Process of producing nanofibrillated cellulose with low energy consumption

Abstract

The present invention refers to the separation of cellulose pulp into distinct fractions with different draining and morphological characteristics, as well as the use of part of these fractions for the production of nanocellulose. The process in reference combines the unitary operations of fiber separation, thickening to a certain consistency, draining and drying of the cellulosic pulp with the high drainage ability and production of nanocellulose from high primary fines content pulp. The process may consider any cellulosic pulp fiber derived from short or long fiber woods such as Eucalyptus, Corymbia, Birch, Aspen, Pinus, recycled fibers, etc., their residues such as bark, sawdust, etc.

Claims

1. Process of producing nanofibrillated cellulose and a market pulp characterized by comprising the steps of: a) cooking and bleaching of biomass generating a cellulosic material comprising a reduced amount of lignin and extractives; b) separating a fiber line from the cellulosic material, wherein the fiber line comprises fines which are in its totality primary fines, and the fiber line has the following characteristics: b.1) average fiber length of 0.3 to 2.5 mm; and b.2) primary fines content of 3% to 30% by mass of the fiber line; c) fractionating the separated fiber line of step b) by means of a fractionating system into at least two streams, a high-primary fines content material stream and a low primary fines content pulp stream; d) separating the high-primary fines content material stream obtained in step c), wherein the high-primary fines content material stream has a content of 10% to 90% of primary fines by mass of the high-primary fines content material stream and consistencies of 0.02% to 1%; e) thickening the high-primary fines content material stream of step d) until its consistencies reach 2% to 15%; f) submitting the thickened material of step e) to a nanofibrillated cellulose production process, wherein it is subjected to mechanical refining energy, being the energy consumption used for the generation of the nanofibrillar cellulose smaller than in comparison with non-fractionated or segregated cellulosic pulp starting material; g) separating the low primary fines content pulp stream of c) which comprises pulp with a °SR reduction of 15% to 50%, and water retention value reduction between 7% and 35% when compared to the cellulosic material; and h) drying of the low primary fines content pulp of step g) in pulp drying machines.

2. Process, according to claim 1, characterized in that the resulting cellulosic material of step a) is selected from bleached cellulose, semi-bleached cellulose, and combinations thereof.

3. Process, according to claim 1, characterized in that step c) is carried out through a fractionating system selected from the group comprising pressurized basket screening systems, fine particulate recovering washers, hydrocyclones and combinations thereof.

4. Process, according to claim 1, characterized in that the refining energy of the nanofibrillated cellulose production process of step f) is associated with enzymatic treatment.

5. Process, according to claim 1, characterized in that the high primary fines content pulp of step d) has °SR between 20 and 95, and water retention values between 140 and 690 percent.

Description

BRIEF DESCRIPTION OF DRAWINGS

(1) The structure and operation of the present invention, together with further advantages thereof nay be better understood by reference to the accompanying drawings and the following descriptions:

(2) FIG. 1 illustrates a simplified scheme of obtainment of products from this invention: nanofibrillar cellulose and high drainage pulp for paper making.

(3) FIG. 2 shows examples of the evolution of fines formation (measured by Britt Jar) and width of fibers (measured by optical morphology) in kraft pulp mills.

(4) FIG. 3 shows the characterization of the fines material present in the pulp samples (Low fines content and high fines content) in extreme conditions.

(5) FIG. 4 illustrates the impact of the fines in drainability of pulp in lab conditions.

(6) FIG. 5(a)-(c) shows a morphological characterization of processed pulp with lower fines content, showing its properties and uniqueness in terms of primary fines content, with increase in general fiber length and width of fibers.

(7) FIG. 6(a)-(d) illustrates the characterization of pulp generated in pilot scale with lower fines content, so called high drainage pulp in terms of resistance to drainage (°SR), water retention value, bulk and water absorption of a never dried Eucalyptus pulp.

(8) FIG. 7 illustrates a pilot plant trial data showing the gains in dryness after press with High Drainage pulp containing reduced primary fines content, and showing the increase in the dryness content for the treated (high drainage) pulp. The dryness is a direct measurement for energy consumption. The higher the dryness, the smaller the energy consumption to dry a pulp in a pulp machine.

(9) FIG. 8(a)-(e) shows the characterization of high fines content pulp, generated through pi I of process, considering its morphology and drainability characteristics.

(10) FIG. 9 shows high resolution microscopy of nanofibrillar cellulose based on 4 different types of pulps, obtained in lab: Reference or Standard common pulp; High primary fines content pulp with 25% primary fines in mass; High primary fines content pulp With 50% primary fines in mass; High primary fines content pulp with 75% primary fines in mass; pilot trial High primary fines content pulp with 37% showing that all samples were able to generate nano dimensions in the final nanofibrillar material.

(11) FIG. 10 shows a picture in scale of standard cellulose fibers, for reference in comparison with the nanofibrillar cellulose. It is to be noted that the scale is 10 times higher than that shown in FIG. 9.

(12) FIG. 11 illustrates the average of the width of nanofibrils from different primary fines content samples, including the High Fines Content Pulp generated in pilot conditions, showing that all the Nanofibrillar celluloses generated have similar width of nanofibrils average.

(13) FIG. 12(a) shows a comparison of tensile strength of a standard pulp added with nanofibrillar cellulose in order to evaluated the quality of the nanofibrillar cellulose in terms of tensile strength generation in a given pulp, showing that in terms of quality of nanofibrils generated all pulps were similar.

(14) FIG. 12(b) shows a comparison of resistance to drainage of a standard pulp added with nanofibrillar cellulose in order to evaluated the quality of the nanofibrillar cellulose in terms of Schopper Riegler degree increment generation in a given pulp, showing that in terms of quality of nanofibrils generated all pulps were similar.

(15) FIG. 13 illustrates the energy consumption in kWh per metric ton consumed to generate a given quality of nanofibrillar cellulose in a pilot plan with capacity to produce 2 tons per day, showing a significant decrease in the energy consumption when using the high primary fines content pulp as starting material for the nanocellulose production.

DETAILED DESCRIPTION OF THE INVENTION

(16) Although the present invention may be susceptible to various embodiments, there are show in the drawings and in the following detailed discussion, preferred embodiments with the understanding that the present disclosure is to be considered as an exemplification of the principles of the invention and is not intended to limit the present invention to what is illustrated and described herein.

(17) The present invention refers to a process of producing nanofibrillated cellulose with lower energy consumption, and a pulp with high drainage ability. The energy consumption set herein is based on the sane treatment performed on a reference (standard or common) pulp, compared to different level s of tri al pulps according to what is proposed in the present invention.

(18) The energy consumption reduction is possible with the production of a raw material of cellulose primary fines obtained by fractionating of cellulose pulp, followed by a refining treatment.

(19) Although the nanofibrillated cellulose production process involves a similar unitary operation, the present invention refers to the new use of pre-fractionated raw material combined with unique process parameters for the production of cellulosic material having nanometric dimensions with significant reduction of energy consumption.

(20) The preferred embodiment of this invention relates to a process of producing nanofibrillated cellulose with Low energy consumption comprising the steps of: a) cooking and bleaching of biomass, generating a mass rich in cellulosic and hemicellulosic polymer chains, comprising very reduced amount of lignin and extractives. b) selecting and directing a cellulosic material from a fiber line having the following characteristics: b. 1) average fiber length: 0.3 to 2.5 mm and b. 2) primary fine content: 3% to 30% of fines by mass; c) fractionating the selected material by means of a fractionating system d) separating one stream with the high-primary fines content material fraction obtained in step c), in a percentage range from 10% to 90% of primary fines and consistencies of 0.02% to 1% e) thickening of this stream until consistencies of 2% to 15% f) submitting the thickened material to a nanofibrillated cellulose production process, wherein it is subjected to mechanical refining energy, associated or not with enzymatic treatment, being the energy consumption used for the generation of the nanofibrillar cellulose smaller than in comparison with common cellulosic pulp starting material. g) separating the other fraction stream with lower primary fines content, so called high drainage pulp, presenting a massic amount of fines of about 3 to 8% preferably between 4% and 7% with significant lower resistance to drainability and water retention value, typically presenting °SR reduction of 15% to 50% more preferable between 20% and 40% water retention value reduction between 7% and 35% more preferable between 10% and 25% h) drying of the Low primary fines content pulp in drying pulp machines with lower consumption of drying energy, this reduction being typically between 2% and 10% in total energy when compared with the energy used to dry common pulp.

(21) In step a), the cellulosic material is selected from cooked materials, and maybe bleached cellulose, semi-bleached cellulose, unbleached cellulose, recycled fibers and combinations thereof.

(22) The process may consider any cellulosic pulp fiber derived from short or long fiber mods such as Eucalyptus, Corymbia, Birch, Aspen, Pinus, etc., their residues such as bark, sawdust, etc., and also any type of recycled fibers, preferably of Eucalyptus and Corymbia genders.

(23) The pre-selected materials then fractionated in step b) preferably through a fractionating system but not limited to pressurized basket screening systems, fines particulate recovering washers or hydrocyclones, in one or more steps, wherein combinations of the aforementioned equipment may be used.

(24) The high-primary fines material fraction obtained from step b) is then subjected to thickening and nanofibrillar cellulose production process, in which it will be subjected to refining energy so that its element sizes are reduced to nanometric fractions.

(25) The fraction of fibers with lower primary fines content, containing a massic amount of fines of about 3 to 8% preferably between 4% and 7% with significant lower resistance to drainability and water retention value.

(26) In step d), the high primary fines content pulp is characterized by °SR between 20 and 95; and water retention values between 140 and 690 percent.

(27) In step g), the absolute variables specific from Eucalyptus treatments in the High Drainage Pulp after pulp dryer are: fines content between 3% to 8.5% preferably between 4 to 7% water retention value between 90 and 140 g/g, more preferable between 110 and 130 and °SR between 12 and 19, more preferable between 14 and 17.

(28) FIG. 1 describes briefly the processual steps from raw material selection until the production of the Nanofibrillated cellulose and the high drainage pulp.

(29) FIG. 2 describes the increase in the fines content in two different kraft mills, showing the crescent profile of fines content according to the course of the process. The profile may be slightly different case by case for each mill due to the kind of equipments, intensity of cooking and mechanical energy suffered by the fibers.

(30) Likewise, the width of the fibers also decreases due to the chemical peeling reactions also contributing to the increase and generation of the fiber category so called primary fines.

(31) FIG. 3 shoes the microscopic aspect of the fibers (in the right) and primary fines (in the left). A high amount of short fibers and small elements is present in the primary fines sample and barely seen in the samples whose material was removed, allowing the high drainability of the pulp trough physical and chemical improved flow through the void volumes Created.

(32) FIG. 4 shows the impact of the primary fines (measured by Britt Jar in mass percentage) in drainability aspects represented by Schopper Rigler degree (°SR) and water retention value. The values clearly indicates the high impact of the presence of primary fines in the drainability of the fibers.

(33) FIG. 5 shows the morphological characteristic of the high drainage pulp, with reduced primary fines content to its half, and increase of fiber length and width.

(34) FIG. 6 show the drainability and absorption properties characterization of pulp generated in pilot scale with lower fines content. The properties of the so called High drainage pulp in terms of resistance to drainage (OSR), water retention value, bulk and water absorption demonstrates that considerable gains in the drainability properties are present, signifying high potential for energy consumption reduction in the drying of this pulp in pulp and paper machines. The absence of fines also creates higher bulk pulp, allowing the pulp to absorb more eater per gram of pulp.

(35) FIG. 7 shows the possible gains in dryness after pulp machine press, allowing the energy saving in between 2 to 10% for pulp drying.

(36) FIG. 8 shoves the properties of the high primary fines content pulp, generated through pilot processes. In FIG. 8-a), the primary fines content show has values obtained from one of the conditions used in pilot trials, and can be higher or lower depending of the need and technology set up used. The impact on drainability as demonstrated in item b and c is enormous, showing very high drainage and voter retention values caused by the presence of the primary fines in the pulp. The items d and e show the average fibers length and width measured, demonstrating that the fibers contained in the materials are also shorter and narrower that the regular ones.

(37) FIG. 9 shows examples of images showing the width of the nanofibrils generated from increasing primary fines content samples.

(38) The average of its width vas done by evaluating 400 measurements for each sample, from at least 10 high resolution images and resulted in very similar width for all the samples, showing that the quality of the nanofibrillated cellulose is the sane, as seen in FIG. 11.

(39) FIG. 12 shows the characterization of the potential of modifying properties in a given standard pulp by adding Nanofibrillar cellulose in terms of tensile Strength and Resistance to drainage increase.

(40) As can be seen from FIG. 12, there is no difference between the quality of the nanofibrillated cellulose generated from standard pulp and from the high primary fines content pulp.

(41) FIG. 13 shows the energy consumption in kWh per metric ton consumed to generate a given quality of nanofibrillar cellulose in a pilot plan with capacity to produce 2 tons/day. By convention, and based on literature and machine construction for nanocellulose obtainment trough refining energy (please see reference WO 2013/188657) when 90% of the particles size in length is smaller than 200 micrometers, obtained in morphological measurements, the product can be considered a nanofibrillated cellulose according to the definition of having at least one of its three dimensions between 1 and 100 nanometers according to ISO/TS 20477:2017—Nanotechnologies Standard terms and their definition for cellulose nanomaterial.

(42) In the chart 13, it is shown that the energy necessary to the obtainment of high quantity of smaller particles is much lower than the standard pulp. Considering the standard value of 90% the total net energy reduces to its half. It is possible also to see that if necessary, the application of energy can be such that the quality of the nanofibrillated celullose can be increase (through the increase of the amount of fibers in smaller size than 200 micrometers).

(43) Thus, although only some embodiments of the present invention have been shown, it will be understood that several omissions, substitutions and changes can be made by a person skilled in the art, without departing from the spirit and scope of this invention. The embodiments described should be considered in all respects only as illustrative and not in a restrictive manner.

(44) It is expressly provided that all combinations of the elements that perform the same function substantially the same way to achieve the same results are within the scope of the invention. Substitution of elements in an embodiment described to another are also fully comprised and contemplated.

(45) It should be also understood that some of the drawings are not necessarily in scale, and are conceptual in nature. The intention is, therefore, to be limited, as indicated by the scope of the attached claims.