Abstract

A plate-shaped chemical heat storage comprising a substrate composed of a net made of metal and a heat storage material composition supported on the substrate, wherein the heat storage material composition comprises at least one selected from the group consisting of magnesium hydroxide or oxide, strontium hydroxide or oxide, barium hydroxide or oxide, calcium hydroxide or oxide, and calcium sulfate, and optionally at least one selected from the group consisting of titanium dioxide, silicon dioxide, alumina silicate fiber, E-glass fiber and cellulose.

Claims

1. A plate-shaped chemical heat storage comprising a substrate composed of a metal net and a layer of a heat storage material composition, wherein the heat storage material is supported on the substrate, wherein the heat storage material composition comprises a chemical heat storage material and at least one additive selected from the group consisting of titanium dioxide, silicon dioxide, alumina silicate fiber, E glass fiber, and cellulose, wherein the plate-shaped chemical heat storage has a plate thickness of 0.3 mm or more and 2 mm or less and has a waveform shape having an amplitude higher than the plate thickness and an outer surface layer composed of the heat storage material composition is arranged along the outer surfaces of the metal net.

2. The plate-shaped chemical heat storage according to claim 1, wherein the at least one additive further comprises an additional additive selected from the group consisting of a heat conductive filler, reinforcing fibers, other than alumina silicate fiber and/or E glass fiber if already present, and binder, other than cellulose if already present.

3. The plate-shaped chemical heat storage according to claim 1, wherein a total amount of the at least one additive is not less than 1% by weight and not more than 40% by weight with respect to a total amount of the chemical heat storage material.

4. The plate-shaped chemical heat storage according to claim 1, wherein the metal net comprises at least one selected from the group consisting of stainless steel, aluminum, aluminum alloy, copper and copper alloy.

5. The plate-shaped chemical heat storage according to claim 1, wherein the metal net is composed of an expanded metal.

6. The plate-shaped chemical heat storage according to claim 1, wherein a mesh size of the net is 10 m or more and not more than 5 mm.

7. The plate-shaped chemical heat storage according to claim 1, wherein the heat storage material composition is supported on the substrate by applying a slurry or paste of the heat storage material composition thereto or compacting a powder of the heat storage material composition therewith.

8. A chemical heat storage system comprising the plate-shaped chemical heat storage according to claim 1.

9. A chemical heat storage structure composed of a stacked product comprising at least one of the plate-shaped chemical heat storage according to claim 1.

10. A chemical heat storage system comprising the chemical heat storage structure according to claim 9.

11. A plate-shaped chemical heat storage comprising a substrate composed of a metal net and a layer of a heat storage material composition, wherein the heat storage material is supported on the substrate, wherein the heat storage material composition comprises at least one selected from the group consisting of magnesium hydroxide or oxide, strontium hydroxide or oxide, barium hydroxide or oxide, calcium hydroxide or oxide, and at least one additive selected from the group consisting of titanium dioxide, silicon dioxide, alumina silicate fiber, E glass fiber, and cellulose, wherein the plate-shaped chemical heat storage has a plate thickness of 0.3 mm or more and 2 mm or less and has a waveform shape having an amplitude higher than the plate thickness and an outer surface layer composed of the heat storage material composition is arranged along the outer surfaces of the metal net.

12. The plate-shaped chemical heat storage according to claim 11, wherein the at least one additive further comprises an additional additive selected from the group consisting of a heat conductive filler, reinforcing fibers, other than alumina silicate fiber and/or E glass fiber if already present, and binder, other than cellulose if already present.

13. The plate-shaped chemical heat storage according to claim 11, wherein a total amount of the at least one additive is not less than 1% by weight and not more than 40% by weight with respect to a total amount of the chemical heat storage material.

14. The plate-shaped chemical heat storage according to claim 11, wherein the metal net comprises at least one selected from the group consisting of stainless steel, aluminum, aluminum alloy, copper and copper alloy.

15. The plate-shaped chemical heat storage according to claim 11, wherein the metal net is composed of an expanded metal.

16. The plate-shaped chemical heat storage according to claim 11, wherein a mesh size of the net is 10 m or more and not more than 5 mm.

17. The plate-shaped chemical heat storage according to claim 11, wherein the heat storage material composition is supported on the substrate by applying a slurry or paste of the heat storage material composition thereto or compacting a powder of the heat storage material composition therewith.

18. A chemical heat storage system comprising the plate-shaped chemical heat storage according to claim 11.

19. A chemical heat storage structure composed of a stacked product comprising at least one of the plate-shaped chemical heat storage according to claim 11.

20. A chemical heat storage system comprising the chemical heat storage structure according to claim 19.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a figure which shows an example of the plate-shaped chemical heat storage of the present invention.

(2) FIG. 2 is a figure which shows an example of the plate-shaped chemical heat storage of the present invention.

(3) FIG. 3 is a figure which shows an example of the plate-shaped chemical heat storage of the present invention.

(4) FIG. 4 is a figure which shows an example of the substrate used for the plate-shaped chemical heat storage of the present invention.

(5) FIG. 5 is a figure which shows an example of the substrate used for the plate-shaped chemical heat storage of the present invention.

(6) FIG. 6 is a figure which shows an example of the chemical heat storage structure of the present invention.

(7) FIG. 7 is a figure which shows an example of the chemical heat storage structure of the present invention.

(8) FIG. 8 is a figure which shows an example of the chemical heat storage structure of the present invention.

(9) FIG. 9 is a figure which shows an example of the chemical heat storage structure of the present invention.

EMBODIMENTS FOR CARRYING OUT THE INVENTION

(10) The plate-shaped chemical heat storage 1 of the present invention comprises a substrate 3 and a heat storage material composition 2 supported on the substrate 3.

(11) The substrate 3 used in the present invention is composed of a metal net. The net may be any of a braided wire rod, a cut and stretched plate material (expanded metal), a perforated plate material (punching metal), and the like.

(12) The material of the net is not particularly limited as long as it is a metal, but a metal having a higher thermal conductivity than the heat storage material composition is preferable, and stainless steel, aluminum, an aluminum alloy, copper, or a copper alloy is preferable.

(13) The mesh size of the net is not particularly limited, but is preferably 10 m or more, more preferably 100 m or more, still more preferably not less than 1 mm and not more than 5 mm, from the viewpoint that the heat storage material composition is difficult to peel off from the substrate and the thermal conductivity between the heat storage material composition and the substrate is enhanced.

(14) The net can be a flat net with a flat main surface, a bump net with bump-shaped ridges on the main surface, a corrugated net with wavy ridges on the main surface, a rib net with protrusions on the main surface, or so on. Since the heat storage material composition enters the mesh and exerts an anchor effect, even a flat net exhibits sufficient strength. For bump net, corrugated net or rib net, bumps, waves or ribs can be expected to further enhance the anchor effect.

(15) The heat storage material composition used in the present invention comprises a chemical heat storage material. As the chemical heat storage material, used is at least one selected from the group consisting of magnesium hydroxide or oxide, strontium hydroxide or oxide, barium hydroxide or oxide, calcium hydroxide or oxide, and calcium sulfate.

(16) A hydroxide or oxide of magnesium is a chemical heat storage material that utilizes heat storage when magnesium hydroxide is dehydrated and converted to magnesium oxide and heat dissipation when magnesium oxide is hydrated and converted to magnesium hydroxide. The heat storage operating temperature of magnesium hydroxide or oxide is around 350 C.

(17) A hydroxide or oxide of strontium is a chemical heat storage material that utilizes heat storage when strontium hydroxide is dehydrated and converted to strontium oxide and heat dissipation when strontium oxide is hydrated and converted to strontium hydroxide.

(18) A hydroxide or oxide of barium is a chemical heat storage material that utilizes heat storage when barium hydroxide is dehydrated and converted to barium oxide and heat dissipation when barium oxide is hydrated and converted to barium hydroxide.

(19) A hydroxide or oxide of calcium is a chemical heat storage material that utilizes heat storage when calcium hydroxide is dehydrated and converted to calcium oxide and heat dissipation when calcium oxide is hydrated and converted to calcium hydroxide. The heat storage operating temperature of calcium hydroxide or oxide is around 500 C.

(20) Calcium sulfate is a chemical heat storage material that utilizes heat storage when calcium sulfate 0.5 hydrate is dehydrated and changed to anhydrous calcium sulfate and heat dissipation when anhydrous calcium sulfate is hydrated and changed to calcium sulfate 0.5 hydrate. The heat storage operating temperature of calcium sulfate is around 90 C.

(21) The heat storage material composition used in the present invention may comprise additives such as a heat conductive filler, reinforcing fibers, or binder in addition to the above chemical heat storage material.

(22) Examples of the heat conductive filler can include molten silica, aluminum oxide, boron nitride, aluminum nitride, silicon nitride, magnesium carbonate, carbon nanotubes, boron nitride nanotubes, beryllium oxide and the like.

(23) Examples of the reinforcing fiber can include carbon fiber, glass fiber, alumina silicate fiber, E glass fiber, aramid fiber, polyolefin fiber, vinylon fiber, steel fiber and the like.

(24) As the other filler, mentioned are titanium dioxide, zeolite, activated white earth, sepiolite, bentonite, parigolstite, hydrotalcite, zinc oxide, iron oxide, barium sulfate, calcium carbonate, talc, aluminum hydroxide, antimony oxide, graphite, ferrite, etc. Of these, a filler in which the heat storage material composition supported on the substrate becomes porous is preferably used.

(25) Examples of binder can include an inorganic binder such as silica sol, silicate, phosphate, cement and silicone; an organic binder such as cellulose acetate, nitrile cellulose, cellulose, polyvinylidene fluoride, polyvinyl alcohol, styrene butadiene rubber, nitrile rubber, polytetrafluoroethylene, polypropylene, polyethylene, acrylic resin, and epoxy resin.

(26) Of these additives, at least one selected from the group consisting of titanium dioxide, silicon dioxide, alumina silicate fiber, E glass fiber, and cellulose can be preferably contained in the heat storage material composition.

(27) The total amount of the additives is preferably not less than 1% by weight and not more than 40% by weight with respect to the total amount of the chemical heat storage material.

(28) In the plate-shaped chemical heat storage of the present invention, the heat storage material composition is supported on the substrate, more specifically, on the outer surface of the net constituting the substrate and in the mesh of the net.

(29) The supporting can be carried out by applying a slurry or paste of the heat storage material composition to the substrate and drying it, by compacting the powder of the heat storage material composition together with the substrate, or by another supporting method.

(30) The plate-shaped chemical heat storage of the present invention has a plate thickness t of preferably 0.3 mm or more and 2 mm or less, and more preferably 0.5 mm or more and 1 mm or less.

(31) The surface of the plate-shaped chemical heat storage of the present invention may be completely covered with the heat storage material composition, or a part of the substrate may be exposed.

(32) The main surface of the plate-shaped chemical heat storage of the present invention may be a smooth surface or a rough surface. When the surface is rough, a slight gap is formed when the plate-shaped chemical heat storage of the present invention is stacked, and water, which is an operating medium for the chemical heat storage material, easily penetrates to the inside deep. From such a viewpoint, the surface roughness of the main surface is preferably several m to several hundred m.

(33) The plate-shaped chemical heat storage of the present invention may be cut into chips, bent into a tubular shape or a box shape, or embossed to be wavy (for example, shape as shown in FIGS. 2 and 3). Further, a plurality of plate-shaped chemical heat storages of the present invention can be stacked, or can be stacked with other plate-shaped materials.

(34) The chemical heat storage structure of the present invention comprises a stacked product comprising at least one plate-shaped chemical heat storage of the present invention.

(35) FIG. 6 shows a chemical heat storage structure 4 in which a large number of plate-shaped chemical heat storages 1a of the present invention are stacked. When there is a gap between adjacent plate-shaped chemical heat storages 1a, water vapor, which is an operating medium, easily passes through this gap. The chemical heat storage structure 4 has a high packing density of the chemical heat storage material per unit volume, can exhibit higher performance of heat storage/heat dissipation, and can stably maintain its shape for a long period of time.

(36) FIG. 7 shows a chemical heat storage structure 5 in which a plate-shaped chemical heat storage 1a of the present invention and another plate-shaped material 3 are alternately stacked.

(37) The other plate-shaped material 3 is not particularly limited, and may be, for example, a substrate 3-a made of a metal net on which no heat storage material composition is supported. In the chemical heat storage structure 5, the plate-shaped material 3 acts as a spacer and the flow path to the plate-shaped chemical heat storage 1 is expanded, and water vapor, which is an operating medium, easily flows to facilitate reaction of dehydration/hydration.

(38) FIG. 8 shows a structure in which plate-shaped chemical heat storage 1c in which ridges and flat portions are alternately formed at predetermined intervals as shown in FIG. 3 are stacked.

(39) FIG. 9 shows a corrugated honeycomb-like structure in which a plate-shaped chemical heat storage 1a and a plate-shaped chemical heat storage 1b as shown in FIG. 2 are alternately stacked.

(40) The stacking height h at this is not particularly limited, but is preferably set to 2 mm or more and 4 mm or less.

(41) In the structure of the present invention, since the substrate functions as a frame material, it is possible to maintain high strength and shape retention for a long period of time. In addition, as long as the form exhibits the action and effect in the present invention, it is not limited to the above, and other shapes may be used.

(42) Examples of the present invention will be shown below, and the present invention will be described in more detail. It should be noted that these are merely examples for explanation, and the present invention is not limited thereto.

Example 1

(43) Water was added to 10 kg of magnesium hydroxide powder and kneaded with a kneader. Thereto, 4 kg of silica-alumina fibers were added, and the mixture was further kneaded to obtain a paste-like chemical heat storage material composition having a water content of about 40%. Using a rolling machine with a pair of rollers, the paste-like chemical heat storage material composition was applied on an expanded metal substrate (metal lath plate, P.sub.1=4.5 mm, P.sub.2=3.0 mm) made of SUS 430 having a width of 500 mm so as to fill a mesh of the metal lath plate. Then, it was cut to a length of 500 mm with a cutting machine. This was dried at 120 C. for 2 hours. Then, it was cut into small pieces of 5050 mm to obtain a plate-shaped chemical heat storage having a thickness of 0.7 mm. The density of the heat storage material composition supported in the plate-shaped chemical heat storage was 0.95 g/cm.sup.3.

Example 2

(44) A plate-shaped chemical heat storage was obtained in the same manner as in EXAMPLE 1 except that the expanded metal substrate made of SUS 430 used in Example 1 was changed to an expanded metal substrate made of aluminum (metal lath plate, P.sub.1=4.5 mm, P.sub.2=3.0 mm). The density of the heat storage material composition supported in the plate-shaped chemical heat storage was 0.92 g/cm.sup.3.

Comparative Example 1

(45) Magnesium hydroxide powder (manufactured by Kishida Chemical Co., Ltd.) was placed in a tableting machine, and a pressure of 700 kg/cm.sup.2 was applied for 10 seconds to obtain a pellet-shaped heat storage having a diameter of 13 mm and a thickness of 2.4 mm. The density of the pellet-shaped heat storage was 0.94 g/cm.sup.3.

Evaluation

(46) A durability test was carried out under the conditions shown in Table 1 with one cycle of dehydration treatment and hydration treatment. The shape, dehydration ratio and hydration ratio of the heat storage were recorded for each cycle. The results are shown in Table 2.

(47) The dehydration ratio was calculated assuming that the initial magnesium hydroxide was completely converted to magnesium oxide as 100%. The hydration ratio was calculated assuming that all magnesium oxide was reconverted to the initial magnesium hydroxide weight as 100%.

(48) The pellet-shaped heat storage of COMPARATIVE EXAMPLE 1 was in a state where cracks were generated in the second cycle, cracks were generated in the entire surface of the pellets in the fifth cycle, and magnesium powder was attached to hands when touched.

(49) On the other hand, in the plate-shaped chemical heat storages of EXAMPLES 1 and 2, minute cracks were visually observed in a part of the heat storage material composition in the 5th cycle, but no detachment or peeling from the substrate was observed, and magnesium powder did not stick to the hands when touched.

(50) As shown in Table 2, the plate-shaped chemical heat storages of EXAMPLES 1 and 2 had higher dehydration ratio and hydration ratio than the pellet-shaped heat storage of COMPARATIVE EXAMPLE 1, and were excellent in heat storage performance.

(51) As is clear from the above results, the plate-shaped chemical heat storage of the present invention has high strength and high reaction efficiency of dehydration/hydration. By using the plate-shaped chemical heat storage of the present invention, it is possible to construct a high-performance and highly durable chemical heat storage system as compared with the case of using the conventional powder-shaped or pellet-shaped heat storage.

(52) TABLE-US-00001 TABLE 1 Dehydration Hydration Ambience In the air In the air Temp.[ C.] 400 85 WaterVapor Pressure [kPa] <4 58 Processing Time [hr] 0.5 5

(53) TABLE-US-00002 TABLE 2 Dehaydration ratio [%] Hydration ratio [%] 1st 2nd 3rd 4th 5th 1st 2nd 3rd 4th 5th Ex. 1 96 92 92 92 92 93 92 92 91 91 Ex. 2 97 95 95 94 94 93 94 93 92 93 Comp. Ex. 1 89 98 99 99 95 85 80 78 76 74

EXPLANATION OF SYMBOLS

(54) 1a, 1b, 1: plate-shaped chemical heat storage 2: heat storage material composition 3: substrate 3-a: substrate composed of a metal net 3-b: substrate composed of an expanded metal 4: heat storage structure 5: heat storage structure