Production of iron

Abstract

A continuous process provides direct reduction of iron ore in a solid state. Briquettes of iron ore fragments and biomass are transported through a preheating chamber and preheated to a temperature of at least 400° C. The preheated briquettes are transported through a heating/reduction chamber that has an anoxic environment, and iron ore and biomass in the briquettes are exposed to electromagnetic energy in the form of microwave energy under anoxic conditions. Microwave energy generates heat within iron ore, and biomass acts as a reductant and reduces iron ore in a solid state, as the briquettes move through the heating/reduction chamber.

Claims

1. A continuous process for direct reduction of iron ore in a solid state comprising transporting briquettes having a major dimension of 1-10 cm successively through a preheating chamber and a heating/reduction chamber, wherein the briquettes include iron ore fragments and biomass, and the biomass being 30-45% by mass of the briquettes supplied to the preheating chamber, the process including: preheating the briquettes to a temperature of at least 400° C. and less than 800° C. as the briquettes move through the preheating chamber; and exposing the preheated briquettes to electromagnetic energy, in the form of microwave energy, under anoxic conditions, as the preheated briquettes move through the heating/reduction chamber, with the microwave energy generating heat within the iron ore fragments and the biomass, and heating the preheated briquettes to a temperature of at least 800° C. and less than 1200° C., and with the biomass acting as a reductant and reducing iron ore in a solid state so that there is at least 90% metallization of iron ore in a solid state metallized product produced in the process.

2. The process defined in claim 1 includes controlling process operating conditions so that iron ore fragments are heated to a temperature in a range at which there is metallization of the iron ore fragments.

3. The process defined in claim 2 includes, in the case of hematite, controlling process operating conditions so that the iron ore fragments are heated to a temperature in a range of 800-950° C. for metallization of the hematite.

4. The process defined in claim 2 includes controlling process operating conditions so that the iron ore fragments are reduced to a required degree of metallization and forms a solid state metallic iron product.

5. The process defined in claim 1 includes heating the iron ore in the preheated briquettes to a temperature in a range of 850-950° C.

6. The process defined in claim 1 wherein the briquettes have a major dimension of 2-10 cm.

7. The process defined in claim 1 wherein the briquettes have a major dimension of 2-6 cm.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) The invention is described further by way of example only with reference to: (a) FIGS. 1 to 13 that relate to a feasibility study in relation to the invention that is described below and (b) FIG. 14 which is a block diagram of an embodiment of the invention, of which:

(2) More particularly:

(3) FIG. 1 is a graph of the dielectric properties of a range of engineering materials and minerals at a frequency of 2450 MHz at 20° C., together with water at different temperatures;

(4) FIG. 2 is a diagram that illustrates a resonant cavity perturbation method used to measure the dielectric properties of materials from 20-1000° C. in the feasibility study;

(5) FIGS. 3 and 4 are graphs for blended briquettes of PBF/biomass at 2450 MHz and 915 MHz, between 20-1000° C. tested in the feasibility study;

(6) FIG. 5 is a plot of penetration depths of blended PBF/biomass briquettes as a function of measurement temperature tested in the feasibility study;

(7) FIG. 6 is a plot of the DSC temperature-heat flow curves for iron ore and blended briquettes of PBF/biomass, in nitrogen, between 20-1000° C. tested in the feasibility study;

(8) FIG. 7 is a plot of the DSC heat flow curve for blended PBF/biomass briquettes alongside a corresponding TGA curve, showing the change in mass with temperature between 20-1200° C., tested in the feasibility study;

(9) FIG. 8 is a schematic of a full microwave treatment system used in the feasibility study;

(10) FIG. 9 is a plot of the mass-temperature curve of blended briquettes of PBF/biomass as determined using TGA under nitrogen between 20-1200° C., tested in the feasibility study;

(11) FIG. 10 is plots of the XRD spectra for ten microwave treatments;

(12) FIG. 11 is a graph of the ratio of XRD peaks as a function of microwave energy input tested in the feasibility study;

(13) FIG. 12 shows the XRD spectra for a PBF/sugar blend compared to a PBF/azolla blend and unprocessed ore fines tested in the feasibility study;

(14) FIG. 13 shows the XRD spectra for three sugar treatments compared to unprocessed ore fines tested in the feasibility study; and

(15) FIG. 14 is a diagram of one embodiment of a process and an apparatus for direct reduction of iron ore in a solid state in accordance with the invention.

DETAILED DESCRIPTION OF THE EMBODIMENTS

(16) In broad terms, the process of the invention includes exposing iron ore and biomass to electromagnetic energy with iron ore and biomass in contact under anoxic conditions, with the electromagnetic energy generating heat within the iron ore, and with the biomass acting as a reductant and reducing iron ore in a solid state.

(17) Feasibility Study

(18) The above-mentioned feasibility study was undertaken to determine the technical feasibility of achieving metallization of iron ore (in the form of the Pilbara Blend Iron Ore Fines (PBF) product of a related company of the applicant) blended with azolla biomass using microwave energy as the heating source for the iron ore and the biomass.

(19) The dielectric and thermal properties of iron ore, biomass and blended briquettes of iron ore/biomass were characterised and evaluated.

(20) The objectives of the study were as follows: Measurement of dielectric properties of PBF, biomass and blended briquettes of PBF/biomass to quantify the relationship between temperature (20-1000° C.) and complex permittivity (microwave absorbing properties) at the industrially utilised frequencies of 2450 MHz and 915 MHz. Differential scanning calorimetry of the PBF and blended briquettes between 20-1000° C. to identify key material transitions in the reduction process under nitrogen, determine the relationship between temperature and metallization and identify the expected temperature required to metallize blended briquettes using microwave energy. Thermogravimetric analysis of the PBF and blended briquettes between 20-1000° C. under nitrogen to determine the relationship between temperature and mass loss during the reduction process, and identify the expected residual mass of blended briquettes metallized using microwave energy. Microwave heating trials of blended briquettes under anoxic conditions at 2.45 GHz to determine the influence of microwave power density (1 or 2 kW applied power), total applied energy (up to 75 GJ/t product) and treatment time (between 1 and 16 minutes) on metallization. Semi-quantitative XRD characterisation of PBF, blended briquettes and all microwave treated samples to identify all iron containing phases and determine the relationship between microwave treatment conditions and the degree of metallization achieved. Microwave treatment of PBF blended with 35%, 50% and 65% sucrose (by mass) to determine the influence of biomass type and biomass content on the degree of metallization. Measurement of external temperatures of a firebrick treatment enclosure following treatment at highest energies and estimation of the heat loss from the sample to the enclosure, to determine the microwave treatment energy balance and potential efficiencies for an optimised industrial process where heat losses are minimised.
1. Materials Characterisation (Work Program 1)

(21) This section presents the theory, methodology and results of characterisation of the PBF, azolla biomass and blended briquettes of PBF/biomass, which were performed to understand their fundamental interactions with microwave energy prior to commencing the test matrix in Work Program 2.

(22) 1.1 Dielectric Characterisation

(23) 1.1.1 Dielectric Theory

(24) The ability of materials to absorb and subsequently heat due to an applied electromagnetic field is dependent on the electrical and magnetic properties of the material, specifically the permittivity (ε), permeability (μ), and conductivity (σ.sub.e). For most materials, the dominant interaction is with electric field; dielectric properties are a measure of this interaction. The dielectric properties of a homogenous material are described by the complex relative permittivity as shown in Equation 1:
ε*=ε′−jε″  Equation 1
Where ε*=complex relative permittivity; ε′=dielectric constant; ε″=dielectric loss factor; j=√−1.

(25) The dielectric constant (real part of the permittivity), ε′, measures the ability a material to be polarised by an external electric field; i.e. the ability of charges and dipoles to be polarised. The dielectric loss factor (imaginary part of the permittivity), ε″, measures the ability of a material to dissipate the stored energy as heat. Dielectric properties of materials can vary according to composition, water content, temperature, frequency and density. FIG. 1 plots the dielectric properties at 2450 MHz, for a range of engineering materials and minerals at 20° C., together with water at different temperatures.

(26) 1.1.2 Complex Permittivity Measurement

(27) Dielectric property measurements were performed on both the PBF and azolla biomass components and also the blended briquettes. Their relationship with temperature up to 1000° C. was quantified. This knowledge provides mechanistic understanding of the process and also crucially informs both the test methodology for WP2 and discussions around the potential for full scale system development. These measurements were performed at the industrially utilised microwave frequencies of 2450 and 915 MHz.

(28) A resonant cavity perturbation method (see FIG. 2) was used to measure the dielectric properties of the materials from 20-1000° C. The resonant cavity consists of a cylindrical copper cavity connected to a vector network analyser, which measures the frequency shift and change in quality factor relative to the empty resonating cavity when a sample is introduced. Finely milled samples (<100 μm) were loaded into a quartz tube, (ceramic wool below the sample and open at the top to minimise air ingress) and held in a conventionally heated furnace above the cavity until the temperature set-point was reached. The tube was then moved into the cavity, and the properties determined at the industrially utilised microwave frequencies of 2450 MHz and 915 MHz. It should be noted that as it was not possible to safely conduct the dielectric characterisation in anoxic conditions (i.e. under nitrogen) as the cavity and furnace were both open to the laboratory.

(29) The results of the dielectric property measurement of the PBF, azolla biomass and the blended briquettes of PBF/biomass at 2450 MHz and 915 MHz, between 20-1000° C., were plotted. FIGS. 3 and 4 are the graphs for blended briquettes of PBF/biomass at 2450 MHz and 915 MHz, between 20-1000° C. In each graph, the temperature is plotted on the horizontal axis, the dielectric constant on the left vertical axis (blue line) and the dielectric loss on the right vertical axis (red line). Measurements at 2450 MHz relate to the frequency commonly used for laboratory scale testing, whilst measurements at 915 MHz relate to the frequency currently utilised for most industrial processing systems at power levels over 50 kW.

(30) The PBF was found to have relatively consistent dielectric properties between 20-600° C. Slight inflections at around 100° C. and 300-400° C. were due to the removal of free water and goethite hydroxyl groups respectively. Above 600° C., PBF exhibited an increase in dielectric properties, attributed to temperature dependent iron oxide phase changes.

(31) The azolla biomass was found to strongly absorb microwave energy below approximately 150° C. and above 500° C. The reduction in dielectric properties between 100-200° C. was due to the removal of free water. The increase above 500° C. was due to the pyrolysis of the biomass, releasing volatiles to leave carbonaceous char and ash (due to the imperfect seal on the tube it is unlikely that fully anoxic conditions would have been achieved).

(32) Not surprisingly given the above results for PBF and biomass separately, the measurement results for the blended briquettes of PBF/biomass exhibited characteristics of both the iron ore and biomass. Inflections between 100-200° C. and between 300-400° C. were due to removal of free water from both the iron ore and the biomass, and removal from goethite hydroxyl groups. The increase between 500-700° C. was due to combustion of the biomass, as again the open tube did not permit a fully reducing atmosphere. The decrease above 700° C. was due to progressive reduction of the iron oxides.

(33) Overall, both the PBF and the azolla biomass, and the blended briquettes of PBF/biomass strongly absorbed microwave energy across the full temperature range measured, at both 2450 MHz and 915 MHz, particularly below 200° C. and above 700° C.

(34) 1.1.3 Penetration Depth

(35) When an electromagnetic energy wave propagates in a dielectric material, its amplitude diminishes due to power absorption in the material. The field intensity and power falls exponentially with depth from the materials surface. Dp, the penetration depth of electromagnetic energy into a material, is defined as the depth at which the power flux falls to 1/e (0.368) of its surface value,

(36) The penetration depth in a material is a good indicator of the potential to achieve heating uniformity within a material. Penetration depth is proportional to wavelength; at higher frequencies surface heating is more likely, whilst at low frequencies volumetric heating is more readily attained. Penetration depth is important when volumetric heating of a material is required. It should be noted that some heating occurs beyond the defined penetration depth, as the electric field has not reached zero until some point after the penetration depth. Selection of the appropriate frequency is important to ensure that the dimensions of the material are not much larger than penetration depth; thus it is a key design parameter when considering process design and scale up.

(37) The penetration depths of blended PBF/biomass briquettes were calculated and are plotted in FIG. 5 as a function of measurement temperature. The blended briquettes exhibited an increase in penetration depth between 100 and 200° C., due to the removal of free water. The penetration depth then decreased around 300° C., with a slight inflection around 350° C. due to the removal of hydroxyl groups. Above 500° C., the penetration depth remained relatively constant. The penetration depth was high at 915 MHz compared to 2450 MHz (approximately 5 cm and 2 cm respectively, above 500° C.). Overall, the penetration depth was similar in scale to the dimensions of the blended briquettes. This suggests that from a microwave heating perspective, it would be possible to achieve volumetric heating of a continuous load of 5-10 cm thick at 915 MHz.

(38) 1.2 Thermal Characterisation

(39) Thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) were performed on both the PBF and blended briquettes of PBF/biomass in anoxic conditions (under nitrogen) and their relationship with temperature up to 1000° C. was quantified.

(40) DSC allows mapping of thermal behavior and identification of ‘thermal events’ during the heating process.

(41) TGA provides a mechanistic understanding of how the briquette mass should change during the microwave treatment process. Combining the thermal behavior data enables the prediction of a ‘metallization range’ based on mass loss of microwave treated samples, as measured following treatment.

(42) FIG. 6 plots the DSC temperature-heat flow curves for both the iron ore and blended briquettes of PBF/biomass, in nitrogen, between 20-1000° C. From these curves, three thermal events can be identified that occur during the direct reduction of iron ore in the presence of biomass under DSC conditions. The first is the removal of free water just above 100° C. from the biomass fraction of the briquettes. The second thermal event is the removal of goethite hydroxyl groups and conversion to hematite; this peak is shifted slightly in the briquette sample. This is possibly due to pyrolysis products from the biomass allowing the conversion of goethite to hematite to occur at a lower temperature. The final thermal event identified is the onset of metallization at around 850° C. in the briquette sample.

(43) In FIG. 7, the DSC heat flow curve for blended PBF/biomass briquettes is plotted alongside the corresponding TGA curve, showing the change in mass with temperature between 20-1200° C. (the temperature measurement range for the briquette was extended from 1000° C. to identify the metallization endpoint). The data suggests a metallization start point around 850° C. and an endpoint at approximately 950° C., under DSC conditions.

(44) At the metallization endpoint, the weight change with temperature of the briquette starts to plateau. The residual mass of the DSC-TGA sample at this temperature was 57%. This suggests that if microwave treatment conditions are the same as those for characterisation, treated samples weighing less than 57% of their original mass should be metallized, with little or no iron oxides present.

(45) 1.3 Work Package 1 Summary

(46) The dielectric properties of the PBF, biomass and blended briquettes of PBF/biomass were measured using the cavity perturbation method, between 20-1000° C. at the industrially utilised frequencies of 2450 MHz and 915 MHz. The results indicate that all the materials exhibit strong microwave absorbing properties across the full range measured. Above 500° C., the penetration depths are relatively constant (˜2 cm at 2450 MHz and ˜5 cm at 915 MHz). This indicates that at 915 MHz it would be possible to achieve volumetric heating of a continuous load 5-10 cm thick, although some heating occurs beyond the defined penetration depth. These results show that the materials should all strongly absorb microwave energy throughout all metallization experiments proposed in Work Package 2. Differential scanning calorimetry of the PBF and blended briquettes of PBF/biomass between 20-1000° C. was used to identify key material transitions in the reduction process under nitrogen, determine the relationship between temperature and metallization and identify the expected temperature required to metallize blended briquettes using microwave energy. The key region for metallization of the briquettes was identified to be between 850-950° C. Thermogravimetric analysis of the PBF and blended briquettes between 20-1000° C. under nitrogen was conducted to determine the relationship between temperature and mass loss during the reduction process, and identify the expected residual mass of blended briquettes metallized using microwave energy. The suggested mass of a metallized sample at 950° C. was ˜57% of its mass prior to reduction. This suggests that if DSC-TGA and microwave treatments provide equivalent reductive atmospheres, samples treated in Work Program 2 with a mass of ˜57% should exhibit metallization.
2. Microwave Proof of Concept Testing (Work Program 2)

(47) This section presents the experimental methodology and results of microwave heating experiments to determine the technical feasibility of achieving full metallization through heating the PBF/azolla blended briquettes using microwave energy in an anoxic atmosphere.

(48) The tests carried out quantify the relationship between energy input, power density, treatment time and the degree of metallization of the product. The outcome of each different microwave treatment was evaluated through semi-quantitative X-ray diffraction (XRD) to determine the degree of metallization that had been achieved relative to the untreated briquettes.

(49) 2.1 Experimental Methodology and Treatment System

(50) A range of laboratory and bespoke microwave systems was available for proof of concept microwave treatments. The dielectric property measurements carried out in Work Program 1 showed that the iron ore/biomass blend has strong microwave absorbing properties.

(51) A laboratory scale multimode system (regions of high and low electric field across the cavity) was selected, with dimensions of 540×425×425 mm. Microwave treatments were carried out at the allocated frequency of 2450 MHz which is best suited to small scale laboratory testing.

(52) For each treatment carried out, an approximately 27 g (˜4 briquettes) sample of material was weighed out and placed into a mullite firebrick enclosure inside the multimode cavity. This material is essentially transparent to microwave energy compared to the briquettes and it was therefore been assumed that all applied energy was absorbed by the sample although in reality there would have been energy dissipation into this phase both through weak microwave heating and heat transfer from the briquettes. This enclosure was used to reduce heat losses from the sample surface during processing.

(53) The system was inverted with nitrogen at a flowrate of 25 litres per minute prior to and during microwave treatment to provide anoxic conditions.

(54) The sample was then treated at the selected power and treatment time.

(55) Air extraction was used during microwave processing to remove any gases and particulates generated during pyrolysis of biomass fraction of the briquettes.

(56) During treatment, the energy absorbed by the load was monitored and controlled using an automatic tuner and PC.

(57) A schematic of the full microwave treatment system is shown in FIG. 8.

(58) For the highest microwave doses, the temperatures on the outside of the firebrick were measured immediately after microwave treatment using an infra-red gun, to allow the heat dissipation into the firebricks and thus energy balance to be estimated.

(59) Once the material had cooled, it was recovered from the firebrick enclosure and re-weighed to determine the mass lost during treatment, then milled to a fine powder for XRD characterisation.

(60) 2.2 Microwave Treatment Results

(61) To determine the influence of energy input and power density/treatment time on the degree of metallization, a matrix of 11 treatments was completed, as shown in Table 1 below.

(62) TABLE-US-00001 TABLE 1 Feasibility study test matrix Applied power Treatment time Actual dose Gross energy (kW) (min) (kWh/t briquettes) GJ/t product 2 1 1081 5 2 2 2132 11 2 4 4568 30 2 6 6164 48 2 8 8373 74 2 10 11296 * 1 2 1319 6 1 4 2365 12 1 8 5345 33 1 12 6643 48 1 16 9531 73 * This sample was molten and penetrated the mullite firebrick enclosure, with repeat treatments yielding the same result. It was therefore not possible to recover a clean sample for comparative XRD analysis and energy balance estimation with other treatments.

(63) Applied power was set at either 1 kW or 2 kW, and treatment times of between 1 and 16 minutes were used. An automatic tuner was used to minimise reflected power and ensure >95% of applied energy was absorbed. These treatments gave resulting microwave energy inputs of between 1000-11300 kWh/t of briquettes, equivalent to between 5 and 74 GJ/t of product (based on the mass treated material recovered).

(64) A visual inspection of the untreated and microwave treated briquette samples after milling showed a clear progressive colour change with increasing energy input, due to the level of reduction of iron minerals from red hematite through to grey metallic iron.

(65) FIG. 9 plots the mass-temperature curve of blended PBF/biomass briquettes as determined using TGA under nitrogen between 20-1200° C.

(66) From the DSC characterisation of the blended briquettes carried out in Work Package 1, the expected endpoint of the reduction process (under DSC conditions) was approximately 950° C. At this temperature, the TGA had a residual sample mass of 57%. By plotting the residual mass for microwave treated samples against microwave energy input in FIG. 9, and fitting a treatment curve for 1 kW and 2 kW applied power, it was possible to determine a predicted metallisation range, based on residual mass. This prediction assumed that all residual mass from the microwave treated samples had been recovered and that reduction conditions for DSC-TGA and microwave treatment were similar.

(67) Based on this, four of the microwave treated samples (highlighted in the yellow region of FIG. 9) showed significant or complete metallization. The curves also suggested that a microwave energy dose of ˜38 GJ/t of product in the un-optimised system used would be sufficient to achieve metallization based on a residual mass of 57%.

(68) FIG. 10 plots the XRD spectra for the ten microwave treatments for which the full residual sample mass was recoverable, together with the XRD spectra for the untreated briquettes. Labels represent the major peaks for each of the iron minerals present in the samples (some minor peaks have not been identified by the mineral identification software)

(69) The XRD results show a clear increase in the level of transformation from hematite to metallic iron with increasing microwave energy input/treatment time. Of the four samples identified in FIG. 10 as likely to have a high degree of metallization, three have significant peaks for metallic iron, namely 1 kW 12 minutes, 1 kW 16 minutes and 2 kW 8 minutes.

(70) The spectra for intermediate treatment energies also reveal the presence of two other iron oxide reduction products, magnetite and wustite. The presence of these intermediates suggests the following metallization pathway under anoxic conditions:
Fe.sub.2O.sub.3.fwdarw.Fe.sub.3O.sub.4.fwdarw.FeO.fwdarw.Fe
Hematite.fwdarw.magnetite.fwdarw.wurstite.fwdarw.iron

(71) The XRD spectra for the samples with a high degree of metallization also revealed a side reaction, which occurs between quartz and magnetite at high temperatures, the production of fayalite (olivine) and additional oxygen:
2Fe.sub.2O.sub.3+3SiO.sub.2.fwdarw.3Fe.sub.2SiO.sub.4+O.sub.2

(72) From the tests conducted in this feasibility study, it was not possible to determine whether the production of intermediates and side products was driven by energy input/treatment time or by the levels of oxygen present during microwave treatment.

(73) Due to the amorphous content of the samples resulting from the high biomass content, it was not possible to provide quantitative results with respect to the amount of iron and iron oxides present in each of the samples. Given that the reduction reaction proceeds from hematite through to iron, it was possible to estimate the degree of metallization. For each sample, the areas under the principal iron peak (44.2<2θ<45.0) and the principal hematite peak (32.3<2θ<33.7) were determined. FIG. 11 plots the ratio of these peaks as a function of microwave energy input.

(74) At treatment energies below 12 GJ/t product (equivalent to approximately 2400 kWh/t blended briquettes) an increase in power density increased the degree of metallization. FIG. 11 shows higher mass loss at equivalent energy inputs at 2 kW compared to 1 kW applied power. This can be attributed to faster heating rates, which are more significant at shorter treatment times. This effect was validated by the XRD spectra in FIG. 10, which shows the presence of goethite in the 1 kW 4 minutes sample, but not in the 2 kW 4 minutes sample, suggesting that the goethite dihydroxylation temperature (between 300 and 400° C.) had not been exceeded at the lower power, even though treatment energies are the same.

(75) 2.4 Additional Sugar Treatment Results

(76) An additional treatment was undertaken, replacing the biomass with white granulated table sugar, i.e. sucrose, C.sub.12H.sub.22O.sub.11.

(77) 12 grams of sucrose was mixed with 18 grams of PBF, together with 5 ml of water, forming a thick paste. The sample was treated using the same method as the briquettes, at 2 kW for 8 minutes.

(78) FIG. 12 shows the XRD spectra for the PBF-sugar blend compared to the PBF/azolla blend and the unprocessed ore fines. The sugar sample exhibited lower levels of metallization compared to the azolla at equivalent microwave energy input. The XRD also shows that higher proportions of the intermediate iron oxides, magnetite and wustite, were formed when using sugar. This is not thought to be due to loss of sugar into the firebrick as high temperature putty was used to reduce the permeability of the treatment enclosure.

(79) A key observation here is that varying the type of biomass used in the direct reduction process provides an opportunity to control the proportion of intermediate oxides formed.

(80) Two additional treatments using sugar were also carried out, at 50% and 70% sugar content by mass.

(81) FIG. 13 shows the XRD spectra for the three sugar treatments compared to unprocessed ore fines. The higher sugar content samples exhibited a higher degree of metallization with lower levels of intermediate iron oxides remaining. This suggests that a higher proportion of reducing gases present leads to better metallization.

(82) 2.5 Energy Balance

(83) Estimates of sensible microwave energy input showed that metallization of iron ore blended with biomass could be achieved at significantly lower microwave energy inputs than those totals quoted and potentially of the same order as the sensible DRI energy used in the best performing commercial DRI processes (˜2 GJ/tonne for gas based system), even at laboratory scale in a non-optimised system.

(84) More particularly, an energy balance with a basic estimate of heat losses during microwave processing indicated that direct reduction of iron ore using microwave heating at small batch scale was achieved at energy inputs of 1.6 GJ/t product. Without estimation of heat losses this is equivalent to around 32 GJ/t of blended briquette feed, or 74 GJ/t product.

(85) It should be possible to reduce this value significantly in an optimised industrial system where heat losses are minimised.

(86) Experience of scale up indicates that significantly higher energy inputs, often of several orders of magnitude greater, are required in small un-optimised batch lab scale systems compared to in the continuous operation of a well-designed optimised industrial process.

(87) 2.6 Work Package 2 Summary

(88) Laboratory scale microwave treatments at 2450 MHz using a non-optimised system and subsequent semi-quantitative XRD analysis, demonstrated that high levels of metallization could be achieved using microwave energy. Analysis of XRD characterisation of briquettes of 35% and 40% biomass content (by mass) processed using a conventional furnace suggests that optimising the biomass type and amount could enhance the reduction process by controlling the reducing atmosphere and associated reactions of iron within that atmosphere. This trend was also observed in the XRD spectra for PBF blended with 35%, 50% and 70% sugar content, with higher sugar loadings resulting in more complete metallization and reduced proportions of intermediate iron oxides at equivalent bulk microwave energy inputs.
3. Conclusions Form Work Packages 1 and 2

(89) The feasibility study showed that it is possible to achieve metallization of iron ore blended with biomass, using microwave energy as the heat source. The dielectric properties measured show that the PBF (iron ore fines) azolla biomass and blended briquettes all interacted strongly with microwave energy at the industrially utilised frequencies of 2450 MHz and 915 MHz. The derived microwave penetration depth of 5 cm at 915 MHz above 500° C. verified that from a microwave heating perspective it would be possible to achieve volumetric heating of a continuous load of 5-10 cm thick (although some heating did occur beyond the defined penetration depth). There was no clear effect of power density (between 1 kW and 2 kW) on the degree of metallisation, at temperatures above 500° C. and 30 GJ/t product microwave energy input. However the ability to provide bulk heating to the material provides the opportunity to overcome heat transfer limitations. This could lead to faster heating rates and shorter residence times, with the resulting lower plant size, direct use of sinter fines, reduced CAPEX and greater process control as possible advantages. The variable production of intermediate iron oxides, (magnetite and wustite) and side reaction products (fayalite) for different biomass loadings indicated that there is an opportunity to optimise the reduction and metallization process by altering biomass content and controlling the reductive atmosphere, leading to metallization at lower microwave energy inputs. Finally, the energy balance estimated heat losses in feasibility testing in the non-optimised system of almost 90%. Metallization at MW energy inputs of ˜2 GJ/t product could therefore be achievable in an optimised industrial process with heat losses minimised.

(90) FIG. 14—Block Diagram of an Embodiment

(91) With reference to the block diagram of FIG. 14, in one embodiment of the invention, briquettes of a blend of a selected ratio of iron ore fines and biomass are supplied as a feed material to a pre-heating furnace 3 and pre-heated to a temperature in the range of 400-600° C. for a pre-determined time.

(92) The pre-heating furnace 3 is designed to operate on a batch basis.

(93) The pre-heated briquettes are then transferred to a reduction assembly 5 and the iron ore fines are heated and reduced in the assembly 5.

(94) The assembly 5 is also designed to operate on a batch basis.

(95) The assembly 5 includes a chamber for the briquettes, a source of microwave energy, a wave guide for transferring electromagnetic energy in the form of microwave energy at 2450 MHz or other suitable frequency to the chamber, a source of inert gas, such as nitrogen, suitable pipework for supplying the inert gas to the chamber to maintain the chamber under anoxic conditions during the treatment of the briquettes in the chamber, and an outlet for discharging gas and any retained particulates that are generated during the treatment in the chamber.

(96) In use, while the chamber is maintained under anoxic conditions, microwave energy heats the iron ore fines and biomass and generates heat within both constituents of the briquettes, with the result of reduction of the iron ore fines in a solid state via the biomass within the briquettes to form a solid state metallised product.

(97) The process includes a control system for controlling the operating conditions so that iron ore is heated to a selected temperature for a selected residence time at temperature. In the case of hematite, the process includes controlling the operating conditions so that the hematite is heated to a temperature in a range of 800-1100° C. to metallise the hematite.

(98) The solid state metallised product can be stored and transported to other plants to be processed as required to produce end-use steel or other products.

(99) Whilst the embodiment described in relation to FIG. 14 is described as a batch process, it can readily be appreciated that the invention is not so limited and could be operated as a continuous process in both pre-heating and reduction steps.

(100) In addition, whilst the embodiment described in relation to FIG. 14 is described as operating with microwave energy, it can readily be appreciated that the invention is not so limited and could be operated with any suitable electromagnetic energy