DENTAL MEMBER

Abstract

The present invention provides a dental member, which has a reduced size, and thus prevents damages to tooth roots upon implantation, has high strength and low elasticity, and is excellent in engraftment stability after implantation. The dental member is produced with an amorphous alloy having a composition represented by formula: Zr.sub.aNi.sub.bCu.sub.cAl.sub.d [wherein a ranges from 60 to 75 at. %, b ranges from 11 to 30 at. %, c ranges from 1 to 16 at. %, and d ranges from 5 to 20 at. %] and is used as an orthodontic anchor screw wherein the screw part has a core diameter of 0.5-1.0 mm or a length of 2-5 mm, a one-piece-type dental implant wherein the screw part has the largest diameter of 0.5-2.9 mm and a length of 2-13.4 mm, or a two-piece-type dental implant wherein the screw part has the largest diameter of 0.5-2.9 mm and a length of 2-5.9 mm.

Claims

1. A dental member, containing an amorphous alloy having a composition represented by formula: Zr.sub.aNi.sub.bCu.sub.cAl.sub.d [wherein a, b, c, and d denote at. %, a ranges from 60 to 75 at. %, b ranges from 11 to 30 at. %, c ranges from 1 to 16 at. %, and d ranges from 5 to 20 at. %].

2. The dental member according to claim 1, comprising an orthodontic anchor screw or a dental implant.

3. The dental member according to claim 1, comprising an orthodontic anchor screw wherein the screw part has a core diameter between 0.5 mm and 1.0 mm or a length between 2 mm and 5 mm.

4. The dental member according to claim 1, comprising a one-piece-type dental implant wherein the screw part has the largest diameter between 0.5 and 2.9 mm and a length between 2 and 13.4 mm, or a two-piece-type dental implant wherein the screw part has the largest diameter between 0.5 and 2.9 mm and a length between 2 and 5.9 mm.

5. The dental member according to claim 1, wherein a ranges from 67 to 73 at. %, b ranges from 11 to 17 at. %, c ranges from 5 to 13 at. %, and d ranges from 5 to 9 at. %.

6. The dental member according to claim 5, wherein c ranges from 7 to 13 at. %, or, d ranges from 5 to 7 at. %.

7. The dental member according to claim 1, wherein a ranges from 69 to 73 at. %, b ranges from 13 to 17 at. %, c ranges from 5 to 10 at. %, and d ranges from 5 to 9 at. %.

8. The dental member according to claim 1, wherein the surface is coated with zirconia ceramics.

9. The dental member according to claim 8, which is produced by heating said amorphous alloy in an atmosphere where oxygen is present at a temperature where no crystallization or no embrittlement takes place.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0015] FIG. 1 shows scanning electron microscope (SEM) photograms (a) a pure titanium screw, as well as the dental members of embodiments of the present invention, orthodontic anchor screws made of amorphous alloys having compositions (b) Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8, (c) Zr.sub.68Ni.sub.12Cu.sub.12Al.sub.8, and (d) Zr.sub.72Ni.sub.16Cu.sub.6Al.sub.6 used in experiments.

[0016] FIG. 2 shows graphs (a) implantation torques and (b) removal torques immediately after implantation in a test of implantation of the dental member of an embodiment of the present invention, an orthodontic anchor screw made of an amorphous alloy having a composition of Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8, into rat tibia.

[0017] FIG. 3 shows graphs (a) removal torques seven days after implantation and (b) removal torques 28 days after implantation in a test of implantation of the dental member of an embodiment of the present invention into rat tibia.

[0018] FIG. 4 shows graphs (a) implantation torques and (b) removal torques seven days after implantation in a test of implantation of the dental members of embodiments of the present invention, orthodontic anchor screws made of amorphous alloys having compositions of Zr.sub.68Ni.sub.12Cu.sub.12Cu.sub.12Al.sub.8 and Zr.sub.72Ni.sub.16Cu.sub.6Al.sub.6, into rat tibia.

[0019] FIG. 5 shows graphs showing changes over time in mobility after implantation (Periotest value) in a test of implantation of the dental member of an embodiment of the present invention, an orthodontic anchor screw made of an amorphous alloy having a composition of Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8 subjected to (a) no immediate loading, (b) 10 g of immediate loading, and (c) 50 g of immediate loading into rat tibia.

[0020] FIG. 6 shows graphs showing changes over time in mobility after implantation (Periotest value) in a test of implantation of the dental members of embodiments of the present invention, orthodontic anchor screws made of amorphous alloys having compositions Zr.sub.68Ni.sub.12Cu.sub.12Al.sub.8 and Zr.sub.72Ni.sub.16Cu.sub.6Al.sub.6 subjected to (a) no immediate loading until seven days after implantation, (b) 10 g of immediate loading until seven days after implantation, and (c) no immediate loading until 28 days after implantation into rat tibia.

[0021] FIG. 7 shows optical microscopic photographs (Scale bars; 1.0 mm) showing undecalcified tissue sections of tibia seven and 28 days after implantation, in a test of implantation of a titanium alloy screw (A) to (D), a pure titanium screw (E) to (H), and the dental member of an embodiment of the present invention (I) to (L); that is, an orthodontic anchor screw made of an amorphous alloy having a composition of Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8, into rat tibia.

[0022] FIG. 8 shows graphs (a) BIC seven days after implantation and (b) BIC 28 days after implantation of each screw found on the basis of optical microscopic photographs shown in FIG. 7.

[0023] FIG. 9 shows graphs (a) BA seven days after implantation and (b) BA 28 days after implantation of each screw found on the basis of the optical microscopic photographs shown in FIG. 7.

[0024] FIG. 10 shows optical microscopic photographs (Scale bars; 1.0 mm) showing undecalcified tissue sections of tibia seven days after implantation, in a test of implantation of (a) a pure titanium screw, as well as the dental members of embodiments of the present invention, orthodontic anchor screws made of amorphous alloys having compositions of (b) Zr.sub.68Ni.sub.12Cu.sub.12Al.sub.8 and (c) Zr.sub.72Ni.sub.16Cu.sub.6Al.sub.6, into rat tibia.

[0025] FIG. 11 shows graphs (vertical axis; dissolution amount [ppt]) showing the results of testing the dissolution of each metal component of Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8 (Zr70), Zr.sub.68Ni.sub.12Cu.sub.12Al.sub.8 (Zr68) and Zr.sub.72Ni.sub.16Cu.sub.6Al.sub.6 (Zr72) amorphous alloys composing the dental members of embodiments of the present invention, orthodontic anchor screws and pure titanium (pure Ti) composing a pure titanium screw.

[0026] FIG. 12 shows scanning electron microscope (SEM) photographs showing the dental member of an embodiment of the present invention, (a) an orthodontic anchor screw made of an amorphous alloy having a composition of Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8, and (b) an orthodontic anchor screw made of a surface-treated Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8 amorphous alloy having the surface coated with zirconia ceramics, which were used in an experiment.

[0027] FIG. 13 is a graph showing changes over time in mobility after implantation (Periotest value) in a test of implantation of the dental member of an embodiment of the present invention, an orthodontic anchor screw made of an amorphous alloy having a composition of Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8, and, an orthodontic anchor screw made of a surface-treated Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8 amorphous alloy having the surface coated with zirconia ceramics, into rat tibia.

[0028] FIG. 14 shows confocal microscope photographs showing the results of observing the surfaces of (a) a pure titanium foil, (b) a Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8 amorphous alloy foil used for the dental member of an embodiment of the present invention, and (c) a surface-treated Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8 amorphous alloy foil after one day of culture in a cell adhesion test.

[0029] FIG. 15 shows (a) a front view, a side view, a bottom view, and a plan view of an example of the screw shape, and (b) a front view and a side view of an example of the button shape, which are the dental members of embodiments of the present invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS OF THE INVENTION

[0030] The embodiments of the present invention will be described in detail as follows with reference to the drawings.

[0031] The dental member of an embodiment of the present invention comprises an amorphous alloy having a composition represented by formula: Zr.sub.aNi.sub.bCu.sub.cAl.sub.d [wherein a, b, c, and d denote at. %, a ranges from 60 to 75 at. %, b ranges from 11 to 30 at. %, c ranges from 1 to 16 at. %, and d ranges from 4 to 20 at. %].

[0032] This amorphous alloy can be produced by metal mold casting, for example. Specifically, first, raw materials including zirconium (Zr), nickel (Ni), copper (Cu), and aluminium (Al) are weighed and mixed to result in a desired composition, and then the mixture is melted and mixed in an inert gas atmosphere to generate a mother alloy. Next, the mother alloy is melted again in air, and then casting is performed with a copper template by an arc-melting tilt-casting method or the like, so that the amorphous alloy can be produced. The shaped raw material of the thus produced amorphous alloy is subjected to machining, and then the dental member of an embodiment of the present invention can be produced.

[0033] The dental member of an embodiment of the present invention is made of an amorphous alloy with higher strength and lower elasticity compared with titanium dental members such as titanium alloy dental members and pure titanium dental members, so that the dental member is hard to be broken or fractured in use and has a low risk of damaging adjacent tooth roots. Moreover, the dental member of an embodiment of the present invention accelerates the formation of new bone around the member after implantation unlike titanium dental members. Hence, the dental member of the present invention is excellent in stability of engraftment to bone after implantation, and has a low risk of becoming unstable or falling off during orthodontic treatment.

[0034] In addition, an amorphous alloy shaped in a desired shape is heated in air at 350 C. to 400 C. to oxidize the surface, and thus a dental member having the surface coated with zirconia ceramics can be produced. In this case, the surface of an amorphous alloy is covered with very strong zirconia ceramics, so that the strength can be increased.

[0035] Experiments shown below were conducted to verify the effect of the dental member of an embodiment of the present invention.

EXAMPLES

[Experimental Outline]

[0036] As the dental members of embodiments of the present invention, an orthodontic anchor screw made of an amorphous alloy having a composition of Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8 (hereinafter, referred to as screw 1 of the present invention), an orthodontic anchor screw made of an amorphous alloy having a composition of Zr.sub.68Ni.sub.12Cu.sub.12Al.sub.8 (hereinafter, referred to as screw 2 of the present invention), and an orthodontic anchor screw made of an amorphous alloy having a composition of Zr.sub.72Ni.sub.16Cu.sub.6Al.sub.6 (hereinafter referred to as screw 3 of the present invention) were produced and subjected to an experiment using rats. Screws 1 to 3 of the present invention used in this experiment are shown in FIG. 1(b) to (d), respectively. In addition, the surfaces of screws 1 to 3 of the present invention were not coated with zirconia ceramics.

[0037] As shown in FIG. 1(b) to (d), each of the produced orthodontic anchor screws had a diameter (outer diameter) of 1.3 mm, a length of 3.0 mm, and a pitch of 0.8 mm. In addition, as comparative samples, a pure titanium screw (99.4% titanium, pitch: 0.8 mm), and a titanium alloy screw (pitch: 0.5 mm), which had the same shape as the other screws, were produced and subjected to the same experiment. The pure titanium screw used in this experiment is shown in FIG. 1(a). The titanium alloy screw used herein was AbsoAnchor (Dentos) that is widely used today in clinical settings.

[0038] Rats used in this experiment were 12-week-old male Wistar rats (body weight: 250 g to 260 g). To reduce the burden on animals due to the experiment, the procedure was performed by intraperitoneal injection of 5 mg/ml pentobarbital under general anesthesia.

[0039] Moreover, in an experiment for measuring values, the thus obtained experimental data were statistically processed by performing one-way analysis of variance, and then performing a multiple comparison test by Tukey-Kramer method. In this test, a significant difference was determined with the significance level of 1% (P<0.01) or 5% (P<0.05), a result with a significance level of less than 1% is denoted as * and a result with a significance level of less than 5% is denoted as * in each drawing.

[Implantation of Screws and Application of Immediate Loading]

[0040] Medial surfaces of both lower extremities of each of a plurality of rats were shaved, skin and fascia incisions, each having an about 15.0 mm long, were made in parallel to the long axis of rat tibia, and then the medial surfaces of the tibiae were exposed with raspatories. When immediate loading was applied, drilling was performed at two positions per a side (a position in the vicinity of and a position in the central part of the joint at the boundary with the femur) at a low rotational speed using a round bar, so as to form a 1.0-mm fossa for implantation of a screw. When no immediate loading was applied, drilling was performed at one position per side (in the vicinity of the joint at the boundary with the femur), so as to form a 1.0-mm fossa for implantation of a screw.

[0041] When immediate loading was applied, a screw was implanted with an anchor driver, vertically with respect to the cortical bone at an implantation part. Skin and fascial incisions were sutured using nonabsorbable sutures (Keisei Medical Industrial Co., Ltd. SU-1160NS). The surgical fields were sterilized with iodine cotton balls, and then 10 g or 50 g of immediate loading was applied by screw types to each screw using coil springs (TOMY INTERNATIONAL INC. SENTALLOY coil springs) made of an orthodontic nickel titanium alloy.

[0042] Loading was applied immediately after implantation of each screw. After implantation of each screw, loading was kept applied for seven and 28 days of evaluation. In addition, screws to be evaluated were screws implanted in the vicinity of the joint at the boundary with the femur, from among screws implanted in tibiae. Screws implanted in the central parts of tibiae were used as anchorage sources when immediate loading was applied. As the screws for anchorage sources, AbsoAnchor processed to have a length of 3.0 mm was used consistently.

[0043] Moreover, when no immediate loading was applied, each screw was implanted with an anchor driver vertically with respect to cortical bone at an implantation part, skin and fascial incisions were sutured with nonabsorbable sutures (Keisei Medical Industrial Co., Ltd. SU-1160NS), and then the surgical fields were sterilized with iodine cotton balls. After implantation of each screw, it was retained for seven or 28 days of evaluation.

[Implantation of Screws and Measurement of Removal Torque Values]

[0044] Screw 1 of the present invention, a titanium alloy screw, and a pure titanium screw were measured for implantation torque values and removal torque values immediately after, seven days after implantation, and 28 days after implantation, respectively, of each screw using a torque gauge (Tohnichi). Implantation torque values were measured by screw types of four screws implanted in the joints. Furthermore, removal torque values were measured by screw types of four screws immediately after implantation. Removal torque values were also measured by screw types of four screws and by weights of immediate loading seven and 28 days after implantation. The highest torque value among torque values of each screw type was employed as a measured torque value. The results of measuring implantation torque values and removal torque values immediately after implantation are shown in FIG. 2(a) and (b), respectively. Moreover, the results of measuring removal torque values seven days after implantation and removal torque values 28 days after implantation are shown in FIGS. 3(a) and (b), respectively.

[0045] As shown in FIG. 2(a), the implantation torque of screw 1 of the present invention was 0.7N cm, that of the titanium alloy screw was 1.5N cm, and that of the pure titanium screw was 0.65N cm. It was thus confirmed that the implantation torque value of the titanium alloy screw was significantly higher than those of the other two screw types. Furthermore, as shown in FIG. 2(b), the removal torque immediately after implantation of screw 1 of the present invention was 0.51N cm, that of the titanium alloy screw was 1.35N cm, and that of the pure titanium screw was 0.49N cm. It was thus confirmed that the removal torque immediately after implantation of the titanium alloy screw was significantly higher than those of the other two screw types, exhibiting the same tendency as in the case of implantation torques. This may be because the pitch width (0.5 mm) of the titanium alloy screw was shorter than the pitch width (0.8 mm) of the other two screw types.

[0046] Furthermore, as shown in FIG. 2, it was confirmed for all screws that the removal torque value immediately after implantation was lower than the implantation torque value. This may be because the bone wall of a fossa for implantation was damaged at the time of implantation of each screw, so that the contact area between the screw and bone was decreased from that at the time of implantation.

[0047] As shown in FIG. 3, it was confirmed for all screws that the removal torque value 28 days after implantation was significantly higher than the same seven days after implantation. This may be because new bone was formed around each screw as time proceeded after implantation. In addition, it was also confirmed for all screws that the removal torque seven days after implantation and the same 28 days after implantation were found to be highest when 10 g of immediate loading was applied.

[0048] As shown in FIG. 3, the removal torque seven days after implantation and the same 28 days after implantation of screw 1 of the present invention were confirmed to be significantly higher than the other two screw types in all immediate loading groups. This may be because more new bone sites were formed around screw 1 of the present invention than those formed around the other two screw types. As shown in FIG. 2 and FIG. 3, the removal torque value of the screw 1 of the present invention increased from the torque immediately after implantation more significantly than those of the other two screw types, suggesting that more new bone sites were quickly formed than those formed around the other two screw types. Accordingly, it was considered that screw 1 of the present invention after implantation became stable more quickly than the other two screw types, maintaining good stability.

[0049] Next, screw 2 and screw 3 of the present invention were similarly measured for implantation torque values and removal torque values seven days after implantation. In addition, for comparison, a titanium alloy screw and a pure titanium screw were also measured. The results of measuring implantation torque values and removal torque values seven days after implantation are shown in FIGS. 4(a) and (b), respectively.

[0050] As shown in FIG. 4(a), it was confirmed for all screws that implantation torque values were almost the same. Moreover, as shown in FIG. 4(b), the removal torque values seven days after implantation were confirmed to be lower than the implantation torque values, except for screw 3 of the present invention subjected to 10 g of immediate loading. This may be because even seven days after implantation, the bone wall of a fossa for implantation, which had been damaged at the time of implantation of a screw, remained affected.

[0051] Moreover, as shown in FIG. 4(b), the removal torque value seven days after implantation of screw 3 of the present invention subjected to 10 g of immediate loading was higher than those of the other screws, and was particularly confirmed to be significantly higher than that of the pure titanium screw subjected to 10 g of immediate loading. This may be because more new bone sites were formed around screw 3 of the present invention subjected to 10 g of immediate loading, than those formed around the other screws.

[Measurement of Screw Mobility]

[0052] For measurement of the stability of the screws after implantation, Screw 1 of the present invention, a titanium alloy screw, and a pure titanium screw were measured for the mobility of the screws implanted into tibiae immediately after implantation, seven days after implantation, and 28 days after implantation using a mobility measuring device, Periotest (Gulden Messtechnik). Measurement was performed by applying Periotest vertically with respect to each screw head portion at 3 sites (one site in the longitudinal direction of tibiae, two sites resulting from 120 rotation from the first site), the mean value of these 3 values was designated as a measurement value (Periotest value). In addition, it is defined that no mobility is confirmed when the Periotest value is between 0 and 9, mobility is sensed by palpation when the Periotest value is between 10 and 19, mobility is visually confirmed when the Periotest value is between 20 and 29, and teeth are moved by tongue and lip when the Periotest value is between 30 and 50. In the case of dental implants such as screws, the value of 10 or higher indicates insufficient osseointegration.

[0053] The results of measuring Periotest values are separately shown in FIG. 5(a) to (c) by weights of immediate loading. As shown in FIG. 5, immediately after implantation, the Periotest value of the titanium alloy screw was confirmed to be significantly lower than those of the other two screw types. This may be because the pitch width (0.5 mm) of the titanium alloy screw was shorter than the pitch width (0.8 mm) of the other two screw types.

[0054] Moreover, in all immediate loading groups, it was confirmed for all screws that Periotest values decreased from those immediately after implantation to seven and 28 days after implantation. This may be because new bone was formed around the screws and gradually became stable as time proceeded after implantation. In addition, it was confirmed for all screws that Periotest values seven and 28 days after implantation were lower in the case of 10 g of immediate loading than the other cases.

[0055] As shown in FIG. 5, in all immediate loading groups, a decrease in Periotest value immediately after implantation of screw 1 of the present invention was confirmed to be more significant compared with the other two screw types. It was also confirmed that screw 1 of the present invention exhibited the lowest value of 10 or less 28 days after implantation in all immediate loading groups. This may be because more new bone sites were more quickly formed around screw 1 of the present invention compared with the other two screw types. Accordingly, it is considered that screw 1 of the present invention after implantation became stable more quickly than the other two screw types, maintaining good stability.

[0056] Next, screw 2 and screw 3 of the present invention were also similarly measured for mobility immediately after implantation and seven days after implantation. In addition, for comparison, a titanium alloy screw and a pure titanium screw were also measured. The results of measuring Periotest values are separately shown in FIG. 6(a) and (b) by weights of immediate loading. As shown in FIG. 6, immediately after implantation, all screws exhibited similar Periotest values; and seven days after implantation, all screws were confirmed to exhibit decreased Periotest values.

[0057] Moreover, as shown in FIG. 6(a), in cases of no immediate loading, Periotest values of screw 2 and screw 3 of the present invention significantly decreased to about 10, seven days after implantation, confirming significant differences when compared with those of the titanium alloy screw and the pure titanium screw. This may be because more new bone sites were quickly formed around screw 2 and screw 3 of the present invention than those formed around the other two screw types.

[0058] Moreover, as shown in FIG. 6(b), in cases of 10 g of immediate loading, the Periotest value of screw 3 of the present invention significantly decreased to about 10, seven days after implantation, confirming significant differences compared with the other three screw types. This may be because more new bone sites were quickly formed around screw 3 of the present invention than those formed around the other 3 screw types. In addition, screw 2 of the present invention exhibited a significant decrease in Periotest value seven days after implantation compared with the titanium alloy screw, but exhibited a Periotest value similar to that of the pure titanium screw.

[0059] Moreover, screw 2 and screw 3 of the present invention in the case of no immediate loading were also measured for mobility 28 days after implantation. The results are shown in FIG. 6(c). As shown in FIG. 6(c), screw 2 and screw 3 of the present invention quickly exhibited Periotest values equivalent to those 28 days after implantation, confirming that screw 2 and screw 3 became stable more quickly than screw 1 of the present invention shown in FIG. 5(a).

[Histological Analysis]

[0060] Screw 1 of the present invention, a titanium alloy screw, and a pure titanium screw were histologically observed by screw type and by weights of immediate loading in order to evaluate the stability of the screws after implantation. Specifically, tissues surrounding the screws were observed seven and 28 days after implantation of the screws. In addition, regarding immediate loading, cases of no immediate loading and 50 g of immediate loading were observed. For observation, first, rats into which screws had been implanted were each subjected to perfusion fixation using a 4% paraformaldehyde solution. Both tibiae of lower extremities were excised, and then bone blocks each containing one screw were prepared. The bone blocks were fixed at 4 C. in a 4% paraformaldehyde solution for 48 hours, and then washed for 30 minutes with running water. After washing, the bone blocks were dehydrated and delipidated with an ethanol rise system under ordinary temperature, followed by treatment with an intermediate agent, xylene. After treatment, resin filtration was performed in a resin permeate (Wako, Osteoresin Embedding Kit) at 4 C., and then resin embedding was performed at 35 C. Resin blocks were processed with Saw Microtome Leica SP1600 (Leica Microsystems) into 100-m-thick resin sections, in parallel to the longitudinal direction of each screw. These sections were stained with Villanueva bone stain reagent (Polysciences, Villanueva Osteochrome Bone Stain).

[0061] Stained sections were observed under an optical microscope, so as to find the ratio of the periphery of each screw to new bone (BIC; Bone-to-Implant Contact). Furthermore, the area ranging from the periphery of each screw to 240 m (equals to the height of a screw blade) from the periphery was designated as an evaluation site for analysis (ROI; Region of Interest), and then the percentage of the area of new bone formed in ROI (BA; Bone Area) was found. BIC and BA were analyzed using ImageJ (National Institutes of Health).

[0062] In addition, BIC and BA are specifically found by the following formulae.

[0063] BIC (%)=[new bone mass (m) in contact with screw surface/Peripheral length of screw portion implanted (m)]100

[0064] BA (%)=[new bone area (m.sup.2) in ROI/ROI area (m.sup.2)]100

[0065] Moreover, when the periphery of a screw tip portion was included in an analysis range, the range includes the existing cortical bone region more than necessary, and thus the resulting analytical value is inappropriate to represent new bone mass. Hence, the periphery of a screw tip portion was excluded from the analysis range.

[0066] Optical microscopic photographs of stained sections seven and 28 days after implantation of each screw are shown in FIG. 7. Moreover, BIC and BA found on the basis of optical microscopic photographs shown in FIG. 7 are shown in FIG. 8 and FIG. 9, respectively. In addition, the images of tissue sections seven days after implantation in FIGS. 7(A), (B), (E), (F), (I), and (J) indicate osseointegration of cortical bone portions (subjected to implantation) with screws. It is thus considered that the repair of the existing cortical bone damaged by implantation of the screws was almost completed seven days after implantation.

[0067] As shown in FIG. 7(A) to (D), in the case of the titanium alloy screw, no clear new bone formation was observed seven days after implantation regardless of the presence or the absence of immediate loading, however, more sites of new bone formation were observed on the surfaces of screw blades subjected to 50 g of immediate loading 28 days after implantation (see white triangle arrows in FIG. 7, the same applies to the following). Moreover, as shown in FIG. 7(E) to (H), in the case of the pure titanium screw, significant new bone formation was not observed both seven and 28 days after implantation regardless of the presence or the absence of immediate loading. Moreover, as shown in FIG. 7(I) to (L), in the case of screw 1 of the present invention, more sites of new bone formation were observed on screw blades seven days after implantation, and particularly more sites of new bone formation were confirmed in the case of 50 g of immediate loading. Twenty eight days after implantation, sites of new bone formation were observed on the surfaces of screw blades, and more sites of new bone formation could be significantly confirmed in the case of particularly 50 g of immediate loading.

[0068] As shown in FIG. 7, in the case of screw 1 of the present invention, more sites of new bone formation can be confirmed than those formed around the other two screw types regardless of the presence or the absence of immediate loading. This may be because screw 1 of the present invention was better than the other two screw types in biocompatibility. In particular, more sites of new bone formation were observed in tissue sections surrounding screw 1 of the present invention seven days after implantation (see FIGS. 7(I) and (J)) than those observed around the other 2 screw types. Hence, the amorphous alloy composition of screw 1 of the present invention can be said to be effective for new bone formation.

[0069] As shown in FIG. 8, the BIC of screw 1 of the present invention was significantly higher seven days after implantation than those of the other two screw types regardless of the presence or the absence of immediate loading. Moreover, 28 days after implantation, the BIC of screw 1 of the present invention was confirmed to be significantly higher than those of the other two screw types in the case of no immediate loading. Furthermore, as shown in FIG. 9, BA of screw 1 of the present invention was significantly higher seven days after implantation than those of the other two screw types in the case of no immediate loading. BA of screw 1 of the present invention subjected to 50 g of immediate loading was confirmed to be significantly higher than that of the pure titanium screw. Twenty eight days after implantation, BA of screw 1 of the present invention was confirmed to be significantly higher than those of the other two screw types regardless of the presence or the absence of immediate loading. These results revealed that after implantation, more sites of new bone were formed on the surface of screw 1 of the present invention than those formed on the other two screw types, and the new bone mass increased as days proceeded. Accordingly, it can be said that screw 1 of the present invention after implantation becomes stable more quickly than the other two screw types, maintaining good stability.

[0070] For evaluation of the stability of screw 2 and screw 3 of the present invention and a pure titanium screw after implantation, tissues surrounding the screws were observed seven days after implantation of screws by screw type (without immediate loading). A staining method employed for observation was the same method as in FIG. 7. Optical microscopic photographs of stained sections for each screw seven days after implantation are shown in FIG. 10.

[0071] As shown in FIG. 10(a) to (c), in the cases of screw 2 and screw 3 of the present invention, more sites of new bone formation were observed seven days after implantation than those formed around the pure titanium screw. This may be because screw 2 and screw 3 of the present invention are better than the pure titanium screw in biocompatibility. It can be said that the amorphous alloy compositions of screw 2 and screw 3 of the present invention are compositions effective for new bone formation. Furthermore, it can be said that screw 2 and screw 3 of the present invention after implantation become stable more quickly than the pure titanium screw, maintaining good stability.

[Dissolution Test]

[0072] Amorphous alloys and pure titanium composing screws 1-3 of the present invention and a pure titanium screw, respectively, were tested for dissolution of components. In this test, first, 5.0 ml of a simulated body fluid (pH7.4) was added to a 15 ml of plastic tube, and then a metallic foil having the surface area of 384 mm.sup.2 and formed of each metal was immersed in the fluid. These tubes were placed in a thermostatic bath and then maintained at 37 C. for seven days. Subsequently, the amount of each metal ion of Al, V, Ti, Ni, Cu, and Zr dissolved in simulated body fluids was measured by ICP-MS (Inductively Coupled Plasma Mass Spectrometer). In addition, as control, the amount of each metal ion was measured even in cases where no metallic foil was added.

[0073] Measurement results are shown in FIG. 11. As shown in FIG. 11, dissolved Ti levels were confirmed to be lower, but dissolved Cu and Zr levels were confirmed to be higher in the cases of amorphous alloys (Zr70, Zr68, and Zr72 in FIG. 11) composing screws 1-3 of the present invention than in the case of pure titanium (pure Ti in FIG. 11) composing the pure titanium screw. They are natural results in view of each metal component. Moreover, the dissolved Ni level, a major cause of metal allergy, of the amorphous alloy composing each of screws 1-3 of the present invention, was low and almost the same as that of pure titanium composing the pure titanium screw, and no significant difference was observed. Accordingly, screws 1-3 of the present invention are considered to have no problem concerning allergies, similarly to pure titanium screws.

[Measurement of Screw Mobility Using Surface-Treated Material]

[0074] An orthodontic anchor screw (screw 1 of the present invention) made of an amorphous alloy having a composition of Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8 was heated at 350 C. for one hour, so as to produce an orthodontic anchor screw made of surface-treated Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8 amorphous alloy (hereinafter, referred to as surface-treated screw), wherein the surface was coated with zirconia ceramics. The thus produced screw was tested for screw mobility using rats. For comparison, screw 1 of the present invention was subjected to the same test. Screw 1 of the present invention and the surface-treated screw used for the test are shown in FIGS. 12(a) and (b), respectively.

[0075] The method for testing screw mobility employed herein was the same method as in FIG. 5 and FIG. 6. No immediate loading was performed. The results of measuring Periotest values are shown in FIG. 13. As shown in FIG. 13, seven days after implantation, the surface-treated screw exhibited the Periotest value significantly lower than that of screw 1 of the present invention. It can be said that the surface-treated screw had high stability. Furthermore, 28 days after implantation, the surface-treated screw and screw 1 of the present invention both exhibited decreases in Periotest value, indicating improved stability. However, there was no significant difference between the two. Accordingly, a Periotest value similar to that 28 days after implantation was obtained early in the case of the surface-treated screw, and it was thus confirmed that the surface-treated screw becomes stable more quickly than the screw 1 of the present invention.

[Cell Adhesion Test Using Surface-Treated Material]

[0076] A pure titanium foil (grade2; The Nilaco Corporation), a Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8 amorphous alloy foil, and a surface-treated Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8 amorphous alloy foil having the surface coated with zirconia ceramics (prepared by heating a metallic glass foil at 350 C. for one hour) were cut into a size of 66 mm. After sterilization, rat bone marrow cells were seeded, 210.sup.4 cells each, and then cultured. To examine the cell adhesion ability of cells after 1 day of culture, actin (green), vinculin (red), and nuclei (blue) were stained by immunofluorescence staining, and then observed under a confocal microscope. Observation results are shown in FIG. 14.

[0077] As shown in FIG. 14, cell adhesion to the surfaces and cell growth were confirmed for all of the pure titanium foil, the Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8 amorphous alloy foil, and the surface-treated Zr.sub.70Ni.sub.16Cu.sub.6Al.sub.8 amorphous alloy foil. Accordingly, it can be said that the amorphous alloy and the surface-treated amorphous alloy to be used for the dental members of embodiments of the present invention have biocompatibility equivalent to or better than that of pure titanium.

[0078] As revealed by the above experimental results, the dental members of embodiments of the present invention quickly exhibit new bone formation around an area subjected to implantation and are excellent in stability of engraftment to bone after implantation, compared with titanium alloy screws and pure titanium screws. Moreover, the dental members of embodiments of the present invention exhibit high removal torques, so that the dental members do not fall off inadvertently after implantation, and can compensate for decreases in mechanical friction due to the decreased surface areas after size reduction. Accordingly, the dental members of embodiments of the present invention can be reduced in size smaller than conventional titanium alloy dental members and pure titanium dental members. For example, an orthodontic anchor screw or a dental implant in a screw shape wherein the core diameter of the screw part is as thin as 0.9 mm as shown in FIG. 15(a), and the same in a button shape wherein the length of the screw part is as short as about 2.5 mm as shown in FIG. 15(b) can be produced.

[0079] As described above, the dental members of embodiments of the present invention can be reduced in size smaller than conventional products, so that the dental members can be designed as orthodontical implants that do not damage tooth roots upon implantation, are completely safe for living bodies, and do not fall off. Furthermore, the design of short dental members as shown in FIG. 15(b) are employed, so that the dental members can be safely implanted into every sites of alveolar bone and palatine bone. In addition, screw heads shown in FIG. 15 are intended for orthodontic ligature wires, elastic rubber, or coil springs to be tied therewith or for wires to be embedded therein. Screw heads are not limited to these screw heads designed as shown in FIG. 15 and may be in any form, as long as they can exhibit these functions.