COMPOSITE ABRASIVE WITH HARD CORE AND SOFT SHELL, MANUFACTURING METHOD AND APPLICATION METHOD

Abstract

Disclosed is a composite abrasive with hard core and soft shell, comprising hard abrasive core with grain diameter in a range of 0.11 m and a soft oxide shell with thickness in a range of 5100 nm, the grain size of the oxide of the soft oxide shell is in a range of 520 nm, the composite abrasive is obtained from aqueous solution of oxide inorganic salt precursor and the hard abrasive by dispersing, constant temperature reflux hydrolyzing, solid-liquid separating, washing and drying. The component abrasive with hard core and soft shell of the present invention can improve the manufacturing efficiency and the surface quality during the ultraprecise manufacturing of the sapphire substrate.

Claims

1. A composite abrasive with hard core and soft shell, wherein comprising hard abrasive core with grain diameter in a range of 0.11 m and a soft oxide shell with thickness in a range of 5100 nm, the grain size of the oxide of the soft oxide shell is in a range of 520 nm, the composite abrasive is obtained from aqueous solution of oxide inorganic salt precursor and the hard abrasive by dispersing, constant temperature reflux hydrolyzing, solid-liquid separating, washing and drying.

2. The composite abrasive with hard core and soft shell according to claim 1, wherein the hard abrasive core comprises at least one kind selected from diamond, cBN, B.sub.4C, SiC and Al.sub.2O.sub.3.

3. The composite abrasive with hard core and soft shell according to claim 1, wherein the oxide comprises at least one kind selected from SnO.sub.2, CeO.sub.2, MgO, FeO and Fe.sub.2O.sub.3.

4. The composite abrasive with hard core and soft shell according to claim 3, wherein the inorganic salt precursor comprises at least one kind selected from chlorine salt, nitrate and sulfate.

5. A manufacturing method of the composite abrasive with hard core and soft shell according to claim 1, wherein comprising the steps: (1) preparing aqueous solution of oxide inorganic salt precursor with concentration of 0.11 mol/L by solving the oxide inorganic salt precursor in deionized water; (2) putting hard abrasive into the aqueous solution, the mass concentration of the hard abrasive in the aqueous solution is in a range of 110%; (3) ultrasonic dispersing the material of step (2) for 1015 minutes to obtain stable emulsion; (4) the emulsion is reflux hydrolyzed in a constant temperature of 6090 C. for 872 hours; (5) the material of step (4) is solid-liquid separated, the solid is washed by distilled water and absolute ethyl alcohol; (6) drying the solid of step (5) in 4045 C. to obtain the composite abrasive with hard core and soft shell.

6. The manufacturing method according to claim 5, wherein in step (5), the material of step (4) is vacuum filtered, the obtained solid is washed by distilled water for 5 times and washed by absolute ethyl alcohol for 3 times in turn.

7. The manufacturing method according to claim 5, wherein in step (6), the drying period is 2030 hours.

8. An application method of the composite abrasive with hard core and soft shell according to claim 1, the composite abrasive is applied in the ultraprecise polishing sapphire wafers.

9. A manufacturing method of the composite abrasive with hard core and soft shell according to claim 2, wherein comprising the steps: (1) preparing aqueous solution of oxide inorganic salt precursor with concentration of 0.11 mol/L by solving the oxide inorganic salt precursor in deionized water; (2) putting hard abrasive into the aqueous solution, the mass concentration of the hard abrasive in the aqueous solution is in a range of 110%; (3) ultrasonic dispersing the material of step (2) for 1015 minutes to obtain stable emulsion; (4) the emulsion is reflux hydrolyzed in a constant temperature of 6090 C. for 872 hours; (5) the material of step (4) is solid-liquid separated, the solid is washed by distilled water and absolute ethyl alcohol; (6) drying the solid of step (5) in 4045 C. to obtain the composite abrasive with hard core and soft shell.

10. A manufacturing method of the composite abrasive with hard core and soft shell according to claim 3, wherein comprising the steps: (1) preparing aqueous solution of oxide inorganic salt precursor with concentration of 0.11 mol/L by solving the oxide inorganic salt precursor in deionized water; (2) putting hard abrasive into the aqueous solution, the mass concentration of the hard abrasive in the aqueous solution is in a range of 110%; (3) ultrasonic dispersing the material of step (2) for 1015 minutes to obtain stable emulsion; (4) the emulsion is reflux hydrolyzed in a constant temperature of 6090 C. for 872 hours; (5) the material of step (4) is solid-liquid separated, the solid is washed by distilled water and absolute ethyl alcohol; (6) drying the solid of step (5) in 4045 C. to obtain the composite abrasive with hard core and soft shell.

11. A manufacturing method of the composite abrasive with hard core and soft shell according to claim 4, wherein comprising the steps: (1) preparing aqueous solution of oxide inorganic salt precursor with concentration of 0.11 mol/L by solving the oxide inorganic salt precursor in deionized water; (2) putting hard abrasive into the aqueous solution, the mass concentration of the hard abrasive in the aqueous solution is in a range of 110%; (3) ultrasonic dispersing the material of step (2) for 1015 minutes to obtain stable emulsion; (4) the emulsion is reflux hydrolyzed in a constant temperature of 6090 C. for 872 hours; (5) the material of step (4) is solid-liquid separated, the solid is washed by distilled water and absolute ethyl alcohol; (6) drying the solid of step (5) in 4045 C. to obtain the composite abrasive with hard core and soft shell.

12. The manufacturing method according to claim 9, wherein in step (5), the material of step (4) is vacuum filtered, the obtained solid is washed by distilled water for 5 times and washed by absolute ethyl alcohol for 3 times in turn.

13. The manufacturing method according to claim 10, wherein in step (5), the material of step (4) is vacuum filtered, the obtained solid is washed by distilled water for 5 times and washed by absolute ethyl alcohol for 3 times in turn.

14. The manufacturing method according to claim 11, wherein in step (5), the material of step (4) is vacuum filtered, the obtained solid is washed by distilled water for 5 times and washed by absolute ethyl alcohol for 3 times in turn.

15. The manufacturing method according to claim 9, wherein in step (6), the drying period is 2030 hours.

16. The manufacturing method according to claim 10, wherein in step (6), the drying period is 2030 hours.

17. The manufacturing method according to claim 11, wherein in step (6), the drying period is 2030 hours.

18. An application method of the composite abrasive with hard core and soft shell according to claim 2, the composite abrasive is applied in the ultraprecise polishing sapphire wafers.

19. An application method of the composite abrasive with hard core and soft shell according to claim 3, the composite abrasive is applied in the ultraprecise polishing sapphire wafers.

20. An application method of the composite abrasive with hard core and soft shell according to claim 4, the composite abrasive is applied in the ultraprecise polishing sapphire wafers.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0018] FIG. 1 illustrates a schematic diagram of the composite abrasive with hard core and soft shell of the present invention.

[0019] FIG. 2 illustrates a stereoscan photograph of the diamond abrasive of the first embodiment of the present invention.

[0020] FIG. 3 illustrates a stereoscan photograph of the composite abrasive with hard core and soft shell of the first embodiment of the present invention.

[0021] FIG. 4 illustrates a profile of sapphire before polishing by the composite abrasive with hard core and soft shell of the first embodiment of the present invention.

[0022] FIG. 5 illustrates a profile of sapphire polished by the composite abrasive with hard core and soft shell of the first embodiment of the present invention.

[0023] FIG. 6 illustrates a transmission electron microscope of the composite abrasive with hard core and soft shell of the third embodiment of the present invention.

DETAILED DESCRIPTION OF THE EMBODIMENTS

[0024] The present invention will be further described with the drawings and the embodiments.

The First Embodiment

[0025] (1) preparing 300 mL of ferric oxide solution with concentration of 1 mol/L by solving ferric chloride in deionized water; [0026] (2) putting 4.5 g of W1 diamond abrasive into the ferric oxide solution, as figured in FIG. 2; [0027] (3) ultrasonic dispersing the material of step (2) for 10 minutes to obtain stable emulsion; [0028] (4) the emulsion is reflux hydrolyzed in a constant temperature bath of 90 C. for 48 hours; [0029] (5) the material of step (4) is vacuum filtered, the obtained solid is washed by distilled water for 5 times and washed by absolute ethyl alcohol for 3 times in turn. [0030] (6) drying the solid of step (5) in 40 C. for 24 hours to obtain the composite abrasive with hard core and soft shell, as figured in FIG. 1 and FIG. 3, the composite abrasive comprising diamond abrasive core with grain diameter 1 m and a soft ferric oxide shell with thickness about 100 nm, the grain size of the ferric oxide of the shell is about 10 nm.

[0031] Above obtained composite abrasive with hard core and soft shell is applied in semisolidification flexible polishing tools to mechano-chemical polish sapphire wafer to obtain a sub-nanometer surface finish quality with Ra 0.8 nm, the before and after of the manufacturing are figured in FIG. 4 and FIG. 5.

The Second Embodiment

[0032] (1) preparing 200 mL of magnesium nitrate solution with concentration of 0.2 mol/L by solving magnesium nitrate in deionized water; [0033] (2) putting 2 g of W0.5 aluminum oxide abrasive into the magnesium nitrate solution; [0034] (3) ultrasonic dispersing the material of step (2) for 10 minutes to obtain stable emulsion; [0035] (4) the emulsion is reflux hydrolyzed in a constant temperature bath of 60 C. for 24 hours; [0036] (5) the material of step (4) is vacuum filtered, the obtained solid is washed by distilled water for 5 times and washed by absolute ethyl alcohol for 3 times in turn. [0037] (6) drying the solid of step (5) in 40 C. for 24 hours to obtain the composite abrasive with hard core and soft shell, as figured in FIG. 1, the composite abrasive comprising aluminum oxide abrasive core with grain diameter 0.5 m and a soft magnesium oxide shell with thickness about 20 nm, the grain size of the magnesium oxide of the shell is about 8 nm

[0038] Above obtained composite abrasive with hard core and soft shell is applied in semisolidification flexible polishing tools to mechano-chemical polish sapphire wafer, the surface roughness Ra of the polished sapphire is 0.6 nm.

The Third Embodiment

[0039] (1) preparing 250 mL of ferrous sulfate solution with concentration of 0.2 mol/L by solving ferrous sulfate in deionized water; [0040] (2) putting 5 g of W0.25 cubic boron nitride abrasive into the ferrous sulfate solution; [0041] (3) ultrasonic dispersing the material of step (2) for 15 minutes to obtain stable emulsion; [0042] (4) the emulsion is reflux hydrolyzed in a constant temperature bath of 85 C. for 36 hours; [0043] (5) the material of step (4) is vacuum filtered, the obtained solid is washed by distilled water for 5 times and washed by absolute ethyl alcohol for 3 times in turn. [0044] (6) drying the solid of step (5) in 45 C. for 20 hours to obtain the composite abrasive with hard core and soft shell, as figured in FIG. 1 and FIG. 6, the composite abrasive comprising cubic boron nitride abrasive core with grain diameter 0.25 m and a soft ferrous sulfate shell with thickness about 15 nm, the grain size of the ferrous sulfate of the shell is about 5 nm.

[0045] Above obtained composite abrasive with hard core and soft shell is applied in semisolidification flexible polishing tools to mechano-chemical polish sapphire wafer, the surface roughness Ra of the polished sapphire is 0.4 nm.

The Fourth Embodiment

[0046] (1) preparing 200 mL of cerous nitrate solution with concentration of 0.5 mol/L by solving cerous nitrate in deionized water; [0047] (2) putting 10 g of W0.5 boron carbide into the cerous nitrate solution; [0048] (3) ultrasonic dispersing the material of step (2) for 10 minutes to obtain stable emulsion; [0049] (4) the emulsion is reflux hydrolyzed in a constant temperature bath of 70 C. for 54 hours; [0050] (5) the material of step (4) is vacuum filtered, the obtained solid is washed by distilled water for 5 times and washed by absolute ethyl alcohol for 3 times in turn. [0051] (6) drying the solid of step (5) in 45 C. for 20 hours to obtain the composite abrasive with hard core and soft shell, as figured in FIG. 1, the composite abrasive comprising boron carbide abrasive core with grain diameter 0.5 m and a soft cerium oxide shell with thickness about 60 nm, the grain size of the cerium oxide of the shell is about 15 nm.

[0052] Above obtained composite abrasive with hard core and soft shell is applied in semisolidification flexible polishing tools to mechano-chemical polish sapphire wafer, the surface roughness Ra of the polished sapphire is 0.9 nm.

The Fifth Embodiment

[0053] (1) preparing 300 mL of stannic chloride solution with concentration of lmol/L by solving stannic chloride in deionized water; [0054] (2) putting 6 g of W1 silicon carbide into the stannic chloride solution; [0055] (3) ultrasonic dispersing the material of step (2) for 10 minutes to obtain stable emulsion; [0056] (4) the emulsion is reflux hydrolyzed in a constant temperature bath of 60 C. for 16 hours; [0057] (5) the material of step (4) is vacuum filtered, the obtained solid is washed by distilled water for 5 times and washed by absolute ethyl alcohol for 3 times in turn. [0058] (6) drying the solid of step (5) in 40 C. for 30 hours to obtain the composite abrasive with hard core and soft shell, as figured in FIG. 1, the composite abrasive comprising silicon carbide abrasive core with grain diameter 1 m and a soft stannic oxide shell with thickness about 20 nm, the grain size of the stannic oxide of the shell is about 5 nm.

[0059] Above obtained composite abrasive with hard core and soft shell is applied in semisolidification flexible polishing tools to mechano-chemical polish sapphire wafer, the surface roughness Ra of the polished sapphire is 1.3 nm.

[0060] A person skilled in this field knows that regulating the components and the parameters within the scope described hereafter can also obtain the similar technical effects to the embodiments, this kind of regulation is still within the scope of the present invention.

[0061] A composite abrasive with hard core and soft shell, comprising hard abrasive core with grain diameter in a range of 0.11 m and a soft oxide shell with thickness in a range of 5100 nm, the grain size of the oxide of the soft oxide shell is in a range of 520 nm.

the composite abrasive is obtained from aqueous solution of oxide inorganic salt precursor and the hard abrasive by dispersing, constant temperature reflux hydrolyzing, solid-liquid separating, washing and drying.

[0062] The hard abrasive core comprises at least one kind selected from diamond, cBN, B.sub.4C, SiC and Al.sub.2O.sub.3.

[0063] The oxide comprises at least one kind selected from SnO.sub.2, CeO.sub.2, MgO, FeO and Fe.sub.2O.sub.3.

[0064] The inorganic salt precursor comprises at least one kind selected from chlorine salt, nitrate and sulfate.

[0065] A manufacturing method of the composite abrasive with hard core and soft shell, comprising the steps: [0066] (1) preparing aqueous solution of oxide inorganic salt precursor with concentration of 0.11 mol/L by solving the oxide inorganic salt precursor in deionized water; [0067] (2) putting hard abrasive into the aqueous solution, the mass concentration of the hard abrasive in the aqueous solution is in a range of 110%; [0068] (3) ultrasonic dispersing the material of step (2) for 1015 minutes to obtain stable emulsion; [0069] (4) the emulsion is reflux hydrolyzed in a constant temperature of 6090 C. for 872 hours; (5) the material of step (4) is solid-liquid separated, the solid is washed by distilled water and absolute ethyl alcohol; [0070] (6) drying the solid of step (5) in 4045 C. to obtain the composite abrasive with hard core and soft shell.

[0071] Although the present invention has been described with reference to the preferred embodiments thereof for carrying out the patent for invention, it is apparent to those skilled in the art that a variety of modifications and changes may be made without departing from the scope of the patent for invention which is intended to be defined by the appended claims.