RFID TAG SUBSTRATE USING PAPER SUBSTRATE, AND RFID TAG

Abstract

An RFID tag substrate contains a paper substrate having an eluted chloride ion amount per unit mass (1 g) of 0.100 mg or less, having formed on a surface thereof a conduction circuit. A specimen of the paper substrate is broken into small pieces each of 100 mm.sup.2 or less. The small pieces are immersed in a polypropylene vessel having 50 mL of water with an electric conductivity of 0.2 mS/m or less. After standing, the water is filtered with a membrane filter to recover a filtrate and the filtrate is analyzed by an ion chromatography method to obtain a chloride ion (Cl.sup.) concentration in the filtrate, from which a total chloride ion amount eluted into 50 mL of the water is obtained, and is divided by the mass (g) of the specimen to provide a value, which is designated as the eluted chloride ion amount per unit mass.

Claims

1. An RFID tag substrate comprising a paper substrate having an eluted chloride ion amount per unit mass (1 g) according to the following item (A) of 0.100 mg or less, having formed on a surface thereof a conduction circuit: (A) a specimen of the paper substrate having an area corresponding to an A4 size (210297 mm) determined in ISO 216 is broken into small pieces each of 100 mm.sup.2 or less; the small pieces are entirely placed in a polypropylene vessel; 50 mL of water having an electric conductivity of 0.2 mS/m or less is added thereto to immerse the small pieces entirely into the water; after allowing to stand at 23 C.2 C. for 1 hour, the water is filtered with a membrane filter to recover a filtrate; and the filtrate is analyzed by an ion chromatography method to obtain a chloride ion (Cl.sup.) concentration in the filtrate, from which a total chloride ion amount eluted into 50 mL of the water is obtained, and is divided by the mass (g) of the specimen of the paper substrate to provide a value, which is designated as the eluted chloride ion amount per unit mass.

2. The RFID tag substrate according to claim 1, wherein the RFID tag substrate is for mounting an IC chip having a metallic bump coated with noble metal plating.

3. The RFID tag substrate according to claim 2, wherein the metal coated with noble metal plating is nickel.

4. The RFID tag substrate according to claim 1, wherein the conduction circuit contains a silver conductive film.

5. An RFID tag comprising an RFID tag substrate containing a paper substrate having an eluted chloride ion amount per unit mass (1 g) according to the following item (A) of 0.100 mg or less, having formed on a surface thereof a conduction circuit, and bonded thereto an IC chip having a metallic bump coated with noble metal plating, the conduction circuit and the metallic bump of the IC chip being electrically connected to each other: (A) a specimen of the paper substrate having an area corresponding to an A4 size (210297 mm) determined in ISO 216 is broken into small pieces each of 100 mm.sup.2 or less; the small pieces are entirely placed in a polypropylene vessel; 50 mL of water having an electric conductivity of 0.2 mS/m or less is added thereto to immerse the small pieces entirely into the water; after allowing to stand at 23 C.2 C. for 1 hour, the water is filtered with a membrane filter to recover a filtrate; and the filtrate is analyzed by an ion chromatography method to obtain a chloride ion (Cl.sup.) concentration in the filtrate, from which a total chloride ion amount eluted into 50 mL of the water is obtained, and is divided by the mass (g) of the specimen of the paper substrate to provide a value, which is designated as the eluted chloride ion amount per unit mass.

6. The RFID tag according to claim 5, wherein the metal coated with gold plating constituting the bump of the IC chip is nickel.

7. The RFID tag according to claim 5, wherein the conduction circuit constituting an antenna contains a silver conductive film.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0015] FIG. 1 is an illustration schematically exemplifying a cross sectional structure of an RFID tag having an IC chip having bumps mounted thereon.

[0016] FIG. 2 is an illustration schematically exemplifying a cross sectional structure of an RFID tag having an IC chip having noble metal plated type bumps mounted thereon.

[0017] FIG. 3 is an illustration showing an example of an antenna circuit pattern of an RFID tag.

[0018] FIG. 4 is a graph showing the eluted chloride ion amount per unit mass of the paper substrate and the communication distance retention ratio of the RFID tag using the same.

[0019] FIG. 5 is a graph showing the eluted sulfate ion amount per unit mass of the paper substrate and the communication distance retention ratio of the RFID tag using the same.

[0020] FIG. 6 is a graph showing the eluted chloride ion amount per unit mass of the paper substrate and the communication distance after the weather resistance test of the RFID tag using the same.

DESCRIPTION OF EMBODIMENTS

[0021] As described above, in the case where an IC tag having a noble metal plated type bump as shown in FIG. 2 is used in an RFID tag containing a paper substrate having an antenna circuit formed on the surface thereof, the bump is often corroded depending on the use environment, and there are cases where drastic decrease of the communication distance occurs in the early stage. According to the research by the inventors, it has been found that the corrosion of the bump of this type occurs due to bimetallic corrosion (galvanic corrosion), in which a local cell is formed between the noble metal plated layer and the internal metal member, which is more negative than the noble metal, and the internal metal as a base metal is dissolved. The corrosion of the bump increases the electric resistance to the antenna circuit, and thereby the performance of the antenna is deteriorated. The presence of a pinhole as a coating defect is unavoidable in the noble metal plated layer, and it is considered that the noble metal plated layer and the internal metal member are connected to each other through the pinhole with a water film caused by water attached to the article or moisture in the air, thereby forming a local cell.

[0022] Even an IC chip that causes no problem in an RFID tag using a resin substrate often undergoes bimetallic corrosion when the IC chip is applied to an RFID tag using a paper substrate. It is considered therefrom that the paper substrate, which is liable to contain water as compared to the resin substrate, becomes a cause of bimetallic corrosion of the bump. On the other hand, the progress of bimetallic corrosion is also largely influenced by the factor of the corrosion environment, i.e., the amount of the ion species (electrolytes) that facilitate the progress of corrosion contained in the aqueous solution in contact with both the metals. There is a high possibility that the ion species are supplied from the paper substrate containing water.

[0023] Under the circumstances, the inventors have made accumulated investigations for finding the relationship among the kind and the amount of the ion source substances contained in the paper substrate and the corrosion of the bump. As a result, it has been found that the amount of a chloride ion (Cl.sup.) supplied from the paper substrate largely influences the bimetallic corrosion of the bump. Specifically, it has been found that the bimetallic corrosion of the bump can be significantly prevented by mounting an IC chip having a noble metal plated type bump on a paper substrate that has an eluted chloride ion amount per unit mass according to the item (A) of 0.100 mg or less. Accordingly, the weather resistance of the RFID tag containing an IC chip having a noble metal plated type bump mounted on a paper substrate antenna can be significantly improved. The use of the paper substrate that has an eluted chloride ion amount per unit mass according to the item (A) of 0.060 mg or less is more effective, and the use of the paper substrate that has an eluted chloride ion amount of 0.050 mg or less is further preferred.

[0024] The operation of breaking the paper substrate specimen into small pieces each of 100 mm.sup.2 or less according to the item (A) is preferably performed by fingers wearing gloves for clean room operations or the like, for preventing contamination. In the case where the paper is broken into small pieces each of 100 mm.sup.2 or less by fingers wearing gloves of this type, the sizes of the small pieces may be generally in a range of from 25 to 100 mm.sup.2. When the sizes of the small pieces broken by fingers are in the range, the influence of the sizes of the paper pieces on fluctuation of the analysis values can be ignored.

[0025] The influence of a sulfate ion (SO.sub.4.sup.2-) among the ion species supplied from the paper substrate has also been investigated. As a result, it has been found that the significant improvement effect of the weather resistance can be basically obtained when the eluted chloride ion amount per unit mass of the paper substrate is sufficiently suppressed, and the influence of a sulfate ion is small. From the standpoint of achieving higher reliability, the eluted sulfate ion amount per unit mass according to the following item (B) is preferably 0.800 mg or less.

[0026] (B) A specimen of the paper substrate having an area corresponding to an A4 size (210297 mm) determined in ISO 216 is broken into small pieces each of 100 mm.sup.2 or less; the small pieces are entirely placed in a polypropylene vessel; 50 mL of water having an electric conductivity of 0.2 mS/m or less is added thereto to immerse the small pieces entirely into the water; after allowing to stand at 23 C.2 C. for 1 hour, the water is filtered with a membrane filter to recover a filtrate; and the filtrate is analyzed by an ion chromatography method to obtain a sulfate ion (SO.sub.4.sup.2-) concentration in the filtrate, from which a total sulfate ion amount eluted into 50 mL of the water is obtained, and is divided by the mass (g) of the specimen of the paper substrate to provide a value, which is designated as the eluted sulfate ion amount per unit mass.

[0027] In this case, when the sizes of the small pieces broken by fingers are in the aforementioned range, the influence of the sizes of the paper pieces on fluctuation of the analysis values can be ignored, as similar to the case of the item (A).

Example

[0028] The substrates in the form of a sheet shown in Table 1 were prepared. The substrate No. 9 is PET (polyethylene terephthalate), and the others are paper. The paper substrates include products of plural manufacturers.

TABLE-US-00001 TABLE 1 Mass of A4 Substrate size paper No. Material (g) Characteristics 1 paper 3.0180 resin coated paper with good dust generation prevention capability 2 paper 3.0568 neutral interleaving paper 3 paper 3.1035 acidic interleaving paper using aluminum nitrate 4 paper 4.3174 neutral paper 5 paper 5.6138 neutral paper added with special chemical 6 paper 8.3147 high smooth paper 7 paper 4.9651 resin coated paper suitable for lid material 8 paper 4.8748 universal copy paper 9 PET PET sheet subjected to easy adhesion treatment with good adhesiveness 10 paper 4.3839 dust generation prevented paper with reduced resin coating amount 11 paper 5.1942 water resistant paper used for yogurt container, etc. 12 paper 5.2746 high dimensional stability paper having strengthening agent fixed to fibers with aluminum nitrate 13 paper 8.8737 base paper for coating with high water resistance 14 paper 4.0650 paper with good dust generation prevention property subjected to acidic treatment 15 paper 5.8494 resin coated paper 16 paper 8.2329 highly designed paper suitable for decoration

Measurement of Eluted Ion Concentration

[0029] The paper substrates were measured for the eluted chloride ion amount per unit mass (1 g) of the paper substrate by a method according to the item (A). Specifically, for example, the chloride ion concentration in the filtrate by ion chromatography was 1.60 ppm for the substrate No. 1. Thus, 0.0016 mg of chloride ions are present in 1 mL of the filtrate. The total amount of chloride ions eluted in 50 mL of water added is 0.001650=0.080 mg. The mass of the A4 size paper substrate No. 1 used in the elution test is 3.018 g, and thus the eluted chloride ion amount per unit mass (1 g) is obtained as 0.080/3.0180.0265 mg.

[0030] The eluted sulfate ion amount per unit mass of the paper substrate was measured by a method according to the item (B).

[0031] The operation of breaking the paper substrate specimen into small pieces was performed by wearing powder-free nitrile gloves for clean room operation (Clean Nol Nitrile Gloves, produced by AS ONE Corporation).

[0032] The analysis by the ion chromatography method was performed by using IC 25, produced by Dionex, under the following conditions.

[0033] Column: Dionex IonPac AS12A

[0034] Column oven temperature: 35 C.

[0035] Flow rate of eluent: 1.5 mL/min

[0036] Suppressor current: 50 mA

Production RFID Tag Substrate

[0037] As a conductive paint, a silver ink (Model PFI-700, produced PChem Associates, Inc.) containing 60% by mass of silver particles having a primary average particle diameter of 15 nm and a secondary average particle diameter of 340 nm, 3.0% by mass of a vinyl chloride copolymer latex, 2.0% by mass of a polyurethane thickener, and 2.5% by mass of propylene glycol was prepared. The silver ink was printed on the surfaces of the paper substrates with a sheet feed flexographic printer (produced by Nihon Denshi Seiki Co., Ltd.) and a flexographic plate under condition of an anilox volume of 8 cm.sup.3/m.sup.2, so as to draw an antenna having the circuit pattern shown in FIG. 3. The circuit pattern is designed to adapt to the IC chip described later. The drawn area of the antenna is 8 mm94 mm, and the line width thereof is approximately 0.6 mm. The antenna after drawing was baked by performing a heat treatment at 155 C. for 30 seconds on a hot plate, thereby forming a conduction circuit having an antenna shape formed of a silver conductive film having an average thickness of from 0.5 to 1.0 m, and thus the RFID tag substrate was obtained.

Production of RFID Tag

[0038] As an IC chip, Monza4, produced by Impinj, Inc., was prepared. The IC chip has a noble metal plated type bump containing nickel having gold plating on the surface thereof. An anisotropic conductive paste (ACP) (TAP0604C, produced by Kyocera Chemical Corporation) containing Au/Ni coated polymer particles was thinly coated on the portion on the RFID tag substrate where the IC chip was to be bonded (i.e., the vicinity of the bump position). The IC chip was disposed on the ACP and then bonded under pressure for 10 seconds by applying a load of 1.0 N at 160 C. with a heat compression bonding machine (TTS300, produced by Muhlbauer AG), thereby mounting the IC chip on the RFID tag substrate, and thus an RFID tag was obtained.

Measurement of Communication Distance

[0039] The RFID tags thus produced above were measured for the communication distance (theoretical communication distance forward) in a frequency range of from 800 to 1,100 MHz (according to ISO/IEC 18000-6C) in a radio black box (MY1530, produced by Micronics Japan Co., Ltd.) with a communication distance measuring device (Tagformance, produced by Voyantic, Ltd.). Before the measurement, the environmental setting (setting with the reference tag attached to Tagformance) was performed under the condition.

[0040] Subsequently, the RFID tags were subjected to an accelerated weather resistance test by retaining in a thermo-hygrostat chamber under condition of 85 C. and 85% RH for 168 hours, and then measured for the communication distance in the same manner as above.

[0041] The communication distance before the accelerated weather resistance test is referred to as an initial communication distance, and the communication distance after the accelerated weather resistance test is referred to as a communication distance after weather resistance test. Herein, the measured values at 920 MHz were used as the initial communication distance and the communication distance after weather resistance test of the RFID tags, and the communication distance retention ratio before and after the accelerated weather resistance test was obtained by substituting the values into the following expression (1).

(communication distance retention ratio (%))=((communication distance after weather resistance test (m))/(initial communication distance (m)))100(1)

[0042] The communication distance retention ratio that is 80% or more can be evaluated to provide practically excellent weather resistance as an RFID tag using a paper substrate. Accordingly, one having a communication distance retention ratio of 80% or more was determined as (good weather resistance), and the others were determined as x (poor weather resistance).

[0043] The results are shown in Table 2. FIG. 4 shows the eluted chloride ion amount per unit mass of the paper substrate and the communication distance retention ratio of the RFID tag using the same. FIG. 5 shows the eluted sulfate ion amount per unit mass of the paper substrate and the communication distance retention ratio of the RFID tag using the same. FIG. 6 shows the eluted chloride ion amount per unit mass of the paper substrate and the communication distance after the weather resistance test of the RFID tag using the same.

TABLE-US-00002 TABLE 2 Eluted ion amount per unit mass of substrate Communication distance Communication (mg/1 g substrate) (920 MHz) (m) distance- Evaluation Substrate Chloride Sulfate After weather retention ratio of weather No. ion ion Initial resistance test *1 (%) resistance Class 1 0.0265 0.116 2.00 1.72 86 invention 2 0.0245 0.0082 3.51 3.18 91 3 0.0193 0.156 4.48 4.15 93 4 0.0336 0.0116 3.60 3.20 89 5 0.0187 0.0143 2.39 2.12 89 6 0.0192 0.307 3.20 2.73 85 7 0.0423 0.691 6.07 5.93 98 8 0.113 0.380 5.88 0.70 12 X comparison 9 4.97 4.77 96 10 0.730 0.0833 0.00 0.00 0 X 11 0.125 1.155 5.59 0.00 0 X 12 1.232 0.550 0.44 0.02 5 X 13 1.521 0.676 4.73 0.00 0 X 14 0.972 0.283 3.31 0.28 8 X 15 0.291 0.385 4.95 0.00 0 X 16 1.215 0.0134 2.96 0.00 0 X *1: 0% for initial read distance of 0.00 m

[0044] It is understood from Table 2 and FIGS. 4 and 6 that the use of the paper substrate having an eluted chloride ion amount per unit mass according to the item (A) of 0.100 mg or less significantly enhances the weather resistance on mounting an IC chip having a noble metal plated type bump. It is understood from Table 2 and FIG. 5 that the paper substrate having a sufficiently low eluted chloride ion concentration exhibits good weather resistance even though the eluted sulfate ion amount per unit mass according to the item (B) is increased close to 0.800 mg.

REFERENCE SIGN LIST

[0045] 1 substrate [0046] 2 conduction circuit [0047] 3 RFID tag substrate [0048] 4 bump [0049] 5 IC chip [0050] 6 conductive adhesive [0051] 7 internal metal member [0052] 8 noble metal plated layer