Ceramic material, powder, and layer system comprising the ceramic material

Abstract

An improved ceramic material for heat insulation with selection of specific stabilizers and adapted proportions, includes zirconium oxide with 0.2 wt. % to 8.0 wt. % of the base stabilizers: yttrium oxide (Y.sub.2O.sub.3), hafnium oxide (HfO.sub.2), cerium oxide (CeO.sub.2), calcium oxide (CaO), and/or magnesium oxide (MgO), wherein at least yttrium oxide (Y.sub.2O.sub.3) is used, and optionally at least one of the additional stabilizers: 0.2 wt. % to 20 wt. % of erbium oxide (Er.sub.2O.sub.3) and/or ytterbium oxide (Yb.sub.2O.sub.3).

Claims

1. A ceramic material based on zirconium oxide (ZrO.sub.2) and comprising: 3.2 wt % to 8.0 wt % of base stabilizers, the base stabilizers comprising: 3.0 wt % to 5.0 wt % yttrium oxide (Y.sub.2O.sub.3), 0.2 wt % to 2.0 wt % hafnium oxide (HfO.sub.2), and a remainder, the remainder comprising: cerium oxide (CeO.sub.2), calcium oxide (CaO) and/or magnesium oxide (MgO), and at least one additional stabilizer, the at least one additional stabilizer comprising 6.0 wt % to 8.0 wt % of ytterbium oxide (Yb.sub.2O.sub.3).

2. The ceramic material as claimed in claim 1, comprising: 3.5 wt % to 4.0 wt % of yttrium oxide (Y.sub.2O.sub.3).

3. The ceramic material as claimed in claim 1, comprising: 6.5 wt % to 7.5 wt % of ytterbium oxide (Yb.sub.2O.sub.3).

4. A ceramic powder comprising, a composition of the ceramic material as claimed in claim 1.

5. A layer system at least comprising: a metallic substrate, optionally a metallic adhesion promoter layer, and at least one ceramic layer based on the ceramic material as claimed in claim 1.

6. The layer system as claimed in claim 5, comprising: the metallic adhesion promoter layer between the at least one ceramic layer and directly on the metallic substrate, wherein the metallic adhesion promoter layer comprises an alloy of the type NiCoCrAlYX, where X is optional and can be Ta, Re and/or Si.

7. The layer system as claimed in claim 5, wherein a ceramic sublayer is present below the at least one ceramic layer, which more particularly is at least 20% thinner than the at least one ceramic layer and comprises yttrium-stabilized zirconium oxide (YSZ).

8. The layer system as claimed in claim 7, which comprises a segmentation comprising, vertical cracks in the ceramic sublayer.

9. The layer system as claimed in claim 8, in which the segmentation is present by means of vertical cracks only in an outermost ceramic layer of the at least one ceramic layer.

10. The layer system as claimed in claim 8, in which the segmentation runs by means of vertical cracks through the ceramic sublayer and one ceramic layer of the at least one ceramic layer.

11. The layer system as claimed in claim 10, in which a number of vertical cracks extend from a surface of the at least one ceramic layer up to the metallic adhesion promoter layer.

12. The layer system as claimed in claim 8, in which numerous vertical cracks extend up to the metallic adhesion promoter layer.

13. A ceramic material based on zirconium oxide (ZrO.sub.2) and comprising: 2.0 wt % to 5.0 wt % yttrium oxide (Y.sub.2O.sub.3); 0.2 wt % to 2.0 wt % hafnium oxide (HfO.sub.2); and 6.0 wt % to 8.0 wt % of ytterbium oxide (Yb.sub.2O.sub.3).

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIGS. 1 to 4 show exemplary embodiments of the invention.

DETAILED DESCRIPTION OF INVENTION

(2) The zirconium oxide is stabilized with 0.2 wt % to 8 wt %, more particularly with 0.2 wt % to 6.0 wt %, of base stabilizers: yttrium oxide, hafnium oxide, cerium oxide, calcium oxide and/or magnesium oxide and optionally with additional stabilizers 0.2 wt % to 20 wt % of erbium oxide and/or ytterbium oxide.

(3) Yttrium oxide is used in any case and at least one of the base stabilizers hafnium oxide, cerium oxide, calcium oxide and/or magnesium oxide is used.

(4) This ceramic composition may be prepared as a powder, and so further additions, as in the use of abrasive layers, comprise cubic boron nitride or other abrasive particles.

(5) In a layer system 1.sup.I (FIG. 1) a ceramic layer 10.sup.I is applied to metal, the substrate 4 present, in the case of nickel- or cobalt-based superalloys used preferably, being a metallic adhesion layer 7 which forms aluminum oxide (TGO; not shown), with the metallic adhesion promoter layer constituting preferably an aluminide, platinum-aluminide or, as a basis, an NiCoCrAlX alloy, optionally with x=Ta, Re, Fe and/or Si.

(6) The ceramic layer of the ceramic material in accordance with the invention may be produced by means of EB-PVD, plasma spraying (APS, etc.), etc. and has a columnar structure or a segmented structure.

(7) The ceramic layers 10.sup.II, 10.sup.III, 10.sup.IV (FIGS. 2-4) preferably has a layer thickness of 100 m to 1000 m.

(8) As shown in FIG. 2, in a layer system 1.sup.II, a ceramic layer 10.sup.II as in FIG. 1 may also have a ceramic sublayer 13.sup.II, the layer thickness of which, however, is at least 20% thinner in configuration than that of the ceramic material of the invention in the ceramic layer 10.sup.II.

(9) The ceramic sublayer 13.sup.II preferably comprises 8YSZ, i.e., zirconium oxide stabilized with 3 mol % to 4 mol % of yttrium, and is therefore distinctly different from the material of the ceramic layer 10.sup.II.

(10) FIGS. 3 and 4 show further examples of layer structures 1.sup.III, 1.sup.IV of the invention.

(11) According to FIG. 3, in comparison to FIG. 1, there is a segmented ceramic layer 10.sup.III of a layer system 1.sup.III, which comprises numerous, relatively long and vertical cracks 15, 15.sup.I, starting from the surface 18 of the outermost ceramic layer 10.sup.III, and extending very largely over the entire ceramic layer thickness, here in particular up to the metallic adhesion layer 7 or the TGO thereof (not shown).

(12) A layer system 1.sup.IV may also comprise a ceramic attachment layer 13.sup.IV (FIG. 4) for attachment of the outermost layer 10.sup.IV of a thermal barrier coating (TBC), in which case the attachment layer 13.sup.IV may be configured as described in FIG. 2.

(13) The outermost ceramic layer 10.sup.IV is more particularly configured like the outermost layer 10.sup.III in FIG. 3.

(14) In the ceramic attachment layer 13.sup.IV, however, cracks 14 extend, preferably likewise vertical, which extend through both ceramic layers 10.sup.IV, 13.sup.IV.

(15) The relatively long cracks have been formed by specific process parameters or production methods, and do not represent cracks between multiple grains.

Exemplary Embodiments

(16) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2

(17) ZrO.sub.2+Y.sub.2O.sub.3+MgO

(18) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2

(19) ZrO.sub.2+Y.sub.2O.sub.3+CaO

(20) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO

(21) ZrO.sub.2+Y.sub.2O.sub.3+MgO+HfO.sub.2

(22) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO

(23) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+HfO.sub.2

(24) ZrO.sub.2+Y.sub.2O.sub.3+MgO+CaO

(25) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+CaO

(26) ZrO.sub.2+Y.sub.2O.sub.3+CaO+CeO.sub.2+HfO.sub.2

(27) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+MgO+CaO

(28) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+CaO

(29) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+HfO.sub.2

(30) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO+CeO.sub.2+MgO

(31) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+Yb.sub.2O.sub.3

(32) ZrO.sub.2+Y.sub.2O.sub.3+MgO+Yb.sub.2O.sub.3

(33) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+Yb.sub.2O.sub.3 (particularly preferred)

(34) ZrO.sub.2+Y.sub.2O.sub.3+CaO+Yb.sub.2O.sub.3

(35) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+Yb.sub.2O.sub.3

(36) ZrO.sub.2+Y.sub.2O.sub.3+MgO+HfO.sub.2+Yb.sub.2O.sub.3

(37) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO+Yb.sub.2O.sub.3

(38) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+HfO.sub.2+Yb.sub.2O.sub.3

(39) ZrO.sub.2+Y.sub.2O.sub.3+MgO+CaO+Yb.sub.2O.sub.3

(40) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+CaO+Yb.sub.2O.sub.3

(41) ZrO.sub.2+Y.sub.2O.sub.3+CaO+CeO.sub.2+HfO.sub.2+Yb.sub.2O.sub.3

(42) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+MgO+CaO+Yb.sub.2O.sub.3

(43) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+CaO+Yb.sub.2O.sub.3

(44) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+HfO.sub.2+Yb.sub.2O.sub.3

(45) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO+CeO.sub.2+MgO+Yb.sub.2O.sub.3

(46) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+Er.sub.2O.sub.3

(47) ZrO.sub.2+Y.sub.2O.sub.3+MgO+Er.sub.2O.sub.3

(48) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+Er.sub.2O.sub.3

(49) ZrO.sub.2+Y.sub.2O.sub.3+CaO+Er.sub.2O.sub.3

(50) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+Er.sub.2O.sub.3

(51) ZrO.sub.2+Y.sub.2O.sub.3+MgO+HfO.sub.2+Er.sub.2O.sub.3

(52) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO+Er.sub.2O.sub.3

(53) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+HfO.sub.2+Er.sub.2O.sub.3

(54) ZrO.sub.2+Y.sub.2O.sub.3+MgO+CaO+Er.sub.2O.sub.3

(55) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+CaO+Er.sub.2O.sub.3

(56) ZrO.sub.2+Y.sub.2O.sub.3+CaO+CeO.sub.2+HfO.sub.2+Er.sub.2O.sub.3

(57) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+MgO+CaO+Er.sub.2O.sub.3

(58) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+CaO+Er.sub.2O.sub.3

(59) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+HfO.sub.2+Er.sub.2O.sub.3

(60) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO+CeO.sub.2+MgO+Er.sub.2O.sub.3

(61) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

(62) ZrO.sub.2+Y.sub.2O.sub.3+MgO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

(63) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+Yb.sub.2O.sub.3+Er.sub.2O.sub.3 (particularly preferred)

(64) ZrO.sub.2+Y.sub.2O.sub.3+CaO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

(65) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

(66) ZrO.sub.2+Y.sub.2O.sub.3+MgO+HfO.sub.2+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

(67) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

(68) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+HfO.sub.2+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

(69) ZrO.sub.2+Y.sub.2O.sub.3+MgO+CaO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

(70) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+CaO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

(71) ZrO.sub.2+Y.sub.2O.sub.3+CaO+CeO.sub.2+HfO.sub.2+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

(72) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+MgO+CaO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

(73) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+CaO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

(74) ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+HfO.sub.2+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

(75) ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO+CeO.sub.2+MgO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

(76) The ceramic material comprises preferably 2.5 wt % to 5.5 wt % of yttrium oxide (Y.sub.2O.sub.3), more particularly 3.0 wt % to 5.0 wt % of yttrium oxide (Y.sub.2O.sub.3), especially 3.5 wt % to 4.0 wt %.

(77) The ceramic material may also comprise preferably 1.5 wt % to 3.0 wt % of yttrium oxide (Y.sub.2O.sub.3), more particularly 2.0 wt % to 2.5 wt % of yttrium oxide (Y.sub.2O.sub.3).

(78) The ceramic material preferably comprises: hafnium oxide (HfO.sub.2) at 0.2 wt % to 4.0 wt %, more particularly 0.5 wt % to 4.0 wt % of hafnium oxide (HfO.sub.2), especially 0.6 wt % to 4.0 wt % of hafnium oxide (HfO.sub.2).

(79) For better, i.e., lower, thermal conductivity, the ceramic material preferably comprises: hafnium oxide (HfO.sub.2) at 0.2 wt % to 2.0 wt %, more particularly at 0.6 wt % to 2.0 wt % of hafnium oxide (HfO.sub.2), especially at 0.8 wt % to 2.0 wt % of hafnium oxide (HfO.sub.2).

(80) For better thermal stability the ceramic material preferably comprises: hafnium oxide (HfO.sub.2) at 2.0 wt % to 4.0 wt %, more particularly 2.4 wt % to 4.0 wt % of hafnium oxide (HfO.sub.2), especially 4.0 wt % to 4.0 wt % of hafnium oxide (HfO.sub.2).

(81) The ceramic material preferably comprises 5.5 wt % to 8.5 wt % of ytterbium oxide (Yb.sub.2O.sub.3), more particularly 6.0 wt % to 8.0 wt % of Yb.sub.2O.sub.3, especially 6.5 wt % to 7.5 wt % of Yb.sub.2O.sub.3.

(82) The ceramic material comprises preferably 3.0 wt % to 4.5 wt % of ytterbium oxide (Yb.sub.2O.sub.3), more particularly 3.5 wt % to 4.0 wt % of ytterbium oxide (Yb.sub.2O.sub.3).

(83) The ceramic material also preferably comprises 2.0 wt % to 4.0 wt % of Er.sub.2O.sub.3, more particularly 2.5 wt % to 3.5 wt % of Er.sub.2O.sub.3.

(84) With further preference the ceramic material comprises (6.0x) wt % of Y.sub.2O.sub.3 and between 2*x wt % and 4*x wt % of Yb.sub.2O.sub.3/Er.sub.2O.sub.3. For example, when x corresponds to 2, the ceramic material would comprise 4.0 wt % of Y.sub.2O.sub.3 between 4 wt % and 8 wt %.