Coloring agent composition and method for producing same

Abstract

Provided is a coloring agent composition to be added to a gypsum-containing raw material powder constituting a gypsum product and to be used for coloring the gypsum product, the coloring agent composition being a powder containing a pigment, calcined gypsum, and amorphous silica. A process for producing the coloring agent composition includes a first step of mixing a pigment, calcined gypsum, and amorphous silica to obtain a mixed powder. Use of the coloring agent composition makes it possible to easily produce gypsum products such as a powder and a hardened body that are excellent in colorability.

Claims

1. A coloring agent composition to be added to a gypsum-containing raw material powder forming a gypsum product and to be used for coloring the gypsum product, the coloring agent composition consisting essentially of: a pigment; calcined gypsum; and amorphous silica, wherein the amorphous silica has a number average particle diameter in a range from 5 to 40 nm, the calcined gypsum is a hemihydrate gypsum, hemihydrate gypsum, or a mixture thereof, and the coloring agent composition is in a powder form.

2. The coloring agent composition according to claim 1, wherein a content of the amorphous silica is in a range from 0.01 to 1 part by mass relative to 1 part by mass of the pigment.

3. The coloring agent composition according to claim 1, wherein a content of the calcined gypsum is in a range from 1 to 100 parts by mass relative to 1 part by mass of the pigment.

4. The coloring agent composition according to claim 1, wherein the amorphous silica has a number average particle diameter in a range from 5 to 30 nm.

5. The coloring agent composition according to claim 1, wherein the pigment, the calcined gypsum, and the amorphous silica have been co-pulverized.

6. A process for producing the coloring agent composition according to claim 1, the process comprising: a first step of mixing the pigment, the calcined gypsum, and the amorphous silica so as to form a mixed powder.

7. The process for producing the coloring agent composition according to claim 6, wherein the pigment, the calcined gypsum, and the amorphous silica are pulverized concurrently with the mixing in the first step.

8. The process for producing the coloring agent composition according to claim 6, further comprising a second step of pulverizing the mixed powder.

9. The process for producing the coloring agent composition according to claim 6, wherein the calcined gypsum has a volume average particle diameter in a range from 20 to 200 m.

10. A colored gypsum powder composition for forming the gypsum product comprising: the coloring agent composition according to claim 1; and the gypsum-containing raw material powder.

11. A process for producing a colored gypsum powder composition, comprising: adding the coloring agent composition according to claim 1 to the gypsum-containing raw material powder.

12. A process for producing a gypsum product, comprising: adding the coloring agent composition according to claim 1 to the gypsum-containing raw material powder so as to form a colored gypsum power composition; forming a slurry of the colored gypsum power composition; and forming the gypsum product from the slurry.

Description

DESCRIPTION OF EMBODIMENTS

(1) Hereinafter, the embodiments according to the present invention will be described, however the present invention is not limited to the following embodiments.

(2) <Coloring Agent Composition>

(3) The coloring agent composition according to the present invention is a powder containing a pigment, calcined gypsum, and amorphous silica. And the coloring agent composition according to the present invention is added to a raw material powder containing gypsum that constitutes a gypsum product (matter to be colored), and is used as a coloring agent (so-called master batch) for coloring the gypsum product.

(4) (Pigment)

(5) The kind of a pigment to be used is not particularly limited, and pigments generally used for coloring industrial products and the like can be used. Specific examples of the pigment that can be used include: organic pigments such as azo pigments and polycyclic pigments; inorganic pigments such as natural mineral pigments and synthetic inorganic pigments; and so on.

(6) (Calcined Gypsum)

(7) The coloring agent composition according to the present invention contains calcined gypsum. The calcined gypsum is a powdered or particle component that can function as a base material. It is preferable that the content of the calcined gypsum in the coloring agent composition is 1 to 100 parts by mass relative to 1 part by mass of the pigment, more preferably 1 to 50 parts by mass. When the content of the calcined gypsum is less than 1 part by mass relative to 1 part by mass of the pigment, there is a tendency that colorability is difficult to improve and color unevenness is liable to occur in the colored gypsum hardened body to be obtained. Moreover, there is also a tendency that the kneading performance of the gypsum product (colored gypsum powder) with water gets worse in the case where the gypsum product is constituted from calcined gypsum. On the other hand, when the content of the calcined gypsum exceeds 100 parts by mass relative to 1 part by mass of the pigment, there is a tendency that the color unevenness is liable to occur in the colored gypsum hardened body.

(8) Examples of the kind of calcined gypsum include a hemihydrate gypsum, hemihydrate gypsum, and type III anhydrous gypsum. These kinds of calcined gypsum can be used alone or in combination of two or more.

(9) (Amorphous Silica)

(10) The coloring agent composition according to the present invention contains amorphous silica. By containing the amorphous silica, the coloring agent composition, when compared with the case where the amorphous silica is not contained, can be prepared so as to make the color unevenness difficult to occur in the colored gypsum hardened body and also make it possible to produce a gypsum product having a remarkably improved colorability. It is preferable that the content of the amorphous silica in the coloring agent composition is 0.01 to 1 part by mass relative to 1 part by mass of the pigment, more preferably 0.1 to 0.8 parts by mass. When the content of the amorphous silica is less than 0.01 parts by mass relative to 1 part by mass of the pigment, it becomes difficult to obtain effects due to blending of the amorphous silica. Thus, there is a tendency that the colorability of the gypsum product is difficult to improve and the color unevenness is liable to occur in the colored gypsum hardened body. On the other hand, when the content of the amorphous silica exceeds 1 part by mass relative to 1 part by mass of the pigment, there is a tendency that the effects hit the ceiling and disadvantage arises in terms of costs.

(11) It is preferable that the amorphous silica has a number average particle diameter of 5 to 40 nm, more preferably 5 to 30 nm. The amorphous silica having a number average particle diameter of less than 5 nm is difficult to handle and is substantially difficult to prepare or obtain because the particle diameter is too small. On the other hand, when the amorphous silica has a number average particle diameter of more than 40 nm, there is a tendency that the colorability of the gypsum product is difficult to improve and the color unevenness is liable to occur in the colored gypsum hardened body. In addition, the number average particle diameter of the amorphous silica in the present DESCRIPTION means the number average particle diameter of primary particles of the amorphous silica.

(12) (Other Components)

(13) Another component that is different from the above-mentioned respective components can be contained as necessary in the coloring agent composition according to the present invention. Examples of the another component that can be contained include, but not particularly limited to, additives that can generally be contained in gypsum products.

(14) <Method of Using Coloring Agent Composition>

(15) Use of the coloring agent composition according to the present invention makes it possible to easily produce a colored gypsum product. Hereinafter, an example of the method of using the coloring agent composition according to the present invention will be described taking the case where a dental model is produced as an example.

(16) In order to produce a colored teeth model, a raw material powder which contains gypsum that constitutes the teeth model is prepared in the first place. As the gypsum, the calcined gypsum, such as hemihydrate gypsum, hemihydrate gypsum, and type III anhydrous gypsum, that constitutes a general teeth model can be used as it is.

(17) Subsequently, the coloring agent composition according to the present invention is added to and mixed with the prepared raw material powder. The addition amount of the coloring agent composition may appropriately be set in consideration of the color, extent of coloration, cost, and so on of the teeth model intended to be produced. Specifically, the addition amount may be approximately 0.01 to 3 parts by mass relative to 100 parts by mass of the gypsum in the raw material powder. In addition, various additives including a hardening adjuster such as sodium citrate can be added to the raw material powder.

(18) The method of mixing the raw material powder and the coloring agent composition is not particularly limited. Specifically, mixing can be performed by a simple method such as placing the raw material powder and the coloring agent composition into a container or bag and shaking the resultant mixture. That is to say, use of the coloring agent composition according to the present invention makes it possible to produce a gypsum product (colored gypsum powder) in which the color unevenness hardly occurs and which is excellent in colorability without using a special mixing apparatus or the like. A colored gypsum slurry can be obtained by adding an appropriate amount of mixing water and stirring the resultant mixture after mixing the raw material powder and the coloring agent composition. And a teeth model which is excellent in colorability, in which the color unevenness does not occur, and which is uniformly colored can be produced by pouring the obtained gypsum slurry into a female impression of teeth, thereafter hardening the gypsum slurry, and removing the impression of teeth.

(19) As mentioned above, use of the coloring agent composition according to the present invention makes it possible to produce, through a simple process, a colored gypsum powder and a colored gypsum hardened body which are excellent in colorability and which are uniformly colored without causing the color unevenness. In addition, the gypsum product that can be produced with the coloring agent composition according to the present invention is not limited to gypsum hardened bodies such as a teeth model and an industrial model, and, for example, liquid or semi-liquid gypsum products such as building materials including gypsum plasters and pate, and powdered gypsum products can also be produced.

(20) <Process for Producing Coloring Agent Composition>

(21) Next, the process for producing a coloring agent composition according to the present invention will be described. The method for producing a coloring agent composition according to the present invention includes a first step of mixing a pigment, calcined gypsum, and amorphous silica to obtain a mixed powder. Hereinafter, the details will be described.

(22) (First Step)

(23) In the first step, a pigment, calcined gypsum, and amorphous silica are mixed to obtain a mixed powder. The mixed powder thus obtained can be used as it is as a coloring agent composition. It is preferable that the calcined gypsum used in this case has a volume average particle diameter of 20 to 200 m, more preferably 20 to 100 m. Use of the calcined gypsum having a volume average particle diameter within the above-described numerical value range makes it possible to obtain a coloring agent composition capable of producing a gypsum product in which the color unevenness is more difficult to occur and which is more excellent in colorability.

(24) It is preferable that the pigment, the calcined gypsum, and the amorphous silica are separately pulverized in advance to be in a powdered form or a granular form. In order to separately pulverize the pigment, the calcined gypsum, and the amorphous silica, a general pulverizer or the like for pulverizing a powder or a granular product can be used. Specific examples of such a pulverizer include pulverizers (such as a ball mill) that make use of the action of collision or friction using a medium and pulverizers (such as an atomizer) that make use of the action of impact/grinding/shearing. In addition, pulverization can simply be performed by using a juicer-mixer in a table test scale. Moreover, any of batch type pulverizers and one path type pulverizers can be used.

(25) In order to mix the pigment, the calcined gypsum, and the amorphous silica, a general mixer or the like for uniformly mixing a powder can be used. Moreover, the pigment, the calcined gypsum, and the amorphous silica may be mixed by shaking a container or bag in which these components are placed. In addition, specific examples of the mixer include a ribbon mixer, a Nauta mixer, a V type mixer, a paddle mixer, and so on.

(26) In the first step, it is preferable that the pigment, the calcined gypsum, and the amorphous silica are pulverized concurrently with being mixed, namely it is preferable to co-pulverize the pigment, the calcined gypsum, and the amorphous silica. By performing co-pulverization, the calcined gypsum is mixed with the amorphous silica concurrently with being pulverized, making it possible to obtain a coloring agent composition capable of producing a gypsum product in which the color unevenness is more difficult to occur and, furthermore, which is more excellent in colorability as compared with the case where the calcined gypsum and the amorphous silica are simply mixed not through a pulverizer.

(27) In order to co-pulverize the pigment, the calcined gypsum, and the amorphous silica, a general dry pulverizer that is capable of pulverizing a powder concurrently with mixing can be used. Specific examples on the general dry pulverizer include the above-mentioned pulverizers (such as a ball mill) that make use of the action of collision or friction using a medium and pulverizers (such as an atomizer) that make use of the action of impact/grinding/shearing. In addition, co-pulverization can simply be performed by using a juicer-mixer in a table test scale. Moreover, any of batch type pulverizers and one path type pulverizers can be used. The pulverization time is different depending on the amounts of the pigment, the calcined gypsum, and the amorphous silica, the pulverization facilities, and, in the pulverizer using a medium, the material quality, size, weight, and so on of the medium, however the effects due to co-pulverization are exhibited even in an extremely short pulverization time.

(28) The order of supplying the pigment, the calcined gypsum, and the amorphous silica to a pulverizer is different depending on the pulverization system of the pulverizer to be used, but can appropriately be selected. In the case, for example, where a pulverizer is used which completes pulverization in a short time as short as approximately a few seconds, it is preferable to simultaneously supply the pigment, the calcined gypsum, and the amorphous silica. On the other hand, in the case where a pulverizer is used which completes pulverization in a few tens of seconds or more, the pigment, the calcined gypsum and the amorphous silica can be supplied in an arbitrary order.

(29) (Second Step)

(30) It is preferable that the process for producing a coloring agent composition according to the present invention further includes a second step of pulverizing the mixed powder obtained in the above-mentioned first step. By further pulverizing the mixed powder obtained in the first step, the same effects as obtained by the co-pulverization can be obtained. Furthermore, as mentioned above, the calcined gypsum is mixed with the amorphous silica concurrently with being pulverized, making it possible to obtain a coloring agent composition capable of producing a gypsum product in which the color unevenness is more difficult to occur, and, furthermore, which is more excellent in colorability as compared with the case where the calcined gypsum and the amorphous silica are simply mixed not through a pulverizer.

(31) In order to pulverize the mixed powder, a general pulverizer for pulverizing a powder, such as the one used in the first step, can be used, and a juicer-mixer can also be used in a table test in the same manner.

EXAMPLES

(32) Hereinafter, the present invention will be described specifically based on Examples, however the present invention is not limited to these Examples. It is to be noted that parts and % in Examples and Comparative Examples are based on mass unless otherwise noticed.

(33) (1) Regarding Number Average Particle Diameter of Amorphous Silica

Examples 1-1 to 1-5

(34) In a juicer-mixer (product number MX-X107, manufactured by Panasonic Corporation), 1 part of a pigment (ultramarine), 30 parts of hemihydrate gypsum (manufactured by Yoshino Gypsum Co., Ltd., volume average particle diameter: 50 m) as a base material, and 0.3 parts of amorphous silica having a number average particle diameter shown in Table 1 were placed, and mixed and pulverized for 60 seconds to prepare a coloring agent composition.

(35) In a plastic bag, 100 parts of hemihydrate gypsum as a raw material powder, 0.1 parts of a hardening adjuster (sodium citrate), and 0.3 parts of the produced coloring agent composition were placed and well shaken for 3 minutes to mix the contents, thereby preparing a colored gypsum powder to evaluate the colorability by the following method. Moreover, to the obtained colored gypsum powder, 24 parts of mixing water was added and mixed, then the resultant slurry was poured into a mold (diameter 50 mm10 mm) and hardened to prepare a colored gypsum hardened body, and the colorability and color unevenness were evaluated by the following methods.

(36) (Evaluation)

(37) [Colorability]

(38) A color difference meter (product name Color Meter ZE 2000 manufactured by Nippon Denshoku Industries Co., Ltd.) was used to measure the b values in a CIE LAB (L*a*b*) of the produced colored gypsum powders and colored gypsum hardened bodies, and the measured values were used to evaluate the colorability. The results are shown in Table 1.

(39) [Color Unevenness]

(40) The color unevenness was evaluated by visually observing the produced colored gypsum hardened bodies in accordance with the criteria shown below. The results are shown in Table 1. In addition, when the coloring agent composition aggregates, the aggregated portion is partially colored densely, so that the decision by visual observation becomes easy.

(41) Excellent: the area of the portion where the coloring agent composition aggregates is 5% or less of the whole surface of the colored gypsum hardened body.

(42) Good: the area of the portion where the coloring agent composition aggregates is more than 5% and 20% or less of the whole surface of the colored gypsum hardened body.

(43) Fair: the area of the portion where the coloring agent composition aggregates is more than 20% and 50% or less of the whole surface of the colored gypsum hardened body.

(44) Poor: the area of the portion where the coloring agent composition aggregates is more than 50% of the whole surface of the colored gypsum hardened body.

(45) TABLE-US-00001 TABLE 1 Examples 1-1 1-2 1-3 1-4 1-5 Pigment (parts) 1 Hemihydrate gypsum (parts) 30 Amorphous silica Blending amount (parts) 0.3 Number average particle 5 10 30 40 50 diameter (nm) Colorability Colored gypsum powder 15.0 14.7 14.3 14.3 13.5 (b value) Colored gypsum 28.6 28.0 27.6 27.3 27.0 hardened body Color unevenness Colored gypsum Excellent Excellent Excellent Good Fair hardened body

(46) As shown in Table 1, it is understood that the colorability of the colored gypsum powder and colored gypsum hardened body to be obtained is improved and the color unevenness of the colored gypsum hardened body is improved as the number average particle diameter of the amorphous silica is small.

(47) (2) Regarding Blending Amount of Amorphous Silica

Examples 2-1 to 2-6 and Comparative Example 1

(48) In a juicer-mixer (product number MX-X107, manufactured by Panasonic Corporation), 1 part of a pigment (ultramarine), 30 parts of hemihydrate gypsum (manufactured by Yoshino Gypsum Co., Ltd., volume average particle diameter: 50 m) as abase material, and amorphous silica (number average particle diameter: 30 nm) in a blending amount shown in Table 2 were placed, and mixed and pulverized for 60 seconds to prepare a coloring agent composition. Moreover, colored gypsum powders and colored gypsum hardened bodies were prepared and the colorability and color unevenness thereof were evaluated in the same manner as in the case of the aforementioned Examples 1-1 to 1-5. The results are shown in Table 2.

(49) TABLE-US-00002 TABLE 2 Comparative Example Examples 1 2-1 2-2 2-3 2-4 2-5 2-6 Pigment (parts) 1 Hemihydrate gypsum (parts) 30 Amorphous silica (parts) 0 0.01 0.1 0.5 0.8 1 1.5 Colorability Colored gypsum powder 10.0 13.2 14.0 15.0 15.2 15.2 15.2 (b value) Colored gypsum 24.6 26.5 27.9 28.1 28.6 28.4 28.1 hardened body Color unevenness Colored gypsum Poor Fair Good Excellent Excellent Excellent Excellent hardened body

(50) As shown in Table 2, it is understood that the colorability-improving effect and the color unevenness-improving effect are weak when the content of the amorphous silica is small. In addition, when the content of the amorphous silica is large, the colorability-improving effect and the color unevenness-improving effect are sufficient, however the colored gypsum powder and the colored gypsum hardened body are disadvantageous in terms of costs in some cases.

(51) (3) Regarding Blending Amount of Calcined Gypsum

Examples 3-1 to 3-8 and Comparative Example 2

(52) In a juicer-mixer (product number MX-X107, manufactured by Panasonic Corporation), 1 part of a pigment (ultramarine), hemihydrate gypsum (manufactured by Yoshino Gypsum Co., Ltd., volume average particle diameter: 50 m) as a base material in a blending amount as shown in Table 3, and 0.3 parts of amorphous silica (number average particle diameter: 30 nm) were placed, and mixed and pulverized for 60 seconds to prepare a coloring agent composition. Moreover, colored gypsum powders and colored gypsum hardened bodies were prepared and the colorability and color unevenness thereof were evaluated in the same manner as in the case of the aforementioned Examples 1-1 to 1-5. The results are shown in Table 3.

(53) TABLE-US-00003 TABLE 3 Comparative Example Examples 2 3-1 3-2 3-3 3-4 3-5 3-6 3-7 3-8 Pigment (parts) 1 Amorphous silica (parts) 0.3 Hemihydrate gypsum (parts) 0 0.5 1 10 30 50 80 100 130 Colorability Colored gyspum powder 10.3 12.9 14.3 15.6 15.5 15.6 15.0 14.3 14.3 (b value) Colored gypsum 25.7 26.0 26.4 27.5 27.5 27.5 27.0 26.8 26.8 hardened body Color unevenness Colored gypsum Poor Fair Excellent Excellent Excellent Excellent Excellent Excellent Good hardened body

(54) As shown in Table 3, it is understood that the colorability-improving effect and the color unevenness-improving effect are weak when the content of hemihydrate gypsum is small. In addition, it is understood that there is a tendency that the color unevenness is liable to occur when the content of hemihydrate gypsum is too large.

(55) (4) Regarding Volume Average Particle Diameter of Calcined Gypsum

Examples 4-1 to 4-7

(56) In a juicer-mixer (product number MX-X107, manufactured by Panasonic Corporation), 1 part of a pigment (ultramarine), 30 parts of hemihydrate gypsum (manufactured by Yoshino Gypsum Co., Ltd.) as a base material having a volume average particle diameter as shown in Table 4, and 0.3 parts of amorphous silica (number average particle diameter: 30 nm) were placed, and mixed and pulverized for 60 seconds to prepare a coloring agent composition. Moreover, colored gypsum powders and colored gypsum hardened bodies were prepared and the colorability and color unevenness thereof were evaluated in the same manner as in the case of the aforementioned Examples 1-1 to 1-5. The results are shown in Table 4.

(57) TABLE-US-00004 TABLE 4 Examples 4-1 4-2 4-3 4-4 4-5 4-6 4-7 Pigment (parts) 1 Amorphous silica (parts) 0.3 Hemihydrate gypsum Blending amount (parts) 30 Volume average particle 10 20 50 100 150 200 250 diameter (m) Colorability Colored gypsum powder 13.3 14.0 15.0 15.0 14.3 13.9 13.4 (b value) Colored gypsum 26.8 26.5 28.6 28.4 28.4 26.8 27.0 hardened body Color unevenness Colored gypsum Fair Excellent Excellent Excellent Good Good Fair hardened body

(58) As shown in Table 4, it is understood that there is a tendency that the color unevenness is liable to occur when the volume average particle diameter of hemihydrate gypsum is too small or too large.

(59) (5) Regarding Kind of Base Material (Calcined Gypsum)

Examples 5-1 to 5-3 and Comparative Examples 3 to 5

(60) In a juicer-mixer (product number MX-X107, manufactured by Panasonic Corporation), 1 part of a pigment (ultramarine), 30 parts of the kind of base material as shown in Table 5, and 0.3 parts of amorphous silica (number average particle diameter: 30 nm) were placed, and mixed and pulverized for 60 seconds to prepare a coloring agent composition. In addition, any of hemihydrate gypsum, hemihydrate gypsum, and type III anhydrous gypsum used was manufactured (volume average particle diameter: 50 m) by Yoshino Gypsum Co., Ltd. Moreover, colored gypsum powders and colored gypsum hardened bodies were prepared and the colorability and color unevenness thereof were evaluated in the same manner as in the case of the aforementioned Examples 1-1 to 1-5. The results are shown in Table 5.

(61) TABLE-US-00005 TABLE 5 Examples Comparative Examples 5-1 5-2 5-3 3 4 5 Pigment (parts) 1 Amorphous silica (parts) 0.3 Base material Bldending amount (parts) 30 Kind Hemihydrate Hemihydrate Type III Calcium Silica Talc gypsum gypsum anhydrous carbonate gypsum Colorability Colored gypsum powder 15.0 14.7 14.3 12.2 12.7 13.4 (b value) Colored gypsum 28.6 28.4 26.8 26.5 27.3 25.2 hardened body Color unevenness Colored gypsum Excellent Excellent Good Fair Poor Poor hardened body

(62) As shown in Table 5, it is understood that the colorability-improving effect and the color unevenness-improving effect are obtained by using hemihydrate gypsum, hemihydrate gypsum, and type III anhydrous gypsum, which are each calcined gypsum, as a base material. In addition, it is understood that a more excellent colorability-improving effect and a more excellent color unevenness-improving effect are obtained in the case where hemihydrate gypsum or hemihydrate gypsum is used as compared with the case where type III anhydrous gypsum is used.

(63) (6) Regarding Mixing Method

Examples 6-1 and 6-2

(64) In a juicer-mixer (product number MX-X107, manufactured by Panasonic Corporation), 1 part of a pigment (ultramarine), 30 parts of the kind of base material as shown in Table 6, and 0.3 parts of amorphous silica (number average particle diameter: 30 nm) were placed, and mixed and pulverized for 60 seconds to prepare a coloring agent composition. Moreover, colored gypsum powders and colored gypsum hardened bodies were prepared and the colorability and color unevenness thereof were evaluated in the same manner as in the case of the aforementioned Examples 1-1 to 1-5. The results are shown in Table 6.

Examples 6-3 and 6-4

(65) In a plastic bag, 1 part of a pigment (ultramarine), 30 parts of the kind of base material as shown in Table 6, and 0.3 parts of amorphous silica (number average particle diameter: 30 nm) were placed and well shaken for 60 seconds to mix the contents, thereby preparing a coloring agent composition. Moreover, colored gypsum powders and colored gypsum hardened bodies were prepared and the colorability and color unevenness thereof were evaluated in the same manner as in the case of the aforementioned Examples 1-1 to 1-5. The results are shown in Table 6.

Comparative Examples 6 and 7

(66) In a plastic bag, 1 part of a pigment (ultramarine) and 30 parts of the kind of base material as shown in Table 6 were placed and well shaken for 60 seconds to mix the contents, thereby preparing a coloring agent composition. Moreover, colored gypsum powders and colored gypsum hardened bodies were prepared and the colorability and color unevenness thereof were evaluated in the same manner as in the case of the aforementioned Examples 1-1 to 1-5. The results are shown in Table 6.

(67) TABLE-US-00006 TABLE 6 Examples Comparative Examples 6-1 6-2 6-3 6-4 6 7 Pigment (parts) 1 Amorphous silica (parts) 0.3 0 0 Base material Blending amount (parts) 30 Kind Hemihydrate Hemihydrate Hemihydrate Hemihydrate Hemihydrate Hemihydrate gypsum gypsum gypsum gypsum gypsum gypsum First step *1 *2 *2 Colorability Colored gypsum powder 14.7 15.0 9.2 10.0 6.2 7.1 (b value) Colored gypusm 28.4 28.6 27.3 24.6 23.0 23.6 hardened body Color unevenness Colored gypsum Excellent Excellent Fair Good Poor Poor hardened body *1: Juicer-Mixer was used (pulverization was performed concurrently with mixing). *2: Plastic bag was used (mixing alone).

(68) As shown in Table 6, it is understood that the colorability-improving effect and the color unevenness-improving effect are more improved by not only simply mixing but also pulverizing the pigment, the base material (calcined gypsum), and the amorphous silica concurrently with mixing (namely, by performing co-pulverization).

(69) (7) Regarding Kind of Gypsum (Matter to be Colored)

Examples 7-1 to 7-5 and 8-1 to 8-5

(70) In a juicer-mixer (product number MX-X107, manufactured by Panasonic Corporation), 1 part of a pigment (ultramarine), 30 parts of the kind of base material (manufactured by Yoshino Gypsum Co., Ltd., volume average particle diameter: 50 m) as shown in Tables 7 and 8, and 0.3 parts of amorphous silica (number average particle diameter: 30 nm) were placed, and mixed and pulverized for 60 seconds to prepare a coloring agent composition. Moreover, colored gypsum powders and colored gypsum hardened bodies were prepared and the colorability and color unevenness thereof were evaluated in the same manner as in the case of the aforementioned Examples 1-1 to 1-5 except that the kinds of gypsum (matter to be colored) as shown in Tables 7 and 8 were used as a raw material powder gypsum (matter to be colored). The results are shown in Tables 7 and 8. However, in the case where dihydrate gypsum or type II anhydrous gypsum was used as gypsum (matter to be colored), the colored gypsum hardened body was not prepared and the evaluation of color unevenness was not conducted. In addition, both the dihydrate gypsum and the type II anhydrous gypsum used were manufactured by Yoshino Gypsum Co., Ltd.

(71) TABLE-US-00007 TABLE 7 Examples 7-1 7-2 7-3 7-4 7-5 Pigment (parts) 1 Amorphous silica (parts) 0.3 Base material Blending amount (parts) 30 Kind Hemihydrate gypsum Gypsum (matter to be colored) Dihydrate Hemihydrate Hemihydrate Type II Type III gypsum gypsum gypsum anhyrous anhydrous gypsum gypsmn Colorability Colored gypsum powder 14.3 14.7 14.9 14.4 14.7 (b value) Colored gypsum 28.4 28.4 27.3 hardened body Color unevenness Colored gypsum Excellent Excellent Excellent hardened body

(72) TABLE-US-00008 TABLE 8 Examples 8-1 8-2 8-3 8-4 8-5 Pigment (parts) 1 Amorphous silica (parts) 0.3 Base material Blending amount (parts) 30 Kind Hemihydrate gypsum Gypsum (matter to be colored) Dihydrate Hemihydrate Hemihydrate Type II Type III gypsum gypsum gypsum anhyrous anhydrous gypsum gypsmn Colorability Colored gypsum powder 14.6 15.0 15.0 14.7 14.7 (b value) Colored gypsum 28.6 28.4 27.6 hardened body Color unevenness Colored gypsum Excellent Excellent Excellent hardened body

(73) As shown in Tables 7 and 8, it is understood that an excellent colorability-improving effect and an excellent color unevenness-improving effect are obtained in the case where any kind of gypsum was used as the matter to be colored.

INDUSTRIAL APPLICABILITY

(74) Use of the coloring agent composition according to the present invention makes it possible to produce, without causing color unevenness, a gypsum hardened body such as a teeth model and an industrial model; and a liquid, semi-liquid, or powdered gypsum product which are uniformly colored.