All-AROUND CURVED POLARIZER

Abstract

An all-around curved polarizer for an all-around curved display device comprises a polarizing layer, a first protective layer and a second protective layer. The first protective layer is arranged on a side of the polarizing layer adjacent to the all-around curved display device and has a first coefficient of thermal expansion. The second protective layer is disposed on the other side of the polarizing layer opposite to the all-around curved display device, and has a second coefficient of thermal expansion, and the second coefficient of thermal expansion is greater than the first coefficient of thermal expansion of the first protective layer.

Claims

1. An all-around curved polarizer for an all-around curved display device, comprising a polarizing layer; a first protective layer disposed at a side of the polarizing layer facing to the all-around curved display device and having a first coefficient of thermal expansion; and a second protective layer disposed at the other side of the polarizing layer opposed to the all-around curved display device and having a second coefficient of thermal expansion; wherein the second coefficient of thermal expansion is more than the first coefficient of thermal expansion of the first protective layer.

2. The all-around curved polarizer as claimed in claim 1, wherein the all-around curved polarizer comprises a flat display area and a curved display area surrounding the flat display area.

3. The all-around curved polarizer as claimed in claim 1, wherein the first coefficient of the thermal expansion of the first protective layer is between 10×10.sup.−6/° C. and 20×10.sup.−6/° C., and the second coefficient of thermal expansion of the second protective layer is between 25×10.sup.−6/° C. and 40×10.sup.−6/° C.

4. The all-around curved polarizer as claimed in claim 2, wherein the flat display area includes four corners, and each of the four corners has a radius of curvature R1 between 5 mm and 10 mm.

5. The all-around curved polarizer as claimed in claim 2, wherein the cross-sectional radius of curvature R2 of the curved display area along the thickness direction is between 2 mm and 6 mm.

6. The all-around curved polarizer as claimed in claim 1, wherein the thickness of the first protective layer is less than or equal to the thickness of the second protective layer.

7. The all-around curved polarizer as claimed in claim 6, wherein the thickness of the first protective layer is between 20 μm and 80 μm, and the thickness of the second protective layer is between 40 μm and 80 μm.

8. The all-around curved polarizer as claimed in claim 1, wherein the first protective layer is a retardation film with a quarter-wavelength retardation to make the all-around curved polarizer be an all-around curved circular polarizer.

9. The all-around curved polarizer as claimed in claim 1, further comprising a quarter-wavelength plate (λ/4 plate) disposed adjacent to the first protective layer to make the all-around curved polarizer be an all-around curved circular polarizer.

10. The all-around curved polarizer as claimed in claim 1, wherein the first protective layer and the second protective layer are independently selected from one of the group consisting of polyimide, polyethylene terephthalate, polymethyl methacrylate, cyclo-olefin polymer, epoxy resin, polysiloxane and cellulose acetate polymer.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0017] FIG. 1 is a perspective view of a conventional mobile device with a curved display area.

[0018] FIG. 2 is a perspective view of an all-around curved polarizer for an all-around curved display device of an embodiment of the present invention.

[0019] FIG. 3A is a cross-sectional view of an all-around curved polarizer of an embodiment of the present invention.

[0020] FIG. 3B is a top view of an all-around curved polarizer of an embodiment of the present invention.

[0021] FIG. 4 is of an all-around curved polarizer of another embodiment of the present invention.

DETAILED DESCRIPTION OF THE DISCLOSURE

[0022] With reference to the following more detailed description and claims taken in conjunction with the accompanying drawings. The purpose of the drawings is only for illustrating the present invention and may not exhibit the true proportions and precise configuration. Thus, the drawings cannot be used limit the concept and scope of the present invention. The present disclosure is only defined by the appended claims.

[0023] The following description together with the accompanying drawings is to illustrate embodiments of the wound treatment system of the present invention. For understanding, the same elements in the following embodiments are described with the same symbols.

[0024] Referring to FIGS. 2 and 3A, FIG. 2 is a perspective view of an all-around curved polarizer 3 for an all-around curved display device 4 of an embodiment of the present invention and FIG. 3A is a cross-sectional view of the all-around curved polarizer 3. The all-around curved polarizer 3 comprises a polarizing layer 31, a first protective layer 32 disposed at a side of the polarizing layer 31 facing to the all-around curved display device 4 and having a first coefficient of thermal expansion, and a second protective layer 33 disposed at the other side of the polarizing layer 31 opposed to the all-around curved display device 4 and having a second coefficient of thermal expansion, wherein the second coefficient of thermal expansion is more than the first coefficient of thermal expansion of the first protective layer 32. The all-around curved polarizer 3 comprises a flat display area 3a and a curved display area 3b surrounding the flat display area 3a.

[0025] Herein, the coefficient of thermal expansion (CTE) described in the present invention is a one-dimensional linear coefficient of thermal expansion. The coefficient of thermal expansion can be obtained by the Formula (1), wherein the coefficient of thermal expansion a is a fractional rate of the dimension change from the length (L.sub.25° C.) of a long-strip film at room temperature 25° C. to the length (L.sub.85° C.) of the long-strip film heated to 85° C. in relation to the original length (L.sub.25° C.) per 1° C. increased.

α=(L.sub.85° C.−L.sub.25° C.)/L.sub.25° C.(85° C.−25° C.)  Formula (1)

[0026] In an embodiment of the present all-around curved polarizer, the first coefficient of the thermal expansion of the first protective layer 32 is between 10×10.sup.−6/° C. and 20×10.sup.−6/° C., and the second coefficient of thermal expansion of the second protective layer 33 is between 25×10.sup.−6/° C. and 40×10.sup.−6/° C.

[0027] FIG. 3B is a top view of the all-around curved polarizer of the present invention. In a preferred embodiment of the present all-around curved polarizer 3, the flat display area 3a in x-y plane includes four corners, and each of the four corners has a radius of curvature R1 between 5 mm and 10 mm.

[0028] In other embodiments of the present all-around curved polarizer with reference to FIG. 3A, according to the application type of display devices and the thickness thereof, the required radius of curvature in thickness direction is decreased with the thickness of the display, such as the mobile phone, the tablet, the watch or the like. The cross-sectional radius of curvature R2 of the curved display area 3b of the all-around curved polarizer 3 in thickness direction (i.e. the cross-section in z-axis) is preferred between 2 mm and 6 mm to satisfy the market demand to commercial portable devices with curved edges.

[0029] In other embodiments of the present all-around curved polarizer, because the first protective layer 32 is disposed at the inner side and the second protective layer 33 is disposed at the outer side, and the required expansion of the first protective layer 32 is less than that of the second protective layer 33, so the thickness of the first protective layer 32 is preferably less than or equal to the thickness of the second protective layer 33.

[0030] In a preferred embodiments of the present all-around curved polarizer, the thickness of the first protective layer is between 20 μm and 80 μm, and the thickness of the second protective layer 33 is between 40 μm and 80 μm.

[0031] In a preferred embodiments of the present all-around curved polarizer, the first protective layer 32 is a retardation film with a quarter-wavelength retardation to make the all-around curved polarizer 3 be a circular polarizer.

[0032] Referring to FIG. 4, in an embodiment of the present all-around curved polarizer, the all-around curved polarizer 3′ further comprises a quarter-wavelength plate (λ/4 plate) 5 disposed adjacent to the first protective layer 32 to make the all-around curved polarizer 3′ be an all-around curved circular polarizer.

[0033] In a preferred embodiments of the present all-around curved polarizer, the materials of the first protective layer 32 and the second protective layer 33 independently can be but not limited to polyimide, polyethylene terephthalate, polymethyl methacrylate, cyclo-olefin polymer, epoxy resin, polysiloxane, cellulose acetate polymer or the like. The materials for the protective films are selected based on the strain thereof after being heated which satisfies the above-mentioned relation of the coefficient of thermal expansion.

[0034] The present invention will be explained in further detail with reference to the examples. However, the present invention is not limited to these examples.

EXAMPLE

Example 1

[0035] An all-around curved polarizer was prepared in Example 1, wherein the polarizing layer was a stretched iodine-type polarizing layer, and a first protective layer was a cellulose triacetate (TAC) film with a coefficient of thermal expansion of 11.3×10.sup.−6/° C. (thickness 40 μm, commercially available from Fujifilm, Japan), and the second protective layer was a polymethyl methacrylate (PMMA) film with a coefficient of thermal expansion of 31.7×10.sup.−6/° C. (thickness 40 μm, commercially available from Toyo Kohan Co., Ltd.). The polarizer was heated to 120° C. for 8 seconds and thermopress molded to force the second protective layer toward the first protective layer bending. The radius of curvature R1 is set to 6 mm, and the radius of curvature R2 is set to 2.6 mm Commonly, the radius of curvature R2 of the cross-sectional plane in the thickness direction is less, the bending stress suffered is more. The more bending stress results in the deformation during thermopress molding process. Thus, in this Example, the radius of curvature R2 was 2.6 mm to obtain an all-around curved polarizer with a flat display area and a curved display area surrounding the flat display area. Next, the edge of the polarizer was trimmed by laser cutting or the like process.

Example 2

[0036] An all-around curved polarizer was prepared in Example 2, wherein the polarizing layer was a stretched iodine-type polarizing layer, and the first protective layer was a cellulose triacetate (TAC) film with a coefficient of thermal expansion of 11.3×10.sup.−6/° C. (thickness 40 μm, commercially available from Fujifilm, Japan), and the second protective layer was a polyethylene terephthalate (PET) film with a coefficient of thermal expansion of 35.6×10.sup.−6/° C. (thickness 80 μm, commercially available from Toyobo, Japan). The polarizer was heated to 120° C. for 8 seconds and thermopress molded to force the second protective layer toward the first protective layer bending, with a radius of curvature R1 of 6 mm and a radius of curvature R2 of 2.6 mm. The all-around curved polarizer was formed with a flat display area and a curved display area surrounding the flat display area. Next, the edge of the curved display area of the polarizer was trimmed by laser cutting or the like process.

Comparative Example 1

[0037] An all-around curved polarizer was prepared in the Comparative Example 1, wherein the polarizing layer was a stretched iodine-type polarizing layer, and a first protective layer was a PET film (thickness 80 μm, commercially available from Toyobo) with a coefficient of thermal expansion of 35.6×10.sup.−6/° C., and a second protective layer was a TAC film (thickness 80 μm, commercially available from Fujifilm) PET film with a coefficient of thermal expansion 10.3×10.sup.−6/° C. The polarizer was heated to 120° C. for 8 seconds and thermopress molded to force the second protective layer toward the first protective layer bending to prepare an all-around curved polarizer with a flat display area and a curved display area surrounding the flat display area, wherein the radius of curvature R1 was set to 6 mm, and the radius of curvature R2 was set to 2.6 mm. The all-around curved polarizer was evaluated and compared in the same way as the Examples. Next, the edge of the curved display area of the polarizer was trimmed by laser cutting or the like process.

Comparative Example 2

[0038] An all-around curved polarizer was prepared in the Comparative Example 2, wherein the polarizing layer was a stretched iodine-type polarizing layer, and both the first protective layer and the second protective layer were PET films (thickness 80 μm, commercially available from Toyobo) with a coefficient of thermal expansion of 35.6×10.sup.−6/° C. The polarizer was heated to 120° C. for 8 seconds and thermopress molded to force the second protective layer toward the first protective layer bending to prepare an all-around curved polarizer with a flat display area and a curved display area surrounding the flat display area, wherein the radius of curvature R1 was set to 6 mm, and the radius of curvature R2 was set to 2.6 mm Next, the edge of the curved display area of the polarizer was trimmed by laser cutting or the like process.

Comparative Example 3

[0039] An all-around curved polarizer was prepared in the Comparative Example 3, wherein the polarizing layer was a stretched iodine-type polarizing layer, and both the first protective layer and the second protective layer were TAC films (thickness 40 μm, commercially available from Fujifilm) with a coefficient of thermal expansion of 11.3×10.sup.−6/° C. The polarizer was heated to 120° C. for 8 seconds and thermopress molded to force the second protective layer toward the first protective layer bending to prepare an all-around curved polarizer with a flat display area and a curved display area surrounding the flat display area, wherein the radius of curvature R1 was set to 6 mm, and the radius of curvature R2 was set to 2.6 mm Next, the edge of the curved display area of the polarizer was trimmed by laser cutting or the like process.

Comparative Example 4

[0040] An all-around curved polarizer was prepared in the Comparative Example 4, wherein the polarizing layer was a stretched iodine-type polarizing layer, and the first protective layer was a PMMA film (thickness 40 μm, commercially available from Toyo Kohan Co., Ltd.) with a coefficient of thermal expansion of 31.7×10.sup.−6/° C., and a second protective layer was a TAC film (thickness 40 μm, commercially available from Fujifilm) with a coefficient of thermal expansion of 11.3×10.sup.−6/° C. The polarizer was heated to 120° C. for 8 seconds and thermopress molded to force the second protective layer toward the first protective layer bending to prepare an all-around curved polarizer with a flat display area and a curved display area surrounding the flat display area, wherein the radius of curvature R1 was set to 6 mm, and the radius of curvature R2 was set to 2.6 mm Next, the edge of the curved display area of the polarizer was trimmed by laser cutting or the like process.

[0041] The all-around curved polarizers obtained from the Examples and the Comparative Examples were evaluated the accuracy of the optical axis, the flatness of the edge appearance, film warpage, curvature deviation. The evaluation results were listed in Table 1. Because the all-around curved polarizer of the present invention not only has a single-dimensional absorption axis like the current plane polarizer, but also has a three-dimensional absorption axis change after being thermopressed to be molded into to a three dimensional shape. Thus, the optical properties of the present all-around curved polarizer cannot be determined by the common measuring instrument for a polarizer with single linear absorption axis. The present all-around curved polarizer was laminated with another standard all-around curved polarizer with each other's absorption axis in a perpendicular direction. The laminated all-around curved polarizers were evaluated by visual observation via a backlight module to see if any light leakage occurred at edge sides and four corners to determine the accuracy of the absorption axis. The evaluation criteria were if the optical properties at the side edges and four corners of the curved display area and the optical properties at flat display area were consistent. If any area appeared an obvious light leakage and/or moire, the all-around curved polarizer marked as (X) to represent the deviation of the absorption axis. If the bright and dark level was uniform, the all-around curved polarizer marked as (∘) to represent that the optical axis of these area was accurate. The flatness of the edge appearance was evaluated by visual observation. If creases appeared on side angle marked as (X), slightly twisted deformation, wrinkles appeared marked as (Δ), no obvious defects marked as (∘). The warpage measurement was determined by placing the all-around curved polarizer on a flat base and measuring the highest height of each corner to the flat base. If the warpage height of the polarizer is more than or equal to 8 mm, it would be adversely to the polarizer aligned to the display during the later process for adhering to the display and then, the warpage marked as (X); the height of the warpage between 5 mm and 8 mm, the warpage marked as (Δ), less than or equal to 5 mm, the warpage marked as (∘). The curvature deviation of the appearance of the polarizer was measured by the Wide-area 3D Measurement System (VR-5000, KEYENCE) to determine the contour of the all-around curved polarizer, configure and calculate the curvature deviation of the side edges and four corners. If the curvature deviated from the set value more than or equal to 5%, the curvature deviation marked as (X); if the curvature deviated from the set value between 1% and 5%, the curvature deviation marked as (Δ); and if the curvature deviated from the set value less than or equal to 1%, the curvature deviation marked as (∘).

TABLE-US-00001 TABLE 1 Example Example Comparative Comparative Comparative Comparative 1 2 Example 1 Example 2 Example 3 Example 4 Appearance Edge ∘ ∘ Δ X X X flatness Warpage ∘ ∘ X Δ X X Curvature ∘ ∘ X Δ X X deviation Optical side angle ∘ ∘ X ◯ X X property light leakage

[0042] As seen from Table 1, when the all-around curved polarizer of Examples 1 and 2 molding to be curved, because the second coefficient of thermal expansion of the second protective layer at the outer side was higher than the first coefficient of thermal expansion of the first protective layer at the inner side, no matter that the thickness of the first protective layer is less than or equal to the thickness of the second protective layer, the all-around curved polarizer had satisfied optical properties and appearance. On the other hand, when the polarizer as obtained in Comparative Examples was molding to be curved, because the second coefficient of thermal expansion of the second protective layer at the outer side was less than the first coefficient of thermal expansion of the first protective layer at the inner side, the optical axis at the curved area of the all-around curved polarizer was shifted to result in light leakage or poor appearance at the edges and corners. The defects of the polarizer as obtained in Comparative Examples affected the subsequent processing and laminating so as to be unable to obtain an all-around curved polarizer with satisfied optical properties and appearance. Thus, the polarizer as obtained in Comparative Examples was not suitable for all-around curved display device.

[0043] Although particular embodiments have been shown and described, it should be understood that the above discussion is not intended to limit the present invention to these embodiments. Persons skilled in the art will understand that various changes and modifications may be made without departing from the scope of the present invention as literally and equivalently covered by the following claims.