Method for manufacturing transparent conductive film

Abstract

A method for manufacturing a transparent conductive film, including: 1) providing a conductive scraper including a slurry feeding mouth and a slurry discharging gap; 2) placing a transparent film including a prefabricated groove on a conductive moving table, moving the conductive moving table horizontally in relation to the conductive scraper, controlling the moving speed of the conductive moving table at between 0.1 and 1 m/min, and allowing the conductive slurry to flow out of the conductive scrapper via the slurry discharging gap; 3) applying a voltage between the conductive moving table and the conductive scraper, and driving the conductive slurry flowing out of the conductive scraper to fill the groove of the transparent film by an electrodynamic force produced by the voltage; and 4) curing the conductive slurry filled in the groove of the transparent film.

Claims

1. A method for manufacturing a transparent conductive film, the method comprising: 1) providing a conductive scraper, the conductive scraper comprising a slurry feeding mouth and a slurry discharging gap, and employing the conductive scraper as a channel for introducing a conductive slurry and as an electrode; 2) placing a transparent film comprising a prefabricated groove on a conductive moving table, moving the conductive moving table horizontally in relation to the conductive scraper, controlling a moving speed of the conductive moving table at between 0.1 and 1 m/min, and allowing the conductive slurry to flow out of the conductive scrapper via the slurry discharging gap thereof; 3) applying a voltage between the conductive moving table and the conductive scraper, controlling an average electric field strength between the conductive scraper and the conductive moving table at between 50 and 5000 V/mm; and driving the conductive slurry flowing out of the conductive scraper to fill the groove of the transparent film by an electrodynamic force produced by the voltage; and 4) curing the conductive slurry filled in the groove of the transparent film, whereby obtaining a transparent conductive film.

2. The method of claim 1, wherein the voltage in 3) is a DC voltage or a low frequency AC voltage; and when the low frequency AC voltage is adopted, a frequency thereof is controlled at no more than 1 kHz.

3. The method of claim 1, wherein a curing mode in 4) comprises: heating curing, ultraviolet light (UV) light curing, and volatile curing; and the curing mode is adopted according to a material quality of the conductive slurry.

4. The method of claim 1, further comprising performing sintering treatment and polishing treatment after 4).

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) The invention is described hereinbelow with reference to the accompanying drawings, in which:

(2) FIG. 1 is a schematic diagram showing a filling process of a transparent film with a conductive slurry driven by an electric field force in accordance with one embodiment of the invention;

(3) FIG. 2 is a filling device driven by an electric field force in accordance with one embodiment of the invention;

(4) FIG. 3A is a picture showing a filling effect obtained from a conventional scrapping method (in the absence of applying a voltage);

(5) FIG. 3B is a picture showing a filling effect obtained from a scrapping method by applying a voltage of 200 V in accordance with one embodiment of the invention;

(6) FIG. 4A is a picture showing uniformity of a conductive material produced from a conventional scrapping method; and

(7) FIG. 4B is a picture showing uniformity of a conductive material produced from a scrapping method by applying a voltage in accordance with one embodiment of the invention.

(8) In the drawings, the following reference numbers are used: 1. Conductive scraper; 2. Conductive slurry; 3. Transparent film comprising groove; and 4. Conductive moving table.

DETAILED DESCRIPTION OF THE EMBODIMENTS

(9) For further illustrating the invention, experiments detailing a method for manufacturing a transparent conductive film are described below. It should be noted that the following examples are intended to describe and not to limit the invention.

(10) A method for manufacturing a transparent conductive film based on filling driven by an external electric field, the method comprises the following steps:

(11) 1) Preparation of a conductive scrapper 1: as shown in FIGS. 1-2, the conductive scrapper 1 comprises a slurry feeding mouth and a slurry discharging gap. The conductive scrapper 1 is used as a channel for introducing a conductive slurry 2 as well as an electrode.

(12) 2) Continuous feeding the conductive slurry: as shown in FIG. 2, a transparent film 3 comprising prefabricated grooves is disposed on a conductive moving table 4. The conductive moving table 4 is enabled to move horizontally in relation to the conductive scraper 1 at a moving speed of between 0.1 and 1 m/min. The conductive slurry 2 flows out of the conductive scrapper 1 via the slurry discharging gap thereof.

(13) 3) Electrodynamic filling: as shown in FIG. 2, a voltage is applied between the conductive moving table 4 and the conductive scraper 1, and an average electric field strength between the conductive scraper 1 and the conductive moving table 4 is controlled at between 50 and 5000 V/mm The voltage herein is a DC voltage or a low frequency AC voltage. When the low frequency AC voltage is adopted, a frequency thereof is controlled at no more than 1 kHz. The conductive slurry 2 flowing out of the conductive scraper 1 is driven by an electrodynamic force produced by the voltage to fill the grooves of the transparent film 3.

(14) 4) Curing the conductive slurry filled in the grooves of the transparent film: curing methods are adopted according to differences in material qualities of different conductive slurries. The curing method comprises: heating curing, ultraviolet light (UV) light curing, and volatile curing. A transparent conductive film is acquired after the curing. Sintering treatment and polishing treatment are conducted subsequently if necessary.

EXAMPLE 1

(15) To illustrate the superiority of the scrapping method adopting the electrodynamic force in the filling efficiency and the filing effect, a UV cured conductive material is used in this example. The UV cured conductive material is filled in the grooves of the transparent film, and a UV light is used to cure the conductive material. The conductive material is then separated from the grooves of the transparent film. The advantage of the filling driven by the external electric filed is evaluated by observation of an integrity of the microstructure of the separated conductive material. Comparisons of the filling efficiencies are made between conventional method and the present method using the external electric field. FIG. 3A is a picture showing a filling effect obtained from the conventional method (in the absence of applying any voltage). FIG. 3B is a picture showing the filling effect obtained from the present method by applying a voltage of 200 V. Both the methods are conducted at a scrapping speed of 0.5 mm/min. It is known from the comparison that the liquid material is more easily filled into the grooves of the transparent film under the condition of applying a voltage.

EXAMPLE 2

(16) Because directions of the grooves of the transparent film are variable in practical operation, filling effects of grooves in different directions are distinct from one another by adopting the conventional filling method. As shown in FIG. 4A, in the conventional scrapping filling method, when the grooves are mutually perpendicularly arranged, the grooves arranged in a direction parallel to the scrapping direction are prone to be filled, whereas the grooves arranged in the direction perpendicular to the scrapping direction are often entrapped with air bubbles. As shown in FIG. 4B, in the filling method driven by the external electric field of the invention, the mutually perpendicular grooves can be completely filled. In practical industrial application, in order to prevent the entrapment of the air bubbles, the conventional scrapping process often requires to reduce the scrapping speed of the scrapper, which largely affects the production efficiency. The method of the invention adopts the electrodynamics effect produced by the external electric field, which is adapted to avoid the defects of the entrapment of the air bubbles to a large degree and enable the scrapper to move at a higher scrapping speed, thereby improving the production efficiency.

(17) While particular embodiments of the invention have been shown and described, it will be obvious to those skilled in the art that changes and modifications may be made without departing from the invention in its broader aspects, and therefore, the aim in the appended claims is to cover all such changes and modifications as fall within the true spirit and scope of the invention.