Process for conversion of levulinic acid to ketones

Abstract

A method for generating desired platform chemicals from feedstocks such as cellulosic biomass feedstocks containing levulinic acid by decarboxylating a feed stock comprising levulinic acid to generate ketones. This is done by passing a feed stock comprising levulinic acid in a gas phase over a non-precious metal catalyst on a neutral support.

Claims

1. A method for decarboxylating a feed stock comprising levulinic acid to generate ketones comprising the step of: passing a feed stock comprising levulinic acid in a gas phase over a metal catalyst on a neutral support having a pH between 5.5 and 8 at a temperature between 350-650 degrees C.

2. The method of claim 1, wherein the step of passing the gas-phase feedstock over a metal catalyst occurs without the presence of a reducing gas.

3. The method of claim 1, wherein the feedstock is introduced continuously over the decarboxylation catalyst to continuously form ketones.

4. The method of claim 1, wherein the catalyst is a transition metal catalyst.

5. The method of claim 1 wherein the neutral support comprises a carbon support.

6. The method of claim 5 where in the carbon support comprises activated carbon.

7. The method of claim 4 wherein the transition metal is a metal selected from the metals in group VIII, group IX, group X, or group XI on the periodic table.

8. The method of claim 1 wherein the metal in the metal catalyst is a non-metal catalyst.

9. The method of claim 8 wherein the non-precious metal catalyst comprises Cu and the neutral support comprises carbon.

10. A method for generating fuels comprising the steps of: decarboxylating a feed stock comprising levulinic acid by passing said feed stock in a gas phase over a metal catalyst on a neutral support having a pH between 5.5 and 8 at a temperature between 350-650 degrees C. to generate ketones, and converting the ketone product over an olefin-forming catalyst to form an olefin.

11. The method of claim 10 wherein the step of decarboxylation is performed over a non-precious metal catalyst without the presence of a reducing gas.

12. The method of claim 10 wherein the feedstock is introduced continuously over the decarboxylation catalyst to continuously form ketones.

13. The method of claim 10, wherein the metal catalyst is a transition metal catalyst.

14. The method of claim 10 wherein the neutral support comprises a carbon support.

15. The method of claim 10 wherein the metal catalyst is not a precious metal.

16. The method of claim 10 wherein the transition metal is selected from the metals in group VIII, group IX, group X, or group XI on the periodic table.

17. The method of claim 1 wherein the metal catalyst comprises Cu and the neutral support comprises carbon.

18. The method of claim 10 wherein the olefin forming catalyst is a mixed-acid base catalyst.

19. The method of claim 10, wherein the olefin-forming catalyst has a formula of ZnxZryOz where x is selected from 0.5 to 15, y is selected from 0.5 to 20, and z is selected from 0.5 to 55.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 shows a process for conversion of biomass containing levulinic acid and formic acid derived from cellulose-containing biomass feedstocks into platform chemicals, and fuels according to one embodiment of the present invention.

DETAILED DESCRIPTION

(2) In the following description, embodiments of the present invention are shown and described by way of illustration of the best mode contemplated for carrying out the invention. It will be clear that the invention may include various modifications and alternative constructions. Accordingly, the description of the preferred embodiments should be seen as illustrative only and not limiting. The present invention includes all modifications, alternative constructions, and equivalents falling within the spirit and scope of the invention as defined in the claims.

(3) FIG. 1 shows a block flow diagram of an exemplary process for converting biomass to fuels through a process whereby levulinic acid (LA) is converted to ketone intermediates including, for example, methyl ethyl ketone (MEK) and acetone, which are then utilized individually as specialty, intermediate or commodity chemicals or which can be further upgraded as turned into carbon chain fuels or other chemicals. The focal point of this process is outlined as the step wherein a catalytic process for the conversion of sugar-derived levulinic acid to fuels and chemicals, via platform intermediates MEK and acetone is performed using inexpensive (non-precious metal) catalysts. This then enables a one-step conversion of MEK and acetone to olefin fuel precursors. Currently obtained from petroleum, the annual worldwide production of MEK and acetone is approximately 2 and 6 million tons/yr, respectively, with market selling prices of 74 and 64/lb, respectively.

(4) The direct decarboxylation of LA provides the simplest pathway, to a singular product (MEK) and whereby the formation of cyclic intermediates does not occur, nor is H2 required. Cyclic intermediates can lead to the formation of lactones that polymerize and deactivate catalysts through coke deposits. While a dehydration and/or hydrogenation process is typically utilized, preliminary results recently obtained at PNNL indicate careful control of operating parameters and choice of catalyst can actually favor the decarboxylation pathway and increase the yields of MEK, acetone, and without addition of external H2. These results were obtained with non-precious metal catalysts and at atmospheric pressure. This is done by passing a feed stock comprising levulinic acid in a gas phase over the metal catalyst on a neutral support at a temperature between 250-650 degrees C. In one instantiation the gas-phase feedstock over a metal catalyst occurs without the presence of a reducing gas. Preferably, the feedstock is introduced continuously over the decarboxylation catalyst to continuously form ketones. In various embodiments the catalyst may be a transition metal catalyst, and preferably a transition metal selected from the metals in group VIII, group IX, group X, or group XI on the periodic table. Preferably the catalyst is copper (Cu) on a neutral carbon support.

(5) The neutral support is preferably a carbon material (activated carbon, carbon black and graphite, carbon fiber, carbon nanotubes), more preferably an activated carbon support made from almond core, coconut shell, palm tree wood or coal, preferably coconut shell. In other embodiments neutral supports include oxides such as SiO2, Al2O3, ZrO2, TiO2, Ta2O5, CeO2, MgO, La2O3, Nb2O5, and combinations thereof. In some instances these materials are modified with at least one alkali and/or alkaline earth metals, and/or group III metals (e.g. Li, Na, K, Rb, Cs, Be, Mg, Ca, Sr, Ba, Y). Once the ketones, typically MEK and acetone, are created they can be passed on to a second step for processing and fuel creation and chemical upgrading through an olefin forming process.

(6) The MEK, acetone and other ketones that are created from this arrangement can be then converted into olefin fuel precursors through a simple one step process. In some embodiments the olefin-forming process includes passing the material over a olefin forming catalyst having a formula of ZnxZryOz where x is selected from 0.5 to 15, y is selected from 0.5 to 20, and z is selected from 0.5 to 2. Continuous feeding of the feedstock through the process allows for conversion of Levulinic acid from cellulosic biomass to ketone based chemicals and further upgrading of those ketone based chemicals into to other platform and commodity chemicals as well as desirable fuels (jet/diesel/gasoline) at a scale relevant for industrial biomass implementation.

(7) In one set of experiments the process was performed with a catalyst on a carbon support that was loaded into a fixed bed reactor between 2 layers of quartz wool. A thermocouple is located in the middle of the bed. The reactor temperature is then increased to 500 C. under nitrogen with a ramp of 3 C./min and held at temperature for 8 hours. The nitrogen flowrate was then adjusted depending of the reaction conditions, the liquid feed pump started and an aqueous solution of levulinic acid is sent through a vaporizer and over the catalyst. Process conditions were operated as follows: W/F (g.Math.s.Math.ml-1) range: between 0.01-20.0, preferentially between 0.1-10.0, more preferentially between 0.3-6.6; Temperature: 250-600 C., preferentially 450-550 C., more preferentially 500 C. Pressure: 1 bar-150 bar, preferentially 1-30 bar, more preferentially 1 bar. While in this instance the reactor was a fixed bed reactor other types of reactors such as fluidized bed reactors, swing reactors, batch reactors or other types of reactors could be utilized. If necessary a nitrogen diluent or other possible diluents such as helium and argon could be utilized. In some applications the reaction could be conducted in absence of diluent. In some applications the levulinic acid (LA) feed can be diluted (preferably with water) to a 5-50 wt % levulinic acid in water, but more preferentially this dilution is between 10-30 wt %, and more preferentially at or about 10 wt %. Formic acid could also be present in the feed without negatively impacting the performance of the process.

(8) The preferred catalysts utilized included at least one metal from the group 8, 9 10, or 11 metal (e.g. Cu, Ag, Pd), preferably Cu supported on a neutral support. The neutral support is preferably a carbon material (activated carbon, carbon black and graphite, carbon fiber, carbon nanotubes), more preferably an activated carbon support made from almond core, coconut shell, palm tree wood or coal, preferably coconut shell. Other neutral supports that could be used are oxides such as SiO2, Al2O3, ZrO2, TiO2, Ta2O5, CeO2, MgO, La2O3, Nb2O5, and combinations of two or more thereof, modified with at least one alkali and/or alkaline-earth metals and/or group 3 metal (e.g. Li, Na, K, Rb, Cs, Be, Mg, Ca, Sr, Ba, Y). The metal loading is between 0.5-40 wt %, preferentially 1-20 wt %, more preferentially 1-5 wt %. If the neutral support is not a carbon the catalyst can be calcined.

(9) The preferred Cu/activated carbon (coconut shell) catalyst is prepared by incipient wetness impregnation of a Cu metal nitrate precursor dissolved in water onto carbon support, dry at 120 C. for 12 hours and finally calcined at 375 C. under inert gas for 4 hours (i.e. Argon, Nitrogen, Helium). While these preparation steps were utilized the preparation process could vary in numerous ways in order to dispose one or more active metals on the support. Impregnation, ion-exchange incipient wetness impregnation, and/or by drying impregnation as well as other methods in single or multiple step arrangements could all be utilized to combine the catalyst and the support. Likewise, while water and alcohols are used as solvents there is no restriction or limitation upon the particular solvent utilized or the nature of the metal precursor.

(10) The following examples show embodiments of the present disclosure and the experimental results obtained there with. The descriptions of the examples are provided in the following paragraphs and the comparative results are included in Table 1.

(11) Example 1

(12) A 3 wt % Cu/Activated carbon catalyst was prepared by incipient wetness impregnation of an aqueous solution of Cu nitrate. The catalyst was dried at 120 C. for 12 hours then calcined at 375 C. under nitrogen for 4 hours. 2 grams of catalyst sieved 60-100 mesh were loaded in the fixed bed reactor. Before reaction, the catalyst was pretreated under nitrogen at 500 C. for 8 hours. A feed of 10 wt % Levulinic acid (LA) in water, nitrogen diluent with flowing rate equal to 40 sccm, at 500 C., 1 bar and W/F=1.5 g.Math.s.Math.ml-1. In this example 98% of the LA was converted with 33.3% becoming methyl-ethyl ketone (MEK), 16.2% becoming acetone, 8.8% becoming C2-C5 olefins, 20.5% converted to carbon dioxide CO2, 5.5% becoming methane (CH4), 12.8% becoming carbon monoxide (CO), 0.8% becoming C2-C5 paraffins, and 2.1% becoming other oxygenates, such as phenol, cresol, methylcyclopentanone.

(13) Example 2

(14) A 3 wt % Cu/Activated carbon catalyst was prepared by incipient wetness impregnation of an aqueous solution of Cu nitrate. The catalyst was dried at 120 C. for 12 hours then calcined at 375 C. under nitrogen for 4 hours. 2 grams of catalyst sieved 60-100 mesh were loaded in the fixed bed reactor. Before reaction, the catalyst was pretreated under nitrogen at 500 C. for 8 hours. Reactivity measurement was conducted with 10 wt % levulinic acid in water, nitrogen diluent with flowing rate equal to 40 sccm, at 500 C., 1 bar and W/F=3.1 g.Math.s.Math.ml-1. In this example 99.5% of the LA was converted with 36.1% becoming methyl-ethyl ketone (MEK), 5.4% becoming acetone, 8.2.% becoming C2-C5 olefins, 29.1% converted to carbon dioxide (CO2), 6.8% becoming methane (CH4), 10.3% becoming carbon monoxide (CO), 1.9% becoming C2-C5 paraffins, and 2.3% becoming other oxygenates.

(15) Example 3

(16) A 3 wt % Cu/Activated carbon catalyst was prepared by incipient wetness impregnation of an aqueous solution of copper (Cu) nitrate. The catalyst was dried at 120 C. for 12 hours then calcined at 375 C. under nitrogen for 4 hours. 2 grams of catalyst sieved 60-100 mesh were loaded in the fixed bed reactor. Before reaction, the catalyst was pretreated under nitrogen at 500 C. for 8 hours. Reactivity measurement was conducted with 10 wt % Levulinic acid in water, nitrogen diluent with flowing rate equal to 40 sccm, at 500 C., 1 bar and W/F=6.3 g.Math.s.Math.ml-1 In this example 99.5% of the LA was converted with 34.6% becoming methyl-ethyl ketone (MEK), 7.2% becoming acetone, 8.1% becoming C2-C5 olefins, 34.6% converted to carbon dioxide CO2, 8.8% becoming methane (CH4), 3.4% becoming carbon monoxide (CO), 2.1% becoming C2-C5 paraffins, and 1.2% becoming other oxygenates

(17) Example 4

(18) A 3 wt % Cu/Activated carbon was prepared by incipient wetness impregnation of an aqueous solution of Cu nitrate. The catalyst was dried at 120 C. for 12 hours then calcined at 375 C. under Nitrogen for 4 hours. 2 grams of catalyst sieved 60-100 mesh were loaded in the fixed bed reactor. Before reaction, the catalyst was pretreated under nitrogen at 500 C. for 8 hours. Reactivity measurement was conducted with 10 wt % Levulinic acid in water, nitrogen diluent with flowing rate equal to 40 sccm, at 450 C., 1 bar and W/F=0.8 g.Math.s.Math.ml-1. In this example 99% of the LA was converted with 12.3% becoming methyl-ethyl ketone (MEK), 3.5% becoming acetone, 7.7% becoming C2-C5 olefins, 26.5% converted to carbon dioxide CO2, 5.1% becoming methane (CH4), 19.6% becoming carbon monoxide (CO), 1.7% becoming C2-C5 paraffins, and 9.4% becoming other oxygenates. This example also resulted in the formation of coke within the reactor system.

(19) Example 5

(20) A 3 wt % Cu/Activated carbon was prepared by incipient wetness impregnation of an aqueous solution of Cu nitrate. The catalyst was dried at 120 C. for 12 hours then calcined at 375 C. under Nitrogen for 4 hours. 2 grams of catalyst sieved 60-100 mesh were loaded in the fixed bed reactor. Before reaction, the catalyst was pretreated under nitrogen at 500 C. for 8 hours. Reactivity measurement was conducted with 10 wt % Levulinic acid in water, nitrogen diluent with flowing rate equal to 40 sccm, at 550 C., 1 bar and W/F=1.5 g.Math.s.Math.ml-1. In this example 97% of the LA was converted with 16.5% becoming methyl-ethyl ketone (MEK), 9.3% becoming acetone, 11.1% becoming C2-C5 olefins, 36.0% converted to carbon dioxide CO2, 9.9% becoming methane (CH4), 9.9% becoming carbon monoxide (CO), 2.9% becoming C2-C5 paraffins, and 4.3% becoming other oxygenates. A comparison of these experiments is shown in Table 1.

(21) TABLE-US-00001 TABLE 1 Selectivity (%) (%) C.sub.2-C.sub.5 C.sub.2-C.sub.5 Other Sample Converted MEK Acetone olefins CO.sub.2 CH.sub.4 CO paraffin oxygenates 1 98 33.3 16.2 8.8 20.5 5.5 12.8 0.8 2.1 2 99.5 36.1 5.4 8.2 29.1 6.8 10.3 1.9 2.3 3 99.5 34.6 7.2 8.1 34.6 8.8 3.4 2.1 1.2 4 99 12.3 3.5 7.7 26.2 5.1 19.6 1.7 9.4 5 97 16.5 9.3 11.1 36.0 9.9 9.9 2.9 4.3

(22) The MEK and acetone by products obtained from decarboxylation of levulinic acid can be further converted into olefins over a Zn1Zr2.5Oz catalyst. In one example, Example 6, a Zn1Zr2.5Oz catalyst was prepared via wet impregnation of a Zn(NO3)26H2O solution on Zr(OH)4. The Zr(OH)4 was initially dried overnight at 105 C. to remove any excess water on the surface before impregnation. After impregnation, the catalysts were dried overnight at room temperature and then for 4 hours at 105 C. prior to calcination. The catalyst then was calcined via a 3 C./min ramp to 400 C. for 2 hours, followed by a 5 C./min ramp to the final calcination temperature of 550 C. for 3 hours. 1 gram of catalyst sieved to a 60 100 mesh was loaded in the fixed bed reactor of FIG. 1. Before reaction, the catalyst was pretreated under nitrogen at 450 C. for 8 hours. A feed of 30 wt % MEK in water, a nitrogen/hydrogen (ratio 4:1 molar) mixture diluent with a flow rate equal to 40 sccm, at 450 C., 1 bar and W/F=0.8 g.Math.s.Math.ml-1 was then passed over the catalyst. In this example 89% of the MEK was converted with 50.2% into pentenes, 13.5% into butenes, 2.2% into propylenes, 0.8% into ethylene, 3.8% into methane, 17.1% into CO2, 0.7% into C2-C5 paraffins, 9.1% into acetone and 2.6% into other oxygenates (principally pentanone).

(23) In another example, example 7, a Zn1Zr2.5Ox catalyst was prepared via wet impregnation of a Zn(NO3)26H2O solution on Zr(OH)4. The Zr(OH)4 was initially dried overnight at 105 C. to remove any excess water on the surface before impregnation. After impregnation, the catalysts were dried overnight at room temperature and then for 4 hours at 105 C. prior to calcination. The catalyst then was calcined via a 3 C./min ramp to 400 C. for 2 hours, followed by a 5 C./min ramp to the final calcination temperature of 550 C. for 3 hours. 1 gram of catalyst sieved 60-100 mesh was loaded in the fixed bed reactor. The reactor of FIG. 1 was used. Before reaction, the catalyst was pretreated under nitrogen at 450 C. for 8 hours. Reactivity measurement was conducted with 30 wt % acetone in water, a nitrogen/hydrogen (ratio 4:1 molar) mixture diluent with flowing rate equal to 40 sccm, at 450 C., 1 bar and W/F=0.8 g.Math.s.Math.ml-1. In this example 95% of the acetone was converted with 0.0 converted % into pentenes, 76.5% into butenes, 5.4% into propylenes, 0.0% into ethylene, 5.0% into methane, 12.3% into CO2, 0.0% into C2-C5 paraffins, 0.0% into acetone and 0.8% into other oxygenates (principally acetic acid).

(24) While exemplary embodiments of the present invention have been shown and described, it will be apparent to those skilled in the art that many changes and modifications may be made without departing from the invention in its true scope and broader aspects. The appended claims are therefore intended to cover all such changes and modifications as fall within the scope of the present invention.