PLATE-SHAPED NUCLEAR FUEL ELEMENT AND METHOD OF MANUFACTURING THE SAME

Abstract

A plate-shaped nuclear fuel element includes a core made of a fissile material and a cladding. The cladding further includes a frame defining a central aperture receiving the core and two cover plates sandwiching the frame and the core. The frame is made of a metallic first cladding material. The cover plates are made of a metallic second cladding material. The first cladding material has a hardness strictly greater than the hardness of the second cladding material.

Claims

1-14. (canceled)

15: A plate-shaped nuclear fuel element comprising: a core made of a fissile material; and a cladding, the cladding comprising: a frame defining a central aperture receiving the core; and two cover plates sandwiching the frame and the core, wherein the frame is made of a metallic first cladding material and the cover plates are made of a metallic second cladding material, the first cladding material having a hardness strictly greater than the hardness of the second cladding material.

16: The plate-shaped nuclear fuel element according to claim 15, wherein said hardness of the first cladding material is strictly lower than that of the core.

17: The plate-shaped nuclear fuel element according to claim 15, wherein the first cladding material is an aluminum alloy or a zirconium alloy.

18: The plate-shaped nuclear fuel element according to claim 15, wherein the first cladding material is an aluminum-magnesium alloy.

19: The plate-shaped nuclear fuel element according to claim 15, wherein the first cladding material is an AG4 or AG5 aluminum-magnesium alloy.

20: The plate-shaped nuclear fuel element according to claim 15, wherein the second cladding material is an aluminum alloy or a zirconium alloy.

21: The plate-shaped nuclear fuel element according to claim 15, wherein the second cladding material is an aluminum-magnesium alloy.

22: The plate-shaped nuclear fuel element according to claim 15, wherein the second cladding material is an AG3 aluminum-magnesium alloy.

23: The plate-shaped nuclear fuel element according to claim 15, wherein the fissile material contains at least one uranium alloy.

24: The plate-shaped nuclear fuel element according to claim 15, wherein the fissile material contains an uranium-silicon alloy, an uranium-molybdenum alloy, an uranium-aluminum alloy, an uranium-zirconium alloy or a combination thereof.

25: The plate-shaped nuclear fuel element according to claim 15, wherein the fissile material is made of U.sub.3Si.sub.2.

26: The plate-shaped nuclear fuel element according to claim 15, wherein a content of uranium of the fissile material is equal to or more than 2.5 gU/cm.sup.3.

27: The plate-shaped nuclear fuel element according to claim 15, wherein a content of uranium of the fissile material is strictly more than 4.8 gU/cm.sup.3.

28: The plate-shaped nuclear fuel element according to claim 15, wherein a content of uranium of the fissile material is less than 6.5 gU/cm.sup.3.

29: The plate-shaped nuclear fuel element according to claim 15, wherein a content of uranium of the fissile material is less than 5.3 gU/cm.sup.3.

30: A method of manufacturing a plate-shaped nuclear fuel element according to claim 15, the method comprising: providing the core, the frame having the aperture and the cover plates; inserting the core into the aperture of the frame; covering the frame containing the core with the two cover plates such that the cover plates sandwich the frame and the core; and rolling the sandwich such that the cover plates are bonded to the frame, the core being sealed into the cladding defined by the frame and the cover plates.

Description

BRIEF SUMMARY OF THE DRAWINGS

[0033] The present disclosure and its advantages will be better understood upon reading the following description given solely by way of non-limiting example and made with reference to the appended drawings, in which:

[0034] FIG. 1 is an front view of a plate-shaped nuclear fuel element;

[0035] FIG. 2 is a cross-sectional view of the nuclear fuel element along II-II on FIG. 1;

[0036] FIGS. 3 and 4 illustrate sealing of the core of the nuclear fuel element shown in FIGS. 1 and 2 into a cladding;

[0037] FIGS. 5 and 6 illustrate cross-sectional views of nuclear fuel elements taken with an optical microscope.

DETAILED DESCRIPTION

[0038] The nuclear fuel element 2 illustrated on FIG. 1 is for example intended to be used as a primary target in a nuclear reactor or as nuclear fuel for a research nuclear reactor in order to obtain neutrons.

[0039] The nuclear fuel element 2 is plate-shaped. The nuclear fuel element 2 has for example a length of approx. 150 mm for a primary target and up to approx. 1000 mm for use as nuclear fuel for research reactor, a width of e.g. 40 to 90 mm, and a thickness of approx. 1 mm to 3 mm. In view of obtaining a cylindrical nuclear fuel product, the plate-shaped fuel element 2 is e.g. rolled and welded on a diameter usually about 20 to 50 mm, e.g. 30 mm.

[0040] As visible on FIG. 2, the nuclear fuel element 2 comprises a core 4 made of a fissile material, the core 4 being sealed in a cladding 6.

[0041] The core 4 is surrounded by the cladding 6 in a sealed manner. The cladding 6 prevents the fissile material of the core 4 from migrating outside the cladding 6. The cladding 6 also holds the fissile products generated during irradiation of the nuclear fuel element 2.

[0042] The fissile material comprises for example uranium. The uranium content of the fissile material is preferably equal or higher than 2.5 gU/cm.sup.3, preferably strictly higher than 4.8 gU/cm.sup.3. The uranium content of the fissile material is for example equal or less than 6.5 gU/cm.sup.3, in particular equal or less than 5.3 gU/cm.sup.3.

[0043] The uranium contained in the fissile material is for example Low Enriched Uranium (LEU). By LEU, it is meant that the proportion of isotope U.sub.235 in the uranium is below 20 wt %, for example around 19.75 wt %.

[0044] The fissile material contains for example an uranium alloy, in particular an uranium alloy chosen among the group consisting of uranium-silicon alloy, uranium-molybdenum alloy, uranium-aluminium alloy and uranium-zirconium alloy, or a mixture thereof.

[0045] In a specific embodiment, the fissile material contains one single uranium alloy, in particular an uranium alloy chosen among the group consisting of uranium-silicon alloy, uranium-molybdenum alloy, uranium-aluminium alloy and uranium-zirconium alloy,

[0046] In a preferred embodiment, the uranium contained in the fissile material of the core 4 is provided as U.sub.3Si.sub.2.

[0047] The cladding 6 comprises a frame 8 having an aperture 10 receiving the core 4 and two cover plates 12 placed on the opposed faces of the frame 8 such that the frame 8 and the core 4 received in the central aperture 10 are sandwiched between the cover plates 12.

[0048] The frame 8 is made in a first cladding material and the cover plates 12 are made of a second cladding material different from the first cladding material.

[0049] The first cladding material has a hardness that is strictly higher than the hardness of the second cladding material and, preferably, strictly lower than the hardness of the core 4 (i.e. the hardness of the fissile material).

[0050] As it will be explained below, a method for manufacturing the nuclear fuel element 2 may comprise a hot-rolling performed at a temperature comprised for example between 300 C. and 600 C., in particular between 350 C. and 450 C.

[0051] In the temperature range comprised between 300 C. and 600 C., in particular in the temperature range comprised temperature 350 C. and 450 C., the first cladding material has for example a Vickers hardness (HV) comprised between 40 and 70 HV, the second cladding material has for example a Vickers hardness comprised between 30 and 60 HV and/or the core 4 has for example a Vickers hardness comprised between 50 and 100 HV.

[0052] As it will be explained below, a method for manufacturing the nuclear fuel element 2 may comprise a cold-rolling performed at room temperature.

[0053] At room temperature, the first cladding material has for example a Vickers hardness (HV) comprised between 50 and 100 HV, the second cladding material has for example a Vickers hardness comprised between 30 and 70 HV and/or the core 4 has for example a Vickers hardness equal to or greater than 100 HV.

[0054] The first cladding material and the second cladding material are for example metallic materials.

[0055] Each of the first cladding material and the second cladding material may be any type of metallic materials generally used in nuclear reactors, i.e. an aluminium alloy, such as EN AW-1050A, EN AW-6061, EN AW-5754, EN AW-5083, EN AW-5019 or AlFeNi, a zirconium alloy such as Zircaloy-2, Zircaloy-4 or ZrNb alloy, a Ni-based alloy such as Alloy 600, or stainless steel such as AISI 304L or AISI 316L.

[0056] The first cladding material is for example an aluminium-magnesium alloy (AlMg) in particular EN AW-5083, also known as AG4, or EN AW-5019, also known as AG5.

[0057] The second cladding material is for example an aluminium-magnesium alloy, in particular EN AW-5754, also known as AG3, comprising for example about 3 wt % of magnesium.

[0058] As illustrated on FIGS. 3 and 4, a method of manufacturing the nuclear fuel element 2 comprises the steps of: [0059] providing the core 4, the frame 8 and the cover plates 12, [0060] inserting the core 4 into the aperture 10 of the frame 8, [0061] placing the cover plates 12 to sandwich the frame 8 containing the core 4 with the cover plates 12 (see FIG. 4), and [0062] rolling the sandwich formed by the core 4 and the frame 8 received between the cover plates 12 such that the cover plates 12 are bonded to the frame 8, the core 4 being sealed into the cladding 6 defined by the frame 8 and the cover plates 12 (see arrow R on FIG. 4).

[0063] In a first substep, uranium and each other component of the uranium alloy of the fissile material are melted in a furnace, for example an arc furnace, an induction furnace or a resistance furnace. If any, the above-mentioned additional element(s) may be added to the melt in this first substep.

[0064] In a second substep, the melt is poured into a mould in order to form an ingot.

[0065] In a third substep, the ingot is grinded in order to obtain a uranium alloy powder. Advantageously the average size of the powder particles is less than 100 m, for example between 40 m and 70 m. For determining the powder particle size, laser granulometry can advantageously be used, in accordance with standard NF ISO 13320.

[0066] In a fourth substep, the powder is compacted to obtain a compact, for example having the shape of a parallelepiped. Advantageously, the compact has approximately the final width of the core 4 in the nuclear fuel product 1.

[0067] The porosity of the compact is advantageously determined by weighing the compact in air, then in water. During the latter measurement, the compact is completely immersed in water, with no air bubbles present on the suspension mechanism or on the compact. The porosity can then be calculated, knowing the theoretical density of the fissile material.

[0068] As an alternative, to shorten treatment duration and/or reduce the quantity of residual porosities, the sintering substep can be performed under high pressure, advantageously between 200 and 1000 bars, and at a temperature comprised between 400 C. and 900 C.

[0069] As an alternative to the fourth and fifth substeps, the powder may be cold-sprayed on a surface, preferably a surface of the cladding 6, advantageously at a temperature comprised between 30 and 500 C. Cold-spraying results in a dense and high quality deposit.

[0070] As an alternative to the second to fifth substeps, the powder may be directly cast in a mold having directly the size of the core 4, the additional elements, if any, being added in the first substep.

[0071] In view of sealing the core 4 with a cladding 6, the core 4 is placed in the central aperture 10 of a frame 8. The aperture 10 has a contour matching that of the core 4. The core 4 has for example a rectangular contour. The frame 8 extends along the sides of the core 4.

[0072] The frame 8 is preferably made integrally in one continuous single piece of material, e.g. by punching a plate to obtain the aperture 10. Alternatively, the frame 8 may comprise several frame pieces arranged around the core 4 to define a frame 8 extending along the sides of the core 4.

[0073] After placing the core 4 inside the frame 8, the cover plates 12 are placed on the opposed faces of the frame 8, in order to form a sandwich 14 comprising the frame 8 receiving the core 4 sandwiched between the two cover plates 12.

[0074] The two cover plates 12 are for example obtained by folding a sheet as shown on FIGS. 3 and 4. In such case, the two cover plates 12 are made integrally in one continuous single piece of material. Alternatively, the two cover plates 12 are provided separately.

[0075] In FIG. 4, the cladding 6 is sealed by rolling the sandwich 14 such that the cover plates 12 are bonded to the frame 8. Each cover plate 12 is thus bonded at its periphery to the frame 8 with closing the frame 8 in a sealed manner.

[0076] The rolling is for example a hot-rolling. The hot-rolling is preferably performed at a temperature comprised between 300 C. and 600 C., in particular a temperature comprised between 35 and 450 C.

[0077] The rolling is preferably performed along one rolling direction R, with one or several passe(s) along this rolling direction R.

[0078] The rolling step brings the core 4 to its final thickness and size and ensures a proper sealing of the core 4 inside the cladding 6 formed by the frame 8 and the upper and lower plates 12.

[0079] Optionally, the rolling step includes cold-rolling of the nuclear fuel element 2 performed after hot-rolling. Cold-rolling is performed at a temperature that is strictly lower than the temperature during hot-rolling. Cold-rolling is performed preferably at room temperature. Cold-rolling is performed e.g. to adjust the thickness and the length of the core 4.

[0080] Optionally, the final planar dimensions of the nuclear fuel element 2 are adjusted by cutting the edges of the nuclear fuel element 2. The cutting by any cutting technique such as press cutting, water cutting, laser cutting . . . .

[0081] Optionally, the final thickness of the nuclear fuel element 2 is adjusted for example by machining, chemical etching . . . .

[0082] Optionally, the nuclear fuel element 2 is submitted to a chemical cleaning according to known processes. Chemial cleaning is performed e.g. to degrease the nuclear fuel element.

[0083] Upon rolling the sandwich 14 in the rolling direction R, waves tends to form in the core 4 and to propagate towards the edges of the core 4 along the corresponding sides of the frame 8.

[0084] The apparition of a wave increases the risk of occurrence of a dog-bone effect with at least one of the cladding covers 12 being too thin in register with the wave, whereby the nuclear fuel element 2 has to be rebutted.

[0085] The size of the wave formed in the fissile material of the core 4 during rolling increases when the flow rate of the fissile material decreases and the flow rate of the fissile material decreases when the density of the fissile material increases.

[0086] Therefore, increasing the uranium content of the core 4 by increasing the density of the core 4 tends to increase the risk of occurrence of a detrimental dog-bone effect.

[0087] However, as the first cladding material of the frame 8 has a hardness that is strictly greater than the hardness of the second cladding material of the cover plates 12, the frame 8 is more resistant to deformation than the cover plates 12 and therefore tends to limit the size of a wave that is formed in the core 4 during rolling.

[0088] Besides, the first cladding material of the frame 8 having a hardness that is strictly lower than the hardness of the core 4 is less resistant to deformation than the core 4 which limits the risk or formation of a wave that is formed in the core 4 during rolling.

[0089] Hence, the frame 8 made of a first cladding material harder than that of the cover plates 12 and less hard than the core 4 allows increasing the uranium content of the core 4 by increasing density of the core 4 with limiting the risk of occurrence of a detrimental dog-bone effect.

[0090] The properties of the nuclear fuel element 2 are important, in particular for use as a primary target in a nuclear reactor or as nuclear fuel for a research nuclear reactor in order to obtain neutrons.

[0091] The geometry and composition of the core 4, including the fissile material and the density of the core 4, are important for neutronics. The cladding material is important for the chemistry of the primary circuit of the nuclear reactor.

[0092] The increase in uranium content of the core 4 with limitation of the risk of occurrence of a dog-bone effect can be obtained with materials (fissile material, first cladding material and second cladding material), shapes, dimensions and manufacturing techniques that are already qualified for uses in nuclear reactors.

[0093] Grinding the ingot into powder and then sintering the compact made from the powder provides a good homogeneity of the core 4 and allows reducing its porosity to a desired level, and therefore increasing its density and its uranium content.

[0094] Direct casting of the core 4 leads to a non-porous core 4.

[0095] FIG. 5 illustrates a view taken with an optical microscope of a cross-section of a first nuclear fuel element 2A having a core 4A made of U.sub.3Si.sub.2 and in which the frame 8A and the cover plates 12A are made of the same material that is AG3 whereby the frame 8A and the cover plates 12A have the same hardness.

[0096] FIG. 6 a view taken with an optical microscope of a cross-section of a second nuclear fuel element 2B that differs from that of FIG. 5 only in that the frame 8B is made of AG5 that is harder than the cover plates 12B made of AG3.

[0097] The first nuclear fuel element 2A and the second nuclear fuel element 2B were both manufactured with the same manufacturing method operated under the same conditions and including rolling a sandwich formed of a core inserted in a frame sandwiched between two cover plates.

[0098] FIGS. 5 and 6 illustrate that the dog-bone effect appears on the first nuclear fuel element 2A in which the frame 8A and the cover plates 12A are made of the same material and is limited or even avoided in the second nuclear fuel element 2B in which the frame 8A and the cover plates 12A are made of different materials, the material of the frame 8B being harder than the material of the cover plates 12A.

[0099] In particular, a first minimal thickness TA of the covers plates 12A of the first nuclear fuel element 2A is strictly lower than a second minimal thickness TB of the covers plates 12B of the second nuclear fuel element 2B.

[0100] In the present case, the first minimal thickness was measured at 204 m and the second minimal thickness was measured at 386 m.