. The first backing layer 41 and the second backing layer 42 are bonded together by a bonding layer 43, and the first backing layer 41 is positioned on the side of the second elastic anti-corrosion adhesive layer 3 away from the first elastic anti-corrosion adhesive layer 1. In the present invention, the composite backing layer 4 adopts a stretchable backing material, which can be tightly wrapped around the surface of the anti-corrosion workpiece through stretching to ensure good adhesion between the elastic anti-corrosion adhesive tape and the workpiece surface. In the present invention, the composite backing layer 4 adopts a double-layer structure, aiming to allow the anti-corrosion adhesive layer to penetrate into the surface of the backing layer without overflowing and to achieve self-fusion with the adhesive layer at the overlap area, thereby completely solving the problem of water seepage at the overlap area. Additionally, it is endowed with a paintable function, where the surface of the second backing layer 42 of the composite backing layer 4 can be coated with functional coatings as needed, thereby providing aesthetic, protective, and weather-resistant effects.

[0056] The first backing layer 41 is made of non-woven fabric with a weight of 50 g to 100 g, preferably ranging from 60 g to 90 g, and more preferably from 70 g to 80 g. The second backing layer 42 is made of non-woven fabric with a weight of 15 g to 30 g, preferably ranging from 17 g to 27 g, and more preferably from 20 g to 25 g. The weight of the first backing layer 41 is slightly greater than that of the second backing layer 42 because the first backing layer 41 is in contact with the surface of the second elastic anti-corrosion adhesive layer 3, and a slightly greater thickness corresponds to a slightly greater capacity to accept the penetration of the anti-corrosion adhesive layer. This allows the anti-corrosion adhesive layer to penetrate as much as possible into the first backing layer 41, reducing the amount of adhesive that can penetrate into the second backing layer 42 and thus minimizing overflow. In actual use, the weight of the first backing layer 41 and the second backing layer 42 can be selected according to the specific requirements. In the present invention, the bonding layer 43 is made of epoxy resin adhesive. The epoxy resin adhesive solidifies and becomes irreversible after being continuously cured at a temperature of 120 to 150 C. for a period of time. Epoxy resin adhesive has excellent stability, heat resistance, corrosion resistance, bending resistance, elasticity, impact resistance, and fatigue resistance. The formed composite backing layer 4 has good firmness, corrosion resistance, heat resistance, and long service life.

[0057] In the present invention, the elastic anti-corrosion adhesive tape further comprises an anti-adhesive isolation layer 5, which is located on the side of the first elastic anti-corrosion layer 1 away from the second elastic anti-corrosion layer 3. In this embodiment, the anti-adhesive isolation film includes: PET base film or PE base film. The thickness of the anti-adhesive isolation layer 5 is 0.05 to 0.1 mm, preferably 0.07 to 0.1 mm. The function of the anti-adhesive isolation layer 5 is to prevent the anti-corrosion adhesive tape from self-adhesion and contamination by dust, water vapor, and other pollutants in the atmosphere. The above description is only a preferred embodiment of the present invention and should not be construed as limiting the scope of the invention. Any modifications, equivalents, improvements, etc., made within the spirit and principle of the present invention should be included within the protection scope of the present invention.