CONFINED EPTAXIAL GROWTH FOR CONTINUED PITCH SCALING

Abstract

A technique relates to manufacturing a finFET device. A plurality of first and second semiconductor fins are formed on a substrate. Gate stacks are formed on the substrate, each including a gate, a hard mask and an oxide layer. A dielectric spacer layer is deposited. A sacrificial fill material is deposited on the finFET device and planarized. A second hard mask is deposited, a trench area is patterned in the hard mask parallel to the first and second semiconductor fins, and the sacrificial fill material is anisotropically etched to create a trench. A dielectric wall is formed in the trench and the second hard mask and sacrificial fill material are removed.

Claims

1. A CMOS transistor comprising: a first transistor comprising a plurality of first semiconductor fins patterned on a substrate, and a first transistor active area, a first epitaxial layer on the first transistor, a second transistor comprising a plurality of second semiconductor fins patterned on a substrate and a second transistor active area, a second epitaxial layer on the second transistor, at least two gate stacks arranged over channel regions of the first and second semiconductor fins, and a dielectric wall having four vertical surfaces positioned in between the first transistor active area and the second transistor active area and extending between two of the at least two gate stacks, wherein the dielectric wall contacts each of the at least two gate stacks with one of the vertical surfaces, wherein the first epitaxial layer is confined to the first transistor by the dielectric wall.

2. The CMOS transistor according to claim 1, wherein the dielectric wall is substantially perpendicular to the gate.

3. The CMOS transistor according to claim 1, wherein the first transistor is an nFET transistor and the second transistor is a pFET transistor.

4. The CMOS transistor according to claim 1, wherein the first epitaxial layer is adjacent to the dielectric wall of the first transistor.

5. The CMOS transistor according to claim 4, wherein the first epitaxial layer does not physically contact the second transistor.

6. The CMOS transistor according to claim 1, wherein the dielectric wall has a height that is greater than a height of the first transistor fins and a height of the second transistor fins.

7. The CMOS transistor according to claim 1, wherein the second epitaxial layer is confined to the second transistor.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0008] The subject matter which is regarded as the invention is particularly pointed out and distinctly claimed in the claims at the conclusion of the specification. The forgoing and other features, and advantages of the invention are apparent from the following detailed description taken in conjunction with the accompanying drawings in which:

[0009] FIG. 1A illustrates a top-down view of a conventional 14 nanometer FinFET transistor.

[0010] FIG. 1B illustrates a top-down view of a conventional transistor with a source-drain short from epitaxial overlap.

[0011] FIG. 1C illustrates a top-down view of a conventional transistor with epitaxial growth into an adjacent transistor.

[0012] FIG. 1D illustrates a conventional approach to avoiding source-drain shorts.

[0013] FIGS. 2A-I illustrate an exemplary method of making a FinFET device according to a first embodiment, in which:

[0014] FIG. 2A is a perspective view of a FinFET device after fins and gate stacks are patterned on a substrate according to an exemplary embodiment.

[0015] FIG. 2B is a perspective view of a FinFET device after depositing a dielectric spacer according to an exemplary embodiment.

[0016] FIG. 2C is a perspective view of a FinFET device after depositing a sacrificial fill material on the device according to an exemplary embodiment.

[0017] FIG. 2D is a perspective view of a FinFET device after depositing a hard mask according to an exemplary embodiment.

[0018] FIG. 2E is a perspective view of a FinFET device after patterning a trench area in the hard mask according to an exemplary embodiment.

[0019] FIG. 2F is a perspective view of a FinFET device after anisotropically etching the sacrificial fill material to create a trench according to an exemplary embodiment.

[0020] FIG. 2G is a perspective view of a FinFET device after forming a dielectric wall in the trench according to an exemplary embodiment.

[0021] FIG. 2H is a perspective view of a FinFET device after selectively removing the sacrificial fill material according to an exemplary embodiment.

[0022] FIG. 2I is a perspective view of a FinFET device after removing the dielectric spacer according to an exemplary embodiment.

[0023] FIG. 3 illustrates a top down view of a CMOS device according to an exemplary embodiment.

[0024] FIG. 4 is a flow diagram of a method for manufacturing a finFET device according to an exemplary embodiment.

DETAILED DESCRIPTION

[0025] Scaling of FinFET devices calls for consideration of epitaxial growth areas. As shown in FIG. 1A, conventional FinFET devices using epitaxial layers include an nFET area 100 containing an n-type fin (nFin) 102 and a pFET area 110 including p-type fin (pFin) 112. One or more epitaxial layers can be grown on a substrate in the transistor area. For example, as shown in FIG. 1A, an nFET epitaxial layer 108 can be grown in the nFET area 100 by an epitaxial growth process starting from the nFin 102. In some cases, a second epitaxial layer, for instance a pFET epitaxial layer 116, can be grown in an adjacent transistor area. Each transistor has an active area. For example, nFin 102 has active area 104 associated with an epitaxial current and gate resistance. The first and second transistor areas can be a source and a drain. Conventional device manufacture uses advanced channel materials and fin height scaling to achieve performance scaling. However, area and performance scaling drive fin pitch scaling. Conventional devices call for lateral spacing between transistors to avoid shorts and other issues. For example, an nFin and pFin can be positioned such that at least two fin spaces 106 and 114, commensurate in area with the size of the fins, separate the fins. Crystallographic proportionality between fin height and lateral epitaxial growth, where the lateral direction is shown in FIGS. 1A-C as the c-direction, can give rise to epitaxy to epitaxy source drain shorts. For example, as shown in FIG. 1B, nFET epitaxial layer 108 and pFET epitaxial layer 116 can overlap, resulting in a short. Moreover, in some cases, errors in placement of masks during patterning can result in epitaxial growth into undesired transistor areas. For example, as depicted in FIG. 1C, an unconfined nFET epitaxial layer 108 can grow into the pFET area 110. A conventional solution is illustrated in FIG. 1D. As shown, an nFET active area 120 is adjacent to a pFET active area 122. These active areas are separated by a two fin gap, which is a gap that includes an area proportional to the size of the nFIN 124 and an area proportional to the size of the pFIN 126. This conventional solution is incompatible with continued pitch scaling.

[0026] Accordingly, embodiments of the disclosure provide methods of making FinFET devices that can confine epitaxial growth. The methods of the disclosure include forming a dielectric wall separating adjacent transistor regions to confine subsequent epitaxial growth.

[0027] The following definitions and abbreviations are to be used for the interpretation of the claims and the specification. As used herein, the terms comprises, comprising, includes, including, has, having, contains or containing, or any other variation thereof, are intended to cover a non-exclusive inclusion. For example, a composition, a mixture, process, method, article, or apparatus that comprises a list of elements is not necessarily limited to only those elements but can include other elements not expressly listed or inherent to such composition, mixture, process, method, article, or apparatus.

[0028] As used herein, the articles a and an preceding an element or component are intended to be nonrestrictive regarding the number of instances (i.e. occurrences) of the element or component. Therefore, a or an should be read to include one or at least one, and the singular word form of the element or component also includes the plural unless the number is obviously meant to be singular.

[0029] As used herein, the terms invention or present invention are non-limiting terms and not intended to refer to any single aspect of the particular invention but encompass all possible aspects as described in the specification and the claims.

[0030] As used herein, the term about modifying the quantity of an ingredient, component, or reactant of the invention employed refers to variation in the numerical quantity that can occur, for example, through typical measuring and liquid handling procedures used for making concentrates or solutions. Furthermore, variation can occur from inadvertent error in measuring procedures, differences in the manufacture, source, or purity of the ingredients employed to make the compositions or carry out the methods, and the like. In one aspect, the term about means within 10% of the reported numerical value. In another aspect, the term about means within 5% of the reported numerical value. Yet, in another aspect, the term about means within 10, 9, 8, 7, 6, 5, 4, 3, 2, or 1% of the reported numerical value.

[0031] FIGS. 2A-I illustrate an exemplary method of making a FinFET device according to a first embodiment of the present disclosure.

[0032] In a first embodiment, as illustrated in FIG. 2A, a transistor is formed with a plurality of first transistor fins 200 and a plurality of second transistor fins 202 patterned on a substrate (not shown) by known methods, such as multiple patterning techniques. For example, the transistor fins 200 and 202 can be patterned by self aligned double patterning (SADP) or self aligned quadruple patterning (SAQP) with active silicon region (RX) and fin cut (FC) layer formation. In some embodiments, for example, the first transistor fins 200 are pFET fins and the second transistor fins 202 are nFET fins.

[0033] Multiple gate stacks 204 are patterned on the transistor, each gate stack having a gate 206, a first hard mask 208, and an oxide layer 210. The gate 206 can be a sacrificial gate containing, for example, polysilicon oxide, germanium or silicon germanium, and/or a nonmetal. In preferred embodiments, a first part of a double-patterning process for forming sacrificial gate structures is used. Double-patterning processes for forming sacrificial gate structures are known and include, for example, patterning a multilayer stack structure including a polysilicon layer and a hard mask on top of the polysilicon layer. A hard-mask open etch process can etch the pattern of the gate lines into the hard mask layer. In some embodiments, a cut lithography (CT) process, which could be the second patterning process of a conventional double patterning process, is not performed at this step. The first hard mask 208 can be a liner or spacer material with low wet etch resistance, such as a silicon nitride, silicon oxide, or mixtures thereof. In preferred embodiments, the first hard mask 208 comprises a composite silicon nitride/silicon oxide material. The first hard mask can be deposited by PVD deposition, for example.

[0034] A substrate can include any silicon containing substrate including, but not limited to Si, bulk Si, single crystal Si, crystalline Si, SiGe, amorphous Si, silicon-on-insulator substrates (SOI), SiGe-on-insulator (SGOI), strained-silicon-on-insulator, annealed poly Si, and poly Si line structures. A source and drain can be implanted in the substrate.

[0035] As used herein, depositing may include any now known or later developed techniques appropriate for the material to be deposited including but not limited to, for example: chemical vapor deposition (CVD), low-pressure CVD (LPCVD), plasma-enhanced CVD (PECVD), semi-atmosphere CVD (SACVD) and high density plasma CVD (HDPCVD), rapid thermal CVD (RTCVD), ultra-high vacuum CVD (UHVCVD), limited reaction processing CVD (LRPCVD), metal-organic CVD (MOCVD), sputtering deposition, ion beam deposition, electron beam deposition, laser assisted deposition, thermal oxidation, thermal nitridation, spin-on methods, physical vapor deposition (PVD), atomic layer deposition (ALD), chemical oxidation, molecular beam epitaxy (MBE), plating, evaporation.

[0036] Deposition is any process that grows, coats, or otherwise transfers a material onto the wafer. Available technologies include, but are not limited to, thermal oxidation, physical vapor deposition (PVD), chemical vapor deposition (CVD), electrochemical deposition (ECD), molecular beam epitaxy (MBE) and more recently, atomic layer deposition (ALD) among others.

[0037] Removal is any process that removes material from the wafer: examples include etch processes (either wet or dry), and chemical-mechanical planarization (CMP), etc.

[0038] Patterning is the shaping or altering of deposited materials, and is generally referred to as lithography. For example, in conventional lithography, the wafer is coated with a chemical called a photoresist; then, a machine called a stepper focuses, aligns, and moves a mask, exposing select portions of the wafer below to short wavelength light; the exposed regions are washed away by a developer solution. After etching or other processing, the remaining photoresist is removed. Patterning also includes electron-beam lithography, nanoimprint lithography, and reactive ion etching.

[0039] Next, in accordance with the first embodiment, as shown in FIG. 2B, an exemplary method includes depositing a spacer layer 220 on the finFET device. In some embodiments, the spacer layer 220 contains a low-k spacer material, such as a poly-open chemical mechanical polish (POC) liner. A low-k spacer is a spacer having a dielectric constant less than the dielectric constant of silicon nitride at room temperature. Examples of low-k materials include, but are not limited to, SiBCN, hydrogen silsesquioxane polymer (HSQ), methyl silsesquioxane polymer (MSQ), polyphenylene oligomer, methyl doped silica or SiOx(CH3)y or SiCxOyHy or SiOCH, organosilicate glass (SiCOH) and porous SiCOH, silicon oxide, boron nitride, silicon oxynitride and the like. The low-k material may be deposited by using any suitable techniques such as, e.g., chemical vapor deposition. Preferably, the spacer layer 220 has lower wet etch resistance than silicon nitride (SiN). In some embodiments the spacer layer 220 is a SiBCN layer.

[0040] Then, as illustrated in FIG. 2C, the exemplary method includes depositing a sacrificial fill material 230 on the finFET device. The sacrificial fill material 230 is selective against the liner 220 in hot ammonia. In some embodiments, the sacrificial fill material 230 is not a FCVD fill material. In preferred embodiments, the sacrificial fill material 230 is a polysilicon material or amorphous silicon. In some embodiments, a steam annealing process can be used. The sacrificial fill material 230 is then recessed to the level of the liner 220 on top of the gate stacks, for example by chemical mechanical planarization (CMP). Optionally, the exemplary method next includes depositing a SiO cap on the sacrificial fill material 230.

[0041] Next, as shown in FIG. 2D, a second hard mask 232 is deposited on the finFET device. In some embodiments, the second hard mask 232 comprises nitride. In some embodiments, the second hardmask is composed of silicon nitride (SiN). In some embodiments, the second hardmask has a thickness of 5 nm to 50 nm, such as from 5 nm to 40 nm, or from 10 nm to 40 nm.

[0042] Then, as illustrated in FIG. 2E, a trench area 240 is created in the nitride layer 232 and optional oxide cap. The trench area 240 can be generated, for example, by patterning with the use of one or more masks that are used to define the contours of the active areas, which include areas that are desired to have epitaxial source or drain. In some embodiments, the trench is parallel to the first transistor fins and/or the second transistor fins. In some embodiments, the trench is equidistant from the first transistor fins and second transistor fins.

[0043] Then, as illustrated in FIG. 2F, the sacrificial fill material 230 in the trench area 240 is removed by anisotropic etching to create a sacrificial fill trench 242, which is a void in the sacrificial fill material in the area directly beneath the trench area 240. The anisotropic etch is selective against surrounding dielectric materials.

[0044] Next, the exemplary method includes forming a dielectric or insulator, such as, for example, SiO.sub.2 (SiO.sub.x) wall in the trench, as illustrated in FIG. 2G. The SiO.sub.2 wall can be grown, for example, by conformal SiO.sub.2 deposition wherein the wall material grows from any of the walls surrounding the trench and is pinched off in the middle of the trench. Thereafter, the second hard mask can be removed from the device, for example by CMP or etching to the top of the oxide layer 210.

[0045] Then, as illustrated in FIG. 2H, ammonia can be deposited on the finFET device to selectively remove the sacrificial fill material. After removal of the sacrificial fill material, the first hard mask 220 remains on the device and lines the first and second transistor fins and the sides of the gate stacks 204. The silicon oxide wall 244 separates the lined first and second transistors (not shown) and is perpendicular to the gate stacks 204.

[0046] Then, as shown in FIG. 2I, the first hard mask can be removed from the device. For example, anisotropic etching can remove the first hard mask and expose the fins 200 and 202 for further processing. In some cases, the silicon oxide wall 244 can partially erode during etching.

[0047] In some embodiments, the method also includes growing one or more epitaxial layers on the transistor after formation of the silicon oxide wall 244. An epitaxial growth process may be performed to deposit a crystalline layer onto the crystalline substrate beneath. The epitaxial silicon, silicon germanium, and/or carbon doped silicon (Si:C) can be doped during deposition by adding a dopant or impurity to form a silicide. The epitaxial source/drain may be doped with an n-type dopant or a p-type dopant, which depends on the type of transistor. The epitaxial growth can be physically confined by the silicon oxide wall 244 such that it does not extend into the adjacent transistor. The silicon oxide wall 244 may partially erode during epitaxial growth processes. Thus, the silicon oxide wall 244 should, prior to epitaxial growth, be of a height in excess of the height required to confine the epitaxial layer, such as a height greater than the expected height of the epitaxial layer.

[0048] The disclosure also relates to a CMOS transistor. For example, with reference to FIG. 3, a CMOS transistor of the disclosure includes a plurality of gate stacks 130, a first transistor active area 132, and a second transistor active area 134. In some embodiments, the gate stacks 130 include sacrificial gates. The CMOS transistor includes a dielectric wall 136 positioned between the first transistor active area 132 and the second transistor active area 134. The transistor active areas can include transistor fins (not shown). In some embodiments, the dielectric wall is an SiO.sub.2 wall. In some embodiments, the dielectric wall 136 is perpendicular to the gates 130. The dielectric wall 136 can provide a physical barrier between the first and second transistor active areas 132, 134. In some embodiments, the dielectric wall 136 is higher than the transistor fins. In some embodiments, the first transistor active area 132 is a pFET active area and the second transistor active area is an nFET active area 134.

[0049] In some embodiments, a CMOS transistor comprises one or more epitaxial layers. The epitaxial layers can be confined by the dielectric wall.

[0050] FIG. 4 is a flow diagram of a method 400 for manufacturing a finFET device according to an exemplary embodiment. The method 400 includes, as shown at block 402, forming first and second semiconductor fins on a substrate. The method 400 also includes, as shown at block 404, forming gate stacks having gate, hard mask, and oxide layers. Next, as shown at block 406, the method 400 includes depositing a dielectric spacer and a sacrificial fill material on the device. Then, as shown at block 408, the device is planarized to the top of the gate stacks. The method 400 then includes, as shown at block 410, depositing a second hard mask. Then, a trench area is patterned in the second hard mask, as shown at block 412. Next, the method 400 includes anisotropically etching sacrificial fill material to create a trench. Then, as shown at block 416, the method 400 includes forming a dielectric wall in the trench. As shown at block 418, the method 400 next includes removing the second hard mask. As shown at block 420, the method 400 also includes selectively removing the sacrificial fill material.

[0051] The descriptions of the various embodiments of the present invention have been presented for purposes of illustration, but are not intended to be exhaustive or limited to the embodiments disclosed. Many modifications and variations will be apparent to those of ordinary skill in the art without departing from the scope and spirit of the described embodiments. The terminology used herein was chosen to best explain the principles of the embodiments, the practical application or technical improvement over technologies found in the marketplace, or to enable others of ordinary skill in the art to understand the embodiments disclosed herein.