LOW ENVIRONMENTAL IMPACT, NON-FLAMMABLE AEROSOL COATINGS

Abstract

An aerosol coating composition contains at least one film-forming resin, trans-1-chloro-3,3,3-trifluoropropene and at least one propellant such as CO.sub.2. The aerosol coating composition is non-flammable and compatible with polyethylene terephthalate. The film-forming resin may be acrylic resins, alkyd resins or mixtures thereof. A glycol ether solvent may be present. The coating composition may have low toxicity, be non-ozone depleting, have low or no VOC, be low in maximum incremental reactivity and/or be low in global warming potential. A method of coating a substrate with the aerosol coating composition comprises providing at least one film-forming resin selected from the group consisting of acrylic resins, alkyd resins, and mixtures thereof and trans-1-chloro-trifluoropropene in a container comprising polyethylene terephthalate, which is charged with a propellant comprising carbon dioxide. The aerosol coating composition is non-flammable. The composition is applied to a substrate and allowed to dry.

Claims

1. An aerosol coating composition comprising: at least one film-forming resin selected from the group consisting of acrylic resins, alkyd resins, and mixtures thereof; trans-1-chloro-3,3,3-trifluoropropene; and at least one propellant, wherein the propellant comprises carbon dioxide; wherein the aerosol coating composition comprises less than 1 percent GHS-flammable solvents.

2. The aerosol coating composition of claim 1, wherein the aerosol coating composition comprises less than 0.5 percent GHS-flammable solvents.

3. The aerosol coating composition of claim 1, wherein the at least one film forming resin comprises an acrylic resin.

4. The aerosol coating composition of claim 1, wherein the at least one film forming resin consists of an acrylic resin.

5. The aerosol coating composition of claim 1, wherein the propellant consists of carbon dioxide.

6. The aerosol coating composition of claim 3, wherein the at least one film forming resin additionally comprises an alkyd resin.

7. The aerosol coating composition of claim 1, wherein the at least one film forming resin comprises an alkyd resin.

8. The aerosol coating composition of claim 7, additionally comprising a glycol ether solvent.

9. The aerosol coating composition of claim 8, wherein the glycol ether is selected from the group consisting of alkyl glycol ethers and aromatic glycol ethers.

10. The aerosol coating composition of claim 8, wherein the glycol ether is selected from the group consisting of diethylene glycol monomethyl ether, dipropylene glycol monobutyl ether, propylene glycol phenyl ether, dipropylene glycol n-butyl ether, and dipropylene glycol n-propyl ether.

11. The aerosol coating composition of claim 8, wherein the composition is contained in a container comprising polyethylene terephthalate.

12. The aerosol coating composition of claim 10, wherein aerosol coating composition comprises one or more properties selected from the group consisting of having an ozone depleting potential of 0, being free of VOC, having a maximum incremental reactivity of 0.5 or less, and having a global warming potential of less than 1.

13. A method of coating a substrate with a coating composition, the method comprising: providing an aerosol coating composition, the aerosol coating composition comprising at least one film-forming resin selected from the group consisting of acrylic resins, alkyd resins, and mixtures thereof, and trans-1-chloro-3,3,3-trifluoropropene, wherein the aerosol coating composition comprises less than 1 percent GHS-flammable solvents, and wherein the aerosol coating composition is provided in a container comprising polyethylene terephthalate, and further wherein the container is charged with a propellant comprising carbon dioxide; applying the aerosol coating composition to a substrate; and allowing the applied aerosol coating composition to dry.

14. The method of claim 13, wherein the aerosol coating composition comprises less than 0.5 percent GHS-flammable solvents.

15. The method of claim 13, wherein the at least one film forming resin comprises an acrylic resin.

16. The method of claim 13, wherein the at least one film forming resin consists of an acrylic resin.

17. The method of claim 13, wherein the propellant consists of carbon dioxide.

18. The method of claim 15, wherein the at least one film forming resin additionally comprises an alkyd resin.

19. The method of claim 13, wherein the at least one film forming resin comprises an alkyd resin.

20. The method of claim 19, wherein the aerosol coating composition additionally comprises a glycol ether.

21. The method of claim 20, wherein the glycol ether is selected from the group consisting of alkyl glycol ethers and aromatic glycol ethers.

22. The method of claim 20, wherein the glycol ether is selected from the group consisting of diethylene glycol monomethyl ether, dipropylene glycol monobutyl ether, propylene glycol phenyl ether, dipropylene glycol n-butyl ether, and dipropylene glycol n-propyl ether.

23. The method of claim 13, wherein aerosol coating composition comprises one or more properties selected from the group consisting selected from the group consisting of having an ozone depleting potential of 0, being free of VOC, having a maximum incremental reactivity of 0.5 or less, and having a global warming potential of less than 1.

24. The method of claim 15, wherein the aerosol coating composition additionally comprises a glycol ether.

25. The aerosol coating composition of claim 3, additionally comprising a glycol ether solvent.

Description

BRIEF DESCRIPTION OF THE DRAWING

[0021] FIG. 1 is a graph showing the resulting pressure in pounds per square inch (psi) versus percentage of carbon dioxide (CO.sub.2) for propellant compositions containing trans-1-chloro-3,3,3-trifluoropropene and CO.sub.2.

DETAILED DESCRIPTION OF THE INVENTION

[0022] The present invention is directed toward an aerosol coating system that utilizes environmentally friendly components that are non-flammable and low in toxicity, are non-ozone depleting, have low or zero VOC, are low in MIR, are low in global warming potential, or have a combination of any of these properties. The following examples should not be viewed as limiting the scope of the invention. The claims will serve to define the inventions.

[0023] The invention provides an aerosol coating composition comprising at least one film-forming resin selected from the group consisting of acrylic resins and alkyd resins, trans-1-chloro-3,3,3-trifluoropropene and at least one propellant. The aerosol coating composition is non-flammable and compatible with polyethylene terephthalate.

[0024] In certain embodiments, the film-forming resin may consist of an alkyd resin or it may consist of an acrylic resin. In other embodiments, the film forming components may comprise a combination of at least one alkyd resin and at least one acrylic resin. In certain embodiments, the ratio of alkyd resin to acrylic resin may be 1:1 or less. In certain embodiments, the ratio of alkyd resin to acrylic resin may be 0.8 or less, 0.7 or less, 0.6 or less, 0.5 or less, 0.4 or less, 0.3 or less, 0.2 or less or 0.1 or less. Alkyd resins that may be used include Perstorp Boltorn U3000, a dendritic (spherically shaped), low viscosity, ˜100 percent solids long oil alkyd. (Perstorp, Sweden) Other suitable alkyds include other non-dendritic, ˜100 percent solids, long oil alkyds, such as EPS 6677 (Engineered Polymer Solutions, Marengo, Ill., US). Dianal MB-7022, is one example of a (very) low molecular weight (20K), thermoplastic film forming acrylate polymer, polyisobutyl methacrylate (IBMA). Other potential acrylate resins include n-butyl methacrylates and blends a copolymers thereof.

[0025] The invention comprises trans-1-chloro-3,3,3-trifluoropropene. Commercially available examples of trans-1-chloro-3,3,3-trifluoropropene include Solstice® PF-C and Solstice® Liquid Blowing Agent (LBA) (Honeywell International, Morris Plains, N.J.). These products are indicated to have a global warming potential of 1, no flash pint by ASTM D3828-97 and ASTM D 1310-86, and an ozone depleting potential of ˜0. Because this compound has a high vapor pressure (108.3 kPa at 20° C.), it functions as both a solvent for the resin and as a propellant. Additional solvents and propellants may be present. In certain embodiments, the solvents present are classified as non-flammable. In 2012, the former test for aerosol flammability, ASTM D 3065 “Flame Extension,” was replaced with the United Nations GHS (Global Harmonization Systems) 2012 program, which includes an “Enclosed Space (drum) Test” and a rigorous “Ignition Distance Test”. Solvent based aerosol coatings, even those that are 100% free of flammable solvents and propellants, frequently fail this test, as the very intense blue flame which it is sprayed through will cause ingredients, such as polymers, plasticizers, and organic pigments, to ignite. In these cases, ignition of these materials may only cause a sparking-like appearance in the test flame, but such results are frequently interpreted as failures. However, included in the same document, the 3rd Revised Edition of the UN GHS 2012, which became effective on May 25, 2012, the GHS test protocol is not required for Class 3 Aerosols, which are defined as aerosol formulas that contains less than 1% of materials that are classified by GHS as flammable, i.e., those materials with flash points below 93 C/200 F and have an indexed heat of combustion under 20 kJ/g. In the invention, the composition may contain less than 1 percent solvents classified by the United Nations GHS (Global Harmonization Systems) 2012 program as flammable (GHS-flammable solvents). In certain embodiments, the composition comprises less than 0.75 percent, 0.5 percent, 0.25 percent or even 0.1 percent solvents classified under the GHS as flammable (GHS flammable solvents). In certain particular embodiments, the composition contains less than 0.05 percent GHS flammable solvents, such as less than 0.04 percent, less than 0.03 percent, less than 0.02 percent or even 0.01 percent or less GHS flammable solvents.

[0026] Solvents may further include triethyl phosphate and various ethers such as glycol ethers. In some embodiments, the glycol ether solvent may be and alkyl or aromatic glycol ether such as diethylene glycol monomethyl ether, dipropylene glycol monobutyl ether, propylene glycol phenyl ether, dipropylene glycol n-butyl ether, or dipropylene glycol n-propyl ether. Glycol ether solvents that may be used also include propylene glycol monomethyl ether, propylene glycol t-butyl ether, ethylene glycol monoethyl ether, propylene glycol n-propyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether, ethylene glycol monobutyl ether, dipropylene glycol monomethyl ether, ethylene glycol n-hexyl ether, and tripropylene glycol methyl ether.

[0027] Low levels of mineral spirits or other aliphatic petroleum distillates may be present in some formulations, provided that the composition remains non-flammable. In such embodiments, drying agents such as cobalt-based, manganese-based, or zirconium-based drying agents or the like may be used. It is envisioned that solvents such as hexane, heptane, methylcyclohexane, cyclohexane, 2-2-dichloropropane and diethylene glycol would not be usable in concentrations over 1 percent due to their flammability.

[0028] In some embodiments, the aerosol coating composition may be devoid of solvents which are flammable or hazardous. These include aromatic solvents such as benzene, toluene, xylene, ethyl benzene, and naphtha, carbonate solvents such as propylene carbonate, ethylene carbonate, dimethyl carbonate, ethyl methylcarbonate and diethyl carbonate, ester solvents such as methyl acetate, n-butyl acetate, ethyl acetate, n-propyl acetate, amyl acetate, ethyl ethoxy proprionate, ethyl hexyl acetate, triacetin, isobutyl isobutyrate and dibasic ester, ketone solvents such as acetone, methyl ethyl ketone (MEK), methyl propyl ketone (MPK), methyl isobutyl ketone (MIBK), methyl isoamyl ketone (MIAK), cyclohexanone, methyl amyl ketone (MAK), disobutyl ketone (DIBK), C-11 ketone, and acetophenone, glycol ether acetate solvents, halogenated solvents, and terpene solvents.

[0029] Pigments may also be used as they commonly are in the coatings industry, at a level appropriate for the desired color of the final product. Example include carbon black, titanium dioxide, JHR1703L, Pigment Red 170 (Napthol Red), (Shanghai JECO Group Ltd., Shanghai, China), 2300, Pigment White 6 (TiO.sub.2, Kronos Worldwide, Dallas, Tex., USA), Heliogen L 6700 F, Pigment Blue 15:6 (Phthalocyanine Blue, BASF Ludwigshafen, Germany), Raven 850, Pigment Black 7, (Aditya Birla, Worli, Mumbai, India), Lysopac 6616B, Pigment Yellow 184, (Cappelle Pigments, Menen, Belgium) Pantint 12G1740P, Pigment Green 36 (chip dispersion, PAN Technologies, Carlstadt, N.J.), BF Micro, BF Micro Plus, and similar pigments.

[0030] The invention will be better understood by reference to the following examples which are included for the purpose of illustration and not limitation.

[0031] A white aerosol coating composition was created with the following components:

[0032] 5.5 weight percent isobutyl methacrylate resin,

[0033] 4.6 weight percent aliphatic petroleum distillate solvent (140 Flash),

[0034] 1.4 weight percent styrene-derived hydrocarbon resin (Piccolastic A5),

[0035] Mixed until dissolved and the added:

[0036] 0.1 weight percent Suspeno 201-MS 20 leveling agent,

[0037] 0.3 weight percent Nuosperse 657 (wetting and dispersing solvent),

[0038] 3.1 weight percent titanium dioxide,

[0039] 80.6 weight percent trans-1-Chloro-3,3,3-trifluoropropene

[0040] 0.7 weight percent Propylene Glycol Phenyl Ether,

[0041] 3.8 weigh percent CO.sub.2

[0042] (weight percentages approximate; +/−0.04 percent)

[0043] The composition provides a show-quality coating with no visible flaws.

[0044] In another example, a high-quality white coating was made:

[0045] 2.5 weight percent n-butyl methacrylate resin (Elvacite 4345)

[0046] 5 percent odorless mineral spirits

[0047] 2.5 weight percent Dipropylene Glycol n-Butyl Ether (DPnB)

[0048] 0.1 weight percent Suspeno 201-MS 20 leveling agent

[0049] 0.1 weight percent Nuosperse 657 wetting and dispersing agent

[0050] 2.3 weight percent Titanium dioxide

[0051] 83.2 weight percent trans-1-Chloro-3,3,3-trifluoropropene

[0052] 4.4 weight percent CO.sub.2

[0053] (weight percentages approximate; +/−0.04 percent)

[0054] Another coating combines 2 low-odor Glycol Ether tail solvents, Diethylene Glycol Monomethyl Ether and Dipropylene Glycol Monobutyl Ether, with a high molecular weight (for durability) butyl methacrylate acrylic resin (for flexibility, toughness), TiO.sub.2 pigment, and the additives, Nuosperse 657 and Suspeno 201-MS, to make a viscous (to minimize flammable solvent content) paint concentrate. To 13 parts of this concentrate, 87.5 parts of trans-1-Chloro-3,3,3-trifluoropropene are added, cans are crimped, and 4.5 parts of CO.sub.2 are added through the valve. Coatings were successfully made from this composition.

[0055] As stated above, trans-1-Chloro-3,3,3-trifluoropropene functions as both a solvent for the resin and as a propellant. Trans-1-Chloro-3,3,3-trifluoropropene may be combined with other propellant gases to provide an aerosol coating composition. Trans-1-Chloro-3,3,3-trifluoropropene is approximately 4 times as volatile as acetone (108.3 kPa vs. 25.0 kPa (@ 20° C.), a solvent which is already recognized as being one of the fastest evaporating (and most common) solvents used in aerosol coatings. It has been discovered that its vapor pressure (15 psi) may be augmented with the addition of accompanying propellants to provide a vapor pressure sufficient to be used as a propellant for a coating composition. In one particular example, a pressure in the range of 70-85 psig is provided. As shown in FIG. 1, levels as high as 13.5% CO.sub.2 have been successfully dissolved into trans-1-chloro-3,3,3-trifluoropropene. In some examples, such as those in which it is desired to minimize over spray during indoor application, the CO.sub.2 concentration to be used may be in a lower range, such as 3% CO.sub.2 (50 psig), 4% CO.sub.2 (65 psig), or 5% CO.sub.2 (80 psig). In one example, a resulting psi of 60 to 65 psig may be used.

[0056] It is envisioned that trans-1-chloro-3,3,3-trifluoropropene may be added in the form of a blended propellant, with 2-5% CO.sub.2. This will provide greater accuracy than attempting to add CO.sub.2 to aerosol. By pre-blending CO.sub.2 with trans-1-chloro-3,3,3-trifluoropropene, that error is decreased to within the very accurate capabilities of commercial propellant blend suppliers.

[0057] With aerosol coatings packaged in steel cans, material loss is limited to components (propellants & some solvents) that are able to escape through valve gaskets. To account for loss of product through aerosol valves, aerosol coatings manufacturers may include an overfill on their aerosol products. With aerosols packaged in plastic, however, there is an added possibility of the same materials escaping (permeating) through the container walls. Polyethylene and polypropylene, for example, have excellent chemical resistance, but are relatively permeable compared to plastics such as polyamide, polyvinylidene dichloride, and ethylene vinyl alcohol. PET is rated as having good barrier properties. The net content of several formulas, packaged in CKS Petaloid containers, were measured over several months and exhibited loss rates comparable to loss rates for steel aerosol cans. In another example, a combination of trans-1-Chloro-3,3,3-trifluoropropene and 5% CO.sub.2 was package in a PET container. No loss of container clarity or expansion with oven storage was observed.

[0058] Compositions according to the invention may have less than 1 percent of materials that are classified as flammable, have flash points below 93° C. (200° F.) and/or an indexed heat of combustion under 20 kJ/g. As mentioned above, such compositions are exempt from flammability tests under the 3.sup.rd revision of the United Nations GHS (Global Harmonization Systems) 2012 program, which became effective on May 25, 2012. Examples of such compositions are provided in Tables 1 and 2 below.

TABLE-US-00001 TABLE 1 Acrylic Formulation % kJ/g % GHS Flam Trans-1-Chloro-3,3,3- 86.57 9.08 0% trifluoropropene Triethyl Phosphate 3.72 38.48 0% Acrylic Resin (Dianal MB- 5.53 25.10 0% 7022) Ethylhexyl Diphenyl Phosphate 0.58 33.09 0% CO.sub.2 3.61 8.94 0% 100.00 11.19 0.00%  

TABLE-US-00002 TABLE 2 Alkyd Formulation % kJ/g % GHS Flam Trans-1-Chloro-3,3,3- 86.84 9.08 0% trifluoropropene Triethyl Phosphate 0.40 38.48 0% Alkyd resin 8.98 30.00 0% Cobalt Drier (Min Sp) 0.05 45.00 88%  Zirconium Drier (Min Sp) 0.09 45.00 76%  MEKO 0.02 42.73 100%  CO.sub.2 3.62 8.94 0% 100.00 11.13 0.06%  

[0059] The acrylic formulation of Table 1 is based on Dianal MB-7022, a (very) low (20K) molecular weight, thermoplastic film forming polymer, polyisobutyl methacrylate (IBMA). Advantages of this formulation strategy include water white clarity, <60 minute dry to touch, high sag resistance, no possibility of a recoat, good exterior durability, and, of particular importance, when packaged in PET plastic, a very strong visual appeal.

[0060] Pigmented coating compositions according to the present invention were also produced. A red coating containing a mixture of acrylic and alkyd resins (1.5:1) was produced having the composition provided in Table 3. A stock solution containing 60 weight percent Paraloid B-67 (IBMA) and 40 weight percent dipropylene glycol n-butyl ether (DPnB) was utilized to provide those components to the composition. Dipropylene glycol n-propyl ether (DPnP) may also be used in place of, or in addition to DPnB.

TABLE-US-00003 TABLE 3 Amt (g) Component % 14.20 Red 170 1.79 17.50 Paraloid B-67 2.21 26.25 DPnB 3.32 22.5 EPS 6677 2.84 0.06 MEKO 0.01 17.50 Paraloid B-67 2.21 26.25 DPnB 3.32 0.13 12% Cobalt 0.02 Cem All 0.09 10% Calcium 0.01 0.16 24% Zirconium 0.02 650.00 Trans-1- 82.17 Chloro-3,3,3- trifluoropropene 16.67 CO.sub.2 2.11 791.04 100.00

[0061] The composition contained 0.04% GHS-flammable solvent and when applied to a substrate by spraying, provided a film with an excellent appearance.

[0062] A similar red composition containing 0.18 alkyd to acrylic resin was also produced with the components provided in Table 4. A stock solution containing Paraloid B-67 (IBMA) and dipropylene glycol n-butyl ether (DPnB) was again utilized to mix components listed. Dipropylene glycol n-propyl ether (DPnP) may also be used in place of, or in addition to DPnB.

TABLE-US-00004 TABLE 4 Amt (g) Component % 14.20 Red 170 1.80 17.50 Paraloid B-67 2.21 26.25 DPnB 3.32 7.50 EPS 6677 0.95 0.06 MEKO 0.01 23.50 Paraloid B-67 2.97 35.25 DPnB 4.46 0.04 12% Cobalt 0.01 Cem All 0.02 10% Calcium 0.00 0.05 24% Zirconium 0.01 650.00 Trans-1- 82.17 Chloro-3,3,3- trifluoropropene 16.67 CO.sub.2 2.11 791.04 100.00
The composition contained 0.01% GHS-flammable solvent and the film provided by the composition was acceptable in appearance.

[0063] A white composition containing 0.78 alkyd to acrylic resin was formulated as shown in Table 5.

TABLE-US-00005 TABLE 5 Amt (g) Component % 6.78 TiO.sub.2 2.33 6.03 Paraloid B-67 2.08 9.05 DPnP 3.12 7.76 EPS 6677 2.67 0.02 MEKO 0.01 5.29 Paraloid B-67 1.82 7.93 DPnP 2.73 0.08 Borchi Dragon 0.03 241.38 Trans-1-Chloro-3,3,3- 83.09 trifluoropropene 6.19 CO.sub.2 2.13 290.51 100.00
The resulting composition contained 0.02% GHS-flammable solvents with low odor. The composition was applied to a substrate by spraying and the resulting film was excellent in appearance and durable.

[0064] A further white composition containing 0.19 alkyd to acrylic resin was formulated as shown in Table 6. A stock solution containing Paraloid B-67 (IBMA) and dipropylene glycol n-butyl ether (DPnB) was again utilized to mix components listed. Dipropylene glycol n-propyl ether (DPnP) may also be used in place of, or in addition to DPnB.

TABLE-US-00006 TABLE 6 Amt (g) Description % 19.66 TiO.sub.2 2.49 17.50 Paraloid B-67 2.21 26.25 DPnB 3.32 7.50 EPS 6677 0.95 0.06 MEKO 0.01 21.34 Paraloid B-67 2.70 32.01 DPnB 4.05 0.07 Borchi Dragon 0.01 0.00 10% Calcium 0.00 0.00 24% Zirconium 0.00 650.00 Trans-1-Chloro-3,3,3- 82.17 trifluoropropene 16.67 CO.sub.2 2.11 791.06 100.00
The resulting composition contained 0.01% GHS-flammable solvent and when applied to a substrate by spraying the resulting film provided a good initial appearance.

[0065] A coating composition containing acrylic resin only and no alkyd resin was formulated as provided in Table 7.

TABLE-US-00007 TABLE 7 Amt (g) Component % 9.91 TiO.sub.2 3.41 8.82 Paraloid B-67 3.03 13.22 DPnP 4.55 7.73 Paraloid B-67 2.66 11.59 DPnP 3.99 233.26 Trans-1-chloro- 80.29 3,3,3- trifluoropropene 5.98 CO.sub.2 2.06 290.51 100.00
The formulation contained 0.0% GHS-flammable solvent and the resulting film after application to a substrate by spraying, had a good initial appearance.

[0066] Black compositions according to the present invention were also formulated. The components of one such composition, containing a 1.5:1 acrylic resin to alkyd resin ratio, are provided in Table 8. A stock solution containing Paraloid B-67 (IBMA) and dipropylene glycol n-butyl ether (DPnB) was again utilized to mix components listed. Dipropylene glycol n-propyl ether (DPnP) may also be used in place of, or in addition to DPnB.

TABLE-US-00008 TABLE 8 Amt (g) Component % 1.49 Black 0.51 6.53 Paraloid B-67 2.25 9.79 DPnB 3.37 7.46 EPS 6677 2.57 0.07 MEKO 0.03 6.53 Paraloid B-67 2.25 9.79 DPnB 3.37 0.07 Borchi Dragon 0.03 0.00 10% Calcium 0.00 0.00 24% Zirconium 0.00 242.54 Trans-1-chloro- 83.49 3,3,3- trifluoropropene 6.22 CO.sub.2 2.14 290.51 100.00
The composition contained 0.02% GHS-flammable solvent and the resulting coating was excellent in appearance after application to a substrate by spraying.

[0067] An additional black coating composition having an alkyd to acrylic ratio of 0.17 was produced with the components listed in Table 9. A stock solution containing Paraloid B-67 (IBMA) and dipropylene glycol n-butyl ether (DPnB) was again utilized to mix components listed. Dipropylene glycol n-propyl ether (DPnP) could also be used.

TABLE-US-00009 TABLE 9 Amt (g) Component % 4.00 Black 0.51 17.50 Paraloid B-67 2.21 26.25 DPnB 3.32 7.50 EPS 6677 0.95 0.06 MEKO 0.01 27.58 Paraloid B-67 3.49 41.37 DPnB 5.23 0.07 Borchi Dragon 0.01 0.00 10% Calcium 0.00 0.00 24% Zirconium 0.00 650.00 Trans-1-chloro- 82.17 3,3,3- trifluoropropene 16.67 CO.sub.2 2.11 791.00 100.00
The composition contained 0.01% GHS-flammable solvent and the resulting coating after spraying onto a substrate exhibited some printability but provided a good coating with an overnight dry.

[0068] A further black coating composition was produced containing only acrylic resin and no alkyd resin was produced with the components listed in Table 10. A stock solution containing Paraloid B-67 (IBMA) and dipropylene glycol n-butyl ether (DPnB) was again utilized to mix components listed. Dipropylene glycol n-propyl ether (DPnP) could also be used.

TABLE-US-00010 TABLE 10 Amt (g) Composition % 1.93 Black 0.66 8.45 Paraloid B-67 2.91 12.68 DPnB 4.36 disperse to 7H 10.40 Paraloid B-67 3.58 15.61 DPnB 5.37 235.48 Trans-l- 81.03 Chloro-3,3,3- trifluoropropene 6.04 CO.sub.2 2.08 290.59 100.00
The composition contained 0.0% GHS-flammable solvent.

[0069] It should be evident that the present invention is highly effective in providing a non-flammable aerosol paint that also has a low impact on the environment. It should be understood that any variations evident fall within the scope of the claimed invention and thus, the selection of specific component elements can be determined without departing from the spirit of the invention herein disclosed and described.

Glossary of Components

[0070] MB 7022: Isobutyl methacrylate resin.
140 Flash aliphatic: aliphatic petroleum distillate solvent.
Piccolastic A5: styrene-derived hydrocarbon resin (Eastman Chemical Co., Kingsport Tenn.).
Suspeno 201-MS 20: leveling agent.
Nuo 657: Nuosperse 657, wetting and dispersing solvent
TI Pure R-960: titanium dioxide

PPH: Propylene Glycol Phenyl Ether

[0071] Elvacite® 2044: n-butyl methacrylate resin (Lucite International Inc., Cordova, Tenn., US)
Elvacite® 4345: n-butyl methacrylate resin with anti-caking agent. (Lucite International Inc., Cordova, Tenn., US)

Methyl Carbitol: 2-(2-Methoxyethoxy)ethanol.

[0072] Kronos 2300 TiO.sub.2: Titanium dioxide
DPnB: Dipropylene Glycol n-Butyl Ether
DPnP: Dipropylene Glycol n-Propyl Ether
Paraloid B-67: isobutyl methacrylate (IBMA) resin, MW 60,000. (Dow Inc., Midland Mich.)
MEKO: methyl ethyl ketoxime
EPS 6677: ˜100 percent solids long oil alkyd (Engineered Polymer Solutions, Marengo, Ill., US)
Borchi® Dragon: Cobalt-free metal ligand catalyst drying agent (Borchers, Westlake, Ohio, US)

Red 170: (Napthol Red), (Shanghai JECO Group Ltd., Shanghai, China)