Polysilsesquioxane-dendron liquid crystals and method for preparing the same

Abstract

Due to excellent processability of the POSS-dendron-structured liquid crystal compound according to the present invention, it is possible to coat and print on the compound and, also, to manufacture large size flexible devices. According to the present invention, it is possible to maximize the physical bond strength between liquid crystals and, thus, to form higher-order structures by controlling the physical bond strength. Since the POSS-dendron-structured liquid crystal compound of the present invention introduces non-functional groups to inorganic chemicals in contrast to the conventional liquid crystals, the compound disperses well into general types of solvents. In addition, the chemical and mechanical properties of the compound of the invention, such as increase of maximum allowable temperature, inhibition of oxidation, increase of surface hardness, etc., improves since polysilsesquioxane includes reactive or non-reactive organic compounds. When the POSS-dendron-structured liquid crystal compound of the invention is used as an additive for liquid crystal layers, it can enhance the orientation of liquid crystal molecules. Moreover, the POSS part of the added liquid crystal compound of the invention may move to the lower surface of the liquid crystal layer and, then, improves the orientation.

Claims

1. A liquid crystal compound of the formula 1 which has POSS-dendron structure: ##STR00005## where Ar is C.sub.6-C.sub.20 aryl, P is polysilsesquioxane, Ar and P are linked with oxygen or NCO group, R.sub.1 and R.sub.2 are independently C.sub.1-C.sub.30 hydrocarbon, M is mesogen of compound of the formula 6, and m is 1-3 ##STR00006## where A is O, COO, OCO or NHCO; B is S, O, N.sub.2 or (CH.sub.2).sub.n; and n is 1-20.

2. The liquid crystal compound of claim 1, wherein the polysilsesquioxane is a POSS-dendron-structured liquid crystal compound of formula 2:
[RSiO.sub.1.5].sub.n [formula 2] where R is selected from the group consisting of C.sub.1-C.sub.3 alkyl, C.sub.1-C.sub.3 alkenyl, C.sub.3-C.sub.10 cycloalkyl, C.sub.6-C.sub.15 aryl, hydrogen and hydroxyl; and n is an integer of 3-1,000.

3. The liquid crystal compound of claim 1, wherein R.sub.1 and R.sub.2 are independently C.sub.2-C.sub.30 linear or branched alkyl, or C.sub.2-C.sub.30 alkenyl.

4. The liquid crystal compound of claim 1, wherein R.sub.1 and R.sub.2 are independently C.sub.1-C.sub.30 alkylene, C.sub.1-C.sub.30 alkoxy, C.sub.1-C.sub.30 fluoroalkylene, C.sub.1-C.sub.30 ether, C.sub.1-C.sub.30 fluoroether, or OR.sub.3O, where R.sub.3 is C.sub.1-C.sub.30 alkylene or C.sub.1-C.sub.30 fluoroalkylene.

5. The liquid crystal compound of claim 1, wherein the compound of formula 1 is selected from the compounds of the following formula 5: ##STR00007## where P is polysilsesquioxane, R.sub.1 and R.sub.2 are independently C.sub.1-C.sub.20 hydrocarbon, M is mesogen, and m is 1-3.

6. The liquid crystal compound of claim 1, wherein the liquid crystal compound of the POSS-dendron structure has a chemical structure of formula 7 ##STR00008## ##STR00009## ##STR00010## ##STR00011## ##STR00012## ##STR00013## ##STR00014##

7. The liquid crystal compound of claim 1, wherein the liquid crystal compound of the POSS-dendron structure has a weight average molecular weight of 500-3,000 g/mol.

8. A method for preparing a liquid crystal compound of the following formula 9 which has POSS-dendron structure, comprising: (i) reacting alkyl chain (R.sub.1) with mesogen (M) in a weight ratio of 1:0.8-1.5; (ii) reacting the R.sub.1-M obtained in the step (i) with R.sub.2 in a weight ratio of 1:2-4; (iii) reacting the R.sub.1-M-R.sub.2 obtained in the step (ii) with benzoate in a certain weight ratio to form R.sub.1-M-R.sub.2Ar; and (iv) reacting the R.sub.1-M-R.sub.2Ar with polysilsesquioxane, ##STR00015## where M is mesogen of compound of the formula 6, ##STR00016## R.sub.1 is CF.sub.3(CF.sub.2)nCH.sub.2CH.sub.2OH, CH.sub.3(CH.sub.2).sub.nBr, CH.sub.3(CH.sub.2).sub.nOH, CH.sub.3(OCH.sub.2CH.sub.2).sub.nOH, CH.sub.3(OCH.sub.2CH.sub.2).sub.nBr, CF.sub.3(CF.sub.2).sub.nBr, CF.sub.3(CF.sub.2).sub.nI, CF.sub.3(CF.sub.2).sub.nCH.sub.2I, CF.sub.3(CF.sub.2).sub.nCH.sub.2OH, CF.sub.3(CF.sub.2).sub.nCH.sub.2CH.sub.2I or CH.sub.3(CH.sub.2).sub.nCl; R.sub.2 is Cl(CH.sub.2).sub.nCl, Br(CH.sub.2).sub.nBr, HO(CH.sub.2).sub.nOH, ClCH.sub.2(CH.sub.2OCH.sub.2).sub.nCH.sub.2Cl, Cl(CF.sub.2).sub.nCl, I(CF.sub.2).sub.nI, Br(CF.sub.2).sub.nBr, HOCH.sub.2(CH.sub.2OCH.sub.2).sub.nCH.sub.2OH, or HOCH.sub.2(CF.sub.2).sub.nCH.sub.2OH; Ar is benzene; and P is polysilsesquioxane.

9. The method of claim 8, wherein the R.sub.1-M-R.sub.2Ar is reacted with the polysilsesquioxane after introducing NCO to the end group of the polysilsesquioxane at the step (iv).

10. A method for forming a liquid crystal display device comprising: providing a liquid crystal material; adding a liquid crystal compound to the liquid crystal material; and using the liquid crystal material with the added liquid crystal compound to form a liquid crystal layer having an upper side and a lower side; wherein the liquid crystal compound improves alignment of liquid crystal molecules of the liquid crystal layer, or enhances orientation of the liquid crystal molecules by being located at either or both of the upper side or lower side of the liquid crystal layer; wherein the liquid crystal compound is of the formula 1 which has POSS-dendron structure: ##STR00017## where Ar is C.sub.6-C.sub.20 aryl, P is polysilsesquioxane, Ar and P are linked with oxygen or NCO group, R.sub.1 and R.sub.2 are independently C.sub.1-C.sub.30 hydrocarbon, M is mesogen of compound of the formula 6, and m is 1-3 ##STR00018## where A is O, COO, OCO or NHCO; B is S, O, N.sub.2 or (CH.sub.2).sub.n; and n is 1-20.

11. The method of claim 10, wherein the polysilsesquioxane is a POSS-dendron-structured liquid crystal compound of formula 2:
[RSiO.sub.1.5].sub.n [formula 2] where R is selected from the group consisting of C.sub.1-C.sub.3 alkyl, C.sub.1-C.sub.3 alkenyl, C.sub.3-C.sub.10 cycloalkyl, C.sub.6-C.sub.15 aryl, hydrogen and hydroxyl; and n is an integer of 3-1,000.

12. The method of claim 10, wherein R.sub.1 and R.sub.2 are independently C.sub.2-C.sub.30 linear or branched alkyl, or C.sub.2-C.sub.30 alkenyl.

13. The method of claim 10, wherein R.sub.1 and R.sub.2 are independently C.sub.1-C.sub.30 alkylene, C.sub.1-C.sub.30 alkoxy, C.sub.1-C.sub.30 fluoroalkylene, C.sub.1-C.sub.30 ether, C.sub.1-C.sub.30 fluoroether, or OR.sub.3O, where R.sub.3 is C.sub.1-C.sub.30 alkylene or C.sub.1-C.sub.30 fluoroalkylene.

14. The method of claim 10, wherein the compound of formula 1 is selected from the compounds of the following formula 5: ##STR00019## where P is polysilsesquioxane, R.sub.1 and R.sub.2 are independently C.sub.1-C.sub.20 hydrocarbon, M is mesogen, and m is 1-3.

15. The method of claim 10, wherein the liquid crystal compound of the POSS-dendron structure has a chemical structure of formula 7 ##STR00020## ##STR00021## ##STR00022## ##STR00023## ##STR00024## ##STR00025## ##STR00026##

16. The method of claim 10, wherein the liquid crystal compound of the POSS-dendron structure has a weight average molecular weight of 500-3,000 g/mol.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 shows chemical formula 3.

(2) FIG. 2 shows chemical formula 4.

(3) FIG. 3 shows chemical formula 5.

(4) FIG. 4 shows chemical formula 7.

(5) FIG. 5 shows reaction scheme 1.

(6) FIG. 6 shows table 3.

(7) FIGS. 7A-7B show table 4.

(8) FIG. 8 shows the synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid methyl ester.

(9) FIG. 9 shows the synthesis of tri(ethylene glycol) bis(p-toluenesulfonate).

(10) FIG. 10 shows the synthesis of 2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethyl p-toluenesulfonate.

(11) FIG. 11 shows the synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid methyl ester.

(12) FIG. 12 shows the synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl alcohol.

(13) FIG. 13 shows the Synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl bromide.

(14) FIG. 14 shows the synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl azide.

(15) FIG. 15 shows the synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid.

(16) FIG. 16 shows the synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]acyl chloride

(17) FIG. 17 shows the synthesis of 3,5-[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid methyl ester.

(18) FIG. 18 shows the synthesis of 3,5-[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl alcohol.

(19) FIG. 19 shows the synthesis of 4-[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid methyl ester.

(20) FIG. 20 shows the synthesis of 4-[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl alcohol.

(21) FIG. 21 shows the synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl methoxy-POSS.

(22) FIG. 22 shows the synthesis of 3,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl methoxy-POSS.

(23) FIG. 23 shows the synthesis of 4-[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl methoxy-POSS.

BEST MODE

(24) The present invention may be carried out by the descriptions below. It should be understood that the following descriptions describe preferable embodiments of the invention and not limit the scope of the invention.

(25) The invention relates to the POSS-dendron-structured liquid crystal compound of the following chemical formula 1,

(26) ##STR00002##
where Ar is C.sub.6-C.sub.20 arylene,
P is polysilsesquioxane,
R.sub.1 and R.sub.2 is independently C.sub.1-C.sub.30 hydrocarbon,
M is mesogen, and
m is 1-3.

(27) The polysilsesquioxane (POSS) may be indicated as the following chemical formula 2 (below) or 3 (see, FIG. 1):
[RSiO.sub.15].sub.n,[Chemical Formula 2]
where R is selected from the group consisting of C.sub.1-C.sub.3 alkyl, C.sub.1-C.sub.3 alkenyl, C.sub.3-C.sub.10 cycloalkyl, C.sub.6-C.sub.15 aryl, hydrogen and hydroxyl; and n is 3-1,000.

(28) The molecular weight of the polysilsesquioxane is 500-100,000 g/mol.

(29) Since the polysilsesquioxane exists as the chemical formula 1 having (Ar)[R.sub.2-M-R.sub.1].sub.m, the problem that it is difficult to disperse the POSS as a complex has be solved.

(30) According to the present invention, the compound of the chemical formula 1 may be formed by introducing NCO to the end group of the POSS, followed by reacting (Ar)[R.sub.2-M-R.sub.1].sub.m therewith, in order to bind (Ar)[R.sub.2-M-R.sub.1].sub.m to the POSS.

(31) In one embodiment of the present invention, the compound of the chemical formula 1 may be POSS-NHCOO(Ar)[R.sub.2-M-R.sub.1].sub.m by binding of OH of Ar with NCO at the end of the POSS.

(32) Although the compound of the chemical formula 1 contains POSS, the liquid crystal compound may disperse well at the level of molecule and, also, easily dissolve in organic solvents.

(33) In addition, due to introduction of a polysilsesquioxane derivative, the polymeric properties, such as working temperature, inhibition of oxidation, surface hardness, mechanical properties, etc., of the liquid crystal compound of the chemical formula 1 are enhanced, and the combustibility, heat evolution and viscosity of the compound is reduced.

(34) When the POSS-dendron-structured liquid crystal compound of the chemical formula 1 is used as an additive to the liquid crystal layer, the POSS moves to the lower surface of the liquid crystal layer and, then, enhances the orientation of the liquid crystal.

(35) Ar of the chemical formula 1 is C.sub.6-C.sub.20 arylene and may include benzene ring compounds, fused benzene ring compounds and hetero ring compounds. At least one carbon atom of the Ar in the chemical formula 1 may be substituted by N, S or O which has non-covalent electron pair(s). Examples of the Ar may include the compounds of the chemical formula 4 (see, FIG. 2).

(36) The chemical formula 1 may be indicated as the following chemical formula 5 (see, FIG. 3):

(37) where P is polysilsesquioxane, R.sub.1 and R.sub.2 are independently C.sub.1-C.sub.30 hydrocarbon, M is mesogen, and m is 1-3.

(38) R.sub.1 and R.sub.2 is independently C.sub.1-C.sub.30 hydrocarbon. At least one of R.sub.1 and R.sub.2 may be hydrophilic or hydrophobic. Preferably, any one of R.sub.1 and R.sub.2 is hydrophilic, the other is hydrophobic.

(39) R.sub.1 and R.sub.2 are interchangeable with each other in the chemical formula 1.

(40) R.sub.1 and R.sub.2 may be independently C.sub.2-C.sub.30 linear or branched alkyl, or C.sub.2-C.sub.30 alkenyl; or C.sub.2-C.sub.30 linear or branched alkyl, or C.sub.2-C.sub.30 alkenyl, of which at least one carbon atom is substituted by O, S, N or F.

(41) R.sub.1 and R.sub.2 are independently C.sub.1-C.sub.30 alkylene, C.sub.1-C.sub.30 alkoxy, C.sub.1-C.sub.30 fluoroalkylene, C.sub.1-C.sub.30 ether, C.sub.1-C.sub.30 fluoroether or OR.sub.3O, where R.sub.3 may be C.sub.1-C.sub.30 alkylene or C.sub.1-C.sub.30 fluoroalkylene.

(42) The mesogen may be indicated as the following chemical formula 6:

(43) ##STR00003##
where A is O, COO, OCO or NHCO; B is S, O, N.sub.2 or (CH.sub.2).sub.n; and n is 1-20.

(44) The mesogen itself has liquid crystallinity and excellent ability of self-assembly by - (interaction.

(45) Examples of the POSS-dendron-structured liquid crystal compound may be indicated as the following chemical formula 7 (see, FIG. 4).

(46) The weight average molecular weight of the POSS-dendron-structured liquid crystal compound may be 500-150,000 g/mol, preferably 500-3,000 g/mol.

(47) The POSS-dendron-structured liquid crystal compound can form a physical bond between liquid crystals. The liquid crystal compound has many non-covalent electron pairs. For example, since carbon atoms in a hydrocarbon chain or an aromatic ring compounds are substituted by N, O, F or S, hydrogen bonds, - interactions, hydrophilic-hydrophobic intermolecular forces can be strengthened and, thereby, physical bonds between liquid crystals may be maximized. The dendron-structured compound may form a supramolecular structure by inducing physical bonds between liquid crystals.

(48) Since the liquid crystal compound includes either of hydrophilic or hydrophobic hydrocarbon, or both of them, it has a wide range of selection for solvents and its processability is excellent. Furthermore, addition of the liquid crystal compound of the invention makes the interactions between the liquid crystal molecules increase, thereby allowing for a wider range of working temperature of the liquid crystal.

(49) According to other aspect of the invention, the invention relates to an LCD device comprising the dendron-structured liquid crystal compound. Preferably, the LCD device of the invention may be applied to vertical alignment modes.

(50) According to one embodiment of the invention, the liquid crystal display device of the invention may comprise a lower substrate with a pixel electrode and a common electrode which are arranged spacedly; a upper substrate arranged opposite to the lower substrate; a liquid crystal layer located between the upper substrate and the lower substrate, which is in an isotropic state without application of an electric field and in an anisotropic state with application of an electric field; and a polarizing plate crossing the upper substrate and the lower substrate.

(51) The upper substrate, the lower substrate, the polarizing plate, the liquid crystal, etc., which are employed in the present invention may be manufactured by the known methods, materials and techniques.

(52) For example, the lower substrate may be manufactured so as to comprise thin film transistors formed at each pixel on an insulating substrate and pixel electrodes connected to the transistors. In addition, the upper substrate plays a role in improvement of an image quality by forming black matrices out of opaque materials such as Cr, which substantially defines pixel-domains on an insulating plate, and is generally formed to overlap with the gates and/or data-lines of the lower substrate in order to reduce influence on an aperture ratio. The upper substrate comprises a color filter which is located below a black matrix and is corresponding to a pixel, and a common electrode formed on the color filter.

(53) The liquid crystal may be a material that is optically isotropic with application of an electric field and optically anisotropic with application of an electric field, or that is optically anisotropic without application of an electric field and optically isotropic with application of an electric field, such as materials exhibiting the Pockels effect or the Kerr effect.

(54) Examples of the liquid crystals which may be used for the present invention include 5CB (p-n-pentyl-p-cyanobiphenyl), JC-1041 (Chisso), etc., and ZLI-4572 (Merck), ISO-(60BA)2, CB-15, etc. may be used as a chiral dopant.

(55) The liquid crystal molecules of the LCD device of the invention aligns vertically. The liquid crystal may be used, of which dielectric anisotropy is negative when it is operated by using vertical electric field.

(56) The POSS-dendron-structured liquid crystal compound may be used as an additive to a liquid crystal layer to enhance the alignment of the liquid crystal molecules. The dendron-structured liquid crystal compound may be employed 0.1-30 wt % relative to the liquid crystal.

(57) When the dendron-structured liquid crystal compound is added to the liquid crystal layer, the POSS part of the liquid crystal may move to the lower surface of the liquid crystal layer and, then, enhance the orientation of the liquid crystal.

(58) Detailed embodiments of the present invention will be described below, but not limiting the scope of the invention.

(59) The chemical formula 8 shows examples of the POSS-dendron-structured liquid crystal compound which can be used for the invention.

(60) ##STR00004##

(61) One example of the method for preparing the POSS-dendron-structured liquid crystal compound of the chemical formula 8 will be described below. First, alkyl chain of R.sub.1 and mesogen of M are reacted by weight ratio of 1:1.2 at 110 C. together with a catalyst of K.sub.2CO.sub.3 and a catalyst activator KI. Oxide chain of R.sub.2 is mixed with tosyl group containing O by weight ratio of 1:2, together with a catalyst of trimethylamine and, then, reacted at room temperature. The reactants, R.sub.1-M and R.sub.2 are mixed by a weight ratio of 1:3 and reacted with addition of a catalyst of K.sub.2CO.sub.3 at 80 C. The thus obtained R.sub.1-M-R.sub.2 is mixed with benzoate containing three OH groups by a weight ratio of 1:5, followed by addition of a catalyst of K.sub.2CO.sub.3, and, after reaction at 80 C., R.sub.1-M-R.sub.2Ar is formed. Subsequently, R.sub.1-M-R.sub.2Ar and LiAH.sub.4 are mixed by weight ratio of 1:10 to convert the end of Ar to CH.sub.2OH. Lastly, the thus obtained R.sub.1-M-R.sub.2Ar and polysilsesquioxane (molecular weight 1,159.99 g/mol) are mixed by a weight ratio of 1.2:1 and, then, reacted at 65 C. with addition of dibutyltin dilaurate as a catalyst to form liquid crystals containing POSS. The above reactions are shown in the following reaction scheme 1 (see, FIG. 5).

(62) Examples of R.sub.1 of the chemical formula 8 are listed in Table 1.

(63) TABLE-US-00001 TABLE 1 CF.sub.3(CF.sub.2).sub.nCH.sub.2CH.sub.2OH CH.sub.3(CH.sub.2).sub.nBr CH.sub.3(CH.sub.2).sub.nOH CH.sub.3(OCH.sub.2CH.sub.2).sub.nOH Chemical Formula 9 Chemical Formula 10 Chemical Formula 11 Chemical Formula 12 CH.sub.3(OCH.sub.2CH.sub.2).sub.nBr CF.sub.3(CF.sub.2).sub.nBr CF.sub.3(CF.sub.2).sub.nI CF.sub.3(CF.sub.2).sub.nCH.sub.2I Chemical Formula 13 Chemical Formula 14 Chemical Formula 15 Chemical Formula 16 CF.sub.3(CF.sub.2).sub.nCH.sub.2OH CF.sub.3(CF.sub.2).sub.nCH.sub.2CH.sub.2I CH.sub.3(CH.sub.2).sub.nCl Chemical Formula 17 Chemical Formula 18 Chemical Formula 19 n is 1-20 in the chemical formulas 9-19.
n is 1-20 in the chemical formulas 9-19.

(64) The OHs of the chemical formulas 9, 11, 12 and 17 can be substituted by tosylate.

(65) R.sub.2 of the chemical formula 8 can be selected from the groups listed in Table 2.

(66) TABLE-US-00002 TABLE 2 Cl(CH.sub.2).sub.nCl Br(CH.sub.2).sub.nBr HO(CH.sub.2).sub.nOH ClCH.sub.2(CH.sub.2OCH.sub.2).sub.nCH.sub.2Cl Chemical Formula 20 Chemical Formula 21 Chemical Formula 22 Chemical Formula 23 Cl(CF.sub.2).sub.nCl I(CF.sub.2).sub.nI Br(CF.sub.2).sub.nBr HOCH.sub.2(CH.sub.2OCH.sub.2).sub.nCH.sub.2OH Chemical Formula 24 Chemical Formula 25 Chemical Formula 26 Chemical Formula 27 HOCH.sub.2(CF.sub.2).sub.nCH.sub.2OH Chemical Formula 28 n is 1-12 in the chemical formulas 20-28.

(67) Either or both of OH of the chemical formulas 22, 27 and 28 can be substituted by tosylate.

(68) M can be selected from the groups listed in Table 3 (see, FIG. 6).

(69) R.sub.1 and R.sub.2 of the chemical formulas 29-40 may bind to M at m- or p-site.

(70) 1-8 nitrogen atoms may be present at the m- or p-site.

(71) In addition, C1-C8 alkyl, instead of hydrogen, may be present at at the m- or p-site.

(72) Detailed embodiments of the derivatives of the chemical formula 8 of the invention is listed in Table 4 (see, FIG. 7), but not limited thereto.

(73) n of Table 4 may be determined by reference to the above-mentioned description.

Example 1

(74) Synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid methyl ester 1-bromooctane (11.7 g, 6058 mmol) and 4,4-biphenol (13.54 g, 72.70 mmol) were added to purified N,N-dimethylformamide (DMF, 80 mL) in a 250 mL 1 neck round flask. Then, potassium carbonate (8.37 g, 60.58 mmol) and potassium iodine (1.01 g, 6.06 mmol) were added, followed by reflux at 110 C. for 12 hr. After reaction, the reaction products and 1,000 mL of water were poured to a 2,000 mL beaker and agitated, followed by filtration. Thereafter, the residue was dissolved by ethyl acetate and, then, filtered. The filtered solvent was evaporated. The thus obtained product was recrystallized by using 150 mL of ethanol. Finally, the product was obtained by filtration. (yield=7.86 g, 43%)

(75) .sup.1H NMR (400 MHz, CDCl.sub.3): 7.45-7.41 (t, 4H), 6.95-6.88 (dd, 4H), 4.72 (s, 1H), 4.00-3.96 (t, 2H), 1.83-1.76 (m, 2H), 1.50-1.25 (m, 10H), 0.90-0.87 (t, 3H). (See, FIG. 8).

Synthesis of tri(ethylene glycol) bis(p-toluenesulfonate)

(76) p-toluenesulfonyl chloride (40.63 g, 213.09 mmol) was dissolved in methylene chloride (MC, 150 mL) in a 500 mL 1 neck round flask and, then, triethyleneglycol (16 g, 105.55 mmol) and triethylamine (29.72 mL, 213.09 mmol) were added. The reacting mixture was stirred at room temperature for 8 hr. After reaction, 200 mL of distilled water was added and extraction was carried out by using 600 mL of chloroform (CHCl.sub.3). After removing the solvents, products were separated by column chromatography (silica, hexane/ethyl acetate=1:1 (v/v)). (yield=42.59 g, 87%)

(77) .sup.1H NMR (400 MHz, CDCl.sub.3): 7.80-7.78 (d, 4H), 7.35-7.33 (d, 4H), 4.15-4.12 (t, 4H), 3.66-3.64 (t, 4H), 3.52 (s, 4H), 2.44 (s, 6H). (See, FIG. 9).

Synthesis of 2-(2-{2[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethyl p-toluenesulfonate

(78) 4-(4-octyloxy)-hydroxybiphenyl (4.88 g, 16.35 mmol) and tri(ethylene glycol) bis(p-toluenesulfonate) (22.50 g, 49.06 mmol) were dissolved in purified N,N-dimethylformamide (DMF, 150 mL) in a 500 mL 1 neck round flask and, then, potassium carbonate (9.04 g, 65.41 mmol) was added. The reaction mixture was refluxed at 80 C. for 5 hr. After removing the solvent, 200 mL of distilled water was added and extraction was carried out by using 600 mL of chloroform. After removing all the solvents, products were separated by column chromatography (silica, hexane/ethyl acetate=1:1 (v/v)) followed by another column chromatography (silica, methylene chloride/ethyl acetate=12:1, (v/v)). (yield=4 g, 42%)

(79) .sup.1H NMR (400 MHz, CDCl.sub.3): 7.80-7.78 (d, 2H), 7.4-7.44 (d, 4H), 7.32-7.30 (d, 2H), 6.96-6.93 (m 4H), 4.17-4.12 (m, 4H), 3.99-3.96 (t, 2H), 3.85-3.82 (t, 2H), 3.71-3.60 (m, 6H), 2.42 (s, 3H), 1.83-1.76 (m, 2H), 1.50-1.29 (m, 10H), 0.90-0.87 (t, 3H). (See, FIG. 10).

Synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid methyl ester

(80) 2-(2-{2-[4-(4-octyloxy)-hydroxybiphenyl]ethoxy}ethoxy)ethyl p-toluenesulfonate (4.03 g, 6.89 mmol) was dissolved in purified N,N-dimethylformamide (DMF, 40 mL) and, then, methy-3,4,5 trihydroxybenzoate (0.25 g, 1.38 mmol) and potassium carbonate (0.76 g, 5.51 mmol) were added. The reaction mixture was refluxed at 80 C. for 3 days under nitrogen atmosphere. After removing the solvent, 200 mL of distilled water was added and extraction was carried out by using 600 mL of chloroform. After removing the solvent, products were separated by column chromatography (silica, chloroform/ethyl acetate=1:1 (v/v)). (yield=1.08 g, 56%)

(81) .sup.1H NMR (400 MHz, CDCl.sub.3): 7.44-7.41 (m, 12H), 7.29 (s, 2H), 6.94-6.90 (m, 12H), 4.25-4.22 (t, 2H), 4.20-4.17 (t, 4H), 4.13-4.09 (m, 6H), 3.98-3.95 (t, 6H), 3.88-3.80 m (m, 12H), 3.86 (s, 3H), 3.73-3.70 (m, 12H), 1.82-1.75 (m, 6H), 1.47-1.28 (m, 30H), 0.90-0.87 (t, 9H). (See, FIG. 11).

Example 2

Synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl alcohol

(82) 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)-hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid methyl ester (0.50 g, 0.35 mmol) was dissolved in chloroform (CHCl.sub.3, 5 mL) in a 25 mL 1 neck flask and, then, lithium aluminium hydride (0.13 g, 3.51 mmol) was added slowly. The reaction mixture was stirred at room temperature for 2 hr. After reaction, distilled water was added to the mixture in an ice bath. A few drops of sulfuric acid (H.sub.2SO.sub.4, 2 M) was then added to the mixture for neutralization. 200 mL of distilled water was added to the mixture and extraction was carried out by using 300 mL of chloroform. The solvents were all removed. (yield=0.46 g, 94%)

(83) .sup.1H NMR: 7.44-7.41 (m, 12H), 6.94-6.90 (m, 12H), 6.60 (s, 2H), 4.53 (s, 2H), 4.17-4.10 (m, 12H), 3.98-3.95 (t, 6H), 3.85-3.79 (m, 12H), 3.73 (s, 12H), 1.82-1.75 (m, 6H), 1.47-1.28 (m, 30H), 0.90-0.87 (t, 9H). (See, FIG. 12).

Example 3

Synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl bromide

(84) 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)-hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl alcohol (0.46 g, 0.33 mmol) and 5 mL of chloroform were added to a 100 mL 1 neck flask. Trimethylsilyl briomide (0.0757 g, 0.495 mmol) was added dropwise to the reaction mixture at 0 C. The thus obtained mixture was stirred at 0 C. for 1 hr and, then, stirred at room temperature for 3 hr. After reaction, all the solvents were removed. (yield: 0.38 g, 79%)

(85) .sup.1H NMR: 7.44-7.42 (m, 12H), 6.94-6.90 (m, 12H), 6.66 (s, 2H), 4.36 (s, 2H), 4.14-4.12 (m, 12H), 3.98-3.95 (t, 6H), 3.85-3.80 (m, 12H), 3.73 (s, 12H), 1.82-1.75 (m, 6H), 1.47-1.28 (m, 30H), 0.90-0.87 (t, 9H). (See, FIG. 13).

Example 4

Synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl azide

(86) 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)-hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl bromide (0.3 g 0.206 mmol), 5 mL of DMF and sodium azide (0.26 g, 4.12 mmol) were added to a 25 mL 1 neck flask. The reaction mixture was stirred for one day under argon atmosphere. After reaction, the solvent was removed. Products were separated by column chromatography (silica, chloroform:ethyl acetate=1:1 (v/v)). (yield: 0.16 g, 54%)

(87) .sup.1H NMR: 7.44-7.41 (m, 12H), 6.94-6.90 (m, 12H), 6.52 (s, 2H), 4.20-4.10 (m, 14H), 3.98-3.95 (t, 6H), 3.86-3.79 (m, 12H), 3.73 (s, 12H), 1.82-1.75 (m, 6H), 1.47-1.28 (m, 30H), 0.90-0.87 (t, 9H). (See, FIG. 14).

Example 5

Synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid

(88) 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)-hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid methyl ester (1.08 g, 0.76 mmol) and 20 mL of tetrahydrofuran were added to a 100 mL 1 neck flask. Aqueous sodium hydroxide (10 M) and 15 mL of methanol were added thereto. The reaction mixture was stirred at 60 C. for 2.5 hr. After reaction, hydrochloric acid was added. After filtration, the thus obtained products were dissolved in chloroform and, then, precipitated in ethanol. (yield: 0.88 g, 82%)

(89) .sup.1H NMR (400 MHz, CDCl.sub.3): 7.43-7.41 (m, 12H), 7.33 (s, 2H), 6.93-6.90 (m, 12H), 4.26-4.24 (t, 2H), 4.19-4.17 (t, 4H), 4.13-4.09 (m, 6H), 3.97-3.94 (t, 6H), 3.87-3.83 (m, 12H), 3.73-3.71 (m, 12H), 1.81-1.74 (m, 6H), 1.47-1.28 (m, 30H), 0.90-0.86 (t, 9H). (See, FIG. 15).

Example 6

Synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]acyl chloride

(90) 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)-hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid (0.88 g, 0.62 mmol) and thionyl chloride (1.85 g, 15.62 mmol) were added to a 100 mL 1 neck flask and, then, the mixture was stirred at 60 C. for 8 hr. The solvent was removed. (yield: 0.88 g, 100%)

(91) .sup.1H NMR (400 MHz, CDCl.sub.3): 7.44-7.42 (m, 12H), 7.37 (s, 2H), 6.94-6.91 (m, 12H), 4.30-4.29 (t, 2H), 4.19-4.18 (t, 4H), 4.13-4.09 (m, 6H), 3.97-3.95 (t, 6H), 3.87-3.80 (m, 12H), 3.74-3.69 (m, 12H), 1.81-1.76 (m, 6H), 1.48-1.27 (m, 30H), 0.90-0.87 (t, 9H). (See, FIG. 16).

Example 7

Synthesis of 3,5-[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid methyl ester

(92) 2-(2-{2-[4-(4-octyloxy)-hydroxybiphenyl]ethoxy}ethoxy)ethyl p-toluenesulfonate (6.64 g, 22.25 mmol) was dissolved in purified N,N-dimethylformamide (DMF, 25 mL) in a 250 mL 1 neck round flask and, then, methyl 3,5-hydroxybenzoate (0.96 g, 5.56 mmol) and potassium carbonate (2.31 g, 16.68 mmol) were added. The reaction mixture was refluxed at 80 C. for 2 days under nitrogen atmosphere. After removing the solvent, 200 mL of distilled water and, then, extraction was performed by using 600 mL of chloroform. After removing all the solvents, products were separated by column chromatography (silica, methylene chloride/ethyl acetate=5:1 (v/v)). (yield=1.64 g, 29%)

(93) .sup.1H NMR (400 MHz, CDCl.sub.3): 7.45-7.43 (m, 4H), 7.19 (d, 2H), 6.95-6.93 (m, 4H), 6.7 (s, 1H), 4.15-4.13 (m, 4H), 4.00-3.97 (t, 2H), 3.90-3.87 (m, 4H), 3.86 (s, 3H), 3.75 (s, 4H), 1.81-1.77 (m, 2H), 1.50-1.29 (m, 10H), 0.90-0.87 (t, 3H). (See, FIG. 17).

Example 8

Synthesis of 3,5-[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl alcohol

(94) 3,5-[2-(2-{2-[4-(4-octyloxy)-hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid methyl ester (1.64 g, 1.61 mmol) was dissolved in chloroform (CHCl.sub.3, 20 mL) in a 100 mL 1 neck flask and, then, lithium aluminium hydride (0.61 g, 16.06 mmol) was added slowly. The reaction mixture was agitated at room temperature for 2 hr. A few drops of sulfuric acid (H.sub.2SO.sub.4, 2 M) were added to the mixture for neutralization (pH 7). 200 mL of distilled water was added to the mixture and extraction was carried out by using 600 mL of chloroform. All the solvents were removed. (yield=1.4 g, 88%)

(95) .sup.1H NMR: 7.45-7.43 (m, 4H), 6.96-6.93 (m, 4H), 6.52-6.51 (d, 2H), 6.42 (s, 1H), 4.57 (s, 2H), 4.14-4.10 (m, 4H), 3.99-3.96 (t, 2H), 3.87-3.84 (m, 4H), 3.74 (s, 4H), 1.81-1.77 (m, 2H), 1.46-1.29 (m, 10H), 0.90-0.87 (t, 3H). (See, FIG. 18).

Example 9

Synthesis of 4-[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid methyl ester

(96) 2-(2-{2-[4-(4-octyloxy)-hydroxybiphenyl]ethoxy}ethoxy)ethyl p-toluenesulfonate (2.3 g, 3.93 mmol) was dissolved in purified N,N-dimethylformamide (DMF, 25 mL) in a 250 mL 1 neck round flask and, then, methyl 4-hydroxybenzoate (0.39 g, 2.62 mmol) and potassium carbonate (0.54 g, 3.93 mmol) were added. The reaction mixture was refluxed at 80 C. for one day under nitrogen atmosphere. After removing the solvent, 200 mL of distilled water was added and, then, extraction was performed by using 600 mL of chloroform. After removing all the solvents, products were separated by column chromatography (silica, methylene chloride/ethyl acetate=12:1 (v/v)). (yield=0.8 g, 54%,)

(97) .sup.1H NMR (400 MHz, CDCl.sub.3): 7.97-7.95 (d, 2H), 7.46-7.44 (d, 4H), 6.96-6.90 (m, 6H), 4.18-4.14 (m, 4H), 3.99-3.96 (t, 2H), 3.90-3.87 (m, 4H), 3.87 (s, 3H), 3.76 (s, 4H), 1.83-1.76 (m, 2H), 1.84-1.29 (m, 10H), 0.90-0.87 (t, 3H). (See, FIG. 19).

Example 10

Synthesis of 4-[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl alcohol

(98) 4-[2-(2-{2-[4-(4-octyloxy)-hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzoic acid methyl ester (0.56 g, 0.99 mmol) was dissolved in chloroform (CHCl.sub.3, 5 mL) in a 100 mL 1 neck flask and, then, lithium aluminium hydride (0.37 g, 9.91 mmol) was added slowly. The reaction mixture was stirred at room temperature for 2 hr and, after reaction, was dipped in an ice bath. A few drops of sulfuric acid (H.sub.2SO.sub.4, 2 M) were added to the mixture for neutralization (pH 7). 200 mL of distilled water was added and extraction was carried out by using 600 mL of chloroform. All the solvents were removed. (yield=0.47 g, 88%)

(99) .sup.1H NMR: 7.45-7.43 (d, 4H), 7.27-7.24 (d, 2H), 6.96-6.88 (m, 6H), 4.59 (s, 2H), 4.16-4.11 (m, 4H), 3.99-3.96 (t, 2H), 3.89-3.86 (m, 4H), 3.76 (s, 4H), 1.83-1.75 (m, 2H), 1.55-1.29 (m, 10H), 0.90-0.87 (t, 3H). (See, FIG. 20).

Example 11

Synthesis of 3,4,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl methoxy-POSS

(100) 3,4,5-[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl alcohol (0.5 g, 0.358 mmol) and POSS-Isocyanate (0.498 g, 0.430 mmol) were dissolved in tetrahydrofuran (THF, 10 mL) in a 100 mL 1 neck flask and, then, dibutyl tin dilaurate (0.022 g, 0.036 mmol) was added. The reaction mixture was refluxed at 65 C. for 18 hr under nitrogen atmosphere. After reaction, all the solvents were removed and, then, products were separated by column chromatography (silica, chloroform/ethyl acetate=3:1 (v/v)). (yield=0.49 g, 54%)

(101) .sup.1H NMR: 7.44-7.41 (m, 12H), 6.94-6.90 (m, 12H), 6.58 (s, 2H), 4.95 (s, 2H), 4.78-4.75 (t, 1H), 4.16-4.10 (m, 12H), 3.98-3.95 (t, 6H), 3.86-3.79 (m, 12H), 3.77-3.71 (m, 12H), 3.19-3.14 (m, 2H), 1.82-1.65 (m, 48H), 1.57-1.16 (m, 60H), 0.90-0.87 (t, 9H), 0.77-0.72 (m, 7H), 0.59-0.55 (m, 2H), 0.12 (s, 6H). (See, FIG. 21).

Example 12

Synthesis of 3,5-tris[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl methoxy-POSS

(102) 3,5-[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl alcohol (0.7 g, 0.704 mmol) and POSS-Isocyanate (0.978 g, 0.845 mmol) were dissolved in tetrahydrofuran (THF, 15 mL) in a 100 mL 1 neck flask and, then, dibutyl tin dilaurate (0.054 g, 0.070 mmol) was added. The reaction mixture was refluxed at 65 C. for 18 hr under nitrogen atmosphere. After reaction, the solvent was removed and products were separated by column chromatography (silica, hexane/ethyl acetate=1.5:1 (v/v)). (yield=0.3 g, 20%)

(103) .sup.1H NMR: 7.45-7.43 (m, 8H), 6.96-6.93 (m, 8H), 6.51-6.50 (d, 2H), 6.44 (s, 1H), 4.99 (s, 2H), 4.78-4.72 (t, 1H), 4.15-4.09 (m, 8H), 3.99-3.96 (t, 4H), 3.88-3.82 (m, 8H), 3.74 (s, 8H), 3.17-3.15 (m, 2H), 1.84-1.63 (m, 40H), 1.51-1.16 (m, 58H), 0.90-0.87 (t, 6H), 0.81-0.70 (m, 7H), 0.59-0.53 (m, 2H), 0.13 (s, 6H). (See, FIG. 22).

Example 13

Synthesis of 4-[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl methoxy-POSS

(104) 4-[2-(2-{2-[4-(4-octyloxy)hydroxybiphenyl]ethoxy}ethoxy)ethoxy]benzyl alcohol (0.077 g, 0.144 mmol) and POSS-Isocyanate (0.2 g, 0.173 mmol) were dissolved in tetrahydrofuran (THF, 5 mL) and, then, dibutyl tin dilaurate (0.027 g, 0.043 mmol) was added. The reaction mixture was refluxed at 60 C. for 18 hr under nitrogen atmosphere. After reaction, the solvent was removed and, then, products were separated by column chromatography (silica, hexane/ethyl acetate=2:1 (v/v)). (yield=0.18 g, 76%)

(105) .sup.1H NMR: 7.45-7.43 (d, 4H), 7.27-7.25 (d, 2H), 6.96-6.92 (t, 4H), 6.89-6.87 (d, 2H), 5.01 (s, 2H), 4.70 (s, 1H), 4.16-4.10 (m, 4H), 3.99-3.96 (t, 2H), 3.88-3.86 (m, 4H), 3.75 (s, 4H), 3.17-3.13 (m, 2H), 1.82-1.72 (m, 44H), 1.56-1.22 (m, 40H), 0.90-0.87 (t, 3H), 0.77-0.73 (m, 7H), 0.58-0.54 (m, 2H), 0.12 (s, 6H). (See, FIG. 23).